β-Ga2O3 thin films were grown on c-plane sapphire substrates by plasma-assisted molecular beam epitaxy. The films were grown using an elemental gallium source and oxygen supplied by an RF plasma source. Reflection high-energy electron diffraction (RHEED) was used to monitor the surface quality in real time. Both in situ RHEED and ex situ X-ray diffraction confirmed the formation of single crystal β-phase films with excellent crystallinity on c-plane sapphire. Spectroscopic ellipsometry was used to determine the film thicknesses, giving values in the 11.6–18.8 nm range and the refractive index dispersion curves. UV-Vis transmittance measurements revealed that strong absorption of β-Ga2O3 starts at ∼270 nm. Top metal contacts were deposited by thermal evaporation for I-V characterization, which has been carried out in dark, as well as under visible and UV light illumination. The optical and electrical measurements showed that the grown thin films of β-Ga2O3 are excellent candidates for deep-ultraviolet detection and sensing.
Consejo Nacional de Ciencia y Tecnología290842339617Universidad Autónoma de Baja California3068UABC-PTC-6341. Introduction
Ultraviolet radiation (UV) covers the wavelengths shorter than 400 nm in the electromagnetic spectrum. The effect of UV radiation depends on the wavelength and can lead to some benefits as in the case of UV-A (400–320 nm) that stimulates photosynthesis, while exposure to other wavelengths can cause skin cancer (UV-B 320–280 nm) and be a risk factor for some eye diseases. The most energetic part of the UV spectrum, UV-C (280–10 nm) causes damage and degradation of organic materials [1–3]. As a result, the development of miniature, fast, highly sensitive, selective, stable, and robust UV detectors is the subject of intense studies [4].
Gallium oxide (Ga2O3) is a wide bandgap (∼5 eV) semiconductor material with the β-phase being the most stable form. Ga2O3 thin films have been used as gas sensors, dielectric coatings for solar cells, and deep-ultraviolet (UV) transparent oxides, among others [5–11]. Wide bandgap semiconductors present advantages over the polymers currently used for UV detection because of their intrinsic visible blindness, temperature stability, and enhanced radiation hardness [12, 13]. A wide variety of techniques have been used to deposit or grow Ga2O3 thin films. Among them is molecular beam epitaxy (MBE) [14–18].
In this work, we report on the preparation and characterization of β-phase Ga2O3 thin films grown by plasma-assisted molecular beam epitaxy (PAMBE) at various growth conditions. The quality of the grown films was inferred from reflection high-energy electron diffraction (RHEED) and X-ray diffraction (XRD). Current-voltage (I-V) measurements were carried out in dark, as well as under visible and UV light illumination to study the possibility of using β-phase Ga2O3 in deep-UV sensors.
2. Materials and Methods
β-Ga2O3 thin films were grown on single-side polished c-plane sapphire substrates by PAMBE in an oxide MBE chamber. The substrates were degreased in acetone and thermally cleaned for 15 min at 850°C in the chamber followed by an oxygen plasma exposure for 30 minutes. A chamber base pressure of <5 × 10−10 Torr was obtained by a combination of turbomolecular and cryogenic pumps. During the growth, the oxide chamber cryopanels were cooled with liquid nitrogen. The films were grown using a well-known method from evaporated Ga and oxygen provided from a radio frequency (RF) plasma source equipped with an ion deflector [19]. The oxygen flow rate was varied from 1.0 to 1.5 sccm using RF plasma power of 200 and 300 W. The elemental evaporated Ga was provided from an effusion cell with a fixed temperature of 800°C (thermocouple temperature). The substrate temperature was varied from 650 to 750°C as measured using a thermocouple. All samples were grown for 60 minutes with the surface quality monitored in real time in situ using RHEED.
The as-grown samples were analyzed by XRD (Bede System diffractometer) to determine the crystalline quality of the films. The thickness and the optical constants of the films were determined by spectroscopic ellipsometry measurements using a J. A. Woollam M-2000 variable angle ellipsometer. Transmission spectra of the samples were measured by the UV-Vis spectrometer Shimadzu 2600. For electrical characterization, a group of samples with 70 × 70 µm Al contacts with spacing of 30 µm between them was prepared by thermal evaporation. I-V measurements of lateral current between two adjacent contacts were carried out in dark as well as under UV-C (254 nm), UV-A (365 nm), and visible light illumination (532, 650 nm) using a Keithley 4200 Semiconductor Characterization System.
3. Results and Discussion
Real-time RHEED was used to monitor the crystallinity and surface quality during the film growth. Figure 1(a) shows a RHEED pattern of pure c-plane sapphire substrate prior to growth presenting a diffuse background. After formation of the Ga2O3 film, the RHEED pattern exhibited a streaky threefold reconstruction, indicating high-degree of crystallinity in the grown films as is shown in Figure 1(b).
