“Graphitic carbon nitride” synthesized by the solvothermal reaction between cyanuric chloride (C3N3Cl3) and sodium amide (NaNH2), which was one of the most common methods reported so far, was carefully examined by several analytical techniques for its chemical and structural characteristics. The chemical quantification by the electron microprobe and combustion methods showed that the product synthesized has a significant amount of hydrogen with a composition C3N5H3. Moreover, we found by FT-IR and IR-Raman measurements that the product consists mainly of stacked s-triazine units on the basis of the structural framework of cyanuric chloride, suggesting that s-triazine-based carbon nitride is more stable than heptazine-based one under a mild temperature condition (~200°C). The present study clearly demonstrates that hydrogen-free, pure graphitic C3N4 cannot be produced by the present solvothermal reaction proposed by the earlier study.
Ehime University1. Introduction
Since highly incompressible carbon nitrides with a stoichiometric composition of C3N4 were theoretically predicted [1, 2], many efforts have been made to experimentally synthesize the potential superhard phases such as by the chemical vapor deposition (CVD) and high-pressure and high-temperature (HPHT) techniques. According to the first-principle calculation by Teter and Hemley [2], among the five polymorphs predicted, cubic-C3N4 is energetically the most favorable under high pressure and could possibly be synthesized from graphitic-C3N4 (g-C3N4) at pressure above 12 GPa. On the other hand, g-C3N4 is thought to be the most stable form at the ambient condition and consists of two types of structural units, s-triazine ring unit [2] and heptazine (tri-s-triazine) ring unit [3], which are connected by nitrogen atoms in 3-fold coordination. In the past few decades, g-C3N4 attracted considerable attention in industrial applications such as photocatalyst (e.g., [4]), hydrogen storage (e.g., [5]), semiconductor (e.g., [6]), and a starting material for synthesizing potential superhard carbon nitride phases (e.g., [7]). A number of reports have been published for the synthesis of g-C3N4 and even other graphitic forms with nonstoichiometric compositions on the basis of various techniques such as CVD [8–10], solid reaction [11–17], solvothermal method [18–22], and thermal decomposition of compounds [23–26]. Among these, one of the easiest and simplest ways to obtain a nanocrystalline powder of g-C3N4 is the solvothermal method, in which the synthesis is achieved through the reaction of chemical sources in a solvent such as benzene and acetonitrile at high temperatures. In particular, a pioneer recipe reported by Guo et al. [18] was commonly used in many previous studies (e.g., [7, 27–29]) to obtain nanocrystalline g-C3N4 powders of various purposes. Their g-C3N4-forming reaction is expressed by the following formula:(1)C3N3Cl3+3NaNH2→g-C3N4+3NaCl+2NH3According to Guo et al. [18], this reaction proceeds in a step-by-step process as follows:(2)2NaNH2→Na2NH+NH3(3)NaNH2+Na2NH→Na3N+NH3(4)C3N3Cl3+Na3N→g-C3N4+NaCl
However, our recent study [7] suggested a strong possibility that such prepared g-C3N4 contains a considerable amount of hydrogen either in its structure or as surface adsorbates. The HPHT experiments using the solvothermally prepared g-C3N4 failed to synthesize any dense carbon nitride phases but instead resulted in the formation of a hydrogen-bearing, carbon nitride imide (C2N2(NH))-related phase [7]. FT-IR spectrum of the g-C3N4 powder also indicates the presence of hydrogen probably in the form of NH, as clearly mentioned in the original paper by Guo et al. [18] (and also pointed out in our earlier paper [7]), although they did not discuss the origin of hydrogen. It is, therefore, highly questionable whether the product obtained by Guo et al.’s recipe [18] is certainly hydrogen-free graphitic C3N4 composed of the stacked layers of s-triazine building blocks. Meanwhile, Guo et al.’s solvothermal recipe and characterization of the product by X-ray and electron diffraction and spectroscopic analyses have been cited by recent studies [30–32], where the authors assumed that their carbon nitride products have the ideal graphitic framework composed of s-triazine and heptazine units through the comparison with Guo et al.’s result. Thus, the careful reexamination of the solvothermal method and the reaction product is necessary and essential for further scientific and industrial applications of this carbon- and nitrogen-based nanomaterial. This may lead to new insights, such as recently reported work by Miller et al. [33] who reexamined the classic “Pharaoh’s serpent reaction,” in which mercury (II) thiocyanate decomposes to HgS, CS2, and g-C3N4 through the self-propagating combustion reaction and found that the reaction results in the formation of unique nanocomposite semiconductor material composed of nano-HgS particles and a porous g-C3N4 matrix. In the present study, we carefully synthesized “g-C3N4” by following the solvothermal method and examined the chemical and structural characteristics by means of various techniques in order to clarify the origin of hydrogen and the real process of the solvothermal reaction.
