Objective. Clinical comparison of the survival rates between stainless steel and ceramic brackets over a 12-month period. Materials and Methods. The study involved 20 consecutive patients with diagnosed malocclusion that required two-arch fixed appliance treatment. The participants were randomly divided into two 10-member groups. Group 1 was treated with Abzil Agile (3M Unitek) stainless steel brackets; group 2 was treated with Radiance (American Orthodontics) monocrystalline ceramic brackets. All the brackets were bonded by the same operator. Over the next 12 months, all bracket failures were recorded with each appointment. The received data were processed statistically using the Mantel–Cox test, Kaplan–Meier method, and Cox hazard model. Results. A total of 381 brackets were bonded, 195 of which were metallic brackets and 186 were ceramic ones. In the 12-month observation period, there were 14 metal (7.2%) and 2 ceramic bracket (1.1%) failures. The overall failure rate was 4.2% (n = 16). The majority of failures (14 brackets; 87.5%) occurred during the first 6 months of the experiment, 12 (83%) of which were metal brackets and 2 (100%) were ceramic brackets. The statistical analysis revealed significant differences between the groups (p<0.05). Conclusions. Metal brackets demonstrated significantly higher failure rates than ceramic brackets for both 6- and 12-month observation periods (p<0.05). The 6% difference between the brackets is clinically significant as it corresponds to one additional failure within 12 months.
Wrocław Medical UniversityST-7541. Introduction
Orthodontic bracket is an essential element of fixed appliance. Its purpose is to transfer forces from the activated archwire to dentition to enable three-dimensional movement of teeth. Currently, stainless steel brackets are most commonly used at the orthodontic office due to their low cost, high corrosion resistance in the mouth, higher modulus of elasticity, and excellent biomechanical properties [1, 2]. Since stainless steel cannot bond chemically with orthodontic adhesives, these brackets have different types of gauge mesh bases for increasing the contact area with the adhesive. During bracket positioning, mesh eyelets are filled with orthodontic adhesive, and the subsequent polymerisation creates a micromechanical bond between the bracket and the adhesive [3]. In addition to numerous advantages, stainless steel brackets also have some drawbacks, which are poor aesthetics and low biocompatibility. Both clinicians and patients are aware of this problem, which leads to increased interest in ceramic brackets due to their cosmetic properties and high biocompatibility [2]. However, ceramic materials, just like stainless steel, do not form chemical compounds with acrylic and diacrylate orthodontic adhesives [4]. Bases of ceramic brackets are usually formed with recesses or covered with additional ceramic particles to ensure a better mechanical interlock to the adhesive. Another method is to coat the ceramic base with silane to provide chemical adhesion [5, 6].
Bond strength of orthodontic brackets is an important factor which can influence the treatment with the use of fixed appliances. Bracket failures may potentially increase the total treatment time and financial costs of the therapy. The optimal bonding force between the bracket and enamel surface should be sufficient to enable a durable bracket position during treatment and to prevent the enamel from iatrogenic damage during the debonding procedure. Bond failures may be caused by numerous factors, including masticatory forces, forces produced by orthodontic appliances, aging of the orthodontic adhesives, mistakes during any step of bonding protocol, or some conservative dentistry therapies performed prior to bonding, such as topical fluoride varnish applications, or bleaching [7–9]. The range of the desired bonding force has not been determined yet. On the basis of their in vitro study, Reynolds and von Fraunhofer [10] stated that the minimum bond strength of 6–8 MPa is considered appropriate, whereas Bishara [11] suggested that the bonding strength ought to exceed 13.5 MPa. Recently Gauge [3] assumed that the ideal orthodontic adhesive should withstand forces over 20 MPa. The majority of the studies that evaluated the bond strength of orthodontic brackets were carried out as in vitro experiments under ideal laboratory conditions that may not reflect all clinical conditions. In vitro experiments provide information about initial bond strength to the enamel but cannot serve as predictors of bracket survivability [12–14]. Therefore, more accurate guidance on the clinical relevance of adhesion protocols is provided by in vivo tests, which assess the failure rate of the enamel-boding agent-bracket interface during treatment.