RHEED pattern of (a) c-plane sapphire substrate and (b) grown Ga2O3 film.
The film thicknesses were determined by Ellipsometry using the Cauchy model [20, 21]. The Cauchy model assumes that the refractive index n can be represented by a slowly varying function of the wavelength n=A+B/λ2+C/λ4, where A, B, and C are fitting parameters that determine the index. The thicknesses were determined by fitting the experimental results only in the 300–1000 nm range, where the films are transparent. The obtained results for the thickness, roughness, and the refractive index at λ = 632.8 nm of the grown samples are shown in Table 1. The dependence of the film thickness on the substrate temperature is shown in Figure 2(a), while Figure 2(b) presents the dispersion curves of the refractive index.
Thickness, roughness, and refractive index at λ = 632.8 nm obtained using the Cauchy model.
Growth temperature (°C)
O2 flux (sccm)
Thickness (nm)
Roughness (nm)
n at 632.8 nm
650
1.0
13.1
0.65
1.864
700
1.0
12.1
0.78
1.868
750
1.0
11.6
1.02
1.876
650
1.5
18.8
0.54
1.875
700
1.5
17.1
0.36
1.879
750
1.5
16.7
0.48
1.873
(a) Film thickness dependence on the substrate temperature at fluxes of 1.5 and 1.0 sccm; (b) dispersion curves of the refractive index.
The reduction of thickness at high temperature is a result of increased desorption of Ga2O molecules on the growing surface whereas higher oxygen flux suppresses the desorption resulting in higher growth rates. For films grown at oxygen flux of 1.0 sccm, the refractive index shows a tendency to increase with the substrate temperature, while for films grown at flux of 1.5 sccm, the dependence of n on T is very weak.
XRD results confirmed the formation of the β-phase single crystal Ga2O3 on sapphire with excellent crystallinity. The X-ray diffractograms were measured in the 10–70° 2θ range. Figure 3 shows XRD spectra of films grown with an oxygen flux of 1.5 sccm and RF plasma power of 300 W at three different substrate temperatures, 650, 700, and 750°C. Three well-defined peaks at 18.9°, 38.4°, and 59.2° can be distinguished, corresponding to diffractions of (−201), (−402), and (−603) planes of β-Ga2O3. Besides the peaks associated to β-Ga2O3 and the substrate, no other significant peaks were found in the spectra, thus excluding the existence of another phase. The intensity of the XRD peaks shows a weak dependence on the growth temperature; higher intensity is observed at lower substrate temperature. Similar results were obtained for films grown at the same plasma power and substrate temperatures and oxygen flux of 1.0 sccm.
XRD spectra of β-Ga2O3 films grown on sapphire at power of 300 W and flux of 1.5 sccm.
High-resolution rocking curves of the peak at 38.4° corresponding to the <−402> plane of β-Ga2O3 confirmed the relation between the peak intensity and the temperature. Higher intensities were measured from films grown at 650°C (Figure 4), a result that is in agreement with the thickness dependence on the temperature (Figure 2).
High-resolution rocking curves corresponding to <−402> plane of β-Ga2O3 of films grown at 650, 700, and 750°C at fluxes of 1.0 and 1.5 sccm.
The UV-Vis spectroscopy results revealed that strong absorption of β-Ga2O3 starts at ∼270 nm, which corresponds to UV-C radiation. Figure 5 shows the UV-Vis spectra of sapphire substrate as well as of β-Ga2O3 thin films grown with RF plasma power of 200 and 300 W at two temperatures, 700 and 750°C. Sapphire is a highly transparent material and exhibits higher transmittance compared to the sapphire/β-Ga2O3 samples. The samples grown with an RF plasma power of 200 W exhibit a lower transmittance than that of samples grown at 300 W, which does not depend on the deposition temperature. In contrast, the increase of the substrate temperature for samples grown at 300 W leads to higher transmittance. The transmittance values shown in Figure 5 are lower than previously reported [14, 22, 23] because of light scattering by the unpolished side of the sapphire substrate.
UV-Vis spectra of sapphire substrate (circles) and β-Ga2O3 thin films grown at 700°C with RF plasma power of 200 and 300 W (squares and triangles) and at 750°C at the same powers (diamonds and crosses).
From the UV-Vis results, the optical bandgaps of the films were determined using the power law for direct bandgap semiconductors [22–26]:(1)αhν=Bhν−Eg1/2,where α is the absorption coefficient, hν is the photon energy, and Eg is the bandgap. The optical absorption coefficients were calculated using the ellipsometrically determined film thicknesses. Eg was estimated graphically by regression analysis of the linear part of the αhν2 versus hν dependence (Figure 6). The obtained values for films grown at 300 W are shown in Table 2 and are similar to previously reported values [27–29].
