Advances in Materials Science and Engineering
Volume 2015 (2015), Article ID 406470, 4 pages
http://dx.doi.org/10.1155/2015/406470

Research Article

Dissolution Behavior of Cellulose in IL + DMSO Solvent: Effect of Alkyl Length in Imidazolium Cation on Cellulose Dissolution

Airong Xu,¹ Lili Cao,¹ Bingjun Wang,² and Junying Ma¹

¹School of Chemical Engineering and Pharmaceutics, Henan University of Science and Technology, Luoyang, Henan 471003, China
²China Iron & Steel Research Institute Group, Beijing 100081, China

Received 22 December 2014; Revised 27 February 2015; Accepted 10 March 2015

Academic Editor: Markku Leskela

Copyright © 2015 Airong Xu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

Four cellulose solvents including [C₂mim][CH₃COO] + DMSO, [C₄mim][CH₃COO] + DMSO, [C₆mim][CH₃COO] + DMSO, and [C₈mim][CH₃COO] + DMSO were prepared by adding dimethyl sulfoxide DMSO in 1-ethyl-3-methylimidazolium acetate [C₂mim][CH₃COO], 1-butyl-3-methylimidazolium acetate [C₄mim][CH₃COO], 1-hexyl-3-methylimidazolium acetate [C₆mim][CH₃COO], and 1-octyl-3-methylimidazolium acetate [C₈mim][CH₃COO], respectively. The solubilities of cellulose in these solvents were determined at 25°C. The effect of the alkyl chain length in imidazolium cation on cellulose solubility was investigated. With increasing alkyl chain length in imidazolium cation, the solubility of cellulose increases, but further increase in alkyl chain length results in decreases in cellulose.

1. Introduction

Recently, considerable attention has been received in the research related to the application of imidazolium-based carboxylate ionic liquids (ILs) in the dissolution of cellulose and delignification of lignocellulosic biomass [1]. This is mainly ascribed to the fact that, for the ILs with the same imidazolium-based cation backbone, imidazolium-based carboxylate ILs generally have lower melting points and higher capacity of cellulose dissolution compared to imidazolium-based chloride or bromide ILs. Fukaya et al. firstly reported the imidazolium-based formate ILs which were liquid at room temperature and could efficiently dissolve cellulose [2]. Xu et al. studied the effect of anionic structure and alkyl chain length of 1-butyl-3-methylimidazolium carboxylate ILs on cellulose solubility and found that cellulose solubility increased due to the replacement of H in the [CH₃COO]⁻ anion of [C₄mim][CH₃COO] by an electron-donating group but decreased because of the replacement of H in the [CH₃COO]⁻ anion of [C₄mim][CH₃COO] by an electron-withdrawing group [3, 4]. By NMR spectroscopic studies technique, Zhang et al. studied the dissolution mechanism of cellulose in [C₂mim][CH₃COO] and suggested that the hydrogen bonding of hydroxyls with [CH₃COO]⁻ anion and [C₂mim]⁺ cation of [C₂mim][CH₃COO] was the major force for cellulose dissolution [5]. Lu et al. studied the effect of cationic structure of acetate ILs on cellulose dissolution and found that cations with acidic protons but without high electronegativity atoms (like oxygen and/or nitrogen) in the cationic backbone and large sized group in the alkyl chain would be a rational choice [6]. Zhang et al. studied the structure-property relationship of 1-allyl-3-methylimidazolium carboxylate ILs, and the carboxylate ILs had less viscosity and higher cellulose solubility than 1-butyl-3-methylimidazolium carboxylate ILs [7]. Moreover, imidazolium-based carboxylate IL such as [C₂mim][CH₃COO] also could be used to dissolve or partition lignocellulosic biomass like wood [8, 9].

