The nanopowders of Ni0.38Cu0.12Zn0.5Fe2O4 with particle size, 20 nm have been synthesised using Microwave-Hydrothermal method and characterized. Then the ferrite samples were microwave sintered at different temperatures in an air atmosphere and characterized. The magnetic properties were measured at room temperature. The dielectric constant (ɛ), initial permeability (μi) and quality factor (Q) has been measured on sintered samples at 1 MHz. Thermal variation of initial permeability has been measured over temperature range of 300 K–600 K. A detailed study of elastic behaviour of NiCuZn ferrites has been under taken using a composite piezoelectric oscillator method over a temperature of 300 K–600 K. The room temperature elastic moduli is found to be slightly sample dependent and decreases with increasing the temperature, except near the Curie temperature, TC, where a small anomaly is observed. The internal friction at room temperature is also found to be more particle size dependent. The temperature variation of internal friction exhibits a broad maximum around 500 K, just below Curie temperature TC 530 K. The above observations were carried on in the demagnetized state; on the application of a 400 mT magnetic field allowed us to reach the saturated state of the sample at any of the measuring temperature. The anomaly observed in the thermal variation of elastic moduli and internal friction is explained with the help of temperature variation of magneto-crystalline anisotropy constant.
1. Introduction
By the development of surface mount technology (SMT) and multilayer chip devices, NiCuZn ferrites have been extensively studied and widely used to fabricate chip inductors and EMI filters because of their relatively low sintering temperature and high resistivity with good performance at high frequencies [1–5]. However, in these ferrites, it was found that the mechanical and magnetic properties are easily changed or deteriorated by the stress caused at the internal electrode. These problems can be reduced by the preparation of NiCuZn ferrites under controlled experimental conditions and with the knowledge of mechanical properties. On the other hand, the mechanical properties of ferrites are often taken for granted during the manufacture and testing. Despite this, the strength of ferrites can be important particularly for parts, which are tightly clamped during their assembly and use to assure minimum changes in devices performance with mechanical shock, temperature, vibration, and so forth. A survey of the literature tells that no information is available for NiCuZn ferrites on the elastic properties.
There is an abundant literature on the propagation of ultrasonic waves in magnetic materials, but a few interpretations only refer to possible effects due to the domain wall (DW) [6]. It was known from the acoustic emission (AE) studies on magnetic materials that the space occupied by a DW is the location of magnetoelastic interactions and ultrasonic bursts are emitted when the DW are created or annihilated [7, 8]. It was also found that the specific DW/lattice magneto-elastic interactions might be one of the origin of the DW relaxation. In order to understand, an interaction of DW with elastic modulus, a detailed study of the thermal variation of elastic modulus, and internal friction on nanocrystalline Ni0.38Cu0.12Zn0.5Fe2O4 have been undertaken over a wide temperature range.
2. Experimental Method
Pure (99.98%) nickel nitrate [Ni(NO3)2.6H2O], (99.95%) copper nitrate [Cu(NO3)2.3H2O], (99.98%) zinc nitrate [Zn(NO3)2.6H2O], and (99.96%) iron nitrate [Fe(NO3)2.9H2O] were dissolved in 50 mL of deionized water. The molar ratio of powders was adjusted to obtain the composition Ni0.38Cu0.12Zn0.5Fe2O4. An aqueous NaOH solution was added to solution until the desired pH (~9.45) value was obtained. The mixture was then treated in Teflon lined vessel using a microwave digestion system (Model MDS-2000, CEM Corp., Mathews, NC). This system uses 2.45 GHz microwaves and can operate at 0–100% full power (630±50W). In the present investigation, the samples were synthesized at 160°C/30 min. The time, pressure, and power were computer controlled. The products obtained were filtered and then washed repeatedly with deionized water, followed by freeze drying overnight. The synthesized powders were weighed, and the percentage yields were calculated from the expected and the amount that was actually crystallized. The yield obtained in the present investigation was 95%. As synthesized powders were characterized by using powder X-ray diffraction (XRD, Philips analytical X-ray diffractometer with Cu-Kα radiation). Particle size and morphology were determined using transmission electron microscopy (TEM, Model JEM-2010, JEOL, Tokyo, Japan).
