The combined effect of cadmium and boric acid on the electrodeposition of zinc-nickel from a sulfate has been investigated. The presence of cadmium ion decreases zinc in the deposit. In solution, cadmium inhibits the zinc ion deposition and suppresses it when deposition potential value is more negative than −1.2 V. Low concentration of CdSO4 reduces the anomalous nature of Zn-Ni deposit. Boric acid decreases current density and shifts potential discharge of nickel and hydrogen to more negative potential. The combination of boric acid and cadmium increases the percentage of nickel in the deposit. Boric acid and cadmium.
1. Introduction
Great interest has been shown in the possibilities offered by the electrodeposition of alloys, particularly in the automotive industry. It is well known that alloys improved mechanical [1–3] and chemical properties of metals. Zn-Ni alloy deposits on iron increases strongly the corrosion resistance [2, 3].
The electrodeposition of Zn-Ni alloys is classified by Brenner [4] as an anomalous codeposition, where zinc, which is the less noble metal, is preferentially deposited. Although this phenomenon has been known since 1907, the codeposition mechanisms of zinc and nickel are not well understood.
Several studies were carried out to explain this behaviour [5] in contradiction with the thermodynamic.
The nature of the anomalous codeposition has been extensively investigated, and one of the explanations is the formation of the hydroxide precipitate of the less noble metal at the cathode. The hydroxide is caused by a local increase of pH. This precipitate may suppress deposition of the noble metal [6]. It was noticed that anomalous codeposition occurred even at low current densities [7], where hydrogen formation is unable to cause large alkanization effects. Another explanation is based on the underpotential (UDP) of zinc on nickel-rich zinc alloys or on nickel nuclei [8]. Matlosz [9] uses a two-step reaction mechanism involving adsorbed monovalent intermediate ions for both electrodeposition of iron and nickel, as a single metal, and combines the two to develop a model for codeposition. Anomalous effects are assumed to be caused by preferential surface coverage due to differences in tafel rate constants for electrodeposition.
Many studies were carried out to attempt minimizing the inhibition phenomenon. Ashassi et al. [10] used a pulsed current in order to decrease zinc hydroxide formation at the cathodic surface. They consider that anomalous codeposition is due to the slow kinetic of nickel on steel. Hu and Bai [11] showed the possibility to obtain a composition of the deposit equal to that of the solution by the use of cyclic voltammetry. From Zhou and JO’Keefe work [12], the anomalous codeposition can be reduced by adding additives as tin.
It has been reported that the deposition of nickel needs low overpotential to create the initial nucleus [13] and the deposit grows at low potentials.
It has been noticed that normal codeposition takes place at low current density. Boric acid and some other reactive have the ability to decrease the current density. According to Karwas and Hepel [14] boric acid inhibits zinc deposition shifting the nickel content in alloys toward Ni-rich phases. From Šupicová and all work [15], boric acid shifts the reduction peak to more negative potentials and increases the peak height. It improves morphology and brightness, as well as the adhesion of the deposited Ni. In addition it acts as a catalyst lowering the overvoltage which allows the deposit of nickel instead of H2. For Hoare [16], boric acid plays a more important role than that of a buffer. Boric acid forms a complex from which nickel can be discharged more easily.
The present work focuses on the study of the Zn-Ni alloy electrodeposition in sodium sulfate baths in presence of boric acid and cadmium. In order to identify the effect of boric acid on current density, polarizations curves were plotted with various boric acid concentrations. The nucleation potential was studied in the presence of boric acid. The behaviour of cadmium on the zinc-nickel deposition was investigated.
2. Experimental
All experiments were carried out in a three-electrode cell with a capacity of 250 mL. A stainless-steel electrode with a surface of 2 cm2 as a working electrode, a titanium grid coated with ruthenium oxide (Ti/RuO2) as a counter electrode, and an electrode of calomel saturated (ECS) as a reference electrode (Hg2Cl2/Hg). The reference electrode was immersed in the upper section of a luggin capillary, and its end was placed as close as possible to the working electrode to minimize errors due to ohmic drop in the electrolytes. The counter electrode was placed in parallel with the working electrode at a distance of 2 cm. Potentiodynamic polarization curves were measured at a scan of 5 mV/s starting from open circuit with a potentiostat (Radiometer analytical PGP201) assisted by a VoltaMster 4 software.
