The relics built with soil are called earthen archaeological sites. Many silt earthen sites exposed to natural environment get seriously damaged and thus require urgent restoration with suitable materials. Previously, lime and glutinous rice slurry were used in the construction of earthen sites. However, lime is usually used in clay, and glutinous rice pulp is difficult to prepare and use on a large scale. Therefore, in this study, starch ether was selected to replace glutinous rice pulp. Lime and starch ether were added to silt as single or double additives, respectively, to prepare the corresponding single-mixed and multiple-mixed modified soil samples. Furthermore, the direct shear test and compression test were carried out and the optimum content was determined. The strength and durability of optimum modified materials were compared with those of the original site soil. When the lime content was 9% or the concentration of starch ether solution was 5%, the shear strength and compression resistance ability of single-mixed modified soil were improved significantly. When lime content was 6% and starch ether solution was 5%, the strength of multiple-mixed modified soil was the best, and the maximum cohesion and internal friction angle were 51.1 and 3.37% higher than those of single-mixed soil, respectively. The strength and durability of the optimum modified soil were similar to or higher than those of the site soil. Thus, it is feasible and effective to use lime together with starch ether as restoration material for silty earthen sites.
As a historical and cultural country, China has a large number of relics. The relics mainly built with soils are called earthen archaeological sites. Noteworthy, there are more than 900 earthen sites listed in the National Key Cultural Relics Protection Catalog of China [
Many earthen sites are large in scale, which are difficult to cover and isolate for protection. Most of them remain usually exposed and thus get significantly affected by natural environment. Many environmental factors, such as sandstorm, rainwater, biological properties, and atmospheric temperature, can cause damage to earthen sites and gradually affect their stability and safety. Recently, some earthen sites have collapsed and even disappeared. Therefore, a lot of more systematic explorations are urgently demanded to protect and restore these earthen sites.
Building materials are one of the important contents for restoration of earthen sites [
Moreover, many scholars have also proposed new soil-modified materials, which also provide new possibilities for the restoration of Earth sites. For example, Arab et al. confirmed the feasibility and effectiveness of using sodium alginate biopolymer for treating weak cohesive subgrades, in particular, under repeated traffic loads for pavement construction applications [
In recent years, progressively a greater number of Chinese scholars have conducted detailed researches on the protection of ruins and achieved a series of useful results [
Early research on restoration materials was mainly focused extensively on modern materials and less on traditional materials. In recent years, significant research efforts have been devoted to the study on traditional materials in the restoration of earthen sites. A number of common traditional materials, such as tung oil, glutinous rice pulp, and lime, have been used as building materials for historical earthen sites in ancient time. These materials are nontoxic, environment-friendly, and economical, with high strength and good durability. Peng et al. revealed that, after mixing with glutinous rice pulp, the mechanical properties of the triad soil became better, the impermeability was significantly improved, and the difference in appearance was not large [
In the existing researches, glutinous rice pulp is mainly used in mortar or triad soil as reinforcement, and lime is mainly utilized in stabilizing and reinforcing clay. Many earthen sites in Northwest China are located in silt areas. Considering the convenience and economic factors, silt is used as the main building material for earthen sites in this area. Silt has unique engineering characteristics. The poor particle gradation makes silt difficult to compact and causes poor engineering properties. The study on whether the lime and glutinous rice pulp are suitable for the restoration of silty earthen sites still needs further systematic explorations. Moreover, due to the difficulty to produce and control the quality of glutinous rice pulp, it is not considered suitable for large-scale application in practical engineering applications. The main component of glutinous rice pulp is starch, with the mass percentage of 75–77%. Moreover, previous studies also indicated that the strengthening mechanism of glutinous rice pulp is mainly based on the regulation of amylopectin on calcium carbonate crystallization in glutinous rice pulp [
In the present study, traditional materials including lime and starch ether were used to modify silt in order to restore silty earthen site. Lime and starch ether were added to silt singly or together to prepare the modified soil samples, respectively. The direct shear test, compression tests, and durability test were carried out. Through comparative analysis of the engineering properties of modified soil and original site soil, the modification effect and mechanism of lime and starch ether on silt were analyzed, and the optimal content was determined.