Bracket failure occurs at one of the three locations within the enamel-adhesive-bracket complex: between the tooth enamel and the adhesive, within the adhesive, or at the adhesive-bracket interface. The adhesive-enamel interface has been well tested as evidenced by numerous articles dedicated to both in vivo and in vitro tests. These surveys mostly assessed the application of self-etching primer which is still controversial [15–19]. The evaluation of identical adhesive systems and two different orthodontic brackets makes it possible to compare the bond strength between the adhesive and the bracket. However, there are few inconsistent results of in vitro tests that compare the bond strength of metal and ceramic brackets with the enamel. Some authors do not observe statistically significant differences between metal and ceramic brackets subjected to shear or tension bond strength testing [20, 21]. On the other hand, Joseph and Russouw [22], as well as Haydar et al. [23], obtained significantly higher mean values of the shear bond strength of ceramic brackets in comparison to their metal counterparts for all tested bonding materials. Regardless of the results of statistical tests, the bond strength of metal and ceramic brackets measured by all the authors exceeded 6–8 MPa, which is considered to be adequate for clinical use [23].
The purpose of this in vivo study was to investigate and compare failure rates of ceramic and stainless steel brackets over a period of 12 months.
2. Materials and Methods
The study involved 20 consecutive patients with diagnosed malocclusion that required two-arch fixed appliance treatment (Figure 1). Completely erupted anterior teeth and premolars were the only inclusion criteria for this study. Patients with enamel defects, fillings, or prosthetic work on buccal surfaces of teeth were excluded from the study. The subjects treated with adjunctive fixed functional appliances (Herbst, Forsus, etc.) were also excluded from the study due to an increased failure rate of lower canine brackets located near their mandibular attachments, which was observed in our practice. Age, gender, and malocclusion differences were ignored. Both extraction and nonextraction patients participated in the study. 16 out of 20 patients were subjected to treatment without extraction; 4 patients had either first or second upper premolars extracted. Furthermore, two patients had the pair of upper premolars extracted in childhood (interview data), and 4 patients were diagnosed with hypodontia of 7 teeth in total. Thus, the study was conducted in relation to a total of 381 teeth. The study was approved by the ethical committee of Wrocław Medical University (181/2013).
The participants were randomly divided into two groups that consisted of 10 subjects in each group. Group 1 was treated with Agile (3M Abzil, São José do Rio Preto, Brazil) stainless steel brackets; group 2 was treated with Radiance (American Orthodontics, Sheboygan, USA) monocrystalline ceramic brackets. No patient was lost to follow-up. The average age of the patients was 25.8 years (range: 13–44 years) (Table 1). Due to the nature of the experiment, both the operator and the patient knew whether they were treated with metal or ceramic brackets.
Gender and age distribution between groups.
Males, n, %
Females, n, %
Malocclusion
Age
Class I, n, %
Class II, n, %
Class III, n, %
Mean, ys
Range, ys
Metallic bracket
2 (20)
8 (80)
5 (50)
5 (50)
0 (0)
21.7
13–33
Ceramic bracket
2 (20)
8 (80)
4 (40)
6 (60)
0 (0)
30.1
16–44
Total
4 (20)
16 (80)
9 (45)
11 (55)
0 (0)
25.7
13–44
All the brackets were bonded by the same operator (TO) in the following manner. After a lip and cheek retractor had been placed, dental biofilm was removed with a brush mounted on a micromotor without using prophylaxis or abrasive paste. Then, Transbond Plus Self Etching Primer (3M Unitek, Monrovia, USA) was rubbed into the clean enamel for 5 seconds. The excessive amount of the solvent was vaporized by an air stream from an oil-free air-water syringe. Afterwards, a thin layer of Transbond XT (3M Unitek, Monrovia, USA) orthodontic adhesive was put on the bracket base. A bracket was positioned on the enamel surface, whereas the excessive amount of the adhesive was removed with a probe. As recommended by the Transbond XT manufacturer, the adhesive was being cured for 20 seconds with a diode polymerisation lamp and 10 seconds for the mesial and distal sides each in the case of applying a metallic bracket or through a bracket in the case of applying a ceramic bracket. The initial archwire was inserted immediately after bracket bonding. If the contact between the upper teeth and the mandibular bracket was observed, an elastomeric ligature with guard (3M Unitek, Monrovia, USA) was applied to the lower bracket, as, according to our clinical experience, it brings sufficient protection from the failures. During the bonding appointment, the patients were instructed how to take care of the fixed appliance and how to maintain proper hygiene of the oral cavity during treatment.