To nanopowders, 2 wt% of poly-vinyl-alcohol was added as a binder and pressed in a die under a pressure of 190 MPa for 10 min into pellets (10 mm diameter, 3 mm thickness), and (50 mm in length, 10 mm diameter), and toroids (12 mm outside diameter, 6 mm inside diameter, 3 mm thickness). After binder burnt out at 300°C, the samples were microwave sintered at 750°C/30 min (MW1), 800°C/30 min (MW2), 850°C/30 min (MW3), 900°C/30 min (MW4), and 930°C/30 min (MW5) in air. The microwave sintering process was carried out using a specially designed applicator which consists of a domestic microwave oven having an output power level tuneable up to a maximum of 800 W and operating frequency of 2.45 GHz.
All the sintered samples were characterized using the X-ray diffraction (XRD). The average grain size (Dm) of the samples was evaluated using the scanning electron microscopy (SEM; LEICA, S440i, UK) pictures. The thermal expansion of the sintered samples has been measured using dilatometer (DIL 402C) in air and at a heating rate of 20°C/min. The saturation magnetization (MS) and coercive field (HC) values of the present samples were obtained from the recorded hysteresis loops using the vibrating sample magnetometer (VSM, model DMS 1660) at room temperature. The initial permeability (μi) and quality factor has been measured on sintered samples at 1 MHz using a LCR meter. Thermal variation of initial permeability has been measured using the LCR meter at 1 kHz.
The elastic constants such as Young’s modulus, Y, and shear modulus, G, were measured on sintered samples over the temperature range of 300 K–600 K using the composite piezoelectric oscillator method [9]. The appropriate quartz crystal transducer was cemented on the specimen with phenyl salicylate and two parts of sodium silicofluoride mixed with one part of barium sulphate in one drop of water glass for room and high temperature measurements, respectively. For Young’s moduli measurements, the piezoelectric crystals were cut to oscillate at 100.245±0.001 kHz in longitudinal direction. Shear moduli were measured on the same specimen sections, using shear crystals oscillating at approximately 165.25±0.002 kHz. Young’s and shear moduli were then determined in the usual way using the following expressions: Y=(λlfl)2ρ, G=(λsfs)2ρ, where ρ is density, λ is the wavelength, f is the resonant frequency, and subscripts “l” and “s” refer to longitudinal and shear waves, respectively. All the measurements were conducted keeping the composite oscillator in a vacuum (10-4 Torr). The vacuum chamber was placed at the centre of pole pieces of an electromagnet. The magnetic field was always applied parallel to the length of the specimen. The temperature of the sample is measured using Cr-Al thermocouple with an accuracy of ±0.1 K. The accuracy of Y, G, and internal friction measurements is about 0.1%, 0.1%, and 0.5% respectively.
3. Results and Discussion
Figure 1(a) gives the XRD patterns for as-synthesized powder of NiCuZn ferrite. It can be seen from the figure that the phase-pure ferrite was obtained. The broad peaks in the XRD pattern indicate the formation of nanopowders. All the peaks in the diffraction pattern have been indexed. The peaks (220), (311), (400), (511), and (440) have been deconvoluted to Lorentzian curves using Peak Fit software for the determination of the average diameter (DXRD) using full-width at half-maximum (FWHM) value. The average particle size (Dm) has been calculated using the Scherrer formula: Dm=kl/bcosθ, where k is a constant, b is the full width half maxima, l is the wavelength of X-rays used, and θ is the diffraction angle. The average particle size of NiCuZn ferrite powder was found to be ~25 nm.
(a) XRD pattern and (b) TEM picture for as-synthesized ferrite powder.
Figure 1(b) shows TEM picture for the as-synthesized ferrite powder. The particles are nearly spherical in shape. The average particle size calculated from the different regions of the image was 20 nm. The selected area electron diffraction (SAED) pattern shows rings made up of discrete spots, indicating high crystallinity; the rings are consistent with the cubic spinel structure with an intense ring pattern form (hkl) planes. No secondary phases are found. The observed average size is consistent with that obtained from the X-ray analysis.
