International Journal of Photoenergy

Volume 2014 (2014), Article ID 643532, 3 pages

http://dx.doi.org/10.1155/2014/643532

Research Article

Sensitization of Perovskite Strontium Stannate SrSnO₃ towards Visible-Light Absorption by Doping

Hungru Chen¹ and Naoto Umezawa1,2,3

¹Environmental Remediation Materials Unit, National Institute for Materials Sciences, Ibaraki Prefecture 305-0044, Japan

²PRESTO, Japan Science and Technology Agency (JST), 4-1-8 Honcho, Kawaguchi, Saitama Prefecture 332-0012, Japan

³TU-NIMS Joint Research Center, School of Materials Science and Engineering, Tianjin University, 92 Weijin Road, Nankai District, Tianjin, China

Received 26 June 2014; Accepted 3 August 2014; Published 18 August 2014

Academic Editor: Wenjun Luo

Copyright © 2014 Hungru Chen and Naoto Umezawa. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

Perovskite strontium stannate SrSnO₃ is a promising photocatalyst. However, its band gap is too large for efficient solar energy conversion. In order to sensitize SrSnO₃ toward visible-light activities, the effects of doping with various selected cations and anions are investigated by using hybrid density functional calculations. Results show that doping can result in dopant level to conduction band transitions which lie lower in energy compared to the original band gap transition. Therefore, it is expected that doping SrSnO₃ can induce visible-light absorption.

1. Introduction

Photocatalysis is an important technology for fuel production and environmental remediation from solar energy conversion [1–4]. Perovskite strontium stannate SrSnO₃ has been reported to be a promising photocatalyst [5–7]. Due to its suitable valence band and conduction band edge positions, it is able to split water into hydrogen and oxygen. The main drawback of SrSnO₃ is the large band gap of 4.1 eV [7] and therefore it can only absorb light in the ultraviolet region. A material for efficient solar energy conversion should be able to absorb the majority of the sunlight, namely, visible light. In order to sensitize wide gap materials to visible light, doping has been a common approach [8–10]. In this study, hybrid density functional theory calculations are carried out to investigate the effect of doping in SrSnO₃. Cations Cr³⁺, Fe³⁺, and Rh³⁺ and anions , , and , which have been reported to be effective dopants for sensitizing titanates to visible light, are considered [10, 11].

2. Computational Methods

All calculations are carried out based on density functional theory [12] with the range separated HSE06 hybrid functional [13]. Valence electrons are described by a plane wave basis set with the energy cutoff of 500 eV. The interactions between core and valence electrons are treated with the projector augmented wave (PAW) method [14]. The k-space is sampled with k-point spacing less than 0.03 . The lattice vectors and atomic positions in all cells are optimized until the force is converged to less than 0.03 eV- at each atomic position. Vienna ab initio simulation package (VASP) [15] is used for all calculations.

SrSnO₃ adopts the orthorhombic perovskite structure with space group symmetry Pbnm [16], as shown in Figure 1. To model doped SrSnO₃, a SrSnO₃ supercell, which contains 16 formula units (80 atoms), is constructed. Cation doping is simulated by substituting a dopant, Cr³⁺, Fe³⁺, or Rh³⁺, for one Sn⁴⁺, which corresponds to 6.25% of B-site cation impurity. To ensure the correct trivalent charge states of cation dopants, in each of the above cases La³⁺ is simultaneously substituted for Sr²⁺. Anion doping is modeled by substituting a dopant, , , or , for one , which corresponds to 2.08% of anion impurity. In the case is simultaneously substituted for .

Figure 1: The orthorhombic perovskite structure of SrSnO₃. The green and red spheres denote strontium and oxygen, respectively. The gray octahedra denote SnO₆ units.

3. Results and Discussions

The calculated lattice parameters for the orthorhombic perovskite SrSnO₃ are  Å,  Å, and  Å, which are in good agreement with experimental values  Å,  Å, and  Å [17]. Figure 2 shows the density of states and band structure from our calculations. The calculated band gap of pristine SrSnO₃ is 3.52 eV, smaller than experimentally reported optical gap 4.1 eV. The origin of this 0.5 eV discrepancy is not clear at the moment. It could be an underestimation from the functional used in calculations. It could be that the transition from the highest occupied state to the lowest occupied state is forbidden [18]. More detailed analysis is necessary to clarify this. The bottom of the conduction band is a mixture of Sn 5s states and O 2p states. Different from d state conduction bands, it is very dispersive and therefore electrons in this band should possess lower effective mass than in d bands. The top of valence band is comprised mainly of oxygen 2p states.

Figure 2: Calculated density of states and band structure of the pristine SrSnO₃.

Figure 3 shows the calculated density of states of cation and anion doped SrSnO₃. It is assumed that dopants do not influence the position of the SrSnO₃ O 2p valence band and the top of O 2p valence band in each cell is aligned at 0 eV. In each case, dopant produces occupied states above the SrSnO₃ valence band maximum (VBM). This indicates the emergence of dopant to conduction band minimum (CBM) transitions. However, in the cases of Cr³⁺, Fe³⁺, and Rh³⁺ doping, the position of CBM is also shifted up by about 0.3 eV compared to pristine SrSnO₃. This is probably due to the s state interaction between Sn⁴⁺ ions, which form the lowest part of conduction band, being disturbed by the presence of cation impurity. Overall, the Cr³⁺ → CBM and Rh³⁺ → CBM transitions are 3.21 eV and 2.63 eV, respectively. The position of Fe³⁺ states above VBM is relatively shallow and therefore the Fe³⁺ → CBM transition 3.53 eV is even higher in energy than the pristine SrSnO₃ band gap. In anion doping cases, the position of CBM is less affected. In the doping case, the CBM is actually downshifted by about 0.1 eV. Overall, the transitions from , , and to CBM are 2.94 eV, 2.45 eV, and 3.09 eV, respectively.

