We have investigated the bulk modulus and thermal properties of La1-xSmxCoO3 (0≤x≤0.2) at temperatures 1 K≤T≤300 K probably for the first time by incorporating the effect of lattice distortions using the modified rigid ion model (MRIM). The calculated specific heat, thermal expansion, bulk modulus, and other thermal properties reproduce well with the available experimental data, implying that MRIM represents properly the nature of the pure and doped cobaltate. The specific heats are found to increase with temperature and decrease with concentration (x) for the present. The increase in Debye temperature (θD) indicates an anomalous softening of the lattice specific heat because increase in T3-term in the specific heat occurs with the decrease of concentration (x).
1. Introduction
Cobaltites of rare-earth elements with the chemical formula LnCoO3 are important agile and multifunctional materials, which are very promising for high temperature oxygen separation membranes and cathodes in solid oxide fuel cells (SOFCs), heterogeneous catalysts, and gas sensors [1, 2]. The LaCoO3 ceramic is at present the best studied representative of the rare-earth cobaltite family. LaCoO3 exhibits two spin state transitions as the temperature increases. The first transition is from low temperature low spin (LS) to intermediate spin (IS) state near 100 K characterized by a steep jump of magnetization at the transition [3–5] and the second one is from IS to high spin (HS) state leading to an insulator-metal (I-M) transition around 500 K [3, 5]. Throughout the ACoO3 series, only LaCoO3 has been analyzed with rhombohedral symmetry [6]; the rest of the members of the family with the ionic radius of the rare-earth smaller than the ionic radius of La exhibit an orthorhombic crystallographic structure [7]. A structural transition from rhombohedral (R3-C) to orthorhombic (Pbnm) symmetry with Sm doping level x>0.08 is found from the X-ray diffraction data in La1-xSmxCoO3 [8].
Recently, we have applied the modified rigid ion model (MRIM) to study the specific heat of cobaltates and manganites [9, 10]. Motivated from the applicability and versatility of MRIM, we have applied MRIM to investigate the temperature dependence of the specific heat, thermal expansion, and elastic and thermal properties of La1-xSmxCoO3 (0 ≤ x ≤ 0.2). It is found that the model is successful in describing temperature dependent (1 K < T < 300 K) specific heat (C), cohesive energy (ϕ), molecular force constant (f), Reststrahlen frequency (υ), Debye temperature (θD), and Gruneisen parameter (γ) of La1-xSmxCoO3 (0 ≤ x ≤ 0.2). The various properties in La1-xSmxCoO3 (0 ≤ x ≤ 0.2) are affected by the exchange of the A ions due to their different ionic radii. The paper is organized in the following way.
The computational details of model formalism are given in Section 2. In Section 3, we discuss the elastic and thermal properties of La1-xSmxCoO3 (0 ≤ x ≤ 0.2). The calculated results are compared with the available experimental results in the same section. Finally, in Section 4, the findings of the present study are concluded.
2. Formalism of MRIM
The effective interionic potential corresponding to the modified rigid ion model (MRIM) frame work is expressed as [9, 10]
(1)ϕ(r)=-e22∑kk′ZkZk′rkk′-1-∑kk′Ckk′rkk′-6+[βk′k′exp{(2rk′-rk′k′)ρi}]nibiβkk′exp{(rk+rk′-rkk′)ρi}+ni′2bi×[βkkexp{(2rk-rkk)ρi}+βk′k′exp{(2rk′-rk′k′)ρi}]].
Here, first term is attractive long range (LR) coulomb interactions energy. The second term represents the contributions of van der Waals (vdW) attraction for the dipole-dipole interaction and is determined by using the Slater-Kirkwood Variational (SKV) method [11]. The third term is short range (SR) overlap repulsive energy represented by the Hafemeister-Flygare-type (HF) interaction extended up to the second neighbour. In (1), rkk′ represents separation between the nearest neighbours, while rkk and rk′k′ appearing in the next terms are the second neighbour separation. rk (rk′) is the ionic radii of k (k′) ion. n (n′) is the number of nearest (next nearest neighbour) ions. The summation is performed over all the kk′ ions. bi and ρi are the hardness and range parameters for the ith cation-anion pair (i=1,2), respectively, and βkk′ is the Pauling coefficient [12] expressed as
(2)βkk′=1+(ZkNk)+(Zk′Nk′)
with Zk (Zk′) and Nk (Nk′) as the valence and number of electrons in the outermost orbit of k (k′) ions, respectively. The model parameters (hardness and range) are determined from the equilibrium condition
(3)[dϕ(r)dr]r=r0=0
and the bulk modulus
(4)B=19Kr0[d2ϕ(r)dr2]r=r0.
