Improvement of Mechanical Properties in Polypropylene-and Glass-Fibre-Reinforced Peach Shell Lightweight Concrete

*e use of the polypropylene fibre and glass fibre with different volume fractions to improve the mechanical properties of peach shell lightweight concrete was investigated in this study.*e volume fractions of 0.25%, 0.50%, and 0.75% were used for each fibre. *e results showed that, as the polypropylene fibre and glass fibre were added into peach shell concrete, the density was reduced by up to 6.1% and the compressive strength, splitting tensile strength, and flexural strength were increased by 19.1%, 54.3%, and 38.6%, respectively. *e highest compressive strength, splitting tensile strength, and flexural strength of 29.3MPa, 2.87MPa, and 3.09MPa, respectively, were produced by peach shell concrete with 0.75% glass fibre. *e results indicated that the incorporation of fibres significantly enhanced the postfailure toughness of peach shell concrete. It was found that the glass fibre was more effective than the polypropylene fibre in improving the mechanical properties of peach shell concrete. Although the incorporation of fibres slightly increased the water absorption and porosity, the type and content of fibres had no significant effect on water absorption and porosity. *erefore, the mechanical properties of peach shell lightweight concrete can be improved by adding polypropylene fibres and glass fibres.


Introduction
e use of agricultural or industrial wastes in concrete to replace the conventional raw material has achieved environmentally friendly and sustainable development by reducing the production costs of the raw material and contributing to waste disposal.e expanding extraction of conventional aggregates such as granite aggregate and sand in concrete production has caused serious environmental pollution problems [1].e use of lightweight aggregates such as expanded clay, foamed slag, and natural pumice instead of conventional coarse aggregates can produce lightweight aggregate concrete (LWAC) [2].LWAC has a lot of advantages including better fire resistance, heat insulation, sound absorption, and frost resistance [3].Recently, the utilization of agricultural wastes such as coconut shell, oil palm shell, and apricot shell as a substitute for normal weight aggregates (NWAs) is gradually rising.On the other hand, the additional advantages of using agricultural wastes instead of normal aggregates to produce LWAC are to reduce environmental pollution and to deal with wastes [4].Agricultural waste is rapidly storing in developing countries, and peach shell (PS) is the seed of peach fruits, which causes environmental problem around their cultivated areas.More than thousand tons of PS wastes need to be discharged each year in China.e lightweight and regenerative characteristic of PS compared to the NWAs can make PS as one of the potential lightweight aggregates and sustainable building materials in the production of LWAC.
is could reduce the environmental pollution caused by PS and contribute to the reutilization of PS. e improvement in the mechanical properties of LWAC depends on the oven-dried density, water-to-cement ratio, addition of other binder materials, aggregate content, and particle size [5,6].Previous studies showed that LWAC with higher compressive strength can be produced, but this concrete was prone to brittle and poor tensile strength due to the fact that the lightweight aggregate is usually weaker under tension [7,8].e tensile strength of LWAC is about one-tenth of its compressive strength [9].e use of PS instead of NWA has a positive impact on density, and a reduction in density up to 30% can be achieved in the peach shell concrete (PSC).However, the splitting tensile and flexural strengths and modulus of elasticity (MOE) of PSC are lower than those of LWAC made of other lightweight aggregates such as pumice and expanded clay.e low tensile strength tends to cause significant tensile cracking to occur under lower tensile loads [10].Hence, the improvement of the mechanical properties of PSC requires more attention.
Incorporation of fibres is an effective way to improve the mechanical properties of concrete, such as splitting tensile and flexural strengths and other related characteristics [11].In fibre-reinforced concrete, the role of fibres is to improve the performance of concrete through the crack bridge effect of fibres and the fibre-cement-aggregate interfacial bond [5].Previous research showed that fibre-reinforced concrete with two types of different fibres had better ductility, crack growth resistance, and impact resistance.In the composite fibre material system, the harder fibres enhance the first crack stress and ultimate strength, and the softer fibres control the crack propagation and increase the ductility [12].Yap et al. [13] reported that oil palm shell lightweight concrete with 0.9% steel and 0.1% polypropylene (PP) fibres had better improvement in flexural toughness characteristics.
Although a lot of study works are ongoing on the addition of fibres in LWAC, there is only little literature on the incorporation of fibres in PSC.In order to make PSC like other LWAC applied to practical building structure elements such as sidewalks, parking lots, roadblocks, and partition walls, the mechanical properties and durability of PSC need to be further improved.e addition of fibres into PSC can make it as a ductile and sustainable building material.Commonly used fibres are the steel fibre, PP fibre, and nylon fibre, and there are few literatures available on the use of glass (G) fibres in LWAC.e main disadvantages of adding steel fibres to LWAC are a significant increase in density and reduced workability.e PP fibre is mainly used in concrete to enhance the ductility, toughness, and impact resistance, but do not expect them to improve the strength [12].Mastali et al. [14] reported that adding G fibres led to a significant improvement in compressive strength, tensile strength, and impact resistance of G fibre-reinforced concrete.Compared to steel fibres, the advantage of adding PP fibres and G fibres to PSC is that the density is less than 2000 kg/m 3 and lower than the upper limit of the density set for LWAC.However, there are few literatures on the comparison of PP fibre-and G fibre-reinforced peach shell lightweight concrete.
e purpose of the present study is to investigate the influence of two types of fibres (PP fibre and G fibre) and each fibre at a volume fraction of 0.25%, 0.50%, and 0.75% on the mechanical properties of peach shell lightweight concrete.A comparison of the performance of PP fibre-and G fibre-reinforced peach shell lightweight concrete is investigated and reported, including workability, density, compressive strength, splitting tensile strength, flexural strength, modulus of elasticity, residual compressive strength, water absorption, and porosity.is work helps to expand the knowledge on the effect of PP fibres and G fibres with different contents on the mechanical properties of peach shell fibre-reinforced concrete (PSFRC).

