A new bioartificial polymeric material consisting of a bilayer of cellulose acetate and poly(vinyl alcohol) was successfully obtained by casting method. The material was characterized by Fourier transform infrared spectroscopy, contact angle, scanning electron microscopy, differential scanning calorimetry, gas permeability, water vapor permeability, and mechanical properties. The characterization indicates that two distinct and well-differentiated surfaces were achieved without detriment to the bulk properties. The interaction between natural and synthetic polymers indeed enhanced the gas permeability as well as the water vapor permeability in comparison to the original components, although mechanical properties were not substantially boosted by the combination of both. Moreover, beyond the interface, there were no detected interactions between the polymers as can be evidenced by the presence of a unique Tg in the bilayer. The amalgamation of the relatively good mechanical properties with the two differentiated surfaces and the improvement of the permeability properties could indicate the potential of the material for being used in medicine.
1. Introduction
A sight to the past evidences that, during the last two decades, synthetic and natural polymers have been separately used as potential biomaterials [1]. Among biomaterials, bioartificial polymeric materials (BAPM) have gained an important place in the field of biomaterials in recent times. They represent a new class of polymeric constituents based on blends of synthetic and natural polymers, designed with the purpose of producing new materials with enhanced properties with respect to the individual components. In this matter, cellulose acetate (CA) which is an abundant natural fiber resource with an excellent tensile strength [2] is widely used in oral pharmaceutical products and is regarded as a nontoxic, nonirritant, and biodegradable material [3]. Among its wide array of applications, cigarette filters, high absorbent diapers, semipermeable membranes for separation processes and fibers, and films for biomedical utilities as well as the textile and the biomedical domain and mats for transdermal drug delivery can be included [4]. In addition, a long term antimicrobial effect for wound healing application was recently reported [5]. As a synthetic polymer, poly(vinyl alcohol) (PVA) is worth mentioning because it is one of the world’s largest volumes synthetic resins produced due to its excellent chemical resistance, physical properties, biocompatibility, and complete biodegradability indeed [6]. PVA is furthermore used in industry due to its high capability of water absorption [7] and its excellent film-forming properties. As a promising biomaterial, diverse researches have been focused on the application of PVA in biomedical and pharmaceutical fields. High mechanical strength, rubber-like elasticity, low-protein adsorption, high water content, and no adhesion to surrounding tissues make PVA gels a potential material for soft contact lenses, soft tissue replacements, articular cartilage, intervertebrate disc nuclei, transcatheter arterial embolization agent, artificial skin, and vocal cord [8–12]. PVA has been used in blends and composites with natural polymers since its hydrophilic and filming character allows for some degree of compatibility with functional natural polymeric materials. The biodegradability and water solubility of PVA ensure its easy degradation and elimination after use [13].
In order to overcome the poor biological performance of synthetic polymers and to enhance the mechanical characteristics of biopolymers, BAPM have been introduced. They should usefully combine the biocompatibility of the biological component with the physical and mechanical properties of the synthetics. The basic philosophy of BAPM is to smooth the interactions between synthetic and living systems creating a two-component material. Such material should behave better macroscopically than a fully synthetic material, with regard to the biological response of the host [1].
BAPM can be cast as films and a variety of potential applications have been targeted including dialysis membranes, wound dressing, artificial skin, cardiovascular devices, nerve guide channels, and implantable devices to release biologically active substances in a controlled manner. A further potential use may be found in orthopedic applications, for instance, bone graft substitutes [14, 15]. Recently, a BAPM composed of bilayer of collagen and PVA has been synthesized and the material exhibits viscoelastic features useful for being used in contact with living organisms [16]. Nonetheless, the use of bilayers within biomedical field is practically nonexistent and there are just few reports in the scientific literature.
For all the aforementioned reasons, bilayers can be therefore included into BAPM category and those systems present different surfaces properties. Despite the plethora of publications on cellulose in general and CA in particular and the broad use of PVA in medical field, the combination of the cited polymers presents a drawback in the research field and is still lacking studies which could contribute to making a comprehensive study of their interaction as bilayers systems. Indeed, according to our best knowledge, it is the first time that the BAPM consisting of CA-PVA is reported and characterized taking into consideration that the material could be an interesting window for use in biomedical field, including but not limiting to reducing fibrous adhesion.
2. Materials and Methods
Cellulose acetate (CA) was purchased from Aldrich Co., USA. Molecular weight (Mw) was 30,000 g mol−1, acetyl content was 39.8 wt%, and degree of substitution (DS) was 2.4. Poly(vinyl alcohol) (PVA, Mw 47,000 g mol−1) with a degree of polymerization of 1,000 and 98% hydrolysis and a 50% water solution of glutaraldehyde (GA) were provided by Sigma Aldrich, The Czech Republic. Polyethylene glycol 400 (PEG) at analytical grade was supplied by Fluka, Germany, whereas lactic acid (LA) (analytical grade) was produced by Lachema, The Czech Republic; hydrochloric acid (H+) (analytical grade) and acetone were supplied by Penta, The Czech Republic. All the reagents were used as they were received.
2.1. Sample Preparation2.1.1. Single Layer
A 10 wt% solution of CA was prepared in acetone at room temperature by the slow addition of the polymer to the solvent under mild magnetic stirring using a Heidolph MR Hei-Standard magnetic stirrer with heating (Heidolph Instruments GmbH, Schwabach, Germany). PEG was added as a plasticizer at 4.5 wt%, and the solution was stirred for 30 more min. The solution then underwent degasification using an ultrasonic cleaning unit (S80 Elmasonic, Elma GmbH, with degasification function, Germany) and 0.5 mL per cm2 was poured on a glass Petri dish and allowed to dry in a no-air circulating oven for 24 h at 35°C [17].
An aqueous solution of PVA at 5 wt% was prepared by dissolving the polymer at 80°C for 6 h under continuous magnetic stirring heating (Heidolph Instruments GmbH, Schwabach, Germany). Once the solution was obtained, GA at 0.25 wt% and hydrochloric acid at 1.2% related to the total amount of polymer were added as cross-linker agent and the solution was heated up to 80°C during 20 min as a crucial step in the cross-linking mechanism. Moreover, LA at 15 wt% related to the total amount of the polymer was used as plasticizer. The solutions were poured (0.5 mL per cm2) and cast on glass Petri dishes and allowed to dry at 35°C for 4 days in a no-air circulating oven. Table 1 summarizes, designs, and describes each sample.
Prepared films.
Number
Sample
Description
1
PVA
A PVA film obtained from a 5 wt% water solution
2
PVA + ADD
A PVA film obtained from a 5 wt% water solution + GA (0.25 wt%) + LA (15 wt%) + HCl (1.2 wt%) related to the total amount of the polymer
3
CA
A CA film obtained from a 10 wt% acetone solution
4
CA + ADD
A CA film obtained from a 10 wt% acetone solution + PEG (4.5 wt%)
5
Bilayer
CA + ADD and on it PVA + ADD
2.1.2. Bilayers (Bioartificial Polymeric Material (BAPM))
A single layer of CA + ADD was obtained and dried, and the PVA + ADD solution was cast on it. The system was allowed to dry under the same conditions as for single layer films.
