CuxAg1−xInS2 solid thin films were fabricated through a low-cost process. Particular process-related enhanced properties lead to reaching a minimum of lattice mismatch between absorber and buffer layers within particular solar cell devices. First, copper-less samples X-ray diffraction analysis depicts the presence of AgInS2 ternary compound in chalcopyrite tetragonal phase with privileged (112) peak (d112=1.70 Å) according to JCPDS 75-0118 card. Second, when x content increases, we note a shift of the same preferential orientation (112) and its value reaches 1.63 Å corresponding to CuInS2 chalcopyrite tetragonal material according to JCPDS 89-6095 file. Finally, the formation and stability of these quaternaries have been discussed in terms of the lattice compatibility in relation with silver-copper duality within indium disulfide lattice structure. Plausible explanations for the extent and dynamics of copper incorporation inside AgInS2 elaborated ternary matrices have been proposed.
1. Introduction
AgInS2 and CuInS2, which are both chalcopyrite ternary solids belonging to I-III-VI2 compounds, are attractive materials of photovoltaic cells and optoelectronic devices because of their good stability under solar radiation, their large absorption coefficient, and their band gap energy lying in 1.5−2.1 eV domain. Theoretical calculation regarding solar conversion efficiencies of 27–32% has been made with I-III-VI2 ternaries as absorbers. Even thin film solar cells of 12% efficiency have been successfully reached [1, 2]. However, these ternaries solar cells are typically fabricated by means of high-cost techniques, so that low-cost methods demand is noticeably increasing.
Indeed, the spray pyrolysis technique has not been widely used for preparing a large scale of such ternary materials for energy conversion purpose. In the same line, the mixture of both Ag and Cu as precursors of ternary materials in the started spraying solutions could lead to some various alloys having interesting physical characterisations. Ciszek has proposed a method to fabricate the quaternary CuxAg1−xInSe2 [3]. It is noted that CuInS2 material solidifies in chalcopyrite structures [4] whereas AgInS2 can solidify in two forms: chalcopyrite and orthorhombic [5, 6]. Moreover, the latest ternary compound could be obtained as n-type or p-type semiconductor using appropriate experimental chemical conditions [7–14].
In this work, we report for the first time the preparation on glass substrates at 420°C of quaternaries CuxAg1−xInS2 thin films using the spray pyrolysis technique from aqueous solutions. Each ternary has been achieved in our laboratory using appropriate conditions [6–8]. On the other hand, the structures of these films were studied by means of X-ray diffraction apparatus (Panalytical X Pert PROMPD, λ=1.54056 Å) within the lattice compatibility theory. The optical properties were obtained from the analysis of the experimental recorded transmission and reflectance spectral data over the wavelength range 300–1800 nm using unpolarized light by means of a spectrophotometer (Shimadzu UV 3100S) [15].
2. Results and Discussion2.1. Experimental Details
Before copper processing, AgInS2 thin films were first prepared at a glass substrate temperature of 420°C using an aqueous solution which contains silver acetate (AgCH3CO2), thiourea (SC (NH2)2), and indium chloride (InCl3) as precursors. The precursor’s concentrations are [Ag+]/[In3+] = 1.3 and [S2−]/[In3+] = 5. Molar ratios were prepared by mixing appropriate volumes of silver acetate 10−2 M., indium chloride 1.310−2 M., and thiourea 510−2 M. This protocol is considered as an optimal condition for preparing such a p-type compound [6–8]. The carrier gas was nitrogen (pressure ≈ 0.35 bar) through a 0.5 mm diameter nozzle. The nozzle-to-substrate plane distance was fixed at the optimal value of 27 cm as demonstrated earlier, for the same disposal, by Boubaker et al. [16]. During the whole deposition process, precursor mixture flow rate was approximately 4 mL/min. In a second step, AgInS2 sprayed thin films were annealed in a copper-rich sealed vacuum medium with different values of x = [Cu2+]/([Ag+]+[Cu2+]). The values of x have been calculated using molar concentration data which were obtained via absorbance measurements. The whole protocol is summarized in Figure 1.
Global synthesis protocol scheme.
2.2. Analyses and Structural Patterns
The XRD spectra of the obtained compounds show in addition to the principle peak (112) the presence of (204), (312), and (116) additional peaks corresponding to the tetragonal structure of AgInS2 with the presence of minor intensity peaks corresponding to AgInS2 orthorhombic phase (Figure 1). These results have been obtained in other works [5–12].