All brackets bonded to the incisors, canines, and premolars were evaluated. During the first 12 months of active treatment, at each appointment, the orthodontist (TO) recorded all the bracket failures. If a failure occurred, the orthodontist bonded a new bracket that was not included in the study. The obtained data were subjected to statistical analysis using the Mantel–Cox test. The correlation between treatment time and failure rate was evaluated with the Kaplan–Meier method. Risk factors were computed using the Cox proportional hazards model. The level of statistical significance for all tests was set at α = 0.05.
3. Results
A total of 381 brackets were bonded, 195 of which were metallic brackets and 186 were ceramic ones. In the 12-month observation period, there were 14 metal (7.2%) and 2 ceramic bracket (1.1%) failures. The overall failure rate was 4. 2% (n = 16). The majority of failures (14 brackets; 87.5%) occurred during the first 6 months of the experiment, 12 (83%) of which were metal brackets and 2 (100%) were ceramic brackets (Table 2). Bracket failure rates were 6.25% for canines, followed by 5% for central incisors. The lowest number of detachments was encountered at the second premolar with failure rate of 1.3% (Table 3).
Number and percentage of failed brackets.
Bracket type
Bonded, N
Failures after 6 months, N
Failures after 12 months, N
Failures after 12 months, %
Metallic
195
12
14
7.2
Ceramic
186
2
2
1.1
Total
381
14
16
4.2
Bracket failure rates per tooth type after 12-month observation period.
Tooth type
Brackets bonded
Failures after 12 months
Failure rate (%)
Mesial incisor
80
4
5
Lateral incisor
79
3
3.8
Canine
80
5
6.25
First premolar
68
3
4
Second premolar
74
1
1.3
The log-rank test showed significant statistical differences between the brackets for both 6- and 12-month observation periods, p=0.008 and p=0.003, respectively. The Kaplan–Meier survival curve plotted for the 12-month observation period showed a greater tendency towards metal bracket failure occurring from the beginning of the treatment (Figure 2). The Cox proportional hazards model showed for both 6- and 12-month observation periods that metal brackets have a 15% greater risk of failure than ceramic ones (p<0.05) (Table 4).
The Cox proportional hazards model for 6- and 12-month observation periods.
Coefficient β
Hazard ratio
95% CL
p
Ceramic brackets (6 months)
1.00
1.00
Metal brackets (6 months)
−1.752
0.173
0.039–0.775
0.022
Ceramic brackets (12 months)
1.00
1.00
Metal brackets (12 months)
−1.913
0.148
0.034–0.650
0.011
4. Discussion
This study investigated the detachment rates of the ceramic and metallic brackets. The failure rate of the ceramic brackets in our study was 1.1%. To date, no data have been reported in relation to the failure rates of the ceramic brackets bonded with composite adhesive and self-etching primer. Hitmi et al. [24] reported a similar failure rate of 0.7% for the ceramic brackets bonded with Fuji Ortho LC, light-cured glass-ionomer resin-modified adhesive. Higher values were obtained by Årtun [25], who compared the failure rates of the ceramic brackets with mechanical or chemical retention and found 1.7% and 3.2%, respectively. Recently, Stasinopoulos et al. [26], in retrospective study, reported a detachment rate of the ceramic brackets of 20%. The authors, however, included in the survey only the patient with at least one bracket failure during the orthodontic treatment.
The failure rate of the metal brackets obtained in our study was 6.2%, and it is within the range of the results (1.15%–17.87%) found by other authors [9, 14, 16, 24, 27–33].
