International Journal of Photoenergy

Volume 2013 (2013), Article ID 526140, 9 pages

http://dx.doi.org/10.1155/2013/526140

Research Article

Correlation of Photocatalysis and Photoluminescence Effect in Relation to the Surface Properties of TiO₂:Tb Thin Films

Damian Wojcieszak, Danuta Kaczmarek, Jaroslaw Domaradzki, and Michal Mazur

Faculty of Microsystem Electronics and Photonics, Wroclaw University of Technology, Janiszewskiego 11/17, 50-372 Wroclaw, Poland

Received 24 November 2012; Accepted 7 February 2013

Academic Editor: Christos Trapalis

Copyright © 2013 Damian Wojcieszak et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

In this paper structural, optical, photoluminescence, and photocatalytic properties of TiO₂ and TiO₂:(2.6 at. % Tb) thin films have been compared. Thin films were prepared by high-energy reactive magnetron sputtering process, which enables obtaining highly nanocrystalline rutile structure of deposited films. Crystallites sizes were 8.7 nm and 6.6 nm for TiO₂ and TiO₂:Tb, respectively. Surface of prepared thin films was homogenous with small roughness of ca. 7.2 and 2.1 nm in case of TiO₂ and TiO₂:Tb samples, respectively. Optical properties measurements have shown that the incorporation of Tb into TiO₂ matrix has not changed significantly the thin films transparency. It also enables obtaining photoluminescence effect in wide range from 350 to 800 nm, what is unique phenomenon in case of TiO₂ with rutile structure. Moreover, it has been found that the incorporation of 2.6 at. % of Tb has increased the photocatalytic activity more than two times as compared to undoped TiO₂. Additionally, for the first time in the current state of the art, the relationship between photoluminescence effect, photocatalytic activity, and surface properties of TiO₂:Tb thin films has been theoretically explained.

1. Introduction

In the recent years there has been a continuous increase of the application possibilities of various metal oxide thin films with certain properties. Thin films play a key role in the development of innovative technologies, for example, in ophthalmic or protective coatings. One of the most important coating materials is titanium dioxide (TiO₂). It is caused by its many advantages like high transparency, high refraction index, thermal, chemical, and mechanical stability, and high photocatalytic activity [1–6].

Proper selection of technological process parameters can influence the TiO₂ crystal structure (brookite, anatase, rutile, or amorphous) and the crystallites sizes. Depending on the type of the crystal structure titanium dioxide may exhibit different properties, for example, optical, electrical, and chemical. Also doping the TiO₂ with various materials influences its structural, optical, and electrical properties [7–9]. Moreover, the properties of thin films based on titanium dioxide can be further modified by the application of postprocess annealing [10–12]. The changes are then caused mainly by the increase in the crystallites sizes and as a result of the structure phase transformation, which usually takes place in elevated temperature.

Some desired properties of titanium dioxide can be obtained by doping with rare earth elements (REs). The application of the Res especially enables obtaining the photoluminescence effect. In practice, such materials can be used, for example, as light emitters in displays or in medical diagnostics. During the past two decades, a dynamic increase in interest of doping such oxides like SiO₂, ZrO₂, SnO₂, ZnO, and TiO₂ with lanthanides has been observed [9, 12–23]. In the present paper TiO₂ doped with terbium (Tb) has been described. Terbium is an f-electron element with the oxidation states of +3 and +4. The doping of oxides with terbium gives a broad photoluminescence spectrum with the maximum emission at the wavelength range corresponding to green light. However, there are rare examples in literature resources of light emission observed from terbium-doped TiO₂ thin films [24]

Incorporation of lanthanides into TiO₂ matrix also allows the modification of surface properties, what is crucial in photocatalysis processes. Photoinduced carriers formed in the matrix can undergo the recombination process, which reduce the photocatalytic activity. Carriers can be also intercepted by the trapping centers, which allows to avoid the recombination, or take part in reaction of pollutants decomposition and form oxidizing compounds. According to Liqiang et al. [25], photocatalytic activity of TiO₂ depends directly on amount of generated carriers, but its efficiency is determined by process of separation, recombination, capture, and transfer of carriers to the surface. It results from the fact that all oxidizing and reducing processes take place at the surface of TiO₂ [4, 26, 27]. Only pollutants, which are in contact with TiO₂ crystallites, can be decomposed. Significant factor in photocatalytic reaction is oxygen amount adsorbed at TiO₂ surface, because it inhibits the carriers recombination [28]. Also holes play significant role, because reaction based on those kinds of carriers is characterized by high quantum efficiency, particularly in oxidizing reaction of TiO₂ surface [28]. Active oxygen, hydroxide radicals, and hydrogen peroxide are the most reactive species formed in photocatalysis process.