XRD analysis corresponding to CuxAg1−xInS2 alloys (Figure 2) exhibits a noticeable shift of (112) principle peak from 2θ position (27.08°), which is assigned to AgInS2 material, to the angle (28.09°) corresponding to CuInS2 solid compound. This proves the incorporation of copper in the AgInS2 tetragonal matrix by taking the silver place.
The XRD diagrams of CuxAg1−xInS2 at various x ratio (x = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0).
2.3. Additional Conjoint Analyses
To reinforce and explain this interesting trend of Cu ions behavior, some lattice calculations were carried out. First, average crystallite size D values are obtained (Figure 1) from the Scherrer formula,
(1)D=Kλβcosθ,
where k is a constant k=0.9. λ the length of wave λ=1. 5418 Å. β is the full width at half maximum and θ is the angle of the strongest peak. Figure 2 gathers the variations of crystallite size along with those of energy band gap of CuxAg1−xInS2 compounds with x ratio. The phenomenon of the decrease in the crystallite size (D<100 nm) for films having 0.2<x<0.4 can be explained by the low crystallization which is affected by the penetration of copper in the structure of AgInS2 compound to form the quaternaries CuxAg1−xInS2. The main event occurs when x is equal to unity and the CuInS2 is definitely implemented while crystallization is highly improved (D=196.95 nm). The parabolic fittings of both Eg and D versus x may explain the degradation of the structure when 0.2<x<0.6 and its enhancement for 0.6<x<1.0. If criteria of stability are reported to a high bandgap along with reduced crystallite sizes [17–19], an optimality zone can be identified (shaded zone in Figure 3) thanks to the established second order fittings. This zone ([0.40; 0.43]) is in good concordance with several recently published values but seems to be more accurate.
Conjoint variation of crystallite size D (nm) and energy band gap Eg of CuxAg1−xInS2 with x ratio.
2.4. Optical Study and Urbach Energy Analyses
The optical properties of the CuxAg1−xInS2 thin films were determined from transmission and reflexion spectra in the range of 300–1800 nm wavelength range. Measurements were guides for evaluating Urbach energy Eu for each sample. In order to understand Urbach tailing alteration following copper ions insertion in the host AgInS2 structures, Urbach energy Eu has been determined. This energy has been adopted as a reliable measure of the inhomogeneous disorder and atomic scale dispersion inside structures as it indicates the width of the band tails of the localized states in presence of defects. Figure 4 shows the low values of Eu corresponding to AgInS2 and CuInS2 compounds, which may be, among others (interstitials, antisites, vacancies, etc.), due to a minimum of distortion of the band gap energy. Yet when 0.4<x<0.5, the Urbach energy presented a maximum of distortion of the gap due to structure degradation and spin insatiability in the compound. These values are in good agreement with those reported in precedent sections concerning structural properties. They also confirm the nonlinearity of composition dependencies, as recorded, for similar compounds by Korzoun et al. [20].
Variations of Urbach energy Eu of CuxAg1−xInS2 with the x ratio.
3. Lattice Compatibility Theory (LCT) Analysis 3.1. Theoretical Fundaments
According to the Lattice Compatibility Theory [21–28] and the generalized Simha-Somcynsky theory [28–31], any host lattice can be considered as a succession of elementary molecules and holes. Each cell in the occupied fraction is either empty or contains the molecule van-der-Waals volume as well as an inherent free volume. The behavior of any doping or introduced element is based on its interaction with existing host edifices. Preludes to this theory have been established by Boubaker et al. [25, 26] in the context of analysing Urbach tailing controversial behaviour in some nanocompounds as well as I-III-O2 ternary oxides instability at low temperatures. It was also confirmed by Boubaker et al. [23, 24] on the bases of investigation on some copper-doped compounds. An original formulation of the Lattice Compatibility Theory [25, 26] has been established as follows:
“The stability of doping agents inside host structures is favorized by geometrical compatibility, expressed in terms of matching patterns between doping agent intrinsic lattice and those of the host.”
3.2. Evidence of Optimality Occurrence
In the actually discussed case (CuxAg1−xInS2 lattice), the nature of the highest occupied bands and the location of holes in both elemental copper and silver ions as well as CuInS2 and AgInS2 chalcopyrite lattice structures have been demonstrated to be determinant. In this context, fundamental geometrical observations concerning the structure of CuInS2 and AgInS2 ternary solid compounds (Figure 5) along with the host matrix were interpreted in terms of conventional lattice-linked parameters.
CuInS2, AgInS2, and CuxAg1−xInS2 lattices elementary configuration.
