Advances in Materials Science and Engineering
Volume 2020 (2020), Article ID 9605941, 9 pages
https://doi.org/10.1155/2020/9605941

Research Article

Effects of Curing Time on the Mechanical Property and Microstructure Characteristics of Metakaolin-Based Geopolymer Cement-Stabilized Silty Clay

Zhang Rong-rong1,2,3 and Ma Dong-dong1,2,3

¹Research Center of Mine Underground Engineering, Ministry of Education, Anhui University of Science and Technology, Huainan 232001, China
²School of Civil Engineering and Architecture, Anhui University of Science and Technology, Huainan, China
³State Key Laboratory of Mining Response and Disaster Prevention and Control in Deep Coal Mine, Anhui University of Science and Technology, Huainan, Anhui 232001, China

Correspondence should be addressed to Ma Dong-dong; dongdonm@126.com

Received 6 May 2019; Revised 18 August 2019; Accepted 20 September 2019; Published 14 February 2020

Academic Editor: Antonio Boccaccio

Copyright © 2020 Zhang Rong-rong and Ma Dong-dong. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

Metakaolin (MK), which has a fine particle size and higher activity in high alkaline environments, has been widely used in the fields of soil treatment engineering to stabilize soils. MK is used to replace part of ordinary Portland cement (OPC) with 0 : 15, 2 :13, 4 : 11 and 6 : 9 mass ratios of MK to OPC in this study. The mechanical property (e.g. stress-strain relationship, strength, and deformation performance) and microstructure characteristics of MK-based geopolymer cemented silty clay are investigated using unconfined compressive strength (UCS), nuclear magnetic resonance (NMR), and scanning electronic microscopy (SEM) tests. In addition, strength increase coefficient (ζs) and elasticity modulus increase coefficient (ζe) are defined to evaluate the effects of curing time on the mechanical property of MK-based geopolymer cemented silty clay. Moreover, the relationships among porosity, UCS, and E₅₀ of MK-cemented silty clay are studied. By incorporating 2% MK, the UCS and E₅₀ of MK-cemented silty clay at 28 d are 1.32 and 1.30 times compared with MK0 group, respectively. The increase rate of UCS and E₅₀ from 1 d to 7 d is faster compared with that from 7 d to 28 d. Furthermore, the microstructure of the sample modified by 2% MK is most homogeneous and dense. Finally, the optimistic mass ratio between MK and cement is 2 : 13 for silty clay in this test condition.

1. Introduction

Cement soil reinforcement technique has been accepted worldwide in the areas of foundation engineering, slope reinforcement, road construction, and rammed earth wall engineering for many years [1–5]. It has been proved as an effective reinforcement technique with many advantages, such as high usage rate of origin soil, low cost, and convenient construction [6, 7]. However, in the cement production process, about 900 kg CO₂ will be emitted into the atmosphere per tonner of cement which contributed to global warming and climate change [8–11]. Therefore, some supplementary cementitious materials (e.g., metakaolin, fly ash, slag, and nanosilica) have been used for replacing part of cement to reduce CO₂ emission associated with cement production [12–14].

As a typical pozzolanic material, metakaolin (MK) is an amorphous aluminosilicate compound produced by calcinations of pure kaolinite at 500°C to 550°C [15], which has high activity and has attracted increasing attention in recent years that could partly replace ordinary Portland cement [16]. Compared with other supplementary cementitious materials, MK has many advantages, including higher activity, larger specific surface, and finer particle size [17]. Studies have emerged that offer contradictory findings about the effects of MK content on physical and mechanical properties of cement soil and concrete materials and acquired abundant accomplishment [15, 16, 18–23]. Wu et al. [15] studied the effect of MK contents on the strength performance of cement-modified soil, and test results reveal that both the unconfined compression and splitting tensile strengths are improved, and the suitable ratio of MK to cement ranges from 1/3 to 1/2. Moreover, the addition of MK led to a higher quantity of hydration products and denser microporosity distribution according to X-ray diffraction (XRD), scanning electronic microscopy (SEM), thermogravimetric analysis (TGA), and mercury intrusion porosimetry (MIP) test results, and a similar series of experiment results are also found [19]. Wang et al. [22] investigated the effects of curing time and coal-metakaolin content on the properties of cemented sandy soils, and test results indicate that the unconfined compression strength at 28 d was improved by 1.68–2.18 times by incorporating coal-metakaolin. Furthermore, similar tests were performed on cemented silty soil, and the optimum mass ratio of coal-metakaolin to cement is between 1 : 6.5 and 1 : 4 [23]. Experimental and theoretical results mentioned above show that MK can significantly improve the strength property of concrete and cemented soils at the appropriate proportion. Meanwhile, the optimum mass ratio of MK to cement is affected by the soil and MK types and test conditions including purity and grain sizes.

