Journal of Textiles
Volume 2015 (2015), Article ID 989807, 10 pages
http://dx.doi.org/10.1155/2015/989807

Research Article

Evaluation of Combined Effect of Mercerized and Dyed Yarns on Physical Properties of Plain Single Jersey Knitted Fabrics

S. M. Elrys, A. El-Hossini, and A. M. EL-Hadidy

Mansoura University, Faculty of Engineering, Textile Department, Mansoura, Egypt

Received 5 August 2015; Accepted 18 November 2015

Academic Editor: Hu Hong

Copyright © 2015 S. M. Elrys et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

A combined effect of mercerized and dyed yarns on physical properties of plain single jersey knitted fabrics has been studied. Plied cotton yarn was produced and mercerized at different NaOH concentrations and temperatures. Then, this yarn was bleached and dyed with two types of dyes, vat dyeing and reactive dyeing. Each of mechanical and color properties were measured to these treated yarns. Plain single jersey knitted fabrics were produced from these treated yarns. The total evaluation of the properties for plain single jersey fabrics was measured by using radar chart method. It was found that the highest area of radar chart, which represents the total physical properties, is achieved at 32°Be′, in case of vat dyeing. Besides, analysis of variance (AVOVA) and MANOVA were applied to illustrate which of the properties would be affected by NaOH con. and types of dyeing for yarns and fabrics.

1. Introduction

The quality of end products like fabrics depends on the quality of their components like yarns. Textile finishing processes are usually used to improve the quality of materials. Among these, mercerization is one of the most important wet finishing processes of cotton materials, as it improves handling and appearance of cotton fibers to simulate the superior properties of synthetic fibers. In addition, Mercerization treatment improves dye ability and luster required for appearance, smoothness and strength required for ability of processing such as sewing threads.

These properties are the most important ones needed to materials for competition with other products.

There are many methods of mercerization where it can be applied to yarns or fabrics. Depending on tension, it can be done in the slack state or under tension state. Depending on temperature, it can be done under high temperatures which is called hot mercerization or under normal temperatures which is called normal mercerization. Also, it can be applied in hank, cheese, and single-end mercerization.

However, all of these methods of mercerization are applied by treating the materials with caustic soda solution at a certain concentration and temperature depending on the type of applied method. Each of these methods has its merits and demerits. The extent of changes that occur depends on the processing time, caustic concentration, temperature, and degree of polymerization, source of cellulose, the physical state of the cellulose, slack or tension treatment, and the degree of tension [1].

Dyeing is another wet process that influences yarn and fabric properties. Cotton and other cellulosic fibers are dyed with direct, sulphur, vat, reactive, and more types than for any other fiber. Each of these classes of dye has its own application methods, dyeing characteristics, cost, fastness properties, colour range, advantages, and disadvantages. Reactive dyes, particularly those used for dyeing cotton, have become one of the major classes of dyes because of their good washing fastness, their bright shades, and their versatile batch and continuous dyeing methods. Furthermore, vat dyes are one of the oldest types of dye. Vat dyes in particular give dyeing on cellulosic fibers with the best overall fastness properties [2].

Single jersey knitted fabrics are used to make underwear and outerwear garments such as T-shirts. The knitted fabrics undergo a series of different processing treatment like bleaching, scouring, dyeing, softener padding, and relax drying. These processes are carried out to impart a particular property related to that process like scouring for absorbency, bleaching for whiteness, dyeing for imparting colour to fabric, and finishing for improving softness and handling the fabric [3].

It can be clear that each wet process has its special influence on the properties of the treated yarns or fabrics. However, studying the combined effect of these wet processes on the physical properties of yarns and plain singles jersey fabrics produced from these treated yarns is rare.

2. Review of Literature

Mercerization is originally discovered by John Mercer in 1844. From this time, mercerization has a major interest to researchers because of its advantages.

