Nd1.85Ce0.15CuO4−δ powders are chemically reduced in supercritical sodium ammonia solutions from room temperature to 350°C. The crystallographic structure of the reduced powders is investigated from Rietveld refinement of X-ray powder diffraction. The atomic positions are maintained constant within experimental errors while temperature factors of all atoms increase significantly after the chemical treatments, especially of Nd/Ce atoms. The ammonothermally reduced Nd1.85Ce0.15CuO4−δ powders show diamagnetic below 24 K which is contributed to the lower oxygen content and higher temperature factors of atoms in the treated compound. The ammonothermal method paves a new way to reduce oxides in supercritical solutions near room temperature.
1. Introduction
The electron-doped (Nd,Ce)2CuO4−δ T′-phase is the best candidate to investigate superconductivity mechanisms [1–4] because of its simple crystallographic structure as well as the hole-doped La2CuO4+y T-phase. The T′-phase superconductor has been synthesized through rare-earth substitution on the Nd site by Ce [5, 6], through fluorine substitution for oxygen [6, 7], or through reduction process [1, 8–10] at high temperatures of 800–1100°C. These traditional high temperature procedures have successfully reduced copper on CuO2 sheets, inducing superconductivity of the T′-phase with transition temperature Tc=22–27 K [1, 5–10]. However it is still challenging to adjust the chemical state of the CuO2 sheets through low temperature treatments. Up to date there is no report on chemical reductions of the T′-phase at low temperatures to induce superconductivity.
On the contrary, the hole-doped La2CuO4+y T-phase, the counterpart of the electron-doped T′-phase, can be chemically oxidized by both traditional high temperature treatments [11, 12] and low temperature treatments [13–15] to achieve superconductivity. It is well known that the superconducting T-phase can be prepared through alkaline earth substitution [11] and high-oxygen pressure treatment [12] at high temperature over 800°C. La2CuO4 has also been oxidized in aqueous solutions below 150°C to achieve superconductivity when strong oxidizing agents (such as potassium permanganate [13, 14] and sodium hypochlorite [15]) are dissolved in water as solvents. Superconductivity transition temperatures Tc of the low-temperature oxidized T-phase are ~40 K [13–15], higher than that of the T-phase (Tc~30 K [11, 12]) prepared by high temperature treatments, indicating the effectiveness of low-temperature aqueous chemical treatments.
The reduction of the electron-doped (Nd,Ce)2CuO4−δ T′-phase is the counterpart of the oxidization of the hole-doped La2CuO4+y T-phase. It has been reported that supercritical hydrothermal technique is a unique method to successfully dope oxygen into the hole-doped La2CuO4+y T-phase in aqueous solutions at 100–180°C. The achieved transition temperature Tc (42 K [14, 16]) of the T-phase superconductors is slightly higher than that achieved by traditional low-temperature chemical treatments (Tc~40 K [13]), showing the best capability to oxidize superconductors among various low-temperature aqueous oxidization treatments. Then two questions raise: (1) is there a supercritical reduction method (counterpart of supercritical hydrothermal technique) to reduce oxides? (2) Is it possible to reduce the electron-doped T′-phase (counterpart of the T-phase) at low temperatures?
In this research, Nd1.85Ce0.15CuO4−δ T′-phase powders are chemically reduced in a supercritical sodium metal ammonia solution, counterpart of the oxidation hydrothermal solutions, below 350°C. The low-temperature reduction treatments greatly affect crystallographic structures and magnetic properties of the powders.
2. Materials and Methods
The polycrystalline Nd1.85Ce0.15CuO4−δ samples used for the experiments are prepared from oxides by a solid state reaction. Appropriate quantities of Nd2O3, CeO2, and CuO powders are mechanically mixed, ground in an agate mortar, sintered in air at 950–1100 ± 5°C for four days, with intermittent regrindings, removed from furnaces, and quenched in air to room temperature. X-ray powder diffraction patterns indicate that the samples are single phase. The single phase samples are then ground into powders and further annealed in a floating Ar atmosphere at 930 ± 5°C for 24 h as starting samples.