Curing time has a significant influence on chemical reaction degree between cement, MK, and water [24, 25], which affects the strength and deformation properties of MK-based geopolymer cemented soil. Specifically, MK-based geopolymer cemented soil requires sufficient time to achieve high mechanical properties and elevated durability. However, by summarizing the theoretical and experimental studies achievements, it can be found that researches mainly concentrate on the MK content and its improvement mechanisms, but there are still insufficient data for effect of curing time, especially at an early curing age. In addition, studies focused on microstructure characteristics of MK cement soil under different curing times are relatively insufficient. Hence, the objective of this research is to investigate the effects of curing time on mechanical property (i.e., unconfined compressive strength, elasticity modulus, and stress-strain relationship) and microstructure characteristic of cement-stabilized soil incorporate with different MK contents. The mass ratio of binder (cement and MK) to dry soil is 15% in this test. Finally, SEM and nuclear magnetic resonance (NMR) techniques are used to study the porosity and microstructure characteristic of MK cement silty clay with 26.5% water content, to analyze the internal microstructure change of MK-cemented silty clay under different MK contents (i.e., 0%, 2%, 4%, and 6%) and curing times (i.e., 1 d, 3 d, 7 d, 14 d, and 28 d).

2. Materials and Experimental Methods

2.1. Materials

The soil used in this study was collected from a foundation reinforce engineering in Huainan (Anhui, China). The physical properties of the soil are shown in Table 1. According to the Chinese National Standard GB 50021-2001 (2009 version) [26], it was categorized as “silty clay.”

Table 1: Physical properties of soil.

Properties
Values

Liquid limit (%)
29.5

Plastic limit (%)
43.6

Plasticity index
14.1

Medium sand content (0.425 mm < diameter < 2 mm)
16.7%

Fine sand content (0.075 mm < diameter < 0.425 mm)
27.1%

Silt and clay content (diameter < 0.075 mm)
56.2%

Soil classification-GB 20021 (Chinese standard)
Silty clay

The ordinary Portland cement (OPC) and MK in this experiment were produced by Bagongshan cement plant and Shanghai HaoFu chemical company, respectively. The chemical compositions of OPC and MK are listed in Table 2. The average particle size, specific surface area, and activity index of MK were 1 μm, 2000 m²/kg, and 122, respectively. From Table 2, it was clearly noticed that the main components of MK were SiO₂ and Al₂O₃.

Table 2: Chemical compositions of OPC and MK.

