In order to fabricate the titanium dioxide (TiO2) nanotubes arrays which were used in the photocatalytic degradation of total volatile organic compounds (TVOC) by anodization, the influence of the electrode gap and anode area on the morphology of the titanium dioxide (TiO2) nanotubes was studied. Titanium dioxide (TiO2) nanotube arrays were prepared by anodization with various electrode gaps and anode areas. Field emission scanning electron microscopy was used to investigate the morphology of the TiO2 nanotubes arrays. The results showed that the morphology of TiO2 nanotubes arrays was influenced by electrode gap and anode area. The appropriate anode area and electrode gap were 5 cm × 2 cm and 20 mm, respectively. Thus, TiO2 nanotube arrays with better morphology (with larger dimension and uniform TiO2 nanotubes) were successfully fabricated by anodic oxidation with 5 cm × 2 cm anode area and 20 mm electrode gap at 30 V.
1. Introduction
TiO2 nanotube arrays are extensively studied for water and air purification because of their nontoxicity, chemical stability, and superior photocatalytic activity [1–9]. TiO2 nanotube arrays can be fabricated by many different methods such as hydrothermal treatment [10–13], template-assistant deposition [14, 15], and electrochemical anodization [16–21]. The anodization method is a simple and effective technique for the rapid preparation of aligned TiO2 nanotubes due to the unnecessity of vacuum and high temperature [20, 22–26]. Moreover, Using anodic oxidation, TiO2 is formed with a chemical bond between the oxide and Ti substrate; TiO2 nanotube arrays have a strong combination with Ti substrate, which provides convenience for TiO2 reusability [27, 28]. In addition, the architecture of the nanotubes by the anodization method can be easily modified by manipulating the anodizing environments [29–31].
Owing to its wide band gap (3.2 eV for anatase), anatase TiO2 can only be excited under ultraviolet irradiation. However, this section occupies only less than 5% of the solar irradiance at the Earth’s surface. For the sake of efficient use of sunlight, enlarging the absorption band border of TiO2 may be an appealing challenge for developing the future generation of photocatalysts. The improvement of photocatalytic efficiency by modifying TiO2 has been focused on for a long time [32, 33]. Coupling TiO2 with a small band-gap semiconductor or doping with transition metal ions such as V, Cr, Mn, Fe, Co, Ni, or Cu extends the absorption spectrum range and improves the efficiency of photocatalyst [34–37]. Yang et al. [38] recently assembled Cu2O nanoparticles on the top surface of the TiO2 nanotube arrays (TNAs) by anodizing method. However, these Cu2O nanoparticles were supported mainly on the top surface of the TNAs, leading to insufficiently effective electron pathways between the Cu2O and TiO2. Therefore, in order to deposit these nanoparticles into the inner and external walls of the nanotubes uniformly, highly structured and orderly arranged TiO2 nanotube arrays with larger pore size must be prepared.
The morphology and the structure of nanotubes are affected strongly by the electrochemical conditions (particularly the anodization voltage) and the solution parameters (in particular the HF concentration, the, pH and the water content in the electrolyte) [39]. Many researchers [3, 9, 26, 31, 40, 41] varied the parameters such as anodization potentials and anodization durations to fabricate the specific morphology of TiO2 nanotubes arrays (TNAs). Kim et al. [42] and Paulose et al. [43] demonstrated that the morphology of nanotubes is strongly influenced by the applied potential, and water content of electrolytes. Several reports [17, 41, 44–46] have shown that F- is crucial to the formation of nanotubular structures, and diluted F- electrolyte is preferred. To increase the nanotubular length, organic and viscous electrolytes have been experimented utilizing ethylene glycol or glycerol [47–49]. A review of the literature related to TiO2 nanotube arrays reveals no published study on the effects of the anode area and electrode gap on the morphology and the structure of the resulting TiO2 nanotube arrays.
In this work, we report the effect of different anode areas and electrode gaps on the morphology of fabricated TiO2 nanotubes in ethylene glycol (EG) electrolytes containing ammonium fluoride (NH4F) and H2O. The microstructures of the samples are investigated by field emission scanning electron microscopy (FE-SEM).
