Advances in Materials Science and Engineering
Volume 2016 (2016), Article ID 7372132, 14 pages
http://dx.doi.org/10.1155/2016/7372132

Research Article

Optimizing Cutting Conditions for Minimum Surface Roughness in Face Milling of High Strength Steel Using Carbide Inserts

Adel Taha Abbas,¹ Adham Ezzat Ragab,² Essam Ali Al Bahkali,¹ and Ehab Adel El Danaf¹

¹Department of Mechanical Engineering, College of Engineering, King Saud University, P.O. Box 800, Riyadh 11421, Saudi Arabia
²Department of Industrial Engineering, College of Engineering, King Saud University, P.O. Box 800, Riyadh 11421, Saudi Arabia

Received 7 December 2015; Revised 3 March 2016; Accepted 6 March 2016

Academic Editor: Fernando Lusquiños

Copyright © 2016 Adel Taha Abbas et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

A full factorial design technique is used to investigate the effect of machining parameters, namely, spindle speed , depth of cut and table feed rate on the obtained surface roughness ( and ) during face milling operation of high strength steel. A second-order regression model was built using least squares method depending on the factorial design results to approximate a mathematical relationship between the surface roughness and the studied process parameters. Analysis of variance was conducted to estimate the significance of each factor and interaction with respect to the surface roughness. For , the results show that spindle speed, depth of cut, and table feed rate have a significant effect on the surface roughness in both linear and quadratic terms. There is also an interaction between depth of cut and feed rate. It also appears that feed rate has the greatest effect on the data variation followed by depth of cut. For , the results show that the table feed rate is the most effective factor followed by the depth of cut, while the spindle speed had a significant small effect only in its quadratic term. The conditions of minimum and are identified through least square optimization. Moreover, multiobjective optimization for minimizing and maximizing metal removal rate is conducted and the results are presented.

1. Introduction

Increasing product quality, delivery time, and productivity of the machined parts are the main challenges of metal-based industry. There has been increased interest in optimizing machining conditions to satisfy manufacturing requirements including the most prominent one, which is surface finish. Surface quality is considered as one of the most important criteria in manufacturing engineering. The performance and quality of a product are directly associated with surface integrity achieved by final machining, which is reflected in having small tolerance and minimum surface roughness, . High productivity and throughput are directly correlated with high speed machining, which can be achieved by computer numerical controlled (CNC) milling technology. The automated and flexible manufacturing systems are employed for that purpose along with CNC machines that are capable of achieving high accuracy with very low processing time. Surface roughness is a key factor of surface quality, since it assumes an essential effect on wear resistance, ductility, tensile, and fatigue strength for machined parts.

Raju et al. [1] modeled and optimized the surface roughness in relation to the cutting parameters for 6061 aluminum alloy processed by end milling with high speed steel (HSS) and carbide tools under dry and wet conditions. A multiple regression analysis using analysis of variance was conducted and a second-order mathematical model of the cutting parameters was suggested. The predicted surface roughness from the model is compared to the values measured experimentally. It is reported, in this study, that feed rate is a dominant parameter and the surface roughness increases rapidly with increasing feed rate and decreases with increasing spindle speed, whereas the effect of depth of cut is not regular.

Pimenov [2] investigated the effect of feed, cutting speed, and tool wear of a T5K10 carbide tool on the roughness of flat surfaces, produced by face milling, of steel 45. The work analyzed the nature of the microprofile of changes in machined surfaces based on increasing the wear surface on the tooth flank. He showed that the roughness grew from 15 to 30% for the chosen cutting conditions with growth in the flank wear from 0 to 3.1–4 mm. The increase in feed at a constant cutting speed led to an increase in the roughness; however, increasing cutting speed at constant feed led to a decrease in roughness. It was shown that, with an increase in the flank wear on the flank surface, the frequency of peaks and troughs of the profilograms of the microprofile of machined surface was decreased.

Pusavec et al. [3] studied alternative cooling/lubrication conditions compared to conventional machining of Inconel 718 and its relation to chip breakability. Genetic algorithms (GA) were used to evaluate and optimize the machining process in terms of tool-life, machined surface quality, chip breakability, productivity, and power consumption.

Felho and Kundrak [4] introduced a new method to calculate both the profile (2D) and surface (3D) parameters of theoretical roughness in the face milling of plain surfaces. This new method was based on an expediently developed CAD model and used a professional program for the roughness evaluation. Cutting experiments were performed on 42CrMo4 specimens in order to validate the accuracy of the model. The results have revealed that the method was able to predict surface roughness with good accuracy.