Oxide content (%)
SiO₂
Al₂O₃
CaO
Fe₂O₃
SO₃
MgO
Na₂O
K₂O
TiO₂

OPC
17.8
5.7
67.5
3.7
2.8
1.4
0.6
0.5
—

MK
53.8
43.1
0.6
0.8
—
0.2
0.2
0.1
1.2

2.2. Sample Preparation

The undisturbed silty clay was put in a dryer at 105°C for more than 24 h to constant weight and then crushed and sifted larger size (2 mm) from the sample. Thereafter, water equal to the original water content (26.5%) was added continuously to the mixture and mixed for about 30 min, and then the silty clay was stored in a closed container for more than 24 h to make the soil saturated. In this experiment, 15% binder (mass ratio of binder to dry soil) was adopted to stabilize the silty clay according to the design guidelines for cemented soil pile established by standard JGJ 79-2012 [27]. The mass ratios of MK to OPC in this test were 0 : 15, 2 : 13, 4 : 11, and 6 : 9, respectively, and the corresponding group were designated MK0, MK2, MK4, and MK6, respectively. Sample preparation procedure was as follows: (1) put MK into the silty clay and mix evenly; (2) mix sodium silicate and NaOH solution (50% concentration) with the mass ratio of 5.8 to 1 for the preparation of alkali activator [28], and then spray them into the mixture equably with a sprinkling can; and (3) add the calculated cement into the mixture and the corresponding water. The action of alkali activator used in this test can provide alkaline environment for MK to perform a three-dimensional network structure which is composed of silica tetrahedron and alumino-octahedron, as shown in Figure 1.

Figure 1: Formation of high-performance geopolymer [29].

2.3. Unconfined Compressive Strength (UCS) Test

The final mixture was divided into five portions and put into a cubic mold with dimensions of 70.7 mm × 70.7 mm × 70.7 mm according to specification for the mix proportion test of cement-mixed soil established by standard JGJ/T 233-2011. To conduct the UCS test, the top of each layer was scratched before adding the next layer to promote suitable bonding. The MK-based geopolymer cemented silty clay samples were removed from the molds after 24 h, and each sample was cured in a standard concrete materials curing room with temperature of (20 ± 2)°C and humidity of (95 ± 2)% [30]. These samples were tested after curing 1 d, 3 d, 7 d, 14 d, and 28 d to determine their unconfined compressive strengths. The UCS tests were conducted by an RWS-200 microcomputer controlled electronic universal testing machine at a loading rate of 1 mm/min. Furthermore, three parallel samples were prepared to improve the test reliability, and test results were considered suitable for presenting if their average error was less than 5%.

2.4. NMR Test

NMR technology has been widely used to obtain the pore structures of cement-based materials [31–35], which was conducted to measure the porosity of MK-based geopolymer cemented soil under different test conditions in this test. In NMR tests, dimension of Φ50 mm × 50 mm is the maximum size for NMR device. The maximum particle diameter for MK-based stabilized clays is the soil particle with 2 mm, and the larger the specimen size, the precise the test results. In addition, considering the possible damage in sample transport process, specimens with the size of Φ50 mm × 25 mm under different curing times and MK contents are prepared for NMR tests.

2.5. SEM Test

Quanta FEG 650 pattern environmental scanning electron microscope was used to investigate the microstructure characteristic of MK-based geopolymer cemented soil under different MK contents and curing times, all of the samples were obtained from the central part of complete samples [36, 37]. These samples were coated with gold for improving their conductivity before imaging. The SEM instrument was operated at 10 kV.

3. Test Results and Discussion

3.1. Stress-Strain Relationship and Failure Mode

The typical stress-strain curves of MK-based geopolymer cemented silty clay obtained from UCS tests are shown in Figure 2. Figure 2(a) is the stress-strain curves of MK0 group at different curing times. The aforementioned figure reveals that with the increase of curing time, the peak stress increases while the stress decreases sharply after peak strain, and the corresponding failure modes change from plastic failure to brittle failure. Figure 2(b) illustrates that at 1 d, the stress of MK6 group increases slowly with increasing axial strain compared with that for MK0, MK2, and MK4 group. With the increase of axial strain, the increase rate of MK2 group is higher compared with other groups.

(a)

(b)

Figure 2: Typical stress-strain curves of MK-cemented silty clay. (a) MK0 at different curing times. (b) Curing time 1 d with different MK contents.

3.2. UCS and Elasticity Modulus

UCS and elasticity modulus are two significant parameters to evaluate the resistance ability of MK-cemented silty clay subject to external loading. In this test, the peak stress is defined as the UCS, and the elasticity modulus (E₅₀) is defined as the slope between the original point and 0.5 UCS. Test data of UCS and E₅₀ of MK-based geopolymer cemented silty clay under different MK contents and curing times are shown in Figure 3.

(a)

(b)

(c)

(d)

Figure 3: UCS and E₅₀ test results of MK-cemented silty clay. (a) UCS at different MK contents, (b) UCS at different curing times, (c) E₅₀ at different MK contents, and (d) E₅₀ at different curing times.