Akhbari et al. investigated the parameters influencing mercerization using RSM method, in order to increase the tensile strength of mercerized yarn [4]. Samei et al. compared the effects of hot mercerization on open-end and ring spun yarns in slack and under tension conditions. Mercerized yarns were bleached and dyed with reactive dye [5]. Gemci applied mercerization process on cotton fabrics with three different weaving patterns using three different time periods and three different processes under factory conditions to examine the dimension stability [6]. Moghassem and Valipour investigated the effects of four mercerization treatment parameters, namely, alkali concentration, time of treatment, bath temperature, and mercerization tension on dimensional properties of plain knitted fabric produced from cotton yarn [7]. Hasani studied the effect of different finishing processes like bleaching, dyeing and softening on mechanical and surface properties of cotton knitted fabrics [8].

Sameii et al. studied the effect of mercerization parameters on cotton fabrics made up of open-end yarns. Reactive dyes were used for dyeing. The results showed that tensile strength of fabrics could be improved in mercerization process [9]. The effect of different wet processing stages and sequences on the physical, dimensional, and dyeing properties of the single jersey knitted fabrics are produced by Murugesh and Selvadass [3].

From the previous studies, there are many researches about the effect of mercerization conditions only on the mercerized yarns. Some of the researchers studied the effect of mercerization and dyeing on mercerized yarns. Others studied the effect of mercerization parameters only on properties of fabrics. Also, little researchers studied the relation between properties of mercerized yarns and properties of plain single jersey knitted fabrics produced from them.

However, the combined effect of mercerization variables and variables of the following finishing operations is scanty. Consequently, this research attempts to expand the study of the effect of mercerization besides some types of dyeing on the produced yarns and properties of plain single jersey knitted fabrics produced from these yarns.

3. Experimental

3.1. Materials

Plied ring spun cotton yarn with a count of 20/2 Ne was produced. It was spun from Egyptian cotton G86 with single twist factor = 3.6 and plied twist factor = 3.5.

3.2. Methods

3.2.1. Mercerization

Mercerization was done on Jaeggli mercerizing yarn machine. Yarn hanks were treated with caustic soda concentration ranging from 26°Be′ to 34°Be′ with 2°Be′ intervals, using wetting agent [(6–8) g/L of FLORANIT 4028 of Pulcra Chemical]. Temperature of treatment was firstly changed by using 19°C and 24°C. Both applied tension and time of treatment were constant. To remove the excess caustic soda after the treatment, the yarn hanks were washed with hot and cold water. The hanks were then neutralized with acetic acid solution (0.5 cm/L) to remove any residual alkali. Yarns were finally rinsed with cold water, squeezed with centrifugal forces, dried at 110°C for 2 hrs.

3.2.2. Bleaching

Mercerized yarns were bleached in an exhaustion procedure, the bleaching bath containing 0.5% hydrogen peroxide, 2% sodium hydroxide, 2% asbicon (detergent used as assistant factor), and 1% Egypttool (wetting agent). The bleaching was carried out at 100°C for 1 hr. Acetic acid was used for neutralization.

3.2.3. Dyeing

Dyeing with vat and reactive dyes were carried out by exhaustion procedure.

(a) Reactive Dyeing. EcoFix.Blue.R (1.5%), Na₂CO₃ (5 g/L), and NaCl (20 g/L) were adjusted at 50°C and then raised to 60°C and maintained at this temperature for 90 min to dye as reactive dyeing. Dyed samples were then washed in a soap solution and then boiled and softened by using fatty acid and, finally, squeezed and dried at 100°C.

(b) Vat Dyeing. Yarns were dyed in a solution containing India Blue CLF (vat dye) (1.5%), NaOH (0.1%), and sodium hydrosulphite (5 g/L). As known, vat dyeing is based on the principle of converting water-insoluble vat dye by alkaline reduction to a water-soluble leuco compound having affinity to cotton. Sodium hydrosulphite is used in the reduction process at 60°C and then raised to 80°C for 20 min and then washed. Finally, it is oxidized by using H₂O₂ at 50°C for 30 min, washed, and softened by using fatty acid.