A direct comparison of the study results is difficult due to the different experiment protocols concerning brackets, adhesive systems, tooth enamel preparation, curing time, curing power, number of operators, length of the study, and the age of the patients. In this study, the failure rate of the metal brackets was seven-times higher than that of the ceramic brackets and this difference was statistically significant (p<0.05). These results are in agreement with the study by Hitmi et al. [24], who compared the detachment rates of the metal, plastic, and ceramic brackets bonded with resin-modified glass-ionomer adhesive and, similarly to our study, discovered a statistically larger percentage of failures of metal brackets than ceramic ones. The difference in the failure rates between the metallic and ceramic brackets found in our study is hard to explain. In the laboratory study, Benkli et al. [34] showed that shear bond strength of the Radiance bracket bonded to human enamel is twice as high as that of the metallic ones. On the other hand, Oginski at al. [35] did not find statistical differences between the bond strength of Radiance brackets and metallic brackets bonded with the self-priming system and colour changing Grengloo adhesive to bovine enamel. Despite the conflicting results of the in vitro investigations, the difference in the failure rates may be contributed to the different degree of cure of the orthodontic adhesive under brackets made from different materials. Eliades et al. [36] investigated the degree of cure of the adhesive under brackets under the irradiation modes used in our study. They found a significantly higher degree of cure of directly irradiated orthodontic light-cured adhesive under monocrystalline brackets in comparison with the indirectly irradiated adhesive under stainless steel attachments. Moreover, monocrystalline brackets had a diffuse visible light transmittance of 80% at 468 nm compared to almost no light transmittance of metallic brackets. Therefore, during the bonding procedure, curing of orthodontic adhesive under ceramic brackets will lead to additional polymerisation of adhesive under previously bonded brackets, resulting in an even more initial difference between the degrees of cure of adhesives under ceramic and stainless steel brackets.
In our investigation, we found that the detachment rate of the second premolar bracket was 1.4% and was lower in comparison with the failure rates of the anterior teeth. These results are in contradiction with numerous researchers that reported higher failure rates in the posterior region [9, 14, 37–39]. This is attributed to higher masticatory forces in posterior region, problems with moisture control, poor access, bracket-tooth contact after bonding, and increased amount of prismatic enamel [37]. On the other hand, Krishnan et al. [33] noted 1.7 times higher failure rate in the anterior region. Recent survey focused on the evaluation of patterns of bracket failure relates this to the increased activation forces exerted by an archwire in the crowded dental arches or increased mastication load [26].
The failure rate of the metal brackets is reported to be much higher during the first 6 months of the treatment [16, 38, 40, 41]. In the studies where the failure rates of the metal brackets bonded with the self-etching primer system were analysed after 6 and 12 months of treatment, it was found that 50–68% of detachments occurred within the first half year of the therapy [15, 42]. In this study, we obtained a higher failure rate of 83%. The difference may be due to the fact that, contrary to other authors [15, 42], we did not apply the pumice paste to the enamel prior to bonding brackets: enamel biofilm was only removed with a brush mounted on a micromotor without using prophylaxis or abrasive paste. We have not found studies comparing the applied procedure with other methods, i.e., cleaning tooth enamel with pumice or refraining from cleaning it completely, but Ireland and Sheriff [43] found in an in vivo study that the application of pumice prior to enamel etching does not improve the bond strength of the metal brackets. Similar results obtained from in vitro experiments were reported by others [44], also in the case of applying a self-etching primer [45]. On the other hand, Lill et al. [46] observed a five-time increase in the bracket failures in the patients whose enamel had not been cleaned with pumice prior to the application of self-etching primer.
A limitation of our study is that we did not evaluate the failure rate of dental brackets by gender, age, or malocclusion. The evidence in relation to the patient’s gender and bracket survival is ambiguous. Numerous researchers reported no difference in the bracket failure rate between males and females [15, 24, 27, 31, 37, 41, 42, 47, 48]. On the other hand, Koupis et al. [49], Hammad et al. [41], and Jung [29] reported a significantly higher failure rate in males than females, whereas Bazagrani et al. [32], who examined the bracket failure rate among adolescents, found that detachments of brackets in boys occurred four times more frequently than in girls.
Also, the relation between the bracket failure rates and the patient’s age is disputable. Jung [29] discovered that adolescents have a higher rate of bracket failures compared to adults. Recently, Bazagrani et al. [32] reported a 3.5 times higher detachment rate among adolescents aged 10–13 than those at the age of 14–18. Other authors did not find a statistical difference for the failure rate with respect to the age of the patient [40, 45, 50].
Likewise, the effect of the malocclusion on the bracket detachments rate is questionable. Although Bherwani et al. [27] reported that class II/2 malocclusion significantly increases the likelihood of bracket failure, other authors did not find significant differences [41, 51]. In our study, we applied an elastomeric ligature with guard (3M Unitek) to every bracket that was in occlusal contact with the opposing teeth after bonding, which might lead to the bond failure.
