International Journal of Polymer Science
Volume 2018 (2018), Article ID 2764749, 8 pages
https://doi.org/10.1155/2018/2764749

Research Article

Preparation of Keratin-Glycine Metal Complexes and Their Scavenging Activity for Superoxide Anion Radicals

Jianfeng Wang, Xiaoxiao Li, Yufeng He, Pengfei Song, and Rong-Min Wang

Key Laboratory of Eco-Environment-Related Polymer Materials of Ministry of Education, Institute of Polymer, College of Chemistry & Chemical Engineering, Northwest Normal University, Lanzhou 730070, China

Correspondence should be addressed to Yufeng He; heyufeng@nwnu.edu.cn and Rong-Min Wang; wangrm@nwnu.edu.cn

Received 19 September 2017; Accepted 22 March 2018; Published 15 May 2018

Academic Editor: Chaoqun Zhang

Copyright © 2018 Jianfeng Wang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

To address the problem of limited application of natural SOD, the development of SOD mimic enzymes is of great importance for bioantioxidation. Herein, we report on a new type of biopolymer antioxidant with excellent scavenging activity for , keratin-glycine metal complexes (FK-GlyM, M = Zn, Cu, Mn, Ni). They are prepared by feather keratin firstly combined with glycine and then metal ions. Using FT-IR, TG, CD, and SEM, the performance of the obtained complexes (FK-GlyM) for scavenging is analysed and investigated. Importantly, the scavenging activity of FK-GlyCu is excellent in all FK-GlyM, and FK-GlyCu₆₀ has the most excellent anti- activity in all FK-GlyC, of which EC₅₀ and degree of simulation were, respectively, up to  μmol/L and 911.1% compared with nature Cu, Zn-SOD. Finally, its mechanism was also discussed. In summary, this method about the simulation strategies will provide a novel idea for exploiting new-type biocompatible and highly reactive antioxidants.

1. Introduction

In vivo, excess oxygen free radical is harmful to the body [1]. Under normal circumstances, the production and the elimination of oxygen radicals are balanced [2]. However, due to the impact of the disease, age, and the external environment, excess oxygen radicals would be accumulated in the cells when the physiological balance was broken [3, 4], leading to host tissue be damaged [5], such as the damage of protein, lipid peroxide, DNA mutation, and enzyme inactivation. However, superoxide dismutase (SOD) as antioxidant is important to protect cells from oxidative damage [6], which can catalyze the disproportion action of superoxide anion radicals () and further balance in vivo. Although the natural SOD has the excellent activity for scavenging , many disadvantages still exist [7], such as complex extract process, high cost, big molecular weight, easy deactivation, and not easily entering the cell membrane, which limited its application in medicine and other fields [8–10]. Therefore, the preparation of SOD mimic enzyme is becoming more and more popular [11, 12].

Currently, a lot of enzyme simulations for scavenging have been synthesized, including porphyrin metal complexes [7, 13], macrocyclic metal complexes [14], and Schiff-base metal complexes [15]. However, due to the low solubility in water, large side effects, and so on, the widespread applications of these SOD mimics based on micromolecule were still limited. Therefore, SOD mimics based on macromolecule become the new direction for simulation of SOD. In SOD mimic based on polymer, there are mainly cyclodextrins [16] and proteins [17–19]. For proteins, they can form directly complexes with metal ions since they contain a large number of amino and carboxyl functional groups with complex function. In general, those metals as SOD activity center mainly include Cu [20], Co [21], Mn [22, 23], and Fe [24]. Ibrahim et al. [25] reported that Ovotransferrin (OTF) had function of scavenging when it combined with Cu and Mn. Besides, there is an important complement oxygen free radical scavenger in vivo: Metallothionein (MT). It is a class of protein containing low molecular weight and abundant thiol groups, which contribute to scavenging by combining with metal ions [26].