Figure 3 reveals that both the UCS and E₅₀ increase with the increase of curing time, and the increase rate shows obviously different at different curing time periods, specifically, the increase rate of UCS and E₅₀ from 1 d to 7 d is faster compared with that from 7 d to 28 d. In addition, with the incorporation of MK, both the UCS and E₅₀ show first increase and then decrease, and the average values of UCS and E₅₀ of MK2 and MK4 groups are larger compared with that of MK0 group under the same curing time. However, both the UCS and E₅₀ of MK6 group are smaller than those of MK0 group, indicating that too much MK content weakens the property of MK-cemented silty clay. For example, at 28 d, the average values of UCS and E₅₀ of MK2 group are 1.32 and 1.30 times compared with the control group MK0, respectively, agreeing with the previous study results [22]. However, these values of MK6 group are only 0.53 and 0.59 times compared with MK0 group. Hence, the optimal mass ratio between MK and cement is 2 : 13 in this experiment, and the corresponding strength of MK-cemented silty clay is the highest. As a contrast, Wang et al. [22] found a similar optimum mass ratio (1 : 6.5–1 : 4) for CMK cemented silty soil, and 1 : 4 mass ratio was found for sandy soil [23]. Wu et al. [15] reported that the optimum mass ratio ranges from 1/3 to 1/2 for silt sand. The reactivity degree of geopolymer and cement is affected by test conditions. Hence, the difference between the above test results may be caused by the soil and MK types [38, 39].

After a detailed evaluation of the changes in the UCS and E₅₀ data, to evaluate the effect of curing time on the mechanical property of MK-cemented silty clay, strength increase coefficient (ζs) and elasticity modulus increase coefficient (ζe) are defined in this research and can be calculated as follows:

where UCSn and UCS₂₈ are the unconfined compressive strength of MK-cemented silty clay at curing time of n d and 28 d, respectively. E50n and E50,28 are the elasticity modulus of MK-cemented silty clay at curing time of n d and 28 d, respectively.

Figure 4 presents the calculated results of ζs and ζe at different curing times. It is clearly noticed that (1) compared with MK0, MK2, and MK4 groups, MK6 group shows relatively small values of ζs and ζe from 1 d to 7 d because there have been no sufficient hydration products to react with geopolymer. For MK6 group, the values of ζs at 1 d and 3 d are 21.9% and 40.6%, respectively, which are much lower than those of other three groups; (2) the values of ζs and ζe for MK2 and MK4 groups are higher than those of MK0 group at 1 d; however, the values of ζs and ζe are close to MK0, MK2, and MK4 groups from 3 d to 28 d. In addition, ζs can reach 75.8% to 77.8% at 7 d for MK0, MK2, and MK4 groups, and the corresponding values of ζe range from 79% to 80.8%, indicating that these three groups show better early strength and deformation resistance ability.

(a)

(b)

Figure 4: Test results of ζs and ζe of MK-cemented silty clay at different curing times. (a) ζs and (b) ζe.

In ground treatment and foundation supporting design engineering practice, the ratio between E₅₀ and UCS is an important evaluation parameter which should lie in the range of 100 to 120 according to the standard JGJ 79-2012. Hence, the relationship between E₅₀ and UCS at different curing times in the present study and other test results [40] are collected and shown in Figure 5. Yilmaz and Ozaydin [40] found that the ratio between E₅₀ and UCS of belite cement (BC) clay and ordinary Portland cement (OPC) clay were 79 and 107, respectively. The ratio between E₅₀ and UCS lied in the range of 60 to 145 in the present study. In addition, most of the test results at 28 d satisfy the standard request.

Figure 5: Test results between E₅₀ and UCS of MK-cemented silty clay.

3.3. NMR Results

The porosity of MK-based geopolymer cemented silty clay with different test conditions are measured by NMR. The obtained NMR data are presented in Table 3. The test samples with 6% MK content at curing time of 1 d, 3 d, and 7 d fall to pieces during saturated process because of their low strength. Moreover, the relationships among porosity, UCS, and E₅₀ are shown in Figure 6.

