Hydration reaction of CO2 is one of the rate limiting steps for CO2 absorption (in aqueous solutions) and aqueous CO2 mineralization. The catalytic activity of nickel nanoparticles (NiNPs) for CO2 hydration is studied at different temperatures, pH, and low CO2 partial pressures to mimic the true flue gas conditions. Results show that NiNPs can work as active catalyst for hydration of CO2 in applications such as CO2 separation and CO2 mineralization. The NiNPs display optimum activity within 20–30°C and at pH value <8. NiNPs show catalytic activity even at low CO2 partial pressures (12 vol%). In 50 wt% K2CO3 solution, an enhancement of 77% is observed in the rate of CO2 absorption with NiNPs. Commercially, CO2 saturated K2CO3 solutions are usually regenerated at 150°C; at these conditions, NiNPs show no considerable surface oxidation. They still exhibit catalytic activity for hydration reaction of CO2. CO2 absorption and mineralization (as CaCO3) in DI water are three times higher in presence of NiNPs. Calcite (CaCO3) particles precipitated in presence of NiNPs are spherical in morphology.
1. Introduction
Recently an increase has been observed in global atmospheric temperatures due to the greenhouse gas emissions resulting from human anthropogenic activities [1]. A major contributor to this global warming is CO2 emitted from combustion of fossil fuels used for power generation and transportation. Consequently, there is a need for reduction of emitted CO2 from the atmosphere and its safe storage. The process of separation, transportation, and storage of CO2 is called carbon capture and storage (CCS) [2, 3].
Hydration of CO2 is an important reaction in CO2 absorption or wet chemical conversion of CO2 to mineral carbonates. Amines and carbonates are widely used for CO2 absorption separation [4–6]. Amine solutions have higher reaction rates with carbonic acid rather than CO2(aq) [7]. Therefore, enhancing the rate of CO2 hydration to carbonic acid can increase the rate of CO2 separation and mineralization. The hydration of CO2 is a pH dependent reaction with two different reaction mechanisms depending on the pH [8]. At pH values above 10, the reaction follows OH− reaction mechanism as shown by (1). At pH values below 8, it follows a H2O based reaction mechanism as shown in (2a) and (2b) [8]:(1)CO2+OH-⟷HCO3-(2a)CO2+H2O⟷H2CO3(2b)H2CO3⟷H++HCO3-The reaction in (1) is faster than in (2a) having the kinetic rate constant of kOH 8500 M−1 s−1 and kCO2 0.03 s−1, respectively [8]. Bhaduri and Šiller [9, 10] observed that the hydration reaction of CO2 with water is autocatalytic, due to the H+ ions generated by the dissociation of carbonic acid (2b) [11].
Carbonic anhydrase (CA) is one of the most studied and effective catalysts for hydration of CO2 with rate constant of 106 molecules per second [12]. Although CA is very efficient, its limitations include difficulty in recovery of catalyst, as it is a homogeneous catalyst [12], cost of immobilization [13–15], catalysing the reverse reaction at pH values below neutral (i.e., pH < 7) [16], and high extraction and processing costs [17, 18]. Therefore, other homogeneous organic [19, 20] and inorganic catalysts [6, 21] have been investigated for the hydration of CO2. Although these catalysts are cheap, they can be lost during use. Therefore, immobilization of these catalysts becomes an important issue.
Recently, it was reported that nickel nanoparticles (NiNPs) can catalyse hydration of CO2 [9, 11, 22]. Due to their magnetic properties, the NiNPs can be easily separated from the reaction mixture and recycled [9, 22]. Also, the NiNPs are more cost-effective to manufacture than CA [9]. Han et al. [23] immobilized NiNPs on silica aerogel support and tested the catalytic activity of supported catalyst for hydration of CO2. Bhaduri and Šiller [9] reported catalytic activity of NiNPs for CO2 hydration reaction at pH of 5.5 and 6.5; activity was found to be pH independent. All previous studies [9, 11, 23] on the kinetics of CO2 hydration in presence of NiNPs have been conducted at 1 atm partial pressure of CO2 using a 100% CO2 stream. The influence of CO2 partial pressure, temperature, and alkaline pH on the activity of CO2 hydration catalysed by NiNPs has not been investigated previously. Therefore, the purpose of this paper is to study the influence of low CO2 partial pressure (12% CO2-air mix), temperature, and alkaline pH on the catalytic activity of NiNPs for hydration of CO2.