Keratin widely exists in hair, feathers, wool, nails, and horns [27]. Due to its special molecular structure, it is hard to be used by humans and casually abandoned, which caused the waste of resources and bad environmental pollution [28]. However, they have a large number of disulfide bonds [29, 30]. If thiol groups produced by the reduction of disulfide bonds combine with metal, the structural system similar to metallothionein will be generated. In this paper, feather keratin (FK) and glycine (Gly) firstly were combined to generate FK-Gly in an aqueous solution, then the transition metal ions (, , , and ) were combined with FK-Gly to generate keratin-based biopolymer metal complexes (FK-GlyM, M = Zn, Cu, Mn, Ni) and further studied its property of scavenging and seriously explored its mechanism.

2. Experiments

2.1. Materials

Glycine (Gly) was purchased from Shanghai Institute of Biochemistry. Ni(OAc)₂·4H₂O, Mn(OAc)₂·4H₂O, Zn(OAc)₂·4H₂O, and Cu(OAc)₂·H₂O were all obtained commercially. Both Chlorinated Nitro blue tetrazolium (NBT) and DL-Methionine are biochemicals, which are products of Zhongqin Chemical Reagent Co., Ltd., in Shanghai and Tianjin Guangfu Fine Chemical Research Institute. Feather keratin (FK) is self-made in our laboratory. Unless otherwise stated, all other chemicals were of analytical grade and used without further purification.

2.2. Equipment for Characterization

Fourier transform infrared spectra (FT-IR) were measured by an FT-IR spectrometer (FTS 3000) of DigiLAB, and the transmittance spectra were collected in the range of 4000–400 cm⁻¹ at a resolution of 0.008 cm⁻¹. Thermogravimetric analyses of products were carried out on a PerkinElmer Pyris Diamond thermogravimetry (TG)/dynamic thermal analyzer at a heating rate of 10°C/min under a nitrogen atmosphere. Circular Dichroism (CD) was recorded by a Jasco J-810 spectropolarimeter (1 cm cell). The wavelength of scanning was from 200 to 250 nm, the speed was 200 nm/min, and a response time was of 1 s. The morphologies of product were studied by scanning electron microscopy (SEM) (Zeiss ULTRA Plus microscope, Germany).

2.3. Preparation of Keratin-Glycine Metal Complexes (FK-GlyM)

Four kinds of metal salt solution [M (OAc)₂] were prepared as follows: Ni (OAc)₂, Mn (OAc)₂, Zn (OAc)₂, and Cu (OAc)₂ were individually dissolved in water and set aside. Glycine solution (0.02 mM) was prepared in a phosphate buffer solution (PBS, 100 mL).

2.3.1. Preparation of Keratin-Glycine Complexes (FK-Gly)

Firstly, certain keratin, Na₂S₂O₃, and glycine were dispersed into water, and then certain concentration of NaOH solution was added to adjust the pH up to 7-8. Finally this mixture was stirred 6–12 h in the dark at room temperature. The keratin-glycine complex (FK-Gly) was successfully prepared.

2.3.2. Preparation of Keratin-Glycine Metal Complexes (FK-GlyMx)

The preparation process of FK-GlyZn₅ is as follows: Zn (OAc)₂ and FK-Gly were added to simple tube ( :  = 1 : 5). After being magnetic stirred 12 h in the dark, FK-GlyZn₅ was obtained and set aside in the dark at 0–4°C. The concentration of FK-GlyZn₅ was calculated according to the amount of FK.

The preparations of FK-GlyCu₅, FK-GlyMn₅ and FK-GlyNi₅ are similar to that of FK-GlyZn₅.

By changing the ratio of Cu(OAc)₂ being added to the mixture, keratin-based metal copper complex with different ratio was also obtained, namely, FK-GlyC (, 10, 20, 30, 40, 50, 60, 80, 100).

3. Results and Discussion

The preparation route of FK-GlyM was shown in Scheme 1, where the FK and FK-SH were the partially crosslinking protein and reduced protein. FK-Gly was modified by Gly and FK-GlyM was keratin-glycine metal complex. Firstly, the disulfide bonds (-S-S-) in keratin firstly were reduced to thiol groups (-SH) by strong reductant, and then these thiol groups reacted with the amino of glycine to generate keratin-glycine complex. Finally, keratin-glycine complex reacted with metal to give keratin-glycine metal complex.

Scheme 1: The preparation process of FK-GlyM (M = , , , ).

