Journal of Nanomaterials

Volume 2013 (2013), Article ID 201845, 4 pages

http://dx.doi.org/10.1155/2013/201845

Research Article

A Novel Technique for the Synthesis of Nanodiamond Powder

Leiming Fang,1,2 Hiroaki Ohfuji,² and Tetsuo Irifune²

¹Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900, China

²Geodynamics Research Center, Ehime University, Matsuyama 790-8577, Japan

Received 15 March 2013; Accepted 8 May 2013

Academic Editor: Ping Xiao

Copyright © 2013 Leiming Fang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

We developed a novel technique to synthesize nanodiamond powder through the decomposition of graphitic C₃N₄ under high pressure and high temperature. The nanodiamond obtained by the present method is in an extremely pure form with no sp² carbon contaminations. Individual nanodiamond grains are very uniform in size and virtually monodispersed single crystals. The grain size can be controlled from less than 1 nm to several hundred nanometers by adjusting the heating temperature (and also potentially by controlling pressure) used for the synthesis. The present product requires neither post-surface treatment to remove outer shell made of sp² carbons nor deglomeration and size classification unlike the case for nanodiamond obtained by the conventional TNT detonation method.

1. Introduction

Nanodiamond powder has been adopted for many industrial uses such as for polishing, coating, lubricant additives, and catalysts due to its excellent thermal and chemical stability combined with the superhard nature [1]. Due to the properties of nontoxicity and high biocompatibility, it has also attracted considerable attention on some new applications, especially in the biomedical field (i.e., imaging, diagnostics, and drug or gene delivery) [2, 3]. To date, the major commercially available technique for nanodiamond powder synthesis is the trinitrotoluene (TNT) detonation method. In this technique, nanodiamond crystals with grain sizes in nanometric ranges were obtained as a result of incomplete combustion of the explosive (TNT) in a closed container. The detonation process is so complex and instantaneous that the indisputable mechanism of nanodiamond formation during detonation has not been put forward so far, although several models have been suggested [4, 5]. The detonation nanodiamond usually consists of a diamond core of 2–4 nm in diameter and an outer surface composed of a graphitic shell or amorphous carbon, which is dominated by dangling bonds. Although the presence of such disordered sp² carbon and surface dangling bonds can be utilized from the viewpoint of functionalization, it is rather unfavorable because it causes strong agglomeration of primary nanodiamond particles (<10 nm), forming secondary clusters up to 100 nm or even larger [3]. In order to fully utilize the intrinsic feature of nanodiamond itself, deaggregation into individual primary particles is often needed. Ozawa et al. [6], for example, demonstrated that mechanical milling using ceramic micro-beads combined with ultrasonic vibration is effective for the deglomeration. However, such mechanical milling may result in chemical/physical contamination by the milling media, and therefore deglomeration of detonation nanodiamond particles is still a challenging task [7].

Here we report a novel technique to produce nanodiamond powders based on a static high pressure and high temperature method. The nanodiamonds obtained by this technique are extremely pure with no contamination of sp² carbon phases and equigranular single crystal particles in a virtually monodispersed state.

2. Experimental Method

Nanodiamond powder synthesis was conducted by high-pressure experiments using a 2000t multianvil apparatus (ORANGE-2000) at Ehime University. WC anvils of 4 mm truncation edge-length and MgO pressure medium (octahedron) of 10 mm edge-length were used. Platinum capsule was used to seal the samples thoroughly during high P-T experiments. The details of the cell assembly used were described in our earlier report [8]. The starting material used was graphitic C₃N₄ (g-C₃N₄) prepared by a benzene-thermal reaction between C₃N₃Cl₃ and NaNH₂ at 220°C for 12 hours by following the method described in [9]. The g-C₃N₄ obtained in such a way is a light yellowish-brown powder of amorphous-like, poorly crystalline particles [8]. The sample was compressed to a desired pressure at room temperature, heated to 800–2000°C for 5–30 min, and then quenched and decompressed to ambient condition. The recovered samples were first analyzed by microfocus X-ray diffraction (Bruker AXS, M21X) and Raman (Renishaw, RS-SYS1000) for phase identification and then examined by field-emission scanning electron microscopy (FE-SEM: JEOL, JSM-7000F) and transmission electron microscopy (TEM: JEOL JEM-2010) for microtexture observation.