However, the imidazolium-based carboxylate ILs still show defects: high viscosity which would make cellulose difficultly disperse in ILs and thus help to dissolve cellulose more effectively and high processing temperatures which would consume/waste energy. To overcome the disadvantages, Rinaldi developed (IL + aprotic polar solvent including dimethyl sulfoxide DMSO and DMF) systems which have lower viscosity and higher dissolving rate than neat ILs [10]. Later on, Xu et al. [11] designed novel [C₄mim][CH₃COO]/DMSO solvents by adding an aprotic polar solvent DMSO to [C₄mim][CH₃COO] and found that the solvents could effectively dissolve cellulose at ambient temperature without heating. Based on molecular dynamics simulations and quantum chemistry calculations, Zhao et al. investigated the mechanism of cellulose in (IL + aprotic polar solvent) systems and concluded that the solvation of [C₄mim]⁺ and [CH₃COO]⁻ by the aprotic solvents makes it possible to produce more “free” [CH₃COO]⁻ anions from anion-cation pairs, which would readily interact with cellulose, leading to the increase in cellulose solubility [12].

Extensive literature survey reveals that few researches have been conducted to investigate how the alkyl length of imidazolium cation in IL + DMSO solvent effect on cellulose dissolution. To have a better understanding of the alkyl length of imidazolium cation in IL + DMSO solvent effect on cellulose dissolution and provide wealthy knowledge for the design of novel IL + DMSO solvents, more detailed studies are still needed. Therefore, in the present work, four cellulose solvents including [C₂mim][CH₃COO] + DMSO, [C₄mim][CH₃COO] + DMSO, [C₆mim][CH₃COO] + DMSO, and [C₈mim][CH₃COO] + DMSO were designed. The solubilities of cellulose in these solvents will be determined at 25°C. The effect of the alkyl chain length of imidazolium cation on cellulose solubility will be investigated in detail.

2. Experimental

2.1. Materials

Microcrystalline cellulose (MCC) with viscosity-average degree of polymerization (DP) being 229 was from Alfa Aesar. 1-Ethyl-3-methylimidazolium acetate [C₂mim][CH₃COO] (99%), 1-butyl-3-methylimidazolium acetate [C₄mim][CH₃COO] (99%), 1-hexyl-3-methylimidazolium acetate [C₆mim][CH₃COO] (99%), and 1-octyl-3-methylimidazolium acetate [C₈mim][CH₃COO] (99%) were purchased from Linzhou Keneng Material Technology Co., Ltd. Dimethyl sulfoxide DMSO was from Tianjin Kemiou Chemical Reagent Co. Ltd. These materials were used as received.

2.2. Preparation of IL + DMSO Solvents

As an example, [C₂mim][CH₃COO] + DMSO solvent was prepared by adding DMSO in dried [C₂mim][CH₃COO] with a given molar ratio (2.5 : 1) of DMSO to [C₂mim][CH₃COO] under stirring. [C₄mim][CH₃COO] + DMSO, [C₆mim][CH₃COO] + DMSO, and [C₈mim][CH₃COO] + DMSO solvents were prepared by using a similar process.

2.3. Dissolution of Cellulose

In a typical dissolution experiment, cellulose was added into a 25 mL colorimetric tube which contained 2.0 g of [C₂mim]Ac + DMSO, and the tube was sealed with parafilm. The tube was then immersed in an oil bath (DF-101S, Gongyi Yingyu Instrument Factory), and the bath temperature was controlled to be 25 ± 0.5°C. The mixture was heated and stirred at a given temperature. Additional cellulose was added until the solution became completely clear under polarization microscope (Nanjing Jiangnan Novel Optics Co., Ltd.). When cellulose became saturated, judged by the fact that cellulose could not be dissolved further within 2 h, its solubility (expressed by gram per 100 g of solvent) at 25°C could be calculated from the amount of the solvent and cellulose added.

3. Results and Discussion

The solubility values of cellulose in IL + DMSO solvents at 25°C are shown in Table 1. It can be seen from Table 1 that the alkyl chain length of imidazolium cation markedly affects the solubility of cellulose. Among the investigated IL + DMSO solvents, [C₄mim][CH₃COO] + DMSO is the most efficient for the dissolution of cellulose. With the exception of [C₄mim][CH₃COO] + DMSO solvent, the solubility of cellulose decreases with increasing alkyl chain length in the order: [C₂mim][CH₃COO] + DMSO > [C₆mim][CH₃COO] + DMSO > [C₈mim][CH₃COO] + DMSO.

