Spectroscopic ellipsometry study was employed for phase pure VO2(M1) thin films grown at different oxygen partial pressures by reactive magnetron sputtering. The optical constants of the VO2(M1) thin films have been determined in a photon energy range between 0.73 and 5.05 eV. The near-infrared extinction coefficient and optical conductivity of VO2(M1) thin films rapidly increase with decreasing O2-Ar ratios. Moreover, two electronic transitions can be uniquely assigned. The energy gaps correlated with absorption edge (E1) at varied O2-Ar ratios are almost the same (~2.0 eV); consequently, the absorption edge is not significantly changed. However, the optical band gap corresponding to semiconductor-to-metal phase transition (E2) decreases from 0.53 to 0.18 eV with decreasing O2-Ar ratios.
1. Introduction
Vanadium dioxide (VO2), one of the most interesting transition metal oxides, exhibits a reversible first-order semiconductor-to-metal phase transition (SMT) at a critical temperature Tc=68°C (for bulk single crystal VO2) [1]. VO2 has a tetragonal rutile structure with the P42/mnm space group (R phase) above the phase transition temperature, where the partially filled d// band localized at the Fermi level and the rutile phase is metallic [2]. Below the phase transition temperature, it transforms to a monoclinic structure with the P21/c space group (M1 phase), in which the partially filled d// band splits into an unoccupied part being pushed past the π* band and a filled part with the d// band dropping below the Fermi level, thus opening up a bandgap of ~0.6 eV between π* and the filled part of d// band [2]. Dramatic changes in the electrical and optical properties across the SMT make VO2 thin films suitable for many applications, such as switching devices, sensors, and smart windows [3–6].
It has been noted that oxygen partial pressure has effects on the structural and resistivity transition behaviors of VO2 [7]. Although the optimized oxygen partial pressure to fabricate VO2 films on glass and the optical properties of those samples were investigated [8], the optical constants, especially extinction coefficient k, which is crucial in understanding band structures, are not involved. Moreover, two energy gaps E1 and E2 are not distinguished as well.
Low visible transparency and unfavorable yellowish colour, which are correlated with absorption edges, limit the application of VO2 smart windows. For most practical applications the phase transition temperature Tc needs to be in the vicinity of room temperature (~25°C) and the Tc may be assumed to be correlated with the optical band gap E2. Consequently, the distinguishment of E1 and E2 plays an important role in improving the performance of VO2.
In this research, we thoroughly investigated the effects of oxygen partial pressures on the optical constants and the electronic transition behaviors of phase pure VO2(M1) thin films deposited on quartz glass by reactive magnetron sputtering. Moreover, two electronic transitions related to absorption edge (E1) and SMT (E2) were distinguished.
2. Experimental Section
VO2 thin films with a thickness of ~70 nm were deposited using a reactive rf magnetron sputtering system with a water-cooled vanadium metal target (50 mm in diameter, 99.9% purity). Quartz glasses (20×20×1 mm) were used as substrates and they were ultrasonically cleaned in acetone and subsequently in ethanol for 15 min, respectively, and then dried with pure nitrogen flow.
After being pumped down to a base pressure of 5×10-4 Pa, the deposition chamber was filled with high purity (99.999%) Ar and O2 mixture gas. The O2-Ar ratio was fixed as 1.0 : 49.0, 1.5 : 48.5, and 2.0 : 48.0, respectively (the unit is sccm). The total gas pressure was maintained at ~1.0 Pa. An rf power of 200 W was applied to the V target. During deposition, the substrate temperature was kept at 450°C for the better crystallinity of VO2 thin films. To improve the film homogeneity, the substrates were rotated along the vertical axis at a speed of 10 rpm.
The structure of the films was characterized by Raman spectrometer (Renishaw inVia Raman microscope) using a 514.5 nm laser. The optical transmittance was measured at a photon energy range of 0.73–5.05 eV at 26°C and 95°C by a spectrophotometer (Hitachi Corp., Model UV-4100). Temperature was measured using a PT100 temperature sensor in contact with the films and was controlled via a temperature controlling unit. Heating was controlled through a temperature-controlling unit. Hysteresis loops were measured by collecting the transmittance of films at a fixed photon energy (0.83 eV) at a temperature interval of ~2.0°C. Spectroscopic ellipsometry (SE J. A. Woollam M-2000) measurements were carried out between photon energies of 0.73 and 5.05 eV at 75° angle of incidence and the results were modeled using a commercial software.