αhν2 versus hν dependence of Ga2O3 thin films grown at different substrate temperatures and a 1.5 sccm O2 flux.
Optical bandgaps of β-Ga2O3 thin films grown at 300 W at different temperatures and oxygen fluxes.
Growth temperature (°C)
O2 flux (sccm)
Eg (eV)
650
1.0
4.84
700
1.0
4.73
750
1.0
4.88
650
1.5
4.82
700
1.5
4.84
750
1.5
4.88
A schematic representation of the structure used in the electrical characterization is shown in Figure 7. I-V measurements were carried out between top Al contacts on Ga2O3 using voltage sweeps from 0 to ± 10 V in dark, as well as under UV light illumination. Symmetric characteristics were obtained at positive and negative voltages (Figure 8), excluding the formation of a Schottky contact between the Al contact and the thin films. The slight asymmetry is an instrumentation effect, which most likely results from the probe station or from small variation of the characteristics of the two source-monitor units (SMUs) of Keithley 4200 SCS. The results in Figure 8 were obtained using SMU1 as a “Force” and SMU2 as a “Ground” for measurements at positive and at negative voltages. By changing the SMU1 to “Ground” and SMU2 to “Force,” the absolute values of the current measured at negative voltages coincide with the current at positive voltages (inset in Figure 8). In the voltage range used, the photocurrent under 254 nm UV illumination reaches values ∼5 times higher than the dark current in both directions.
Schematic representation of the structure used in the I-V measurements.
Dark current and photocurrent measured under 245 nm UV illumination. The inset figure shows I-V characteristics measured using SMU1 as “Force” at positive and as “Ground” at negative voltages.
In order to prove that the observed photocurrent is exclusively due to UV-C excitation, the samples were exposed to illumination with light sources of 650 nm (red), 532 nm (green), and 366 nm (UV-A). In Figure 9, a plot of the electrical behavior of β-Ga2O3 thin films under different illuminations is shown proving that the photocurrent was generated only under UV-C exposure. The I-V results are in agreement with the UV-Vis measurements where strong absorption occurs at wavelengths shorter than 270 nm.
I-V characteristics of Ga2O3 thin films in dark and under different illuminations.
4. Conclusions
β-Ga2O3 thin films with high crystal quality were grown successfully on c-plane sapphire substrate by plasma-assisted molecular beam epitaxy. In this work, the combined effect of substrate temperature, RF plasma power, and oxygen flux was studied showing that at a fixed O2 flux the thickness of the grown film decreases with the increase of the temperature. Ellipsometry measurements revealed that, at oxygen flux of 1.0 sccm, the refractive index increases with the substrate temperature, while at flux of 1.5 sccm this dependence is very weak. The samples grown at 300 W RF plasma power exhibited higher transmittance than those grown at 200 W. Optical measurements showed that β-Ga2O3 starts to absorb at wavelengths lower than ∼270 nm, in the range of UV-C radiation. The electrical measurements under UV-C illumination showed that the grown thin films of β-Ga2O3 are excellent candidates for deep-ultraviolet sensing.
Conflicts of Interest
The authors declare that they have no conflicts of interest.
Acknowledgments
The authors thank CONACTY-México for the International Research Fellowship No. 290842 and National Research Fellowship No. 339617. The Autonomous University of Baja California is acknowledged for the financial support through the projects 3068 and UABC-PTC-634. Special acknowledgements are due to the MBE Lab Staff (Texas State University) for the support and use of their facilities.
