The present work develops a MOS-based e-nose with sensors modified with zeolite Y. For this purpose, the following SnO2 doped with Pd and/or Pt have been prepared: M1 ((0.25 Pd/0.75 Pt)/SnO2), M2 ((0.50 Pd/0.50 Pt)/SnO2), M3 ((0.75 Pd/0.25 Pt)/SnO2), Pd/SnO2, and Pt/SnO2, at the total concentrations of the noble metals of 0.1% and 0.2% for use in gas sensors and be part of the electronic nose. Then, the sensors were assembled with the oxides using the screen printing method. Different electronic noses of four sensors were prepared by combining tin oxides doped with palladium and/or platinum and zeolite Y. The physicochemical characterization of oxides using FRX, FTIR, sorption of N2, and RAMAN has been performed. Measurements for the detection of wine volatile compounds such as ethanol, methanol, 1-phenyl ethanol, propionic acid, and acetic acid were carried out with these sensors located in a gas chamber and using a program that includes the Labview software, which serves to automate the sensing process. It was found that the sensors modified with zeolite were the ones that in general had higher detections of volatile compounds and PCAs showed positive correlations only for ethanol and the mixture of ethanol at 12% and methanol at 3%. This is related to better detection of these sensors.
The sense of smell results from a series of specific and nonspecific molecular surveys that can be used to measure the quality of food, beverages, etc. [
As mentioned above, until now, we try to imitate the sense of smell by constructing e-noses based on the criterion of a nonspecific perception. However, single molecule detection requires specific recognition in the case of sample differentiation. For instance, the food industry needs to detect if the product is spoiled, adulterated, etc. For this reason, we consider not only the base material of the sensor but also some modification that allows improving its selectivity. From this, our objective is to modify sensors of SnO2-based composites with zeolites in order to eliminate the passage of some compounds to the SnO2 surface of the sensor and allow the detection of a target molecule, such as ethanol.
The following solutions were prepared for preparation of 0.1% doped tin oxide with mixture platinum and palladium:
In a 100 mL beaker, an amount of H2Cl6Pt and PdCl2 was dissolved with 20 mL of 0.005 M HCl.
In a 100 mL beaker, a mass of SnCl2 was dissolved with 20 mL of 0.005 M HCl. In a 300 mL beaker, 100 mL of 0.005 M HCl and 3 g of SnO2 were added together with the platinum salt solution, kept at 30°C for 15 min under constant stirring. Subsequently, the SnCl2 solution was added and stirred for 50 min at 30°C. The resulting mixture was filtered with Whatman No. 42 paper, followed by washing it with 0.005 M HCl and then with water in order to eliminate the chloride ions. The solid sample was dried at 80°C for 24 h. Subsequently, it was calcined at 400°C for 1 h. This procedure has been used in previous researches [
A template was formed with the adhesive tape to define the area that would cover the film on the surface of two alumina plates. Subsequently, 0.1 gram of doped tin oxide was combined with 0.1% Pd or Pt with 0.02 g of ethylcellulose and 32
Activation of zeolite Y was performed by three ion exchanges, using 600 mL of (NH4)NO3 1 M with 6 grams of zeolite. The ((NH4)NO3 solution containing the zeolite was placed in the two-neck balloon and brought to the reflux system at 60°C for 24 h under constant agitation. The product obtained was centrifuged at 4000 rpm for 25 min, and the aqueous part was decanted. This procedure was repeated three times. After the ionic exchanges, the solid product was washed with distilled water and dried in the oven at 100°C for 16 h. The solid was calcined in the muffle using a heating branch of 350°C for 2 h and 500°C for 3 h.
In a beaker containing 0.05 g of tin oxide doped with Pt or with Pd, 0.01 g of ethylcellulose and 16
In order to prepare a thin layer of zeolite Y, 1,2-propanediol is used as a solvent following the procedure described by Vilaseca et al. [
The alumina plate including the printed electrodes is placed on a steel plate which in turn acts as a heater, replacing the four sensor heaters. This replacement allows a homogeneous heating. The way to obtain a homogeneous temperature is an innovative element, given that former sensors had its own resistance. This means a lower cost in terms of the heating process.
Table
Nomenclature of oxides prepared.
Nomenclature | Description |
---|---|
0.1% Pd/SnO2 | Tin oxide doped with 0.1% palladium |
0.1% Pt/SnO2 | Tin oxide doped with 0.1% platinum |
0.2% Pd/SnO2 | Tin oxide doped with 0.2% palladium |
0.2% Pt/SnO2 | Tin oxide doped with 0.2% platinum |
M1 0.1%/SnO2 | Tin oxide doped with a mixture of palladium and platinum (0.25 Pd/0.75 Pt) at 0.1% of metals in its entirety |
M2 0.1%/SnO2 | Tin oxide doped with a mixture of palladium and platinum (0.50 Pd/0.50 Pt) at 0.1% of metals in its entirety |
M3 0.1%/SnO2 | Tin oxide doped with a mixture of palladium and platinum (0.75 Pd/0.25 Pt) at 0.1% of metals in its entirety |
M1 0.2%/SnO2 | Tin oxide doped with a mixture of palladium and platinum (0.25 Pd/0.75 Pt) at 0.2% of metals in its entirety |
M2 0.2%/SnO2 | Tin oxide doped with a mixture of palladium and platinum (0.50 Pd/0.50 Pt) at 0.2% of metals in its entirety |
M3 0.2%/SnO2 | Tin oxide doped with a mixture of palladium and platinum (0.75 Pd/0.25 Pt) at 0.2% of metals in its entirety |
From the FTIR (Figures
FTIR for oxides doped to 0.1%.