FITR spectroscopy analysis was carried out on NICOLET 6700 FTIR spectrometer device (Thermo Scientific, United States) equipped with attenuated total reflectance (ATR) accessory utilizing the Zn-Se crystal and software package OMNIC over the range of wavelengths from 4,000 to 600 cm−1 at room temperature under resolution 4 cm−1. Each spectrum represents 64 coadded scans referenced against an empty ATR cell spectrum.
Wettability of the samples was evaluated by contact angle measurement. The sessile drop method was used for this purpose on a Surface Energy Evaluation (SEE) system equipped with a CCD camera (Advex Instruments, The Czech Republic). Deionized water, ethylene glycol, and diiodomethane were used as testing liquids at 25°C and 50% relative humidity. The droplets volume was set to 5 μL for all experiments and a photo was taken immediately after the deposition of every drop. The contact angle value was an average of 10 independent measurements. The substrate surface free energy was evaluated by using the acid-basic model.
2.3. Scanning Electron Microscopy (SEM)
Surface morphology of the films as well as the cross section of the BAPM was investigated by scanning electron microscope Vega II LMU (Tescan, Czech Republic), after coating with a thin layer of gold/palladium by the sputter coater SC 7640 (Quorum Technologies, UK). The microscope was operated under high vacuum at an acceleration on voltage of 5 kV.
2.4. Differential Scanning Calorimetry (DSC)
Calorimetric measurements were carried out in a DSC 1 calorimeter, Mettler Toledo (Greifensee, Zurich, Switzerland), under nitrogen flowing at a rate of 30 mL min−1. The specimens were pressed in sealed aluminum pans. Heating cycle was performed in order to obtain glass transition temperature (Tg) and melting temperature (Tm). The samples were cooled down by nitrogen at an exponentially decreasing rate. The heating of the cycle was performed from 25 to 250°C at a rate of 20°C/min. Tg was determined as the midpoint temperature by standard extrapolation of the linear part of DSC curves using Mettler Toledo Stare software and Tm as the maximum value of the melting peak.
2.5. Gas Permeability
The experimental method to determine the permeability of a polymer is based on the principle that molecules could permeate a polymer film. The gas permeability test was performed by using the pressure difference gas permeation instrument (VAC-V1, Labthink Instrument Co., Jinan, China). A test specimen is mounted in a gas transmission cell to form a sealed barrier between two chambers. The lower-pressure chamber is evacuated at 20 Pa whereas the higher-pressure chamber has a pressure of 0 kPa during 4 hours. A gas is introduced into the evacuated higher-pressure chamber at 106 kPa and permeates into the lower-pressure chamber. Circular specimens with a diameter of 10 cm were cut although the tested area was 38.48 cm2 and the thickness was between 75 and 300 μm. The test was performed at 28°C and the relative humidity was 28%. Nitrogen, oxygen, air, and carbon dioxide were tested. The end of the test is judged by a proportion. If the rates of change of three consecutive data points are all smaller than the present proportion, system automatically terminates the test, calculates the slope of the change, and generates gas transmission rate (GTR) and permeability coefficient (Coef P).
2.6. Water Vapor Permeability (WVP)
The WVP was determined by desiccant method at 25°C and at 70% of relative humidity. The films were firmly fixed and sealed onto an open capsule with a diameter of 5 cm containing silica gel as desiccant. The systems were placed in climatic chamber (Challenge 250 from Angelantoni Industrie, Cimacolle, Italy) and they were weighed in an analytic balance (Denver Instrument SI-64, Göttingen, Germany). The water vapor transmission (WVT) was calculated using (1)WVT=Δmt∗A,where Δm is the mass change (kg), t is the time (s), and A is the membrane area (m2). The value was calculated by linear regression from the points of weight gained and time in the constant rate period. From this data, WVP was obtained by (2)WVP=WVT∗ls∗RH1-RH2,where l is the membrane average thickness (m), s is the saturation pressure (3.159 kPa at 25°C), RH1 is the relative humidity of the conditioned chamber, and RH2 is the relative humidity inside the sample (both expressed as a fraction). Tests were performed in triplicate for single layers and four specimens (two per each side) for BAPM. The thicknesses were calculated as the mean of 5 different measurements across the specimen using a micrometer with the accuracy of 0.01 mm.
2.6.1. Mechanical Testing
Young’s modulus (E), stress at break (σ), and elongation at break (ε) were tested on five specimens per sample using a rectangular test specimen specified in ISO 527-3 with a length of 100 mm, width of 10 mm, and thickness of about 0.200 mm [18]. The experiment was carried out using an Instron-type tensile testing machine (Testometric M350-5CT, Lincoln Close, Rochdale, England) and the rate was 50 mm/min. The test conditions are specified in ISO 291 [19]. The thickness of the samples was measured by a micrometer with the accuracy of 0.01 mm.
3. Results and Discussions3.1. Fourier Transform Infrared (FTIR)
One of the main characteristics of the bilayers systems is that they present different surfaces on each side which implies enormous benefits as a promising material in the biomedical field. Therefore, FTIR spectroscopy can be considered as a pertinent identification criterion which provides information about those differences.
The PVA spectrum has been elucidated in different studies and in the present work the results are in accordance with those reported in literature [16, 20–23] (Figure 1). There is a strong broad absorption band at 3,325 cm−1 which is characteristic for OH group. The bands at 2,947 and 2,914 cm−1 belong to saturated C–H stretching, whereas the band situated at 1,415 cm−1 is related to –CH2– bending [24]. The spectrum does not exhibit bands in the region of 1,700 cm−1, indicating the absence of acetate groups, an effect of the highly hydrolyzed PVA. The small peaks at 1,650 and 1,560 cm−1 can be attributed to conjugated diones or single carbonyls in conjugation with C=C double bonds in solid state [23, 25–27]. The C–O stretching modes and strong dependency of its intensity on crystallinity degree of the solid PVA material were observed at 1,137 cm−1 [28, 29]. Other authors [30, 31], however, have reported this band as a manifestation of C–O–C in ether bridges. The bands at 1,415 and 1,329 cm−1 can be attributed to combination frequencies of CH and OH [32]. There is a strong peak in the region of 1,060–1,030 cm−1 that can be assigned to stretching of C–O in C–O–H group [31] although the band is shifted to 1,070 cm−1 due to interaction with unsaturated bonds [24]. The CH2 rocking band at 928 cm−1 and a peak at 848 cm−1, which are associated with C–O stretching, are evidenced in the spectra as well [28].
FTIR for the prepared films: (a) PVA; (b) PVA + ADD; (c) CA; (d) CA + ADD; (e) BAPM PVA + ADD side; and (f) BAPM CA + ADD side.
