The realisation of high quality silicon-germanium-on-insulator (SGOI) is a major goal for the field of silicon photonics because it has the potential to enable extremely low power active devices functioning at the communication wavelengths of 1.3 μm and 1.55 μm. In addition, SGOI has the potential to form faster electronic devices such as BiCMOS transistors and could also form the backbone of a new silicon photonics platform that extends into the mid-IR wavelengths for applications in, amongst others, sensing and telecoms. In this paper, we present a novel method of forming single crystal, defect-free SGOI using a rapid melt growth technique. We use tailored structures to form localised uniform composition SGOI strips, which are suitable for the state-of-the-art device fabrication. This technique could pave the way for the seamless integration of electronic and photonic devices using only a single, low cost Ge deposition step.
1. Introduction
Silicon-germanium (Si1-xGex) is a well-established material in the photonics and electronics industries. It is fully miscible across its entire composition range, therefore enabling the tuning of properties such as the lattice constant [1] and band gap [2], between those of bulk Ge and bulk Si. SiGe alloys can therefore be either optically transparent or optically absorbing at telecoms wavelengths (1.3 μm and 1.55 μm), depending on its composition. This results in the potential for the fabrication of active optical devices for both modulation [3, 4] and detection [5–7]. Additionally, SiGe also has a higher electron mobility and higher hole mobility relative to Si [8], potentially leading to faster electronic devices such as bipolar complementary metal-oxide semiconductor (BiCMOS) transistors [9, 10]. Tuning of the SiGe lattice constant also enables lattice matching for epitaxial III–V growth [11–13].
Conventional methods of growing SiGe directly on Si include reduced pressure chemical vapour deposition (RPCVD) [14], low energy plasma enhanced chemical vapour deposition (LEPECVD) [15], and molecular beam epitaxy (MBE) [16]. However, due to the 4.2% lattice mismatch between Si and Ge, these methods inevitably introduce high defect densities at the growth interface.
An alternative method of growing SiGe, this time on a localised insulator, is rapid melt growth (RMG). This technique was invented in the 1960s [17] and further developed in the 1970s for the fabrication of LEDs [18], detectors [19], and laser diodes [20]. Originally used for III–V crystal growth, RMG was pioneered by Liu et al. [21] for localised germanium-on-insulator (GOI) growth in 2004. Since then, it has been studied by various groups [22–27] and adapted for silicon-germanium-on-insulator (SGOI) growth [28–37].
A localised SGOI platform paves the way for the monolithic integration of electronic devices with photonic devices on Si substrates, providing a complementary solution to the silicon-on-insulator (SOI) substrates generally used for photonic devices [38]. Process flexibility, CMOS compatibility, and cost are all reasons why the migration of silicon photonic devices to Si substrates is of major interest. The use of dielectric optical waveguides [39], with localised buried SiO2 layers for optical confinement, can enable such a platform. Alternative techniques for fabricating localised SGOI include Ge condensation [40] and layer transfer using a donor wafer [41].
The RMG technique relies on the fact that Si has a higher melting point than Ge (1414°C and 938°C, resp. [42]). This means that, at temperatures greater than 938°C, the Ge is melted whilst the Si remains solid, maintaining its crystal structure, so that it can act as a template for the recrystallisation of the liquid Ge. Due to the nature of the lateral regrowth upon an insulator, extremely low threading dislocation densities (TDD) can be achieved, potentially leading to improved device characteristics. Additionally, during the melting phase, Si diffuses from the seed into the Ge layer, leading to the formation of SiGe layers from an initial Ge deposition. This deposition is noncritical since it will subsequently be melted to initiate regrowth. Therefore, fabrication complexity is significantly reduced, since the initial Ge deposition does not need to be modified to achieve a different SiGe composition and can be performed using any low cost technique.
However, until now, this RMG technique has resulted in graded SiGe composition profiles or only very high Ge composition uniform areas. In this paper, we firstly describe the RMG fabrication process and subsequently present a novel method for realising uniform composition, tuneable localised SGOI layers, demonstrating a large range of SiGe compositions.