Another limitation of this study is related to the fact that all brackets were bonded by the same orthodontist (TO). Thus, according to Nandhra at al. [31], the results of this investigation may only be attributed to that clinician. Also, due to a clearly visible difference in colour between stainless steel and ceramic brackets, neither the operator nor the patient could have been blinded in terms of the type of brackets used during the treatment.
Bearing in mind the diversity of ceramic bracket bases, extreme caution should be exercised in generalizing our findings and extrapolating them to other ceramic brackets, especially when differences between the construction of ceramic bases are a known factor that has a significant impact on the results of in vitro bond strength studies [52].
In the modern era, with the technology development and the associated diversity of both orthodontic attachments and bonding materials, studies must be carried out to evaluate the usefulness of constantly improved orthodontic products. Since in vitro tests cannot exactly reflect clinical conditions, further in vivo studies are necessary to develop clinically acceptable adhesion protocols for orthodontic brackets.
5. Conclusions
This clinical study showed that metal brackets exhibited significantly higher failure rates than ceramic brackets for both 6- and 12-month observation periods (p<0.05). The 6% difference between the failure rates of tested brackets is clinically significant as it corresponds to one additional failure within 12 months. The Cox proportional hazard model showed that metal brackets have a 15% greater risk of failure than ceramic ones (p<0.05). However, both ceramic and metal brackets bonded with self-etching primer had acceptable failure rates, and both of them can be recommended to clinicians.
The majority of bracket failures (87.5%) occurred during the first six months of the treatment.
Data Availability
The data used to support the findings of this study are included within the article.
Conflicts of Interest
The authors declare that there are no conflicts of interest.
Acknowledgments
This work was supported by the Wrocław Medical University under Grant ST-754.
OhK.-T.ChooS.-U.KimK.-M.KimK.-N.A stainless steel bracket for orthodontic application200527323724410.1093/ejo/cji0052-s2.0-22144450699KeimR. G.GottliebE. L.NelsonA. H.VogelsD. S.III2008 JCO study of orthodontic diagnosis and treatment procedures. Part 1: results and trends20084211625640GaugeP.The evolution of bonding in orthodontics20151474S56S6310.1016/j.ajodo.2015.01.0112-s2.0-84931076810SwartzM. L.Ceramic brackets19972228288BisharaS. E.FehrD. E.Ceramic brackets: something old, something new, a review19973317818810.1016/s1073-8746(97)80068-02-s2.0-0031219390RussellJ. S.Current products and practice: aesthetic orthodontic brackets200532314616310.1179/1465312052250210242-s2.0-23044465804Scougall-VilchisR. J.Gonzalez-LopezB. S.Contreras-BulnesR.Rodriguez-VilchisL. E.Garcia-Niño de RiveraM. W.Kubodera-ItoT.Influence of four systems for dental bleaching on the bond strength of orthodontic brackets201181470070610.2319/100510-587.12-s2.0-79960174305LeódidoG. d. R.FernandesH. O.TonettoM. R.PresotoC. D.BandécaM. C.FiroozmandL. M.Effect of fluoride solutions on the shear bond strength of orthodontic brackets201223669870210.1590/s0103-644020120006000122-s2.0-84872948729MohammedR. E.AbassS.AbubakrN. H.MohammedZ. M. S.Comparing orthodontic bond failures of light-cured composite resin with chemical-cured composite resin: a 12-month clinical trial2016150229029410.1016/j.ajodo.2016.02.0132-s2.0-84994840445ReynoldsI. R.von FraunhoferJ. A.Direct bonding of orthodontic brackets-a comparative study of adhesives19763314314610.1179/bjo.3.3.1432-s2.0-0016975524BisharaS. E.Ceramic brackets and the need to develop national