2. Experimental2.1. Materials
Titanium foils (0.2 mm thick, 99.95% purity) were mechanically polished by different abrasive papers (600#, 1000#, 1200#, and 1800#) then followed by sonicating acetone, ethanol, and deionized water for 30 min. respectively. Then the titanium foils were dried at room temperature in air. All the other chemicals were of analytical grade and used as received without further purification.
2.2. Preparation of TiO2 Nanotube Arrays
A two-electrode polyethylene plastic cell (V=300mL) was used to perform the anodization process. The pretreated Ti foil was used as an anode and Pt sheet as the cathode. Both electrodes were immersed in 200 mL organic electrolyte containing 0.4wt.% NH4F, 5 vol.% H2O, and 95 vol.% ethylene glycol (EG). All electrolytes were prepared from analytical grade and deionized water (>18 M Ω cm). Ti foil was cut into 5cm×0.5cm, 5cm×1cm, 5cm×2cm, and 5cm×4cm, with 4cm×0.5cm, 4cm×1cm, 4cm×2cm, and 4cm×4cm areas exposed to the bulk electrolyte, respectively. The applied voltages were set to 10, 20, and 30 V by a DC power source (DH1718E-4), respectively. The electrochemical experiments were carried out at room temperature (~28°C), and the electrolyte was kept uniform with constant magnetic stirring, the stirring speed was kept constant at ~180 rpm. The specimens were anodized for 1 h. under different electrochemical conditions. The detailed electrochemical conditions are listed in Table 1. The anode area and electrode gap were changed for the systemic investigation of the formation of TiO2 nanotubes. The as-anodized samples were rinsed with deionized water and dried in air.
Electrochemical conditions and the morphologies of the samples.
Exp.
Anode area (cm2)
Electrode Gap (mm)
Applied voltage (V)
Average diameter (nm)
Length (μm)
1
5 × 0.5
Without nanotube
2
5 × 1
20
20±5 (with crannies)
—
3
5 × 2
15±5
—
4
5 × 4
10
Without nanotube
5
5
Without nanotube
6
10
15±5 (with crannies)
—
7
5 × 2
40
Without nanotube
8
20
20
75±5
1.0±0.2
9
30
180±20
2±0.4
2.3. Characterization Technique
The surface morphologies of obtained samples were observed using field emission scanning electron microscope (FE-SEM, Hitachi S-4800). Direct SEM cross-sectional observations were carried out on flat and cracked samples.
3. Results and Discussion3.1. Influence of Anode Area on the Top Morphology of TiO2 Nanotube
The TiO2 nanotubes formation mechanism includes the following processes [50–52].
Formation of oxide layer at the surface of the metal takes place due to interaction of the metal with O2- or OH- ions. After the development of an initial oxide layer, these ions move through the oxide layer towards the metal/oxide interface where they react with the Ti metal. The reaction can be represented as follows:(1a)Ti-4e-⟶Ti4+(1b)O2+4e-⟶2O2-(1c)Ti4++2O2-⟶TiO2(1d)Ti4++2OH-⟶TiO2+2H+.
Field-assisted dissolution of Titanium oxideMetal ion (Ti4+) transfer from the Ti metal at the metal/oxide interface by ejection under application of an electric field and migrate towards the oxide/electrolyte interface. Ti4+ cations dissolve into the electrolyte, and the free O2- anions transfer towards the metal/oxide interface to interact with the Ti metal. The field-assisted dissolution of titanium oxide is represented by the following reaction:
(2)TiO2⟶Ti4++2O2-.
Chemical dissolution of the Ti metal or oxide also occurs due to the acidic and fluorine contained electrolyte, which then causes more etching at the pore-bottom than at the opening and the walls. Therefore, in the early stages of the anodization process, small pits are formed. The formation of these small pits is represented by the following reaction:
(3)TiO2+6F-+4H+⟶TiF62-+2H2O.