2. Experimental Methods
Nanocrystalline “graphitic” carbon nitride was prepared through the solvothermal reaction (1) between cyanuric chloride (C3N3Cl3) and sodium amide (NaNH2) by following the procedure reported by Guo et al. [18]. Cyanuric chloride (99 %) and sodium amide (98 %) reagents purchased from Sigma-Aldrich Co. LLC were used. Since sodium amide is highly sensitive to moisture and readily decomposes to produce sodium hydroxide and ammonia when hydrated, it was kept carefully under nitrogen atmosphere to avoid a potential alteration caused by moisture. The two reactants (0.003 mol each) were introduced into a Teflon inner vessel of an autoclave together with 45 ml of benzene (99 %). The autoclave was then placed in an oven and heated at 200°C for a duration of 6, 12, 24, 48, or 72 hours. The recovered product was first washed three times with acetone to remove any organic impurities and further washed three times with distilled water to remove sodium chloride, which is a byproduct of reaction (1). The final product obtained was a slightly yellowish white powder similar to that synthesized by Guo et al. [18]. It was dried at 100°C in a vacuum condition for at least 24 hours before measurements, in which no change in color was observed.
The chemical composition of the synthetic products was analyzed by electron microprobe using field emission-scanning electron microscope (FE-SEM, JEOL JSM-7000F) equipped with an energy-dispersive X-ray spectrometer (EDS, Oxford Instruments, X-Max 20) and also checked by combustion elemental analysis using a CHN analyzer (Yanaco Co. Ltd., MT-5). It has previously been technically difficult to accurately quantify light elements such as C and N by EDS due to high attenuation nature of the low-energy characteristic X-rays in the volume excited by electron beam. However, we recently demonstrated that a surface conductive coating of thin osmium layer is effective for EDS quantitative analysis particularly of light elements such as C, N, and O in both inorganic and organic materials [7, 38]. The validity of this method for carbon nitride analysis was indeed shown in Kojima and Ohfuji [7], in which the accuracy of quantification for C and N was evaluated to be less than 0.5%. For quantitative analysis, powdered carbon nitride samples were pelletized by using a hydraulic press and coated with a 5 nm thick osmium layer. Pure SiC and cubic BN standards with the same surface coating were used for quantitative calibration of carbon and nitrogen, respectively. Measurements were made carefully by beam-scanning on each target area of the products (at 1 nA and 15 kV) to avoid potential damage by the electron beam [38], which might result in modification of the C/N ratio. Since EDS cannot technically detect hydrogen, the amount of hydrogen in the products was estimated from the result of the combustion analysis.
Powder XRD profiles of the products were collected by using an X-ray diffractometer (Rigaku Co. Ltd., Ultima IV) equipped with a copper anode and a high speed and highly sensitive semiconductor detector (Rigaku, D/teX Ultra 250). The use of this detector was found to be very effective to obtain XRD patterns with better S/N ratio even from the poorly crystalline carbon nitride products. The FT-IR measurement was carried out by using a FT-IR spectrometer (Spectrum One, Perkin-Elmer, Inc.) with a resolution of 4 cm−1. The sample was pelletized with KBr prism material at the weight ratio of 1 : 50 for the measurement. Raman spectroscopic measurements were performed by using a confocal Raman microscope system (JASCO Co., Ltd., NRS-5000) with green (532 nm) and near-infrared (1064 nm) lasers. However, in the present case, the excitation by the green laser was found to be unsuitable for Raman spectroscopy due to a strong green fluorescence emitted from the carbon nitride samples. Peak fitting of XRD, FT-IR, and Raman profiles was carried out by using PeakFit ver. 4.12 software (HULINKS).