Materials
2.1.1.Cement and Silica Fume.Type I 42.5 grade ordinary Portland cement was used in this study and obtained from a local cement company.e Blaine specific surface area and specific gravity are 3532 cm 2 /g and 3.14 g/cm 3 , respectively.In addition, silica fume (SF) was added in concrete as an additional mineral binder to improve the performance of concrete.SF content at 10% of the cement weight was used in all mixes.

Coarse and Fine
Aggregates.Peach shell (PS) was used as an alternative coarse aggregate, and crushed pebble was used as a normal weight coarse aggregate.e density of PS is 63% lower than that of normal weight aggregates (NWAs), which is significant for reducing dead loads of building structures.River sand was used as a fine aggregate and obtained from a local sand company.e physical properties of the aggregates are shown in Table 1.PS was collected from a local peach plantation.Before using, they were washed to remove the residual dried peach pulp and the dust from the PS surface.
en, the dry PS was crushed by a crushing machine in the laboratory.Crushed PS was sieved with 4.75 mm and 9.5 mm sieves, respectively.Particles of size 4.75-9.5 mm were considered as coarse aggregates.Uncrushed and crushed PS and scanning electron microscopic (SEM) image at 5000 magnification times of crushed PS are shown in Figure 1.As can be seen from Figure 1, crushed PS has an irregular and rough surface, and the PS aggregate has a lot of circular porosity on the surface, and the diameter of the micropore is about 10-20 μm.Although a large number of porosity on the surface of PS reduces the density, it leads to the fact that PS has a higher water absorption compared to NWA. erefore, PS was submerged in water for 24 h and kept in an internal saturated and surface dry condition before mixing.

Water and Superplasticizer.
e water used in this study was normal tap water.A high-range naphthalene sulphonated superplasticizer (SP) was used in the study to increase the workability of fresh concrete.SP content at 1% of the cement weight was used in all mixes.
2.1.4.Fibres.Two different fibres used in this study are the (i) polypropylene (PP) fibre and (ii) glass (G) fibre.e properties of fibres are shown in Table 2.