The most visible difference between PVA and PVA + ADD is the growth of the intensity of the O–H peaks in the spectrum of the cross-linked material. Initially, it can be considered that the peak undergoes a decrease in the intensity as a manifestation of the presence of acetal bridges which causes a lower amount of hydroxyl groups in the material [23]. Nonetheless, apart from GA, the plasticizing function of LA affects the morphology of the material and the contrary effect appears. The presence of the C=O band at approximately 1,720 cm−1 may indicate that the aldehyde groups of GA did not completely react with O–H groups of the PVA chain or the contribution of remaining acetate groups of the PVA structure. In addition, the C–O stretching at 1,088 cm−1 in pure PVA is replaced by a broader absorption band located between 1,000 and 1,140 cm−1 which can be attributed to the ether (C–O) and the acetal ring (C–O–C) bands formed by the cross-linking reaction of PVA with GA. It can be assumed that GA has acted as a chemical cross-linker among PVA polymer chains [33].
The spectrum of CA shows a weak and broad band at 3,562 cm−1 which corresponds to the stretching of unsubstituted O–H group [34] followed by the presence of the stretching vibration mode of –CH– located at 2,956 and 2,891 cm−1 [35–37]. There is a strong adsorption band at 1,750 cm−1 related to the symmetric stretching C=O of the acetyl group and the medium intensity band at 1,374 cm−1, connected to the angular distortion of the C–H in the ester methyl group typical of partially acetylated cellulose [34, 38]. The bands placed at 1,239 and 1,051 cm−1 correspond to the asymmetric vibration of C–O–C for ether bridge and pyranose ring, respectively [35]. The presence of PEG in the spectrum is manifested only as an outstanding increase of the signal for OH groups and CH stretching at 3,485, 2,947, and 2,864 cm−1.
The spectrum for each side of the BAPM evidences a high degree of correspondence between the single layers which can be considered as indicator that the surfaces keep their morphology after the formation of the bilayers.
3.2. Contact Angle (Surface Energy)
The contact angle values of deionized water (θw), ethylene glycol (θe), and diiodomethane (θd) and the corresponding evaluated surface energies are shown in Table 2. The Lifshitz-Van der Waals/acid-base (LW/AB) theory was employed to obtain the total surface energy ϒtot and its components: dispersion ϒLW and polar ϒAB. LW refers to the total dispersive Lifshitz-Van der Waals interactions and AB is related to the Lewis acid-base (electron acceptor/electron donor) interactions, where ϒ+ and ϒ- are the acidic and basic parts. The method was used for evaluating both sides in each film indicated in Table 2 as air and substrate side for single components and air interface and substrate side for BAPM.
Contact angle and surface energy values for the prepared materials.
Sample
Contact angle (°)
Surface energy (mJ/m2)
θw
θe
θd
γtot
γLW
γAB
γ+
γ-
CA (air side)
63.75 ± 2.14
38.14 ± 4.78
39.27 ± 4.47
42.14
39.97
2.17
0.06
18.48
CA (substrate side)
64.12 ± 2.89
38.38 ± 3.92
43.62 ± 4.48
41.44
37.74
3.69
0.19
17.96
CA + ADD (air side)
42.03 ± 4.47
28.78 ± 3.98
30.75 ± 2.39
50.53
43.91
6.62
0.26
47.81
CA + ADD (substrate side)
39.85 ± 7.04
32.18 ± 2.54
30.83 ± 1.45
54.95
43.88
11.07
0.56
54.30
PVA (air side)
54.79 ± 11.66
30.19 ± 3.49
39.36 ± 4.63
43.13
39.93
3.20
0.09
27.20
PVA (substrate side)
62.81 ± 7.19
29.14 ± 1.84
38.19 ± 3.12
46.10
40.51
5.59
0.51
15.21
PVA + ADD (air side)
75.55 ± 5.58
42.49 ± 5.28
44.15 ± 3.59
41.48
37.46
4.01
0.64
6.58
PVA + ADD (substrate side)
74.49 ± 2.52
40.77 ± 3.32
45.40 ± 4.48
41.54
36.79
4.75
0.82
6.87
BAPM: PVA + ADD (air side)
49.93 ± 5.25
28.91 ± 2.88
38.47 ± 5.10
41.77
40.37
1.40
0.01
34.27
BAPM: PVA + ADD (interface)
40.75 ± 4.27
24.31 ± 5.90
35.54 ± 5.45
43.70
41.78
1.92
0.02
46.69
BAPM: CA + ADD (interface)
49.21 ± 3.37
32.91 ± 2.41
34.79 ± 5.42
45.59
42.13
3.47
0.08
38.39
BAPM: CA + ADD (substrate side)
46.04 ± 3.88
26.98 ± 3.44
38.81 ± 2.47
41.03
40.20
0.82
0.00
39.49
The surface energy of CA films shows that the electron acceptor components (ϒ+ or Lewis acid) are very small whereas the electron donor components (ϒ- or Lewis base) are large and represent the main interactions with the electron acceptor ϒ+ components of the contacting liquids [39]. The number of acetyl groups increases the formed hydrogen bonding generating a wettable material which is supported by the values of contact angle as well as the total surface energy ϒtot. As a plasticizer, PEG interrupts the sequence of hydrogen bonding and the intermolecular forces are affected with the relevant rise in the basic character and ϒtot. It is not surprising that CA + ADD material exhibits the lowest contact angle values and the highest basic components or, in other words, the most wettable film [40].
PVA is a hydrophilic polymer and its hydrophilicity is caused by the hydrogen bonding occurring in the surface between free OH groups and the water molecules showing a basic nature (ϒ+<ϒ-). This nature is reduced substantially in PVA + ADD because the cross-linker agent diminishes the amount of available hydroxyl groups in the polymer matrix generating a rise of the contact angle values for the three tested liquids [41]. Moreover, the hydrophilicity is affected by the crystallinity as well, and DSC results (see below) indicated a higher value for PVA + ADD than just for PVA. Nonetheless, a slight drop in ϒtot indicates that the wettability in this material is lower since the proportion of hydrogen bonding was reduced and because the wettability of liquid droplets on solid surfaces is governed mainly by both the chemical composition and the geometrical microstructure [42].
The measured values are slightly different depending on the surface that the polymer is in contact with (air, substrate, or interface). In the case of PVA, the variation can be attributed to the probability of the polymer chains mobility toward neighboring molecules. In the air side, the hydrophilic groups migrate to the inner bulk part due to the hydrophobic character of the air. On the contrary, in the substrate side, the polar groups migrate from the bulk to the substrate as the glass is hydrophilic material. As a result, higher values for the contact angle in the air side can be expected. However, a competition between glass (substrate) and surrounded molecules (water) is presented and PVA exhibits higher values for the substrate side. These effects were not detected for the other films and the values do not present notable differences because the repulsion to hydrophobic surface is attenuated by the presence of additives.