The powder XRD patterns for microwave sintered NiCuZn ferrites under investigation reveal a single-phase cubic spinel structure without any other impurity phases (Figure 2). The lines are board, which is a typical characteristic of nanocrystalline nature. The grain sizes were calculated from the XRD line broadening of the peak (311) using the Scherrer relationship, and the obtained values are presented in Table 1. Figure 3 shows the typical SEM pictures for microwave sintered samples. It can be seen from the figures that with an increase of sintering temperature, microstructure of the ferrite has become finer and finer. The microwave sintered samples exhibit fine and uniform microstructures due to the small soaking time. The grain sizes (Dm) as measured from SEM picture for the presently investigated ferrites were presented in Table 1. It can be observed from the table that the grain size of sintered ferrites increases with an increase of sintering temperature.
Room temperature data on NICuZn ferrites.
Sample
TS (°C/min)
dX (g/cc)
TD %
Dm (nm)
ε1 MHz
μi1 MHz
Q1 MHz
MS (emu/g)
HC (Oe)
MW1
750/30
5.312
97
80
12
448
50
50
80
MW2
800/30
5.325
97.1
68
12
460
50
53
75
MW3
850/30
5.376
98
56
10
485
53
60
71
MW4
900/30
5.398
98.4
45
10
510
60
68
68
MW5
930/30
5.459
99.5
35
8
535
65
76
60
XRD patterns for microwave sintered NiCuZn ferrites.
SEM pictures for microwave sintered samples (a) MW3, (b) MW4, and (c) MW5.
The value of lattice constant (a) has been calculated using the XRD data, and the average value of lattice constant is 8.3374±0.0001Å. The bulk density (dX) of the sintered samples has been measured using Archimedes’s method, and the obtained results are presented in Table 1. It can be observed from the table that the value of bulk density increases with an increase of sintering temperature. It can also be seen from the table that the theoretical density (TD) samples have reached 97% at a sintering temperature of 750°C. Finally, a theoretical density of 99.5% has been achieved at a low sintering temperature of 930°C. The ultrafine particle size and relatively uniform grains are responsible for achieving this very high densification at low temperature. We could not reach theoretical value (99.9% of TD) because of the ferrite particle being too fine to be completely dispersed in the liquid suspension and, therefore, flocculated to some extent by Van der Waals bonding. This slightly flocculated suspension resulted in some agglomerated regions distributed in the microstructure of samples. This was confirmed by microstructure. Rearrangement and differential micro-densification processes could not, thus, be wholly avoided during the sintering of these slightly inhomogeneous packed compacts, and therefore completely dense fired bodies were not achieved.
Magnetic properties such as saturation magnetization (MS) and coercivity (HC) obtained from the recorded hysteresis loops are presented in Table 1. The NiCuZn ferrite sintered at 930°C/30 min exhibits optimum magnetic property, a saturation magnetization of 76 emu/g, and HC=60 Oe. It is also observed from the table that value of MS increases with increasing sintering temperature, as a result of increasing crystallinity. The values of HC decrease with increasing sintering temperature. From the magnetic properties results, one can notice that the maximum MS corresponds to a smaller particle size of 35 nm; thus, control of crystal growth by varying sintering temperature can produce ultrafine magnetic powders.
Table 1 also gives initial permeability (μi), dielectric constant (ɛ), and quality factor (Q) values for sintered ferrites at 1 MHz. It can be seen from the table that the samples sintered at 930°C/30 min exhibit an optimum μi value of 535. It can be observed from the table that μi increases with increasing sintering temperature from 750°C to 930°C as a result of increasing densification. The ferrite sintered at 930°/30 min. also shows a maximum quality factor value of 65. The dielectric constant for present ferrites varies from 8 to 12. The smaller dielectric constant has been observed for MW5 sample.
The elastic constants such as Young’s (Y), shear modulus (G), and internal friction (Q-1) were measured at room temperature on sintered samples and presented in Table 2. The table also gives the computed values of Bulk modulus (B=(YG)/3(3G-Y). It can be seen from table that the values of Y and G are found to increase with an increase of sintering temperature. This shows that an increase of sintering temperature increases the atomic binding force markedly. The average value of Poisson’s ratio (σ=(Y/2G)-1) for the samples under investigation is 0.3. The microwave sintered ferrites possess higher values of Y and G when compared to those of ferrites prepared by using solid state sintering method [10]. This is due to the high densification of the present samples.
Elastic modulus data for NiCuZn ferrites at room temperature.