For the purpose of the present work, thin films have been manufactured by magnetron sputtering method. In industrial application, sputtering processes are commonly used for deposition of thin oxide films [29–34]. These methods allow for deposition of films on the basis of infusible materials in relatively simple and cost-effective way. Additionally, magnetron sputtering gives the opportunity to control structure and stoichiometry of manufactured thin films. Huge advantage of this process is the possibility of deposition of dielectric, semiconductor, and metal films on large surfaces with different shapes. Proper selection of the magnetron sputtering process parameters enables the densification of thin-film crystal structure. The use of the modified process can result in nanocrystalline structure of deposited films with crystallites sizes varied from few to several nanometers [35, 36]. Densification of the structure is obtained by an increase in the sputtered species energy, that condenses at the substrate surface. This can be obtained by, for example, decrease of working gas pressure, increase in magnetron powering conditions, and application of voltage bias to the substrate.

In this paper, the influence of 2.6 at. % of Tb dopant on structural, optical, and photocatalytic properties of TiO₂ has been presented. Due to the lack of such description in the current state of the art, novel theoretical explanation of the relationship of photoluminescence effect and photocatalytic activity and the surface properties of TiO₂ doped with terbium has been presented.

2. Experimental

Titanium dioxide thin films doped with terbium have been deposited by high-energy reactive magnetron sputtering process (HERMS) [36–38]. Thin films were deposited in pure oxygen plasma (without argon as a working gas) by sputtering of metallic titanium target. Doping was obtained by sputtering of Ti-Tb mosaic target. Several sets of TiO₂ thin films doped with different amount of terbium were prepared. Samples consisted of 2.6 at. % of Tb were selected for further investigation due to simultaneous existence of photoluminescence and photocatalytic effects. Thickness of TiO₂ and TiO₂:Tb thin films was equal to 377 nm and 585 nm, respectively. The amount of the terbium dopant has been analyzed using energy-dispersive spectrometer.

X-ray diffraction (XRD) measurements were performed with the aid of Dron-2 powder diffractometer with Fe-filtered Co K radiation. Average crystallite sizes were determined using the standard Sheerer formula. Surface morphology of deposited samples was examined by atomic force microscope UHV VT AFM/STM Omicron operating in contact mode.

Optical properties of TiO₂:Tb thin films were investigated on the basis of transmission spectra. Transmission is the basic parameter defining the transparency level of the thin films and is defined as the ratio of light passing through the sample to the light incident the sample.

Emission properties of TiO₂:Tb thin films deposited on silica substrates were investigated by the photoluminescence (PL) method. For photoluminescence measurements UV argon laser with the excitation wavelength of 302 nm was used. Thin films were measured at room temperature.

The influence of terbium doping on photocatalytic properties of nanocrystalline TiO₂ thin films was estimated based on phenol decomposition reaction. The experimental setup consisted of a UV-Vis light source ( W Phillips lamps with intensity of UV and Vis radiation: 183 W/m2 and 167 W/m², resp.) and cylindrical reservoir which contained 100 mL of solution with the phenol concentration of 10 mg/L. To avoid the heating of the solution, the reaction temperature was controlled by circulation of water through the jacket at constant temperature of ca. 15°C. All experiments were carried out under agitation with a magnetic stirrer operating at 500 rpm in order to provide a good mixing of the suspension. No external oxygen supply was used. The phenol concentration was calculated from the absorption peak at 270 nm by means of a calibration curve. After 30 minutes of premixing at constant temperature, lights were switched on to initiate the reaction. To determine the change of the phenol concentration, samples of phenol solutions were withdrawn regularly every 60 minutes for 5 hours from the reactor. The final transparent solution was poured into a quartz cuvette and analyzed by UV-Vis spectrophotometer, in the wavelength range of 200–700 nm.

3. Results

As it was mentioned above, doping with lanthanides can result in modification of structural properties of TiO₂ thin films in a wide range. The significant role plays the amount of the dopant incorporated into titanium dioxide matrix. By selection of the dopant amount the specified crystal structure of TiO₂ directly after deposition process can be obtained. In Figure 1 results of XRD measurements of undoped TiO₂ and TiO₂:Tb deposited on silica substrates have been presented.

Figure 1: XRD measurements results of (a) undoped TiO₂ thin film, (b) TiO₂:Tb thin film, and (c) standard patterns for TiO₂-rutile structure. : crystallite size.

Broad peaks in the XRD patterns have shown that both thin films had nanocrystalline structure. Undoped TiO₂ have rutile structure with crystallites sizes of 8.7 nm. Doping with 2.6 at. % of terbium the TiO₂ matrix resulted in 25% decrease of crystallites sizes to 6.6 nm; however, the structure was still the rutile [37, 39, 40]. No diffraction peaks of Tb or Tb-O compounds have been found. These indicate that Tb (or its compounds) particles were too small to be detected by XRD or that Tb ions were incorporated into TiO₂ nanocrystals. Taking into account the ionic radius of Tb³⁺ the latter is less probable. It is more reasonable to assume that Tb dopant is localized at the surface of TiO₂ nanocrystals.