Table 3: Porosity results of MK-cemented silty clay.

Curing time (d)
MK content (%)
Porosity (%)

1
0
25.84

2
22.92

4
26.21

6
—

3
0
24.77

2
22.52

4
25.80

6
—

7
0
24.23

2
21.88

4
25.44

6
—

14
0
23.85

2
21.67

4
24.78

6
27.89

28
0
23.25

2
21.22

4
24.31

6
27.12

Figure 6: Relationships between porosity and of UCS and E50.

Table 3 reveals that at the same curing time, MK2 group shows the smallest porosity values compared with other three groups. Moreover, the porosity decreases with increasing curing time at the same MK content, which is attributed to the pozzolanic reaction between geopolymer, cement, and water [41]. Figure 6 illuminates that both UCS and E₅₀ of MK-based geopolymer cemented silty clay decrease with the increase of porosity and exhibit a linear correlation. In this test, the porosity of MK-based geopolymer cemented soil increases from 21.22% to 26.21%, the corresponding values of UCS decreases from 2.95 MPa to 0.92 MPa, while it decreases from 303 MPa to 117 MPa for E₅₀, and the decreasing degrees of them are 69.5% and 61.4%, respectively.

3.4. SEM Analysis

The microstructure can reflect the variations of physical and mechanical properties of MK-based geopolymer cemented silty clay [15, 22, 23]. SEM tests are conducted to observe the microstructure characteristic and hydration products in the bulk binder phase.

Figure 7 shows the SEM images of samples at curing time of 28 d with different MK contents at 800x amplification. MK content has a significant influence on the microstructure characteristic of MK-based geopolymer cemented soil. Figure 7(a) is the representative SEM images of MK0 group. It can be found that the microstructure of mixture without MK is loose and not uniform, and some cracks and pores are observed between soil particles. As a contrast, Figure 7(b) demonstrates that with the incorporation of MK, the microstructure of MK2 group is relatively denser and uniform, while the number of cracks and pores clearly decrease. This finding primary attributes to accelerate cement hydration caused by secondary reaction between geopolymer and hydration product of cement [29]. For the MK4 group, there exist more cracks and pores compared with that of MK2 group, while better than that of MK0 group. Furthermore, widely distributed cracks and pores are found for MK6 group, which also exhibits the loosest microstructure. Hence, 6% MK content has a negative effect on MK-based geopolymer cemented silty clay, which reduces its UCS and E₅₀. By comparing the microstructure characteristics of four groups, it is obvious that the microstructure of the sample modified by 2% MK is most homogeneous and dense.

(a)

(b)

(c)

(d)

Figure 7: SEM images of at 28 d with different MK contents. (a) MK0, (b) MK2, (c) MK4, and (d) MK6.

Figure 8 represents SEM images of MK2 group with different curing times at 800x and 12000x amplification, respectively. The SEM images at 800x amplification can easily observe the cracks and pores inside, while the microcracks, micropores, and hydration products such as C-S-H, which improve the property of MK cemented soil [41], can be observed at 12000x amplification. As shown in Figure 8(a), loose microstructure and lots of cracks and pores are found at 1 d, meanwhile, a small quantity of C-S-H is observed on the surface of the soil particles because there has been no sufficient time for cement hydration reaction. At 3 d and 7 d, due to the accelerate cement hydration caused by geopolymer, a number of C-S-H can be obviously found and some of them have filled in the pores, while the size of micropores and microcracks decreases with increasing curing time, as shown in Figures 8(b) and 8(c). From Figure 8(d) it can be clearly noticed that no obvious cracks can be observed at curing time of 14 d, and a number quantity of C-S-H has covered most of the soil particles and connected with each other. Figure 8(e) illustrates that the structure of MK2 at 28 d is denser, while both macropores and micropores are filled with C-S-H, thereby improving its macromechanical properties, such as strength and elastic modulus.