Rawangwong et al. [5] conducted a study on the surface roughness of a semisolid AA 7075 machined by face milling, using CNC milling machine with 63-millimeter diameter fine type carbide tool with twin cutting edge. The process factors were the speed, feed rate, and depth of cut. The results showed that the factor affecting surface roughness was the ratio of feed rate to the cutting speed while the depth of cut had no effect.

Kivak [6] used analysis of variance (ANOVA), Taguchi method, and regression analysis to investigate the effects of the machining parameters on surface roughness and flank wear for milling of Hadfield steel with PVD TiAlN- and CVD TiCN/Al₂O₃-coated carbide inserts under dry milling conditions. Several experiments were conducted using full factorial design with a mixed orthogonal array on a CNC vertical machining center. The process variables were the cutting tool, cutting speed, and feed rate. It was concluded that the feed rate was the dominant factor affecting surface roughness, while cutting speed was the dominant factor affecting flank wear.

Rawangwong et al. [7] investigated the effect of main machining factors on the surface roughness of nodular cast iron FCD 400 face milled by carbide tools. The etching experiments were done using semiautomated milling machine Obraeci Strojie brand FGV 32 model. The factors studied were the speed, feed rate, and depth of cut. The experiments illustrated that the factors affecting surface roughness were feed rate and cutting speed with tendency for reduction of roughness values at lower feed rate and greater cutting speed.

Abbas [8] presented a performance comparative analysis, involving the criteria of surface roughness (, , and ) during high strength steel’s turning operation, between the conventional and wiper inserts. The main parameters considered in this study were the speed of cutting, the feed rate, and the depth of cut. The results showed the significance of cutting depth and feed rate in the reduction of surface roughness. It was reported that the quality of the surface derived with the wiper carbide insert had significant improvement in comparison to the conventional carbide insert. The maximum improvement of 3.5 times between the wiper insert and conventional insert was achieved at a cutting speed of 75 m/min.

The current work focuses on providing a comprehensive study on the effect of machining process parameters, namely, feed fate, cutting speed, and depth of cut, on the surface roughness, through a DOE full factorial design for face milling of high strength steel using carbide tools. Four levels for each process parameter are investigated. Analysis of variance (ANOVA) will be used to determine the effects of the machining parameters on surface roughness and to develop a mathematical model through regression analysis that best describes the variation within the experimental data.

2. Materials and Methods

This research study aims to investigate the effect of main factors on the surface roughness of high strength steel in face milling process using CNC milling machine and carbide inserts. Emco Mill Concept 45 CNC vertical milling machine equipped with Sinumeric 840-D with technical specifications including a speed range of 50–10,000 rpm and feed rate 0–10 m/min was used. Workpiece samples are high strength steel with the chemical composition shown in Table 1. The heat treatment given to the material involved austenitizing at 900°C for 5 hr, followed by air cooling, heating at 880°C for 5 hr, quenching in oil, tempering at 590–600°C for 8 hr, and then air cooling. The resulting hardness achieved was HRC 41–43. The surface area of each sample is  mm and height 60 mm. The cutting tool with carbide inserts model face mill with tool holder Sandvik R245-063Q22-12M and Sandvik carbide coated inserts R245-12 T3M-PM4240 was used. The diameter of the cutter is 63 mm with 5 edges. This type of milling cutter was designed for high metal removal and mirror surface finish. It is designed with enhanced corners to reduce burr formation and frittering of the component. This type of cutter is suitable for face milling applications in all types of materials such as steel, stainless steel, cast iron, aluminum, and heat resistant and titanium alloys. The test rig for machining workpieces is shown in Figure 1. The surface roughness measuring device for evaluating the surface topography is model TESA Rugosurf 90-G and is shown in Figure 2.

Table 1: Chemical composition for high strength steel material.

C
Si
Mn
Ni
Cr
Mo
V
S
Cu
P
Al
Fe

0.356
0.221
0.728
2.697
1.030
0.617
0.103
0.005
0.176
0.010
0.006
Balance

Figure 1: Test rig for machining the workpieces.

Figure 2: Test rig measuring the surface roughness.