Sample name
Y×10-10 (N/m2)
G×10-10 (N/m2)
K×10-10 (N/m2)
Q-1
Vl (m/s)
VS (m/s)
α
MW1
17.82
7.28
10.76
0.71
6345
3345
0.22
MW2
18.03
7.34
11.12
0.65
6468
3675
0.22
MW3
18.10
7.45
8.42
0.45
6675
3890
0.22
MW4
18.25
7.56
10.39
0.26
6915
3962
0.21
MW5
18.54
7.67
9.38
0.20
6920
3974
0.21
It is clear from the table that the room temperature Y and G were found to increase from 17.82 N/m2 to 18.54 N/m2 and from 7.28 N/m2 to 7.67 N/m2 with an decreasing the grain size from 80 nm to 35 nm, respectively. Reciprocally, the internal friction was found to decrease from 0.71 to 0.20. In the present samples, the increase in density has decreased the grain size from 80 nm to 35 nm. As the porosity (~0.3) of samples remained nearly constant, the increase in the elastic modulus and decrease in the internal friction may be considered due to an decrease in the grain size. This is because, presently, microwave sintered samples have densities in the range from 5.312 g/cm3 to 5.459 g/cm3. This density variation is small compared to the variation of grain size (35 nm to 80 nm). Therefore grain size, not density, has the dominant effect on elastic properties.
No elastic modulus data is available in the literature on nanocrystalline NiCuZn ferrites. However, the present elastic modulus data is in fair agreement with that of previously investigated elastic behaviour of several polycrystalline ferrites [11–13]. Using the elastic modulus data, we have estimated the longitudinal velocity (Vl) and shear velocity (Vs) for all the samples, and results are presented in Table 2. The values of Vl and Vs are found to increase with an increase of sintering temperature. With the help of velocities, the Debye characteristic temperature (Θ) has been estimated using the Anderson method [14]. The average value of the Debye temperature for present ferrites is 546 K.
The elastic behaviour on NiCuZn ferrites has been measured in the temperature range of 300 K–600 K. For these experiments, a fused silica buffer rod was used to isolate the piezoelectric crystals from the heated specimen [15]. Fractional variation in frequency was measured and related to fractional modulus variations through the expansion coefficient.
Consider that YT or GT/YRT or GRT=(1+αΔT)-1(fsT/fs)2, where YRT, GRT, and fs are Young’s modulus, shear modulus, and resonance of the specimen at the reference temperature (room temperature or 300 K), YT, GT, and fsT are the same quantities at any other temperature, ΔT is the difference between the measured and reference temperature, and α is the coefficient of linear expansion over the measured temperature range.
The values of the coefficient of thermal expansion (α) for the present specimens are measured using the dilatometer method in the temperature range of 300 K–600 K. It was found that the variation of “α’’ with temperature (T) for samples MW1, MW2, MW3, MW4, and MW5 are given by the following:
(1)α=6.261×10-6+0.65×10-8(T)+0.532×10-11(T2),(2)α=6.372×10-6+0.75×10-8(T)+0.58×10-11(T2),(3)α=6.485×10-6+0.92×10-8(T)+0.542×10-11(T2),(4)α=6.578×10-6+0.71×10-8(T)+0.645×10-11(T2),(5)α=6.278×10-6+0.25×10-8(T)+0.141×10-11(T2).
Figures 4 and 5 give the thermal variation of Young’s and shear modulus measured in the demagnetized state, for all samples. It can be seen from the figures that the values of Y and G decrease smoothly with increasing temperature and attain a minimum at a certain temperature (T1) below the Curie point. Beyond this temperature the elastic modulus shows a positive temperature coefficient and attains a maximum value at a temperature T2. With further increase of temperature the both Y and, G are found to decrease. For samples, MW2, MW3, and MW4, the values of Y are very close to each other and are found to decrease by about 14% between 300 K and TC. In all these samples, anomalous behaviour occurs in between 520 K and 530 K. The thermal variation of G for all the samples is found to be similar and the variation is about 5% between 300 K and TC. A less (525 K to 535 K) pronounced increase of G with temperature is observed near the Curie point. No hysteresis has been observed during cooling. At a given temperature elastic modulus decreases when the mean grain size increases; this tendency is maintained all over the investigated temperature range. The decrease of Y and G with temperature is mainly due to the softening of the material. Murthy et al. [12, 13, 16, 17] also observed a similar variation of Vl and Vs with temperature in the vicinity of Curie temperature in case of polycrystalline YIG, and observed changes were used to understand the interaction of ultrasonic waves with annihilation/creation of domain walls.