2. Materials and Methods
Fabrication was carried out on 6-inch (100) Si wafers. Firstly, a 50 nm SiO2 insulating layer is deposited using plasma enhanced chemical vapour deposition (PECVD), upon which the lateral regrowth occurs. Alternatively, a Si3N4 layer can be used. The layer thickness can also be varied to satisfy the design requirements. This layer was subsequently densified in a rapid thermal annealer (RTA) to reduce the amount of trapped hydrogen in the SiO2 film. This prevents outgassing during subsequent annealing steps, which could lead to void formation in the SiGe as it recrystallises. Seed areas are then formed into this insulating layer using a dilute (20 : 1) HF wet etch in order to expose the underlying Si, which acts as a template for the SiGe recrystallisation process. Next, nonselective 400 nm Ge growth was performed by PECVD using GeH4 (10%) diluted in H2 (2.5 sccm) and H2 (100 sccm), at a temperature of 250°C. More details of this Ge growth can be found in [36]. Prior to Ge growth, an HF dip was performed to remove the native SiO2 layer formed on the Si surface and also to terminate the dangling bonds at the Si surface with H, preventing the formation of a native SiO2 during transfer to the Ge growth chamber. This HF last approach eliminates the need for a high temperature prebake (to remove the native SiO2) prior to epitaxial Ge growth [45]. Figure 1 shows a cross section scanning electron microscope (SEM) image at the seed edge after the Ge growth, confirming nonselective growth.
Cross section SEM image of Ge growth at the seed edge.
The Ge was then inductively coupled plasma (ICP) etched into the desired structures, ensuring that one end of the Ge pattern overlapped with the Si seed area. A 1 μm SiO2 layer was then deposited by PECVD to encapsulate the Ge structures to contain the liquid Ge during subsequent melting in an RTA. In this melting step, the temperature of the RTA was stabilised at approximately 500°C, before ramping up to the peak temperature at a rate of approximately 100°C/s. The temperature was held at its peak for 1 second, before cooling naturally (i.e., switching off the RTA lamps).
2.1. Regrowth Mechanism
When the temperature is raised above the melting point of Ge, Si diffusion from the seed is greatly enhanced [46], leading to the formation of a SiGe liquid. Upon cooling, regrowth is then initiated at the Si seed, firstly because the substrate acts as a heat sink and secondly because the slightly higher Si composition in the seed area results in solidification at a slightly higher temperature, as defined by the SiGe phase diagram shown in Figure 2. Epitaxial regrowth then propagates laterally along the SiGe structure. It has been shown that all threading dislocations are confined to the seed area by a defect necking mechanism, as shown in [36].
SiGe phase diagram, adapted from [43].
2.2. Material Characterisation
The SiGe material has been characterised using 532 nm Raman spectroscopy to determine its composition. Raman spectroscopy is a nondestructive, microscale technique, which does not require any sample preparation, and is commonly used for this type of analysis [23, 47–49]. A 50x objective lens was used, resulting in a laser spot size of approximately 0.5 μm. The data gathered by this technique relates to the near-surface information only because a laser of this wavelength has a penetration depth of several tens of nanometers in high Ge percentage SiGe (depending on the composition [50]). It is therefore possible that there is a nonuniform vertical distribution of Ge. However, this is predicted to be negligible [33], especially in areas away from the seed, since the epitaxial regrowth front propagates laterally.
Lateral scans were performed along each structure, resulting in a series of Raman spectra, each of which can be analysed to determine the SiGe composition at that point. Two characteristic peaks can be seen in each spectrum: the first at a wavenumber between 280 cm−1 and 300 cm−1, corresponding to the GeGe mode vibrations, and the second at a wavenumber between 390 cm−1 and 410 cm−1, corresponding to the SiGe mode vibrations. The wavenumber of each mode depends on the composition of the measured material, which therefore enables the composition to be determined using the peak location [48, 51]. Shin et al. [51] showed that the unstrained GeGe Raman peak location, ωGeGe, can be calculated by (1)ωGeGe=280.8+19.37x,where x is the Ge concentration. However, this type of measurement is complicated by the fact that the peak location also depends on strain [52–54]. In fact, an in-plane strain of 1% will induce a peak shift of approximately 3.85 cm−1 [52]. Nevertheless, as proposed by Mooney et al. [47] (2), the composition can be determined using the relative intensities of the SiGe and GeGe peaks, independently of the strain:(2)ISiGeIGeGe=21-xkx,where I(SiGe) and I(GeGe) are the integrated intensities of the SiGe and GeGe modes, respectively, x is the Ge concentration, and k, which is dependent on the excitation wavelength, is an experimental setup specific constant that can be determined from samples of known composition. Using this particular setup, k was determined to be 1.2.