Structure densification is clearly seen on AFM images presented in Figure 2. Despite nanocrystalline structure, as-deposited thin films are very homogenous with small surface roughness. Root mean square (RMS) value is 3 times lower in case of terbium-doped titanium dioxide in comparison to undoped matrix. It was 7.2 and 2.1 for TiO₂ and TiO₂:Tb thin films, respectively. Symmetrical shape of grains size histogram in direction testifies about homogenous distribution of grains in deposited thin films.

(a)

(b)

Figure 2: AFM images of (a) TiO₂ thin film and (b) TiO₂:Tb thin film with height distribution of grains size in direction and surface roughness determined by RMS factor.

Influence of terbium doping on transparency of TiO₂ thin films was determined on the basis of transmission characteristics presented in Figure 3(a). Visible minima and maxima are connected with light interferences. Measurements have shown that the incorporation of Tb into TiO₂ matrix with the rutile structure has not changed significantly the transparency of the thin films. Moreover, doping has shifted the cutoff wavelength through longer wavelengths.

(a)

(b)

Figure 3: Optical properties of TiO₂ and TiO₂:Tb: (a) transmission characteristics and (b) Tauc plots for allowed indirect transitions. : thin film thickness.

Transmission measurements results allow for estimation of absorption coefficient, and on this basis the width of optical energy gap () has been determined. Characteristics, which were used to define optical energy gap, are presented in Figure 3(b). Results have shown that lower value was obtained for TiO₂:Tb and was equal to 2.96 eV.

As the result of TiO₂ matrix excitation with ultraviolet illumination, the photoluminescence spectrum in wide emission range, from 350 to 800 nm, has been observed (Figure 4). This spectrum is the superposition of six emission lines of various wavelengths, which corresponds to radiative recombination of carriers from different energy levels. Characteristic emission lines of Tb³⁺ ions, which occur at the wavelength of: 418 nm, 431 nm, 491 nm, 545 nm, and 619, correspond to electron transitions between ⁵D₃–⁷F₅, ⁵D₃–⁷F₄, ⁵D₄–⁷F₆, ⁵D₄–⁷F₅, and ⁵D₄–⁷F₃ levels, respectively. Moreover, light emission at 370 nm is connected with defect states transitions of titanium dioxide. Photoluminescence of terbium ions in TiO₂ matrix with rutile structure is unique phenomenon. Sheng et al. [24] have confirmed that such unique phenomenon was obtained only by authors of current paper.

Figure 4: TiO₂:Tb thin film photoluminescence spectrum under the excitation of Ar laser.

Kinetics of photocatalytic decomposition of organic compounds at the TiO₂ surface is usually consistent with Langmuire-Hinshelwood relationship [27, 41, 42]:

where is oxidizing rate, is solution concentration, is exposure time, is reaction rate constant, and is absorption coefficient.

For solutions with low initial concentration (at  mol level) the above equation can be simplified as follows [14, 28, 41]:

or

where is corrected reaction rate constant and is solution concentration after time .

The value of corrected reaction rate constant can be determined from slope of characteristic in the function of light exposure .

Results of phenol decomposition have shown that investigated thin films were photocatalytic. Photocatalytic activity was determined under the exposure to UV light based on dependence of in time function. Measurement results for TiO₂ and TiO₂: (2.6 at. % Tb) thin films have been shown in Figure 5. Those results were used to calculate phenol decomposition as thin film’s photocatalytic activity, which can be defined as

where is area of thin film.

Figure 5: Photocatalytic activity of TiO₂ and TiO₂:Tb thin films with rutile structure exposed to UV light time function based on dependence of .

By the reason of small sample size of approximately 1 cm², the phenol decomposition was estimated as %/cm². It has been found that the incorporation of 2.6 at. % of Tb has increased the photocatalytic activity more than two times as compared to undoped TiO₂ matrix. After five hours TiO₂ doped with terbium has decomposed ca. 4.7% of phenol, while, in the same time, undoped TiO₂ has decomposed just 2.2% of phenol. Such results are unique in case of TiO₂ with the rutile structure. Corrected reaction rate constant was also two times higher for TiO₂:Tb in comparison to TiO₂ thin film.

4. Discussion

Nanocrystalline TiO₂ thin film doped with Tb exhibits photoluminescence properties and increased photocatalytic activity in comparison to undoped nanocrystalline TiO₂ thin film with rutile structure. From the state of the art it is well known that materials with nanocrystalline structure composed of crystallites in size of less than 10 nm exhibit higher photoluminescence or photocatalytic activity as compared to materials with larger crystallites [43–45]. In case of materials with such nanocrystalline structure, the influence of quantum size effect on luminescence properties was first described by Bhargawa et al. [46]. According to the literature [43–45], both specific energy levels and the decrease of energy band gap in nanocrystalline oxide matrix can be observed as size of the crystallites is in the range from 2 to 10 nm. Size of the crystallites has an essential influence on series of different properties of metal oxides connected with the degree of the surface area development. Similarly, as in case of photoluminescence, also photocatalytic activity of the thin films based on TiO₂ is the highest for matrix composed of crystallites in size that ranges from 5 to 10 nm [42, 43, 47].