The main materials used in the tests were silt, lime, and starch ether. Silt was collected from the periphery of the Tongwan City site. The site is located in Jingbian County, Northwest China, with a history of nearly 1600 years. Through sieving and adjusting soil particles, the test soil was prepared as similar as possible to the original site soil in gradation and physical properties. The particle gradation and physical index of the two types of soil are presented in Tables
Particle-size distribution of test soil.
Particle-size distribution (%) | |||
---|---|---|---|
>0.5 mm | 0.5–0.25 mm | 0.25–0.075 mm | <0.075 mm |
2.8 | 19.7 | 27.1 | 50.4 |
Physical indexes of the original site soil and test soil.
Materials | Indicators | ||||
---|---|---|---|---|---|
Water content (%) | Specific gravity (%) | Liquid limit (%) | Plastic limit (%) | Plastic index | |
Site soil | 6.55 | 2.65 | 14.2 | 9.5 | 4.7 |
Test soil | 6.80 | 2.66 | 14.5 | 8.6 | 5.9 |
Particle-size distribution curve of test soil.
The lime used in the test was ordinary building lime with uniform and delicate particles (Figure
Test materials: (a) lime and (b) starch ether.
Physical indexes of lime.
Appearance | Porosity (%) | Ca (OH)2 (%) | Whiteness (%) | CaO (%) |
---|---|---|---|---|
325 meshes residual screening <0.5% | 32 | >65 | 90 | >30 |
Physical indexes of starch ethers.
Appearance | Solubility | Fineness ( | pH | Viscosity (mPa·s) | Water content (%) |
---|---|---|---|---|---|
White powders | Dissolved in cold water | ≤500 | 8–11 | >300 | <5% |
Lime and starch ether were added to slit as single or double additives, respectively, to prepare the corresponding single-mixed modified soil samples and multiple-mixed modified soil samples.
In the tests, the site soil was sampled with ring knife. The area of ring knife was 30 cm2 and the height was 20 mm.
In general, the volume ratio of lime to soil is 1 : 9, 2 : 8, and 3 :7 in practical engineering applications and the corresponding mass percentage of lime is about 6, 9, and 12%. Therefore, the mass percentages of lime used in the samples were selected as 0, 3, 6, 9, and 12%, respectively. During sample preparation, lime was mixed proportionally with dried soil, and water was added to the set content. Starch ether was mixed with water to prepare solutions with concentrations of 0, 5, 10, 15, and 20%, respectively. Then these solutions were mixed with soil and stirred evenly. The samples were prepared by static compaction; and the diameter and height of the so-obtained sample were 61.8 and 20 mm, respectively. The dry density was 2.07 g·cm−³ and the water content was 6.55%, which were similar to those of the original site soil. After the sample was prepared, it was sealed in a humidifying cylinder for 7, 14, and 28 days for experimental tests.
Based on the analysis and comparison of the single-mixed modified soil test results, the lime-soil mixtures with lime mass percentage of 6, 9, and 12% were prepared first, and then the starch ether solutions with concentrations of 5, 10, and 15% were added to the lime-soil mixtures to prepare multiple-mixed soil samples. The preparation method of the multiple-mixed soil samples was similar to that for single-mixed modified soil samples.
The direct shear test and compression test were carried out on the single-mixed modified soil and multiple-mixed modified soil samples at different ages.