3. Results and Discussion3.1. Composition Profiles of Straight Strips
After RMG was performed, the encapsulating SiO2 was removed in 20 : 1 HF acid to enable SEM viewing of the SiGe structures. Figure 3 shows an array of strip widths, each with a length of 200 μm.
SEM image of RMG straight strips showing agglomeration at large strip widths.
From this image, it is evident that there is a maximum strip width, above which RMG becomes unstable. Closer inspection reveals the maximum width to be approximately 5 μm, using the fabrication process described above. The liquid SiGe agglomerates at widths greater than 5 μm, possibly due to the high interface energy between SiO2 and SiGe [25], resulting in dewetting of the SiO2 surface when the SiGe is in the liquid phase. Agglomeration is suppressed at strip widths less than 5 μm, so only strips with a width of 5 μm or less are investigated in detail.
Figure 4(a) shows the composition profile as a function of distance from the Si seed for a variety of strip lengths. The annealing temperature of the SiGe has been estimated from the SiGe phase diagram to be 1008°C, based on the lowest observed Ge composition.
SiGe composition profiles for a range of straight strip lengths: (a) as a function of distance from the seed and (b) normalised by dividing the distance from the seed by the total strip length. Strip width = 5 μm. Estimated maximum SiGe temperature = 1008°C. The strips have been fitted with the complete mixing model [33].
From Figure 4(a), it can be observed that the composition varies in the straight strips, from lower Ge composition at the seed to 100% Ge at the distal end of the strip. The composition profile is independent of length (for this range of lengths), which can be seen in Figure 4(b), where the strip length has been normalised by dividing each point by the total length of each respective strip. This graded composition profile is a result of the large separation between the solidus and liquidus curves of the SiGe phase diagram (Figure 2), which therefore results in preferential Si rich solid formation at the regrowth front, with rejection of Ge into the liquid. The complete mixing model [33], based on analysis originally carried out by Scheil [55], has been added to each curve and is described in the following.
3.2. Segregation Coefficient
The segregation coefficient, k, of a SiGe alloy defines the degree of segregation between Ge and Si. It is defined as the ratio of the Ge solid composition, CS, to the Ge liquid composition, CL, at any particular temperature:(3)k=CSCL.k can be calculated from the SiGe phase diagram, as shown in Figure 5(a). This is then plotted as a function of the solid Ge composition in Figure 5(b).
SiGe segregation coefficient. (a) Calculating the segregation coefficient from the phase diagram and (b) SiGe segregation coefficient as a function of Ge composition. A linear fit has been applied between Ge compositions of 0.4 and 1.0.
As the Ge composition approaches 100% Ge, the segregation coefficient approaches unity. On the contrary, as the Ge composition decreases, there is a higher degree of segregation. A simple linear fit has been applied between Ge compositions of 0.4 and 1.0, leading to (4) for the segregation coefficient as a function of the Ge solid composition, CS:(4)k=CSCL=0.78CS+0.21.In this paper, no Ge compositions lower than 0.4 have been measured, therefore deeming this approximation valid.
3.3. Scheil Equation
The simplest model of binary alloy solidification is possibly the Scheil equation [55]:(5)CS=kC01-fSk-1,where fS is the fraction of the strip that has solidified and C0 is the average Ge composition in the liquid at the point when solidification commences. The Scheil equation makes 3 assumptions:
There is complete mixing of Ge and Si in the melt, resulting in a uniform composition.
There is no diffusion in the solid.
k is constant. This is only valid if the phase diagram is simplified to become straight lines, which is approximately true for small composition ranges.
The segregation coefficient (3) determines the solid composition to commence at kC0, since the liquid is at a uniform composition of C0. The fact that the Scheil equation assumes complete mixing in the melt means that it is only accurate when the regrowth front propagation speed is slow, therefore providing enough time for the rejected Ge at the regrowth front to fully diffuse into the melt.
3.4. Complete Mixing Model
A more complete version of the Scheil equation is the complete mixing model [33]. This model does not assume a constant value of k. Assumptions (1) and (2) (listed above) still remain valid. In this paper, the simplified linear equation for the segregation coefficient (4) has been used.
To derive the complete mixing model, we must consider a small progression of the regrowth front, as shown in Figure 6.
Diagram showing the derivation of the complete mixing model.