In current state of the art only one article [25] can be found, which tries to describe mutual relationship between the photocatalysis and the photoluminescence. The key factor for conjunction of photoluminescence effect and the decomposition of pollutants, which proceeds at the surface of material, is the oxygen vacancies concentration [25]. These defects are the trapping centers, which inhibit recombination and simultaneously enables on efficient joining electrons with oxygen. Moreover, they are active centers for surface absorption of water particles and OH⁻ groups, which are necessary for carrying out of the photocatalytic reaction.

One of the main limits for these both effects is relatively low total quantum efficiency connected with high level of recombination of the electron-hole pairs generated at the TiO₂ surface [25]. Therefore, increasing of light emission intensity or photocatalytic activity of thin films based on TiO₂ can be obtained by, for example, decrease of crystallites size [48, 49] or by doping [8, 50, 51]. It is because, for nanomaterials, diffusion rate is much larger than recombination rate. The most often, thin films with high photocatalytic activity exhibit weak photoluminescence effect, which is connected with low carriers recombination efficiency [52, 53]. However, in the current state of the art there are also examples of materials characterized by strong photoluminescence effect and high photocatalytic activity [54, 55]. It indicates that these results are inconsistent, and explanation of reasons of such different interpretations needs much more detailed analysis of carriers: excitation and recombination mechanisms. For TiO₂:(2.6% at. % Tb) strong photoluminescence and high photocatalytic activity have been found simultaneously; hence, it is necessary to elaborate on the model, which takes into consideration the relationship between these two phenomena.

Explanation of relationship between photoluminescence effect and photocatalysis phenomenon needs the complex analysis of different types of recombination, which occurs in titanium dioxide [25, 56–59]. In such material, electrons and holes are generated under the photoexcitation. Photoexcited electrons transit to the conduction band and fill the energy levels, which correspond to excitation energy. These carriers can easily recombine and return to valence band in different ways, and their energy can be emitted as photons or phonons. Excited electrons can transit directly to valence band with release of energy in the form of light emission. This type of direct transitions can take place also in case of electrons with higher energy than ; however, transfer of carriers proceeds then directly from levels situated above the bottom edge of conduction band. The recombination process can also occur via sublevels in energy band gap (defect states of the matrix) and it is an indirect radiative transition.

In case of photoluminescence effect, which is present as the result of direct radiative recombination, lower recombination of generated carriers causes the decrease of light emission intensity. However, this process simultaneously increases the photocatalytic activity of the semiconductor [53]. Whereas, in case of indirect radiative recombination, the relation between photoluminescence effect intensity and photocatalytic activity depends on the type of the incorporated dopant. According to Liqiang et al. [25], lower recombination cause smaller photoluminescence intensity and higher photocatalytic activity of semiconductor. Although, sometimes also the increase of defects amount and oxygen vacancies at the thin film surface allow to obtain higher intensity of photoluminescence and photocatalytic activity [25]. Such relations can be applied for analysis of TiO₂ thin films doped with rare earth elements, in which emission levels are below defect states of the matrix. For prepared TiO₂:(2.6 at. % Tb) thin film, none of the abovementioned explanations can be accepted as a basis for analysis of relation between photoluminescence and photocatalysis phenomena. Therefore, it was necessary to elaborate on individual model, which takes into consideration properties of prepared thin films and mechanisms occurring during both discussed processes.

The abovementioned processes proceed at the titanium dioxide nanograin surface with rutile structure. Under the exposure to light, generated electrons in matrix pass from the valence to conduction band and take part in reaction with oxygen adsorbed at the film surface, creating oxygen radicals () [28]. On the other hand, holes from valence band take part in reaction with water and hydroxide groups (OH⁻) adsorbed at the surface. Consequently hydroxide radicals (OH•) are formed [28]. Moreover, electrons trapped by the matrix’s defect states also can take part in process of oxygen radicals formation, which is caused by considerably shorter time of diffusion than recombination in case of nanograins. In the following stages, at the surface of nanocrystalline film, the decomposition of contaminations proceeds with the participation of oxygen () and hydroxide (OH•) radicals. Final products of these reactions are CO₂ and H₂O.

Doping TiO₂ matrix with 2.6 at. % of terbium allows obtaining thin film with photoluminescence properties, which exhibits two times higher photocatalytic activity as compared to undoped titanium dioxide. The incorporation of terbium dopant causes increase in the number of energy levels to which electrons generated in TiO₂ matrix can be transferred. Therefore, photocatalytic rate increases and favorably influences thin film activity. In Figure 6 scheme of processes proceeding at the TiO₂:Tb surface with the rutile structure is presented.