standards2000117559559710.1016/s0889-5406(00)70212-52-s2.0-0034185206RomanoF. L.CorrerA. B.Correr-SobrinhoL.MagnaniM. B. B. D. A.RuellasA. C. D. O.Clinical evaluation of the failure rates of metallic brackets201220222823410.1590/s1678-775720120002000182-s2.0-84862730829HouseK.IrelandA. J.SherriffM.An investigation into the use of a single component self-etching primer adhesive system for orthodontic bonding: a randomized controlled clinical trial2006331384410.1179/1465312052250213752-s2.0-33646168545WardJ. D.WolfB. J.LeiteL. P.ZhouJ.Clinical effect of reducing curing times with high-intensity LED lights20058561064106910.2319/080714-556.12-s2.0-84945948814Elekdag-TurkS.CakmakF.IsciD.TurkT.12-month self-ligating bracket failure rate with a self-etching primer20087861095110010.2319/112507-552.12-s2.0-56049123217DominquezG. C.TotamanoA.de Moura LopesM. V.CatharinoP. C.MoreaC.A comparative clinical study of the failure rate of orthodontic brackets bonded with two adhesive systems: conventional and Self-Etching Primer (SEP)2013182556010.1590/s2176-945120130002000142-s2.0-84882932571ElkhademA.OrabiN.Weak evidence suggests higher risk for bracket bonding failure with self-etch primer compared to conventional acid etch over 12 months2013142525310.1038/sj.ebd.64009362-s2.0-84887473052HuH.LiC.LiF.Enamel etching for bonding fixed orthodontic braces201311CD00551610.1002/14651858.CD005516.pub22-s2.0-84900779673OzerM.BayramM.DincyurekC.TocalakF.Clinical bond failure rates of adhesive precoated self-ligating brackets using a self-etching primer200484115516010.2319/022013-149.12-s2.0-84891944390LiuJ.-K.ChungC.-H.ChangC.-Y.ShiehD.-B.Bond strength and debonding characteristics of a new ceramic bracket2005128676176510.1016/j.ajodo.2004.03.0412-s2.0-29144516748RochaJ. M. d.GravinaM. A.CamposM. J. D. S.QuintãoC. C. A.EliasC. N.VitralR. W. F.Shear bond resistance and enamel surface comparison after the bonding and debonding of ceramic and metallic brackets2014191778510.1590/2176-9451.19.1.077-085.oar2-s2.0-84901376298JosephV. P.RussouwE.The shear bond strengths of stainless steel and ceramic brackets used with chemically and light-activated composite resins198997212112510.1016/0889-5406(90)70084-P2-s2.0-0025378238HaydarB.SartkayaS.ÇehreliZ. C.Comparison of shear bond strength of three bonding agents with metal and ceramic brackets1999695457462HitmiL.MullerC.MujajicM.AttalJ.-P.An 18-month clinical study of bond failures with resin-modified glass ionomer cement in orthodontic practice2001120440641510.1067/mod.2001.1159312-s2.0-0035489166ÅrtunJ.A post-treatment evaluation of multibonded ceramic brackets in orthodontics199719221922810.1093/ejo/19.2.2192-s2.0-0031109843StasinopoulosD.PapageorgiouS. N.KirschF.DaratsianosN.JägerA.BourauelC.Failure patterns of different bracket systems and their influence on treatment duration: a retrospective cohort study201888333834710.2319/081817-559.12-s2.0-85046152947BherwaniA.FidaM.AzamI.Bond failure with a no-mix adhesive system200878354554810.2319/010707-6.12-s2.0-43449112984GroverS.SidhuM. S.PrabhakarM.JenaS.SoniS.Evaluation of fluoride varnish and its comparison with pumice prophylaxis using self-etching primer in orthodontic bonding—an in vivo study201234219820110.1093/ejo/cjr0032-s2.0-84859362945JungM.