3. Results and Discussion
Table 1 shows the chemical quantification data of the carbon nitride product (synthesized by heating for 24 hours) obtained by EDS and combustion elemental analyses. The EDS spectra showed the presence of no other elements including sodium and chlorine (NaCl), which was produced as a by-product in reaction (1), removed by the postsynthesis treatment as mentioned above. Both methods gave a C/N ratio of 3 to 5 for the product, which clearly differs from the stoichiometry of C3N4. The combustion analysis revealed that the product contains a considerable amount of hydrogen equivalent to approximately 5 moles when the molar amount of carbon is assumed to be 3. Therefore, the chemical formula of the product obtained in this study can be written as C3N5H5. We also conducted additional runs with shorter/longer heating durations, but no clear changes were observed in the composition of the products (Figure 1), indicating that the reaction between cyanuric chloride and sodium amide has completed in a short time period and no further changes occurred. It should, however, be noted that the amount of hydrogen measured by the combustion analysis may have been overestimated due to contamination of H2O molecules that were potentially trapped at the surface of the poorly crystalline sample. Taking these points into account, the chemical reaction formula (1) proposed for the solvothermal method by Guo et al. [18] should be rewritten as follows:(5)C3N3Cl3+3NaNH2→C3N5H3+3NaCl+NH3where the molar content of hydrogen in the carbon nitride product is assumed to be 3 based on the stoichiometry of the reaction. This means that the reaction does not involve the decomposition of NaNH2 to form Na3N, and the step-by-step process (formulas (2) to (4)) proposed by Guo et al. [18] is unlikely, as discussed later.
The results of chemical quantification analysis by EDS and by combustion method (using organic elemental analyzer).
Method
C
N
H
O
EDS
At.%
35.67
59.90
-
4.17
Molar ratio∗
3
5.04
-
0.35
CHN
At.%
23.19
38.28
38.53
-
Molar ratio∗
3
4.95
4.98
-
The∗ amount of carbon is fixed to be 3.
The atomic concentrations of carbon, nitrogen, and hydrogen in the products synthesized at various heating durations, determined by combustion method.
Figure 2 shows the FT-IR spectrum of the sample synthesized by heating for 24 hours following the recipe of Guo et al. [18], in which strong absorptions are observed in the range of 800-1800 and 2800-3600 cm−1. Since in-plane C-N stretching and bending vibration modes of the s-triazine-based g-C3N4 show broad bands at 1150-1650 cm−1 region [8, 35], the several bands observed in the 1400-1600 cm−1 region (two intense peaks at 1432 and 1568 cm−1) are likely attributed to the stretching vibration mode of CN as well as the deformation mode of NH2 [14, 35]. Although Larkin et al. [37] pointed out that CN ring deformation mode generates the IR absorption peaks at 675 and 748 cm−1, these peaks were not observed in this study. On the other hand, the peak at 814 cm−1 can be assigned to the out-of-plane bending mode of the s-triazine and/or heptazine ring vibration [37, 39]. The bands at 1249 and 1316 cm−1 indicate the presence of C-N chain bonds between the heptazine rings and NH groups associated with C-NH-C units [14, 40] (Table 2), suggesting that the polymerization of aromatic rings has occurred during the reaction. A shoulder peak at 1647 cm−1 and the broad peaks in 3200-3400 cm−1 region are assigned to the deformation and stretching modes of bridging –NH- and terminal –NH2 groups, respectively [34, 35]. The origin of hydrogen is likely from NH2 and/or OH molecules, which are derived from the NaNH2 precursor and water (moisture) adsorbed on the surface. The small peak at 2181 cm−1 band is originated from C≡N bonds [10, 12, 15, 17, 36], which probably terminate dangling bonds as is the case of NH2 group. Figure 3(a) shows the Raman spectra of the product collected with an excitation wavelength of 1064 nm, and Figure 3(b) shows the same spectra after background subtraction. Raman peak position of the present product and the reported peak positions of melem [13], melon [13], and melamine [34] are listed in Table 3. The peaks at 691, 983, 1156, and 1527 cm−1 observed from our sample are assigned to the ring breathing mode, bending mode of CNC and NCN, deformation mode of the ring and NH2, and a combination of CN stretching mode and NH2 bending mode, respectively [34], which are also observed at almost the same positions for the reference materials (Table 3). The broad peaks at 1307, 1407, and 1605 cm−1 are assigned to the bending mode of NH, CH, and NH2, respectively [34, 40]. The presence of 1165 cm−1 band in IR spectra from the sample and melamine implies that our product has s-triazine ring units, while the ring mode at 747 cm−1 in Raman spectra, which is commonly observed for melem and melon, suggests the presence of the heptazine ring unit in the product. This means that the carbon nitride obtained through the solvothermal reaction is made up of not only s-triazine ring units but also heptazine ring units, suggesting that it is an intermediate product during the polymerization of s-triazine ring to heptazine ring. However, the degree of polymerization may not be so high due to the dominance of N-H, C-H, and C≡N bonds terminating the bonded chains.