By analyzing ϒtot in the BAPM, one piece of data deserves a deeper sight. The film CA + ADD (substrate side) is considerably higher in the BAPM than in the individual component whereas the other components exhibit surprising closer values. A plausible explanation for these unexpected results is correlated to the surface morphology. SEM evidenced those differences (see below). Despite the slight differences, it is possible to claim that, in the BAPM, the surfaces of the individual components retain their surface characteristics which are an important indicative of their potential use as a material in medical field.
3.3. Scanning Electron Microscopy (SEM)
The SEM images provide valuable information which can confirm the results found through surface energy analysis. No differences were seen in PVA and PVA + ADD either as a single component or as a part of the BAPM in the bilayer structures. Nonetheless, a dissimilar analysis can be done for the changes in CA films. As was explained, during drying process, the polar groups tend to migrate in a different manner according to the interface which the material is in contact with. As a hydrophobic substance, there is important repulsion of the CA molecules in air generating a roughness surface whereas the substrate (glass) side looks smoother (Figures 2(a) and 2(b)).
SEM images for the surface of the prepared materials. (a) CA air side; (b) CA substrate side; (c) CA + ADD air side; (d) CA + ADD substrate side; (e) bilayer: CA + ADD interface; (f) bilayer: CA + ADD substrate side; and (g) cross section of the BAPM (bilayer structure).
However, the surface smoothness decreases due to the presence of PEG as can be seen in Figures 2(a) and 2(c) as well as in Figures 2(b) and 2(d). The porous formation causes these differences. The PEG boosts the formation of pores in the structure which indeed can be correlated with the results for gas permeability where CA + ADD exhibit higher values than CA (shown below). CA molecules on the other hand are immobilized in a glassy state as a consequence of the effect of acetone during the casting and the crystallinity of this film is considerably lower than the crystallinity of CA + ADD (see DSC results) [43, 44]. By comparing Figures 2(c) and 2(d), minor differences in the roughness are revealed. They are caused by the interaction of the material with the hydrophilic and hydrophobic character of the interface. Nonetheless, the analysis of Figures 2(c) and 2(e) as well as Figures 2(d) and 2(f) indicates that the most notable difference is the appearance of a needle-shaped structure on the interfaces of the bilayers. The surfaces of the interfaces look smoother than the single component in contact with the same media, probably due to the interaction of the plasticizer with water and PVA molecules. Moreover, the aqueous solution of PVA induces the formation of crystals on the surface, and it causes a reduction on the pores formation (the surface of the material in Figure 2(e) appears smoother than in Figure 2(f)).
3.4. Differential Scanning Calorimetry (DSC)
A representative DSC thermogram of the second scan for CA films is shown in Figure 3(a). The melting temperature (Tm) is centered at 216°C whereas the glass transition temperature (Tg) is located at 177°C, transitions which have been reported somewhere else [45–47]. Nevertheless, CA with different degrees of acetylation shows Tg values between 190 and 220°C [48, 49] and a higher DS causes a lower possibility of forming hydrogen bonding and consequently a lower Tg is manifested [50]. In addition, detecting those transitions is difficult since the heat capacity change of polymers at Tg is related to the increase in molecular mobility which is not very large in rigid cellulose acetate [51]. The proximity of Tg and Tm interferes with the crystallization process that occurs between them. CA revealed that only the mixed esters, in which the bulkier acyl group is in the range of DS 0.3–1.0, have a Δ(Tm-Tg) value in excess of 40°C [52]. The thermal behavior of CA is also influenced by the regiochemistry and the method of preparation [53]. The addition of low molecular weight plasticizer results in the decrease of the intermolecular forces between the polymer chains due to shielding of functional (polar) groups along the polymer chains. That leads to an increase in free volume and chain mobility. As a result, Tg of CA + ADD should be lower than the value for CA. Furthermore, it has been reported that Tg for CA plasticized with PEG is reduced depending on the concentration of the plasticizer [54]. However, it was not detected as was explained previously [55] and because, in a conventional DSC, a reversing event like the glass transition may be hidden by a no reversing event, such as enthalpic relaxation [50].
DSC thermograms for (a) CA systems and (b) PVA systems.
In Figure 3(b), the thermal transitions for the second scan of PVA are shown. Two main events appeared: Tm which is located at 221°C and Tg at 73°C. Although several sources report that Tg can be found at 85°C [56–62], it is well known that the presence of water could act as a plasticizer causing a reduction in this value [63]. The effects caused by ADD were analyzed in a previous study [60]. Nonetheless, it can be mentioned that PVA + ADD exhibits a lower Tm than pure PVA. The addition of the ADD shows that plasticizing effect of LA predominated in the system because it has the highest concentration in the system (15% in comparison with 0.25% of GA) and because LA is partially grafted on hydroxyl groups of PVA which, generally, causes disturbing or attenuation of hydrogen bonding between parallel PVA chains as well as disturbing of regularity of chain stacking by the presence of randomly distributed lactide groups pendant to polymer chains [19].
The first scan for BAPM is exhibited in Figure 3(b). As can be observed, CA + ADD transitions are hidden by the PVA + ADD one. Nonetheless, it is worth mentioning that both individual polymers do not interact beyond the interface because the polymers interactions are evidenced by this technique as a unique Tg. If any sample of a binary polymer system exhibits a single glass transition between the Tg values of both components and a composition-dependent shift in Tg of the blend is clearly observed, then the system can be regarded as a highly miscible one. In the case where one component is crystalline, observation of a melting point depression of this polymer also supports the miscibility of the polymer pair [64]. However, it is not the present case, which confirms that CA + ADD and PVA + ADD keep their structural, functional, and morphological integrity in the BAPM.
3.5. Gas Permeability
The permeability coefficient is the volume of gas which, under steady conditions, crosses unit area and unit thickness of the sample in unit time under unit pressure difference and at constant temperature.
Table 3 shows the permeability coefficient in Barrer (10−10 cm3 (STP) cm/cm2 s cm Hg) for the tested samples. Gas transmission process includes three phases. In the first one, the molecules in the room with higher pressure are condensed on the surface of the film. Next, the gas is dissolved into the film and finally it leaves the polymer and experiments desorb.
Permeability coefficient in Barrer for the studied material.
Film
Air
Nitrogen (N2)
Oxygen (O2)
Carbon dioxide (CO2)
CA
0.1142
0.3201
0.5321
0.5910
CA + ADD
0.2205
0.5360
0.5619
0.5946
PVA
0.0067
0.0073
0.0106
0.0852
PVA + ADD
0.0033
0.0040
0.0090
0.0528
Bilayer (CA + ADD down∗)
0.4061
0.4445
0.7709
4.0960
Bilayer (PVA + ADD down∗)
0.3947
0.4070
0.7196
2.3140
∗In contact with the lower chamber or chamber with the lower pressure.