(a)

(b)

(c)

(d)

(e)

Figure 8: SEM images of MK2 group with different curing times. (a) 1 d, (b) 3 d, (c) 7 d, (d) 14 d, and (e) 28 d.

4. Conclusions

(1)Both the UCS and E₅₀ increase with the increase in curing time, and the increase rate from 1 d to 7 d is faster compared with that from 7 d to 28 d. With the incorporation of MK, both the UCS and E₅₀ show the regular first increase and then decrease. 2% MK content shows the highest UCS and E₅₀ in this test, and the average values of them are 1.32 and 1.30 times compared with MK0 group at 28 d, respectively. In addition, the ratio between E₅₀ and UCS lied in the range of 60 to 145 in the present study, and most of the test results at 28 d satisfy the standard request.(2)NMR results indicate that at the same curing time, the MK2 group shows the lowest porosity compared with other three groups. Moreover, the porosity decreases with increasing curing time. Both the UCS and E₅₀ of the MK-based geopolymer cemented silty clay decrease with the increase of porosity and exhibit a linear correlation. In this test, the porosity of MK-based geopolymer cemented silty clay increases from 21.22% to 26.21%, the corresponding values of UCS decreases from 2.95 MPa to 0.92 MPa, while it decreases from 303 MPa to 117 MPa for E₅₀.(3)SEM results reveal that the microstructure of the sample modified by 2% MK is most homogeneous and dense compared with other MK content groups. With the increasing curing time, the size of both micropores and microcracks decrease which contributes to improving its strength and elastic modulus.

Data Availability

The datasets generated and analyzed during the current study are available from the corresponding author on reasonable request.

Conflicts of Interest

The authors declare that there are no conflicts of interest regarding the publication of this paper.

Acknowledgments

This research received financial support from Anhui Provincial Natural Science Foundation (no. 1908085QE212) and Doctoral Fund Project of Anhui University of Science and Technology (nos. 11695 and 13190025). The authors thank the Engineering Research Center of Underground Mine Construction, Ministry of Education, Anhui University of Science and Technology, and State Key Laboratory of Mining Response and Disaster Prevention and Control in Deep Coal Mine, for providing the experiment conditions.

References

F. Xu, H. Wei, W. X. Qian, and T. B. Cai, “Composite alkaline activator on cemented soil: multiple tests and mechanism analyses,” Construction and Building Materials, vol. 188, pp. 433–443, 2018.

K. Yao, W. Wang, N. Li, C. Zhang, and L. X. Wang, “Investigation on strength and microstructure characteristics of nano-MgO admixed with cemented soft soil,” Construction and Building Materials, vol. 206, pp. 160–168, 2019.

N. C. Consoli, D. A. Rosa, R. C. Cruz, and A. D. Rosa, “Water content, porosity and cement content as parameters controlling strength of artificially cemented silty soil,” Engineering Geology, vol. 122, no. 3-4, pp. 328–333, 2011.

A. J. Choobbasti, H. Tavakoli, and S. S. Kutanaei, “Modeling and optimization of a trench layer location around a pipeline using artificial neural networks and particle swarm optimization algorithm,” Tunnelling and Underground Space Technology, vol. 40, pp. 192–202, 2014.

C. A. Anagnostopoulos, “Strength properties of an epoxy resin and cementstabilized silty clay soil,” Applied Clay Science, vol. 114, pp. 517–529, 2015.

S. Kolias, V. Kasselouri-Rigopoulou, and A. Karahalios, “Stabilisation of clayey soils with high calcium fly ash and cement,” Cement and Concrete Composites, vol. 27, no. 2, pp. 301–313, 2005.

J. M. Ortega, M. D. Esteban, I. Sanchez, and M. A. Climent, “Performance of sustainable fly ash and slag cement mortars exposed to simulated and real in situ mediterranean conditions along 90, warm season days,” Materials, vol. 10, no. 11, p. 1254, 2017.

F. Pacheco-Torgal and S. Jalali, “Reusing ceramic wastes in concrete,” Construction and Building Materials, vol. 24, no. 5, pp. 832–838, 2010.