2
Advances in Materials Science and Engineering

Mix Proportioning.
e mix proportion of concretes is presented in Table 3.A total of six concrete mixes were prepared with different fibre contents, and a control mix without the addition of fibres was also produced for comparison purpose.e total amount of materials for all mixes was the same except in the case of two different fibres and three fibre volumes.

Specimen Preparation and Test Methods.
e procedure of specimen preparation of peach shell fibre-reinforced concrete (PSFRC) was detailed as follows: firstly, PS and river sand were poured into a blender and dry mixed for 2 min.en, fibres and cement and SF were added to the mixture and dry mixed for 1 min.Before the fibres were mixed, fibres were manually distributed.Following this, 60% water mixed with SP was added to the mixture and mixed for 3 min.Finally, 40% water was added to the mixture and mixed for 5 min.After mixing was complete, the slump test was carried out immediately, and then, the specimens were cast in oiled plastic moulds.All specimens were compacted by the vibrating table.Immediately after compaction, all specimens along with the moulds were covered by a plastic sheathing to prevent moisture evaporation.Specimens were removed from the moulds after 24 h.Finally, specimens were stored in a controlled room with a relative humidity of 95% ± 5% and a temperature of 20 °C ± 2 °C until the test age.
e workability of all mixes was measured by the slump test according to ASTM C143/C143M-12 (Figure 2).e density of all specimens was measured in accordance with ASTM C138. 100 mm cube specimens were used for the compressive strength test (BS EN12390-2:200 9 and BS EN12390-3:200 9) at the age of 3, 7, 28, and 56 days (Figure 2).e splitting tensile and flexural strengths and modulus of elasticity of all mixes were measured at the age of 28 days according to ASTM C496/C496M-11, ASTM C78-10, and ASTM C469-10 (Figure 2), respectively.e average value of at least three specimens is taken for each test result.
e water absorption test was carried out according to the procedures prescribed in ASTM C642.All specimens were oven-dried at 110 ± 5 °C for not less than 24 h to remove moisture and achieve constant before testing.e specimens were then submerged in water for 24 h.e water absorption values of the specimen were calculated using the following formula: where M 1 is the mass of the oven-dried specimen in air (g) and M 2 is the mass of the surface-dried specimen in air after immersion (g).e porosity of all specimens was determined in accordance with ASTM C642.Absolute density is necessary to determine the total porosity by the method prescribed in ASTM C642; hence, the pycnometry method was applied for

Total porosity volume(
where ρ a is the absolute density of the specimen (g/cm 3 ) and ρ b is the bulk density of the specimen (g/cm 3 ).Open porosity volume(%) where M 1 is the mass of the oven-dried specimen in air (g); M 2 is the mass of the surface-dried specimen in air after immersion (g); M 3 is the mass of the surface-dried specimen in air after immersion and boiling (g); and M 4 is the apparent mass of the specimen in water after immersion and boiling (g).