-H.Survival analysis of brackets and tubes:A twelve-month assessment20148461034104010.2319/122613-946.12-s2.0-84908883058MeniniA.CozzaniM.SfondriniM. F.A 15-month evaluation of bond failures of orthodontic brackets bonded with direct versus indirect bonding technique: a clinical trial2014157010.1186/s40510-014-0070-92-s2.0-84964695207NandhraS. S.LittlewoodS. J.HoughtonN.Do we need primer for orthodontic bonding? A randomized controlled trial201537214715510.1093/ejo/cju0242-s2.0-84926684641BazarganiF.MagnusonA.LöthgrenH.KowalczykA.Orthodontic bonding with and without primer: a randomized controlled trial201638550350710.1093/ejo/cjv0752-s2.0-84990890007KrishnanS.PandianS.RajagopalR.Six-month bracket failure rate with a flowable composite: a split-mouth randomized controlled trial2017222697610.1590/2177-6709.22.2.069-076.oar2-s2.0-85021260093BenkliY. A.BuyukS. K.AtaliP. Y.TopbasiN. M.TopbaÅŸiF. B.Shear bond strength of metallic and ceramic brackets bonded with different new generation composite systems20173210.29011/2574-7347.100025OginskiT.SzustA.KawalaB.Evaluation of shear bond strength of various orthodontic brackets bonded to bovine enamel with use of grengloo adhesive: an in vitro study20144213335EliadesT.EliadesG.BrantleyW. A.JohnstonW. M.Polymerization efficiency of chemically cured and visible light-cured orthodontic adhesives: degree of cure1995108329430110.1016/s0889-5406(95)70024-22-s2.0-0029376924MillettD. T.HallgrenA.CattanachD.A 5-year clinical review of bond failure with a light-cured resin adhesive1998684351356SunnaS.RockW. P.Clinical performance of orthodontic brackets and adhesive systems: a randomized clinical trial199825428328710.1093/ortho/25.4.2832-s2.0-0032199123SukhiaR. H.SukhiaH. R.AzamS. I.NuruddinR.RizwanA.JalalS.Predicting the bracket bond failure rate in orthodontic patients: a retrospective cohort study201917220821510.1016/j.ortho.2019.03.0022-s2.0-85064082118CampoyM. D.PlasenciaE.VicenteA.BravoL. A.CibriánR.Effect of saliva contamination on bracket failure with a self-etching primer: a prospective controlled clinical trial2010137567968310.1016/j.ajodo.2008.06.0322-s2.0-77954667235HammadS. M.El BannaM. S.ElsakaS. E.Twelve-month bracket failure rate with amorphous calcium phosphate bonding system201335562262710.1093/ejo/cjs0502-s2.0-84885026529ManningN.ChadwickS. M.PlunkettD.MacfarlaneT. V.A randomized clinical trial comparing “one-step” and “two-step” orthodontic bonding systems200633427628310.1179/1465312052250218252-s2.0-39049184563IrelandA. J.SherriffM.The effect of pumicing on thein vivouse of a resin modified glass poly (alkenoate) cement and a conventional no-mix composite for bonding orthodontic brackets200229321722010.1093/ortho/29.3.2172-s2.0-0036718871LindauerS. J.BrowningH.ShroffB.MarshallF.AndersonR. H. B.MoonP. C.Effect of pumice prophylaxis on the bond strength of orthodontic brackets1997111659960510.1016/s0889-5406(97)70311-12-s2.0-0031159293FitzgeraldI.BradleyG. T.BosioJ. A.HeftiA. F.BerzinsD. W.Bonding with self-etching primers—pumice or pre-etch? An in vitro study201234225726110.1093/ejo/cjq1972-s2.0-84859299821LillD. J.LindauerS. J.TüfekçiE.ShroffB.Importance of pumice prophylaxis for bonding with self-etch primer2008133342342610.1016/j.ajodo.2006.03.0392-s2.0-40249097567MavropoulosA.KaramouzosA.KolokithasG.AthanasiouA. E.In vivo evaluation of two new moisture-resistant orthodontic adhesive systems: a comparative clinical trial200330213914710.1093/ortho/30.2.1392-s2.0-0142093616MurfittP.QuickA.SwainM.HerbisonG.A randomised clinical trial to investigate bond failure rates using a self-etching primer200628544444910.1093/ejo/cjl0072-s2.0-33749642667KoupisN. S.EliadesE.AthanasiouA. E.Clinical evaluation of bracket bonding using two different polymerization sources200878592292510.2319/072807-351.12-s2.0-50949097497KinchA. P.TaylorH.WarltlerR.OliverR. G.NewcombeR. G.A clinical trial comparing the failure rates of directly bonded brackets using etch times of 15 or 60 seconds198894647648310.1016/0889-5406(88)90005-42-s2.0-0024225878MillettD. T.McCluskeyL. A.McAuleyF.CreanorS. L.NewellJ.LoveJ.A comparative clinical trial of a compomer and a resin adhesive for orthodontic bonding2000703233240SoderquistS. A.DrummondJ. L.EvansC. A.Bond strength evaluation of ceramic and stainless steel bracket bases subjected to cyclic tensile loading20061292175.e7175.e1210.1016/j.ajodo.2005.09.0232-s2.0-32344438253