The test plan was carried out through 64 test specimens, group (A), and repeated for producing replicates in group (B). Each group was divided into 16 groups. Every four groups are subjected to one common machining spindle speed. Groups 1–4, 5–8, 9–12, and 13–16 were processed using spindle speed machining of 500 rpm, 750 rpm, 1000 rpm, and 1250 rpm, respectively. Each group has been machined using four levels of cutting depth (0.25, 0.50, 0.75, and 1.0 mm) and each depth was processed using four levels of table feed rates (50, 75, 100, and 125 mm/min). To apply the above conditions, CNC milling machine equipped with Sinumeric 840-D was used. The surface roughness tester TESA was used to measure the surface roughness parameters, and , where is arithmetic average deviation of the assessed profile and is maximum height of the profile. The machined surfaces were duplicated for each set of cutting conditions. Three readings of surface roughness were measured on each surface and the average was recorded in the Appendix for groups (A) and (B).

3. Experimental Design

Full factorial design is a comprehensive technique that requires a large number of experiments and yields a detailed description of all system relations and interactions. In this research, full factorial design was used to build the experiment with three independent variables (factors) and four levels for each. Table 2 summarizes the variables and their levels. Analysis of variance (ANOVA) was conducted to test the significance of the factors and their interaction with a confidence level of 95%. Least squares method was used to build second-order multiple regression models. Minitab 17 was used to run the DOE analysis.

Table 2: The cutting parameters and their levels used in the factorial design experiment.

Designation
Process parameter
Level 1
Level 2
Level 3
Level 4

Spindle speed (rpm)
500
750
1000
1250

Depth of cut (mm)
0.25
0.50
0.75
1.00

Feed rate (mm/min)
50
75
100
125

4. Results and Discussion

Figures 3(a) and 3(b) represent the effect of table feed rate on for different depth of cuts at spindle speed 500 rpm in (a) and 1000 rpm in (b). Preliminary observation of these curves indicates that the surface roughness values () increase with increasing table feed rate for both rotational speeds. Comparing the effect of rotational speeds for two values of depth of cuts, of 1.0 and 0.25 mm, can be seen in Figure 4. For a depth of cut of 1.0 mm, the value of surface roughness () at spindle speed 1000 rpm is higher compared to the 500 rpm. Opposing conclusion can be made for the 0.25 mm depth of cut, where the value of is higher at spindle speed 500 rpm compared to the 1000 rpm. This draws towards the possibility of a saddle (minimax) point existing among the different machining conditions tested. This will be clearly verified in the surface plots presented in the next section. More detailed analysis will be conducted through analysis of variance in the following section.

(a)

(b)

Figure 3: The effect of table feed rate on for different depth of cuts (mm) at 500 rpm in (a) and 1000 rpm in (b).

Figure 4: Effect of table feed rate on for two values of depth of cut, of 1.0 and 0.25 mm, for two rotational spindle speeds of 500 and 1000 rpm.

4.1. ANOVA Results for

Using Minitab 17 multiple regression option, the data were fit into a cubic model. However, the results showed a high level of multicollinearity between the cubic terms (third-order terms) and linear terms, even with coded data. To avoid this problem, the cubic terms were removed from the model. The adequacy of the model fit, measured by the coefficient of determination (adjusted -squared), was reduced from 82% to 79% due to removing the cubic terms.

ANOVA results of the model are presented in Table 3. values less than 0.05 indicate a significant term. Insignificant terms were then removed from the model one by one starting with terms that have the greatest value, unless it is a part of higher level term or interaction (Zhang and Chou [9], Fydrych and Rogalski [10], and Ding et al. [11]). The ANOVA results of the reduced model are given in Table 4. The percentage contribution column is calculated for each term as the percentage of the term’s adjusted sum of squares to the total adjusted sum of squares. It provides a rough but effective estimation to the relative importance of each model term (Montgomery [12]).

Table 3: ANOVA for .

Source
DF
Adj. SS
Adj. MS
-value
value

Regression
10
0.476642
0.047664
47.92
0

1
0.005935
0.005935
5.97
0.016

1
0.102187
0.102187
102.74
0

1
0.317063
0.317063
318.79
0

1
0.01274
0.01274
12.81
0.001

1
0.017414
0.017414
17.51
0

1
0.011724
0.011724
11.79
0.001

1
0
0
0
0.999

1
0.002544
0.002544
2.56
0.112

1
0.00683
0.00683
6.87
0.01

1
0.000205
0.000205
0.21
0.65

Error
117
0.116365
0.000995

Lack-of-fit
53
0.116245
0.002193
1174.66
0

Pure error
64
0.000119
0.000002

Total
127
0.593006

Table 4: ANOVA for after removing insignificant terms.