3.1. Structure Characterization of FK-GlyM

The obtained FK-GlyM was characterized by FT-IR spectra, TG, CD, and SEM. Moreover, we also discussed the mechanism of antioxidation activity.

3.1.1. FT-IR Spectra

The prepared keratin-glycine Cu complex (FK-GlyCu₆₀) was frozen in the refrigerator at −20°C for 24 h. After being lyophilized, the products and KBr were mixed with 1 : 100 and made into transparent tablet for measuring FT-IR spectra. The result was shown in Figure 1. In FT-IR spectrum of FK, some characteristic absorption peaks at 1647 cm⁻¹, 1522 cm⁻¹, and 1236 cm⁻¹ were, respectively, assigned to amide I, II, III band of FK, which indicated that the secondary structure of FK was mainly free coil. However, for FK-GlyCu₆₀, the characteristic absorption peaks of amide I, II, III band demonstrated that the secondary structure of FK-GlyCu₆₀ was mainly free coil and β-sheet structure. Therefore, the secondary structure of FK had been changed, and some random coil structures also had been into β-sheet structure in the preparation process of FK-GlyM. Besides, characteristic absorption peaks of S-S bonds had happened red shift from 580 cm⁻¹ to 546 cm⁻¹, which illustrated that S-S bonds had become less stable in the preparation process. It could be conjectured that some S-S bond had shifted and might generate -SH or sulfur anion in preparation process.

Figure 1: The IR spectra of FK-GlyCu₆₀ complex.

3.1.2. TG Analysis

TG curves of FK and FK-GlyCu₆₀ were presented in Figure 2. It could be seen that FK gave three weight losses within total temperature range, which could be assigned to the weight loss of adsorbed water at about 100°C and keratin decomposition at 200°C and 375°C. Meanwhile, FK-GlyCu₆₀ also gave three weight losses within total temperature range, caused by the decomposition of FK at 200 and 375°C as well as no weight loss after 575°C. In summary, compared with feather keratin, the thermodynamic stability of the obtained keratin-glycine metal complexes was reduced.

Figure 2: The TG of FK and FK-GlyCu₆₀.

3.1.3. CD Analysis

Circular Dichroism (CD) of FK-GlyC (0.005 mM) was measured at the wavelength of 190–300 nm and room temperature. The results were shown in Figure 3. The characteristic peaks of random coil structure of FK appeared at near 195 nm while the characteristic peaks of β-sheet layer structure of FK-GlyC complex appeared in the vicinity of 200 nm. Therefore, it was showed that the secondary structures of the prepared FK-GlyC were mainly β-sheet and random coil, which could be attributed to the fact that the part random coil of secondary structure of the FK-GlyC complex had transformed into β-sheet compared with pure FK. The result was the same as FT-IR spectrum analysis.

Figure 3: The CD spectra of FK-GlyC complexes.

3.1.4. SEM Images

After being lyophilized, the microstructure of dry FK and FK-GlyCu₆₀ was characterized by scan electron microscopy (SEM). As showed in Figure 4, in contrast to FK, it was found that they had the porous support structure and the pore size was 0.2–2 μm in FK-GlyCu₆₀. These porous structures would facilitate the adsorption of small molecules and macromolecular compounds.

Figure 4: The SEM images of FK-GlyCu₆₀.

3.2. Scavenging Activity of FK-GlyM

Using NBT photochemical reduction method to investigate scavenging superoxide anion radicals () activity of keratin (FK) and the keratin-glycine complex (FK-Gly), the results were shown in Table 1 and Figure 5. According to the results, FK and FK-Gly ([FK] = 5 μmol/L) both presented some anti- activity, and the scavenging activity of FK-Gly was better than FK. Compared with FK, the activity of FK-Gly was doubled.

Table 1: EC₅₀ of FK-Gly and FK.

FK-GlyCu₅
EC₅₀ (μmol/L)
Degree of simulation (%)

FK

4.8

FK-Gly

9.3

FK-GlyCu₅

61.2

FK-GlyCu₆₀

911.1

Cond: [FK] = 5 μmol/L, n (FK) : n (Gly) = 1 : 0.2; = 20°C.