Figure 6: The scheme of processes proceeding at the TiO₂:Tb surface with rutile structure. Designations: , , energy of the bottom edge of the conduction band and the top of the valence band, respectively; , electron; , hole; O₂, oxygen; , oxygen radical; H₂O, water; H⁺, hydrogen; OH⁻, hydroxide group; OH•, hydroxide radical; (ads), surface adsorption.

In case of photocatalysis process, presence of terbium at the surface causes changes of the surface energy parameters. Both terbium ions on +3 and +4 oxidation states can accept and return electrons. Presence of these ions facilitates the transfer of carriers, which is necessary in photocatalysis reaction.

Briefly, based on structural and optical properties analysis of the TiO₂:Tb thin films, it was found that the incorporation of terbium dopant during high-energy reactive magnetron sputtering process allowed for preparing of homogenous, densely packed films, which were composed of crystallites in size of 6.6 nm. Such small crystallites sizes and significantly higher degree of order of film structure (in comparison to undoped titanium dioxide) favorably influence both discussed phenomena by the increasing of active area. Smaller crystallites size causes that the range of transition to make for electrons is also smaller [25, 42, 43]. Therefore, the probability of carrier transfer between the TiO₂ crystallites and Tb ions localized at the surface is large. Except nanocrystalline structure, the key role for both phenomena plays amount of the dopant, which should be incorporated into TiO₂ matrix in high-energy deposition process. It is necessary to incorporate the sufficient amount of the dopant to obtain the suitable number of the ions at the +3 oxidation state.

5. Conclusions

In present paper analysis of the influence of 2.6 at. % terbium dopant on the TiO₂:Tb thin films properties has been outlined. Thin films deposited in high-energy reactive magnetron sputtering process were homogenous and densely packed. TiO₂:Tb film had rutile structure with crystallites size of 6.6 nm.

Investigations of photocatalytic properties have shown that doping with terbium favorably influence the increase of TiO₂ matrix surface activity. Moreover, based on optical properties analysis, it was found that terbium did not deteriorate the high transparency of TiO₂, but influence the position shift of cutoff wavelength and width of optical band gap. The incorporation of terbium allowed for obtaining photoluminescence effect of Tb³⁺ in TiO₂ matrix with the rutile structure, which is unique and has not been reported yet by other authors. TiO₂:Tb after 5 hours of the photocatalytic activity investigation has decomposed two times more phenol as compared to undoped TiO₂.

Results of investigations have shown that, to increase the photocatalytic activity of TiO₂:Tb thin films the presence of Tb³⁺ at the surface of TiO₂ nanocrystals is necessary. The addition of terbium to TiO₂ matrix caused that additional energy levels have appeared and favorably influenced energy transfer mechanism. Thanks to terbium doping of titanium dioxide, it was possible to obtain effective photoinduced carriers transfer mechanism, which is necessary requirement for the presence of both phenomena: photocatalysis and photoluminescence.

Acknowledgments

The authors would like to thank E. L. Prociow from Wrocław University of Technology for his help in the experimental part of this work. This work was financed from the sources granted by the NCN in the years 2011–2013 as a research project no. N N515 4963 40, in years 2013–2015 as a research project no. 2012/05/N/ST7/00173, and from the statute sources given by the MNiSW in the years 2012-2013.

References

H. Bieber, P. Gilliot, M. Gallart et al., “Temperature dependent photoluminescence of photocatalytically active titania nanopowders,” Catalysis Today, vol. 122, no. 1-2, pp. 101–108, 2007.

U. Diebold, “The surface science of titanium dioxide,” Surface Science Reports, vol. 48, pp. 53–229, 2003.

K. Eufinger, D. Poelman, H. Poelman, R. De Gryse, and G. B. Marin, “Photocatalytic activity of dc magnetron sputter deposited amorphous TiO₂ thin films,” Applied Surface Science, vol. 254, no. 1, pp. 148–152, 2007.

A. Fujishima, T. N. Rao, and D. A. Tryk, “Titanium dioxide photocatalysis,” Journal of Photochemistry and Photobiology C, vol. 1, no. 1, pp. 1–21, 2000.

G. Li, L. Chen, M. E. Graham, and K. A. Gray, “A comparison of mixed phase titania photocatalysts prepared by physical and chemical methods: the importance of the solid-solid interface,” Journal of Molecular Catalysis A, vol. 275, no. 1-2, pp. 30–35, 2007.

Y. Xie and C. Yuan, “Transparent TiO₂ sol nanocrystallites mediated homogeneous-like photocatalytic reaction and hydrosol recycling process,” Journal of Materials Science, vol. 40, no. 24, pp. 6375–6383, 2005.