Source
DF
Adj. SS
Adj. MS
-value
value
% contribution

Regression
7
0.473893
0.067699
68.2
0

1
0.005935
0.005935
5.98
0.016
10.0

1
0.102187
0.102187
102.95
0
17.2

1
0.317063
0.317063
319.42
0
53.5

1
0.01274
0.01274
12.83
0
2.1

1
0.017414
0.017414
17.54
0
2.9

1
0.011724
0.011724
11.81
0.001
2.0

1
0.00683
0.00683
6.88
0.01
1.2

Error
120
0.119114
0.000993

Lack-of-fit
56
0.118994
0.002125
1138.02
0

Pure error
64
0.000119
0.000002

Total
127
0.593006

Model summary

-sq.: 79.91%; -sq. (adj.): 78.74%; -sq. (pred.): 77.39%

The results show that spindle speed, depth of cut, and table feed rate have a significant effect on the surface roughness () in both linear and quadratic terms. There is also an interaction between depth of cut and feed rate. However, looking at the percentage contribution column, it appears that factor (table feed rate) has the greatest effect on the data variation followed by factor (depth of cut).

Figure 5 shows the residual plots for the response . Apparently, the residuals show no pattern and are distributed randomly against the fitted values and observation order. The normal probability plot and histogram show the normality of the residuals. The normality was tested using Anderson-Darling normality test and the results proved that the residuals are normally distributed with AD value = 0.545 and value = 0.158 ( value < 0.05 shows nonnormality) as shown in Figure 6.

Figure 5: Residual plots for the response .

Figure 6: Anderson-Darling normality test results for residuals.

Model adequacy measures, reflected in the values of the coefficients of determination (-squared, adjusted -squared, and predicted -squared), show reasonable levels of model adequacy. With respect to adjusted -squared, the model explains about 80% of the variation in the data. The value of 77% of the predicted -squared is very close to the adjusted -squared, which proves that the model is not overfit and has a good predictability.

Equation (1) is the regression equation for given by the reduced model. The optimum (minimum ) is given by the values  rpm,  mm, and  mm/min. Figure 7 shows the optimization for

Figures 8–10 show the surface plots of versus two of the processing parameters while fixing the third parameter at its mean value. The figures show the moderate curvature nature of the relationship between and the studied factors.

Figure 7: Optimization plot for .

Figure 8: Surface plots for versus spindle speed and depth of cut at a mean table feed rate of 87.5 mm/min.

Figure 9: Surface plots for versus spindle speed and table feed rate at mean depth of cut of 0.625 mm.

Figure 10: Surface plots for versus depth of cut and table feed rate at a mean spindle speed of 875 rpm.

4.2. ANOVA Results for

Running the analysis as described in Section 4.1, Table 5 shows the ANOVA final results of the model for . However, the model could not be reduced due to the existence of significant third-level interaction ABC. The results show that the table feed rate is the most effective factor followed by the depth of cut on , while the spindle speed had a significant small effect only in its quadratic term. Also, the interaction between the feed rate and depth of cut does exist as in the case of .

Table 5: ANOVA for .

Source
DF
Adj. SS
Adj. MS
-value
value
% contribution

Regression
10
23.6589
2.3659
56.45
0

1
0.0003
0.0003
0.01
0.928
0.0

1
4.7025
4.7025
112.21
0
16.5

1
14.9689
14.9689
357.19
0
52.4

1
0.9405
0.9405
22.44
0
3.3

1
0.8653
0.8653
20.65
0
3.0

1
1.0068
1.0068
24.02
0
3.5

1
0.0193
0.0193
0.46
0.499
0.1

1
0.1679
0.1679
4.01
0.048
0.6

1
0.2752
0.2752
6.57
0.012
1.0

1
0.7122
0.7122
16.99
0

Error
117
4.9032
0.0419

Lack-of-fit
53
4.9031
0.0925
37711.35
0

Pure error
64
0.0002
0

Total
127
28.5622

Model summary

: 0.204714; -sq.: 82.83%; -sq. (adj.): 81.37%; -sq. (pred.): 79.01%

Figure 11 shows the residual plots for the response . Apparently, the residuals show no pattern and are distributed randomly against the fitted values and observation order. The normal probability plot and histogram show the normality of the residuals. The normality was tested using Anderson-Darling normality test and the results proved that the residuals are normally distributed with AD value = 0.425 and value = 0.311 as shown in Figure 12.