An autoclave is pre-cooled by liquid nitrogen. Then liquid ammonia is poured from a high pressure (130 PSI) tank into the autoclave. An alkali metal bar is cut to a desired weight under a protected atmosphere and dropped into the liquid ammonia contained in a clean quartz cuvette to form an alkali metal ammonia solution. Nd1.85Ce0.15CuO4−δ starting powders are then dropped into the ammonia solution once the alkali solution turns blue completely. The autoclave is cooled down to −33°C, the boiling point of ammonia at one atmosphere. The autoclave is then sealed quickly at one atmosphere before the autoclave is warmed up. The sealed autoclave is heated up to 10–350°C for 72 h in a furnace. According to ammonia phase diagram, the ammonia pressure in the autoclave is 20–1000 kPa depending on the treatment temperature and the liquid ammonia filling rate. Then the ammonothermally treated powders are collected, filtered, thoroughly washed with distilled water and ethanol in sequence, and dried at room temperature in vacuum. The details of the ammonothermal procedure have been described in other literatures [17–19].
The X-ray powder diffraction (XRD) patterns are measured on a Rigaku D/max-2400 diffractometer with Cu-Kα radiation at room temperature. All data are collected in a step scanning mode with a step of 0.02° (2θ) and a measuring time of 0.5 s per step. An angular range from 10° to 80° is applied and NBS SRM 640 Si is added as an internal standard for lattice parameter determinations. The lattice parameters are calculated using the DICVOL91 program [20] after the experimental peak positions are calibrated. The X-ray diffraction data are also collected over an angular range of 10–130° for Rietveld refinements. The divergence, scattering, and receiving slits are set at 1°, 1°, and 0.10 mm, respectively. A total of 6001 points with a maximum count of about 15,000 and 123 independent reflections are measured for Rietveld refinements. The Rietveld refinement is then carried out using the computer program DBWS-9411 [21].
Magnetic susceptibility of the powders is measured with a SQUID magnetometer under a DC magnetic field down to 4.2 K.
The oxygen content of the samples is chemically determined by an iodometric titration [22]. Sodium thiosulfate titrant is standardized against 99.999%-pure CuO powders. The Nd1.85Ce0.15CuO4−δ powders are put into 50% potassium iodide solutions at room temperature and dissolved with 10% hydrochloric acid. Starch with a concentration of 2% is used as an endpoint indicator.
3. Results and Discussion
The powders are black before and after the ammonothermal treatments when the treatment temperature is lower than 150°C. Scanning electron microscopic observation shows that the grain size of the powders is slightly decreased by 5% to 10% after the treatments. XRD studies indicate that the T′-phase is thermally stable up to 150°C in the sodium ammonia solution. All the powders are single phase with a space group of I4/mmm (T′-phase) before and after the reduction treatments. Figure 1 shows XRD patterns of the T′-phase powders before and after the ammonothermal treatments at 54°C. Lattice parameters are nearly identical within experimental errors. a=b=3.9430(4) Å and c=12.070(2) Å before the powders are ammonothermally treated while a=b=3.9433(3) Å and c=12.072(1) Å after the powders are ammonothermally treated at 54°C.
X-ray diffraction patterns of Nd1.85Ce0.15CuO4−δ powders (a) before and (b) after ammonothermal treatments at 54°C in sodium ammonia solutions.
The ammonothermal reduction treatments affect magnetization properties of the T′-phase. SQUID magnetic measurements indicate that the untreated T′-phase Nd1.85Ce0.15CuO4−δ powders did not show any magnetization transition above 4.2 K to 50 K, similar to the reported earlier [23]. After the powder is ammonothermally treated at 54°C, a magnetic transition is observed near 24 K. Figure 2 is the susceptibility χ versus temperature T in a temperature range of 4.2–50 K for the Nd1.85Ce0.15CuO4−δ powders that are ammonothermally treated at 54°C. The powders are paramagnetic above 24 K while they are diamagnetic below 22 K. The transition temperature of 24 K is comparable to that (Tc=22–24 K) achieved by the traditional high temperature reduction treatments at 850–1050°C [1, 3, 8–10], slightly lower than that (Tc=27 K) achieved by the fluorine substitution for oxygen [7]. Therefore the supercritical ammonothermal reduction treatments are a simple but effective method to achieve superconductivity in the T′-phase.
