Co doped CdTe powder samples were prepared by solid-state reaction method. In the present work effect of Co doping on structural, optical, and magnetic properties has been studied. X-ray diffraction studies confirm zinc blend structure for all the samples. The lattice parameter showed linear increase with the increase in Co content. The elemental constituents were characterized by EDAX. Optical studies showed the increase in band gap with increase in Co level. The samples were diluted magnetic semiconductors and exhibited clear hysteresis loop showing room temperature ferromagnetism as confirmed by vibrating sample magnetometer.
1. Introduction
Doping of magnetic atoms like Mn, Fe, Cr, Co, Ni, and so forth into II-VI, II-V, III-V, and IV-VI host semiconductors leads to a new class of materials called dilute magnetic semiconductors (DMS) [1]. In recent years, considerable amount of research work has been devoted to form new DMS and to improve the ferromagnetic properties of the known DMS in an effort to develop new spintronic devices, such as spin valves, spin light emitting diodes, magnetic sensors, logic devices, and ultrafast optical switches [2]. The unique properties of DMS attracted the scientific community and are extensively studied for their distinctive behavior in spintronic devices which allow control of both the spin and the charge of carriers [3, 4]. II-VI DMS systems are particularly interesting, since doping of magnetic ions in II-VI systems is more effective than metal oxide systems. Ferromagnetic semiconductors formed in this manner by varying the concentration of the magnetic material received much attention as the presence of magnetic ions allows tailoring the energy gap and lattice constant leading to a number of unusual electronic and magnetic properties resulting from the large sp-d exchange interaction between the magnetic ions and the band electrons. These interactions are strongly influenced by the ground state of the particular substituted magnetic ion [5, 6]. In order to realize the practical implication of spin-based devices, DMS must exhibit room temperature ferromagnetism. Though room temperature ferromagnetism was reported in II-VI DMS in both experimentally and theoretically investigations by several researchers, the exact origin of magnetism in DMS is still a challenge to scientific community. II-VI based DMS with Mn as the dopant has been studied extensively, but the studies with other magnetic dopants like Fe, Co, Ni, and so forth are meager. Limited number of reports are available on Co doped CdTe crystals. This could be due to the difficulties in preparing homogeneous crystals with sufficient amounts of substituted Co as its solubility is very low. Magnetic properties of Co based CdTe materials have been studied [7–9] and the large p-d interaction and d-d exchange interaction were established between Co2+ and Cd2+ ions [10–12]. Studies on Co doped CdTe alloy powders have not been reported so far. These factors and the interesting properties exhibited by Co doped CdTe system are the motivation to carry out this study. In the present work, the structural, optical, and magnetic properties on Co doped CdTe alloy powders prepared by solid-state reaction method have been reported.
2. Experimental
Co doped CdTe powders with Co concentrations of 5 at.% and 8 at.% were synthesized by single step solid-state reaction method. 5N purity CdTe, Co, and Te (99.99%, M/S Sigma-Aldrich) were used as source materials. Appropriate quantities of freshly prepared CoTe and CdTe were mixed and ground thoroughly for 16–18 hours to ensure homogeneity and then sintered at 500°C for 6 hours under a pressure of 10−3 Torr. The sintered Co doped CdTe alloy powder were characterized by different techniques. Powder X-ray diffraction (XRD) patterns of all the samples were recorded using X-ray diffractometer (Bruker, D8 Advance), equipped with Ni filter, and operated at 40 kV, 30 mA (CuKα radiation, λ = 0.15406 nm) with a scan speed of 0.02°s−1 in the 2θ range of 20°–80°. The elemental composition of the samples was arrived at using EDAX (Genesis X4M attached to the JSM 840A). The room temperature diffuse reflectance spectra of the samples were recorded using double beam UV-Vis-NIR spectrophotometer (Jasco V-670) in the wavelength range of 200–2500 nm. Magnetic measurements were carried out using a vibrating sample magnetometer (Lakeshore VSM 7410) at an applied field of 15,000 Gauss at room temperature.