Flue gas generally contains 12% of CO2 [24]; therefore, 12% CO2-air mixture is used to test the catalytic activity of NiNPs. At lower partial pressures, a reduction is observed in the rate of CO2 hydration in the presence of NiNPs. The flue gas is emitted at a temperature of 60°C. Thus it is important to test the catalytic activity of NiNPs at a range of temperatures. Studies are carried out at temperatures between 10°C and 60°C using the methodology previously reported [9]. The NiNPs show optimum catalytic activity within 20–30°C.
Industrially, CO2 capture is done using alkaline solutions such as amines and carbonates [25]. Therefore, the catalytic activity of NiNPs for hydration of CO2 is evaluated for neutral and alkaline pH conditions. It is found at neutral pH values (i.e., <8) that the NiNPs are active catalysts for hydration of CO2 but at higher pH values (i.e., >10) minimal catalytic activity is observed.
Potassium carbonate solutions (50 wt%) are commercially used for the separation of CO2 [26] from flue gas stream [4, 26]. The K2CO3 solution has higher CO2 loading capacity than amine solutions but is limited by low kinetic rates [26]. Therefore, the rate of CO2 absorption in K2CO3 solutions has been studied using various homogeneous catalyst [5, 26–28]. The use of NiNPs for enhancing CO2 absorption in K2CO3 solution has not been reported. Therefore, the rate of absorption of CO2 in 50 wt% K2CO3 solution with NiNPs is studied. When carbonates are used for the separation of CO2 from flue gases, the solvent is regenerated by heating the CO2 saturated bicarbonate solution at 150°C to release the absorbed CO2 [4, 26, 29]. Therefore, heat treatment of NiNPs was carried out to test the extent of oxidation of NiNP surface.
Bodor et al. [22] reported the use of NiNPs to enhance the mineralization of CO2 as CaCO3 and MgCO3 using alkaline waste as Ca and Mg sources. They found that the rate of CaO and MgO carbonation in slurries can be reduced to half using NiNPs. But at higher solid-liquid ratio in the slurry the NiNPs were ineffective. Therefore, we have tested the enhancement of the capture and mineralization of CO2 in DI water as CaCO3 in presence and absence of NiNPs. We observe that CaCO3 crystals developed on the NiNPs to form spherical calcite precipitate, thus blocking the active sites of NiNPs and limiting their catalytic activity.
2. Experimental
The NiNPs are bought from NanoTechnology, Korea. Sodium hydroxide, calcium chloride, potassium carbonate, sodium carbonate, Bis-Tris buffer, and concentrated HCl (analytical grade) are purchased from Sigma Aldrich, UK. 99% CO2 and 12% CO2-air synthetic gas were bought from BOC. 18.2 MΩ/cm resistivity water was used for all experiments obtained from Nanopure Barnstead UK.
The Bis-Tris-HCl buffer was prepared by mixing the Bis-Tris buffer in DI water (0.1 M). The pH of the buffer was adjusted by adding drop by drop of concentrated HCl. 0.1 M Na2CO3 solution was also prepared by mixing Na2CO3 in DI water. Saturated solution was made by bubbling CO2 in DI water for 4 hours until it saturates. The procedure for qualitative kinetic analysis was carried out by the procedure described by Mirjafari et al. [30]. 20 mL of Bis-Tris-HCl buffer (or Na2CO3 solution 0.1 M) was taken in a 50 mL beaker. The pH of the solution was monitored using HI2500 pH meter (Hanna Instruments) in Log mode with data logging after every 5 sec. After 5 stable readings logged in the pH log, 20 mL of saturated CO2 solution was added to the Bis-Tris-HCl buffer (or Na2CO3 solution 0.1 M). The pH was recorded until a stable reading was observed. For the NiNPs catalyst run, 30 ppm suspension of Bis-Tris-HCl buffer (or Na2CO3 solution) was prepared and the above process was repeated for this solution. The experiment was performed three times and the average of the results is presented.
The CO2 hydration kinetics experiment was performed similar to the method used by Bhaduri and Šiller [9]. The CO2 hydration rate was carried out in a 250 mL glass jar within a fixed volume (200 mL) of DI water (or 30 ppm NiNPs suspension). The CO2 gas was sparged into the solution at a flow rate of 50 mL/min at 0.1 MPa pressure using a glass sinter (Pyrex 1, Sigma Aldrich, UK). The pH changes of the solution are monitored during the bubbling experiments using a HI2550 pH meter (Hanna Instruments). The readings were at an interval of 20 seconds. The temperature of the sample was maintained by immersing the glass jar in a water bath (BS5, Fisher Scientific) at different temperatures (i.e., 10°C, 20°C, 30°C, 40°C, 50°C, and 60°C, resp.). The same experiment with 12% CO2-air synthetic gas 20°C is repeated five times and its average results are presented.