Magnetic susceptibility χ of treated Nd1.85Ce0.15CuO3.961 as a function of temperature T. The zero-field-cooled measurement is carried out under 10 Oe. The insert shows enlarged susceptibility as a function of temperature near the transition. The powders are ammonothermally reduced at 54°C in sodium ammonia solutions.
The oxygen content (4−δ) of the T′-phase powders is determined by the iodometric titration. The oxygen content of the as-prepared powders is 3.975(5) while it is 3.961(5) of the chemically treated powders at 54°C. Therefore the supercritical ammonothermal treatments lower the oxygen content of the T′-phase and reduce the chemical state of the CuO2 sheets, resulting in the diamagnetic properties of the T′-phase powders.
It is well known that alkali metal, such as sodium, is very soluble in liquid ammonia [24]. Sodium produces solvated cations and solvated electrons in liquid ammonia:(1)Na+x+yNH3⟶NaNH3y++e-NH3xwhere e- is the solvated electron in the ammonia solution. The [e-(NH3)x] ions can reduce oxides effectively. Thus the alkali ammonia solution is one of the strongest reductive solutions [24], providing a homogeneous environment to reduce (Nd,Ce)2CuO4−δ T′-phase compounds here under supercritical conditions. The abundant solvated electrons in the ammonia solution can directly dope into the CuO2 sheets of the T′-phase, changing the carrier concentration of CuO2 sheets to induce diamagnetic properties of the T′-phase below 24 K.
However, the sodium ammonia solution is not thermally stable at high temperatures, 2Na + 2NH3 → 2NaNH2 + H2↑, and loses reduction activity over 100°C. In order to examine temperature effects, the (Nd,Ce)2CuO4−δ T′-phase powders are also chemically treated in the sodium ammonia solution over 100°C. No diamagnetic behavior of the treated powders is detected. The reduction activity of the sodium solution is also lower at lower temperatures (room temperature to 30°C), resulting in no significant magnetic change of the T′-phase powders. The optimum treatment temperature is 54°C.
Besides sodium ammonia solution, other alkali metal (such as potassium and lithium) ammonia solutions have similar chemical activities and should also work as reduction solutions to induce diamagnetic characterization of T′-phase powders. We test potassium ammonia solutions and (Nd,Ce)2CuO4−δ T′-phase powders can be reduced in potassium ammonia solutions at 50°C.
In order to explore how the ammonothermal treatments affect the crystallographic structures of Nd1.85Ce0.15CuO4−δ powders besides the lattice parameters and oxygen content, X-ray Rietveld structural refinements of the powders are carried out to determine more detailed crystallographic structures of the powders.
The Rietveld refinements are performed with initial positional parameters according to those of Nd2CuO4 [25]. Nd and Ce atoms are located statistically on the site 4e(0,0,z) with the initial atomic ratio Nd : Ce = 1.85 : 0.15. The oxygen atoms are set on the sites 4c(0, 0.5, 0) and 4d(0, 0.5, 0.25). The total oxygen content 4−δ is 3.961 for the reduced samples (Figure 3(b)) and 3.975 for the untreated samples (Figure 3(a)), according to the iodometric titration. The Cu atoms are put on the site 2a(0, 0, 0). The space group of the powders is I4/mmm. X-ray diffraction peaks are fitted as a pseudo-Voigt function in shape. Background values are obtained by linear interpolation between average values in regions between diffraction peaks. The Debye-Waller factor for the compounds is corrected for absorption.
Final Rietveld refinement patterns of (a) Nd1.85Ce0.15CuO3.975 powders without treatments and (b) Nd1.85Ce0.15CuO3.961 powders ammonothermally treated at 54°C in sodium ammonia solutions. Black crosses represent the experimental values and the red solid line the calculated pattern. The green solid line at the bottom is the difference between the experimental and calculated data. The blue bars represent the position of Bragg reflections.
Figure 3 shows the final Rietveld refinement patterns of the untreated and treated powders. Table 1 lists the final Rietveld refined positional and thermal parameters of atoms in the samples.
Final Rietveld refined parameters of Nd1.85Ce0.15CuO4−δ powders from X-ray powder diffraction data.