The observed IR vibrational modes in comparison with melem, melon, and melamine as references. The abbreviations in the assignment column are as follows, b.: bending; def.: deformation; str.: stretching.
This study
Melema
Melona
Melamineb
Assignment
814
804
808
810
out-of-plane b. [34, 35]
887
Unassigned
1022
def. (ring) + def. (NH2) [35]
1101
Unassigned
1163
1170
def. (ring)+ def. (NH2) [35]
1194
1249
1246
str. (CN) associated with C-NH-C
1316
1308
1321
unit [10, 35]
1432
1418
1432
str. (CN) + b. (NH2) [34]
1487
1456
1465
1526
str. (CN) + b. (NH2) [34]
1568
1570
1567
1605
1616
1632
1626
b. (NH2) [34]
1647
1646
2181
C≡N [10, 12, 15, 17, 36]
3126
3163
3123
str. (NH) [34, 35]
3249
3178
3323
3420
3417
3453
3468
Refa. [14]; Refb. [34]
The observed Raman peak positions (cm−1) of our product together with those of melem, melon, and melamine as references. The abbreviations in the assignment column are as follows, b.: bending; t.: twisting; bre.: breathing; def.: deformation; str.: stretching; w.: wagging.
This study
Melema
Melona
Melamineb
Assignment
462
462
478
Unassigned
542
549
549
580
b. (NCN) + t. (NH2) [34]
635
595
Unassigned
691
688
705
675
bre. (ring) [34]
747
748
754
b. (ring) [14]
983
983
985
982
b. (CNC) + b. (NCN) [34]
1157
1157
1029 1189
def. (ring) + def. (NH2) [34]
1156
1243
Unassigned
1307
1302
b. (NH) [34]
1407
1408
1427
b. (CH) [37]
1456 1537
1471
1442 1554
str. (CN) + b. (NH2) [34]
1527
1605
1587 1657
1572
1657
b. (NH2) [34]
Refa. [14]; Refb. [34]
FT-IR spectrum of the sample obtained after heating for 24 hours.
IR-Raman spectrum of the sample obtained after heating for 24 hours before (a) and after (b) background correction.