According to the results of mechanical tests of the single-mixed modified soil and multiple-mixed modified soil samples, the optimum samples were selected to carry out the environmental durability tests, including wear test, freeze-thaw test, and water stability test. Same tests were carried out on the original earthen site soil samples as well for comparative analysis. There are few test standards for environmental durability of earthen sites; therefore, the environmental durability test performed herein was based on the existing relevant or similar test method . Wear test The natural environment of Tongwan City site is dry, windy, and sandy. As a famous historical site, many tourists visit this site every year and the contact between human and site is inevitable. Therefore, wind-sand erosion and contact wear are two important damage factors for the site. Figure SCL-1 disintegration test device is usually used to test the ability of rock to resist softening and disintegration. In this study, it was used to test the resistance of the site soil to contact wear under dry condition. Granular soil sample (30 g) was prepared and placed into the instrument. When the rolling cage started to rotate, contact wear of the samples occurred. Each group of samples was tested five times, and each time lasted for 10 min. After each test, the mass of the samples was measured and the wear ratio of the samples was obtained. Figure Freeze-thaw cycles test The main objective of this test was to study the influence of freezing and thawing on the soil and to obtain the variation ratio of the mass and volume of the samples. The test was carried out using an environment testing instrument, as shown in Figure The highest test temperature was 40°C and the lowest test temperature was −20°C. One test cycle started from high temperature to low temperature and then returned to high temperature. Each cycle lasted for 4 h, and the total number of cycles was 30. The samples were made into cubes with side length of 5 cm. The variation ratios of mass and volume of the samples were measured after every 10 cycles. Immersion stability test The surface of the earthen site gets easily eroded due to rainwater, which can cause damage of pits and gullies. In this study, the samples of modified soil and site soil were soaked in water, respectively, and immersion stability of different soils was compared by observing the disintegration degree of soil in water.
SCL-1 disintegration testing instrument.
The diagram of wind-sand blowing erosion device.
The environment testing instrument.
The lime or starch ether was added to the soil individually to prepare the single-mixed modified soil samples for the test.
For samples with different extent of ageing, the relationship curves of shear parameters with lime content and concentration of starch ether solution are shown in Figures
The relationship between shear strength parameters and lime content. (a) The relationship between cohesion and lime content. (b) The relationship between internal friction angle and lime content.
The relationship between shear strength parameters and concentration of starch ether solution. (a) The relationship between cohesion and concentration of starch ether solution. (b) The relationship between internal friction angle and concentration of starch ether solution.
The test results showed that the shear strength parameters of samples could be improved by adding lime or starch ether individually. Regarding samples age, the cohesion
Lime is the earliest and the most widely used cementitious material, and use of lime to modify soil is a common engineering method [
According to the test data, the reactions in lime soil were developed rapidly in the early stage, and reaction was relatively sufficient when the age reached 14 days. Further, the reaction speed slowed down. Moreover, when lime content was less than 9%, with the increase of lime content, the gel substances increased. Therefore, the connection of soil particles became stronger, the structure of soil became denser, and the strength of soil was enhanced due to the addition of lime. When the content of lime was more than 9%, the excessive NaOH crystal adhered to the surrounding of the soil particles, which hindered the connection between the soil particles, resulting in loose structure of lime soil and reduction of the strength. Therefore, the cohesion and internal friction angle of lime modified-soil increased when the lime content was less than 9% and decreased slightly when the lime content was more than 9%.
Starch ether is a type of modified starch with ether bond, which is also called etherified starch. Starch acquires certain viscosity after gelatinization. Etherified starch exhibits better viscosity and stability, and it is widely used in mortar construction, food, textile, and other fields. Addition of starch ether results in sticking together of the soil particles, which leads to the effective improvement in the shear strength of soil. Some scholars have also found that the slip resistance performance of the mortar gets significantly improved by adding starch ether [
When the concentration of starch ether solution was less than 5%, the bonding effect was found to be good and the strength of soil increased. However, when the concentration of starch ether solution was more than 5%, excessive starch ether solution became the lubricant between soil particles, which reduced the ability of the soil to resist shear. Therefore, the cohesion and internal friction angle of starch-ether-modified soil increased when the concentration of starch ether solution was less than 5% and decreased when the lime content was more than 5%. With respect to the addition of lime or starch ether, the optimum proportion should be selected in the actual project to obtain the best performance.