All solutions were freshly prepared with analytical grade chemicals (Merck) and distilled water. The electrolyte for the alloy deposition was a solution of 0.5 M sodium sulfate. The Zn-Ni alloys deposits were obtained at room temperature from electrolyte containing 0.02 M of ZnSO4·7H2O and 0.02 M of NiSO4·6H2O.
The working electrode was polished with abrasive paper (#320, #1200 and #2000 SiC) and finished with polishing slurry of 0.5 μm Al2O3 powder followed by washing with distilled water then with acetone and finally dried under warm airflow.
Before each experiment, the solution was purified with pure nitrogen for 10 mn to release oxygen dissolved and maintained under nitrogen atmosphere during the run of experiments.
The temperature was kept constant at 25°C by using a water-jacketed cell. The solution was agitated with a mechanical stirrer in order to have uniform bulk pH. The rotational speed of the stirrer was kept at 250 rpm for all experiments.
After deposition, the electrode is removed from the solution rinsed with distilled water and then dried.
In order to determine the alloy composition, the working electrode was immersed in concentrated nitric acid to remove the deposits obtained.
The surface morphology of the deposit was analysed using scanning electron microscopy (JSM-5500LV, SEM, Japan).
The composition of the deposits was determined using atomic absorption spectrophotometry (PERKIN-ELMER, AA 5000). Deposition current efficiency was calculated for each deposit using electrochemical equivalents of Ni (II) and Zn (II).
3. Results and Discussions3.1. Effect of Boric Acid on the Polarization and Potential Curves
Figure 1 shows the effect of boric acid on the polarization curves of a solution containing 0.5 M of sodium sulfat. The measured current density decreases with increasing boric acid concentration suggesting that boric acid inhibits protons reduction that is extended to more negative potentials. This effect is attributed to adsorption of boric acid species on the substrate.
Polarization curves of 0.5 M sodium sulfate solution for different concentrations of boric acid.
Figure 2 shows the influence of boric acid on the curves potential—time during the deposition of zinc-nickel alloy on steel at constant current density. The nucleation potential and the nucleation time are where a sudden change in the slope occurs. This sudden change in the slope is an indication of diffusion controlled reduction system. In the presence of boric acid the nucleation potential decreases and nucleation time increases. Therefore, in the presence of boric acid the nucleation time increases and the nucleation potential shifts to positive values. Thus boric acid by reducing nucleation potential leads to reduce anomalous deposition and hydrogen evolution reaction.
Chronopotentiometric curves at 5 mA/cm2 on steel electrode.
3.2. Effect of Cadmium on Zinc and Nickel Deposition
Figure 3 shows the effect of cadmium on the deposition of zinc. With a concentration ten-times smaller than that of zinc, the presence of cadmium decreases the deposition of zinc. Moreover in the presence of cadmium, the deposition of zinc is suppressed when the cathodic potential sweep is reversed at −1.2 V represented by dotted lines in the voltammogram.
Cyclic voltammetry at a scan of 5 mV/s of a metallic solution containing |Na2SO4| = 0.5 M at pH = 3.5.
In Figure 4, cyclic voltammograms behavior of steel in the bath solutions were represented. As for the previous figure, the peak observed at −0.95 V/SCE disappears in the presence of cadmium indicating that it concerns the zinc. Many authors attribute this peak to the formation of δ-phase (Ni3Zn22). This observation confirms that zinc is inhibited by cadmium regardless of the form in which it appears.
Cyclic voltammograms at a scan rate 5 mV/s of a metallic solution containing |Na2SO4| = 0.5 M at pH = 3.5.
We can notice, on the other hand, that cadmium has no effect on the nickel deposit.
3.3. Combined Effect of Boric Acid and Cadmium on Zinc-Nickel Deposition
Figure 5 shows the combined effect of boric acid and cadmium on the deposition of zinc and nickel. As mentioned above, cadmium has a strong effect on the zinc deposit. It reduces zinc deposition. The presence of boric acid decreases the zinc deposit while it shifts the reduction peak of nickel to more negative potentials and increases the peak height.