A. M. Rashad and S. R. Zeedan, “The effect of activator concentration on the residual strength of alkali-activated fly ash pastes subjected to thermal load,” Construction and Building Materials, vol. 25, no. 7, pp. 3098–3107, 2011.

E. Benhelal, G. Zahedi, E. Shamsaei, and A. Bahadori, “Global strategies and potentials to curb CO₂ emissions in cement industry,” Journal of Cleaner Production, vol. 51, pp. 142–161, 2013.

F. Pelisser, E. L. Guerrino, M. Menger, M. D. Michel, and J. A. Labrincha, “Micromechanical characterization of metakaolin-based geopolymers,” Construction and Building Materials, vol. 49, pp. 547–553, 2013.

A. M. Rashad, “Alkali-activated metakaolin: a short guide for civil engineer—an overview,” Construction and Building Materials, vol. 41, pp. 751–765, 2013.

A. Al-Swaidani, I. Hammoud, and A. Meziab, “Effect of adding natural pozzolana on geotechnical properties of lime-stabilized clayey soil,” Journal of Rock Mechanics and Geotechnical Engineering, vol. 8, no. 5, pp. 714–725, 2016.

H. Mola-Abasi and I. Shooshpasha, “Influence of zeolite and cement additions on mechanical behavior of sandy soil,” Journal of Rock Mechanics and Geotechnical Engineering, vol. 8, no. 5, pp. 746–752, 2016.

Z. L. Wu, Y. F. Deng, S. Y. Liu, Q. W. Liu, Y. G. Chen, and F. S. Zha, “Strength and micro–structure evolution of compacted soils modified by admixtures of cement and metakaolin,” Applied Clay Science, vol. 127-128, pp. 44–51, 2016.

T. W. Zhang, X. B. Yue, Y. F. Deng, D. W. Zhang, and S. Y. Liu, “Mechanical behavior and micro-structure of cement-stabilised marine clay with a metakaolin agent,” Construction and Building Materials, vol. 73, pp. 51–57, 2014.

K. G. Kolovos, P. G. Asteris, D. M. Cotsovos, E. Badogiannis, and S. Tsivilis, “Mechanical properties of soilcrete mixtures modified with metakaolin,” Construction and Building Materials, vol. 47, pp. 1026–1036, 2013.

J. H. Xie, W. Chen, J. J. Wang, C. Fang, B. X. Zhang, and F. Liu, “Coupling effects of recycled aggregate and GGBS/metakaolin on physicochemical properties of geopolymer concrete,” Construction and Building Materials, vol. 226, pp. 345–359, 2019.

Y. F. Deng, X. B. Yue, S. Y. Liu, Y. G. Chen, and D. W. Zhang, “Hydraulic conductivity of cement-stabilized marine clay with metakaolin and its correlation with pore size distribution,” Engineering Geology, vol. 193, pp. 146–152, 2015.

A. J. Choobbasti and S. S. Kutanaei, “Microstructure characteristics of cement-stabilized sandy soil using nanosilica,” Journal of Rock Mechanics and Geotechnical Engineering, vol. 9, no. 5, pp. 981–988, 2017.

K. Wianglor, S. Sinthupinyo, M. Piyaworapaiboon, and A. Chaipanich, “Effect of alkali-activated metakaolin cement on compressive strength of mortars,” Applied Clay Science, vol. 141, pp. 272–279, 2017.

H. Wang, X. Y. Li, Y. Cheng, Y. F. Zhang, and X. H. Bai, “Effects of coal-bearing metakaolin on the compressive strength and permeability of cemented silty soil and mechanisms,” Construction and Building Materials, vol. 186, pp. 174–181, 2018.

L. H. Wang, X. Y. Li, Y. Cheng, and X. H. Bai, “Effects of coal-metakaolin on the properties of cemented sandy soil and its mechanisms,” Construction and Building Materials, vol. 166, pp. 592–600, 2018.

F. G. M. Aredes, T. M. B. Campos, J. P. B. MacHado, K. K. Sakane, G. P. Thim, and D. D. Brunelli, “Effect of cure temperature on the formation of metakaolinite-based geopolymer,” Ceramics International, vol. 41, no. 6, pp. 7302–7311, 2015.