The symbol K is the crystal structure constant, r0 is the equilibrium nearest neighbor distance of the basic perovskite cell, and B is the bulk modulus. The cohesive energy for La1-xSmxCoO3 (0≤x≤0.2) is calculated using (1) and other thermal properties such as the Debye temperature (θD), Reststrahlen frequency (υ), molecular force constant (f), Gruneisen parameter (γ), specific heat (C), and thermal expansion (α) are computed using the expressions given in [9, 10]. The results are thus obtained and discussed below.
3. Results and Discussion3.1. Model Parameters
The values of input data like unit cell parameters and interionic distances for Sm doped LaCoO3 are taken from [8], for the evaluation of model parameters (b1, ρ1) and (b2, ρ2) corresponding to the ion pairs Co3+-O2− and La3+/Sm3+-O2. The values of model parameters (b1, b2, ρ1 and ρ2) are listed in Table 1. The tolerance factor t(t=(rA+rO)/2(rB+rO)) for these compounds is reported in Table 1, which satisfies the condition that t for a stable perovskite phase is above 0.84 [16]. Depending on the composition of the perovskite, critical radius (rcr) can be calculated by using (5) (Table 1) which describes the maximum size of the mobile ion to pass through. Consider(5)rcr=a0((3/4)a0-2rB)+rB2-rA22(rA-rB)+2a0,
where rA and rB are the radius of the A ion and B ion, respectively, and a0 corresponds to the lattice parameter (V1/3). The condition that critical radius does not exceed 1.05 Å [17] for typical perovskite material is satisfied in our compounds. The values of ionic radii and atomic compressibility for La3+, Sm3+, Co3+, and O2− are taken from [18, 19]. We defined the variance of the La/Sm ionic radii as a function of x, σ2=∑(xiri2-rA2). Here, xi, ri, and rA are the fractional occupancies, the effective ionic radii of cation of La and Sm, and the averaged ionic radius (rA=(1-x)rR3++xrA3+), respectively. The effect of ionic radii on tolerance factor and A-site variance is shown in Figure 1. In La1-xSmxCoO3, the A-site cation radius reduces with decrease in x, and the buckling of Co-O-Co angle progressively increases with x, which leads to increased distortions of the lattice. Here, we have computed the bulk modulus (B) on the basis of Atoms in Molecules (AIM) theory [20] which emphasizes the partitioning of static thermophysical properties in condensed systems into atomic or group distributions. The computed values of bulk modulus for La1-xSmxCoO3 (0.02≤x≤0.2) are in good agreement with value predicted by Cornelius et al. [13].
Values of average cation radius at A-site, tolerance factor, critical radius, and model parameters of La1-xSmxCoO3 (0.0 ≤ x ≤ 0.2).
Compound
rA (Å)
Tolerance factor (t)
rcr(Å)
Model parameters
(A-site)
b1 × 10−19(J)
ρ1(Å)
b2 × 10−19(J)
ρ2(Å)
LaCoO3
1.360
0.9958
0.9148
1.662
1.114
0.225
0.404
La0.98Sm0.02CoO3
1.357
0.9953
0.9159
1.636
1.105
0.222
0.399
La0.96Sm0.04CoO3
1.355
0.9947
0.9164
1.605
1.095
0.219
0.394
La0.94Sm0.06CoO3
1.352
0.9941
0.9168
1.596
1.093
0.218
0.392
La0.92Sm0.08CoO3
1.350
0.9936
0.9168
1.551
1.071
0.213
0.383
La0.88Sm0.12CoO3
1.205
0.9420
1.0102
1.317
1.757
0.197
0.364
La0.84Sm0.16CoO3
1.202
0.9413
1.0143
1.288
1.751
0.192
0.355
La0.80Sm0.20CoO3
1.199
0.9407
1.0169
1.269
1.751
0.190
0.351
The variation of bulk modulus, size mismatch, tolerance factor, and A-site variance of La1-xSmxCoO3 (0.0≤x≤2.0) with the radius of A-site cation.
3.2. Cohesive Energy
The cohesive energy (ϕ) is a measure of the strength of forces that bind atoms together in the solid states and is descriptive in studying the phase stability. The cohesive energy of Sm doped LaCoO3 is computed using (1) and is reported in Table 2. The negative value of the ϕ indicates that these compounds are stable at ambient temperature. The calculated cohesive energy of La1-xSmxCoO3 is quite comparable with the reported value of the lattice energy for SmCoO3, −144.54 eV [14]. The variation of the cohesive energy (ϕ) of La1-xSmxCoO3 (0≤x≤0.2) as a function of A-site ionic radius is displayed Figure 2. Further, to ascertain the validity of the MRIM, we have used the generalized Kapustinskii equation [21]. The lattice energy obtained using the Kapustinskii equation is close to the MRIM. According to generalized Kapustinskii equation, the lattice energies of crystals with multiple ions are given as
(6)U/KJ mol-1=-1213.9〈r〉(1-ρ〈r〉)∑nkzk2,
where 〈r〉 = weighted mean cation-anion radius sum and ρ is the average value of model parameters ρ1 and ρ2.