3. Results and Discussion3.1. Structural Analysis
Powder XRD patterns of pure and Co doped CdTe alloy powders are shown in Figure 1. All the peaks seen in the pattern coincided with standard cubic CdTe structure (JCPDS Card no. 89-3053) and the subsequent patterns are indexed with their respective planes. No peak related to Co or CoTe was observed in the X-ray diffraction pattern after thorough analysis by Rietveld software confirming that Co has been incorporated into the crystal lattice of CdTe without changing the cubic structure of CdTe. It can be seen that all the samples exhibited zinc blend structure with (111) predominant orientation. Figure 2 shows variation of “a” with Co. The lattice parameter was found to decrease linearly with increase in “x” obeying Vegard’s law. The decrease in lattice parameter with the increase in Co concentration implies the lattice contraction. Change in lattice parameter may be due to the difference in ionic radii of cobalt and cadmium. The ionic radii of Co2+ and Cd2+ in tetrahedral site are (0.58Å) and (0.78Å) [13] respectively. The difference between the two ionic radii is small. As a consequence, changes in lattice cell parameters and cell volume with cobalt substitution are also small. As the Co2+ ions were in a tetrahedral environment, these results a decrease in lattice parameter by considering the smaller ionic radius of Co2+ ions. Hence it can be concluded that the doped Co2+ ions substitute the host lattice at tetrahedral site symmetry that brings expansion in CdTe lattice.
X-ray diffraction pattern of Cd1-xCoxTe alloy powders.
Variation of lattice parameter with increase in Co level.
3.1.1. EDAX Analysis
The spectra shown in Figure 3 depict the chemical composition of the Co doped CdTe alloy powders at 5 at.% and 8 at.%. The EDAX spectra revealed that the peaks corresponding to Cd, Te, and Co and their weight (wt.%) ratio and atomic (at.%) ratio compositions are shown in the inset of Figure 3. It is clear that the at.% of Cd element decreases with increasing Co content indicating the formation of Co doped CdTe alloy powder as confirmed by powder XRD.
EDAX spectra of (a) Cd0.95Co0.05Te and (b) Cd0.92Co0.08Te alloy powders.
3.2. Optical Properties
Figure 4 shows the optical reflectance spectra of pure and Co doped CdTe alloy powders in the photon energy range of 1.0–2.5 eV. Inset of Figure 4 shows the expanded view of fundamental band edge E0 with the observed electronic transitions labeled as E0, E0+Δ0, E1, E1+Δ1, and E2 peaks. It is evident from Figure 4 that the fundamental absorption edge (E0) shifted systematically near the IR region towards higher energy with increase in Co level. This observed increase in absorption edges with increase in Co concentration indicates that the Co2+ ions have replaced the Cd2+ ions in the CdTe lattice. Variation of optical gap energy as a function of Co concentration is illustrated in Figure 5 and the optical band gap energy was found to increase with the increase in Co concentration. Kim et al. [14] have also reported similar variation optical band gap in Zn1-xCoxO thin films. In general, it is interpreted that the increase in the band gap in Co doped CdTe alloy powders may be due to sp-d exchange interactions between band electrons and localized d electrons of Co ions.
Plot of reflectance versus photon energy (eV) for pure and Co doped CdTe alloy powders.
Variation of band gap of Cd1-xCoxTe powders with Co concentration.
3.3. Magnetic Studies
The magnetic properties of pure and Co doped CdTe for 5 at.% and 8 at.% alloy powders were investigated by magnetization measurements carried out at room temperature. The M-H curves of pure and Co doped CdTe are shown in Figure 6. Ferromagnetism in pure CdTe was not expected as it is diamagnetic in nature, whereas all the Co doped samples exhibited a well defined magnetization hysteresis confirming ferromagnetic behaviour at room temperature. It was observed from Figure 6 that the saturation magnetization increased with increase in Co concentrations. The obtained magnetization (Ms) for 5 at.% and 8 at.% of Co are 0.00086 emu/g and 0.0054 emu/g. Generally ferromagnetism in DMS is considered to originate from the exchange interaction between free delocalized carriers and the localized d spins on the Co ions [15]. Presence of free carriers is therefore necessary for the appearance of ferromagnetism. Alver et al. [16] have reported ferromagnetism in Co doped CdTe thin films at room temperature and at low temperatures, but the doping composition dependent magnetization study was not carried out.