The ammonothermal treatments do not affect the atomic positions within experimental errors. The fact is in good agreement with previous neutron Rietveld refinements [26] of superconducting and nonsuperconducting (Nd,Ce)CuO4-y T′-phases.
The thermal parameters of the T′-phase compounds are increased significantly by the ammonothermal treatments. The B in Table 1 is the isotropic temperature factor, B=8π2u2¯, where u is the vibrational amplitude of atoms. The ammonothermal treatments have enhanced the isotropic temperature factor B of O(1) atoms 4.5 times while they have not affected that of O(2) atoms within experimental errors. The result is in agreement with the Raman and infrared transmission studies [2] and the microscopic oxygen-reduction mechanism of T′-phase [4, 5]. It is suggested that the reduction processes only remove oxygen in the CuO2 sheets to destroy the long-range antiferromagnetism and increase the mobility of charge carriers for superconductivity, while they do not affect apical oxygen, resulting in the great change of thermal vibration of O(1) atoms but not O(2) atoms.
Simultaneously, the thermal parameter B of Nd atoms and Ce atoms is increased 11 times after the ammonothermal treatments while that of Cu is increased 2.3 times. The significant changes of the thermal parameters should also be important factors to cause the diamagnetic behavior shown in Figure 2.
4. Conclusions
The T′-phase Nd1.85Ce0.15CuO4−δ compounds were chemically reduced at 54°C in supercritical sodium ammonia solutions, resulting in a diamagnetic transition near 24 K. X-ray Rietveld refinements indicated that the ammonothermal treatments enhanced the isotropic temperature factors of atoms, especially Nd/Ce atoms and O(1) atoms, of the oxide powders while their lattice parameters were unchanged. The strong reduction environment of sodium ammonia solutions induced the diamagnetic properties of the T′-phase.
Conflict of Interests
The authors declare that there is no conflict of interests regarding the publication of this paper.
Acknowledgments
The work is partially supported by the Defense Threat Reduction Agency under Grant HDTRA122221. Yucheng Lan acknowledges the support from US Department of Energy under the Contract DE-NA0000720 through the Program of S. P. Massie Chair of Excellence. Feng Lin is supported by the National Basic Research Program of China (973 Program), Grant no. 2012CB933004.
SchultzA. J.JorgensenJ. D.PengJ. L.GreeneR. L.Single-crystal neutron-diffraction structures of reduced and oxygenated Nd2-xCexCuOy19965395157515910.1103/physrevb.53.51572-s2.0-0000465298RichardP.RiouG.HetelI.JandlS.PoirierM.FournierP.Role of oxygen nonstoichiometry and the reduction process on the local structure of Nd2-xCexCuO4±δ200470606451310.1103/physrevb.70.0645132-s2.0-19544368137MangP. K.LarochelleS.MehtaA.VajkO. P.EricksonA. S.LuL.BuyersW. J. L.MarshallA. F.ProkesK.GrevenM.Phase decomposition and chemical inhomogeneity in Nd2−xCexCuO4±δ200470909450710.1103/physrevb.70.0945072-s2.0-20844462056KangH. J.DaiP.CampbellB. J.ChupasP. J.RosenkranzS.LeeP. L.HuangQ.LiS.KomiyaS.AndoY.Microscopic annealing process and its impact on superconductivity in T'-structure electron-doped copper oxides20076322422910.1038/nmat18472-s2.0-33847631365TokuraY.TakagiH.UchidaS.A superconducting copper oxide compound with electrons as the charge carriers1989337620534534710.1038/337345a02-s2.0-0342698973CavaR. J.TakagiH.FlemingR. M.KrajewskiJ. J.PeckW. F.Jr.BordetP.MarezioM.BatloggB.RuppL. W.Jr.Metal atom stoichiometry in the