Figure 11: Residual plots for the response .

Figure 12: Anderson-Darling normality test results for residuals.

The coefficients of determination values are comparable to that of and, hence, the same conclusions are valid. Equation (2) represents the relationship between and studied factors:

The values for optimum (minimum) are as follows:  rpm,  mm, and  mm/min. It is noticed that only the feed rate value is common between minimum and minimum .

4.3. Multiobjective Optimization for and Metal Removal Rate

Though reducing the feed rate and depth of cut improves the surface roughness, it also reduces the metal removal rate which is a measure of productivity during the machining process. Maximizing should be a goal from the economic point of view. In this analysis, multiobjective optimization was conducted to minimize and maximize simultaneously. Metal removal rate was calculated according to

where is working engagement being 35 mm in all test experiments.

A target was set to minimize and to maximize keeping between 0.15 and 0.2 μm (from industrial experience for fine milling) with higher priority to optimizing . The optimization resulted in spindle speed = 1250 rpm, depth of cut = 1.0 mm, and table feed rate = 67 mm/min with composite desirability of 0.83. Composite desirability measures the goodness of optimization and ranges between zero and one, where one is the ideal case and zero means that at least one of the terms is out of limits. The expected and were calculated to be 0.15 μm and 2333 mm³/min, respectively. Figure 13 shows the multiobjective optimization plot.

Figure 13: Multiobjective optimization plot for and metal removal rate .

High strength steel has relatively high hardness that correlates well with good surface quality. This is due to the harder material possessing low plastic flow capability which results in better surface finish. This is attributed to the brittle nature of the interaction between the cutting tool and the workpiece surface, for the hard materials, that leads to material separation rather than plastic flow that would result in surface irregularities. Surface roughness was found to increase with increasing feed rate and depth of cut which both result in bigger cut areas that are consequently associated with higher cutting forces and higher friction which lead to poor surface finish. It was noticed from the surface roughness profile that high feed rates were associated with larger roughness markings horizontal spacing. Also, with higher depth of cuts, the vertical spacing between peaks and troughs of the surface irregularities was larger. Thus, higher feed rates and depth of cuts led to higher surface roughness.

Figure 14 represents an optical microscopy of the machined surface under spindle speed of 1250 rpm, depth of cut of 0.5 mm, and table feed rate of 50 mm/min, while Figure 15 represents an optical microscopy for the following cutting conditions: spindle speed of 1250 rpm, depth of cut of 0.5 mm, and table feed rate of 125 mm/min. The effect of feed rate is obvious, in a sense that low feed rate produced relatively thin surface roughness markings that are closely spaced, whereas high feed rate produced relatively thick roughness markings that are distantly spaced.

Figure 14: Optical microscopy of the machined surface under spindle speed = 1250 rpm, depth of cut = 0.5 mm, and table feed rate = 50 mm/min.

Figure 15: Optical microscopy of the machined surface under spindle speed = 1250 rpm, depth of cut = 0.5 mm, and table feed rate = 125 mm/min.

5. Conclusion

ANOVA and regression analysis, through a DOE full factorial design (4³), were conducted to relate the surface roughness of face milled high strength steel to the most common machining parameters, namely, table feed rate, depth of cut, and spindle speed. Two surface roughness indicators, namely, and , were experimentally measured through a set of 64 experiments and their replicates. The recorded roughness values are the average of four readings on each surface. For , the results show that speed, depth of cut, and table feed rate have a significant effect on the surface roughness in both linear and quadratic terms. There is also an interaction between depth of cut and feed rate. It also appears that feed rate has the greatest effect on the data variation followed by depth of cut. The minimum was achieved at the following machining conditions: spindle speed = 1250 rpm, depth of cut = 0.447 mm, and table feed rate = 50 mm/min. For , the results show that the feed rate is the most effective factor followed by the depth of cut, while the speed had a significant small effect only in its quadratic term. Also, the interaction between the feed rate and depth of cut does exist as in the case of . The minimum was achieved at the following conditions: spindle speed = 500 rpm, depth of cut = 0.29 mm, and table feed rate = 50 mm/min. It is noticed that only the feed rate value is common between minimum and minimum . Moreover, multiobjective optimization was conducted with the target of minimizing and maximizing metal removal rate . The optimization resulted in spindle speed of 1250 rpm, depth of cut of 1.0 mm, and table feed rate of 67 mm/min with a composite desirability of 0.83, to give and values of 0.15 and 2333 mm³/min, respectively.