T. L. Chen, Y. Furubayashi, Y. Hirose, T. Hitosugi, T. Shimada, and T. Hasegawa, “Anatase phase stability and doping concentration dependent refractivity in codoped transparent conducting TiO₂ films,” Journal of Physics D, vol. 40, no. 19, article 026, pp. 5961–5964, 2007.

W. Choi, A. Termin, and M. R. Hoffmann, “The role of metal ion dopants in quantum-sized TiO₂: correlation between photoreactivity and charge carrier recombination dynamics,” Journal of Physical Chemistry, vol. 98, no. 51, pp. 13669–13679, 1994.

K. L. Frindell, M. H. Bartl, M. R. Robinson, G. C. Bazan, A. Popitsch, and G. D. Stucky, “Visible and near-IR luminescence via energy transfer in rare earth doped mesoporous titania thin films with nanocrystalline walls,” Journal of Solid State Chemistry, vol. 172, no. 1, pp. 81–88, 2003.

J. Domaradzki, D. Kaczmarek, A. Borkowska et al., “Influence of annealing on the structure and stoichiometry of europium-doped titanium dioxide thin films,” Vacuum, vol. 82, no. 10, pp. 1007–1012, 2008.

Y. Q. Hou, D. M. Zhuang, G. Zhang, M. Zhao, and M. S. Wu, “Influence of annealing temperature on the properties of titanium oxide thin film,” Applied Surface Science, vol. 218, no. 1–4, pp. 97–105, 2003.

A. Podhorodecki, G. Zatryb, J. Misiewicz, J. Domaradzki, D. Kaczmarek, and A. Borkowska, “Influence of annealing on europium photoexcitation doped into nanocrystalline titania film prepared by magnetron sputtering,” Journal of the Electrochemical Society, vol. 156, no. 3, pp. H214–H219, 2009.

G. Feng, S. F. Wang, M. K. Lu et al., “Luminescent characteristics of Eu³⁺ in SnO₂ nanoparticles,” Optical Materials, vol. 25, no. 1, pp. 59–64, 2004.

F. Gourbilleau, P. Choppinet, C. Dufour et al., “Emission of Er- and Si-doped silicate glass films obtained by magnetron co-sputtering,” Materials Science and Engineering B, vol. 105, no. 1–3, pp. 44–47, 2003.

P. G. Kik and A. Polman, “Exciton-erbium energy transfer in Si nanocrystal-doped SiO₂,” Materials Science and Engineering, vol. 81, no. 1–3, pp. 3–8, 2001.

K. Kuratani, M. Mizuhata, A. Kajinami, and S. Deki, “Synthesis and luminescence property of Eu³⁺/ZrO₂ thin film by the liquid phase deposition method,” Journal of Alloys and Compounds, vol. 408-412, pp. 711–716, 2006.

Z. Liu, J. Zhang, B. Han et al., “Solvothermal synthesis of mesoporous Eu₂O₃-TiO₂ composites,” Microporous and Mesoporous Materials, vol. 81, no. 1–3, pp. 169–174, 2005.

A. Peng, E. Xie, C. Jia, R. Jiang, and H. Lin, “Photoluminescence properties of TiO₂: Eu³⁺ thin films deposited on different substrates,” Materials Letters, vol. 59, no. 29-30, pp. 3866–3869, 2005.

B. Schaudel, P. Goldner, M. Prassas, and F. Auzel, “Cooperative luminescence as a probe of clustering in Yb³⁺ doped glasses,” Journal of Alloys and Compounds, vol. 300, pp. 443–449, 2000.

M. Sendova-Vassileva, M. Nikolaeva, D. Dimova-Malinovska, M. Tzolov, and J. C. Pivin, “Room-temperature photoluminescence from Tb³⁺ ions in SiO₂ and a-SiC:H thin films deposited by magnetron co-sputtering,” Materials Science and Engineering B, vol. 81, no. 1–3, pp. 185–187, 2001.

D. Kaczmarek, J. Domaradzki, A. Borkowska, A. Podhorodecki, J. Misiewicz, and K. Sieradzka, “Optical emission from Eu, Tb, Nd luminescence centers in TiO₂ prepared by magnetron sputtering,” Optica Applicata, vol. 37, no. 4, pp. 433–438, 2007.

J. Domaradzki, E. L. Prociow, D. Kaczmarek et al., “X-ray, optical and electrical characterization of doped nanocrystalline titanium oxide thin films,” Materials Science and Engineering B, vol. 109, no. 1–3, pp. 249–251, 2004.

J. Domaradzki, D. Wojcieszak, E. Prociow, and D. Kaczmarek, “Characterization of transparent and nanocrystalline TiO₂:Nd thin films prepared by magnetron sputtering,” Acta Physica Polonica A, vol. 116, pp. S75–S77, 2009.