Thermal variation of Young’s modulus (Y) with temperature for microwave sintered NiCuZn ferrites.
Thermal variation of shear modulus (G) with temperature for microwave sintered NiCuZn ferrites.
The anomalous behaviour observed in the case of the presently investigated ferrites can be explained qualitatively with help of the temperature variation of the magneto-crystalline anisotropy constant (k1). The temperature variation of k1 was measured on the brother samples and found that k1 becomes zero just below the Curie temperature, that is, at 522±1 K. The measurements of initial permeability versus temperature on the brother sample have shown that the Curie temperature of the present samples is 530±0.1 K.
As can be seen from Figures 4 and 5, the Y and G for present samples have reached a minimum value at temperature 520 K and 525 K (T1), while k1 becomes zero at 522 K. Similarly, the Y and G attain a maximum value at a temperatures 530 K and 535 K (T2), respectively, while the Curie point of samples under investigation is 530 K. Thus, the minimum (T1) and maximum (T2) temperatures of Y and G verses temperature plots coincide with the temperatures of k1=0 and the Curie temperature, respectively.
The magneto-crystalline anisotropy constant can be considered as a measure of the magnetic energy barrier to the movement of domain walls in the magnetic materials. As such, domains will be free to move at a temperature at which k1=0; the substance undergoes a maximum strain for a given stress; in other words, the Y and G increases till the Curie temperature is reached. Beyond the Curie temperature, both the elastic moduli have shown a decrease with an increase of temperature, since at TC the ferrite losses its spontaneous magnetization and becomes paramagnetic.
In Figures 4 and 5 for the sample MW5, we present the temperature dependence of Y and G measured with H=400 mT; this field was checked to be high enough to saturate the sample at any of the measuring temperatures. In saturated state Y (or G) is slightly higher than in the demagnetized state, expect above TC, where both the values are identical, as expected. When the sample is subjected to magnetic field, it is observed that the minimum of elastic moduli-temperature curve is shifted to the low temperature side and becomes shallow. As the magnetic field increased further the minimum continuous to shift to the low temperature side becoming more and more shallow. Finally, the dip disappears when the magnetic field equal to saturation field of the sample (Figure 6).
Thermal variation of Young’s modulus (Y) with temperature for microwave sintered NiCuZn ferrites in the vicinity of the Curie temperature at applied magnetic fields.
The magnetic contribution to the velocity variations with temperature can be considered as a “second order effect,” superimposed on the purely mechanical effects; it is more pronounced for the large grain size samples. The magnetic contribution dY defined as the difference between the elastic modulus in the saturated and demagnetized states is, respectively, given by dYS=YS(H=400mT)-Y(H=0) which is not more than 2% of the total elastic moduli and varies like the temperature variation of saturation magnetization (MS). Similar variation of Y on temperature and magnetic field was observed for all the other samples.
Figure 7 gives the thermal variation of internal friction (Q-1) measured at zero fields for all samples. It can be seen from the figure that the sample shows a small maximum around 400 K and broad maximum just below the Curie temperature. The rapid increase of Q-1 has been extended over 10 K below TC: the very sharp decrease of Q-1 from about 0.97 down to 0.2 is accomplished in less than ±2K. This abrupt change is the signature of the high chemical homogeneity of our samples.
Thermal variation of internal friction (Q-1) with temperature for microwave sintered NiCuZn ferrites.
In Figure 7, for the sample MW5, we present the temperature dependence of Q-1 measured with H=400 mT. The value of Q-1 in the saturated state is almost temperature independent (=0.17) and is equal to the zero field value above TC. Similar variation of Q-1 on temperature and magnetic field was also observed for all the other samples under investigation, it is observed that the temperature corresponding to the peak in the Q-1 versus temperature curve is near the temperature at which both the velocities show maximum value. As the internal friction is the complementary phenomena of the elastic behaviour, as such the peak observed in Q-1 versus T curve can be attributed to the k1=0. As the internal friction is the complementary phenomena of elastic behaviour, the qualitative explanation given above can be extended for the occurrence of peaks in the Q-1 versus T curves.