3.2.4. Knitting Process

Plain single jersey knitted fabrics were produced on Stoll flat knitting machine, G 12, and loop length 0.6 cm. The specification of the pretreated produced samples can be illustrated in Table 1.

Table 1: Fabrics production plan.

Types of dyeing
NaOH conc. (Be′)

26
28
30
32
34

Vat dyeing
√
√
√
√
√

Reactive dyeing
√
√
√
√
√

In addition, two samples of Plain single jersey knitted fabrics were produced from without mercerized, bleached, vat, and reactive dyed yarns. These two samples were used for comparison.

3.3. Testing Methods

Testing methods were carried on both of yarns and finished plain single jersey knitted fabrics as follows.

3.3.1. Testing Methods of Yarns

Breaking load and extension of yarns were measured by using USTER Tensorapid 4. Color strength of yarns was observed by using Data color International SF 600 at D65. Yarn abrasion resistance was measured according to ASTM D6611.

3.3.2. Testing Methods of Fabrics

A sensitive digital balance device with accuracy of two digits was used to measure the weight of the samples and then fabric weight in g/m² was estimated. Thickness of fabric samples was measured by using K094 SDL Atlas digital thickness gauge tester according to ASTM D1777, Standard Test Method for Thickness of Textile Material.

The fabric bursting strength and elongation due to burst were tested using H5KT Tinius Olsen universal testing machine using ASTM D 3787 bursting strength in knitted goods standard test method. Fabric abrasion resistance of fabrics was measured by using Taber Abrasion (Rotary Platform) tester according to ASTM D3884. The air permeability was tested using M021A SDL Atlas air permeability tester using ASTM D 737 standard test method. Fabric stiffness was measured by using the circular bend procedure according to ASTM D 4032. K/S was measured using D412G1 color i5 spectrophotometer using daylight condition (D65). K/S is used to evaluate the depth of dyed color after mercerization.

The Shrinkage value was defined by (1), for American AATCC number 135-1987

where is the length of the sample before laundering and drying and is the length of the sample after laundering and drying.

4. Experimental Results and Discussion

4.1. Results of Yarns

At the end of each treatment process, the yarn samples were collected and tested for some of the mechanical and color properties. The experimental results of yarns are compared to grey yarn as illustrated in the following equation:

where is the treated samples of yarns and is the grey sample.

4.1.1. Effect of Mercerization Temperature and NaOH Concentration on Yarn Breaking Load

Figure 1 shows the effect of temperature of mercerizing and NaOH concentration on the breaking load of yarns. It can be clearly seen that breaking load rose from 27.7% to 34.6% with an average value of 31.37%. In general, there is an increase in the strength in case of temperature 24°C more than temperature 19°C. In case of temperature 19°C, the highest value of breaking load occurs at 30°Be′, which is nearly equal to the highest value at 24°C which occurs at 28°Be′. This means that there is a relationship between mercerization temperature and NaOH concentration. In AS, with increasing temperature and with lower NaOH concentration, the same value can be obtained with increasing NaOH concentration at lower temperature.

Figure 1: Effect of mercerization temperature and NaOH conc. on yarn breaking load.

Of course, lower concentration with higher temperature is economically better. Consequently, the temperature 24°C is selected to be studied where the average increase value reaches 32.88%. The main reason of increasing the breaking load after mercerization process because cotton fibers are modified during mercerizing process and transformed from cellulose I to cellulose II. Fibers become more amorphous and less crystalline.

4.1.2. Effect of Mercerization and Dyeing on Breaking Load of Mercerized Yarns

Figure 2 shows the effect of both vat and reactive dyeing on the breaking load for the mercerized yarn at 24°C and at different NaOH concentrations. As shown, there is an increase generally in breaking load after vat dyeing more than reactive dyeing compared to bleaching.

Figure 2: Effect of vat and reactive dyeing on breaking load of mercerized yarns.