Workability (Slump).
Relationship between the bre content and slump value is shown in Figure 3. Yew et al. [9] reported that the incorporation of di erent types of PP bres in oil palm shell concrete caused a considerable decrease in the slump value.As expected, the results showed that the slump values of the fresh PSC with PP bres and G bres were reduced to 55 mm and 60 mm, respectively.e reason for this phenomenon can be explained by the fact that the bre-cement paste interfacial bond in concrete restricts the dispersion and ow of the cement paste and improves the viscosity of the mixtures.With the increase in bre volume fraction, the capability of the bre-cement paste interfacial bond in concrete becomes stronger as more bres absorb the cement paste to wrap around it.erefore, the workability of concrete decreased as the bre volume (V f ) increased from 0% to 0.75%.Mehta and Monteiro [15] reported that the LWAC with a slump value of 50-75 mm is similar to normal weight concrete with a 100-125 mm slump value.In the case of PSC, the slump value of PP bre-and G bre-reinforced PSC between 55 mm and 60 mm can easily be compacted.
Figure 3 also shows that the two types of bres have an impact on the workability of concrete.For all V f , the G bre produced slightly higher slump values than the PP bre.e increase in slump values at a range of 5-10 mm and the biggest di erence between the G bre and PP bre were observed at V f 0.50%, and the slump value of G50 was 7.8% higher than that of PP50.Song et al. [16] reported that the workability of bres with a shorter length was lower than that of longer bres.e shorter bres have more surface area for the reinforcing bre-cement paste bond [9].Since the length of the G bre is longer than that of the PP bre and the surface of the G bre is smoother, G bres have lower e ective surface area to develop a bre-cement paste bond compared to PP bres.Hence, the slump value of PSC incorporated with G bres was slightly higher than that of PP bres.Advances in Materials Science and Engineering of 1600-2000 kg/m 3 [17].Relationship between the fibre content and ODD is shown in Figure 4. e results showed that the ODD of all PSC ranged from 1758 kg/m 3 to 1872 kg/m 3 and fulfilled the requirement of LWAC because PS is about 63% lighter than NWA.e addition of PP fibres and G fibres in concrete reduced the ODD of PSC because fibres have a low specific gravity.When the volume fraction of PP fibres is added at percentages of 0.25%, 0.50%, and 0.75%, the ODD of these concretes decreased by 1.5%, 5.0%, and 6.1%, respectively, compared to the control mix.
Figure 4 also showed that the different types and volume fractions of fibres had an influence on the ODD of PSC.It was found that concrete with G fibres produced a slightly higher ODD than PP fibres, and the difference in the ODD of PSC is more significant as fibre volume fraction ranges from 0.25% to 0.75%.At V f � 0.75%, G75 had the lowest ODD of 1778 kg/m 3 , and it was only 1.1% higher than PP75.It should be noted that although the specific gravity of PP fibres and G fibres is significantly different, its impact on the ODD of PSC is not obvious.However, compared to the density of approximately 2400 kg/m 3 for ordinary weight concrete, the ODD of PSC is reduced by about 26%, which is a significant reduction in the weight of concrete.

Compressive Strength.
e development of the compressive strength of concretes up to 56 days is shown in Figure 5.
e test results revealed that the compressive strength of all concretes increased as the curing age increased.As can be seen from Figure 5, there is a significant difference in the compressive strength between PSC containing different types and contents of fibres and control mix without any fibres.
e enhancement of the ultimate compressive strength may be attributed to the fact that fibres arrest the growth of cracks due to the fibre-cement paste interfacial bond and the crack bridging effect of fibres [18].
e addition of PP fibres and G fibres had significantly increased the compressive strength of PSC at all ages, and the compressive strength increased as an increase in fibre content.e 28-day compressive strength of all mixes varied between 24.6 MPa and 29.3 MPa, which fulfilled the requirements for the strength and density of LWAC.It can be observed that compared to the control mix, the 28-day compressive strength of PP25, PP50, and PP75 increased by 8.1%, 9.8%, and 14.2%, respectively, and the 28-day compressive strength of G25, G50, and G75 increased by 6.1%, 14.6%, and 19.1%, respectively.Except for V f � 0.25%, the 28-day compressive strength of G fibre-reinforced PSC was slightly higher than that of PP fibre. is phenomenon indicated that the use of G fibre-reinforced PSC is a good choice.
Table 4 shows the compressive strength of concretes.All concretes attained approximately 66%-75% of compressive strength at 3 days and 87%-92% of compressive strength at 7 days.
is indicated that all PSC developed high early compressive strength because the incorporation of SF increased the cohesiveness of cement paste and reduced the advance of microcracks, and eventually, the early compressive strength of PSC is increased.e addition of PP fibres and G fibres in concrete increased the 28-day compressive strength by about 6%-19%.At V f � 0.75%, G75 produced the highest 28-day compressive strength of 29.3 MPa, which is 19.1% higher than the control mix of 24.6 MPa.Although not every kind of lightweight aggregate is suitable for the production of LWAC, the results based on this study indicate that it is feasible to produce LWAC using PS as a lightweight aggregate.
Generally, the initiation and advance of cracks in concrete are due to the continuous increase in compressive loading.Since the tensile stress generated by the fibre is perpendicular to the crack propagation path, the debonding begins at the interface between the fibre and cement paste.Once the advancing cracks reach the fibre-cement paste interface, the stress concentration at the crack tip is released, and as a result, the development of the advancing crack is blunted and blocked.e fibre is like a bridge in this process that arrests the advancing cracks and consequently improves the strength of concretes [19,20].erefore, the addition of PP fibres and G fibres enhanced the bonding of the fibrecement paste interface and improved the compressive strength [16].e compressive strength of G fibre-reinforced PSC is higher than that of PP fibre-reinforced PSC. is reason can be explained by the following: firstly, the tensile strength of G fibres in this study is 2.4 times that of PP fibres, and thus, compared to the PP fibre, the G fibre is easier to transfer higher tensile stress from a cracked fibre-cement interface to fibre.Secondly, under the same fibre volume fraction, the density of G fibre-reinforced PSC in this study is higher than that of PP fibre-reinforced PSC.Although the addition of fibres in this study reduced the density of PSC, for normal weight concrete, the higher the density the higher the compressive strength.us, the compressive strength of higher density of G bre-reinforced PSC is higher than that of PP bre-reinforced PSC.
Due to the importance of knowing the 28-day compressive strength from the early age compressive strength, Figures 6 and 7 show the relationship between the 28-day compressive strength and compressive strength at early ages of 3 days and 7 days, respectively.As can be seen from Figures 6 and 7, there is a linear relationship with the high correlation coe cient between the 28-day compressive strength and the early compressive strength, and the 28-day compressive strength of PSC can be predicted by the early compressive strength.