Appendix

See Tables 6 and 7.

Table 6: Cutting conditions for group A.

Test
Group
Spindle speed
Depth of cut
Table feed
Surface finish (µm)

number
#
(rpm)
(mm)
(mm/min)

A1
A1
500
0.25
50
0.042
0.295

A2
75
0.120
1.039

A3
100
0.151
1.198

A4
125
0.202
1.419

A5
A2
500
0.5
50
0.055
0.336

A6
75
0.129
0.945

A7
100
0.171
1.256

A8
125
0.210
1.366

A9
A3
500
0.75
50
0.073
0.855

A10
75
0.165
1.132

A11
100
0.194
1.369

A12
125
0.233
1.426

A13
A4
500
1.00
50
0.087
0.928

A14
75
0.206
1.216

A15
100
0.241
1.400

A16
125
0.253
1.596

A17
A5
750
0.25
50
0.083
0.607

A18
75
0.184
1.220

A19
100
0.208
1.736

A20
125
0.239
1.478

A21
A6
750
0.5
50
0.085
0.871

A22
75
0.104
1.069

A23
100
0.115
1.149

A24
125
0.143
1.177

A25
A7
750
0.75
50
0.094
0.901

A26
75
0.118
1.103

A27
100
0.136
1.316

A28
125
0.167
1.547

A29
A8
750
1.00
50
0.109
1.002

A30
75
0.201
1.991

A31
100
0.294
2.140

A32
125
0.354
2.263

A33
A9
1000
0.25
50
0.046
0.334

A34
75
0.104
0.899

A35
100
0.120
1.005

A36
125
0.140
1.174

A37
A10
1000
0.5
50
0.094
0.601

A38
75
0.116
0.950

A39
100
0.134
1.109

A40
125
0.236
1.719

A41
A11
1000
0.75
50
0.109
0.743

A42
75
0.220
1.364

A43
100
0.239
1.675

A44
125
0.259
1.855

A45
A12
1000
1.00
50
0.115
0.853

A46
75
0.243
1.598

A47
100
0.265
1.914

A48
125
0.278
2.140

A49
A13
1250
0.25
50
0.060
0.859

A50
75
0.110
1.082

A51
100
0.144
1.112

A52
125
0.165
1.435

A53
A14
1250
0.5
50
0.064
0.404

A54
75
0.121
0.896

A55
100
0.137
0.907

A56
125
0.165
0.996

A57
A15
1250
0.75
50
0.068
0.321

A58
75
0.128
1.233

A59
100
0.174
1.348

A60
125
0.203
2.186

A61
A16
1250
1.00
50
0.072
0.409

A62
75
0.163
1.514

A63
100
0.190
1.713

A64
125
0.223
1.820

Table 7: Cutting conditions for group B.

Test
Group
Spindle speed
Depth of cut
Table feed
Surface finish (µm)

number
#
(rpm)
(mm)
(mm/min)