Results showed that the breaking load rose from 8.6% to 27.9% with the average value 16.24% in case of vat dyeing.

Also, results showed that the breaking load increased to 24.1% in case of reactive dyeing because of the effect of chemical bonds between the dye and the fibers. Moreover, reactive dye can also be bonded with more than one fiber consequently increasing the tensile strength. The increase in breaking load in case of reactive ranges from 5.5% to 24.1% with an average value of 13.22%.

The highest value in the breaking load for vat dyeing occurs at 34°Be′ (27.9%) but for reactive dyeing it occurs at 28°Be′ (24.1%).

On the other hand, the lowest value in breaking load for vat dyeing occurs at 28°Be′ (8.6%) but for reactive dyeing it occurs at 32°Be′ (5.5%).

As mercerizing process leads to the increase of dyeing absorption because of breaking the hydrogen bonds between the fibers in the crystalline regions and converting them to amorphous regions. This increase in vat dyeing is arranged during washing with alkali soap after dyeing process. In addition, the increase of these spaces between fibers with the presence of vat dyeing may be the reason for the rise of the breaking load.

4.1.3. Effect of Mercerization and Dyeing on Yarn Breaking Extension

Figure 3 shows the effect of mercerization and dyeing on the mercerized yarn at different NaOH concentrations and at 24°C. As shown mercerizing process affects the breaking extension negatively.

Figure 3: Effect of types of finishing on yarn breaking extension.

From the results after mercerization, breaking extension decreases from −16.7% to −22.5% with average value −20.5%. However, after bleaching breaking extension decreases from −19.4% to −31.4% with average value −24.4%.

Also there is a decrease after vat dyeing from −19.5% to −31.2% with average value −25.3%. Moreover, breaking extension decreases sharply after reactive dyeing from −16.1% to −35.2% with average value −29.1%. The decrease percentage of breaking extension can be illustrated due to the axis parallel alignment of fibers in the yarn centre [10].

4.1.4. Effect of Mercerization and Dyeing on Yarn Abrasion Resistance

Figure 4 shows the effect of both mercerization and dyeing on abrasion resistance of yarns at different NaOH concentrations. It can be clearly seen that there is an increase in abrasion resistance of yarns after mercerization from 55% to 178%. There is an increase after vat dyeing from 7% to 155%, and after reactive dyeing from 46% to 87%.

Figure 4: Effect of mercerization and dyeing on yarn abrasion resistance.

Abrasion of the yarn is followed by the gradual removal of fibers from the yarns when they are subjected to repeated distortion. Factors affecting the cohesion of the fibers in the yarn and yarn to yarn friction will have influence on the abrasion resistance. They mainly depend on the fiber surface, supramolecular structure of fibers, yarns surfaces, and yarn compressibility in addition to the magnitude of the normal pressure acting between them [11].

4.1.5. Effect of Vat and Reactive Dyeing on Color Strength of Mercerized Yarns

Figure 5 shows the effect of vat and reactive dyeing after mercerization at different NaOH concentrations and at 24°C on the color strength of yarns. In general, there is an increase in color strength in reactive dyeing more than vat dyeing. It can be clearly seen that color strength increased from 160.7% to 223.2% with average value 183% in case of vat dyeing because mercerizing process converts fibers to cylindrical shape leading to the increase of the spaces between the fibers, so the dye molecules can easily penetrate into the fibers and increase the color strength of this vat dye. Also, results showed an increase in color strength of reactive dyeing from 195.1% to 226.6% with average value 210.3% because molecules of this reactive dye are bonded with covalent bonds with the fibers, so the color strength of the dye increases.

Figure 5: Effect of vat and reactive dyeing on color strength of mercerized yarns.

The highest value in vat dyeing occurs at 34°Be′ (223.2%) and in reactive dyeing occurs at 32°Be′ (226.6%).

4.2. Results of Knitted Fabrics

Experimental results of fabric physical and colour properties are compared to the two unmercerized samples as illustrated in the following equation:

where MD is the mercerized, bleached, and dyed samples and BD is the unmercerized, bleached, and dyed samples, with the knowledge that each dyed sample is compared to its same type of dyed sample.

