Journal of Materials

Volume 2013 (2013), Article ID 603648, 5 pages

http://dx.doi.org/10.1155/2013/603648

Research Article

PLD Grown Polycrystalline Tungsten Disulphide (WS₂) Films

Salman Alfihed,¹ Mohammad Hossain,2,3 Abdulaziz Alharbi,¹ Ahmed Alyamani,¹ and Fahhad H. Alharbi1,2

¹King Abdulaziz City for Science & Technology, Riyadh, Saudi Arabia

²Qatar Environment & Energy Research Institute, Qatar Foundation, Doha, Qatar

³Solar Energy Research Institute (SERI), Universiti Kebangsaan Malaysia, Selangor, 43600 Bangi, Malaysia

Received 30 November 2012; Accepted 17 June 2013

Academic Editor: Ram Katiyar

Copyright © 2013 Salman Alfihed et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

Polycrystalline WS₂ films were grown by pulsed laser deposition (PLD) system at relatively low temperature. The main objective of this study is to optimize the growth conditions for polycrystalline WS₂ films at relatively low temperature to use them for photovoltaics (PVs). Different growth conditions and substrates are used and examined systematically. It is found out that films grown on strontium titanate SrTiO₃ (STO) substrate have the best structural properties when compared to other substrates examined in this work. X-ray diffraction and optical characterizations of these films reveal crystallographic growth and very promising optical properties for PVs. Furthermore, it was observed that higher growth temperature (>300°C) has an unfavorable effect on the layers by creating some tungsten metallic droplets.

1. Introduction

The rising interest and research on alternative, abundant, and nontoxic absorber materials like tungsten disulfide  (WS₂) could play a major role to advance the photovoltaics field and renewable energy market [1–7]. WS₂  is layered transition metal dichalcogenide (TMDC) material. For decades [8, 9], it has been known to be a promising alternative solar cell material to replace the conventional ones such as Si, CIGS, and CdTe due to its matching optical and electrical properties. However, WS₂ has been investigated mainly for non-optoelectronic applications [10] such as using it as lubricant. For electronics and optoelectronics devices, the TMDC materials start gaining very growing attention recently [2, 9, 11].

The p-type WS₂ is an indirect band gap material (1.29 eV) with direct transitions start about 1.7 eV. Along the layers, it has excellent transport properties; some reports estimated the diffusion length to be in the range of 200 μm [12, 13]. Yet, its transport is anisotropic and is very small between the layers. Optically, it has absorption coefficient of greater than 10⁵ cm⁻¹ for photon energies above 1.75 eV [14, 15]. The required absorption length to catch most of the absorbable photons from solar radiation is less than 1 μm [1]. This is much less than the measure diffusion length and exhibits WS₂ strong potential for PVs. In 1982, an efficiency of 6% (the short circuit current 26 mA cm², the open circuit voltage 0.42 V, and fill factor 60%) was achieved from WS₂ photoelectrochemical cell [16].

In thin-film form, WS₂ has been grown by various techniques like sputtering [17], pulsed laser deposition (PLD) [18], chemical bath deposition (CBD) [19], electrodeposition technique [20], and many others. The growth of polycrystalline films with large grain sizes in inclined orientation at relatively low growth temperature is necessary to make efficient solar cells [21]. For most TMDC, the substrates play important role in the crystal growth for them [22] as they have a tiny tolerance for lattice mismatch. It is not uncommon to end up with amorphous films. Furthermore, the high lattice mismatch at the junction results in high defect.

In this work, good-quality polycrystalline WS₂ thin films have been grown at relatively low temperatures of 250°C and 300°C using PLD technique on STO substrates. XRD data shows preferred orientation for the as deposited films. The measured structural and optical properties are presented and discussed.

2. Experimental

All the thin films of WS₂ that were studied for this paper were deposited on soda-lime glass, quartz, STO, and sapphire substrates at different temperature using the PLD/MBE-2300 system from PVD Products, Inc. KrF (248 nm) excimer laser (Compex Pro 205) with pulse duration of 20 ns and a repetition with rate of 10 Hz was used for ablation of the target, which was held in a rotating carousel to enable uniform ablation of the target surface. The incident angle of the laser with respect to the target was ~45° with laser energy of 300 mJ; the partial pressure was sustained at 2 × 10⁻⁶ mTorr during the growth process. A WS₂ target of 99.9% purity from American Elements Co. is used. The as deposited films were characterized using X-ray diffraction (XRD) and ellipsometer for structural and optical data.

3. Results and Discussions

3.1. XRD Analysis

Figure 1 shows the diffraction patterns of WS₂ films deposited on STO and soda-lime glass substrates with the diffraction angle varied between 10° and 60° at different growth temperatures ranging between 200°C and 400°C. No peaks are obtained from the films grown on top of glass substrates and films turned to be amorphous. This amorphous phase is also obtained for the films grown on quartz and sapphire due to the high lattice mismatch between the deposited films and substrate [22–27].

(a)

(b)

(c)

(d)

(e)

Figure 1: XRD patterns of WS₂ films on STO and soda-lime glass substrates at different temperatures ranged between 200°C and 400°C at 50°C increment.