3. Results and Discussion3.1. Structural Characterization
Raman measurements were conducted to examine the effect of O2-Ar ratio on the microstructure of VO2 (Figure 1(a)). The Raman spectrum at room temperature shows characteristic vibration modes for the M1 semiconducting phase of VO2. Comparing to previous works, Raman peaks are identified as 194(Ag), 223(Ag), 262(Bg), 307(Bg), 391(Ag), 492(Ag), and 618(Ag) cm−1 [9–11]. No Raman shifts for other kinds of vanadium oxides and any types of other polymorphs of VO2 (M2/T) [12, 13] were identified within the measurement accuracy (±0.2 cm−1). The XRD spectra are shown in Figure 1(b). All peaks can be indexed to VO2(M) and (011) was the prominent plane for VO2 thin film. No reflections due to other VOx phases such as V4O7, V6O13 and V3O7 were observed [14, 15].
Raman (a) and XRD (b) spectra for VO2 films deposited at different O2-Ar ratios.
3.2. Optical Properties of the VO2 Films
Figures 2(a) and 2(b) show the transmittance and absorptivity spectra of the prepared VO2 thin films at different O2-Ar ratios. The SMT transition is clearly observed with a dramatic change in the infrared transmittance with varied temperature ranges. The absorption edge, luminous (lum) transmittance (Tlum, 1.64–3.27 eV), and near-infrared (NIR) transmittance (0.73–1.64 eV) at the high temperature of 95°C were almost the same for all of the samples studied here. However, low temperature (below 26°C) phase VO2(M1) showed a gradually decreased NIR transmittance but increased absorptivity with decreasing O2-Ar ratios.
(a) Transmittance spectra of VO2 films deposited at different O2-Ar ratios. Solid and dashed lines refer to low temperature (26°C) and high temperature (95°C), respectively. (b) Low temperature (M1 phase) absorptivity spectra. Thermal hysteresis loops of optical transmittance at photon energy of 0.83 eV and phase transition temperature Tc are shown in (c) and (d).
Thermooptical hysteresis curves were deduced by measuring the transmittance at 0.83 eV with varying temperatures, which are shown in Figure 2(c). For comparison, the vertical axis of this figure has been normalized as X. From the X-temperature (T) data, a plot of dX/dT was obtained, yielding one peak with a well-defined maximum. Each of the dX/dT curves has been analyzed with a Gaussian function using the single peak fitting module of Originpro 8.0 software. The temperature corresponding to the maximum of dX/dT was defined as the phase transition temperature during a heating/cooling cycle; T1 and T2 represent the SMT temperature of heating and cooling branches, respectively. The SMT temperature was defined as Tc=(T1+T2)/2. As shown in Figure 2(d), the SMT temperatures were 46.2°C, 59.8°C, and 66.4°C for VO2 films deposited at the O2-Ar ratio of 1.0 : 49.0, 1.5 : 48.5, and 2.0 : 48.0, respectively. The phase transition temperature Tc consistently decreased as the O2-Ar ratio decreased. It was pointed out that vanadium interstitials and/or oxygen vacancies could reduce the SMT temperature of VO2 [16], which is also responsible for the decreased SMT temperatures at low O2-Ar ratios of this work. Low O2-Ar ratios can introduce both extra electrons and internal strains in nonstoichiometric VO2 (related data was revealed in a paper submitted to Thin Solid Films, Manuscript Number: TSF-D-13-00641).
3.3. Optical Constant
The electronic transitions, optical constants, and optical band gap (OBG) in the vicinity of the phase transition temperature have been investigated by Li et al. [17]. For a standard bulk VO2 sample, when temperature was increased to 67°C, contributions from the Drude response become more prominent. The extinction coefficient k and the optical conductivity σr values at the NIR region rapidly increase with increasing temperature. In this research, electron concentration increases with decreasing O2-Ar ratios and the Drude response is also responsible for the increased k and σr value at the NIR region (Figure 3). However, refractive index n was not significantly changed.