4.2.1. Fabric Thickness

Figure 6 shows the effect of both of mercerization and dyeing processes on the thickness of plain single jersey knitted fabrics. As shown, there is generally an increase in thickness in vat dyeing more than reactive dyeing with 26%. The same effect of the thickness is obtained in both vat dyeing and reactive dyeing depending on NaOH concentration.

Figure 6: Effect of mercerization and dyeing on thickness of plain single jersey knitted fabrics.

There is an increase in case of vat dyeing from 13.9% to 50% compared to vat standard sample, with average increase value 26.4%, while, in case of reactive dyeing, the average increase value of thickness was 0.7% compared to reactive standard sample. The highest value of thickness at vat dyeing occurs at 32°Be′ and at reactive dyeing occurs at 28°Be′.

4.2.2. Fabric Weight

Figure 7 shows the effect of mercerization and dyeing on the weight of plain single jersey knitted fabrics. As shown, the same effect on the weight of fabrics in both dyeing with increasing NaOH concentration. As in the case of the thickness, the weight of fabrics at vat dyeing is more than that at reactive dyeing. As in the case of vat dyeing, increasing temperature of mercerization leads to increase of the swelling, converting crystalline regions to amorphous regions. Consequently, there are greater opportunities to soak up water moisture because of the increase of the free amounts of hydroxyl groups which forms the hydrogen bonds. On the other hand, there is a decrease in the weight in the case of reactive dyeing because increasing the temperature leads to the removal of starching materials and some of natural impurities materials.

Figure 7: Effect of mercerization and dyeing on weight of plain single jersey knitted fabrics.

The average increase value in case of vat dyeing is 3.4%, but the average decrease value in case of reactive dyeing is 8.4%.

4.2.3. Fabric Shrinkage

Figures 8 and 9 show the effect of mercerization and dyeing on the shrinkage in both wales and courses directions of plain single jersey knitted fabrics. It can be clearly seen that there is a rise in the shrinkage in length direction in case of vat more than reactive dyeing. This means that reactive dyeing is better in shrinkage in length direction. The increase in shrinkage in length in case of vat dyeing ranges from 1.8% to 2.8% with average value 2%, but the increase in shrinkage in case of reactive ranges from 0.5% to 0.9% with average value 0.7%.

Figure 8: Effect of mercerization and dyeing on shrinkage in courses direction of plain single jersey knitted fabrics.

Figure 9: Effect of mercerization and dyeing on shrinkage in wales direction of plain single jersey knitted fabrics.

Of course the opposite happened in courses direction for both vat dyeing and reactive dyeing. As shown in Figure 9, the increase in shrinkage in courses direction in case of reactive dyeing is more than vat dyeing. This means that vat dyeing is better in the shrinkage in width more than reactive dyeing. The best values for shrinkage in wales direction occur at 26°Be′ for reactive dyeing and at 34°Be′ for vat dyeing. Besides, the best values for shrinkage in courses direction occur at 26°Be′ for vat dyeing and at 30°Be′ for reactive dyeing.

4.2.4. Bursting Strength of Plain Single Jersey Fabrics

Figure 10 shows the effect of mercerization and dyeing on the bursting strength of plain single jersey knitted fabrics. The results showed that the same effect on the tensile strength happens for the two dyeing until a certain point, and then the opposite happens. In general, there is an increase in tensile strength of knitted fabrics in case of vat dyeing more than reactive dyeing. The increase of tensile strength in case of vat dyeing rises from 0.5% to 19% with average value 8.4%. Also, increase of tensile strength in case of reactive dyeing ranges from 1.1% to 18.1% with average value 7.1%. In fact, the increase in tensile strength is because of strengthening of the weak points along the fiber and also the modifications in orientation and consolidation of weak points.

Figure 10: Effect of mercerization and dyeing on bursting strength of plain single Jersey knitted fabrics.