The four gases permeate in a greater extent (CA + ADD) than just CA and the reason can be found in the higher porosity that exhibits the CA + ADD as a consequence of the structural changes that are caused by PEG which is a hydrophilic plasticizer and a pore former [65]. Manifestations of those changes were corroborated by SEM (see above) in which CA + ADD film seems to exhibit a more roughness surface in comparison with CA. In addition to the structural modifications, PEG reduces slightly the crystallinity of the natural polymer (see DSC results). Therefore, the permeability is increased because the crystalline zones act as excluded volumes for the sorption process and are impermeable barriers for the diffusion. Two more effects on the gas diffusion are owing to the crystalline regions. The increase in the effective path length of diffusion and the reduction of the mobility in the amorphous phase (because chain ends are trapped in the neighboring crystalline lamellae) cause a higher activation energy of diffusion [66].
PVA is a good gas barrier polymer and this behavior is a consequence of the large inter- and intramolecular cohesive energy that results from the highly polar alcohol (–OH) functionality with the low polarity gases [67] combined with the presence of crystalline regions in the matrix. It is well worth bringing the attention to the fact that PVA + ADD is even less permeable than PVA. By reducing those interactions in presence of ADD, lesser amounts of available hydroxyl groups are present in the matrix; therefore a reduction in the interaction points is achieved and decreases in permeability are presented because the polymer cohesions are weakened. Moreover, the higher crystallinity of PVA + ADD in comparison with PVA (evidenced in DSC) reduces the gas solubility and a more tortuous path for the diffusing species occurs [68].
Air displays the lowest permeation to the films. On the contrary, CO2 flaunts the highest permeability for every single material because of its small kinetic diameter, its high condensability, and more interaction of this gas with polar groups in polymer compared to O2 and N2 [69–71]; meanwhile oxygen gas values were greater than those of nitrogen, regardless of types of film. This is mainly due to the difference in the size of the gases.
A different issue appears for the bilayer. As a first step, the bilayer system consists of two monolayers that exhibit different permeabilities and thicknesses. However, the used apparatus considers the material as a unique film and for that reason the permeability coefficient is calculated using the thickness of the bilayer, provoking a variation in the final result. The theories developed in order to understand how a bilayer is permeated are still in constant evolution and there is no end point in this topic. However, the steady-state barrier properties of multilayer films are a valuable tool which explains partially this phenomenon by treating the individual layers as resistances in series as is shown in (3)1P′=LtPt=L1P1+L2P2+⋯+LnPn,where Pt, Lt, and P are permeability, thickness, and permeance of the composite structure, and P1,P2,…,Pn and L1,L2,…,Ln are the permeabilities and thicknesses of the individual layers [72]. A second consideration has to be taken into account. When the pressure on the upstream side of the membrane is increased, two opposite effects may occur: a hydrostatic pressure increase leads to an increase of the polymer density, via polymer compaction, thereby reducing the free volume inside the polymer; the pressure increase corresponds to an increase of the penetrant concentration in the membrane. These diffusing molecules plasticize the macromolecular chains. The first one of these two mechanisms tends to retard the diffusion process by reducing the segmental motions whereas the second enhances it [66]. Furthermore, the diffusion process has been explained whether by obeying or not the Fick diffusion law. In the first case, the mobility of the penetrant is slower than the polymer chain mobility and the rate of penetrant mass uptake is proportional to the square root of time. In the second case, the rate of mass uptake is directly proportional to time. Penetrant diffusion rate is faster than the chain mobility, thereby leading to swelling of the polymer. Anomalous sorption occurs during comparable mobility of both the penetrant and the polymer chain. Due to the complex nature of the sorption kinetics, this behavior is termed either anomalous or non-Fickian [73]. By combining all the aforementioned reasons, the permeation in the bilayers is unusually high in comparison with the monolayers.
3.6. Water Permeability
Table 4 presents the water vapor transmission (WVT) and water vapor permeability (WVP) results for the prepared materials. As can be noticed, PVA presents the lowest values of these two parameters which might be caused by the hydrophilic behavior of the synthetic polymer. In fact, it absorbs water vapor and provokes a decrease on the WVT of the films by comparing with the other films [74]. On the other hand, PVA + ADD film shows higher values than just PVA. It is well known that increasing the hydrophilic nature of a polymer membrane induces water vapor tendency and as a result increases water vapor permeation [75, 76]. Into the bargain, it might be thought that GA can decrease WVT because the water vapor transfer process across the films depends on the degree of cross-linking and PVA chains covalently cross-linked to each other block the pathway of water and restrict the water vapor penetration across the films [74]. Nonetheless, PVA + ADD is less hydrophilic than PVA (see contact angle results) although it is more porous (confirmed by SEM) and the plasticizing effect caused by LA generates a rise in the free volume. The combination of these factors produces a material with a higher WVT. By contrast, CA and CA + ADD films are the least permeable to water. CA is the second most hydrophobic material in this study which can be interpreted as a signal of its low WVT character. Notwithstanding, PEG as a hydrophilic additive changes the membrane morphology forming micropores in the film structures due to the microphase separation process. As a result, the pure water permeation is increased [77, 78] 2.3 times approximately. The water absorption capacity is boosted by an improvement in the surface free energy [75] and these results are supported by the contact angle results and vice versa. Finally, although it can be expected that the material with the lowest WVT dominates the permeability in the BAPM, it has to be mentioned that the thicknesses of the layers which conform the BAPM are not the same; therefore the obtained values are different and they are located in between the WVP of CA + ADD and PVA + ADD.
Water vapor transmission and water vapor permeability for the prepared materials.
Sample
WVT (kg/s·m2)
WVP (kg·m/s·m2·kPa)
CA
9.6694 × 10−07 ± 3.7695 × 10−08
9.5310 × 10−11 ± 6.1328 × 10−12
CA + ADD
2.2465 × 10−06 ± 2.1142 × 10−07
1.9991 × 10−10 ± 5.9032 × 10−11
PVA
4.9046 × 10−09 ± 8.4208 × 10−10
3.3116 × 10−13 ± 1.1558 × 10−13
PVA + ADD
4.8077 × 10−08 ± 4.2441 × 10−09
4.7179 × 10−12 ± 7.6930 × 10−13
Bilayer CA side waxed
7.5240 × 10−08 ± 1.1491 × 10−08
2.6514 × 10−11 ± 5.4760 × 10−12
Bilayer PVA side waxed
4.2572 × 10−07 ± 2.8003 × 10−08
8.0962 × 10−11 ± 1.0785 × 10−11
3.7. Mechanical Properties
Young’s modulus (E), stress at break (σ), and elongation at break (ε) were chosen for evaluating the prepared material as well as the influence of the ADD in the single components. Table 5 shows the obtained results. CA is a brittle polymer which exhibits notably high Young’s modulus and a small elongation at break. No yield point was manifested during the measurements, confirming the brittleness of the material [50, 64]. Plasticization, on the contrary, is assumed to increase the flexibility of chains and lead to a decrease in stiffness [79]. The presence of PEG produces polymer-plasticizer interactions among the macromolecules to the detriment of polymer-polymer interactions and it causes a decrease of the hardness as well as Young’s modulus whereas the elongation at break was increased. In case of PVA, the stress-strain curve is affected by molecular weight, crystallinity, type, and proportion of additives. The elongation at break for PVA + ADD in comparison with PVA was significantly higher as a consequence of the plasticizing effect caused by LA [80]. Furthermore, the low elongation at break for the bilayer is a result of the poorer mechanical features of CA + ADD. As a remarkable point, in the BAPM systems, during the test CA + ADD failed always at first, and it demonstrates that in the BAPM the mechanical properties are governed by the natural polymer as the weakest material in the bilayer.