Therefore, the growth and propagation of the pores occur by inward movement at the oxide/metal interface, which is determined by the amount of fluorine on the anode surface and the degree of electric field. Figure 1 shows the surface images of the samples during anodization of titanium at 10 V in 0.4wt% NH4F + 5wt% H2O EG solution with different anode areas. With 5cm×0.5cm anode area, the top of the sample is covered by much debris, and no nanotube is found on the surface (Figure 1(a)). We suppose that with a smaller anode area, the current density and the field effect are too high. Thus, the higher electric field would polarise and weaken Ti-O bond resulting in dissolution of oxide rapidly before small pores formation. In addition, the rate of the chemical dissolution on the anodes of the smaller area is higher due to the more fluoride ions per anode unit area, resulting in dissolution of oxide rapidly before small pores formation. With 5 cm × 1 cm anode area, the surface morphologies consist of ring-like structures whose the openings are around 20 nm in diameter, and numerous crannies are observed on the surface (Figure 1(b)). The samples prepared with 5 cm × 2 cm anode at 10 V (Figure 1(c)) consist of a ring-like structure with diameter of less than 20 nm, no debris and crannies are found on the surface. At the initial stage of anodisation, the rate of the field-assisted dissolution on the anodes of different area is equal due to the same applied voltage, while the rate of the chemical dissolution on the anodes of the larger area is lower due to the less fluoride ions per anode unit area, which results in the oxide thickness reduction being slower on the larger area anode [53]. As the anodisation proceeds and oxide thickens, the rate of the field-assisted dissolution on the larger area anode decreases faster than that of the smaller area anode [53]. So, we can speculate that with the increase of the anode area, the electric field-assisted dissolution of the oxide is weakened, the chemical dissolution dominates electric field-assisted dissolution, and the growth and propagation of the tubes occur by inward movement at the oxide/metal interface, thereby forming nanotubes. At the meantime, when the current density is beyond certain value, electric field-assisted dissolution is believed to occur too rapidly, polarizing and weakening the Ti-O band not only at the bottom part of the nanotubes but also along the longitudinal direction of the nanotubes as well; hence more crannies are produced.
FE-SEM images of the surface morphology of TiO2 nanotube arrays formed at 10 V in ethylene glycol containing 0.4wt% NH4F and 5wt% H2O electrolyte for 1 h. with different anode areas: (a) 5 cm × 0.5 cm, (b) 5 cm × 1 cm, (c) 5 cm × 2 cm, and (d) 5 cm × 4 cm.
As shown in Figure 1(d) for the 5 cm × 4 cm anode area, the TiO2 layer is more compact and only some small pits disperse sparsely, no nanotubes are observed; however, Ti is partly etched. Under this condition, the anode area is too large, resulting in the fact that the amount of fluorine ions per square centimeter at the anode surface is less, the rate of the reaction (3) decreases rapidly [54]; thus, the TiO2 layer is thicker, which results in less electric field dissolution [53]. Therefore, the formation of nanotubes by anodization fails. The appreciate anode area for TiO2 nanotube formation is, therefore, around 5 cm × 2 cm in the 200 mL 0.4wt% NH4F + 5wt% H2O EG solution.