Figure 4 shows the XRD profile of the product obtained by heating for 24 hours, where two intense broad peaks are seen at 2θ around 11° and 27°. The latter, most intense peak can be deconvoluted into three peaks centered at 26.79, 27.24, and 27.77°, respectively (Figure 4(a), inset). The strongest second peak (d = 3.27 Å) is likely attributed to the stacking of conjugated s-triazine ring layers, as its d-spacing corresponds well to the interlayer (002) spacing of the precursor cyanuric chloride (d = 3.26 Å) [41]. The first broad peak at 26.79° (d = 3.32 Å) can be assigned as the 310 reflection associated with the alignment of the aromatic rings of the structural framework of cyanuric chloride. On the other hand, the peak position of the third peak (d = 3.21 Å) corresponds to that of 002 (d =3.24 Å) of graphitic carbon nitride (g-C3N4) composed of the stacked layers of heptazine building blocks [26, 39]. Since the Raman and FT-IR spectra both showed peaks derived from s-triazine and heptazine ring units (Figure 2), the formation of g-C3N4 is also partly expected. The weak peaks in the low-angle region (centered at 10.89 and 12.12°, corresponding to d = 8.11 and 7.29 Å) may be attributed to (100) plane of heptazine-based carbon nitride, which is comparable to the in-plane structural packing motif such as the hole-to-hole distance of nitrogen pores [42, 43]. These peaks derived from the heptazine layers were detected from all the products synthesized with various heating durations (6-72 hours). Figure 5 shows the d-values and full width at half maximum (FWHM) of each observed peak and the relative intensity of 002 reflection of the s-triazine-based and heptazine-based layers (Ihep002/Itri002) versus heating time. The products obtained by heating for less than 24 hours showed more or less larger d-values and FWHM, which seem to have decreased with heating time. This implies that the s-triazine and heptazine layers were constructed gradually based on the structural framework of cyanuric chloride during heating. On the other hand, the d-values and FWHM values became constant after longer (> 24 hours) heating, suggesting that the construction of the layered structure had been completed. Since Ihep002/Itri002 decreased with heating duration (Figure 5(c)), the layered structure is considered to consist mainly of s-triazine-based network. However, a first-principle calculation [3] reported that heptazine-based carbon nitride is thermodynamically more stable than the s-triazine-based one, and some experimental studies also showed the production of the heptazine-based carbon nitride under high temperatures [13, 42, 44, 45]. Thomas et al. [43] reported that the condensation of s-triazine ring unit to heptazine ring unit occurred at above 390°C through the elimination of ammonia. It is known that heptazine-based polymers are formed (rearranged) from s-triazine-based compounds such as melamine via several intermediate components such as melam, melem, and melon [43]. The result of the present study suggests that the s-triazine-based carbon nitride is more stable at the mild temperature of around 200°C than heptazine-based carbon nitride. Therefore, the products obtained by shorter heating (< 24 hours) include the metastable heptazine-based carbon nitride, which then transformed to triazine-based carbon nitride by further heating for more than 24 hours.
(a) XRD profile of the sample obtained after 24-hour heating. The strongest peak at around 27° can be deconvoluted into three peaks drawn by red dotted line (inset). (b) Comparison of the strongest peak of each product synthesized at different heating durations with the peaks of the C3N3Cl3 precursor.
The variation of the main XRD peaks at around 27° of the products obtained at various heating durations. ((a) and (b)) d-value and FWHM of the three deconvoluted peaks; diamond: s-triazine ring alignment of structural framework of cyanuric chloride 310 peak, square: s-triazine ring interlayer plane 002 peak, and triangle: heptazine ring interlayer plane 002 peak. (c) Intensity ratio of each 002 peak from the interlayer planes of s-triazine ring and heptazine ring (Itri002/Ihep002).
According to Guo et al. [18], the solvothermal reaction forming g-C3N4 from C3N3Cl3 and NaNH2 is a step-by-step process through reactions (2)–(4). However, the formation of Na3N in formula (3) is questionable, since it is very unstable and has been synthesized only under extreme conditions such as ultrahigh vacuum [46] and high pressure [47]. In fact, Khabashesku et al. [36] detected a significant amount of hydrogen by FT-IR in the solid-solid reaction product of C3N3Cl3 and Li3N, an analogue alkali-metal mononitride of Na3N, at 380°C under N2 atmosphere. Furthermore, Guo and his colleagues [19] also identified the presence of hydrogen in the product obtained by the solvothermal reaction between C3N3Cl3 and NaN3. These results suggest a strong chemical affinity between alkali-metal nitrides such as Li3N and NaN3 and hydrogen (mostly from moisture) to form N-H bonds in the reaction. The result of the present study demonstrates that the reaction between NaNH2 and C3N3Cl3 proceeds by substituting the Cl groups of the latter by NH2 and NH groups of the former to form C3N5H3 compound. Taking into account the presence of NH groups, the decomposition of NaNH2 to Na2NH may have partly occurred. Such Na2NH and NaNH2 may directly react with C3N3Cl3, and thus the true process is expressed as follows:(6)2NaNH2→Na2NH+NH3(7)C3N3Cl3+NaNH2+Na2NH→C3N5H3+3NaClThe fact that the chemical compositions of our products synthesized at various heating durations are almost identical (Figure 1) suggests that the reaction completes within 6 hours of heating and further heating only promotes the construction of the layered structure composed of s-triazine ring units.