F. Slaty, H. Khourya, H. Rahier, and J. Wastiels, “Durability of alkali activated cement produced from kaolinitic clay,” Applied Clay Science, vol. 104, pp. 229–237, 2015.

M. o. C. o. PRC., Code for Investigation of Geotechnical Engineering, Architecture and Building Press, Beijing, China, 2009.

M. o .C. o. PRC., Technical Code for Ground Treatment of Buildings, China Architecture Industry Press, Beijing, China, 2012.

K. Gao, K. L. Lin, D. Y. Wang et al., “Effects SiO₂/Na₂O molar ratio on mechanical properties and the microstructure of nano-SiO₂ metakaolin-based geopolymers,” Construction and Building Materials, vol. 53, pp. 503–510, 2014.

Y. F. Deng, Z. L. Wu, S. Y. Liu et al., “Influence of geopolymer on strength of cement-stabilized soils and its mechanism,” Chinese Journal of Geotechnical Engineering, vol. 3, pp. 446–453, 2016.

C. S. Poon, L. Lam, S. C. Kou, Y. L. Wong, and R. Wong, “Rate of pozzolanic reaction of metakaolin in high-performance cement pastes,” Cement and Concrete Research, vol. 31, no. 9, pp. 1301–1306, 2001.

W. P. Halperin, J. Y. Jehng, and Y. Q. Song, “Application of spin-spin relaxation to measurement of surface area and pore size distributions in a hydrating cement paste,” Magnetic Resonance Imaging, vol. 12, no. 2, pp. 169–173, 2003.

V. Bortolotti, P. Fantazzini, R. Mongiorgi, S. Sauro, and S. Zanna, “Hydration kinetics of cements by time-domain nuclear magnetic resonance: application to portland-cement-derived endodontic pastes,” Cement and Concrete Research, vol. 42, no. 3, pp. 577–582, 2012.

A. Valori, P. J. McDonald, and K. L. Scrivener, “The morphology of C-S-H: lessons from 1H nuclear magnetic resonance relaxometry,” Cement and Concrete Research, vol. 49, pp. 65–81, 2013.

J. M. Xiao and H. H. Fan, “Application of solid-state nuclear magnetic resonance techniques in research of cement and hydration products,” Journal of Materials Science & Engineering, vol. 1, pp. 166–172, 2016.

Y. Wang, Q. Yuan, D. H. Deng, T. Ye, and L. Fang, “Measuring the pore structure of cement asphalt mortar by nuclear magnetic resonance,” Construction and Building Materials, vol. 137, pp. 450–458, 2017.

M. Arif, V. Gupta, H. Choudhary, S. Kumar, and P. Basu, “Performance evaluation of cement concrete containing sandstone slurry,” Construction and Building Materials, vol. 184, pp. 432–439, 2018.

Z. F. Zhao, M. Benzerzour, N. Abriak, D. Damidot, and L. Courard, “Use of uncontaminated marine sediments in mortar and concrete by partial substitution of cement,” Cement and Concrete Composites, vol. 93, pp. 155–162, 2018.

M. Murat, “Hydration reaction and hardening of calcined clays and related minerals: II. Influence of mineralogical properties of the raw-kaolinite on the reactivity of metakaolinite,” Cement and Concrete Research, vol. 13, no. 4, pp. 511–518, 1983.

G. Kakali, T. Perraki, S. Tsivilis, and E. Badogiannis, “Thermal treatment of kaolin: the effect of mineralogy on the pozzolanic activity,” Applied Clay Science, vol. 20, no. 1-2, pp. 73–80, 2001.

Y. Yilmaz and V. Ozaydin, “Compaction and shear strength characteristics of colemanite ore waste modified active belite cement stabilized high plasticity soils,” Engineering Geology, vol. 155, pp. 45–53, 2013.

S. Barbhuiya, P. Chow, and S. Memon, “Microstructure, hydration and nanomechanical properties of concrete containing metakaolin,” Construction and Building Materials, vol. 95, pp. 696–702, 2015.