Mechanical properties for the prepared material.
Sample
Young’s modulus (MPa)
Tensile strength (MPa)
Elongation at break (%)
Thickness (mm)
CA
1,832 ± 71
38 ± 4
7 ± 3
0.253 ± 0.01
CA + ADD
660 ± 87
13 ± 2
10 ± 2
0.311 ± 0.03
PVA
1,174 ± 189
16 ± 6
69 ± 15
0.128 ± 0.04
PVA + ADD
49 ± 6
18 ± 3
217 ± 25
0.094 ± 0.01
Bilayer
590 ± 53
11 ± 3
13 ± 4
0.340 ± 0.02
4. Conclusions
The primary aim of this research was to obtain and characterize a new bioartificial polymeric material prepared from CA and PVA. Casting method, as a simple polymer production technique, was used for that purpose and a bilayer with two separated and well-differentiated surfaces was successfully obtained. The characterization techniques have provided relevant and sufficient data which allows claiming that the achieved material fulfills one of the basic requirements for BAPM: to enhance the mechanical characteristics of biopolymers. FTIR, contact angle, and SEM have indicated that the BAPM exhibits two independent surfaces which are closely related to the polymers that compose the bilayer. On the other hand, DSC did not indicate any evidence of the formation of a blend or an interpenetrating structure in the interface by the exhibition of just one Tg. A substantial reduction in the brittleness of the natural polymer was achieved by adding PEG meanwhile Young’s modulus was three times smaller and a slight but relevant rise in elongation was achieved. PVA was modified using LA, GA, and H+, thus accomplishing a material with a stunning reduction in Young’s modulus and a significant improvement in elongation at break. The mechanical properties of BAPM are closer to CA + ADD than to PVA + ADD; therefore, it could be argued that the natural polymer dominates the behavior of the bioartificial polymeric material.
The improvement in the permeability is crucial considering the potential use of the material in the medical field, since gases or nutrients can penetrate in a higher proportion into the film and, as a consequence, into the possible biological scaffold including exudation as a relevant part of the healing and regeneration. For all of the given reasons, the BAPM can be considered as a promising candidate that should undergo further analysis in order to determine its applicability in medicine field.
Competing Interests
The authors declare that they have no competing interests.
Acknowledgments
This work was supported by the Ministry of Education, Youth and Sports of the Czech Republic-Program NPU I (LO1504).
CasconeM. G.Dynamic-mechanical properties of bioartificial polymeric materials1997431556910.1002/(SICI)1097-0126(199705)43:1<55::AID-PI762>3.0.CO;2-#2-s2.0-0031145220WangH.-M.ChouY.-T.WuC.-S.YehJ.-T.Polyester/cellulose acetate composites: preparation, characterization and biocompatible20121262E242E25110.1002/app.369652-s2.0-84864655428OhnoT.YoshizawaS.MiyashitaY.NishioY.Interaction and scale of mixing in cellulose acetate/poly(N-vinyl pyrrolidone-co-vinyl acetate) blends200512328129110.1007/s10570-004-5836-72-s2.0-26644468601KonwarhR.KarakN.MisraM.Electrospun cellulose acetate nanofibers: the present status and gamut of biotechnological applications201331442143710.1016/j.biotechadv.2013.01.0022-s2.0-84874971757LiuX.LinT.GaoY.XuZ.HuangC.YaoG.JiangL.TangY.WangX.Antimicrobial electrospun nanofibers of cellulose acetate and polyester urethane composite for wound dressing201210061556156510.1002/jbm.b.327242-s2.0-84863723223DingB.KimH.-Y.LeeS.-C.ShaoC.-L.LeeD.-R.ParkS.-J.KwagG.-B.ChoiK.-J.Preparation and characterization of a nanoscale poly(vinyl alcohol) fiber aggregate produced by an electrospinning method200240131261126810.1002/polb.101912-s2.0-0036644203KaczmarekH.PodgórskiA.The effect of UV-irradiation on poly(vinyl alcohol) composites with montmorillonite20071912-320921510.1016/j.jphotochem.2007.04.0252-s2.0-34548236390AlexyP.BakošD.HanzelováS.KukolíkováL.KupecJ.CharvátováK.ChielliniE.CinelliP.Poly(vinyl alcohol)-collagen hydrolysate thermoplastic blends: I. Experimental design optimisation and biodegradation behaviour200322780180910.1016/S0142-9418(03)00016-32-s2.0-0043125550ChanL. W.HaoJ. S.HengP. W. S.Evaluation of permeability and mechanical properties of composite polyvinyl alcohol films199947101412141610.1248/cpb.47.14122-s2.0-0344069761El-ZaherN. A.OsirisW. G.Thermal and structural properties of poly(vinyl alcohol) doped with hydroxypropyl cellulose20059651914192310.1002/app.216282-s2.0-19944386641JiangY.SchädlichA.AmadoE.WeisC.OdermattE.MäderK.KresslerJ.In-vivo studies on intraperitoneally administrated poly(vinyl alcohol)201093127528410.1002/jbm.b.315852-s2.0-77949516665ZhouW. Y.GuoB.LiuM.LiaoR.RabieA. B. M.JiaD.Poly(vinyl alcohol)/Halloysite nanotubes bionanocomposite films: properties and in vitro osteoblasts and fibroblasts response20109341574158710.1002/jbm.a.326562-s2.0-77951572369ParkJ.-S.ParkJ.-W.RuckensteinE.A dynamic mechanical and thermal analysis of unplasticized and plasticized poly(vinyl alcohol)/methylcellulose blends200180101825183410.1002/app.12782-s2.0-0035816040AhmadS. I.HasanN.AbidC. K. V. Z.MazumdarN.Preparation and characterization of films based on crosslinked blends of gum acacia, polyvinylalcohol, and polyvinylpyrrolidone-iodine complex2008109277578110.1002/app.281402-s2.0-47949085828ScotchfordC. A.CasconeM. G.DownesS.GiustiP.Osteoblast responses to collagen-PVA bioartificial polymers in vitro: the effects of cross-linking method and collagen content1998191–311110.1016/s0142-9612(97)00236-62-s2.0-0031813186BernalA.BalkovaR.KuritkaI.SahaP.Preparation and characterisation of a new double-sided bio-artificial material prepared by casting of poly(vinyl alcohol) on collagen201370243145310.1007/s00289-012-0802-22-s2.0-84878502616YuanJ.ShangP. P.WuS. H.Effects of polyethylene