3. Results and Discussion

In the present study, all the nanodiamond samples were obtained through the decomposition of g-C₃N₄ at high P-T conditions. After pressure release, a sample container made of platinum was taken out from the cell, and one of the capsule ends was carefully cut open by using a sharp razor. Note that there is clearly a space (gap) between the white diamond powders compacted in a cylindrical form and the surrounding platinum capsule (Figure 1(a) inset). This opening space is probably derived from the liquid nitrogen that had been formed through the decomposition of g-C₃N₄ at high temperature but was vaporized and released to the air during decompression. In fact, the phase stability diagram for pure nitrogen obtained through experimental studies [10] shows that nitrogen melts to form N₂ above 700–1000 K in the studied pressure range (15–25 GPa). Therefore, the diamond powders produced in the present study are considered to crystallize in liquid nitrogen regime.

(a)

(b)

Figure 1: The variation of XRD (a) and Raman (b) patterns collected from the samples heated to different temperatures at 22 GPa, respectively. Inset in (a) is a microscopic image of diamond nanopowder enclosed in a Pt capsule (recovered from 1600°C).

Figure 1 shows X-ray diffraction patterns and micro-Raman spectra collected from the samples synthesized at 1000, 1400, and 1600°C at 22 GPa. The XRD result shows that diamond is the only phase found in the sample containers, although a few peaks forming the surrounding platinum capsule were also detected. The observed diamond 111 and 220 peaks are considerably broad and weak at 1000°C but become sharper and more intense with increase in heating temperature, suggesting a remarkable grain growth of the diamond crystals formed. It is also seen that the nanodiamonds obtained from 22 GPa apparently show broader peaks than those at 15 GPa, suggesting that the higher the synthesis pressure, the smaller the grain sizes of the diamond crystals formed.

The Raman spectrum of the sample quenched from 1000°C at 22 GPa shows continuous broad bands ranging from 1400 to 1600 cm⁻¹, which implies the presence of minor amounts of disordered (amorphous) carbon species such as diamond-like carbon [11] in addition to poorly crystalline diamond, while those of the samples recovered from 1400 to 1600°C are characterized by the diamond vibration mode centered at 1331 cm⁻¹ (Figure 1(b)). The diamond Raman peak becomes sharper and more intense as the heating temperature increases, again suggesting significant grain growth of the crystals with temperature increase.

We also examined the nanodiamond products by transmission electron microscopy. Figure 2 shows TEM images of the nanodiamond samples synthesized at 1000–1600°C and 22 GPa. The product obtained from 1000°C was found to be so fine and poorly crystalline (Figure 2(a)) that individual crystals cannot be recognized even at the high magnification (Figure 2(b)). The selected area electron diffraction (SAED) pattern collected from a local area of 1.2 μm diameter shows two faint but continuous diffraction rings which can be indexed as 111 and 220 reflections of diamond, indicating a randomly oriented, amorphous-like feature of the product. On the other hand, the diamond crystals synthesized at temperatures above 1400°C show well-developed euhedral morphology with grain sizes ranging from several tens of nanometers to a half of micrometer as the heating temperature increases from 1400 to 1600°C (Figures 2(c) and 2(d)). SAED pattern analysis and high-resolution imaging also showed that these individual grains are purely single crystals of diamond with no graphite/amorphous carbon phases. It is also important to note that the nanodiamond crystals synthesized at a given pressure and temperature are remarkably uniform and all discrete unlike those produced from the TNT detonation methods.

(a)

(b)

(c)

(d)

Figure 2: TEM images of nanodiamond samples recovered from different temperatures at 22 GPa: (a) 1000°C, (b) high-resolution image of (a), (c) 1400°C, and (d) 1600°C.

Figure 3 shows the relationship between heating temperature and grain size of diamond produced at different pressures. It is clearly seen that the grain size of diamond crystals increases drastically (i.e., almost linearly in a log scale) from ~1 nm to 1 μm with increasing heating temperature. There also seems to be a pressure effect that the higher the pressure the larger the grain size of the diamond synthesized. Such a pressure effect can be interpreted in terms of the difference in activation energy required for the diamond nucleation at different pressures. In the theory of crystallization (e.g., [12]), the critical nucleus size (i.e., minimum size required to energetically stabilize the initial nuclei) generally decreases with increase in pressure. In other words, at higher pressure the rate of nucleation tends to become predominant over the rate of the subsequent crystal growth, resulting in the formation of smaller crystals than the case at lower pressure.

Figure 3: The relationship between grain size and heating temperature of diamond produced at different pressures.