FTIR of 1000–2500 cm−1 range for oxides to 0.1%.
FTIR of 1000–0 cm−1 range for oxides to 0.1%.
The band at 1615 cm−1 corroborates the presence of the hydroxyl group due to sample moisture. Apparently, the palladium and platinum charges in the tin oxide are not composing any bond or distorting the bonds of the tin oxide.
Table
Surface area of SnO2 doped with Pd and/or Pt.
Sample | Surface area (m2/g) | Microporous area (m2/g) | Mesoporous area (m2/g) |
---|---|---|---|
0.1% Pt/SnO2 | 7 | — | 7 |
M1 0.1%/SnO2 | 11 | — | 11 |
M2 0.1%/SnO2 | 12 | — | 12 |
M3 0.1%/SnO2 | 7 | 2 | 5 |
0.1% Pd/SnO2 | 7.5 | 0.5 | 7 |
0.2% Pt/SnO2 | 7.5 | — | 7.5 |
M1 0.2%/SnO2 | 7 | — | 7 |
M2 0.2%/SnO2 | 8.7 | — | 8.7 |
M3 0.2%/SnO2 | 7.5 | 0.5 | 7 |
0.2% Pd/SnO2 | 8 | — | 8 |
According to the International Union Pure and Applied Chemistry (IUPAC), classification isotherms (Figures
Adsorption-desorption isotherms of N2 for oxides of 0.1%.
Adsorption-desorption isotherms of N2 for 0.2% oxides.
As previously stated and observing that for low relative pressure values (
It is well known that SnO2 has a tetragonal structure with six atoms (2 Sn and 4 O) per unit cell [
RAMAN spectra of SnO2 doped at 0.1% Pd and/or Pt.
RAMAN spectrum of the SnO2 doped at 0.2% Pd and/or Pt.
If there are no changes in the spectrum, like other peaks, it may be due to the little disorder in the SnO2 that exists when low percentages of Pd and/or Pt are incorporated. Among the possible ways in which palladium and platinum can be found is that of metal-oxide clusters [
Palladium has an ion ratio (86 A) which is larger than the platinum one (80 A) so if it were in a higher concentration, we could observe a disorder generated in the tin oxide network.
This would be corroborated by the decrease in the intensity of the palladium peaks [
Using the FRX technique, palladium and platinum have been found in samples of tin oxide that are only doped with palladium and platinum. Although palladium and platinum were observed in M1, the other samples only registered one of these elements. It is possible that the platinum signal can no longer be seen at concentrations lower than 0.05% or an overlap of the palladium spectrum is also occurring with it. It was possible to identify transitions L1 (11–0711 eV)
In a previous study, and in order to select the samples, Peruvian wines were analyzed with gas chromatography (GC). The findings showed that the compounds that characterized the wine aroma were ethanol, 1 phenyl ethanol, and propanoic acid, which were selected due to their highest average concentrations. In winemaking, acetic acid was selected as the most important product of the process of fermentation.
In this study, the Agilent Technologies 7890A gas chromatograph coupled to the Agilent Technologies 5975 selective mass detector and HP-FFAP polar capillary column (30 m × 250
The sensing process used a static system. Vacuum was applied in an airtight bubbler, and steam was extracted from the sample, which was carried by the pneumatic system to the gas chamber, where the sensor array was located. Then, applying a data acquisition card, the detection was monitored on the sensors by a computer. There, we observed the voltage variation for each sensor while they were in contact with the sample.
Sensitivity is measured by calculating the difference between the two signals, the baseline signal, and the signal of the plateau.
Sensitivity of wine aroma compounds is measured following these steps: The sample is placed in a container Vacuum is made with a pump and the aroma compound (sample) is carried through a pneumatic system The sample reaches the sensor surface and is detected
Table
Sensitivity of sensors based on oxides prepared.