Here, the solid line shows the composition profile at any given point in time, with the solid composition on the left-hand side and the liquid composition on the right-hand side. The dashed line shows the composition profile after a small progression of the regrowth front, df. Ge is rejected from the solid into the liquid at the regrowth front. Therefore, conservation of mass enables equating the amount of Ge in the two hashed areas:(6)CL-CSdf=1-fSdCL.The segregation coefficient, k, can then be used to replace CS. Rearranging (4) gives(7)CS=0.21CL1-0.78CL.Substituting (7) into (6) and integrating both sides result in (8)1-fS=CseedCS1/0.790.79-0.78CS0.79-0.78Cseed0.21/0.790.78CS+0.210.78Cseed+0.21,where Cseed is the solid composition at the edge of the seed. This is the complete mixing model, valid for Ge compositions between 0.4 and 1.0. The full derivation of the complete mixing model can be found in Appendix D of [56]. This equation is also only valid when the regrowth front propagation speed is low because of the assumption that the melt has a uniform composition (i.e., complete mixing of the rejected Ge into the melt). In addition, this equation is also valid when the distance left to solidify is low (i.e., a few microns), since complete mixing can still occur.
Figure 4 shows that the complete mixing model is a close match to the measured data, suggesting that, for straight strips of these lengths (<100 μm), the regrowth front propagation speed is slow enough to enable complete mixing of the rejected Ge into the melt.
However, for the fabrication of the state-of-the-art devices using this material, it is essential to form uniform composition areas of SGOI. This can be achieved by steady-state solidification, whereby Ge diffusion into the melt is dramatically reduced by increasing the regrowth front propagation speed.
3.5. Steady-State Solidification
In steady-state solidification, there is limited Ge diffusion into the melt. When the regrowth front propagation speed is nonnegligible, this is a more accurate model than both the Scheil equation and the complete mixing model. Here, diffusion of the rejected Ge at the regrowth front is balanced by the propagation of the regrowth front, therefore resulting in a uniform composition profile. Diffusion of Ge is given by Fick’s second law:(9)dCSdt=DLd2CSdx2.Also,(10)dCSdt=dCSdxdxdt=vdCSdx,where v is the regrowth front propagation speed, DL is the diffusivity of Ge in liquid SiGe, and x is the length in the liquid with a nonuniform composition. This equation assumes a constant regrowth propagation speed. These equations combine to give (11)DLd2CSdx2-vdCSdx=0.This is a second-order differential equation. Therefore, the solution is of the following form:(12)CS=αeβx+γ.The first- and second-order differentials of this equation are(13)dCSdx=βαeβx,d2CSdx2=β2αeβx.Substituting these two equations into (11) gives (note the change in sign since Ge diffusion and regrowth are in the same direction)(14)DLβ2αeβx+vβαeβx=0,which simplifies to(15)β=-vDL.Substituting this into the general solution of a second-order differential equation results in (16)CS=αe-x/DL/v+γ.The boundary conditions for this equation are CS=C0 when x=∞ and CS=CL when x=0. Substituting the boundary conditions into (16) results in(17)γ=C0.And, therefore,(18)α=CL-C0.Substituting these back into (16),(19)CS=C0+CL-C0e-x/DL/v,which becomes(20)CS=C0+C01-kke-x/DL/v.This is the steady-state equation for alloy solidification, which is detailed in Figure 7.
In steady-state solidification, the regrowth front propagation speed is faster than that in the complete mixing model. Therefore, as the Ge is rejected from the solid at the regrowth front, there is insufficient time for it to fully diffuse into the bulk melt. This results in an initial build-up of a Ge “bow” (Figure 7(a)) at the regrowth front as solidification commences, followed by a steady-state period once the solid Ge composition reaches C0 (Figure 7(b)). At this point, the propagating regrowth front effectively sees the same Ge composition in the melt directly ahead of it, independent of the distance from the seed, and therefore a uniform composition is achieved. However, at the distal end of the structure, when x becomes small, completed diffusion is realised and the composition profile follows the complete mixing model.
Steady-state solidification composition profiles can be predicted using the University of Cambridge website “Dissemination of IT for the Promotion of Materials Science” [44] simulation software. Figure 8 shows the predicted composition profile as the regrowth front propagation speed is increased from Figures 8(a)–8(c).