The CaCO3 precipitation experiments were carried out using the following methodology. 100 mL of DI water (or 30 ppm NiNPs suspension) was taken in a 150 mL glass jar and was bubbled with CO2 with a flow rate of 1.96 mM/min, at 0.1 MPa pressure different time intervals (i.e., 0.5 hr, 1 hr, 2 hrs, and 4 hrs, resp.). To the respective CO2 saturated samples were added 10 mL of 1 M NaOH solution and 10 mL of 1 M CaCl2 solution. The samples were stirred and the calcium carbonate was allowed to precipitate in the glass jar. The precipitates are filtered using a vacuum filter using a Watman 54, air dried at 60°C for 1 hour, and then weighted. The CaCO3 precipitated in the presence of NiNPs were characterized using scanning electron microscopy (SEM) and X-ray diffraction (XRD) for shape and structural determination. All experiments have been repeated three times and average data is presented.
To study the influence of NiNPs on the absorption rate of CO2 in K2CO3 solutions, the 50% (by weight) K2CO3 solution was prepared in 50 mL DI water. For the NiNPs suspension-K2CO3 solution, 1.5 mg of NiNPs was added into 50% K2CO3 solution and sonicated in the ultrasonic bath at constant temperature to make a 30 ppm solution. The concentration of 30 ppm was selected based on our previous studies [9]. The CO2 absorption experiments are performed in a 180 mL glass jar (Wheaton Industries, UK). The solution with the glass bubbler (Pyrex 1) was assembled and weighed before the introduction of CO2. The CO2 gas was bubbled at a flow rate of 1.69 mM/min at a pressure of 0.1 MPa. The final weight was obtained when there was no further possibility of gas flow though the bubbler. The gas bubbler was blocked by the formation of potassium bicarbonate crystals on the glass bubbler. The entire absorption experiment was carried out at 20°C using a water bath (BS5, Fisher Scientific). All the above experiments were carried out in triplets and average data is presented.
For the heat treatment, the NiNPs were placed in a silica crucible and heated in an oven at 150°C for 8 hours. The NiNPs was kept in an air tight container with ample desiccator beads to absorb any moisture present until further use. X-ray photoelectron spectroscopy (XPS) of the NiNPs before and after heat treatment was carried out using (Kratos Axis Ultra) equipped with a monochromatic Al Kα X-ray source, with a pass energy of 20 eV. The spectra were fitted with Shirley background [31] and mixed singlet peaks [32]. The spectra were calibrated by assigning the C 1s peak at 284.4 eV to adventitious carbon [33, 34]. All binding energy values reported are within an error of ±0.1 eV. The CO2 hydration catalysis using the heat treated NiNPs was carried out using the same methodology used for temperature dependent kinetics mentioned above. CO2 catalysis was carried out for the heat treated NiNPs using same methodology as Bhaduri and Šiller [9] at room temperature and atmospheric pressure. The kinetic analysis of the heat treated NiNPs and DI water was carried out in triplet and average data is presented.
3. Results and Discussions3.1. HRTEM and Particle Size Distribution of Nickel Nanoparticles
Figure 1(a) shows the high resolution transmission electron microscope images of the commercially purchased NiNPs to determine their size distribution. The particle size distribution of the nanoparticles based on statistical analysis is presented in Figure 1(b). The average particle size of the NiNPs was determined by fitting the distribution curve with a Gaussian function and was ~43 nm. The majority of the particles smaller than the prescribed manufacture size of 100 nm.
(a) HRTEM image of the NiNPs and (b) particle size distribution of nickel NiNPs determined by HRTEM.
3.2. Kinetics of CO2 Hydration Reaction with NiNPs at Low Partial Pressure of CO2
It is known that the rate of CO2 hydration is dependent on the concentration of CO2(aq) [4, 9, 35]. CO2(aq) concentration depends on the partial pressure of CO2 in the gas phase. As the partial pressure decreases in the gas phase, the concentration of CO2 molecules decreases at the interface and thus the reaction kinetics should decrease [35].