B1
B1
500
0.25
50
0.044
0.298

B2
75
0.122
1.042

B3
100
0.153
1.200

B4
125
0.204
1.417

B5
B2
500
0.5
50
0.056
0.338

B6
75
0.130
0.948

B7
100
0.173
1.257

B8
125
0.211
1.368

B9
B3
500
0.75
50
0.075
0.854

B10
75
0.166
1.133

B11
100
0.196
1.371

B12
125
0.235
1.428

B13
B4
500
1.00
50
0.087
0.928

B14
75
0.208
1.216

B15
100
0.242
1.401

B16
125
0.256
1.598

B17
B5
750
0.25
50
0.085
0.605

B18
75
0.186
1.223

B19
100
0.209
1.738

B20
125
0.240
1.479

B21
B6
750
0.5
50
0.088
0.872

B22
75
0.106
1.067

B23
100
0.117
1.150

B24
125
0.146
1.179

B25
B7
750
0.75
50
0.098
0.900

B26
75
0.121
1.102

B27
100
0.138
1.318

B28
125
0.169
1.549

B29
B8
750
1.00
50
0.110
1.002

B30
75
0.200
1.990

B31
100
0.296
2.143

B32
125
0.356
2.261

B33
B9
1000
0.25
50
0.049
0.338

B34
75
0.100
0.896

B35
100
0.120
1.007

B36
125
0.140
1.176

B37
B10
1000
0.5
50
0.096
0.605

B38
75
0.118
0.952

B39
100
0.136
1.112

B40
125
0.239
1.722

B41
B11
1000
0.75
50
0.110
0.746

B42
75
0.221
1.362

B43
100
0.240
1.677

B44
125
0.262
1.857

B45
B12
1000
1.00
50
0.118
0.856

B46
75
0.242
1.600

B47
100
0.268
1.917

B48
125
0.279
2.142

B49
B13
1250
0.25
50
0.060
0.861

B50
75
0.110
1.084

B51
100
0.145
1.113

B52
125
0.165
1.437

B53
B14
1250
0.5
50
0.065
0.406

B54
75
0.122
0.899

B55
100
0.138
0.908

B56
125
0.166
1.000

B57
B15
1250
0.75
50
0.068
0.323

B58
75
0.129
1.235

B59
100
0.175
1.346

B60
125
0.201
2.189

B61
B16
1250
1.00
50
0.075
0.412

B62
75
0.165
1.516

B63
100
0.192
1.715

B64
125
0.225
1.822

Nomenclature

: | Depth of cut, mm
: | Working engagement, mm
: | Spindle speed, rpm
: | Cutting speed, m/min
: | Table feed rate, mm/min
: | Total number of teeth in cutter
: | Metal removal rate, mm³/min.

Competing Interests

The authors declare that they have no competing interests.

Acknowledgments

This project was supported by King Saud University, Deanship of Scientific Research, College of Engineering Research Center.

References

K. V. M. K. Raju, G. R. Janardhana, P. N. Kumar, and V. D. P. Rao, “Optimization of cutting conditions for surface roughness in CNC end milling,” International Journal of Precision Engineering and Manufacturing, vol. 12, no. 3, pp. 383–391, 2011.

D. Y. Pimenov, “Experimental research of face mill wear effect to flat surface roughness,” Journal of Friction and Wear, vol. 35, no. 3, pp. 250–254, 2014.

F. Pusavec, A. Deshpande, S. Yang et al., “Sustainable machining of high temperature Nickel alloy—Inconel 718: part 2—chip breakability and optimization,” Journal of Cleaner Production, vol. 87, pp. 941–952, 2015.

C. Felho and J. Kundrak, “CAD-based modelling of surface roughness in face milling,” International Journal of Mechanical, Aerospace, Industrial and Mechatronics Engineering, vol. 8, no. 5, pp. 814–818, 2014.

S. Rawangwong, J. Chatthong, R. Burapa, and W. Boonchouytan, “An investigation of optimum cutting conditions in face milling semi-solid AA 7075 using carbide tool,” International Journal of Innovation, Management and Technology, vol. 3, no. 6, pp. 692–696, 2012.

T. Kivak, “Optimization of surface roughness and flank wear using the Taguchi method in milling of Hadfield steel with PVD and CVD coated inserts,” Measurement, vol. 50, no. 1, pp. 19–28, 2014.

S. Rawangwong, J. Chatthong, J. Rodjananugoon, R. Burapa, and W. Boonchouytan, “An investigation of optimum cutting conditions in face milling nodular cast iron FCD 400 using carbide tool,” International Journal of Materials, Mechanics and Manufacturing, vol. 1, no. 4, pp. 309–313, 2013.

A. T. M. Abbas, “Comparative assessment of wiper and conventional carbide inserts on surface roughness in the turning of high strength steel,” Journal of Materials Science Research, vol. 5, no. 1, pp. 32–45, 2015.

Y. Zhang and K. Chou, “A parametric study of part distortions in fused deposition modelling using three-dimensional finite element analysis,” Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture, vol. 222, no. 8, pp. 959–967, 2008.

D. Fydrych and G. Rogalski, “Effect of shielded-electrode wet welding conditions on diffusion hydrogen content in deposited metal,” Welding International, vol. 25, no. 3, pp. 166–171, 2011.

T. Ding, S. Zhang, Y. Wang, and X. Zhu, “Empirical models and optimal cutting parameters for cutting forces and surface roughness in hard milling of AISI H13 steel,” International Journal of Advanced Manufacturing Technology, vol. 51, no. 1, pp. 45–55, 2010.

D. C. Montgomery, Design and Analysis of Experiments, John Wiley & Sons, 2013.