Cyclic voltammetry at a scan of 5 mV/s of a metallic solution containing |Na2SO4| = 0.5 M at pH = 3.5.
Boric acid has an effect on the cadmium deposition since the intensity of the anodic stripping decreases.
The effect of the presence of Cd2+ on the electrodeposition of nickel can be seen from Figure 6. The current remained unchanged when the concentration of Cd2+ is lower than 0.02 M. At 0.02 M the current of redissolution of nickel decreases and the decrease may be attributed to the adsorption of cadmium [17], which blocks the active sites of the cathode surface and inhibits electrocrystallisation of nickel.
Anodic stripping voltammetry at a scan of 5 mV/s of a metallic solution containing |Na2SO4| = 0.5 M |H3BO3| = 0.8 M at pH = 3.5.
Figure 7 illustrates the influence of cadmium on nickel and zinc in the deposit.
Effect of cadmium concentration on (a) Zn and (b) Ni at 4 mA/cm2.
At 4 mA/cm2 the increases of cadmium in the bath decreases the zinc content and not nickel content. The zinc content decreased from 77% to 57% while the cadmium was increased from 0.5 to 3 g/L. The figure also shows that the composition can be easily controlled when, lower amount of cadmium (0.5 and 1 g/L) is introduced in the bath.
Figure 8 show, the effect of amount of cadmium sulfat on the morphology of final deposits at a current density of 4 mA/cm2. When cadmium sulfat concentration is below 2 g/L, a smooth and uniform deposition can be obtained. Above 2 g/L of sulfat cadmium leads to a non-uniform surface with higher cadmium content on the surface.
SEM photographs of electrodeposition of Zn-Ni on steel at 4 mA/cm2. (a) |CdSO4| = 1.5 g/L, (b) |CdSO4| = 2.5 g/L.
A comparison of the optical micrographs in Figure 9 shows a remarkably refined Zn-Ni coating structure in the presence of boric acid. Coating in the presence of boric acid looked compact, bright, and smooth.
SEM Zn-Ni electrodeposited on steel at 4 mA/cm2 from a bath containing 0.02 M ZnSO4, 0.02 M NiSO4, and 0.5 M Na2SO4. (a) Without boric acid, (b) |H3BO3| = 0.8 M.
Figure 10 shows the effect of boric acid on the surface morphology of Zn-Ni alloy deposits in the presence of cadmium and cadmium boric acid. In the presence of cadmium boric acid smaller particles in the range of 1-2 μm are observed. The decrease of particles in presence of boric is due to the preferred homogeneous nickel deposit that occurs at lower current densities. Boric acid acts on lowering current density.
SEM Zn-Ni electrodeposited on steel at 4 mA/cm2 from a bath containing 0.02 M ZnSO4, 0.02 M NiSO4, and 0.5 M Na2SO4. (a) |Cd2+| = 0.001 M, (b) |Cd2+| = 0.001 M boric acid = 0.8 M.
The current efficiency is plotted with the molar ratio |Zn2+|/|Ni2+| in the Figure 11.
Current efficiency on the molar ratio plotted at 5 mA/cm2 in a solution containing |Na2SO4| = 0.5 M.
The increase of the current efficiency, for the ratio between 0<|Zn2+|/|Ni2+|<1, results in the strong reduction of nickel. The increase is more important for baths containing boric acid and boric acid-cadmium than for those without boric acid. This observation confirms that boric acid increases the percentage of nickel in the deposit and inhibits the deposition of zinc and protons discharge. Boric acid would be expected to influence reactions that take place at the electrode surface as hydrogen evolution, zinc, and nickel deposition. According to Karwas and Hepel [14], boric acid suppresses the secondary nucleation while it increases the primary nucleation density. However, cadmium has no effect on the current efficiency. For |Zn2+|/|Ni2+| ratio values greater than 1 the current efficiency is slightly dependent on the changes in the |Zn2+|/|Ni2+| ratio. For |Zn2+|/|Ni2+| ratio values higher than 2, the percentage of nickel in the deposit slightly decreases. This diminution is attributed to the weak rate of hydrogen reaction on the cathodic surface recovered with zinc compared to the one observed on bare steel for example [18].