4. Conclusion
The present study clearly demonstrates that “graphitic” carbon nitride synthesized by the solvothermal reaction (Guo et al.’s recipe) contains a large amount of hydrogen at a molar ratio of C : H = 1 : 1. The structure of the product (C3N5H3) is mainly built up of stacked layers of s-triazine ring units with low degree of polymerization similar to melamine oligomer with dangling bonds terminated by N-H and O-H molecules. This means that pure graphitic carbon nitride (C3N4) cannot be obtained by the reported solvothermal method due to the strong chemical affinity between hydrogen and nitrogen/carbon. This can explain why our attempt to synthesize a dense cubic carbon nitride under high pressure and high temperature failed and the products were always hydrogen-containing forms such as C2N2(NH) [7].
Conflicts of Interest
The authors declare that there are no conflicts of interest regarding the publication of this paper.
Acknowledgments
The authors thank H. Kamada at the Division of Material Science of the Advanced Research Support Center (ADRES), Ehime University, for her technical assistance in combustion analysis using the CHN analyzer. IR-Raman measurements were performed with the cooperation of JASCO Co., Ltd. This work was partly supported by Research Unit Program for “Materials Science under Ultrahigh Pressure” of Ehime University.
LiuA. Y.CohenM. L.Prediction of new low compressibility solids198924549208418422-s2.0-2044437332810.1126/science.245.4920.841TeterD. M.HemleyR. J.Low-compressibility carbon nitrides1996271524553552-s2.0-003056971710.1126/science.271.5245.53KrokeE.SchwarzM.Horath-BordonE.KrollP.NollB.NormanA. D.Tri-s-triazine derivatives. Part I. From trichloro-tri-s-triazine to graphitic C3N4 structures200226550851210.1039/b111062b2-s2.0-0036105570WangX.BlechertS.AntoniettiM.Polymeric graphitic carbon nitride for heterogeneous photocatalysis201228159616062-s2.0-8486459305410.1021/cs300240xBaiX. D.ZhongD.ZhangG. Y.MaX. C.LiuS.WangE. G.ChenY.ShawD. T.Hydrogen storage in carbon nitride nanobells20017910155215542-s2.0-034771367210.1063/1.1402958WangX.MaedaK.ChenX.TakanabeK.DomenK.HouY.FuX.AntoniettiM.Polymer semiconductors for artificial photosynthesis: hydrogen evolution by mesoporous graphitic carbon nitride with visible light200913151680168110.1021/ja809307s2-s2.0-67849122733KojimaY.OhfujiH.Structure and stability of carbon nitride under high pressure and high temperature up to 125 GPa and 3000 K201339172-s2.0-8488274649710.1016/j.diamond.2013.07.006KouvetakisJ.BandariA.ToddM.WilkensB.CaveN.Novel synthetic routes to carbon-nitrogen thin films19946681181410.1021/cm00042a0182-s2.0-33751158752MaL. P.GuY. S.DuanZ. J.YuanL.PangS. J.Scanning tunneling microscopy investigation of carbon nitride thin films grown by microwave plasma chemical vapor deposition1999349110132-s2.0-003268218510.1016/S0040-6090(99)00061-9HidekazuT.SougawaM.TakarabeK.SatoS.AriyadaO.Use of nitrogen atmospheric pressure plasma for synthesizing carbon nitride2007464 A159615992-s2.0-3454785630210.1143/JJAP.46.1596GuY.ChenL.ShiL.MaJ.YangZ.QianY.Synthesis of C3N4 and graphite by reacting cyanuric chloride with calcium cyanamide200341132674267610.1016/S0008-6223(03)00357-92-s2.0-0141749190ZimmermanJ. L.WilliamsR.KhabasheskuV. N.MargraveJ. L.Synthesis of Spherical Carbon Nitride Nanostructures20011127317342-s2.0-000028255610.1021/nl015626hKomatsuT.Prototype