The highest value of breaking load in case of vat dyeing occurs at 34°Be′, and the highest value in case of reactive dyeing occurs at 26°Be′.

4.2.5. Fabric Stiffness of Plain Single Jersey Fabrics

Figure 11 shows the effect of mercerization and dyeing on the stiffness of plain single jersey fabrics.

Figure 11: Effect of mercerization and dyeing on stiffness of plain single jersey knitted fabrics.

For vat dyeing, stiffness of plain jersey fabrics decreases with the increasing NaOH concentration. However, for reactive dyeing, the stiffness is decreased then increased and finally remained constant. The lowest value of stiffness at vat dyeing occurs at 34°Be′ and at reactive dyeing occurs at 28°Be′.

4.2.6. Abrasion Resistance of Plain Single Jersey Fabrics

Figure 12 shows the effect of mercerization and dyeing on the abrasion resistance of plain single jersey fabrics. As before in the bursting strength, the same effect on fabric abrasion resistance for the vat and reactive dyeing happens till 30°Be′; after that the opposite happens. Abrasion resistance fabric of vat dyeing increases from 1.7% to 62.9% with average value 26.8%. In addition, abrasion resistance fabric of reactive dyeing increases from 4.8% to 55.1% with average value 20%. The highest value of fabric abrasion resistance in case of vat dyeing occurs at 32°Be′, and the highest value of fabric abrasion resistance in case of reactive dyeing occurs at 26°Be′.

Figure 12: Effect of mercerization and dyeing on abrasion resistance of plain single jersey knitted fabrics.

4.2.7. Air Permeability of Plain Single Jersey Fabrics

Figure 13 shows the effect of mercerization and dyeing on air permeability of plain single jersey fabrics. As shown, the increase in air permeability in case of vat dyeing is more than reactive dyeing. The results show that there is significant increase in air permeability in case of vat dyeing from 35% to 47% with average value 42.3%. Also, air permeability in case of reactive dyeing rises from 18.7% to 40% with average value 31.8%. The highest value for air permeability in case of vat dyeing occurs at 28°Be′, and in case of reactive dyeing it occurs at 34°Be′. The increase of air permeability in both vat dyeing and reactive dyeing can be explained due to the fiber arrangement in the cross-section of the yarn.

Figure 13: Effect of mercerization and dyeing on air permeability of plain single jersey knitted fabrics.

4.2.8. K/S of Plain Single Jersey Fabrics

Figure 14 shows the effect of mercerization and dyeing on K/S of plain single jersey fabrics. As shown, vat dyeing is higher than reactive dyeing regarding K/S values. The increase in K/S values in case of vat dyeing ranges from 53% to 90% with average value 72.5%.

Figure 14: Effect of mercerization and dyeing on K/S values of plain single jersey knitted fabrics.

Besides, the K/S values in case of reactive dyeing rise from 4.8% to 43.7% with average value 27.5%. The highest value of K/S in case of vat dyeing occurs at 34°Be′, and in case of reactive dyeing also occurs at 34°Be′.

The increase in color properties can be explained generally because of the destruction of crystalline regions during swelling and changes in microstructure and morphology.

5. Analysis of Variance

The influence of NaOH concentration on the properties of yarns after mercerization, bleaching, and vat and reactive dyeing was analyzed by the main effects analysis of variance (ANOVA). The results of values (variables have significant effect on the measured properties ) are given in Table 2.

Table 2: Effect of NaOH conc. on yarn properties.

Type of test
value of NaOH conc.

B-Force after mercerization
0.358

B-Force after bleaching
0.007

B-Force after vat dyeing
0.000

B-Force after reactive dyeing
0.013

Elongation after mercerization
0.000

Elongation after bleaching
0.000

Elongation after vat dyeing
0.000

Elongation after reactive dyeing
0.000

Abrasion resistance after mercerization
0.000

Abrasion resistance after bleaching
0.000

Abrasion resistance after vat dyeing
0.004

Abrasion resistance after reactive dyeing
0.147

It was found that NaOH conc. had a significant effect on B-Force (after bleaching and dyeing), elongation (after each treatment), and abrasion resistance (after mercerization, bleaching, and only vat dyeing) of yarns.