3.2. Influence of Electrode Gap on the Top Morphology of TiO2 Nanotubes
Figure 2 shows the surface images of TiO2 nanotubes prepared with different electrode gaps. When the electrode gap is 5 mm, the morphology which is covered by the thicker oxide layer with severely localized shedding is observed (Figure 2(a)). Because the smaller electrode gap is, the solution resistance between electrodes is lower, the rate O2− or OH− ions to the anode increase; therefore, the rate of the reactions (1a), (1b), (1c), and (1d) is higher; that is, the formation of TiO2 layer is faster. On the other hand, the F− ions quickly reach the anode and the Ti4+ ions quickly leave the anode, resulting in the fact that the chemical dissolution and electric field dissolution of the TiO2 layer rapidly occur. So the oxide layer on the sample surface is etched severely. Samples anodized at a 10 mm electrode gap consist of a ring-like structure with a diameter of <30 nm and some crannies (Figure 2(b)). With increased electrode gap, the rate of the TiO2 layer formation and dissolution is slowed down. Under this condition, the reaction (3) on the bottom of the pits continues, so lots of ring-like structures occur, but the higher the electric field intensity due to the smaller electrode gap results in stronger field-assisted dissolution of TiO2 on the sample surface. Therefore, there are lots of TiO2 crannies on the sample surface. Increasing the electrode gap to 20 mm, Figure 1(c) shows the ring-like structure without any cranny on the sample surface. The inward movement rate of the oxide/metal interface is approximately equal to the rate of the reaction (3). So, a discrete, hollow-like cylindrical structure was formed which developed into the nanotubular structure with diameters of <20 nm. At the meantime, with decreased electric field intensity, the electric field dissolution of the oxide occurs much slower, thus without forming crannies on the surface. At 40 mm electrode gap (Figure 2(c)), the TiO2 layer is more compact and many pit structures are observed. Under this condition, the higher electrical resistance due to the larger electrode gap results in that the inward movement rate of the F− ions is decreased, only small pits are formed without any nanotubes on the surface. And the weaker electric field dissolution due to the smaller electric field intensity does not generate crannies on the sample surface.
FE-SEM images of the surface morphology of TiO2 nanotube arrays formed at 10 V in ethylene glycol containing 0.4wt% NH4F and 5wt% H2O electrolyte for 1 h. with different electrode gaps: (a) 5 mm, (b) 10 mm, and (c) 40 mm.
According to the aforementioned experiments, it is inferred that samples anodized with 20 mm electrode gap will suffer from appreciate chemical and electric field dissolution forming nanotube structure with smaller diameter with the ratio of electrode area to electrolyte volume being 0.05 cm−1. Under this condition, anodisation experiments at higher voltages (20 V, 30 V) were carried out to seek the possibility of increasing the length and diameter of the nanotubes further. Surface morphologies of TiO2 formed at 20 V and 30 V are shown in Figures 3(a) and 3(b) when the samples are anodized for 1 h. The surface morphologies consist of ring-like structures related to the opening of nanotubes. The insets are the cross-sectional images and higher magnifications of the same sample. The length of the nanotubes increases from 1 μm to 2.4 μm, and the diameter of the nanotubes increases from 70 nm to 200 nm for samples anodized at 20 and 30 V, respectively. As reported by Lockman et al. [53], pore growth occurs at a higher voltage, thereby increasing the length and diameter of the nanotubes, but the nanotubes structure starts to be deteriorated at 25 V and is completely lost at 30 V. Therefore, the joint effect of electrolysis conditions such as voltage, electrode area, electrode gap, composition of the electrolytic solution, and temperature on the nanotubes morphologies needs to be studied further.
FE-SEM images of the surface morphology of TiO2 nanotube arrays formed in ethylene glycol containing 0.4wt% NH4F and 5wt% H2O electrolyte at different voltages for 1 h. (a) 20 and (b) 30 V.
4. Conclusion
In conclusion, it is demonstrated that the surface morphology of TiO2 nanotube arrays which were used in the photocatalytic degradation of total volatile organic compounds (TVOC) can be modified by anodization of Ti foils in EG solution consisting of 0.4% NH4F and 5% wt H2O using the appropriate anode area and electrode gap. The effect of anode area and electrode gap on surface morphology of TiO2 nanotube arrays was investigated and the results of SEM show that the highly ordered TiO2 nanotube arrays cannot be formed with inappropriate anode area and electrode gap. Moreover, a detailed theoretical interpretation of the influence of anode area and electrode gap on the morphology of TNAs was introduced. With appropriate anode area 5 cm × 2 cm and electrode gap 20 mm, larger-dimension, and uniform TiO2 nanotube arrays were successfully formed after 1 h. of anodization of pure titanium foil in a two-electrode bath with 200 mL electrolyte solution at 30 V.
Acknowledgment
The work has been supported by Science and Technology Planning Project of the Ministry of Science and Technology of China (no. 2012BAB12B02).