Figure 5: scavenging activity of FK-Gly and FK.

3.2.1. Scavenging Activity of FK-Gly under Different Environment

In order to get better FK-Gly, the effect factors on its scavenging activity, such as temperature, pH, and Gly content, were investigated.

At Different Temperature. Under the condition of the same ratio, the effects of temperature on the scavenging activity of FK-Gly for were investigated. The results were shown in Table 2 and Figure 6, turning out that FK-Gly had the best scavenging activity for at 20°C and EC₅₀ and degree of simulation could, respectively, reach  μmol/L and 7.1%.

Table 2: EC₅₀ of FK-Gly at different temperatures.

(°C)
EC₅₀ (μmol/L)
Degree of simulation (%)

10

6.7

20

7.1

30

6.3

40

6.8

Cond: [FK] = 5 μmol/L, n (FK) : (Gly) = 1 : 0.2.

Figure 6: The comparison of scavenging activity of FK-Gly at different temperatures.

At Different pH Value. Under the condition of the same ratio and temperature, the effects of different pH on the scavenging activity of FK-Gly for were investigated. The results were shown in Table 3 and Figure 7, which indicated that the scavenging activity of FK-Gly was best when the pH was 7-8 and EC₅₀ and degree of simulation could, respectively, up to  μmol/L and 17.8%.

Table 3: EC₅₀ of FK-Gly at different pH values.

pH
EC₅₀ (μmol/L)
Degree of simulation (%)

12.6

7.5

11.0

16.4

10.0

14.6

8.7

9.8

7.3

17.8

Cond: [FK] = 5 μmol/L, n (FK) : (Gly) = 1 : 0.2, T = 20°C.

Figure 7: The comparison of scavenging activity of FK-Gly at different pH values.

At Different Gly Content. Under the condition of the same temperature and pH, the effects of different Gly content on the scavenging activity of FK-Gly for were investigated, and the results were shown in Table 4 and Figure 8. It was found that the scavenging activity of FK-Gly was best and EC₅₀ and degree of simulation could, respectively, reach  μmol/L and 19.5% when the ratio of FK and Gly was 1 : 0.6 though the scavenging activity was similar when the ratios of FK and Gly were 1 : 0.2–1 : 0.6.

Table 4: EC₅₀ of FK-Gly at different mounts of Gly.

n (FK) : n (Gly)
EC₅₀ (μmol/L)
Degree of simulation (%)

1 : 0.2

17.8

1 : 0.4

17.8

1 : 0.6

19.5

1 : 0.8

8.2

1 : 1

5.4

Cond: [FK] = 5 μmol/L, = 20°C, pH = 7-8.

Figure 8: The comparison of scavenging activity of FK-Gly at different amounts of Gly.

3.2.2. Scavenging Activity of FK-GlyM

Similarly, adopting NBT photochemical reduction method investigated anti- activity of FK-GlyM₅ (M = Zn, Cu, Mn, Ni). Although they all had certain anti- activity, the different metal complexes had different activity. To compare anti- activity and EC₅₀ of different FK-GlyM in Table 5 and Figure 9, the results revealed that FK-GlyCu₅ had the most active for scavenging superoxide anion radicals, of which EC₅₀ was  μmol/L and degree of simulation was 61.2% comparing with nature Cu, Zn-SOD. However, the activity of FK-GlyZn₅ was most weak and its EC₅₀ was only  μmol/L and degree of simulation was 17.1% comparing with nature Cu, Zn-SOD. To sum up, the scavenging activity for of four kinds of keratin-glycine metal complexes was FK-GlyCu₅ > FK-GlyMn₅ > FK-GlyNi₅ > FK-GlyZn₅.

Table 5: EC₅₀ of FK-GlyM₅.

FK-GlyM₅
EC₅₀ (μmol/L)
Degree of simulation (%)

FK-GlyZn₅

17.1

FK-GlyCu₅

61.2

FK-GlyMn₅

26.1

FK-GlyNi₅

18.6

Cond: [FK] = 0.005 mmol/L, n (FK) : n (M (OAc)₂) = 1 : 5 (M = Zn, Cu, Mn, Ni).