Besides, the effect of both NaOH concentration and type of dyeing on the properties of plain knitted fabrics was analyzed by the main effects analysis of variance (MANOVA). The results of values of fabrics are shown in Table 3.

Table 3: Effect of NaOH conc. and types of dyeing on the properties of plain knitted fabrics.

Types of test
value of NaOH conc.
value of types of dyeing

Fabric thickness
0.000
0.084

Fabric weight
0.002
0.027

Shrinkage in wales direction
0.228
0.070

Shrinkage in courses direction
0.719
0.032

Bursting strength
0.000
0.001

Fabric stiffness
0.684
0.166

Abrasion resistance
0.000
0.000

Air permeability
0.031
0.257

The results showed that NaOH concentration had a significant effect on the fabric thickness, bursting strength, fabric weight, abrasion resistance, and air permeability of plain knitted fabrics. On the other hand, the types of dyeing had a significant effect on fabric weight, shrinkage in course direction, bursting strength, and abrasion resistance of plain knitted fabrics.

6. Overall Evaluation of Yarn and Fabric Properties

Hypothesis testing was used to know if the best properties of yarns occur at the same variables for the produced knitted fabrics or not. This was considered the null hypothesis, while the alternative hypothesis occurred when the yarns highest area of radar chart does not occur at the same variables which represent the fabric highest area of radar chart.

Figures 15 and 16 show the total evaluation of the properties for yarns by using Performance Diagram method based on the absolute values. It was found that the highest area of radar chart occurred at 26°Be′ in case of vat dyeing as shown in Table 4. The lowest area of Performance Diagram in case of vat dyeing occurred at 32°Be′. The highest area of Performance Diagram in case of reactive dyeing occurred at 32°Be′, but the lowest area is achieved at 34°Be′.

Table 4: Total area of overall yarn properties.

Types of dyeing
NaOH conc. (Be′)

26
28
30
32
34

Vat dyeing
81%
72%
65%
58%
64%

Reactive dyeing
69%
73%
71%
79%
68%

Actual area/ideal area.

Figure 15: Overall evaluation of yarn properties at vat dyeing.

Figure 16: Overall evaluation of yarn properties at reactive dyeing.

Figures 17 and 18 show the total evaluation of the properties for plain single jersey fabrics by using radar chart method based on absolute values. It was found that the highest area of Performance Diagram, which represents the total physical properties, is achieved at 32°Be′, in case of vat dyeing as shown in Table 5. On the contrary, the lowest area of Performance Diagram in case of vat dyeing occurred at 26°Be′.

Table 5: Total area of overall fabric properties.

Types of dyeing
NaOH (Be′)

26
28
30
32
34

Vat dye
55%
56%
67%

77%

68%

Reactive dye
59%

56%

58%

57%

54%

Figure 17: Overall evaluation of fabric properties at vat dyeing.

Figure 18: Overall evaluation of fabric properties at reactive dyeing.

The average of improvement in the overall physical properties in case of vat dyeing is 65%.

The highest area of Performance Diagram in case of reactive dyeing is achieved at 26°Be′; the lowest area occurred at 34°Be′. The average improvement in the overall physical properties in case of reactive dyeing is 57%.

This means that the null hypothesis was not obtained as the yarns properties are not necessarily equal to the properties of fabrics produced from them.

It was noticed that the vat dyeing maintains the physical properties generally more than reactive dyeing.

7. Conclusion

(i) Mercerizing process of yarns at different NaOH concentrations, at 24°C, followed by bleaching and dyeing with vat and reactive dyeing, has an influence on the final properties of plain jersey fabrics.

(ii) There is an increase of thickness by about 3.4% to 50%, but mercerized dyed fabrics with vat dyeing are thicker than the reactive ones compared to unmercerized samples.