Compounds | 0.1% (Pt) | M1 0.1% | M2 0.1% | M3 0.1% | 0.1% (Pd) | 0.2% (Pt) | M1 0.2% | M2 0.2% | M3 0.3% | 0.2% (Pd) |
---|---|---|---|---|---|---|---|---|---|---|
Ethanol 12% (et) | 2 | 0.75 | 1.5 | 0.3 | 0.25 | 0.2 | 0.5 | 2.5 | 0.55 | 0.2 |
Methanol 3% (met) | 0.5 | 0.4 | 0.9 | 0.35 | 0.4 | 0.1 | 0.25 | 1.4 | 0.25 | 0.1 |
Mixture (ethanol 12%/methanol 3%) (et12met3) | 0.75 | 1.8 | 2.8 | 1.2 | 0.5 | 0.35 | 0.8 | 3.2 | 0.8 | 0.35 |
1 Phenyl etanol ( |
0.2 | 0.18 | 0.4 | 0.25 | 0.05 | 0 | 0.2 | 1.2 | 0.2 | 0 |
Propionic acid ( |
0.7 | 0.55 | 0.95 | 0.55 | 0.1 | 0.05 | 0.2 | 1.6 | 0.2 | 0 |
Acetic acid ( |
0.6 | 0.25 | 0.5 | 0.25 | 0.1 | 0.05 | 0.15 | 1.1 | 0.15 | 0 |
The order of detection in most of the cases is as follows (considering that sensors at 0.1% are the most stable): mix 12% ethanol/methanol 3% > 12% ethanol > propionic acid > 3% methanol > acetic acid > 1 phenyl ethanol.
Most of the cases show that the mixture of ethanol and methanol obtains higher values of voltage than the sum of the two detections, so it must be said that a synergic effect is occurring.
The data obtained by the sensitivity measurements using electronic noses with composite sensors were processed using the principal component analysis (PCA).
Figures
PCA of wine volatile compounds obtained using an e-nose with sensors doped with palladium and platinum at 0.1% and 0.2%.
PCA of wine volatile compounds obtained using an e-nose with sensors doped with a mixture of palladium and platinum at 0.1%.
PCA of wine volatile compounds obtained using an e-nose with sensors doped with a mixture of palladium and platinum at 0.2%.
PCA of wine volatile compounds obtained using an e-nose with sensors doped with palladium and/or platinum with zeolite Y at 0.1% and 0.2%.
Tin oxide doped with a mixture of palladium and platinum shows results as good as those obtained from doped oxides with platinum. This mixture implies a cost reduction because platinum is more expensive than palladium.
Previously, sensors doped with palladium and platinum were used in order to increase the active sites for the detection of the substance to be analyzed. However, the platinum, which shows the best results, is very expensive. So we try to mix it with palladium, which is less expensive. In order to find a composite with better sensorial properties, we experimented with mixtures of palladium and platinum at different percentages (M1, M2, and M3).
Mixture M2 at 0.1% and 0.2% showed sensorial properties similar to Pt/SnO2 at 0.1%. In addition, PCA and the total variance of the PCAs corroborated the results mentioned above.
For PCA mixtures at 0.2%, the results are not as good as the former PCAs, but it tends to a parabolic drift (displacement of the points of the same sample), which is not common.
The correlations of the data tend to zero, as well as the squared cosines. Both indicate the independence of the variables. Therefore, the samples of wine volatile compounds are different, and the objective of replacing sophisticated techniques such as gas chromatography is achieved basing on PCA results and e-nose device.
The use of zeolite Y to modify the sensors is a novel contribution for this research.
It is important to mention that sensors modified with zeolite Y allow the differentiation and/or transformation of compounds of the same mixture.
In this way, the system would have two parts: a sensor or sensing element (SnO2) and the transforming element in order to modify or restrict the composition of the gas under analysis, so that it is ready to interact with the sensor element [
The zeolites are composed of a tetrahedron structure TO4 (
Zeolites are used to improve the selectivity, because this is a problem that common sensors usually have to face, that is, a mixture in which other molecules can interfere, such as water: On the one hand, there is the action of the zeolites as molecular sieves. In this case, the fact that zeolites are crystalline solids with fixed-dimension channels can be used to exclude molecules whose sizes are larger than that of the zeolite pore On the other hand, zeolites are capable of having specific interactions with some molecules of the gaseous mixture, using mainly selective adsorption mechanisms.
Zeolite Y consists of a skeleton of SiO4 and AlO4 tetrahedral bonded by oxygen atoms, as mentioned above. Its chemical formula is 0.9 Â ± 0.2 Na2O : Al2O3 :
In general, the method was accepted, especially in the case of zeolite-modified sensors, and we can trust the results due to low correlations as well as the low values of the square cosines.
Previous studies [
It is very likely that for the case of ethanol (the molecule with which the zeolite-modified sensor increases its sensitivity), there is a donation of a proton from the acid site of the zeolite to ethanol, causing an electron release to the surface of the semiconductor oxide and an increase of the conduction.
The electronic nose allowed classifying the aroma components such as ethanol and organic acids, among others.
The M2 0.1% (yin oxide doped with a mixture 0.50 Pd/0.50 Pt, at 0.1% of metals) showed a very good sensitivity as much as that of the oxide 0.1% Pt.
The sensors array modified with zeolite Y showed a good performance.
We can conclude that a good differentiation of volatile compounds of wine aromas can be obtained from a nose with 4 sensors, in spite of its simplicity. It is possible to affirm that this sensor array could be applied to differentiate samples of a wine or a group of wines.
The multivariate data analysis, PCA, allowed interpreting the results.
The authors declare that the data are not included because it belongs exclusively to the project 159-2015-FONDECYT, which is sponsored by CONCYTEC-FONDECYT.
The authors declare that there are no conflicts of interest regarding the publication of this paper.