Figure 9: scavenging activity of FK-GlyM₅.

Further, the effect of different ratios of FK-GlyC on scavenging activity for was investigated in order to get the best FK-GlyCu. Firstly, the following complexes were prepared: FK-GlyCu₅, FK-GlyCu₁₀, FK-GlyCu₂₀, FK-GlyCu₃₀, FK-GlyCu₄₀, FK-GlyCu₅₀, FK-GlyCu₆₀, FK-GlyCu₇₀, FK-GlyCu₈₀, FK-GlyCu₉₀, and FK-GlyCu₁₀₀, and then they contrasted their anti- activity in Table 6 and Figure 10. The results indicated that the mount of metal ions () had important effect for anti- activity of FK-GlyC complex. With the increase of metal ion , the anti- activity of FK-GlyC was first increased and then decreased. The scavenging activity of FK-GlyCu₆₀ for was strongest in Table 6 and Figure 10. Compared with the literature [31], of which EC₅₀ and degree of simulation, respectively, were  μmol/L and 107%; here EC₅₀ of prepared FK-GlyCu₆₀ was far below it and the degree of simulation was much bigger than it. The values, respectively, were up to  μmol/L and 911.1%.

Table 6: The effect of the mount of for scavenging activity of FK-GlyC.

FK-GlyC
EC₅₀ (μmol/L)
Degree of simulation (%)

FK-GlyCu₅

35.7

FK-GlyCu₁₀

74.5

FK-GlyCu₂₀

256.3

FK-GlyCu₃₀

251.5

FK-GlyCu₄₀

315.4

FK-GlyCu₅₀

525.6

FK-GlyCu₆₀

911.1

FK-GlyCu₇₀

585.7

FK-GlyCu₈₀

205.0

FK-GlyCu₉₀

167.4

FK-GlyCu₁₀₀

221.6

Figure 10: scavenging activity of FK-GlyC with different ratios.

3.3. Suggested Mechanism of Active Center

According to our reported results, the active center and mechanism of FK-GlyM for scavenging were suggested. There exist possibly three active reaction centers (Scheme 2). (1) Metal ion and N from the histidine and amino acid chain of FK residues formed coordination bonds, obtaining a six-member ring structure which provided reaction centers. (2) Metal ions and N, O in amino acid chain of FK coordinated, respectively, to form a plurality of annular reaction center, and the synergy of multiple active centers improved the scavenging activity of FK-GlyM for . Meanwhile, due to the introduction of glycine, the aggregation of polymer chains in keratin became difficult and further increased the solubility of FK-GlyM. (3) For FK-GlyM, the partial COO⁻ of glycine and M²⁺ occurred to electrostatic attraction that led to form new reactive center. Moreover, the thiol (-SH) from S-S had active hydrogen atom which could cause the free radical of chain growth to become less active and further generate the free radical with poor reactivity or extremely stable inhibitor free radical via providing active hydrogen. In either of these two cases, the inhibitor slowed down the original radical reaction and even stopped the reaction carrying out.

Scheme 2: The active center for scavenging of FK-GlyM.

4. Conclusion

In summary, a simple biopolymer antioxidant (FK-GlyM) with excellent scavenging activity has been gained via simply combining FK with Gly and metal ions. It was found that the scavenging activity of FK-GlyM for was prior to FK-Gly and FK. After exploring the effect of temperature, pH, and ratios on scavenging activity, the results proved that the optimal conditions were 20°C, pH = 7-8, and n (FK) : n (FK-Gly) = 1 : 0.6, where the scavenging capacity of FK-Gly for was best. In four kinds of FK-GlyM, it turned out that the order of scavenging activity was FK-GlyCu₅ > FK-GlyMn₅ > FK-GlyNi₅ > FK-GlyZn₅. And FK-GlyCu₆₀ was proved to have the most outstanding anti- activity in all FK-GlyC, of which EC₅₀ and degree of simulation separately reached  μmol/L and 911.1% compared with nature Cu, Zn-SOD. The reutilization of discarded feather keratin to prepare biopolymer antioxidant points out a new idea for both the problem of resources environment and the research on biopolymer antioxidant to us.