Considering that the shear strength parameters of lime- or starch-ether-modified soil tend to get stabilized after 28 days, the samples with 28-day age were selected for compression tests. The curves of variation of compression parameters with content of lime and starch ether are presented in Figures
The relationship between compression parameters and lime content. (a) The relationship between compression coefficient and lime content. (b) The relationship between compression index and lime content.
The relationship between compression parameters and concentration of starch ether solution. (a) The relationship between compression coefficient and starch ether concentration. (b) The relationship between compression index and starch ether concentration.
The compression coefficient
The test results clearly revealed that, with the increase of lime content, the compression coefficient and compression index of samples were basically reduced. When the lime content was 9%, the compression coefficient and compression index of lime-modified soil reached the minimum values, 0.037 MPa−1 and 0.0124, respectively. However, with the increase of starch ether concentration, the compression coefficient and compression index of the samples first decreased and then increased. The compression coefficient reached the minimum value of 0.056 MPa−1, when the concentration of starch ether solution was 5%. Moreover, the compression index reached the minimum value of 0.0266, when the concentration of starch ether solution was 10%. The compressibility coefficient and compression index of lime-modified soil were lower than those of starch-ether-modified soil. The mechanism explanation of consolidated compression test results is similar to that of direct shear test results.
The starch ether solution with different concentrations of 5, 10, and 15% was added to the lime soils with lime content of 6, 9, and 12%, respectively, in order to prepare the multiple-mixed modified soil samples for direct shear and compression tests. The results are as follows.
After adding starch ether solutions with different concentrations, respectively, to lime soil with 6, 9, and 12% lime content, the direct shear tests were performed on multiple-mixed modified soil samples and the corresponding results are shown in Figures
The relationship between shear strength parameters and concentration of starch ether solution (lime content: 6%). (a) The relationship between cohesion and starch ether concentration. (b) The relationship between internal friction angle and starch ether concentration.
The relationship between shear strength parameters and concentration of starch ether solution (lime content: 9%). (a) The relationship between cohesion and starch ether concentration. (b) The relationship between internal friction angle and starch ether concentration.
The relationship between shear strength parameters and concentration of starch ether solution (lime content: 12%). (a) The relationship between cohesion and starch ether concentration. (b) The relationship between internal friction angle and starch ether concentration.
Test results showed that the influence of curing age on multiple-mixed modified soil sample was found to be similar to that on single-mixed modified soil sample. After starch ether was added to lime soil, the cohesion and internal friction angle of multiple-mixed modified soil were generally higher than those of single-mixed modified soil containing same content of lime.
With the increase of starch ether concentration, the cohesion and internal friction angle of multiple-mixed modified soil first increased and then decreased. When the concentration of starch ether solution was 5%, the cohesion and internal friction angle of multiple-mixed soil reached the maximum values. Noteworthy, when the lime content was 6% and the starch ether concentration was 5%, the cohesion and internal friction angle of the multiple-mixed soil reached the maximum values, 121.4 kPa and 50.24°, respectively. The maximum values of cohesion and internal friction angle of the multiple-mixed modified soil were 67.6 and 3.37% higher than those of the lime-modified soil and were 51.1 and 18.8% higher than those of the starch-ether-modified soil, respectively.
For the comprehensive and visual understanding of the relationship between shear strength parameters, starch ether solution concentration, and lime content, the relationship between cohesion, concentration of starch ether solution, and lime content under different ages is shown in Figure
The relationship of cohesion, concentration of starch ether solution, and lime content under different ages: (a) 7 d age, (b) 14 d age, and (c) 28 d age.
The relationship of internal friction angle, concentration of starch ether solution, and lime content under different ages: (a) 7 d age, (b) 14 d age, and (c) 28 d age.