carbon nitrides similar to the symmetric triangular form of melon20011138028052-s2.0-003509991210.1039/b007165jKomatsuT.The first synthesis and characterization of cyameluric high polymers2001202119252-s2.0-003594164310.1002/1521-3935(20010101)202:1<19::AID-MACP19>3.0.CO;2-G10.1002/1521-3935(20010101)202:1<19::AID-MACP19>3.0.CO;2-GLuX.GaiL.CuiD.WangQ.ZhaoX.TaoX.Synthesis and characterization of C3N4 nanowires and pseudocubic C3N4 polycrystalline nanoparticles200761214255425810.1016/j.matlet.2007.01.0762-s2.0-34447300156ZhangZ.LeinenweberK.BauerM.GarvieL. A. J.McMillanP. F.WolfG. H.High-pressure bulk synthesis of crystalline C6N9H3·HCl: A novel C3N4 graphitic derivative2001123327788779610.1021/ja01038492-s2.0-0034808010YangS. J.ChoJ. H.OhG. H.NahmK. S.ParkC. R.Easy synthesis of highly nitrogen-enriched graphitic carbon with a high hydrogen storage capacity at room temperature2009476158515912-s2.0-6314915795310.1016/j.carbon.2009.02.010GuoQ.XieY.WangX.LvS.HouT.LiuX.Characterization of well-crystallized graphitic carbon nitride nanocrystallites via a benzene-thermal route at low temperatures20033801-284872-s2.0-014176826610.1016/j.cplett.2003.09.009GuoQ.XieY.WangX.ZhangS.HouT.LvS.Synthesis of carbon nitride nanotubes with the C3N4 stoichiometry via a benzene-thermal process at low temperatures200410126272-s2.0-1642458315BaiY.-J.LüB.LiuZ.-G.LiL.CuiD.-L.XuX.-G.WangQ.-L.Solvothermal preparation of graphite-like C3N4 nanocrystals20032473-450550810.1016/S0022-0248(02)01981-42-s2.0-0037212749CuiY.TangY.WangX.Template-free synthesis of graphitic carbon nitride hollow spheres for photocatalytic degradation of organic pollutants20151611972002-s2.0-8494051722810.1016/j.matlet.2015.08.106GuQ.LiaoY.YinL.LongJ.WangX.XueC.Template-free synthesis of porous graphitic carbon nitride microspheres for enhanced photocatalytic hydrogen generation with high stability20151655035102-s2.0-8491007020310.1016/j.apcatb.2014.10.045MontigaudH.TanguyB.DemazeauG.AlvesI.CourjaultS.The high pressure synthesis of the graphitic form of C3N420003525472552GillanE. G.Synthesis of nitrogen-rich carbon nitride networks from an energetic molecular azide precursor20001212390639122-s2.0-003450032610.1021/cm000570yMillerD. R.HolstJ. R.GillanE. G.Nitrogen-rich carbon nitride network materials via the thermal decomposition of 2,5,8-triazido-s-heptazine2007467276727742-s2.0-3424712907310.1021/ic061296yYanS. C.LiZ. S.ZouZ. G.Photodegradation performance of g-C3N4 fabricated by directly heating melamine20092517103971040110.1021/la900923z2-s2.0-69949171130MingL. C.ZininP.MengY.LiuX. R.HongS. M.XieY.A cubic phase of C3N4 synthesized in the diamond-anvil cell200699303352010.1063/1.21685672-s2.0-33645502328LiuJ. J.GaoX.ChenP. W.A possible new C-N phase originated from graphitic carbon nitride loaded by shock wave20116732432462-s2.0-7995629524610.4028/www.scientific.net/MSF.673.243HuC. C.WangM. S.HungW. Z.Influence of solvothermal synthesis on the photocatalytic degradation of carbon nitride under visible light irradiation20171671910.1016/j.ces.2017.03.053WangH.YuanX.WangH.ChenX.WuZ.JiangL.XiongW.ZengG.Facile synthesis of Sb2S3/ultrathin g-C3N4 sheets heterostructures embedded with g-C3N4 quantum dots with enhanced NIR-light photocatalytic performance2016193364610.1016/j.apcatb.2016.03.0752-s2.0-84962810200PapailiasI.TodorovaN.GiannakopoulouT.KarapatiS.BoukosN.DimotikaliD.TrapalisC.Enhanced NO2 abatement by alkaline-earth modified g-C3N4 nanocomposites for efficient air purification201843022523310.1016/j.apsusc.2017.08.0842-s2.0-85028311307HuC.