Yet, there are sharp peaks for the WS₂ grown on STO substrates. The large peaks at equal to 22.8° and 46.5° are due to the STO substrates. All the other peaks are associated with WS₂ films. This illustrates that WS2 films crystal orientation can be controlled by a proper selection of substrates, and this feasible possibility is shown in the next paragraph through growing preferred orientation.

Figure 2 combines all XRD data of the films grown on STO substrates. The peaks are associated with (101), (012), (104), and (015) orientations, which corresponds to the rhombohedral WS₂ (JCPDS 35-0651) with the aforementioned peaks being intense among others. Due to the small lattice mismatch of about 3%, it was possible to realize a polycrystalline growth WS₂ films on STO [22].

Figure 2: XRD patterns of polycrystalline WS₂ films on STO substrates at different temperatures ranged between 200°C and 400°C at 50°C increament.

3.2. Optical Characterization

The optical characterization of the as grown samples was carried out using an ellipsometer. Figure 3 shows the measured extinction coefficient values for the films deposited at the various temperatures. It can be observed at the higher temperature (>350°C) that is not vanishing for low energies. The formation of metallic tungsten droplets at these comparatively high temperatures is the main reason for this effect. Beside this, the high value of refractive index () (Figure 4) is obtained for all the WS₂/STO films, which is certainly desirable for PVs [1, 2, 28].

Figure 3: values of the grown WS₂ films.

Figure 4: values of the grown WS₂ films.

Figure 5 shows the absorption coefficients for the as deposited films. It is fractionally smaller than what has been reported before [1, 15, 16]. Yet, the obtained values are still very promising for PVs.

Figure 5: The absorption coefficients of the grown WS₂ films.

3.3. Thickness and Roughness Analysis

The thicknesses and roughnesses are also estimated from ellipsometry measurements. Figures 6 and 7 show the thickness and the ratio between the roughness and thickness variations, respectively, with temperature. Clearly, the thickness has a decreasing trend with the temperature. This behavior is common for the sulfides where the sulfur deficiency increases with the temperature. For the roughness, the ratio values between it and thickness are obviously increasing with the temperature due to the formation of droplets and also the reduction of the thickness.

Figure 6: Thickness variation of WS₂ films for the temperature 200°C−400°C.

Figure 7: The ratio values between the roughness and thickness of WS₂ films (200°C−400°C).

4. Conclusion

Polycrystalline WS₂ films were grown by PLD at relatively low temperature. This is part of the initial work to use WS₂ for PVs. The main objective of this initial study is to optimize the growth conditions for polycrystalline WS₂ films at relatively low-temperature. As known, the low-temperature growth of polycrystalline is desirable as PVs are largely multilayer. Different growth conditions and substrates are used and examined systematically. It is found out that films grown on STO substrate resulted in the best structural properties when compared to other substrates examined in this work. This is mainly due to the small lattice mismatch of 3%. X-ray diffraction and optical characterizations of these films reveal crystallographic growth and very promising optical properties for PVs. Furthermore, it was observed that higher growth temperature (>300°C) has an unfavorable effect on the layers by creating some tungsten metallic droplets.

References

F. Alharbi, J. D. Bass, A. Salhi, A. Alyamani, H.-C. Kim, and R. D. Miller, “Abundant non-toxic materials for thin film solar cells: alternative to conventional materials,” Renewable Energy, vol. 36, no. 10, pp. 2753–2758, 2011.

M. I. Hossain and F. H. Alharbi, “Recent advances in alternative materials photovoltaics,” Materials Technology, vol. 28, pp. 88–97, 2013.

H. Tributsch, “Hole reactions from d-energy bands of layer type group VI transition metal dichalcogenides,” Journal of the Electrochemical Society, vol. 125, no. 7, pp. 1086–1093, 1978.

O. Lignier, G. Couturier, and J. Salardenne, “Growth mechanism of 2H-WS₂ thin films: a similar process to graphitization,” Thin Solid Films, vol. 338, no. 1-2, pp. 75–80, 1999.

Q. H. Wang, K. Kalantar-Zadeh, A. Kis, J. N. Coleman, and S. Michael Strano, “Electronics and optoelectronics of two-dimensional transition metal dichalcogenides,” Nature Nanotechnology, vol. 7, pp. 699–712, 2012.

L. Liu, S. B. Kumar, Y. Ouyang, and J. Guo, “Performance limits of monolayer transition metal dichalcogenide transistors,” IEEE Transactions on Electron Devices, vol. 58, no. 9, pp. 3042–3047, 2011.

W. S. Hwang, M. Remskar, R. Yan, et al., “Transistors with chemically synthesized layered semiconductor WS₂ exhibiting 10⁵ room temperature modulation and ambipolar behavior,” Applied Physics Letter, vol. 101, Article ID 013107, 4 pages, 2012.

R. Tenne, L. Margulis, M. Genut, and G. Hodes, “Polyhedral and cylindrical structures of tungsten disulphide,” Nature, vol. 360, no. 6403, pp. 444–446, 1992.