For the comprehensive and visual understanding of the relationship between shear strength parameters, starch ether solution concentration, and lime content, the relationship between cohesion, concentration of starch ether solution, and lime content under different ages is shown in Figure
Figures
In multiple-mixed modified soil, when lime reacts with soil, starch ether also binds particles. Under such double effect, the strength of multiple-mixed modified soil becomes higher than that of single-mixed soil. The water contents in multiple-mixed and single-mixed soil are the same. The comparative analysis indicates that, in single-mixed modified soil, water reacts with lime or starch ether alone. In contrast, in multiple-mixed modified soil, the same amount of water is required to interact with both lime and starch ether at the same time, which may lead to insufficient reaction. As a result, the strengthening effect of lime and starch ether on multiple-mixed modified soil is not as much as that on single-mixed soil. Therefore, although the strength of multiple-mixed modified soil is higher, its value is not the simple summation of the strength of lime-modified soil and starch-ether modified soil but is lower than this summation.
Moreover, the optimal lime content of the single-mixed soil was 9%, while the optimal lime content of the multiple-mixed soil was decreased to 6%. Starch ether has better water absorption and retention properties; thus the actual reaction of water with lime in the multiple-mixed soil is relatively less, which leads to the increase in the content of unreacted lime, resulting in the decrease of soil strength. Therefore, in the multiple-mixed soil sample, the optimal content of lime gets reduced.
The compression test results of the samples with 6, 9, and 12% lime content with different concentrations of added starch ether solution are shown in Figure
The relationship between compression parameters and starch ether concentration of multiple-mixed modified soil with different lime content. (a) The relationship between compression coefficient and starch ether concentration. (b) The relationship between compression index and starch ether concentration.
When the concentration of starch ether solution was 5%, the compression coefficient and compression index of modified soil containing different lime contents were generally close to the minimum value. Noteworthy, when the concentration of starch ether solution was less than 5%, the content of lime exhibited significant influence on the compression coefficient and compression index of multiple-mixed modified soil. In contrast, when the concentration of starch ether solution was more than 5%, the effect of lime content on the compressibility of soil was not significant. The mechanism explanation of compression test results is also similar to that of direct shear test results.
Therefore, for multiple-mixed modified soil, when the lime content was 6% and the starch ether concentration was 5%, the shear strength reached the maximum value and the compressibility acquired the minimum value. Compared to those of single-mixed modified soil, the engineering properties of multiple-mixed modified soil were significantly improved.
Most earthen sites are generally exposed to the natural environment; thus, environmental factors have significant impact on the integrity and safety of these earthen sites. Therefore, in addition to mechanical properties, environmental durability should also be an important characteristic of restoration materials for earthen sites. According to the above-mentioned test results, the modified soil can obtain better mechanical properties after adding 5% starch ether solution and 6% lime. Therefore, this type of multiple-mixed modified soil was selected as the optimum material for environmental durability testing. The engineering properties of this optimum modified soil were comprehensively compared with those of the original site soil to verify its suitability and feasibility as a restoration material for earthen sites.
Table
Shear strength and compressibility indexes of original site soil and modified soil.
Sample | Parameter | |||
---|---|---|---|---|
Cohesion (kPa) | Internal friction angle (°) | Compressibility coefficient (MPa−1) | Compression index | |
Site soil | 110.07 | 40.51 | 0.072 | 0.078 |
Modified soil | 121.40 | 50.24 | 0.042 | 0.016 |
The test results of original site soil and modified soil in contact wear test and wind-sand erosion test are shown in Figures
The results of contact wear test.
The results of wind-sand erosion test.
The results indicated that the mass loss ratio of modified soil was larger than that of original site soil. In the contact wear test, the difference of test results between two types of samples was relatively small; however, in the wind-sand erosion test, this difference was significant. The reaction between lime and soil is a long-term process. Although the strength of the modified soil increased rapidly in the early stage and slowly in the later stage, the age of modified soil was only 28 days. Considering that the original site soil has existed for thousands of years, the cumulative growth value of the soil strength and structure in the later stage cannot be ignored altogether in such a long time. Therefore, the mass loss ratio of original site soil was found to be relatively small, which is likely to be related to the short age and insufficient soil structure of the modified soil. Thus, herein, the more comprehensive reason requires further in-depth investigation in the future.
Table
Freeze-thaw cycles test results of original site soil and modified soil.