Simulations of Ge composition profiles formed by steady-state solidification using the University of Cambridge software [44] showing increasing regrowth front propagation speed from (a) to (c).
These simulations demonstrate that increasing the regrowth front propagation speed results in a flatter composition profile because the diffusion of the rejected Ge into the melt at the regrowth front is balanced by the propagation of the regrowth front itself.
It is therefore necessary to maximise the regrowth front propagation speed to achieve a uniform composition profile. This can be realised by maximising the cooling rate of the SiGe structures after melting [57]. This cannot be accomplished by altering the RTA cooling process since the lamps are already switched off immediately after heating. Therefore, it is necessary to increase the cooling rate by other means.
3.6. SiGe Composition Profiles of Tailored Structures
In order to realise a uniform SiGe composition, a tailored tree-like structure was designed, as shown in Figure 9. Branches were added to the main central strip, which act as radiating elements with the purpose of increasing the cooling rate and therefore the regrowth front propagation speed of the structure.
SEM image of a tailored tree-like structure. Dimensions are defined as follows: centre strip length CL, centre strip width CW, branch length BL, branch width BW, branch separation BS, and number of branches n.
The composition profile of the complete tree-like structure is shown in Figure 10.
SiGe composition profile of a tailored tree-like structure. (a) Graph and (b) schematic. CW = 3 μm, CL = 65 μm, BW = 5 μm, BL = 20 μm, and BS = 3 μm. The final set of branches have been omitted to display only the uniform composition region. Estimated maximum SiGe temperature = 975°C. A linear fit has been added to the central strip.
Figure 10 shows that a uniform composition has been achieved in the central strip of a tree-like structure, when the central strip width is 3 μm. Only the uniform composition area (first 56 μm, corresponding to 7 out of 8 sets of branches) has been shown. After the first 56 μm (penultimate set of branches), the cooling effects of the branches are reduced, and the length of strip left to solidify becomes small, resulting in a nonuniform SiGe composition profile. Each branch exhibits a graded composition profile, suggesting that the central strip solidifies first and then subsequently acts as a seed for the regrowth of the branches.
Figure 11 compares the composition profile of the central strip of a tree-like structure with a straight strip with the same dimensions.
Comparison of SiGe composition profiles of the central strip of a tailored tree-like structure and a straight strip. (a) Graph and (b) schematic. The final set of branches have been omitted from the central strip of the tailored tree-like structure to display only the uniform composition region. The straight strip data has been normalised from Figure 4 to match the length of the tailored tree-like structure. The complete mixing model has been fitted to the straight strip data [33]. A linear fit has been added to the tailored tree-like structure data.
3.7. SiGe Composition Tuning by Annealing Temperature
It is desirable to be able to tune the SiGe composition in the central strip, without the need to alter the initial Ge growth conditions, so that this RMG technique can be used for a whole range of device designs. This can be achieved simply by modifying the annealing temperature, according to the phase diagram, as shown in Figure 12.
SiGe composition tuning by varying the RMG annealing temperature. (a) Composition profiles in the central strips of tailored tree-like structures annealed at a range of temperatures. A linear fit has been added to each data set and (b) average Ge composition along the central strip of a tailored tree-like structure as a function of annealing temperature. Only the uniform region up to 56 μm has been considered. The error bars show the maximum and minimum values observed along each strip. CW = 3 μm, CL = 65 μm, BL = 20 μm, BW = 5 μm, and BS = 3 μm.
Figure 12(a) shows that a uniform composition is realised for all the demonstrated annealing temperatures. A higher annealing temperature results in greater Si diffusion into the structure before solidification commences and therefore leads to a lower Ge composition upon solidification. This is demonstrated in Figure 12(b), where the average Ge composition in the central strip of the tree-like structures has been plotted as a function of annealing temperature.
3.8. Material Quality Analysis
Transmission electron microscopy (TEM) has been performed to image a cross section of the central strip of a SiGe tree-like structure. Figure 13 confirms single crystal, defect-free SGOI fabrication using this RMG method.
High resolution cross section TEM image of RMG SiGe in the central strip of a tree-like structure.
Electron backscatter diffraction (EBSD) measurements were also performed to measure the crystal orientation of the RMG SiGe. Figure 14 shows a pole figure of an area approximately 3 μm × 3 μm. The observed data confirms single crystal (001) orientated SiGe, matching the crystal orientation of the Si substrate, as expected.