P. N. Keating, “Photovoltaic effect in photoconductors,” Journal of Applied Physics, vol. 36, no. 2, pp. 564–570, 1965.

L. Rapoport, N. Fleischer, and R. Tenne, “Applications of WS₂ (MoS₂) inorganic nanotubes and fullerene-like nanoparticles for solid lubrication and for structural nanocomposites,” Journal of Materials Chemistry, vol. 15, no. 18, pp. 1782–1788, 2005.

B. Radisavljevic, A. Radenovic, J. Brivio, V. Giacometti, and A. Kis, “Single-layer MoS₂ transistors,” Nature Nanotechnology, vol. 6, no. 3, pp. 147–150, 2011.

D. Tonti, F. Varsano, F. Decker, C. Ballif, M. Regula, and M. Remškar, “Preparation and photoelectrochemistry of semiconducting WS₂ thin films,” Journal of Physical Chemistry B, vol. 101, no. 14, pp. 2485–2490, 1997.

J. A. Baglio, G. S. Calabrese, E. Kamieniecki et al., “Characterization of n-type semiconducting tungsten disulfide photoanodes in aqueous and nonaqueous electrolyte solutions-photoxidation of halides with high efficiency,” Journal of the Electrochemical Society, vol. 129, no. 7, pp. 1461–1472, 1982.

D. A. Dholakia, G. K. Solanki, S. G. Patel, and M. K. Agarwal, “Two- and three-dimensional models for analysis of optical absorption in tungsten disulphide single crystals,” Bulletin of Materials Science, vol. 24, no. 3, pp. 291–296, 2001.

H. Jiang, “Electronic band structures of molybdenum and tungsten dichalcogenides by the GW approach,” Journal of Physical Chemistry C, vol. 116, no. 14, pp. 7664–7671, 2012.

G. Kline, K. K. Kam, R. Ziegler, and B. A. Parkinson, “Further studies of the photoelectrochemical properties of the group VI transition metal dichalcogenides,” Solar Energy Materials, vol. 6, no. 3, pp. 337–350, 1982.

V. Weiß, S. Seeger, K. Ellmer, and R. Mientus, “Reactive magnetron sputtering of tungsten disulfide (WS2-x) films: influence of deposition parameters on texture, microstructure, and stoichiometry,” Journal of Applied Physics, vol. 101, no. 10, Article ID 103502, 9 pages, 2007.

J. S. Zabinski, M. S. Donley, S. V. Prasad, and N. T. McDevitt, “Synthesis and characterization of tungsten disulphide films grown by pulsed-laser deposition,” Journal of Materials Science, vol. 29, no. 18, pp. 4834–4839, 1994.

P. P. Hankare, A. H. Manikshete, D. J. Sathe, P. A. Chate, A. A. Patil, and K. M. Garadkar, “WS₂ thin films: opto-electronic characterization,” Journal of Alloys and Compounds, vol. 479, no. 1-2, pp. 657–660, 2009.

J. J. Devadasan, C. Sanjeeviraja, and M. Jayachandran, “Electrodeposition of p-WS₂ thin film and characterisation,” Journal of Crystal Growth, vol. 226, no. 1, pp. 67–72, 2001.

S. Brunken, R. Mientus, and K. Ellmer, “In-situ energy-dispersive X-ray diffraction of metal sulfide assisted crystallization of strongly (001) textured photoactive tungsten disulfide thin films,” Thin Solid Films, vol. 517, no. 10, pp. 3148–3151, 2009.

M. Genut, L. Margulis, R. Tenne, and G. Hodes, “Effect of substrate on growth of WS₂ thin films,” Thin Solid Films, vol. 219, no. 1-2, pp. 30–36, 1992.

M. Regula, C. Ballif, J. H. Moser, and F. Lévy, “Structural, chemical, and electrical characterisation of reactively sputtered WSx thin films,” Thin Solid Films, vol. 280, no. 1-2, pp. 67–75, 1996.

I. Martin-Litas, P. Vinatier, A. Levasseur, J. C. Dupin, D. Gonbeau, and F. Weill, “Characterisation of r.f. sputtered tungsten disulfide and oxysulfide thin films,” Thin Solid Films, vol. 416, no. 1-2, pp. 1–9, 2002.

S. B. Sadale and P. S. Patil, “Synthesis of type-I textured tungsten disulfide thin films on quartz substrate,” Journal of Crystal Growth, vol. 286, no. 2, pp. 481–486, 2006.

K. Ellmer, “Preparation routes based on magnetron sputtering for tungsten disulfide (WS₂) films for thin-film solar cells,” Physica Status Solidi B, vol. 245, no. 9, pp. 1745–1760, 2008.

Z. Li-Na, W. Cheng-Biao, W. Hai-Dou et al., “Tribological properties of WS₂ composite film prepared by a two-step method,” Vacuum, vol. 85, no. 1, pp. 16–21, 2010.

P. Würfel, Physics of Solar Cells: from Principles to New Concepts, Wiley-VCH, Weinheim, Germany, 2005.