Advances in Optics

Volume 2014 (2014), Article ID 459065, 4 pages

http://dx.doi.org/10.1155/2014/459065

Research Article

Effects of Li⁺ Codoping on the Optical Properties of SrAl₂O₄ Long Afterglow Ceramic Phosphors

Timur Sh. Atabaev,¹ Hong Ha Thi Vu,¹ Mac Kim,² Yong Suk Yang,² Hyung-Kook Kim,¹ and Yoon-Hwae Hwang¹

¹Department of Nanomaterials Engineering, Pusan National University, Miryang 627-706, Republic of Korea

²Department of Nano Fusion Technology, Pusan National University, Busan 609-735, Republic of Korea

Received 1 April 2014; Accepted 15 July 2014; Published 4 August 2014

Academic Editor: Marco Consales

Copyright © 2014 Timur Sh. Atabaev et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

Rare-earths codoped long afterglow strontium aluminate phosphors with high brightness were synthesized via a facile combustion synthesis method using urea as a fuel. The resulted phosphor particles were analyzed by using X-ray diffraction and field emission scanning electron microscope, whereas their optical properties were monitored by photoluminescence spectroscopy. The prepared SrAl₂O₄:Eu²⁺, Dy³⁺, Li⁺ samples showed a broad green-yellowish emission, peaking at 512 nm when excited by 348 nm. Compared to traditional SrAl₂O₄:Eu²⁺, Dy³⁺ phosphor, the initial luminescence brightness of SrAl₂O₄:Eu²⁺, Dy³⁺, codoped with Li⁺ improved from 1.89 cd/m² to 2.71 cd/m² and the afterglow decay time was prolonged from 103 to 121 min. The possible mechanism of SrAl₂O₄:Eu²⁺, Dy³⁺, Li⁺ phosphorescence enhancement has been discussed.

1. Introduction

Long afterglow phosphor is a kind of energy-storing material, which can absorb the light photons, store the energy, and then release the energy as visible light. Alkaline aluminates based phosphor materials generally generate more defect-related traps when they are doped with rare-earths RE. The luminescence emission of these RE-doped alkaline aluminates is strongly dependent on the host lattice and can occur from the ultraviolet to the red region. For example, CaAl₄O₇:Eu²⁺, Dy³⁺ phosphors exhibited a broad blue emission band with the main peak at 445 nm [1]. The emission colour of MgAl₄O₇:Eu²⁺, Dy³⁺ nanoparticles shifts from bluish (700°C) to reddish (900°C) with increasing calcination temperature [2]. Recently, strontium aluminates activated with rare-earths have attracted a lot of attention since they exhibit excellent properties such as long afterglow time, high quantum efficiency, good phase stability, and bright emitting color [3], when compared with known sulfide long afterglow phosphors. Since the lifetime greatly exceeds that of any other material, this offers an unexpectedly large field of applications for the use of these aluminates [4, 5].

Although many studies have examined the optical properties of RE-doped alkaline aluminates, only a few have investigated the codoping of three or more different ions in the same host material. It is also known that optical properties of phosphorescent materials are strongly influenced by the incorporation of auxiliary activators. Among them, smaller cationic radius of Li⁺ ions are favored for their movement and site occupation in the host matrix and these advantages make them attractive for tailoring the crystal field of host lattice [6]. There are many reports on significant enhancement in emission intensity with Li⁺ codoping in different hosts [7, 8]. To the best of our knowledge, there is no report on improvement of green phosphorescence with Li⁺ ion incorporation in SrAl₂O₄:Eu²⁺, Dy³⁺ phosphors.