Pole figure of RMG SiGe measured by EBSD. The measured area was approximately 3 μm × 3 μm.
A more detailed material quality analysis can be found in [36].
4. Conclusion
In conclusion, the rapid melt growth technique described here presents a fabrication process for producing localised single crystal SiGe layers of uniform composition, suitable for the state-of-the-art device fabrication. This method enables the simple tuning of the SiGe composition, without the need to alter the initial growth conditions, and uses low cost, readily available CMOS fabrication tools. It offers the potential for the migration of silicon photonics to bulk Si substrates, enabling the coexistence of SiGe photonic and electronic devices on the same chip.
Competing Interests
The authors declare that they have no competing interests.
Acknowledgments
The research leading to these results was funded by the UK Engineering and Physical Sciences Research Council (EPSRC) under the grant “HERMES” and is also supported by the National Research Foundation of Singapore (NRF-CRP12-2013-04). The fabrication was carried out at the Southampton Nano Centre, University of Southampton, UK. The data in this paper can be accessed at 10.5258/SOTON/393034.
DismukesJ. P.EkstromL.PaffR. J.Lattice parameter and density in germanium-silicon alloys196468103021302710.1021/j100792a0492-s2.0-0042054706BraunsteinR.MooreA. R.HermanF.Intrinsic optical absorption in germanium-silicon alloys1958109369571010.1103/PhysRev.109.6952-s2.0-36149024990LiuJ.BealsM.PomereneA.BernardisS.SunR.ChengJ.KimerlingL. C.MichelJ.Waveguide-integrated, ultralow-energy GeSi electro-absorption modulators20082743343710.1038/nphoton.2008.992-s2.0-46349093650LuoY.ZhengX.LiG.ShubinI.ThackerH.YaoJ.LeeJ.-H.FengD.FongJ.KungC.-C.LiaoS.ShafiihaR.AsghariM.RajK.KrishnamoorthyA. V.CunninghamJ. E.Strong electro-absorption in GeSi epitaxy on silicon-on-insulator (SOI)20123234536310.3390/mi30203452-s2.0-84866724297ChaisakulP.Marris-MoriniD.FrigerioJ.ChrastinaD.RouifedM.-S.CecchiS.CrozatP.IsellaG.VivienL.Integrated germanium optical interconnects on silicon substrates20148648248810.1038/nphoton.2014.732-s2.0-84901692561LittlejohnsC. G.HuY.GardesF. Y.ThomsonD. J.ReynoldsS. A.MashanovichG. Z.ReedG. T.50 Gb/s silicon photonics receiver with low insertion loss201426771471710.1109/LPT.2014.23035782-s2.0-84897868700LittlejohnsC. G.KhokharA. Z.ThomsonD. J.HuY.BassetL.ReynoldsS. A.MashanovichG. Z.ReedG. T.GardesF. Y.Ge-on-Si plasma-enhanced chemical vapor deposition for low-cost photodetectors20157410.1109/jphot.2015.24560692-s2.0-84938251126FischettiM. V.LauxS. E.Band structure, deformation potentials, and carrier mobility in strained Si Ge, and SiGe alloys19968042234225210.1063/1.3630522-s2.0-0001038893ThomsonD. J.PorteH.GollB.KnollD.LischkeS.GardesF. Y.HuY.ReedG. T.ZimmermannH.ZimmermannL.Silicon carrier depletion modulator with 10 Gbit/s driver realized in high-performance photonic BiCMOS20148118018710.1002/lpor.2013001162-s2.0-84891823528ZimmermannL.High-performance photonic BiCMOS—next generation more-than-Moore technology for the large bandwidth era2014641318BakkersE. P. A. M.van DamJ. A.De FranceschiS.KouwenhovenL. P.KaiserM.VerheijenM.WondergemH.van der SluisP.Epitaxial growth of InP nanowires on germanium200431176977310.1038/nmat12352-s2.0-16544366658LiuH.WangT.JiangQ.HoggR.TutuF.PozziF.SeedsA.Long-wavelength InAs/GaAs quantum-dot laser diode monolithically grown on Ge substrate20115741641910.1038/nphoton.2011.1202-s2.0-79959861999LeeA. D.JiangQ.TangM.ZhangY.SeedsA. J.LiuH.InAs/GaAs quantum-dot lasers monolithically grown on Si, Ge, and Ge-on-Si substrates2013194, article 190110710.1109/jstqe.2013.22479792-s2.0-84877870957HikavyyA. Y.RosseelE.DhayalanS. K.