NakataK.OchiaiT.MurakamiT.FujishimaA.Photoenergy conversion with TiO2 photocatalysis: new materials and recent applications201284103111ZhangA.ZhouM.HanL.ZhouQ.The combination of rotating disk photocatalytic reactor and TiO2 nanotube arrays for environmental pollutants removal20111862-3137413832-s2.0-7975153737010.1016/j.jhazmat.2010.12.022BaiJ.LiuY.LiJ.ZhouB.ZhengQ.CaiW.A novel thin-layer photoelectrocatalytic (PEC) reactor with double-faced titania nanotube arrays electrode for effective degradation of tetracycline2010983-41541602-s2.0-7795462457410.1016/j.apcatb.2010.05.024LiuH.LiuG.FanJ.ZhouQ.ZhouH.ZhangN.HouZ.ZhangM.HeZ.Photoelectrocatalytic degradation of 4,4′-dibromobiphenyl in aqueous solution on TiO2 and doped TiO2 nanotube arrays201182143472-s2.0-7865019478510.1016/j.chemosphere.2010.10.013MuramatsuY.JinQ.FujishimaM.TadaH.Visible-light-activation of TiO2 nanotube array by the molecular iron oxide surface modification2012119-1207480JiangF.ZhengS.AnL.ChenH.Effect of calcination temperature on the adsorption and photocatalytic activity of hydrothermally synthesized TiO2 nanotubes20122581871887194LiH.CaoL.LiuW.SuG.DongB.Synthesis and investigation of TiO2 nanotube arrays prepared by anodization and their photocatalytic activity201238757915797MacakJ. M.ZlamalM.KrysaJ.SchmukiP.Self-organized TiO2 nanotube layers as highly efficient photocatalysts2007323003042-s2.0-3384707686710.1002/smll.200600426LaiY.ZhuangH.SunL.ChenZ.LinC.Self-organized TiO2 nanotubes in mixed organic-inorganic electrolytes and their photoelectrochemical performance20095426653665422-s2.0-6924913339710.1016/j.electacta.2009.06.029KasugaT.HiramatsuM.HosonA.SekinoT.NiiharaK.Titania nanotubes prepared by chemical processing1999111513071311ChenQ.ZhouW.DuG. H.PengL. M.Trititanate nanotubes made via a single alkali treatment2002141712081211TsaiC. C.TengH.Regulation of the physical characteristics of titania nanotube aggregates synthesized from hydrothermal treatment20041622435243582-s2.0-704426314510.1021/cm049643uNianJ. N.TengH.Hydrothermal synthesis of single-crystalline anatase TiO2 nanorods with nanotubes as the precursor20061109419341982-s2.0-3364565762210.1021/jp0567321HoyerP.Formation of a titanium dioxide nanotube array1996126141114132-s2.0-0000364624LeeJ. H.LeuI. C.HsuM. C.ChungY. W.HonM. H.Fabrication of aligned TiO2 one-dimensional nanostructured arrays using a one-step templating solution approach20051092713056130592-s2.0-2294443738810.1021/jp052203lZwillingV.Darque-CerettiE.Boutry-ForveilleA.DavidD.PerrinM. Y.AucouturierM.Structure and physicochemistry of anodic oxide films on titanium and TA6V alloy19992776296372-s2.0-0000811689GongD.GrimesC. A.VargheseO. K.HuW.SinghR. S.ChenZ.DickeyE. C.Titanium oxide nanotube arrays prepared by anodic oxidation20011612333133342-s2.0-0035739786VargheseO. K.GongD.PauloseM.GrimesC. A.DickeyE. C.Crystallization and high-temperature structural stability of titanium oxide nanotube arrays20031811561652-s2.0-0037820387VargheseO. K.PauloseM.ShankarK.MorG. K.GrimesC. A.Water-photolysis properties of micron-length highly-ordered titania nanotube-arrays200557115811652-s2.0-2374448170510.1166/jnn.2005.195OmidvarH.GoodarziS.SeifA.AzadmehrA. R.Influence of anodization parameters on the morphology of TiO2 nanotube arrays201150126392-s2.0-7995882528010.1016/j.spmi.2011.04.006PalmasS.Da PozzoA.MasciaM.VaccaA.ArduA.MatarreseR.NovaI.Effect of the preparation conditions on the performance of TiO2 nanotube arrays obtained by electrochemical oxidation20113615889489012-s2.0-7995881098710.1016/j.ijhydene.2011.04.105KılınçN.