Y. Sheng, L. Zhang, H. Li et al., “Photoluminescence of TiO₂ films co-doped with Tb³⁺/Gd³⁺ and energy transfer from TiO₂/Gd³⁺ to Tb³⁺ ions,” Thin Solid Films, vol. 519, no. 22, pp. 7966–77970, 2011.

J. Liqiang, Q. Yichun, W. Baiqi et al., “Review of photoluminescence performance of nano-sized semiconductor materials and its relationships with photocatalytic activity,” Solar Energy Materials and Solar Cells, vol. 90, no. 12, pp. 1773–1787, 2006.

A. Fujishima, X. Zhang, and D. A. Tryk, “TiO₂ photocatalysis and related surface phenomena,” Surface Science Reports, vol. 63, no. 12, pp. 515–582, 2008.

H. Ohsaki, N. Kanai, Y. Fukunaga, M. Suzuki, T. Watanabe, and K. Hashimoto, “Photocatalytic properties of SnO2/TiO₂ multilayers,” Thin Solid Films, vol. 502, no. 1-2, pp. 138–142, 2006.

U. I. Gaya and A. H. Abdullah, “Heterogeneous photocatalytic degradation of organic contaminants over titanium dioxide: a review of fundamentals, progress and problems,” Journal of Photochemistry and Photobiology C, vol. 9, no. 1, pp. 1–12, 2008.

L. Chen, M. E. Graham, G. Li, and K. A. Gray, “Fabricating highly active mixed phase TiO₂ photocatalysts by reactive DC magnetron sputter deposition,” Thin Solid Films, vol. 515, no. 3, pp. 1176–1181, 2006.

M. Gómez, J. Rodríguez, S.-E. Lindquist, and C. G. Granqvist, “Photoelectrochemical studies of dye-sensitized polycrystalline titanium oxide thin films prepared by sputtering,” Thin Solid Films, vol. 342, no. 1, pp. 148–152, 1999.

C. H. Heo, S.-B. Lee, and J. H. Boo, “Deposition of TiO₂ thin films using RF magnetron sputtering method and study of their surface characteristics,” Thin Solid Films, vol. 475, no. 1-2, pp. 183–188, 2005.

E. P. Lokshin and T. A. Sedneva, “On stabilization of anatase with the fluoride ion,” Russian Journal of Applied Chemistry, vol. 79, no. 8, pp. 1220–1224, 2006.

M. D. Stamate, “On the non-linear I–V characteristics of dc magnetron sputtered TiO₂ thin films,” Applied Surface Science, vol. 205, no. 1–4, pp. 353–357, 2003.

S. F. Wang, Y. F. Hsu, and Y. S. Lee, “Microstructural evolution and optical properties of doped TiO₂ films prepared by RF magnetron sputtering,” Ceramics International, vol. 32, no. 2, pp. 121–125, 2006.

J. Domaradzki, D. Kaczmarek, E. L. Prociow, and Z. J. Radzimski, “Study of structure densification in TiO₂ coatings prepared by magnetron sputtering under low pressure of oxygen plasma discharge,” Acta Physica Polonica A, vol. 120, no. 1, pp. 49–52, 2011.

D. Kaczmarek, E. Prociów, J. Domaradzki, A. Borkowska, W. Mielcarek, and D. Wojcieszak, “Influence of substrate type and its placement on structural properties of TiO₂ thin films prepared by the high energy reactive magnetron sputtering method,” Materials Science-Poland, vol. 26, no. 1, pp. 113–117, 2008.

D. Kaczmarek, D. Wojcieszak, J. Domaradzki et al., “Influence of nanocrystalline structure and composition on hardness of thin films based on TiO₂,” Central European Journal of Physics, vol. 9, no. 2, pp. 349–353, 2011.

R. Wasielewski, J. Domaradzki, D. Wojcieszak et al., “Surface characterization of TiO₂ thin films obtained by high-energy reactive magnetron sputtering,” Applied Surface Science, vol. 254, no. 14, pp. 4396–4400, 2008.

J. Domaradzki, D. Kaczmarek, E. Prociów et al., “Study of structural and optical properties of TiO₂:tb thin films prepared by high energy reactive magnetron sputtering method,” Optica Applicata, vol. 39, no. 4, pp. 815–823, 2009.

D. Kaczmarek, J. Domaradzki, D. Wojcieszak et al., “Structural investigations of TiO₂:Tb thin films by X-ray diffraction and atomic force microscopy,” Applied Surface Science, vol. 254, no. 14, pp. 4303–4307, 2008.

I. K. Konstantinou and T. A. Albanis, “Photocatalytic transformation of pesticides in aqueous titanium dioxide suspensions using artificial and solar light: intermediates and degradation pathways,” Applied Catalysis B, vol. 42, no. 4, pp. 319–335, 2003.