(Invited) high Ge content SiGe thin films: growth, properties and integration201464683183910.1149/06406.0831ecstRosenbladC.Von KänelH.KummerM.DommannA.MüllerE.A plasma process for ultrafast deposition of SiGe graded buffer layers200076442742910.1063/1.1257762-s2.0-0001445067BurleN.EscoubasS.KasperE.WernerJ.OehmeM.LyutovichK.X-ray imaging and diffraction study of strain relaxation in MBE grown SiGe/Si layers2013101525510.1002/pssc.2012005442-s2.0-84872969499NelsonH.Epitaxial growth from the liquid state and its application to the fabrication of tunnel and laser diodes196324603615SaulR. H.RoccaseccaD. D.Vapor‐doped multislice LPE for efficient GaP green LED's197312081128113110.1149/1.24036442-s2.0-0015656768WiederH. H.ClawsonA. R.McWilliamsG. E.InxGa1−xAsyP1−y/InP heterojunction photodiodes197731468470PanishM. B.HayashiI.SumskiS.Double-heterostructure injection lasers with room-temperature thresholds as low AS 2300 A/SQ CM2197016832632710.1063/1.16532132-s2.0-0014770844LiuY.DealM. D.PlummerJ. D.High-quality single-crystal Ge on insulator by liquid-phase epitaxy on Si substrates200484142563256510.1063/1.16911752-s2.0-2342592574TweetD. J.LeeJ. J.MaaJ.-S.HsuS. T.Characterization and reduction of twist in Ge on insulator produced by localized liquid phase epitaxy20058714314190810.1063/1.20778602-s2.0-28344434845MiyaoM.TanakaT.TokoK.TanakaM.Giant Ge-on-insulator formation by Si-Ge mixing-triggered liquid-phase epitaxy20092404550310.1143/APEX.2.0455032-s2.0-64749097793MiyaoM.TokoK.TanakaT.SadohT.High-quality single-crystal Ge stripes on quartz substrate by rapid-melting-growth2009952302211510.1063/1.31827952-s2.0-67650714654HashimotoT.YoshimotoC.HosoiT.ShimuraT.WatanabeH.Fabrication of local ge-on-insulator structures by lateral liquid-phase epitaxy: effect of controlling interface energy between ge and insulators on lateral epitaxial growth20092606650210.1143/apex.2.0665022-s2.0-67949089744SakaneT.TokoK.TanakaT.SadohT.MiyaoM.Strained single-crystal GOI (Ge on Insulator) arrays by rapid-melting growth from Si (1 1 1) micro-seeds2011601222510.1016/j.sse.2011.01.0372-s2.0-79955524106TokoK.OhtaY.SakaneT.SadohT.MizushimaI.MiyaoM.Single-crystalline (100) Ge networks on insulators by rapid-melting growth along hexagonal mesh-pattern201198404210110.1063/1.35440572-s2.0-79551643323TanakaT.TokoK.SadohT.MiyaoM.High quality single-crystalline Ge-rich SiGe on insulator structures by Si-doping controlled rapid melting growth20103303130110.1143/APEX.3.0313012-s2.0-77949787226KohH. Y. S.2011Stanford, Calif, USADepartment of Electrical Engineering, Stanford UniversityMatsumuraR.TojoY.KurosawaM.SadohT.MizushimaI.MiyaoM.Growth-rate-dependent laterally graded SiGe profiles on insulator by cooling-rate controlled rapid-melting-growth20121012424190410.1063/1.47699982-s2.0-84871292047ArmourN.2012Victoria, CanadaDepartment of Mechanical Engineering, University of VictoriaTojoY.MatsumuraR.YokoyamaH.KurosawaM.TokoK.SadohT.MiyaoM.High-quality formation of multiply stacked SiGe-on-insulator structures by temperature-modulated successive rapid-melting-growth2013102909210210.1063/1.47944092-s2.0-84875186017BaiX.ChenC.