Herein, we report the synthesis of Li⁺-tailored SrAl₂O₄:Eu²⁺, Dy³⁺ prepared by combustion method, which shows better luminescent properties than the bare SrAl₂O₄:Eu²⁺, Dy³⁺ phosphor. The optimal synthesis conditions were researched systematically. The optical characteristics were investigated by analyzing the normalized room-temperature emission spectra. Codoping Li⁺ into SrAl₂O₄:Eu²⁺, Dy³⁺ could enhance the emission intensity of SrAl₂O₄:Eu²⁺, Dy³⁺, and the emission intensity of SrAl₂O₄:Eu²⁺, Dy³⁺ varied with the Li⁺ concentration. Thus, the present study was set up to investigate the influence of Li⁺ concentration on the emission spectra and discuss the mechanism of the enhanced phosphorescence.

2. Experimental

2.1. Fabrication

High purity Sr(NO₃)₂, Al(NO₃)₃9H₂O, Eu(NO₃)₃5H₂O, Dy(NO₃)₃5H₂O, LiNO₃, and CO(NH₂)₂ were purchased from Sigma-Aldrich and used as received. In a typical synthesis method, Sr(NO₃)₂, Al(NO₃)₃9H₂O, Eu(NO₃)₃5H₂O, Dy(NO₃)₃5H₂O, and LiNO₃ were dissolved in a minimum amount of deionized DI water at a molar ratio of 1 : 2 : 0.03 : 0.03 : X , respectively. Second, 5 g of urea was added to each sample. After mixing, the samples were introduced into a muffle furnace and then heated to about 300°C for 1 h, where the organic fuels and metal nitrates were automatically ignited and reacted to burn. Finally, the samples were precalcinated at 800°C in air atmosphere for 2 h to remove residual carbon and subsequently calcined at 1200°C under Torr vacuum for 3 h.

2.2. Characterization

The structure of the prepared powders was examined by XRD using a Bruker D8 discover diffractometer (Bruker Optics Inc., MA, USA) with Cu Kα radiation ( nm) and a 2θ scan range of 20 to 60°. The morphologies of the particles were characterized by FESEM (Hitachi S-4700, Hitachi, Ltd., Tokyo, Japan). Elemental analysis was carried out by energy dispersive X-ray spectroscopy (EDX, Horiba. 6853-H). The PL measurements were measured by placing the powders to standard powder holder on a Hitachi F-7000 (Hitachi, Ltd., Tokyo, Japan) spectrophotometer equipped with a 150-W xenon lamp as an excitation source. All the measurements were performed at room temperature.

3. Results and Discussion

FESEM study was carried out to investigate the surface morphology and the crystallite sizes of the synthesized powders. Figure 1(a) shows the representative FESEM image of the bare SrAl₂O₄:Eu²⁺, Dy³⁺ powder. From the FESEM image, it is apparent that the crystallite sizes of the bare SrAl₂O₄:Eu²⁺, Dy³⁺ powder vary from nanometer range to several tens of microns. It was observed that the crystallite sizes are nearly the same for all compositions prepared (not shown for other samples). The EDX analysis of SrAl₂O₄:Eu²⁺, Dy³⁺ powder confirmed the presence of europium and dysprosium elements in the SrAl₂O₄ host matrix as shown in Figure 1(b).

(a)

(b)

Figure 1: FESEM micrographs (a) and EDX spectra (b) of SrAl₂O₄:Eu²⁺, Dy³⁺ powder.

All the samples were further examined by PL at room temperature under 348 nm excitation to examine the effects of Li⁺ concentration on the phosphorescent properties of the synthesized samples. Figure 2 shows the normalized PL excitation and emission spectra of the samples measured in the range of 200–700 nm. PL excitation spectra of SrAl₂O₄:Eu²⁺, Dy³⁺ codoped with 0.03 mol% of Li⁺ (black line) shows a strong broad absorption with a maximum at 348 nm (4f⁷(⁸S7/2) → 4f⁶5d transition) in the ultraviolet UV region. All the samples emit green-yellowish light with a very broad band centered at 512 nm when they were excited by the 348 nm UV light, which can be identified as the 4f⁶5d¹ → 4f⁷ electric dipole–allowed transition of Eu²⁺ [3]. The shapes and position of the bands remain the same irrespective to the Li⁺ content, whereas the intensity varies with Li⁺ concentration. The normalized emission intensity of the samples linearly increases with increased Li⁺ content and reached a maximum when the concentration was 0.03 mol% and then decreased at higher concentrations.