(iii) The average increase value of weight is 3.4% in case of vat dyeing. On the contrary, the average decrease value of weight in case of reactive dyeing is 8.4% compared to unmercerized samples.

(iv) For the shrinkage in wales direction, the increase in shrinkage for reactive dyeing is less than that for vat dyeing. On the contrary in courses direction, the increase in shrinkage for vat is less than reactive dyeing compared to unmercerized samples.

(v) There is an increase of bursting strength in case of vat dyeing from 0.5% to 19% and in case of reactive dyeing from 1.1% to 18.1% compared to unmercerized samples.

(vi) Consequently, mercerized plain jersey fabrics dyed with vat dyeing are stiffer than those of the reactive ones.

(vii) There is an increase of the fabric abrasion resistance for vat dyeing from 1.7% to 62.95% and for reactive dyeing from 4.8% to 55.1% compared to unmercerized samples.

(viii) Mercerized dyed fabrics with vat dyeing have higher air permeability values than reactive dyeing.

(ix) In general, there is an increase of the color properties for both vat dyeing and reactive dyeing compared to unmercerized samples because of the mercerization effect.

(x) From the overall evaluation of physical properties by Performance Diagram, the highest area occurred at 32°Be′ in case of vat dyeing.

(xi) Vat dyeing maintains the physical properties of the fabric generally more than reactive dyeing.

(xii) Analysis of variance showed the properties of yarns and fabrics affected by NaOH conc. and types of dyeing.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

References

T. Wakida, M. Lee, S. J. Park, and A. Hayashi, “Hot mercerization of cottons,” Fiber, vol. 58, pp. 304–307, 2002.

A. D. Broadbent, Basic Principles of Textile Coloration, Society of Dyers and Colourists, Bradford, UK, 2001.

B. K. Murugesh and M. Selvadass, “Influence of wet processing on properties of single jersey knitted fabrics,” International Journal of Fiber and Textile Research, vol. 3, no. 1, pp. 18–30, 2013.

M. Akhbari, A. Zahiri, and S. J. E. Bassam, “Optimization of parameters influencing mercerization using the RSM method in order to increase the tensile strength of mercerized yarn,” Fibres & Textiles in Eastern Europe, vol. 94, no. 5, pp. 30–35, 2012.

N. Samei, S. M. Mortazavi, A. Rashidi, and S. S. Najjar, “Changes in physical properties of hot mercerized ring and open-end spun cotton yarns,” Iranian Polymer Journal, vol. 17, no. 12, pp. 937–945, 2008.

R. Gemci, “Examining the effects of mercerization process applied under different conditions to dimensional stability,” Scientific Research and Essays, vol. 5, no. 6, pp. 560–571, 2010.

A. R. Moghassem and P. Valipour, “An extensive look in to the effect of mercerization treatment on dimensional properties of cotton plain knitted fabric,” Fibers and Polymers, vol. 14, no. 2, pp. 330–337, 2013.

H. Hasani, “Effect of different processing stages on mechanical and surface properties of cotton knitted fabrics,” Indian Journal of Fibre and Textile Research, vol. 35, no. 2, pp. 139–144, 2010.

N. Sameii, S. M. Mortazavi, A. S. Rashidi, and S. Sheikhzadah-Najar, “An investigation on the effect of hot mercerization on cotton fabrics made up of open-end yarns,” Journal of Applied Sciences, vol. 8, no. 22, pp. 4204–4209, 2008.

Y. Huh, Y. R. Kim, and W. Oxenham, “Analyzing structural and physical properties of ring, rotor, and friction spun yarns,” Textile Research Journal, vol. 72, no. 2, pp. 156–163, 2002.

I. Jordanov, B. Mangovska, and P. F. Tavčer, “Mechanical and structural properties of mercerized cotton yarns, bio-scoured with pectinases,” Tekstil, vol. 59, no. 10, pp. 439–446, 2010.