Table 1: The solubility (g per 100 g of solvent) of MCC in IL + DMSO solvents at 25°C.

Entry
Solvent

Solubility

1
[C₂mim][CH₃COO] + DMSO ( = 2.5 : 1)
2.5 : 1
12.5

2
[C₄mim][CH₃COO] + DMSO ( = 2.5 : 1)
2.5 : 1
15.0

3
[C₆mim][CH₃COO] + DMSO ( = 2.5 : 1)
2.5 : 1
11.0

4
[C₈mim][CH₃COO] + DMSO ( = 2.5 : 1)
2.5 : 1
10.0

is the molar ratio of DMSO to IL.

It is well known that the electron-donating capacity of alkyl group increases as alkyl chain length increases. Therefore, as the alkyl chain length in imidazolium cation increases, the electron cloud density of carbon atoms C₂ and C₄ (see Figure 1) bounded to nitrogen atom N₃ decreases, which results in an increase in acidity of hydrogen atoms H₂ and H₄. Furthermore, the increased acidity of hydrogen atoms in imidazolium cation contributes to the hydrogen bond formation between acidic hydrogen and hydroxyl oxygen of cellulose and thus cellulose dissolution [5]. Therefore, the solubility of cellulose in [C₄mim][CH₃COO] + DMSO solvent is higher than that in [C₂mim][CH₃COO] + DMSO solvent. However, as alkyl chain length further increases, the steric hindrance of the hydrogen bond formation between acidic hydrogen and hydroxyl oxygen increases, and the hydrophilicity of imidazolium cation decreases [6]. Therefore, further increase in alkyl chain length conversely can cause a decrease in cellulose solubility. That is why the cellulose solubility decreases with increasing alkyl chain length in the order: [C₄mim][CH₃COO] + DMSO > [C₂mim][CH₃COO] + DMSO > [C₆mim][CH₃COO] + DMSO > [C₈mim][CH₃COO] + DMSO. Similar trend was also observed for the 1-alky-3-methylimidazolium chlorides in which [Cnmim]⁺ cation has varying alkyl chain lengths [13].

Figure 1: Schematic structures for the investigated ILs in the IL + DMSO solvents.

In addition, it is also found that, at 25°C, cellulose is not dissolved in all the ILs [C₂mim][CH₃COO], [C₄mim][CH₃COO], [C₆mim][CH₃COO], and [C₈mim][CH₃COO]. However, after DMSO was added in these ILs, respectively, cellulose becomes readily soluble. This is due to the fact that, upon adding DMSO in IL, DMSO serves to partially dissociate the strong ion pairs in IL into solvated cations and anions, and the solvated cations and anions in IL + DMSO solvent are more accessible to the hydroxyl proton of cellulose than those in neat IL, which is beneficial to the disruption of the hydrogen bonds in cellulose and thus to the cellulose dissolution [11, 12, 14]. This is the reason why cellulose becomes readily soluble in [C₂mim][CH₃COO] + DMSO, [C₄mim][CH₃COO] + DMSO, [C₆mim][CH₃COO] + DMSO, and [C₈mim][CH₃COO] + DMSO solvents.

4. Conclusions

In this work, four cellulose solvents including [C₂mim][CH₃COO] + DMSO, [C₄mim][CH₃COO] + DMSO, [C₆mim][CH₃COO] + DMSO, and [C₈mim][CH₃COO] + DMSO were prepared to investigate the effect of the alkyl chain length of imidazolium cation on cellulose solubility. With increasing alkyl chain length in imidazolium cation, the cellulose solubility decreases in the order: [C₄mim][CH₃COO] + DMSO > [C₂mim][CH₃COO] + DMSO > [C₆mim][CH₃COO] + DMSO > [C₈mim][CH₃COO] + DMSO. This is mainly ascribed to the fact that the increasing alkyl chain length leads to an increase in the acidity of the hydrogen atoms H₂ and H₄ in imidazolium cation which contributes to the hydrogen bond formation between acidic hydrogen and hydroxyl oxygen of cellulose and thus cellulose dissolution. However, as alkyl chain length further increases, the steric hindrance of the hydrogen bond formation between acidic hydrogen and hydroxyl oxygen increases, and the hydrophilicity of imidazolium cation decreases, which goes against cellulose dissolution.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgment

This work was supported financially by the National Natural Science Foundation of China (no. 21373078).