Figure 2: Normalized PL excitation and emission spectra of the samples as a function of Li⁺ content.

Owing to its small size, Li⁺ ions, when codoped into SrAl₂O₄:Eu²⁺, Dy³⁺, can diffuse to various interstitial sites in the host lattice. Thus the banned transitions can become allowed for Li⁺-tailored phosphors, since the inversion symmetry can be easily destroyed by the interstitial Li⁺ ions in the host matrix [9]. Therefore, the distortion of the local symmetry in the host matrix favors to enhanced phosphorescent emission. However, the enhanced phosphorescent emission can be also associated with a better crystallinity of the final composites, leading to fewer defects and a stronger emission [10]. Figure 3 shows the typical XRD patterns of the bare SrAl₂O₄:Eu²⁺, Dy³⁺ (without Li⁺) and SrAl₂O₄:Eu²⁺, Dy³⁺, Li⁺ (codoped with 0.03 mol%, optimum codoping concentration) samples. Both samples exhibited identical diffraction patterns, which can be indexed to the spinel structure of SrAl₂O₄ (JCPDS No. 34-379). Obviously, the XRD peaks of the SrAl₂O₄:Eu²⁺, Dy³⁺, Li⁺ were sharper and stronger than those of bare SrAl₂O₄:Eu²⁺, Dy³⁺ (without Li⁺), suggesting their better crystallinity. The calculated mean crystallite sizes of the samples (based on Debye-Scherrer’s equation) were equal to  nm and  nm for bare SrAl₂O₄:Eu²⁺, Dy³⁺ (without Li⁺) and SrAl₂O₄:Eu²⁺, Dy³⁺, Li⁺ powders, respectively. This shows that the crystallinity of the SrAl₂O₄:Eu²⁺, Dy³⁺, Li⁺ was improved with the addition of Li⁺ ions. Therefore, the incorporation of Li⁺ ions does not alter the emission peak positions but improves the emission intensity thanks to the improved crystallinity and distortion of the local symmetry in the host matrix.

Figure 3: Typical XRD patterns of the bare SrAl₂O₄:Eu²⁺, Dy³⁺ and SrAl₂O₄:Eu²⁺, Dy³⁺/0.03 mol% Li⁺.

Figure 4 shows comparative decay curves of the bare SrAl₂O₄:Eu²⁺, Dy³⁺ and SrAl₂O₄:Eu²⁺, Dy³⁺/0.03 mol% Li⁺. The results indicate that the decay process of the two kinds of phosphors contains both rapid and slow decay processes. It is clear from the figure that SrAl₂O₄:Eu²⁺, Dy³⁺/3 mol% Li⁺ sample displays a higher intensity and longer afterglow time than the bare SrAl₂O₄:Eu²⁺, Dy³⁺; the initial luminescence brightness was improved from 1.89 candela cd/m² to 2.71 cd/m² and the long afterglow time was prolonged from 103 to 121 min. Thus, the introduction of Li⁺ enhances the initial brightness and extends the afterglow time in SrAl₂O₄:Eu²⁺, Dy³⁺. The addition of Li⁺ probably increases the number of oxygen vacancies, which might act as a sensitizer for the energy transfer to rare-earth ions due to the strong mixing of charge transfer states resulting in the highly enhanced emission intensity [10]. However, the phosphorescence quenching also occurs at higher doping content of Li⁺ due to the excess oxygen vacancies at the host, which destroy the crystallinity of the host material [11].

Figure 4: Decay curves of the bare SrAl₂O₄:Eu²⁺, Dy³⁺ and SrAl₂O₄:Eu²⁺, Dy³⁺/0.03 mol% Li⁺ powders. Inset is digital photography of excited phosphorescent SrAl₂O₄:Eu²⁺, Dy³⁺/0.03 mol% Li+ powder.