Values of bulk modulus, cohesive and thermal properties of La1-xSmxCoO3 (0.0 ≤ x ≤ 0.2).
Compound
BT (GPa)
Cohesive property
Thermal property
ϕ (eV) MRIM
ϕ (eV) Kapustinskii Eqn.
f (N/m)
υ
(THz)
θD (K)
γ
LaCoO3
180.6
−148.5
−147.5
35.20
9.40
451.9
3.08
La0.98Sm0.02CoO3
184.2
−148.8
−147.9
35.87
9.49
456.0
3.12
La0.96Sm0.04CoO3
187.8
−149.2
−148.2
36.56
9.57
460.2
3.15
La0.94Sm0.06CoO3
189.5
−149.4
−148.4
36.85
9.61
461.9
3.17
La0.92Sm0.08CoO3
195.9
−150.0
−148.9
38.05
9.76
469.1
3.23
La0.88Sm0.12CoO3
211.1
−151.4
−150.5
41.23
10.2
487.9
3.40
La0.84Sm0.16CoO3
217.5
−151.7
−151.1
42.50
10.3
495.1
3.47
La0.80Sm0.20CoO3
221.3
−152.1
−151.5
43.25
10.4
499.1
3.52
Others
180a
−144.54b
480c
areference [13], breference [14], and creference [15].
Variation of cohesive energy with radius of A-site cation for La1-xSmxCoO3 (0.0≤x≤2.0).
3.3. Thermal Properties
We have also predicted the molecular force constant (f), Reststrahlen frequency (υ), and Gruneisen parameter (γ) for Sm doped LaCoO3 (Table 2). In the Debye approach, we consider the vibrations of the collective positive ion lattice with respect to the negative ion lattice. The frequency of vibration obtained by this model is also reported here as Reststrahlen frequency. This is clear from Table 2 that as the Sm doping increases the Reststrahlen frequency increases. The Debye temperature estimated for the analysis of specific heat is also reported in Table 2. Our calculated values of Debye temperature for La1-xSmxCoO3 (0.02≤x≤0.2) are close to reported value of LaCoO3 which is 480 K [15]. Since the ionic radius of Sm is larger than that of La, the bulk modulus and other thermal properties systematically increase with increasing x (Table 2). We have displayed the variation of the Debye temperature (θD) of Sm doped LaCoO3 as a function of molar volume in Figure 3 and the θD is observed to be increasing with increasing basic perovskite molar cell volume.
Variation of Debye temperature (θD) for La1-xSmxCoO3 (0.0≤x≤2.0) with molar volume (cm3) of the basic perovskite cell.
3.4. Specific Heat and Thermal Expansion
The specific heat in the normal state of the material is usually approximated by the contribution of the lattice specific heat. The temperature dependence (10 K ≤ T ≤ 300 K) of specific heat for La1-xSmxCoO3 (0≤x≤0.2) is computed as displayed in Figure 4. We find that when the temperature is below 300 K the specific heat (Figure 4) is strongly dependent on temperature which is due to the anharmonic approximation. However, at higher temperatures, the anharmonic effect on C is suppressed, and C is almost constant at high temperature. The computed results on specific heat for LaCoO3 compared with the experimental work of Tsubouchi et al. [22] in temperature range (10 K ≤ T ≤ 300 K) are displayed in the inset of Figure 4. The calculated dependence of C on temperature does not show any anomalous behavior and is in good agreement with the other experimental data [22].
The variation of calculated specific heat of La1-xSmxCoO3 (0.0≤x≤0.2) as a function of temperature (10 ≤ T ≤ 300 K). The curves of higher cation doping are shifted upward by 10 J each from the preceding curve for clarity. Inset shows the specific heat of LaCoO3 in the temperature interval (10 K ≤ T ≤ 300 K) and its comparison with the experimental values [22]. The solid line (—) and open square (□) represent the model calculation and experimental curve, respectively.
Encouraged by the specific heat results, we tried to compute the thermal expansion coefficient (α) as a function of temperature using the well-known relation, α=γC/BTV, where BT, V, and C are the isothermal bulk modulus, unit formula volume, and specific heat at constant volume, respectively, and γ is the Gruneisen parameter. It is important to note that in Figure 5 (for 10 K) that thermal expansion shows a significant decrease due to the doping of Sm in LaCoO3. Our results on volume thermal expansion coefficients will certainly serve as a guide to experimental workers in future.
The variation of thermal expansion (α) with composition (x) in La1-xSmxCoO3 (0.0 ≤ x ≤ 0.2) at 10 K.