Nanodiamond powders synthesized by the present high pressure and high temperature (HPHT) technique have some advantages over those obtained by the conventional TNT detonation method: nanodiamond by HPHT technique is a purely single phase of diamond with virtually no sp² carbon contamination (although the product synthesized at 1000°C and 22 GPa likely contains a minor amount of sp² carbon species as shown by its Raman spectrum), while detonation diamond occurs in the form of aggregated particles whose outermost layer is usually covered by sp² (graphitic/amorphous) carbons. This means that the nanodiamond prepared by the present technique does not require post-surface treatment unlike the latter case and can be used for various applications in the as-synthesized form. In addition, in the former case individual grains are dispersed single crystals of a uniform size range, which can be readily controlled by changing the heating temperature for synthesis; that is, deglomeration processing and particle size classification are also not necessary. Taking into account these superior features, nanodiamond synthesized by the present method is expected to expand the range of potential applications in various fields.

4. Conclusions

We found a new technique to synthesize diamond nano-powders through the decomposition of graphitic C₃N₄ under HPHT. Compared with nanodiamond obtained by the conventional TNT detonation method, the present product exhibits some outstanding features and advantages; it is purely a single phase of diamond with no sp² carbon contamination, it occurs substantially as monodispersive crystals of a uniform size range, and the grain size can be controlled by adjusting heating temperature for the synthesis. This means that the nanodiamond obtained by the present method requires neither post-surface treatment to remove sp² carbon outer shell nor deglomeration and size classification, which should be routinely performed for detonation nanodiamond. This novel method is important and helpful for producing high-purity nanodiamond powder and its potential applications in various fields.

Acknowledgments

This work was conducted in Geodynamics Research Center, Ehime University, Japan, and was supported by the Global COE program “Center for Advanced Experimental and Theoretical Deep Earth Mineralogy”. It was also supported partly by Grant-in-Aid for Young Scientists (B) (no. 20740255, representative: H. Ohfuji) from the Ministry of Education, Science and Culture, Japan, and also by Grant-in-Aid for Specially Promoted Research (no. 20001005, representative: T. Irifune) from the Japan Society for the Promotion of Science. The authors thank T. Shinmei of Ehime University for his technical support in performing the experiments.

References

A. Krueger, “Diamond nanoparticles: jewels for chemistry and physics,” Advanced Materials, vol. 20, no. 12, pp. 2445–2449, 2008.

A. M. Schrand, S. A. C. Hens, and O. A. Shenderova, “Nanodiamond particles: properties and perspectives for bioapplications,” Critical Reviews in Solid State and Materials Sciences, vol. 34, no. 1-2, pp. 18–74, 2009.

V. N. Mochalin, O. Shenderova, D. Ho, and Y. Gogotsi, “The properties and applications of nanodiamonds,” Nature Nanotechnology, vol. 7, no. 1, pp. 11–23, 2012.

V. V. Danilenko, “Nanocarbon phase diagram and conditions for detonation nanodiamond formation,” in Synthesis, Properties and Applications of Ultrananocrystalline Diamond, D. M. Gruen, O. A. Shenderova, and A. Y. Vul, Eds., vol. 192, pp. 181–198, Springer, New York, NY, USA, 2005.

V. Y. Dolmatov, “On the mechanism of detonation nanodiamond synthesis,” Journal of Superhard Materials, vol. 30, no. 4, pp. 233–240, 2008.

M. Ozawa, M. Inaguma, M. Takahashi, F. Kataoka, A. Krüger, and E. Osawa, “Preparation and behavior of brownish, clear nanodiamond colloids,” Advanced Materials, vol. 19, no. 9, pp. 1201–1206, 2007.

E. Osawa, “Recent progress and perspectives in single-digit nanodiamond,” Diamond and Related Materials, vol. 16, no. 12, pp. 2018–2022, 2007.

L. Fang, H. Ohfuji, T. Shinmei, and T. Irifune, “Experimental study on the stability of graphitic C₃N₄ under high pressure and high temperature,” Diamond and Related Materials, vol. 20, no. 5-6, pp. 819–825, 2011.

Q. Guo, Y. Xie, X. Wang, S. Lv, T. Hou, and X. Liu, “Characterization of well-crystallized graphitic carbon nitride nanocrystallites via a benzene-thermal route at low temperatures,” Chemical Physics Letters, vol. 380, no. 1-2, pp. 84–87, 2003.

D. A. Young, C. S. Zha, R. Boehler et al., “Diatomic melting curves to very high pressure,” Physical Review B, vol. 35, no. 10, pp. 5353–5356, 1987.

C. L. Guillou, F. Brunet, T. Irifune, H. Ohfuji, and J. N. Rouzaud, “Nanodiamond nucleation below 2273 K at 15 GPa from carbons with different structural organizations,” Carbon, vol. 45, no. 3, pp. 636–648, 2007.

F. Ye and K. Lu, “Crystallization kinetics of amorphous solids under pressure,” Physical Review B, vol. 60, no. 10, pp. 7018–7024, 2009.