4. Conclusions

In conclusion, Li⁺-modified SrAl₂O₄:Eu²⁺, Dy³⁺ ceramic powders were fabricated by combustion synthesis method. The crystal structure and morphology of the synthesized powders were characterized by XRD, FESEM, and EDX. The PL spectroscopy was used to examine the phosphorescent properties of synthesized powders. The Li⁺ concentration dependence on the phosphorescent properties of those powders was also examined. The enhancement of emission intensity was attributed with a distortion of the local crystal field in the host matrix combined with a better crystallinity effect of final powder composites. The initial brightness and afterglow properties of Li⁺-modified SrAl₂O₄:Eu²⁺, Dy³⁺ ceramic powders were enhanced by the introduction of Li⁺ into the SrAl₂O₄:Eu²⁺, Dy³⁺ matrix.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of  this paper.

Acknowledgment

This work was supported by the National Research Foundation of Korea (Grant no. 2012R1A1B3001357).

References

A. N. Yerpude and S. J. Dhoble, “Combustion synthesis of blue-emitting submicron CaAl₄O₇:Eu²⁺, Dy³⁺ persistence phosphor,” Luminescence, vol. 27, no. 6, pp. 450–454, 2012.

A. S. Maia, R. Stefani, C. A. Kodaira, M. C. F. C. Felinto, E. E. S. Teotonio, and H. F. Brito, “Luminescent nanoparticles of MgAl₂O₄:Eu, Dy prepared by citrate sol-gel method,” Optical Materials, vol. 31, no. 2, pp. 440–444, 2008.

B. Cheng, Z. Znang, Z. Han, Y. Xiao, and S. Lei, “SrAl₂O₄:Eu²⁺,Dy³⁺ nanobelts: synthesis by combustion and properties of long-persistent phosphorescence,” Journal of Materials Research, vol. 26, pp. 2311–2315, 2011.

G. Blasse and B. C. Grabmaier, Luminescent Materials, Springer, Berlin, Germany, 1994.

W. He, T. S. Atabaev, H. K. Kim, and Y. H. Hwang, “Enhanced sunlight harvesting of dye-sensitized solar cells assisted with long persistent phosphor materials,” The Journal of Physical Chemistry C, vol. 117, no. 35, pp. 17894–17900, 2013.

T. S. Atabaev, Z. Piao, Y. H. Hwang, H. K. Kim, and N. H. Hong, “Bifunctional Gd₂O₃:Er³⁺ particles with enhanced visible upconversion luminescence,” Journal of Alloys and Compounds, vol. 572, pp. 113–117, 2013.

S. H. Shin, J. H. Kang, D. Y. Jeon, and D. S. Zang, “Enhancement of cathodoluminescence intensities of Y₂O₃:Eu and Gd₂O₃:Eu phosphors by incorporation of Li ions,” Journal of Luminescence, vol. 114, no. 3-4, pp. 275–280, 2005.

G. Rajan and K. G. Gopchandran, “Effect of substrates on the photoemission properties of Li doped Gd₂O₃:Eu³⁺ nanocrystalline films,” Optical Materials, vol. 33, no. 3, pp. 494–500, 2011.

T. S. Atabaev, H. H. T. Vu, Z. Piao, Y. H. Hwang, and H. K. Kim, “Tailoring the luminescent properties of Gd₂O₃:Tb³⁺ phosphor particles by codoping with Al³⁺ ions,” Journal of Alloys and Compounds, vol. 541, pp. 263–268, 2012.

Q. Du, G. Zhou, J. Zhou, X. Jia, and H. Zhou, “Enhanced luminescence of novel Y₂Zr₂O ₇:Dy³⁺ phosphors by Li⁺ co-doping,” Journal of Alloys and Compounds, vol. 552, pp. 152–156, 2013.

L. Li, H. K. Yang, B. K. Moon, et al., “Photoluminescence properties of CeO₂:Eu³⁺ nanoparticles synthesized by a sol-gel method,” The Journal of Physical Chemistry C, vol. 113, pp. 610–617, 2009.