Splitting Tensile and Flexural Strengths.
Splitting tensile strength and exural strength of all mixes are shown in Table 5. Comiloli et al. [21] reported that the incorporation of PP bres in concrete can slightly enhance the exural toughness of concrete.e bre enhances the strength of concretes by the crack bridging e ect and carrying part of load [12].e results showed that the incorporation of PP bres and G bres in concrete increased both splitting tensile strength and exural strength of PSC, and the more the bre content, the higher the splitting tensile strength and exural strength.
e addition of PP bres from 0.25% to 0.75% and glass bres from 0.25% to 0.75% increased the splitting tensile strength up to 10.2%-36.6% and 7.5%-54.3%,respectively.Furthermore, the exural strength of PP bre-and G brereinforced PSC was also improved.e exural strength of PSC increased as an increase in bre volume fraction.When the bre volume fraction varies from 0.25% to 0.75%, the exural strength for PP bre and G bre reinforced PSC increased by 6.7%-17.9%and 5.4%-38.6%,respectively.e advantage of PSC could be further explained based on Figure 8. From Figure 8, it was evident that the control concrete without any bres failed once the ultimate splitting tensile strength was reached due to low ductility.Furthermore, the brereinforced PSC showed excellent crack arresting performance as the specimen was not broken into two pieces even after the failure load. is phenomenon attributed to the crack bridging e ect of bres, and bres in concrete provide additional strength to the bre-cement interfacial bond which carries a partial load.
Although the ODDs of PP75 and G75 were lower in this study, the splitting tensile strength and exural strength of PP75 and G75 were higher than those of the control mix.Since the tensile stress of G bres is greater than that of PP bres, glass-bre reinforced PSC produced a higher splitting tensile strength and exural strength.At V f 0.50% and 0.75%, splitting tensile strength and exural strength of PSC containing G bres were found to be about 12.5%-13.0%and 7.6%-17.5%,respectively, and higher than those of PP bres.Splitting tensile strength and exural strength of G75 were 2.87 MPa and 3.09 MPa, respectively, which increased by 54.3% and 38.6%, respectively, compared to the control mix.Compared to the PP bre, the higher tensile stress of the G bre is more e ective in transferring the tensile stress.At the  Advances in Materials Science and Engineering same bre volume fraction, the G bre has a smaller diameter, leading to more bres to join the cracks [22].Due to the bridging e ect of bres, the stress concentration around cracks is reduced and the development of cracks is hindered.Eventually, the tensile strength of PSC is improved.e relationship between the compressive strength and splitting tensile strength and exural strength for PSC at 28 days is shown in Figures 9 and 10, respectively.As can be seen from Figures 9 and 10, the splitting tensile strength and exural strength of PSFRC increase as an increase in compressive strength.5 shows the modulus of elasticity (MOE) of all concretes, which ranges between 8.71 and 11.32 GPa.