electron doped superconductor (Nd, Ce)2CuO419921991-2657210.1016/0921-4534(92)90541-j2-s2.0-0026902412JamesA. C. W. P.MurphyD. W.ZahurakS. M.Superconductivity at 27 K in fluorine-doped Nd2CuO41989338621224024110.1038/338240a02-s2.0-33748733073TakagiH.UchidaS.TokuraY.Superconductivity produced by electron doping in CuO2-layered compounds198962101197120010.1103/physrevlett.62.11972-s2.0-3643133490PlebańczykM.KlimczukT.SadowskiW.Influence of the improved reduction technique on superconductivity in Nd1.85Ce0.15Cu1±yO4-δ2007460–46243243310.1016/j.physc.2007.03.1112-s2.0-34548169907HoryńR.Crystallochemical characterization of Ce/RE substituted phases of T′-structure type: quantitative analysis of Cu valence (V) and its content (1-y) in superconducting sample of nominal composition Nd1.95-xCexCuO4(x=0.15)2012524778210.1016/j.jallcom.2012.02.057BednorzJ. G.MüllerK. A.Possible high Tc superconductivity in the Ba-La-Cu-O system198664218919310.1007/BF01303701ZhouJ.SinhaS.GoodenoughJ. B.Comment on, ‘identification of a superoxide in superconducting La2CuO4+δ by X-ray photoelectron’ spectroscopy19893916123311233310.1103/PhysRevB.39.12331Takayama-MuromachiE.SasakiT.MatsuiY.Direct oxidation of La2CuO4 in an aqueous solution of KMnO419932071-29710110.1016/0921-4534(93)90427-r2-s2.0-0027553259LanY. C.ChenX. L.CaoY. G.HuangJ. K.CheG. C.LiuG. D.XuY. P.XuT.LiJ. Y.Structure and superconducting properties of chemically oxidized La2CuO4+y under hydrothermal conditions20003361-215115610.1016/s0921-4534(00)00281-12-s2.0-0033721176TuQ.ChenX.MaB.ZhaoZ.LanY.LiangJ.Superconductivity at 45 K in La2CuO4+δ oxidized by NaClO2002741798210.1007/s003390100839LanY. C.ChenX. L.CheG. C.CaoY. G.LiJ. Y.TuQ. Y.Hydrothermal oxidation: a new chemical oxidation method to dope oxygen in La2CuO4+δ200013101415141810.1088/0953-2048/13/10/3022-s2.0-0034295656LanY. C.ChenX. L.CaoY. G.XuY. P.XunL. D.XuT.LiangJ. K.Low-temperature synthesis and photoluminescence of AlN1999207324725010.1016/S0022-0248(99)00448-0LanY. C.ChenX. L.XuY. P.CaoY. G.HuangF.Syntheses and structure of nanocrystalline gallium nitride obtained from ammonothermal method using lithium metal as mineralizator20003514-152325233010.1016/S0025-5408(00)00447-52-s2.0-0034312854LanY. C.ChenX. L.CrimpM. A.CaoY. G.XuY. P.XuT.LuK. Q.Single crystal growth of gallium nitride in supercritical ammonia2005272066206910.1002/pssc.200461557BoultifA.LoueerD.Indexing of powder diffraction patterns for low-symmetry lattices by the successive dichotomy method199124698799310.1107/S00218898910064412-s2.0-0026368044YoungR. A.SakthivelA.MossT. S.Paiva-SantosC. O.DBWS-9411: an upgrade of the DBWS*.* programs for Rietveld refinement with PC and main-frame computer199528part 336636710.1107/S0021889895002160HarrisD. C.HewstonT. A.Determination of Cu3+/Cu2+ ratio in the superconductor YBa2Cu3O8-x198769118218510.1016/0022-4596(87)90025-9MatsudaM.YamadaK.KakuraiK.KadowakiH.ThurstonT. R.EndohY.HidakaY.BirgeneauR. J.KastnerM. A.GehringP. M.MouddenA. H.ShiraneG.Three-dimensional magnetic structures and rare-earth magnetic ordering in Nd2CuO4 and Pr2CuO419904216100981010710.1103/physrevb.42.100982-s2.0-0000852259NicholisD.1979Amsterdam, The NetherlandsElsevier ScientificWilhelmH.CrosC.RenyE.DemazeauG.HanflandM.Influence of pressure on the crystal structure of Nd2CuO419988122729273210.1039/a805886e2-s2.0-0000023184IzumiF.MatsuiY.TakagiH.UchidaS.TokuraY.AsanoH.Neutron and electron diffraction study of the electron-doped superconductor Nd1.845Ce0.155CuO4−y1989158343343910.1016/0921-4534(89)90240-22-s2.0-0024656664