ŞennikE.ÖztürkZ. Z.Fabrication of TiO2 nanotubes by anodization of Ti thin films for VOC sensing20115203953958LiuY.WangD.CaoL.ChenS.Structural engineering of highly ordered TiO2 nanotube array by periodic anodization of titanium2012236871OkadaM.TajimaK.YamadaY.YoshimuraK.Self-organized formation of short TiO2 nanotube arrays by complete anodization of Ti thin films201232714718WangJ.LinZ.Freestanding TiO2 nanotube arrays with ultrahigh aspect ratio via electrochemical anodization2008204125712612-s2.0-4054914559110.1021/cm7028917AntonyR. P.MathewsT.DasguptaA.DashS.TyagiA. K.RajB.Rapid breakdown anodization technique for the synthesis of high aspect ratio and high surface area anatase TiO2 nanotube powders201118436246322-s2.0-7995245308610.1016/j.jssc.2011.01.020LiL.ZhouZ.LeiJ.HeJ.ZhangS.PanF.Highly ordered anodic TiO2 nanotube arrays and their stabilities as photo(electro)catalysts2012258836473651CrawfordG. A.ChawlaN.DasK.BoseS.BandyopadhyayA.Microstructure and deformation behavior of biocompatible TiO2 nanotubes on titanium substrate2007333593672-s2.0-3414717004410.1016/j.actbio.2006.08.004OuH. H.LoS. L.Review of titania nanotubes synthesized via the hydrothermal treatment: fabrication, modification, and application20075811791912-s2.0-3534902009310.1016/j.seppur.2007.07.017YuY.YuJ. C.ChanC. Y.CheY. K.ZhaoJ. C.DingL.GeW. K.WongP. K.Enhancement of adsorption and photocatalytic activity of TiO2 by using carbon nanotubes for the treatment of azo dye2005611-21112-s2.0-2214449834810.1016/j.apcatb.2005.03.008SunK. C.ChenY. C.KuoM. Y.WangH. W.LuY. F.ChungJ. C.LiuY. C.ZengY. Z.Synthesis and characterization of highly ordered TiO2 nanotube arrays for hydrogen generation via water splitting20111291-235392-s2.0-7995882984210.1016/j.matchemphys.2011.03.081XiongL.YangF.YanL.YanN.YangX.QiuM.YuY.Bifunctional photocatalysis of TiO2/Cu2O composite under visible light: Ti3+ in organic pollutant degradation and water splitting2011729110411092-s2.0-7996061668310.1016/j.jpcs.2011.06.016ZhangS.ZhangS.PengF.ZhangH.LiuH.ZhaoH.Electrodeposition of polyhedral Cu2O on TiO2 nanotube arrays for enhancing visible light photocatalytic performance20111388618642-s2.0-7996071360110.1016/j.elecom.2011.05.022ZangL.MacykW.LangeC.MaierW. F.AntoniusC.MeissnerD.KischH.Visible-light detoxification and charge generation by transition metal chloride modified titania2000623793842-s2.0-0033956206BoscF.EdwardsD.KellerN.KellerV.AyralA.Mesoporous TiO2-based photocatalysts for UV and visible light gas-phase toluene degradation20064951-22722792-s2.0-2804444874710.1016/j.tsf.2005.08.361HanC.LiZ.ShenJ.Photocatalytic degradation of dodecyl-benzenesulfonate over TiO2-Cu2O under visible irradiation200916812152192-s2.0-6734921434810.1016/j.jhazmat.2009.02.020LiuH.ShonH. K.SunX.VigneswaranS.NanH.Preparation and characterization of visible