Refractive index n, extinction coefficient k, and optical conductivity σr of low temperature phase VO2 deposited at different O2-Ar ratios.
3.4. Band Gap
The indirect OBG can be estimated using the power law:
(1)(αE)1/2∝(E-Eg),
where α=4πk/λ is the absorption coefficient and Eg is the OBG energy. The Eg value is extrapolated by the linear portion of the plot to (αE)1/2=0.
Two electronic transitions can be uniquely assigned, as shown in Figures 4(a) and 4(b). The gaps correlated with absorption edge (E1) at varied O2-Ar ratios are almost the same (~2.0 eV); consequently, the absorption edge was not significantly changed, as shown in Figure 2(a). However, the optical band gap corresponding to SMT (E2) decreases from 0.53 to 0.18 eV with decreasing O2-Ar ratios, as shown in Figures 4(b) and 4(d). The OBG E2 of semiconducting VO2 can be assigned to the indirect transition from the top of filled d// bands to the bottom of empty π* band, as shown using a red arrow in Figure 4(c). Note that E2 at an O2-Ar ratio of 2.0 : 48.0 is similar to that from a previous report by theoretical calculation (0.6 eV) [18] and experimental results by photoemission spectroscopy (0.6 eV) [2]. Besides, the 0.41 eV band gap of the VO2 film prepared at an O2-Ar ratio of 1.5 : 48.5 agrees to a calculated intermediate structure at 339.8 K (0.36 eV) [18]. E2 at 1.0 : 49.0 O2-Ar ratio further decreased to 0.18 eV.
(a) and (b) (αE)1/2 versus E which is determined from extinction coefficient k and the extrapolating dashed lines are drawn to obtain the value of the band gap E1 and E2, respectively. (b) is the enlarged low photon energy portion of (αE)1/2 versus E. (c) Schematic diagram of electronic band structures in the VO2 film. (d) Variation of optical band gap E2 of VO2 thin films deposited at different O2-Ar ratios.
When decreasing O2-Ar ratios, the filled d// bands and the empty π* band are shifted to the higher and lower energy, respectively. Both the d// and π* bands gradually moved closely, resulting in a redshift of E2. The decreasing E2 results in a decrement in the SMT energies; therefore the SMT temperature decreased with decreasing O2-Ar ratios. Moreover, with decreasing the O2-Ar ratio, the NIR transmittance of the film evidently decreases. This behavior is because the bandgap E2 of the film, which is narrowing at low O2-Ar ratios, is different at the distinct O2-Ar ratio regions. It can enhance the electronic transitions and results in more interband absorptions at lower O2-Ar ratios, as shown in Figure 2(b).
4. Conclusions
To summarize, diverse phase transformation properties are reported for phase pure VO2(M1) thin films grown at different oxygen partial pressures by reactive magnetron sputtering. The transmittance and absorptivity spectra below phase transition temperatures are closely related to O2-Ar ratios. The phase transition temperature Tc decreased from 66.4°C to 46.2°C as the O2-Ar ratio decreased from 2.0 : 48.0 to 1.0 : 49.0. The optical constants of the VO2(M1) thin films have been determined between 0.73 and 5.05 eV. The near-infrared extinction coefficient k and optical conductivity σr increase with decreasing O2-Ar ratios. Moreover, two electronic transitions were identified. The energy gaps correlated with absorption edge at varied O2-Ar ratios are almost the same, while the optical band gap corresponding to semiconductor-to-metal phase transition decreases from 0.53 to 0.18 eV with decreasing O2-Ar ratios.
Conflict of Interests
The authors declare that there is no conflict of interests regarding the publication of the article.
Acknowledgments
This study was financially supported by the National Natural Science Foundation of China (NSFC, no. 51032008, 51272273, 51102270, 51272271, 51172265, and 51372264), the high-tech project of MOST (2012AA030605 and 2012BAA10B03), and Science and Technology Committee of Shanghai (no. 13PJ1409000).