-C.WangM.-S.HungW.-Z.Influence of solvothermal synthesis on the photocatalytic degradation activity of carbon nitride under visible light irradiation2017167192-s2.0-8501642241510.1016/j.ces.2017.03.053MillerT. S.d'AleoA.SuterT.AlievA. E.SellaA.McMillanP. F.Pharaoh's Serpents: New Insights into a Classic Carbon Nitride Material2017643211572158010.1002/zaac.201700268MircescuN. E.OlteanM.ChisV.LeopoldN.FTIR, FT-Raman, SERS and DFT study on melamine2012621651712-s2.0-8486565961210.1016/j.vibspec.2012.04.008MillerT. S.JorgeA. B.SuterT. M.SellaA.CoràF.McMillanP. F.Carbon nitrides: Synthesis and characterization of a new class of functional materials2017192415613156382-s2.0-8502200437310.1039/c7cp02711g10.1039/C7CP02711GKhabasheskuV. N.ZimmermanJ. L.MargraveJ. L.Powder synthesis and characterization of amorphous carbon nitride20001211326432702-s2.0-003450723110.1021/cm000328rLarkinP. J.MakowskiM. P.ColthupN. B.The form of the normal modes of s-triazine: Infrared and Raman spectral analysis and ab initio force field calculations1999555101110202-s2.0-000815188310.1016/S1386-1425(98)00244-3OhfujiH.YamamotoM.EDS quantification of light elements using osmium surface coating201511041891952-s2.0-8494558811710.2465/jmps.141126LotschB. V.DöblingerM.SehnertJ.SeyfarthL.SenkerJ.OecklerO.SchnickW.Unmasking melon by a complementary approach employing electron diffraction, solid-state NMR spectroscopy, and theoretical calculations - Structural characterization of a carbon nitride polymer20071317496949802-s2.0-3425034222210.1002/chem.200601759JürgensB.IrranE.SenkerJ.KrollP.MüllerH.SchnickW.Melem (2,5,8-triamino-tri-s-triazine), an important intermediate during condensation of melamine rings to graphitic carbon nitride: Synthesis, structure determination by x-ray powder diffractometry, solid-state NMR, and theoretical studies20031253410288103002-s2.0-004238862310.1021/ja0357689XuK.HoD. M.PascalR. A.Azaaromatic chlorides: a prescription for crystal structures with extensive nitrogen-chlorine donor-acceptor interactions1994116110511010.1021/ja00080a013DaiH.GaoX.LiuE.YangY.HouW.KangL.FanJ.HuX.Synthesis and characterization of graphitic carbon nitride sub-microspheres using microwave method under mild condition2013381091172-s2.0-8488109219710.1016/j.diamond.2013.06.012ThomasA.FischerA.GoettmannF.AntoniettiM.MüllerJ.-O.SchlöglR.CarlssonJ. M.Graphitic carbon nitride materials: variation of structure and morphology and their use as metal-free catalysts200818414893490810.1039/b800274f2-s2.0-54049153179FinaF.CallearS. K.CarinsG. M.IrvineJ. T. S.Structural investigation of graphitic carbon nitride via XRD and neutron diffraction2015277261226182-s2.0-8492773271410.1021/acs.chemmater.5b00411LotschB. V.SchnickW.New light on an old story: Formation of melam during thermal condensation of melamine20071317495649682-s2.0-3425036710410.1002/chem.200601291FischerD.JansenM.Synthesis and Structure of Na3N200241101755175610.1002/1521-3773(20020517)41:10<1755::AID-ANIE1755>3.0.CO;2-CEversJ.MünsterkötterM.OehlingerG.PolbornK.SendlingerB.Natriumdinitridoborat mit dem linear gebauten, symmetrischen BN23- -Anion19901621L17L222-s2.0-002547745710.1016/0022-5088(90)90476-Z