Conclusion
The electrodeposition of Zn-Ni alloys is anomalous when the percentage of nickel in the deposit is lower than that in the solution. Boric acid extends the proton discharge potential to more cathodic values. It shifts the reduction peak to more negative potentials, and increases the peak height. Boric acid enhances the Ni nucleation process, and improved deposition of Ni consequently decreases anomalous deposition.
Cadmium decreases strongly the deposition of zinc but has no effect on nickel. As shown in the morphology of Zn-Ni-Cd with varying CdSO4 concentration well-defined particles are seen up to 2 g/L of CdSO4 and nonuniform surface was obtained beyond 2 g/L.
For a ratio |Zn2+|/|Ni2+| = 0.5, and in the presence of cadmium-boric acid at a concentration of 0.8 M the codeposition tends toward normal deposition since the point on the curve corresponding to the ratio 0.5 is almost coincident with that on the curve CRL. Boric acid enhances the current efficiency while cadmium has no effect on current efficiency.
LinY. P.SelmanJ. R.Electrodeposition of corrosion-resistant Ni-Zn alloy. I.Cyclic voltammetric study19931405129913032-s2.0-0027592171MiyoshiY.State of the art in precoated steel sheet for automotive body materials in Japan1991311110WakanoS.ShibuyaA.HoboY.NishiharaM.Corrosion Performance of Zn alloy Precoated Steels for Automotive Body198318967BrennerA.19631-2New York, NY, USAAcademic PressBakerB. C.WestA. C.Electrochemical impedance spectroscopy study of nickel-iron deposition II. Theoretical interpretation19971441169175FukushimaH.AkiyamaT.HigashiK.Electrodeposition behavior of Zn-Ni alloys from sulfate baths over a wide range of current density19884232422472-s2.0-0023983211HorkansJ.Effect of plating parameters on electrodeposited NiFe198112814549NicolM. J.PhilipH. I.Underpotential deposition and its relation to the anomalous deposition of metals in alloys1976702233237MatloszM.Competitive adsorption effects in the electrodeposition in iron-nickel alloys19931408227222792-s2.0-0027642325Ashassi-SorkhabiH.ashassi@ark.tabrizu.ac.irHagrahA.Parvini-AhmadiN.ManzooriJ.Zinc-nickel alloy coatings electrodeposited from a chloride bath using direct and pulse current2001140327828310.1016/S0257-8972(01)01032-5HuC. C.BaiA.The inhibition of anomalous codeposition of iron-group alloys using cyclic voltammetry200214911C615C62210.1149/1.1511753ZhouZ.O’KeefeT. J.Modification of anomalous deposition of Zn-Ni alloy by using tin additions199796169191MüllerC.c.muller@qf.ub.esSarretM.BenballaM.Some peculiarities in the codeposition of zinc-nickel alloys200146182811281710.1016/S0013-4686(01)00493-5KarwasC.HepelT.Morphology and composition of electrodeposited cobalt-zinc alloys and the influence of boric acid19891366167216782-s2.0-0024683636ŠupicováM.magdas@pobox.skRozikR.TrnkováL.OriňákováR.magdas@pobox.skGálováM.magdas@pobox.skInfluence of boric acid on the electrochemical deposition of Ni2006102616810.1007/s10008-005-0656-8HoareJ. P.Boric acid as a catalyst in nickel plating solutions198713412310231032-s2.0-0023572443KazuoK.TakahiroS.KunioaS.Morphology evolution of zinc-nickel binary alloys electrodeposited with cadmium additive199514210L193L195LodhiZ. F.MolJ. M. C.J.M.C.Mol@tudelft.nlHovestadA.TerrynH.de WitJ. H. W.Electrodeposition of Zn-Co and Zn-Co-Fe alloys from acidic chloride electrolytes20072021849010.1016/j.surfcoat.2007.04.070