4. Conclusion
On the basis of an overall discussion, it may be concluded that the description of the thermodynamic properties of Sm doped LaCoO3 given by us is remarkable in view of the inherent simplicity and less parametric nature of the modified rigid ion model (MRIM). Our results are probably the first reports of specific heat and thermal expansion at these temperatures for La1-xSmxCoO3 (0.02≤x≤0.2). To the best of our knowledge, the values on bulk modulus, cohesive and lattice thermal properties for La1-xSmxCoO3 (0.0≤x≤0.2) have not yet been measured or calculated, hence our results can serve as a prediction for future investigations.
Conflict of Interests
The authors declare that there is no conflict of interests regarding the publication of this paper.
Acknowledgment
The authors are thankful to the University Grant Commission (UGC), New Delhi, for providing the financial support.
InagakiT.MiuraK.YoshidaH.MaricR.OharaS.ZhangX.MukaiK.FukuiT.High-performance electrodes for reduced temperature solid oxide fuel cells with doped lanthanum gallate electrolyte: II. La(Sr)CoO3 cathode2000861-234735110.1016/S0378-7753(99)00431-0ChenC. H.BouwmeesterH. J. M.Van DoomR. H. E.KruidhofH.BurggraafA. J.Oxygen permeation of La0.3Sr0.7CoO3-δ1997981-271310.1016/S0167-2738(97)00097-02-s2.0-0031169370YamaguchiS.OkimotoY.TaniguchiH.TokuraY.Spin-state transition and high-spin polarons in LaCoO31996536R2926R292910.1103/PhysRevB.53.R29262-s2.0-0000873068KobayashiY.FujiwaraN.MurataS.AsaiK.YasuokaH.Nuclear-spin relaxation of 59Co correlated with the spin-state transitions in LaCoO3200062141041410.1103/PhysRevB.62.4102-s2.0-0001470163Señarís-RodríguezM.GoodenoughJ.LaCoO3 revisited19951162224231RadaelliP. G.CheongS. W.Structural phenomena associated with the spin-state transition in LaCoO320026609440810.1103/PhysRevB.66.094408AlonsoJ. A.Martínez-LopeM. J.de La CalleC.PomjakushinV.Preparation and structural study from neutron diffraction data of RCoO3 (R = Pr, Tb, Dy, Ho, Er, Tm, Yb, Lu) perovskites2006161555156010.1039/b515607f2-s2.0-33744465782SunJ. R.LiR. W.ShenB. G.Spin-state transition in La1-xSmxCoO3 perovskites2001891331ThakurR.ThakurR. K.GaurN. K.Thermophysical properties of Pr1-xCaxCoO32012550535810.1016/j.tca.2012.09.025ThakurR. K.SamathamS.KauravN.GanesanV.GaurN. K.OkramG. S.Dielectric, magnetic, and thermodynamic properties of Y1-xSrxMnO3 (x = 0.1 and 0.2)20121121010411510.1063/1.47667512-s2.0-84870669534SlaterJ. C.KirkwoodJ. G.The van der waals forces in gases193137668269710.1103/PhysRev.37.6822-s2.0-36149017081PaulingL.1945Ithaca, NY, USACornell University PressCorneliusA. L.KletzS.SchillingJ. S.Simple model for estimating the anisotropic compressibility of high temperature superconductors19921973-420922310.1016/0921-4534(92)90004-VFarhanM. A.AkhtarM. J.Negative pressure driven phase transformation in Sr doped SmCoO3201022707540210.1088/0953-8984/22/7/075402HeC.ZhengH.MitchellJ. F.FooM. L.CavaR. J.LeightonC.Low temperature Schottky anomalies in the specific heat of LaCoO3: defect-stabilized finite spin states2009941010251410.1063/1.3098374FangC.-M.AhujaR.Structures and stability of ABO3 orthorhombic perovskites at the Earth's mantle conditions from first-principles theory20061571-21710.1016/j.pepi.2006.02.007MogensenM.LybyeD.BonanosN.HendriksenP. V.PoulsenF. W.Factors controlling the oxide ion conductivity of fluorite and perovskite structured oxides20041741–427928610.1016/j.ssi.2004.07.0362-s2.0-10044238931ShannonR. D.Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides19763275176710.1107/S0567739476001551KittelC.19765thNew York, NY, USAWileyPendásA. M.CostalesA.BlancoM. A.RecioJ. M.LuañaV.Local compressibilities in crystals2000621397010.1103/PhysRevB.62.13970GlasserL.Lattice energies of crystals with multiple ions: a generalized Kapustinskii equation199534204935493610.1021/ic00124a003TsubouchiS.KyomenT.ItohM.OguniM.Kinetics of the multiferroic switching in MnWO4200469144406