DiffeyB. L.Sources and measurement of ultraviolet radiation200228141310.1016/s1046-2023(02)00204-92-s2.0-0036384201MonroyE.OmnèsF.CalleF.Wide-bandgap semiconductor ultraviolet photodetectors2003184R33R5110.1088/0268-1242/18/4/2012-s2.0-0037397570SklarL. R.AlmutawaF.LimH. W.HamzaviI.Effects of ultraviolet radiation, visible light, and infrared radiation on erythema and pigmentation: a review2013121546410.1039/c2pp25152c2-s2.0-84871231509ChenH.LiuK.HuL.Al-GhamdiA. A.FangX.New concept ultraviolet photodetectors201518949350210.1016/j.mattod.2015.06.0012-s2.0-84945447056HigashiwakiM.SasakiK.MurakamiH.Recent progress in Ga2O3 power devices201631303400110.1088/0268-1242/31/3/0340012-s2.0-84959432103BarticM.BabanC. I.SuzukiH.OgitaM.IsaiM.Beta-gallium oxide as oxygen gas sensors at a high temperature20079092879288410.1111/j.1551-2916.2007.01842.x2-s2.0-34548483427XiangY.ZhouC.WangW.Characterization of spin-coated gallium oxide films and application as surface passivation layer on silicon20176991192119810.1016/j.jallcom.2016.12.3202-s2.0-85009920680LawrenzF.LangeP.SeverinN.RabeJ. P.HelmC. A.BlockS.Morphology, mechanical stability, and protective properties of ultrathin gallium oxide coatings201531215836584210.1021/acs.langmuir.5b008712-s2.0-84930657864OritaM.OhtaH.HiranoM.Deep-ultraviolet transparent conductive β-Ga2O3 thin films200077254166416810.1063/1.1330559LiuJ.YanJ.ShiL.LiT.Electrical and optical properties of deep ultraviolet transparent conductive Ga2O3/ITO films by magnetron sputtering2010311010300110.1088/1674-4926/31/10/1030012-s2.0-78649418070ShanF. K.LiuG. X.LeeW. J.Structural, electrical, and optical properties of transparent gallium oxide thin films grown by plasma-enhanced atomic layer deposition200598202350410.1063/1.19805352-s2.0-23844468509ParisiA. V.KimlinM. G.TurnbullD. J.MacaranasJ.Potential of phenothiazine as a thin film dosimeter for UVA exposures200541190710.1039/b508553e2-s2.0-28044455198LeeM. E.ArmaniA. M.Flexible UV exposure sensor based on UV responsive polymer20161101251125510.1021/acssensors.6b004912-s2.0-85026370685OrtizA.AlonsoJ. C.AndradeE.UrbiolaC.Structural and optical characteristics of gallium oxide thin films deposited by ultrasonic spray pyrolysis20011482F2610.1149/1.13421832-s2.0-0008723743GartenL. M.ZakutayevA.PerkinsJ. D.Structure property relationships in gallium oxide thin films grown by pulsed laser deposition20166434835310.1557/mrc.2016.502-s2.0-84996995655Patil-ChaudhariD.OmbabaM.OhJ. Y.Solar blind photodetectors enabled by nanotextured β-Ga2O3 films grown via oxidation of GaAs substrates2017921710.1109/jphot.2017.26884632-s2.0-85018773116GuoD.WuZ.LiP.Fabrication of β-Ga2O3 thin films and solar-blind photodetectors by laser MBE technology201445106710.1364/ome.4.0010672-s2.0-84901453877ParkS. Y.LeeS. Y.SeoS. H.KangH. C.Self-catalytic growth of β-Ga2O3 nanowires deposited by radio-frequency magnetron sputtering201361010500110.7567/apex.6.1050012-s2.0-84887672314GhoseS.RahmanM. S.Rojas-RamirezJ. S.Structural and optical properties of β-Ga2O3 thin films grown by plasma-assisted molecular beam epitaxy201634202L10910.1116/1.49420452-s2.0-84960881336WollamJ. A.2014Lincoln, NE, USAJ. A. Woollam Co., Inc.FujiwaraH.2007Hoboken, NJ, USAJohn Wiley & Sons Ltd.Sampath KumarS.RubioE. J.Noor-A-AlamM.Structure, morphology, and optical properties of amorphous and nanocrystalline gallium oxide thin films201311784191420010.1021/jp311300e2-s2.0-84874623387RebienM.HenrionW.HongM.MannaertsJ. P.FleischerM.Optical properties of gallium oxide thin films200281225025210.1063/1.14916132-s2.0-79956015067GullapalliS. K.VemuriR. S.RamanaC. V.Structural transformation induced changes in the optical properties of nanocrystalline tungsten oxide thin films2010961717190310.1063/1.34215402-s2.0-77952410126RubioE. J.RamanaC. V.Tungsten-incorporation induced red-shift in the bandgap of gallium oxide thin films20131021919191310.1063/1.48038022-s2.0-84877994815ZhangF. B.SaitoK.TanakaT.NishioM.GuoQ. X.Structural and optical properties of Ga2O3 films on sapphire substrates by pulsed laser deposition20143879610010.1016/j.jcrysgro.2013.11.0222-s2.0-84888417879TippinsH. H.Optical absorption and photoconductivity in the band edge of β-Ga2O319651401A316A31910.1103/physrev.140.a3162-s2.0-36149011447MüllerS.von WencksternH.SplithD.SchmidtF.GrundmannM.Control of the conductivity of Si-doped β-Ga2O3 thin films via growth temperature and pressure201421113410.1002/pssa.2013300252-s2.0-84892914135VogtP.BierwagenO.Kinetics versus thermodynamics of the metal incorporation in molecular beam epitaxy of (InxGa1−x)2O320164808611210.1063/1.49615132-s2.0-84983628528