glycol on morphology, thermomechanical properties, and water vapor permeability of cellulose acetate-free films2001251062742-s2.0-0347572406ISOPlastics—determination of tensile properties—part 3: test conditions for films and sheets1995527-3:1995ISOPlastics —standard atmospheres for conditioning and testing1997291:1997BernalA.KuritkaI.KasparkovaV.SahaP.The effect of microwave irradiation on poly(vinyl alcohol) dissolved in ethylene glycol2013128117518010.1002/app.381332-s2.0-84872313617FinchC.1992Chichester, UKJohn Wiley & SonsHollandB. J.HayJ. N.The thermal degradation of poly(vinyl alcohol)200142166775678310.1016/S0032-3861(01)00166-52-s2.0-0343338270MansurH. S.SadahiraC. M.SouzaA. N.MansurA. A. P.FTIR spectroscopy characterization of poly (vinyl alcohol) hydrogel with different hydrolysis degree and chemically crosslinked with glutaraldehyde200828453954810.1016/j.msec.2007.10.0882-s2.0-40949157499LambertJ.ShurvellH.LighnerD.GrahamR.2001New York, NY, USAPrentice HallDabrowskiJ.TencerM.Rotational Isomerism in β-Diketone cis and trans Enol Ethers. An IR and PMR Study197649498198610.1246/bcsj.49.981GrenE. Y.GrinvaldeA. K.VanagG. Y.Infrared spectra and enolization of simple 1, 3-diketones19706214615010.1007/BF006043392-s2.0-34250480439TayyariS. F.Zahedi-TabriziM.LalehS.Moosavi-TekyehZ.RahemiH.WangY. A.Structure and vibrational assignment of 3,4-diacetyl-2,5-hexanedione. A density functional theoretical study20078271–317618710.1016/j.molstruc.2006.05.0282-s2.0-33846471063BhatN. V.NateM. M.KurupM. B.BamboleV. A.SabharwalS.Effect of γ-radiation on the structure and morphology of polyvinyl alcohol films20052373-458559210.1016/j.nimb.2005.04.0582-s2.0-34249305405WongS.-S.AltinkayaS. A.MallapragadaS. K.Crystallization of poly(vinyl alcohol) during solvent removal: infrared characterization and mathematical modeling200745893093510.1002/polb.211012-s2.0-34247338077AlekseevaN. V.EvtushenkoA. M.ChikhachevaI. P.ZubovV. P.KubrakovaI. V.Effect of microwave irradiation on the structuring of polyvinyl alcohol2005417017210.1070/MC2005v015n04ABEH0021472-s2.0-22244467058PetrovaN. V.EvtushenkoA. M.ChikhachevaI. P.ZubovV. P.KubrakovaI. V.Effect of microwave irradiation on the cross-linking of polyvinyl alcohol20057871158116110.1007/s11167-005-0470-12-s2.0-26644440172HemanthaG. N.LakshmanaJ.GopalN.NarasimhuluK.ChakradharR.Varada RajuluA.Spectroscopic investigations of Mn2+ ions doped polyvinylalcohol films200445165407541510.1016/j.polymer.2004.05.0682-s2.0-4143147376AndradeG.Barbosa-StancioliE. F.Piscitelli MansurA. A.VasconcelosW. L.MansurH. S.Design of novel hybrid organic-inorganic nanostructured biomaterials for immunoassay applications20061422123410.1088/1748-6041/1/4/0082-s2.0-33846865601AluigiA.VineisC.CeriaA.ToninC.Composite biomaterials from fibre wastes: Characterization of wool-cellulose acetate blends200839112613210.1016/j.compositesa.2007.08.0222-s2.0-37149014129IlharcoL. M.Brito De BarrosR.Aggregation of pseudoisocyanine iodide in cellulose acetate films: structural characterization by FTIR200016249331933710.1021/la000579e2-s2.0-0342538754IlharcoL. M.GarciaA. R.Lopes Da SilvaJ.Vieira FerreiraL. F.Infrared approach to the study of adsorption on cellulose: influence of cellulose crystallinity on the adsorption of benzophenone199713154126413210.1021/la962138u2-s2.0-0031186570KondoT.SawatariC.A Fourier transform infra-red spectroscopic analysis of the character of hydrogen bonds in amorphous cellulose199637339339910.1016/0032-3861(96)82908-92-s2.0-0000554919ZhouW.HeJ.CuiS.GaoW.Studies of electrospun cellulose acetate nanofibrous membranes20115515510.2174/1874088x011050100512-s2.0-79959927239ErbilH. Y.Calculation of spreading pressure of water on cellulosic films from contact angle data19972143323452-s2.0-0031283981GuezguezI.MrabetB.FerjaniE.XPS and contact angle characterization of surface modified cellulose acetate membranes by mixtures of PMHS/PDMS201331320821110.1016/j.desal.2012.11.0182-s2.0-84873047144BahramiB.KordestaniS.MirzadehH.MansooriP.Blending of PVA and chitosan improves bulk and surface hydrophilicity of blended films2003122139146WuS.QinX.LiM.The structure and properties of cellulose acetate materials: a comparative study on electrospun membranes and casted films2014441859810.1177/15280837134774432-s2.0-84904741394LiuL.KhangG.RheeJ. M.LeeH. B.Preparation and characterization of cellulose acetate membrane for monolithic osmotic tablet1999752892962-s2.0-0033407336MuhammedA.HashashE.MekewiGuirguisRamadanHassanienPolyvinyl alcohol-cellulose acetate composite reverses osmosis membranes: I. Synthesis and characterization20123, article 13110.4172/2157-7587.1000131FilhoG. R.da SilvaR. C.da Silva MeirelesC.de AssunçãoR. M. N.OtaguroH.Water flux through blends from waste materials: cellulose acetate (from sugar cane bagasse) with polystyrene (from plastic cups)200596251652210.1002/app.214742-s2.0-15944405368Rodrigues FilhoG.ToledoL. C.CerqueiraD. A.De AssunçãoR. M. N.Da Silva MeirelesC.OtaguroH.RogeroS. O.LugãoA. B.Water flux, DSC, and cytotoxicity characterization of membranes of cellulose acetate produced from sugar cane bagasse, using PEG 6002007591738110.1007/s00289-007-0744-22-s2.0-34347217026NakaiY.YoshimizuH.TsujitaY.Enhanced gas permeability of cellulose acetate membranes under microwave irradiation20052561-2727710.1016/j.memsci.2005.02.0082-s2.0-19444363692Chia-WenC.2010Vancouver, CanadaThe University of British ColumbiaAokiD.TeramotoY.NishioY.Cellulose acetate/poly(methyl methacrylate) interpenetrating networks: synthesis and estimation of thermal and mechanical properties20111861441145410.1007/s10570-011-9580-52-s2.0-80855132114CaoY.WuJ.MengT.ZhangJ.HeJ.LiH.ZhangY.Acetone-soluble cellulose acetates prepared by one-step homogeneous acetylation of cornhusk cellulose in an ionic liquid 1-allyl-3-methylimidazolium chloride (AmimCl)200769466567210.1016/j.carbpol.2007.02.0012-s2.0-34249056625SzámelG.KlébertS.SajóI.PukánszkyB.Thermal analysis of cellulose acetate modified with caprolactone200891371572210.1007/s10973-007-8684-52-s2.0-45449119653GlasserW. G.SamaranayakeG.DumayM.DavéV.Novel cellulose derivatives. III. Thermal analysis of mixed esters with butyric and hexanoic acid199533142045205410.1002/polb.1995.090331406IwataT.FukushimaA.OkamuraK.AzumaJ.