Conflicts of Interest

The authors declare that there are no conflicts of interest regarding the publication of this paper.

Acknowledgments

The project was supported by the NSFC of China (21364012 and 21263024).

References

I. Fridovich, “The biology of oxygen radicals,” Science, vol. 201, no. 4359, pp. 875–880, 1978.

M. Pesce, A. Rizzuto, I. La Fratta et al., “Super-oxide anion production and antioxidant enzymatic activities associated with the executive functions in peripheral blood mononuclear cells of healthy adult samples,” Neuroscience Research, vol. 106, pp. 23–28, 2016.

O. Iranzo, “Manganese complexes displaying superoxide dismutase activity: a balance between different factors,” Bioorganic Chemistry, vol. 39, no. 2, pp. 73–87, 2011.

T. Zhao, Y. F. He, Y. Wang, J. Mao, R. M. Wang, and L. Y. Yang, “Albumin conjugating Schiff-bases metal complexes for removing radical,” Chemical Research and Application, vol. 25, no. 7, pp. 970–975, 2013.

G. Blander, R. M. De Oliveira, C. M. Conboy, M. Haigis, and L. Guarente, “Superoxide dismutase 1 knock-down induces senescence in human fibroblasts,” The Journal of Biological Chemistry, vol. 278, no. 40, pp. 38966–38969, 2003.

Y. Y. Chia, M. S. Kanthimathi, J. Rajarajeswaran, K. S. Khoo, and H. M. Cheng, “Antioxidant, antiproliferative, genotoxic and cytoprotective effects of the methanolic extract of Padina tetrastromatica on human breast adenocarcinoma and embryonic fibroblast cell lines,” Frontiers in Life Science, vol. 8, no. 4, pp. 411–418, 2015.

F. Pei, Y. F. He, X. Li, R. M. Wang, G. Li, and T. T. Zhao, “SOD mimics based on macromolecules,” Progress in Chemistry, vol. 25, no. 0203, pp. 340–349, 2013.

D. P. Riley, “Functional Mimics of Superoxide Dismutase Enzymes as Therapeutic Agents,” Chemical Reviews, vol. 99, no. 9, pp. 2573–2587, 1999.

A. J. Wu, J. E. Penner-Hahn, and V. L. Pecoraro, “Structural, spectroscopic, and reactivity models for the manganese catalases,” Chemical Reviews, vol. 104, no. 2, pp. 903–938, 2004.

B. J. Day, “Catalytic antioxidants: a radical approach to new therapeutics,” Drug Discovery Therapy, vol. 9, no. 13, pp. 557–566, 2004.

S. Asayama, T. Mori, S. Nagaoka, and H. Kawakami, “Chemical modification of manganese porphyrins with biomolecules for new functional antioxidants,” Journal of Biomaterials Science, Polymer Edition, vol. 14, no. 11, pp. 1169–1179, 2003.

S. Purtaş, M. Köse, F. Tümer, M. Tümer, A. Gölcü, and G. Ceyhan, “A novel porphyrin derivative and its metal complexes: Electrochemical, photoluminescence, thermal, DNA-binding and superoxide dismutase activity studies,” Journal of Molecular Structure, vol. 1105, pp. 293–307, 2016.

S. A. Güngör, M. Köse, F. Tümer, and M. Tümer, “Photoluminescence, electrochemical, SOD activity and selective chemosensor properties of novel asymmetric porphyrin-Schiff base compounds,” Dyes and Pigments, vol. 130, pp. 37–53, 2016.

S. Cuzzocrea, E. Mazzon, R. Di Paola et al., “Effects of combination M40403 and dexamethasone therapy on joint disease in a rat model of collagen-induced arthritis,” Arthritis & Rheumatology, vol. 52, no. 6, pp. 1929–1940, 2005.

X. M. Dang, G. Li, Y. F. He, T. Zhao, and M. R. Wang, “Amino acid Schiff-bases metal complexes conjugating with albumin for removing oxygen radical,” Chemical Research and Application, vol. 24, no. 8, pp. 1217–1220, 2012.