Plot of magnetization versus magnetic field of pure CdTe and Co doped CdTe alloy powders.
4. Conclusions
Co doped CdTe (with Co concentrations of 5 at.% and 8 at.%) powders were synthesized by single step solid-state reaction method. From X-ray diffraction, the crystal structure was confirmed to be cubic. The Co ions replaced the Cd ions without changing the CdTe crystal structure and the lattice parameter increased linearly with increase in Co level following Vegard’s law. EDAX spectra revealed the existence of Co in Cd1-xCoxTe alloy powders. The reflectance measurement shows the increase in optical band gap energy with increase in Co level. The magnetization measurements clearly showed room temperature ferromagnetism in 5% and 8% Co doped CdTe alloy powders.
Acknowledgments
The authors thank the Defense Research and Development Organization (DRDO), New Delhi, India, for providing financial support to carry out the present research work. The authors also express their thanks to SAIF-IIT Madras for providing the VSM and EDAX studies.
FurdynaJ. K.KossutJ.198825Boston, Mass, USAAcademic PressDiluted Magnetic SemiconductorsPeartonS. J.AbernathyC. R.NortonD. P.HebardA. F.ParkY. D.BoatnerL. A.BudaiJ. D.Advances in wide bandgap materials for semiconductor spintronics20034041371682-s2.0-0037470283OhnoH.Making nonmagnetic semiconductors ferromagnetic199828153799519562-s2.0-0032516694WolfS. A.AwschalomD. D.BuhrmanR. A.DaughtonJ. M.Von MolnárS.RoukesM. L.ChtchelkanovaA. Y.TregerD. M.Spintronics: a spin-based electronics vision for the future20012945546148814952-s2.0-003590039810.1126/science.1065389HassK. C.EhrenreichH.Electronic and magnetic properties of II-VI diluted magnetic semiconductors1990861–48142-s2.0-0023165696ChuuD.-S.ChangY.-C.HsiehC.-Y.Growth of CdMnS films by pulsed laser evaporation19973041-228352-s2.0-0031186145AlawadhiH.MiotkowskiI.LewickiA.RamdasA. K.MiotkowskaS.McElfreshM.Magnetic susceptibility and compositional dependence of the energy gap in Cd1-xCoxTe20021417461146202-s2.0-003702965610.1088/0953-8984/14/17/330ShihO. W.AggarwalR. L.VuT. Q.BeclaP.Bandedge magnetoreflectance and magnetization of Cd1-xCoxTe19928132452492-s2.0-0026685429AbramishvilyV. G.RyabchenkoS. M.SavchukA. I.SemenovY. G.KomarovA. V.Carrier-ion exchange interactions in crystals Cd1-xCoxTe199710163974022-s2.0-0031078875AlawadhiH.MiotkowskiI.SouwV.McElfreshM.RamdasA. K.MiotkowskaS.Excitonic Zeeman effect in the zinc-blende II-VI diluted magnetic semiconductors Cd1-xYxTe (Y=Mn, Co, and Fe)20016310155201ZielinskiM.RigauxC.LemaîtreA.MycielskiA.DeportesJ.Exchange interactions and magnetism of Co2+ in Zn1-xCoxTe19965326746842-s2.0-0000133189ZielinskiM.RigauxC.MycielskiA.MenantM.Zeeman spectrum of the 1s exciton in very diluted Cd1-xCoxTe compounds200063392-s2.0-0035134633035202ShannonR. D.Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides197632part 5751767KimJ. H.KimH.KimD.YoonS. G.ChooW. K.Optical and magnetic properties of laser-deposited Co-doped ZnO thin films2004131116776802-s2.0-394309866510.1016/j.ssc.2004.06.033BouloudenineM.ViartN.ColisS.KortusJ.DiniaA.Antiferromagnetism in bulk Zn1-xCoxO magnetic semiconductors prepared by the coprecipitation technique200587532-s2.0-3364553056810.1063/1.2001739052501AlverÜ.BacaksızE.YanmazE.Structural, magnetic and optical properties of Co-diffused CdTe thin films20084561-269