-Y.GriffinP. B.PlummerJ. D.Si incorporation from the seed into Ge stripes crystallized using rapid melt growth2014104505210410.1063/1.48639762-s2.0-84899837778LittlejohnsC. G.NedeljkovicM.MashanovichG. Z.ReedG. T.GardesF. Y.Silicon-germanium composition engineering for next generation multilayer devices and systemsProceedings of the 11th International Conference on Group IV Photonics (GFP '14)August 2014Paris, France1210.1109/group4.2014.69620552-s2.0-84914159969LittlejohnsC. G.GardesF. Y.NedeljkovicM.MashanovichG. Z.ReedG. T.Silicon diffusion engineering in rapid melt growth of silicon-germanium on insulator201464615515710.1149/06406.0155ecstLittlejohnsC. G.NedeljkovicM.MallinsonC. F.WattsJ. F.MashanovichG. Z.ReedG. T.GardesF. Y.Next generation device grade silicon-germanium on insulator20155, article 828810.1038/srep08288LittlejohnsC. G.Dominguez BucioT.NedeljkovicM.Towards a fully functional integrated photonic-electronic platform via a single SiGe growth step201661942510.1038/srep19425ThomsonD. J.LittlejohnsC. G.StankovicS.NedeljkovicM.ReynoldsS. A.2015John Wiley & SonsGardesF. Y.Bucio DominguezT.LittlejohnsC. G.ReedG.DebnathK.O'FaolainL.Group IV functionalization of low index waveguidesProceedings of the 16th Photonics North ConferenceMay 2014Montréal, CanadaTezukaT.SugiyamaN.MizunoT.SuzukiM.TakagiS.-I.A novel fabrication technique of ultrathin and relaxed SiGe buffer layers with high Ge fraction for sub-100 nm strained silicon-on-insulator MOSFETs20014042866287410.1143/jjap.40.28662-s2.0-0035300641TaraschiG.PiteraA. J.FitzgeraldE. A.Strained Si, SiGe, and Ge on-insulator: review of wafer bonding fabrication techniques20044881297130510.1016/j.sse.2004.01.0122-s2.0-2342563124SzeS. M.20012ndNew York, NY, USAWileyOlesinskiR. W.AbbaschianG. J.The Ge−Si (Germanium-Silicon) system19845218018310.1007/bf028689572-s2.0-52449147835University-of-Cambridge2014http://www.doitpoms.ac.uk/HarameD. L.MeyersonB. S.The early history of IBM's SiGe mixed signal technology200148112555256710.1109/16.9603832-s2.0-0035507071PavlovP. V.DobrokhotovE. V.Self-diffusion in liquid germanium197012225226MooneyP. M.DacolF. H.TsangJ. C.ChuJ. O.Raman scattering analysis of relaxed GexSi1-x alloy layers199362172069207110.1063/1.1094812-s2.0-0001439097PagèsO.SouhabiJ.TorresV. J. B.PostnikovA. V.RustagiK. C.Re-examination of the SiGe Raman spectra: percolation/one-dimensional-cluster scheme and ab initio calculations201286404520110.1103/physrevb.86.0452012-s2.0-84863659617PerovaT. S.WasylukJ.LyutovichK.KasperE.OehmeM.RodeK.WaldronA.Composition and strain in thin Si1−xGex virtual substrates measured by micro-Raman spectroscopy and x-ray diffraction20111093033502HumlíčekJ.GarrigaM.AlonsoM. I.CardonaM.Optical spectra of SixGe1−x alloys19896572827283210.1063/1.3427202-s2.0-21544466317ShinH. K.LockwoodD. J.BaribeauJ.-M.Strain in coherent-wave SiGe/Si superlattices20001141050551010.1016/s0038-1098(00)00111-32-s2.0-0033905222TsangJ. C.MooneyP. M.DacolF.ChuJ. O.Measurements of alloy composition and strain in thin GexSi1-x layers199475128098810810.1063/1.3565542-s2.0-22844432802GroenenJ.CarlesR.ChristiansenS.AlbrechtM.DorschW.StrunkH. P.WawraH.WagnerG.Phonons as probes in self-organized SiGe islands199771263856385810.1063/1.1205252-s2.0-4244193712PengC.-Y.HuangC.-F.FuY.-C.YangY.-H.LaiC.-Y.ChangS.-T.LiuC. W.Comprehensive study of the Raman shifts of strained silicon and germanium2009105808353710.1063/1.31101842-s2.0-65449163369ScheilE.Bemerkungen zur schichtkristallbildung1942347072LittlejohnsC. G.2015Optoelectronics Research Centre, University of SouthamptonJonesH.1983London, UKInstitution of Metallurgists