MorinF. J.Oxides which show a metal-to-insulator transition at the neel temperature19593134362-s2.0-424401486910.1103/PhysRevLett.3.34KoetheT. C.HuZ.HaverkortM. W.Schüßler-LangeheineC.VenturiniF.BrookesN. B.TjernbergO.ReicheltW.HsiehH. H.LinH.-J.ChenC. T.TjengL. H.Transfer of spectral weight and symmetry across the metal-insulator transition in VO2200697112-s2.0-3374868110410.1103/PhysRevLett.97.116402116402ZhangZ.GaoY.LuoH.KangL.ChenZ.DuJ.KanehiraM.ZhangY.WangZ. L.Solution-based fabrication of vanadium dioxide on F:SnO2 substrates with largely enhanced thermochromism and low-emissivity for energy-saving applications2011410429042972-s2.0-8005333900610.1039/c1ee02092gGaoY. F.WangS. B.KangL. T.ChenZ.DuJ.LiuX. L.LuoH. J.KanehiraM.VO2-Sb:SnO2 composite thermochromic smart glass foil2012582348237GaoY.LuoH.ZhangZ.KangL.ChenZ.DuJ.KanehiraM.CaoC.Nanoceramic VO2 thermochromic smart glass: a review on progress in solution processing2012122212462-s2.0-8485825236110.1016/j.nanoen.2011.12.002BoriskovP. P.VelichkoA. A.PergamentA. L.StefanovichG. B.StefanovichD. G.The effect of electric field on metal-insulator phase transition in vanadium dioxide20022854064082-s2.0-003601840910.1134/1.1482750GriffithsC. H.EastwoodH. K.Influence of stoichiometry on the metal-semiconductor transition in vanadium dioxide1974455220122062-s2.0-001606079410.1063/1.1663568LiJ.DhoJ.Anomalous optical switching and thermal hysteresis behaviors of VO2 films on glass substrate201199232-s2.0-8345523076710.1063/1.3668089231909JonesA. C.BerwegerS.WeiJ.CobdenD.RaschkeM. B.Nano-optical investigations of the metal-insulator phase behavior of individual VO2 microcrystals2010105157415812-s2.0-7795234722710.1021/nl903765hSchilbeP.Raman scattering in VO22002316-3176006022-s2.0-003656697810.1016/S0921-4526(02)00584-7ChouJ. Y.Lensch-FalkJ. L.HemesathE. R.LauhonL. J.Vanadium oxide nanowire phase and orientation analyzed by Raman spectroscopy200910532-s2.0-6044911404010.1063/1.3075763034310MariniC.ArcangelettiE.di CastroD.BaldassareL.PerucchiA.LupiS.MalavasiL.BoeriL.PomjakushinaE.ConderK.PostorinoP.Optical properties of V1-xCrxO2 compounds under high pressure200877232-s2.0-4534908868310.1103/PhysRevB.77.235111235111AtkinJ. M.BerwegerS.ChavezE. K.RaschkeM. B.CaoJ.FanW.WuJ.Strain and temperature dependence of the insulating phases of VO2 near the metal-insulator transition20128522-s2.0-8485644037410.1103/PhysRevB.85.020101020101JiY. D.PanT. S.BiZ.LiangW. Z.ZhangY.ZengH. Z.WenQ. Y.ZhangH. W.ChenC. L.JiaQ. X.LinY.Epitaxial growth and metal-insulator transition of vanadium oxide thin films with controllable phases2012101071902JinP.TanemuraS.Formation and thermochromism of VO2 films deposited by RF magnetron sputtering at low substrate temperature1994333 A147814832-s2.0-0028403916ZhangS.KimI. S.LauhonL. J.Stoichiometry engineering of monoclinic to rutile phase transition in suspended single crystalline vanadium dioxide nanobeams2011114144314472-s2.0-7995455643010.1021/nl103925mLiW. W.YuQ.LiangJ. R.JiangK.HuZ. G.LiuJ.ChenH. D.ChuJ. H.Intrinsic evolutions of optical functions, band gap, and higher-energy electronic transitions in VO2 film near the metal-insulator transition region201199242-s2.0-8375517871110.1063/1.3665626241903YaoT.ZhangX.SunZ.LiuS.HuangY.XieY.WuC.YuanX.ZhangW.WuZ.PanG.HuF.WuL.LiuQ.WeiS.Understanding the nature of the kinetic process in a VO2 metal-insulator transition2010105222-s2.0-7864934077310.1103/PhysRevLett.105.226405226405