In this context, main lattice parameters of both CuInS2 and AgInS2 have been gathered in Figure 6, as extreme schemes (x=0 and x=1, resp.) for the x-dependent CuxAg1−xInS2. Stoichiometry-related evolution of cooper element incorporation inside the host matrix is equivalent to a gradual reduction of the first lattice parameter (a) along with a more amplified magnification of the third one (c). Under the presumption of a first-order linear x-dependent evolution, in concordance with Vergard’s law (in reference to difference in ionic radii between Ag and Cu, which prevents formation of solid solutions in the CuxAg1−xInS2 system), a critical point could be detected at approximately x=0.42 (Figure 6). This value is strongly supported by precedent analyses and studies about copper/silver substation kinetics and extents [23, 24, 27–35] ternary chalcopyrite structures.
CuInS2, AgInS2, and CuxAg1−xInS2 main lattice parameters x-dependent evolution scheme.
The Lattice Compatibility Theory (LCT) may give hence an explanation to the limit of incorporation of copper ions in the AgInS2 host matrix by taking silver’s place, as confirmed earlier by the recorded XRD peak shift (Section 2.2).
4. Conclusion
The structural properties of CuxAg1−xInS2 thin solid films, deposited on glass substrates by the spray pyrolysis technique from aqueous solutions using various ratios x = [Cu]/([Ag]+[Cu]) at 420°C as the substrate temperature, have been investigated. X-ray diffraction analysis confirms that all obtained solid films consist essentially of CuxAg1−xInS2 quaternary tetragonal chalcopyrite compounds with (112) strong peak. On the other hand, it was recorded that the physical properties have been influenced by the penetration of the copper in the structure that showed clearly a band gap energy Eg shift from 1.7 eV of AgInS2 to 1.51 eV of CuInS2. A confirmed and experimentally supported extent of the cooper-to-silver ratio has been established through structure alteration in the framework of the Lattice Compatibility Theory (LCT) along withSimha-Somcynsky principles.
Conflict of Interests
The authors declare that there is no conflict of interests regarding the publication of this paper.
MeeseJ. M.ManthuruthilJ. C.LockerD. R.CuInS2 diodes for solar-energy conversion197520696697BraungerD.HariskosD.WalterT.SchockH. W.An 11.4% efficient polycrystalline thin film solar cell based on CuInS2 with a Cd-free buffer layer19964029710210.1016/0927-0248(95)00069-02-s2.0-0030124530CiszekT. F.Melt growth and some properties of CuxAg1-xInSe2 and CuInyGa1-ySe2 chalcopyrite solid solution crystals1986791–368969410.1016/0022-0248(86)90538-52-s2.0-0000398143GuezmirN.OuerfelliJ.BelgacemS.Optical properties of sprayed CuInS2 thin layers200696111612310.1016/j.matchemphys.2005.06.0592-s2.0-28944436405GherouelD.GaiedI.BoubakerK.YacoubiN.AmloukM.Some physical investigations of AgInS2-xSex thin film compounds obtained from AgInS2 annealed in seleneide atmosphere201254519019910.1016/j.jallcom.2012.07.1482-s2.0-84866077969GherouelD.GaiedI.AmloukM.Effect of heat treatment in air on physical properties of AgInS2 sprayed thin films201356614715510.1016/j.jallcom.2013.02.1882-s2.0-84875962139AissaZ.Ben NasrallahT.AmloukM.BernèdeJ. C.BelgacemS.Some physical investigations on AgInS2 sprayed thin films2006907-81136114610.1016/j.solmat.2005.07.004AissaZ.AmloukM.Ben NasrallahT.BernèdeJ. C.BelgacemS.Effect of S/In concentration ratio on the physical properties of AgInS2-sprayed thin films200791648949410.1016/j.solmat.2006.10.022Ortega-LopezM.Morales-AcevedoA.Solorza-FeriaO.Physical properties of AgInS2 films prepared by chemical spray pyrolysis20013851-212012510.1016/S0040-6090(01)00758-12-s2.0-0043260013AguileraM. L.Ramírez-RosalesD.González-TrujilloM. A.Change from n-type to p-type conductivity on AgInS2 and AgInS2:Sn polycrystalline thin films prepared by spray pyrolysis technique200951772535253710.1016/j.tsf.2008.11.062Ortega LopezM.Vigil-GalanO.Cruz GandarillaF.SolorizaO.Preparation of AgInS2 chalcopyrite thin films by chemical spray