Modulus of Elasticity. Table
e control concrete in this study produced a minimum MOE of 8.71 GPa.
e results showed that the types of G bres and PP bres had a signi cant e ect on MOE.At V f 0.25%, 0.50%, and 0.75%, the MOE of PP bre-and G bre-reinforced PSC increased by 10.6% and 12.4%, 16.5% and 23.4%, and 24.6% and 30.0%, respectively.e incorporation of bres enhances the MOE of PSC because bres arrest the initial cracks caused by shrinkage, and the crack bridging e ect reduces the strain caused by the compression loading and consequently improves the MOE.
e MOE of PSFRC was found to depend on the bre volume fraction, while the type of bres had an insigni cant in uence on it.
e volume fraction of G bres increased from 0.25% to 0.75%, the MOE of G bre-reinforced PSC increased by 15.6% from 9.79 GPa to 11.32 GPa, and the MOE of G bre-reinforced PSC was 1.7%, 5.9%, and 4.3%, respectively, slightly higher than that of PP bre.
Figure 11 shows the relationship between the compressive strength and MOE.As can be seen from Figure 11, there is a good relationship between the MOE and 28-day compressive strength of PSFRC, and the MOE of PP brereinforced PSC and glass bre-reinforced PSC can be predicted by the 28-day compressive strength, respectively.

Residual Compressive Strength.
Residual compressive strength (RCS) can be used to evaluate the residual strength toughness of concretes.Figure 12 shows residual compressive strength of concretes.Because the crack bridging e ect of bres existed at two crack surfaces, in the brereinforced concrete, additional loading forces are required for further growth of the crack.As expected, the incorporation of PP bres and G bres enhanced the residual strength toughness of PSC. e control concrete without any bres had no RCS as the control concrete was immediately failed when the ultimate loading strength is reached.In addition, the more the bre content, the higher the RCS value.At V f 0.75%, PP bre-and G bre-reinforced PSC had the highest RCS value.It might be attributed to the crack bridging e ect of bres that existed at two crack surfaces, which can hinder further propagation of cracks, even after microcrack cracking.e results indicated that the in uence of adding bres on the improvement of postfailure toughness of PSC was very signi cant.

Water Absorption and Porosity. Twenty-four-hour
water absorption and open porosity for all mixes are shown in Figure 13.Lo et al. [23] studied that the water absorption of the lightweight aggregate a ected the internal microstructure of the hardened mortar and the interfacial zone of concrete, and an increase in the water absorption of the lightweight aggregate resulted in an increase in the number of pores in the interfacial zone of concrete.Figure 13 clearly showed that the incorporation of bres slightly increased the water absorption and open porosity of PSC, and the water absorption values of all concretes varied from 7.5% to 8.8%.However, the type and content of bres had an insigni cant e ect on water absorption and open porosity, and the more the number of open pores, the higher the water absorption for all concretes.e addition of bres might a ect the number and area of micropores in PSC, which resulted in a small increase in water absorption and open porosity.Neville and Brooks [24] reported that although the water absorption cannot be used to determine the quality of concrete, the water absorption of most of the good-quality concretes usually is much lower than 10% by mass.It can be seen from Figure 13 that all concretes have less than 10% water absorption and meet the requirements of good concrete.
Total porosity and open porosity of concretes are shown in Figure 14. e result showed that the total porosity of PSC was between 15.1% and 16.5%, and the open porosity Advances in Materials Science and Engineering varied from 11.2% to 12.6%.Furthermore, most of the total porosity in PSC was open porosity, and closed porosity accounted for a small portion of the total porosity because the surface of PS aggregates contains a lot of microscopic and connective pore structures.Results also showed that the type and content of bres had an insigni cant in uence on the porosity of PSC, and the addition of bres slightly increased the porosity of PSC.In addition, a slight increase in the total porosity was another reason that adding bres reduced the density of PSC.