H. Fu, Y.-H. Zhou, W.-L. Chen et al., “Complexation, structure, and superoxide dismutase activity of the imidazolate-bridged dinuclear copper moiety with β-cyclodextrin and its guanidinium-containing derivative,” Journal of the American Chemical Society, vol. 128, no. 15, pp. 4924-4925, 2006.

R. M. Olinescu and F. A. Kummerow, “Fibrinogen is an efficient antioxidant,” The Journal of Nutritional Biochemistry, vol. 12, no. 3, pp. 162–169, 2001.

X. Li, G. Li, Y. He F, and M. Wang R, “Advances in polymer antioxidants,” Chemistry, vol. 74, no. 4, pp. 316–324, 2011.

X. Yin, G. Li, R. Wang, Y. He, and Y. Xiong, “Antioxidant activity of conjugation of metalloporphyrin combining with bovine serum albumin,” Science China Chemistry, vol. 43, no. 2, pp. 171–177, 2013.

J. Vančo, O. Švajlenová, E. Račanská, J. Muselík, and J. Valentová, “Antiradical activity of different copper(II) Schiff base complexes and their effect on alloxan-induced diabetes,” Journal of Trace Elements in Medicine and Biology, vol. 18, no. 2, pp. 155–161, 2004.

F. Bellot, R. Hardré, G. Pelosi, M. Thérisod, and C. Policar, “Superoxide dismutase-like activity of cobalt(II) complexes based on a sugar platform,” Chemical Communications, no. 43, pp. 5414–5416, 2005.

S. R. Doctrow, K. Huffman, C. B. Marcus et al., “Salen-manganese complexes as catalytic scavengers of hydrogen peroxide and cytoprotective agents: Structure-activity relationship studies,” Journal of Medicinal Chemistry, vol. 45, no. 20, pp. 4549–4558, 2002.

M. Kose, P. Goring, P. Lucas, and V. Mckee, “Mono-, di- and tri-nuclear manganese(II) complexes derived from a quinquedentate ligand: Superoxide dismutase and catalase mimetic studies,” Inorganica Chimica Acta, vol. 435, pp. 232–238, 2015.

G.-F. Liu, M. Filipović, F. W. Heinemann, and I. Ivanović-Burmazović, “Seven-coordinate iron and manganese complexes with acyclic and rigid pentadentate chelates and their superoxide dismutase activity,” Inorganic Chemistry, vol. 46, no. 21, pp. 8825–8835, 2007.

H. R. Ibrahim, M. I. Hoq, and T. Aoki, “Ovotransferrin possesses SOD-like superoxide anion scavenging activity that is promoted by copper and manganese binding,” International Journal of Biological Macromolecules, vol. 41, no. 5, pp. 631–640, 2007.

M. Vašák, “Advances in metallothionein structure and functions,” Journal of Trace Elements in Medicine and Biology, vol. 19, no. 1, pp. 13–17, 2005.

J. Wang, W. Qian, Y. He, Y. Xiong, P. Song, and R.-M. Wang, “Reutilization of discarded biomass for preparing functional polymer materials,” Waste Management, vol. 65, pp. 11–21, 2017.

Y. F. He, W. Z. Qian, J. F. Wang, Y. B. Xiong, P. F. Song, and M. R. Wang, “High value-added reutilization approach for waste biomass materials,” Transactions of the Case, vol. 32, no. 15, pp. 1–8, 2016.

W. Z. Qian, Y. F. He, J. F. Wang, J. Chen, and M. R. Wang, “Advanced on functional materials based on discarded natural polymers,” Polymer Bulletin, vol. 4, pp. 1–8, 2017.

K. Sun, J. Guo, Y. He, P. Song, Y. Xiong, and R.-M. Wang, “Fabrication of dual-sensitive keratin-based polymer hydrogels and their controllable release behaviors,” Journal of Biomaterials Science, Polymer Edition, vol. 27, no. 18, pp. 1926–1940, 2016.

G. Yan, Y. He, G. Li, Y. Xiong, P. Song, and R.-M. Wang, “Bovine Serum Albumin Metal Complexes for Mimic of SOD,” Journal of Chemical Sciences, vol. 128, no. 11, pp. 1783–1788, 2016.