light responsive Fe2O3-TiO2 composites201125713581358192-s2.0-7995253430310.1016/j.apsusc.2011.01.110YangL.LuoS.LiY.XiaoY.KangQ.CaiQ.High efficient photocatalytic degradation of p-nitrophenol on a unique Cu2O/TiO2 p-n heterojunction network catalyst20104419764176462-s2.0-7795736183510.1021/es101711kMacakJ. M.TsuchiyaH.GhicovA.YasudaK.HahnR.BauerS.SchmukiP.TiO2 nanotubes: self-organized electrochemical formation, properties and applications2007111-23182-s2.0-4444917350010.1016/j.cossms.2007.08.004NarayananR.KwonT. Y.KimK. H.TiO2 nanotubes from stirred glycerol/NH4F electrolyte: roughness, wetting behavior and adhesion for implant applications20091172-34604642-s2.0-6765121146210.1016/j.matchemphys.2009.06.023PrakasamH. E.ShankarK.PauloseM.VargheseO. K.GrimesC. A.A new benchmark for TiO2 nanotube array growth by anodization200711120723572412-s2.0-3425034964310.1021/jp070273hKimS. E.LimJ. H.LeeS. C.NamS. C.KangH. G.ChoiJ.Anodically nanostructured titanium oxides for implant applications20085314484648512-s2.0-4104908981910.1016/j.electacta.2008.02.005PauloseM.ShankarK.YoriyaS.PrakasamH. E.VargheseO. K.MorG. K.LatempaT. A.FitzgeraldA.GrimesC. A.Anodic growth of highly ordered TiO2 nanotube arrays to 134 μm in length2006110331617916184LeeB. G.ChoiJ. W.LeeS. E.JeongY. S.OhH. J.ChiC. S.Formation behavior of anodic TiO2 nanotubes in fluoride containing electrolytes20091948428452-s2.0-6854911530810.1016/S1003-6326(08)60361-1ChoiW. Y.ChungJ.ChoC. H.KimJ. O.Fabrication and photocatalytic activity of a novel nanostructured TiO2 metal membrane20112791–3359366RuffT.HahnR.SchmukiP.From anodic TiO2 nanotubes to hexagonally ordered TiO2 nanocolumns201125719817781812-s2.0-7995880611110.1016/j.apsusc.2011.03.050ZengX.GanY. X.ClarkE.SuL.Amphiphilic and photocatalytic behaviors of TiO2 nanotube arrays on Ti prepared via electrochemical oxidation201150924L221L2272-s2.0-7995622716010.1016/j.jallcom.2011.03.154SrimuangmakK.NiyomwasS.Effects of voltage and addition of water on photocatalytic activity of TiO2 nanotubes prepared by anodization method20119435439ShankarK.MorG. K.FitzgeraldA.GrimesC. A.Cation effect on the electrochemical formation of very high aspect ratio TiO2 nanotube arrays in formamide-water mixtures2007111121262-s2.0-3384763390110.1021/jp066352vEl Ruby MohamedA.RohaniS.Modified TiO2 nanotube arrays (TNTAs): progressive strategies towards visible light responsive photoanode, a review201144106510862-s2.0-7995365565510.1039/c0ee00488jSunL.LiJ.WangC. L.LiS. F.ChenH. B.LinC. J.An electrochemical strategy of doping Fe3+ into TiO2 nanotube array films for enhancement in photocatalytic activity20099310187518802-s2.0-6834910198510.1016/j.solmat.2009.07.001MoJ.ZhangY.XuQ.LamsonJ. J.ZhaoR.Photocatalytic purification of volatile organic compounds in indoor air: a literature review20094314222922462-s2.0-6314915265410.1016/j.atmosenv.2009.01.034LockmanZ.SreekantanS.IsmailS.Schmidt-MendeL.MacManus-DriscollJ. L.Influence of anodisation voltage on the dimension of titania nanotubes201050323593642-s2.0-7795667254610.1016/j.jallcom.2009.12.093OhH. J.KimI. K.JangK. W.LeeJ. H.LeeS.ChiC. S.Influence of electrolyte and anodic potentials on morphology of titania nanotubes2012184673677