Indicators | Sample | Number of freeze-thaw cycles | ||
---|---|---|---|---|
10 | 20 | 30 | ||
Mass variation ratio (%) | Site soil | −0.12 | −0.13 | −0.15 |
Modified soil | −0.13 | −0.15 | −0.18 | |
Volume variation ratio (%) | Site soil | −0.62 | −0.78 | −3.58 |
Modified soil | −0.76 | −0.88 | −1.67 |
Water is an important factor to investigate the damage of earthen sites. Therefore, immersion stability is another necessary property to be considered for restoration materials for earthen sites. After 30 min of water immersion, the disintegration degree of the original site soil and modified soil was obtained as shown in Figure
Comparative analysis of water immersion stability: (a) original site soil and (b) modified soil.
Clearly, after water immersion, the site soil sample disintegrates seriously; nonetheless, the modified soil sample hardly disintegrates. Calcium hydroxide in lime of modified soil crystallizes after absorbing water to form crystal lattice structure. The formed crystals get easily combined with each other and can be combined with soil particles to form eutectic. In this way, the soil particles are cemented as a whole. Compared to the non-crystallinity of calcium hydroxide, the solubility of calcium hydroxide crystal is almost reduced by half, thus improving the water stability of modified soil.
Moreover, noteworthy, the pH of the original test soil is 7.9, which belongs to alkaline soil. Lime and starch ether are basic materials; thus, the pH of modified soil increases to 9.3. In general, when the pH of soil is greater than 9.0, it is not suitable for the plants to grow. Therefore, the strong alkalinity of modified soil can avoid the damage caused due to plant growth, which is beneficial to the restoration and protection of earthen sites.
Importantly, economy is another factor to be considered in practical engineering. Lime and starch ether are widely used materials because of their cost-effectiveness. It is estimated that, by using 6% lime and 5% starch ether to modify silt, the cost of each ton of modified soil increases by only 54.27 RMB, equivalent to 7.75 US dollars. Therefore, the material selected in this study also has good economic value.
In this study, the restoration materials for silty earthen sites have been studied using lime and starch ether to modify the soil. A series of tests on the modified soil have been carried out, and the engineering properties of the modified soil and the original site soil have been compared. The conclusions of the study are listed as follows.
The shear strength and compressive ability of soil could be improved significantly by adding lime or starch ether individually. For single-mixed modified soil, the optimum lime content is 9%, and the cohesion and internal friction angle of the modified silt are 72.45 kPa and 48.6°, respectively. The optimal concentration of starch ether solution is 5%, and the cohesion and internal friction angle of the modified silt are 80.32 kPa and 42.3°, respectively. The deformation of the modified soil with the optimum content also reaches the minimum value.
Furthermore, the shear strength and compressibility of multiple-mixed modified soil were generally higher than those of single-mixed modified soil. For the multiple-mixed modified soil, when the lime content was 6% and the starch ether concentration was 5%, the shear strength was found to be the largest and the compressibility was the smallest. The maximum values of cohesion and internal friction angle of multiple-mixed modified soil were 67.6 and 3.37% higher than those of the lime-modified soil and were 51.1 and 18.8% higher than those of the starch-ether-modified soil, respectively. Therefore, compared to those of single-mixed modified soil, the mechanical properties of multiple-mixed modified soil were significantly improved.
For the multiple-mixed modified soil with the optimum content, the environmental durability was also similar to or higher than that of the original site soil. These results clearly indicated that the main engineering properties of the optimum modified soil are generally similar to those of the original site soil. Moreover, the restoration material selected in this study also has good economic value. Therefore, it is feasible and effective to use lime together with starch ether as an efficient restoration material for earthen sites.
The data used to support the findings of this study are included within the article.
The authors declare that there are no conflicts of interest regarding the publication of this paper.
This work was funded by Shaanxi Natural Science Foundation Project (Grant no. 2020JM-235), Shaanxi Postdoctoral Research Funding Project (2017BSHEDZZ114), the Open Project of State Key Laboratory of Green Building in Western China (LSKF 201905), and Science and Technology Planning Project of Yulin Technology Division (214028170376).