The effects of microstructure are well marked on the internal friction, but they are not as dominant as for the elastic modulus. It can be seen from Figure 7 that the microstructure contribution to Q-1 is of the order of 95% of the total. The substantial magnetic contribution to Q-1 seems to result from two contributions: an electronic diffusion related magnetoelastic interaction in the 400 K regions and an interaction of ultrasonic waves with the domain walls in the vicinity of TC. We know that the ferrites exhibit magnetic after-effects due to small deviations from the stoechiometry and the relaxation time of which falls in the microsecond range above room temperature; consequently, an ultrasonic wave can induce—through the magnetoelastic coupling—spin rotations or domain wall movements, which one leads to electronic migrations: this can explain the relative maximum of Q-1 observed around 400 K.
Acknowledgment
The author is thankful to UGC-BSR, New Delhi, for providing grants to carryout this work.
LebourgeoisR.AgeronJ.VincentH.GanneJ. P.Low losses NiZnCu ferritesProceedings of the 8th International Conference on Ferrites (ICF '00)2000Tokyo, JapanYanS.GengJ.YinL.ZhouE.Preparation of nanocrystalline NiZnCu ferrite particles by sol-gel method and their magnetic properties20042771-284892-s2.0-244267814710.1016/j.jmmm.2003.10.014FuY.-P.LinC.-H.LiuC.-W.Preparation and magnetic properties of Ni0.25Cu0.25Zn0.5 ferrite from microwave-induced combustion2004283159642-s2.0-544422932910.1016/j.jmmm.2004.03.053SuH.ZhangH.TangX.Effects of Bi2O3-WO3 additives on sintering behaviors and magnetic properties of NiCuZn ferrites200511732312342-s2.0-1414425628910.1016/j.mseb.2004.11.028KrishnaveniT.KanthB. R.RajuV. S. R.MurthyS. R.Fabrication of multilayer chip inductors using Ni-Cu-Zn ferrites20064141-22822862-s2.0-3364585644510.1016/j.jallcom.2005.07.029LecrawR. C.ComstockR. L.ThurstonR. N.PierceA. D.Magnetoelastic interactions in ferromagnetic insulators19653Bchapter 4Mason127199MurthyS. R.GuyotM.CaganV.Ultrasonic velocity changes in Polycrystalline garnetsProceedings of the International Conference on Magnetism (ICM '88)July 1988Paris, France134135GuyotM.CaganV.The acoustic emission along the hysteresis loop of various ferro and ferrimagnets19911011–32562622-s2.0-0026243415BalamuthL.A new method for measuring elastic moduli and the variation with temperature of the principal young's modulus of rocksalt between 78°K and 273°K193445107157202-s2.0-004037143810.1103/PhysRev.45.715MurthyS. R.Low temperature sintering of NiCuZn ferrite and its electrical, magnetic and elastic properties20022186576602-s2.0-003709202310.1023/A:1015608625798MurthyS. R.RevathiB.RaoT. S.Temperature and composition dependence of the elastic moduli of NiZn ferrites197857129372-s2.0-0017921650MurthyS. R.RaoT. S.Effect of magnetic field and temperature on the elastic behaviour of cobalt-zinc ferrites197965119262-s2.0-0018466314KawaiY.OgawaT.Acoustic losses in single crystals of Mn-Zn ferrite and titanium substituted Mn-Zn ferrites1978456183018342-s2.0-0006848820AndersonO. L.Derivation of wachtman's equation for the temperature dependence of elastic moduli of oxide compounds196614425535572-s2.0-3604905527410.1103/PhysRev.144.553RamaiahB.MurthyS. R.Measurement of Elastic moduli on MnZn ferrites at several Ultrasonic frequencies199721710MurthyS. R.Elastic behaviour and internal friction studies on thin films of NiZn ferrites200291519PraveenaK.SadhanaK.MurthyS. R.Elastic behaviour of microwave hydrothermally synthesized nanocrystalline Mn1−x−Znx ferrites2012474109611032-s2.0-8485800041210.1016/j.materresbull.2011.11.054