References

H. Wang, G. Gurau, and R. D. Rogers, “Ionic liquid processing of cellulose,” Chemical Society Reviews, vol. 41, no. 4, pp. 1519–1537, 2012.

Y. Fukaya, A. Sugimoto, and H. Ohno, “Superior solubility of polysaccharides in low viscosity, polar and halogen-free 1,3-dialkylimidazolium formates,” Biomacromolecules, vol. 7, no. 12, pp. 3295–3297, 2006.

A. R. Xu, J. J. Wang, and H. Y. Wang, “Effects of anionic structure and lithium salts addition on the dissolution of cellulose in 1-butyl-3-methylimidazolium-based ionic liquid solvent systems,” Green Chemistry, vol. 12, no. 2, pp. 268–275, 2010.

A. R. Xu, Y. B. Zhang, W. W. Lu, K. S. Yao, and H. Xu, “Effect of alkyl chain length in anion on dissolution of cellulose in 1-butyl-3-methylimidazolium carboxylate ionic liquids,” Journal of Molecular Liquids, vol. 197, pp. 211–214, 2014.

J. M. Zhang, H. Zhang, J. Wu, J. Zhang, J. S. He, and J. F. Xiang, “NMR spectroscopic studies of cellobiose,” Physical Chemistry Chemical Physics, vol. 12, no. 8, pp. 1941–1947, 2010.

B. Lu, A. Xu, and J. Wang, “Cation does matter: how cationic structure affects the dissolution of cellulose in ionic liquids,” Green Chemistry, vol. 16, no. 3, pp. 1326–1335, 2014.

Y. J. Zhang, A. R. Xu, B. L. Lu, Z. Y. Li, and J. J. Wang, “Dissolution of cellulose in 1-allyl-3-methylimizodalium carboxylates at room temperature: a structure–property relationship study,” Carbohydrate Polymers, vol. 117, pp. 666–672, 2015.

N. Sun, M. Rahman, Y. Qin, M. L. Maxim, H. Rodríguez, and R. D. Rogers, “Complete dissolution and partial delignification of wood in the ionic liquid 1-ethyl-3-methylimidazolium acetate,” Green Chemistry, vol. 11, no. 5, pp. 646–655, 2009.

M. Zavrel, D. Bross, M. Funke, J. Büchs, and A. C. Spiess, “High-throughput screening for ionic liquids dissolving (ligno-)cellulose,” Bioresource Technology, vol. 100, no. 9, pp. 2580–2587, 2009.

R. Rinaldi, “Instantaneous dissolution of cellulose in organic electrolyte solutions,” Chemical Communications, vol. 47, no. 1, pp. 511–513, 2011.

A. R. Xu, Y. J. Zhang, Y. Zhao, and J. J. Wang, “Cellulose dissolution at ambient temperature: role of preferential solvation of cations of ionic liquids by a cosolvent,” Carbohydrate Polymers, vol. 92, no. 1, pp. 540–544, 2013.

Y. L. Zhao, X. M. Liu, J. J. Wang, and S. J. Zhang, “Insight into co-solvent effect on cellulose dissolution in imidazolium-based ionic liquid solvent systems,” Journal of Physical Chemistry B, vol. 117, no. 30, pp. 9042–9049, 2013.

J. Vitz, T. Erdmenger, C. Haensch, and U. S. Schubert, “Extended dissolution studies of cellulose in imidazolium based ionic liquids,” Green Chemistry, vol. 11, no. 3, pp. 417–424, 2009.

A. Xu, Y. Zhang, Z. Li, and J. Wang, “Viscosities and conductivities of 1-butyl-3-methylimidazolium carboxylates ionic liquids at different temperatures,” Journal of Chemical & Engineering Data, vol. 57, no. 11, pp. 3102–3108, 2012.