Conclusions
e in uences of incorporating two types of bres (polypropylene bre and glass bre) and di erent bre volume fractions (0.25%, 0.5%, and 0.75%) on the mechanical properties of peach shell lightweight concrete have been investigated in this study.e following conclusions can be drawn based on the present study: (1) e polypropylene bre and glass bre decrease the slump value of peach shell concrete.e slump values of the fresh peach shell concrete with polypropylene bres and glass bres are reduced to 55 mm and 60 mm, respectively.However, the concrete containing glass bres produced slightly higher slump values than polypropylene bres.
(2) e addition of polypropylene bres and glass bres reduces the oven-dried density of peach shell concrete.e oven-dried density of all concretes ranges from 1758 kg/m 3 to 1872 kg/m 3 and ful lls the requirement of lightweight aggregate concrete.In addition, the oven-dried density of peach shell concrete reduces with an increase in bre content.(3) All concretes have high early compressive strength.
Polypropylene bres and glass bres signi cantly increase the compressive strength of peach shell concrete, and the compressive strength of peach shell concrete increases as an increase in bre content.In addition, an increase in the 28-day compressive strength of peach shell concrete is about 6%-19%.(4) e addition of polypropylene bres and glass bres in concrete increases the splitting tensile strength of peach shell concrete.Furthermore, the more the bre content, the higher the splitting tensile strength.e addition of polypropylene bres and glass bres from 0.25% to 0.75% increases the splitting tensile strength up to 10.2%-36.6% and 7.5%-54.3%,respectively.(5) e exural strength of peach shell concrete increases as an increase in bre volume fraction.e exural strength for polypropylene bres and glass bres from 0.25% to 0.75% reinforced the peach shell concrete increase by 6.7%-17.9%and 5.4%-38.6%,respectively.(6) e glass bre-reinforced peach shell concrete produces a higher splitting tensile strength and exural strength.At V f 0.50% and 0.75%, the splitting tensile strength and exural strength of peach shell concrete containing glass bres are found to be about 12.5%-13.0%and 7.6%-17.5%,respectively, and higher than those of polypropylene bres.( 7) e e ect of incorporating polypropylene bres and glass bres enhances the modulus of elasticity of peach shell concrete.Modulus of elasticity of all concretes ranges between 8.71 and 11.32 GPa.At V f 0.25%, 0.50%, and 0.75%, the modulus of elasticity of polypropylene bre-and glass brereinforced peach shell concrete increases by 10.6% and 12.4%, 16.5% and 23.4%, and 24.6% and 30.0%, respectively.(8) e control peach shell concrete produced no residual compressive strength.However, the addition of polypropylene bres and glass bres enhances the residual strength toughness of peach shell concrete.
In addition, the higher the bre volume content, the higher the residual compressive strength.At V f 0.75%, the polypropylene bre-and glass brereinforced peach shell concrete have the highest residual compressive strength values and increase by 46% and 82%, respectively.(9) e incorporation of bres slightly increases the water absorption and porosity of peach shell concrete.However, the type and content of bres have an insigni cant e ect on water absorption and porosity.

Conflicts of Interest
e authors declare that they have no con icts of interest.would also like to thank Dr. Ai Ting for her assistance in conducting some of the tests in this paper.

Figure 1 :
Figure 1: (a) Uncrushed PS, (b) crushed PS, and (c) SEM image of the crushed PS particle at 5000 magnification times.

Figure 14 :
Figure 14: Total and open porosity of concretes.

Table 1 :
Physical properties of the aggregates.

Table 2 :
Properties of the PP fibre and G fibre.

Table 3 :
Mix proportion of concretes.

Table 4 :
Compressive strength of concretes.Note.Values in brackets denote the percentages of compressive strength to the corresponding 28-day compressive strength.
6Advances in Materials Science and Engineering

Table 5 :
Splitting tensile and exural strengths and modulus of elasticity of concretes (28 days).