pyrolysis2003381556110.1016/S0025-5408(02)00999-6AguileraM. L. A.HernándezJ. R.TrujilloM. A. G.LópezM. O.PuenteG. C.Photoluminescence studies of chalcopyrite and orthorhombic AgInS2 thin films deposited by spray pyrolysis technique2007515156272627510.1016/j.tsf.2006.12.106AkakiY.KuriharaS.ShirahamaM.TsurugidaK.SetoS.KakenoT.YoshinoK.Structural, electrical and optical properties of AgInS2 thin films grown by thermal evaporation method200566111858186110.1016/j.jpcs.2005.09.0052-s2.0-29144443693TadjarodiA.CheshmekhavarA. H.ImaniM.Preparation of AgInS2 nanoparticles by a facile microwave heating technique; Study of effective parameters, optical and photovoltaic characteristics201226344945610.1016/j.apsusc.2012.09.0802-s2.0-84869498130ZribiM.KanzariM.RezigB.Optical constants of Na-doped CuInS2 thin films20066019810310.1016/j.matlet.2005.08.0012-s2.0-27544469350BoubakerK.ChaouachiA.AmloukM.BouzouitaH.Enhancement of pyrolysis spray disposal performance using thermal time-response to precursor uniform deposition200737110510910.1051/epjap:20070052-s2.0-33847203263RabehM. B.KanzariM.Optical constants of Zn-doped CuInS2 thin films2011519217288729110.1016/j.tsf.2011.01.1392-s2.0-80052169341YakuphanogluF.CukurovaliA.YilmazI.Single-oscillator model and determination of optical constants of some optical thin film materials20043533-421021610.1016/j.physb.2004.09.0972-s2.0-10444229662ParkM. S.HanS. Y.BaeE. J.LeeT. J.ChangC. H.RyuS. O.Synthesis and characterization of polycrystalline CuInS2 thin films for solar cell devices at low temperature processing conditions2010103S379S38210.1016/j.cap.2010.02.0172-s2.0-77955513369KorzounB. V.BodnarI. V.YasyukevichL. V.Preparation and physical properties of AgxCu1-xS2 solid solutionsProceedings of the 11th Conference on Ternary and Multinary Compounds (ICTMC '97)September 1997Salford189192PetkovaP.BoubakerK.The Lattice Compatibility Theory (LCT): an attempt to explain Urbach tailing patterns in copper-doped bismuth sillenites (BSO) and germanates (BGO)201254617617910.1016/j.jallcom.2012.08.0862-s2.0-84866487059BelgacemS.BennaceurR.Propriétés optiques des couches minces de SnO2 et CuInS2 airless spray199025121245125810.1051/rphysap:0199000250120124500BoubakerK.Preludes to the Lattice Compatibility Theory LCT: urbach tailing controversial behavior in some nanocompounds20122012417319810.5402/2012/173198SimhaR.SomcynskyT.On the statistical thermodynamics of spherical and chain molecule fluids19692434235010.1021/ma60010a0052-s2.0-0001287841BoubakerK.The lattice compatibility theory: arguments for recorded I-III-O2 ternary oxide ceramics instability at low temperatures beside ternary telluride and sulphide ceramics20132013673401510.1155/2013/734015SimhaR.WilsonP. S.Thermal expansion of amorphous polymers at atmospheric pressure. II. Theoretical considerations19736690891410.1021/ma60036a023BoubakerK.AmloukM.LouartassiY.LabiadhH.About unexpected crystallization behaviors of some ternary oxide and sulfide ceramics within lattice compatibility theory LCT framework20134911151172-s2.0-84876566212PrigogineI.TrappeniersN.MathotV.1957Amsterdam, The NetherlandsNorth HollandPrigogineI.TrappeniersN.MathotV.Statistical thermodynamics of r-MERS and r-MER solutions1953159310710.1039/DF95315000932-s2.0-0002494403WilsonP. S.SimhaR.Thermal expansion of amorphous polymers at atmospheric pressure. I. Experimental19736690290810.1021/ma60036a022PrigogineI.1957Amsterdam, The NetherlandsNorth-HollandHirschfelderJ. O.CurtissC. F.BirdR. B.1954New York, NY, USAWileyParkJ.KimH.A new equation of state based on hole theory19981441-2778610.1016/S0378-3812(97)00246-X2-s2.0-0031995505AsadovY. G.AlyevY. I.BabaevA. G.Effect of selenium or tellurium substitution for half of the sulfur atoms in AgCuS on its structure and the temperatures of its polymorphic transformations200844433734410.1007/s10789-008-4003-12-s2.0-42249101219GraedelT. E.FraneyJ. P.GualtieriG. J.KammlottG. W.MalmD. L.On the mechanism of silver and copper sulfidation by atmospheric H2S and OCS198525121163118010.1016/0010-938X(85)90060-52-s2.0-0022392972