Figure 3: The calculated density of states in the pristine and doped cases. The shaded areas denote total density of states and the red lines denote the dopant states. The positions of the highest occupied state and the edge of conduction band minimum are marked by green lines. The magnitudes of the dopant to conduction band minimum transitions in each case are listed.

4. Conclusions

Through hybrid density functional calculations, it is shown that the doping of various cations and anions introduces occupied dopant states above the SrSnO₃ O 2p valence band. Transitions from these dopant states to the SrSnO₃ conduction band cost lower energies than the original band gap transition, apart from the Fe³⁺ case, and are hoped to contribute more towards visible-light photocatalytic activities. Among all considered cation dopants, Rh³⁺ gives rise to the deepest in gap states. The transition from Rh³⁺ to SrSnO₃ conduction band is 0.89 eV lower than the band gap. Among all considered anion dopants, appears to show the best result. The transition from to SrSnO₃ conduction band is 1.07 eV lower than the SrSnO₃ band gap. Nevertheless, one should be cautioned that whether or not dopant associated localized states can really contribute to steady-state activities is a question [8, 19].

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This work is partly supported by the Japan Science and Technology Agency (JST) Precursory Research for Embryonic Science and Technology (PRESTO) program and by the World Premier International Research Center Initiative on Materials Nanoarchitectonics (MANA), MEXT.

References

S. C. Roy, O. K. Varghese, M. Paulose, and C. A. Grimes, “Toward solar fuels: photocatalytic conversion of carbon dioxide to hydrocarbons,” ACS Nano, vol. 4, no. 3, pp. 1259–1278, 2010.

F. E. Osterloh and B. A. Parkinson, “Recent developments in solar water-splitting photocatalysis,” MRS Bulletin, vol. 36, no. 1, pp. 17–22, 2011.

M. R. Hoffmann, S. T. Martin, W. Choi, and D. W. Bahnemann, “Environmental applications of semiconductor photocatalysis,” Chemical Reviews, vol. 95, no. 1, pp. 69–96, 1995.

F. E. Osterloh, “Inorganic materials as catalysts for photochemical splitting of water,” Chemistry of Materials, vol. 20, no. 1, pp. 35–54, 2008.

D. Chen and J. Ye, “SrSnO₃ nanostructures: synthesis, characterization, and photocatalytic properties,” Chemistry of Materials, vol. 19, no. 18, pp. 4585–4591, 2007.

W. F. Zhang, J. Tang, and J. Ye, “Structural, photocatalytic, and photophysical properties of perovskite MSnO3 (M = Ca, Sr, and Ba) photocatalysts,” Journal of Materials Research, vol. 22, no. 7, pp. 1859–1871, 2007.

W. F. Zhang, J. Tang, and J. Ye, “Photoluminescence and photocatalytic properties of SrSnO₃ perovskite,” Chemical Physics Letters, vol. 418, no. 1–3, pp. 174–178, 2006.

K. Mizushima, M. Tanaka, A. Asai, S. Iida, and J. B. Goodenough, “Impurity levels of iron-group ions in TiO2(II),” Journal of Physics and Chemistry of Solids, vol. 40, no. 12, pp. 1129–1140, 1979.

H. P. Maruska and A. K. Ghosh, “Transition-metal dopants for extending the response of titanate photoelectrolysis anodes,” Solar Energy Materials, vol. 1, no. 3-4, pp. 237–247, 1979.

R. U. E. 't Lam, L. G. J. de Haart, A. W. Wiersma, G. Blasse, A. H. A. Tinnemans, and A. Mackor, “The sensitization of SrTiO3 photoanodes by doping with various transition metal ions,” Materials Research Bulletin, vol. 16, no. 12, pp. 1593–1600, 1981.

K. Iwashina and A. Kudo, “Rh-doped SrTiO₃ photocatalyst electrode showing cathodic photocurrent for water splitting under visible-light irradiation,” Journal of the American Chemical Society, vol. 133, no. 34, pp. 13272–13275, 2011.

P. Hohenberg and W. Kohn, “Inhomogeneous electron gas,” vol. 136, pp. B864–B871, 1964.

J. Heyd, G. E. Scuseria, and M. Ernzerhof, “Erratum: “Hybrid functionals based on a screened Coulomb potential” [J. Chem. Phys.118, 8207 (2003)],” The Journal of Chemical Physics, vol. 124, no. 21, Article ID 219906, 2006.

P. E. Blöchl, “Projector augmented-wave method,” Physical Review B, vol. 50, no. 24, pp. 17953–17979, 1994.

G. Kresse and J. Furthmüller, “Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set,” Physical Review B—Condensed Matter and Materials Physics, vol. 54, no. 16, pp. 11169–11186, 1996.

E. H. Mountstevens, S. A. T. Redfern, and J. P. Attfield, “Order-disorder octahedral tilting transitions in SrSnO₃ perovskite,” Physical Review B, vol. 71, no. 22, Article ID 220102, 2005.

M. A. Green, K. Prassides, P. Day, and D. A. Neumann, “Structure of the and member of the Ruddlesden-Popper series,Sr(n+1)SnnO3n+1,” International Journal of Inorganic Materials, vol. 2, no. 1, pp. 35–41, 2000.

V. T. Agekyan, “Spectroscopic properties of semiconductor crystals with direct forbidden energy gap,” Physica Status Solidi A, vol. 43, no. 1, pp. 11–42, 1977.

J. B. Goodenough, A. Hamnett, M. P. Dare-Edwards, G. Campet, and R. D. Wright, “Inorganic materials for photoelectrolysis,” Surface Science, vol. 101, no. 1–3, pp. 531–540, 1980.