-I.DSC study on regioselectively substituted cellulose heteroesters19976581511151510.1002/(SICI)1097-4628(19970822)65:8<1511::AID-APP8>3.0.CO;2-J2-s2.0-0031199647WangF.-J.YangY.-Y.ZhangX.-Z.ZhuX.ChungT.-S.MoochhalaS.Cellulose acetate membranes for transdermal delivery of scopolamine base2002201-29310010.1016/S0928-4931(02)00018-82-s2.0-0037205330ZepnikS.KabasciS.KopitzkyR.RaduschH.-J.WodkeT.Extensional flow properties of externally plasticized cellulose acetate: influence of plasticizer content20135387388910.3390/polym50308732-s2.0-84885110524BorogluM. S.CavusS.BozaI.AtaA.Synthesis and characterization of poly(vinyl alcohol) proton exchange membranes modified with 4,4-diaminodiphenylether-2,2-disulfonic acid20115547047810.3144/expresspolymlett.2011.452-s2.0-79952930692PengZ.KongL. X.A thermal degradation mechanism of polyvinyl alcohol/silica nanocomposites20079261061107110.1016/j.polymdegradstab.2007.02.0122-s2.0-34248378310GuirguisO.MoselheyM.Thermal and structural studies of poly(vinyl alcohol) and hydroxypropyl cellulose blends201241576710.4236/ns.2012.41009SudhamaniS. R.PrasadM. S.UdayaK.DSC and FTIR studies on Gellan and polyvinyl alcohol (PVA) blend films200317324525010.1016/s0268-005x(02)00057-72-s2.0-0037612003BernalA.KuritkaI.SahaP.Preparation and characterization of poly(vinyl alcohol)-poly(vinyl pyrrolidone) blend: a biomaterial with latent medical applications201312753560356810.1002/app.377232-s2.0-84870543132BhajantriR. F.RavindracharyV.HarishaA.CrastaV.NayakS. P.PoojaryB.Microstructural studies on BaCl2 doped poly(vinyl alcohol)200647103591359810.1016/j.polymer.2006.03.0542-s2.0-33646128950LiangS.YangJ.ZhangX.BaiY.The thermal-electrical properties of polyvinyl alcohol/AgNO3 films2011122281381810.1002/app.340602-s2.0-79960102613SartiB.ScandolaM.Viscoelastic and thermal properties of collagen/poly(vinyl alcohol) blends1995161078579210.1016/0142-9612(95)99641-X2-s2.0-0029329235MiyashitaY.SuzukiT.NishioY.Miscibility of cellulose acetate with vinyl polymers200293-421522310.1023/A:10211448278452-s2.0-0036765151MohammadiT.SaljoughiE.Effect of production conditions on morphology and permeability of asymmetric cellulose acetate membranes20092431–31710.1016/j.desal.2008.04.0102-s2.0-65549142768KlopfferM. H.FlaconnècheB.Transport properties of gases in polymers: bibliographic review200156322324410.2516/ogst:20010212-s2.0-1642575426LabuschagneP. W.GermishuizenW. A.VerrynS. M. C.MoolmanF. S.Improved oxygen barrier performance of poly(vinyl alcohol) films through hydrogen bond complex with poly(methyl vinyl ether-co-maleic acid)20084472146215210.1016/j.eurpolymj.2008.04.0152-s2.0-47249096566GrunlanJ. C.GrigorianA.HamiltonC. B.MehrabiA. R.Effect of clay concentration on the oxygen permeability and optical properties of a modified poly(vinyl alcohol)20049331102110910.1002/app.205642-s2.0-3042604526HoudeA. Y.KrishnakumarB.CharatiS. G.SternS. A.Permeability of dense (homogeneous) cellulose acetate membranes to methane, carbon dioxide, and their mixtures at elevated pressures199662132181219210.1002/(SICI)1097-4628(19961226)62:13<2181::AID-APP1>3.0.CO;2-F2-s2.0-0030382052SemsarzadehM. A.GhaleiB.Preparation, Characterization and gas permeation properties of polyurethane-silica/polyvinyl alcohol mixed matrix membranes201343211512510.1016/j.memsci.2013.01.0052-s2.0-84873925120HassanajiliS.MasoudiE.KarimiG.KhademiM.Mixed matrix membranes based on polyetherurethane and polyesterurethane containing silica nanoparticles for separation of CO2/CH4 gases201311611210.1016/j.seppur.2013.05.0172-s2.0-84878843874DhootS. N.FreemanB. D.StewartM. E.Barrier polymers2002New York, NY, USAJohn Wiley & Sons10.1002/0471440264.pst025SuloffE.2002Blacksburg, Va, USAVirginia Polytechnic Institute and State UniversityDadfarS. M. M.KavoosiG.DadfarS. M. A.Investigation of mechanical properties, antibacterial features, and water vapor permeability of polyvinyl alcohol thin films reinforced by glutaraldehyde and multiwalled carbon nanotube20143591736174310.1002/pc.228272-s2.0-84905867827AsadinezhadA.NovákI.LehockýM.BílekF.VeselA.JunkarI.SáhaP.PopelkaA.Polysaccharides coatings on medical-grade PVC: a probe into surface characteristics and the extent of bacterial adhesion20101521007102710.3390/molecules150210072-s2.0-77649225101RoyN.SahaN.HumpolicekP.SahaP.Permeability and biocompatibility of novel medicated hydrogel wound dressings20108433835710.1080/1539445X.2010.5029552-s2.0-78649496435SaljoughiE.SadrzadehM.MohammadiT.Effect of preparation variables on morphology and pure water permeation flux through asymmetric cellulose acetate membranes2009326262763410.1016/j.memsci.2008.10.0442-s2.0-58149295952MeierM. M.KanisL. A.de LimaJ. C.PiresA. T. N.SoldiV.Poly(caprolactone triol) as plasticizer agent for cellulose acetate films: influence of the preparation procedure and plasticizer content on the physico-chemical properties2004151059360010.1002/pat.5172-s2.0-8644278875QuintanaR.PersenaireO.BonnaudL.DuboisP.Recent advances in (reactive) melt processing of cellulose acetate and related biodegradable bio-compositions20123359159510.1039/c1py00421b2-s2.0-84857343341SedlaříkV.SahaN.KuřitkaI.SáhaP.Preparation and characterization of poly (vinyl alcohol)/lactic acid compounded polymeric films200611425327010.1080/102366606007501902-s2.0-33745177757