A. Mills and S. Le Hunte, “An overview of semiconductor photocatalysis,” Journal of Photochemistry and Photobiology A, vol. 108, no. 1, pp. 1–35, 1997.

H. R. Kim, T. G. Lee, and Y. G. Shul J, “Photoluminescence of La/Ti mixed oxides prepared using sol-gel process and their pCBA photodecomposition,” Journal of Photochemistry and Photobiology A, vol. 185, no. 2-3, pp. 156–160, 2007.

T. Y. Wei, C. Y. Kuo, Y. J. Hsu, S. Y. Lu, and Y. C. Chang, “Tin oxide nanocrystals embedded in silica aerogel: photoluminescence and photocatalysis,” Microporous and Mesoporous Materials, vol. 112, no. 1–3, pp. 580–588, 2008.

M. Zalewska and A. M. Kłonkowski, “Energy transfer from TiO₂ nanocrystals to Tb³⁺ ions incorporated into silica,” Optical Materials, vol. 30, no. 5, pp. 725–729, 2008.

R. N. Bhargawa, D. Gallagher, X. Hong, and A. Nurmikko, “Optical properties of manganese-doped nanocrystals of ZnS,” Physical Review Letters, vol. 72, no. 3, pp. 416–419, 1994.

K. M. Reddy, C. V. G. Reddy, and S. V. Manorama, “Preparation, characterization, and spectral studies on nanocrystalline anatase TiO₂,” Journal of Solid State Chemistry, vol. 158, no. 2, pp. 180–186, 2001.

A. J. Maira, K. L. Yeung, C. Y. Lee, P. L. Yue, and C. K. Chan, “Size effects in gas-phase photo-oxidation of trichloroethylene using nanometer-sized TiO₂ catalysts,” Journal of Catalysis, vol. 192, no. 1, pp. 185–196, 2000.

Z. Xu, J. Shang, C. Liu, C. Kang, H. Guo, and Y. Du, “The preparation and characterization of TiO₂ ultrafine particles,” Materials Science and Engineering B, vol. 63, no. 3, pp. 211–214, 1999.

J. Soria, J. C. Conesa, V. Augugliaro, L. Palmisano, M. Schiavello, and A. Sclafani, “Dinitrogen photoreduction to ammonia over titanium dioxide powders doped with ferric ions,” Journal of Physical Chemistry, vol. 95, no. 1, pp. 274–282, 1991.

J. C. Yu, J. G. Yu, K. W. Ho, Z. T. Jiang, and L. Z. Zhang, “Effects of F⁻ Doping on the photocatalytic activity and microstructures of nanocrystalline TiO₂ powders,” Chemistry of Materials, vol. 14, no. 9, pp. 3808–3816, 2002.

X. Z. Li, F. B. Li, C. L. Yang, and W. K. Ge J, “Photocatalytic activity of WOx-TiO₂ under visible light irradiation,” Journal of Photochemistry and Photobiology A, vol. 141, no. 2-3, pp. 209–217, 2001.

J. G. Yu, H. G. Yu, B. Chen, X. J. Zhao, J. C. Yu, and W. K. Ho, “The effect of calcination temperature on the surface microstructure and photocatalytic activity of TiO2 thin films prepared by liquid phase deposition,” The Journal of Physical Chemistry B, vol. 107, no. 50, pp. 13871–13879, 2003.

J. Liqiang, S. Xiaojun, X. Baifu, W. Baiqi, C. Weimin, and F. Honggang, “The preparation and characterization of la doped TiO₂ nanoparticles and their photocatalytic activity,” Journal of Solid State Chemistry, vol. 177, no. 10, pp. 3375–3382, 2004.

L. Q. Jing, F. L. Yuan, H. G. Hou, B. F. Xin, W. M. Cai, and H. G. Fu, “Relationships of surface oxygen vacancies with photoluminescence and photocatalytic performance of ZnO nanoparticles,” Science China Chemistry, vol. 48, no. 1, pp. 25–30, 2005.

M. R. Hoffmann, S. T. Martin, W. Choi, and D. W. Bahnemann, “Environmental applications of semiconductor photocatalysis,” Chemical Reviews, vol. 95, no. 1, pp. 69–96, 1995.

A. L. Linsebigler, G. Lu, and J. T. Yates, “Photocatalysis on TiO₂ surfaces: principles, mechanisms, and selected results,” Chemical Reviews, vol. 95, no. 3, pp. 735–758, 1995.

M. I. Litter, “Heterogeneous photocatalysis: transition metal ions in photocatalytic systems,” Applied Catalysis B, vol. 23, no. 2-3, pp. 89–114, 1999.

D. Wojcieszak, D. Kaczmarek, J. Domaradzki, E. Prociów, A. W. Morawski, and M. Janus, “Photocatalytic properties of nanocrystalline TiO₂ thin films doped with Tb,” Central European Journal of Physics, vol. 9, no. 2, pp. 354–359, 2011.