Figure 2(a) shows the change in pH of DI water and NiNPs suspension when 100% CO2 gas is bubble in them, respectively. Figure 2(b) shows that the pH change is still more rapid in the presence of NiNPs in suspension as compared to DI water when 12% CO2-air gas mixture is bubbled through them, respectively. This result is similar to the results observed previously [9]. The results in Figure 2(c) show that the catalytic hydration rate of CO2 (in presence of NiNPs) slightly decreases when the partial pressure of the CO2 in the gas phase is decreased. However, it can be observed from Figure 2(d) that the autocatalytic activity of CO2 hydration in DI water is highly reduced when the partial pressure of CO2 is reduced. This proves the assumption made previously about partial of CO2 affecting the rate of CO2 hydration.
(a) pH changes when 100% CO2-air mixture is bubbled in DI water and 30 ppm NiNPs suspension, (b) pH changes when 12% CO2-air mixture is bubbled in DI water and 30 ppm NiNPs suspension, (c) pH change when 12% and 100% CO2 is bubbled in 30 ppm NiNPs suspension, and (d) pH change when 12% and 100% CO2 is bubbled in DI water.
All the above data suggest that in the presence of the NiNPs the rate limiting step is the transfer of CO2g to CO2(aq) rather than the hydration of reaction of CO2. The reduction in rate of CO2 hydration (observed as the rate of pH change in Figure 2(c)) is due to the slow gas-liquid mass transfer due to the low partial pressure of CO2.
3.3. pH Dependence of Catalytic Activity of NiNPs for CO2 Hydration Reaction
A qualitative method was used to test the pH dependence of the NiNPs’ activity for CO2 hydration. The methodology was adapted from kinetic study of CA hydration as described by Mirjafari et al. [30] on recommendation of Britt [36]. Bis-Tris-HCl buffer has terminal OH groups for regulation of pH. As the NiNPs also have OH groups on their surface when dispersed in water [9], the adsorption of buffer would thus be limited. Figure 3 shows the pH changes in Bis-Tris-HCl buffer (Figure 3(a)) and sodium carbonate solutions (Figure 3(b)) when a CO2 saturated solution was added. Figure 3(a) shows a faster pH drop in Bis-Tris-HCl buffer solution with addition of NiNPs. This indicates an increase in catalytic activity due to the presence of NiNPs at pH values below 8 with CO2 hydration following the reaction mechanism described by (2a) (see Section 1) [8]. Figure 3(b) shows the pH changes at alkaline pH values (i.e., pH > 10) in Na2CO3 solution. The NiNPs catalysis is minimal at alkaline pH (i.e., pH > 10) but can be observed when the pH drops below 10 (Figure 3(b)). Above pH 10, CO2 hydration can be described by (1) (see Section 1) whilst it operates via a mixed mechanism ((1) and (2a)) at pH values between 10 and 8 [8]. Therefore, NiNPs catalysis cannot be observed at alkaline pH values above 10 but can be observed at pH values below 10.
pH dependent hydration of CO2 in presence of NiNPs at different pH (a) at pH 7 using Bis-Tris-HCl buffer and (b) at pH 11.5 using sodium carbonate solution.
3.4. Temperature Dependent Kinetics of Catalytic Hydration Reaction of CO2 with NiNPs
NiNPs catalysis is analysed by observing the rate of change of pH when CO2 is bubbled in DI water or NiNPs suspension. The change in pH is due to the formation of carbonic acid in solution. The results show (Figures 4(a)–4(f)) that in the presence of NiNPs the pH drop is more rapid than in its absence, but in the DI water system, there is an initial slow decrease in pH followed by a rapid decrease in pH. This is an autocatalytic behaviour of CO2 hydration first observed by Bhaduri and Šiller [9] and is explained to be caused by the presence of H+ ions (see Supplementary Information of [11] in Supplemetary Material available online at http://dx.doi.org/10.1155/2015/581785). Similar behaviour is observed in the current study. Due to the autocatalytic activity of hydration of CO2 in DI water, the interpretation of the catalytic activity of NiNPs is done by observing the proximity of the catalysed and uncatalysed curves to one another. If the catalysed and uncatalysed curves are close to one another, the catalytic activity of NiNPs is low but if they are further apart from one another the catalytic activity of the NiNPs is high.
Change in pH of DI water (square) or NiNPs suspension (circle) when CO2 is bubbled through liquid maintained at temperatures (a) 10°C, (b) 20°C, (c) 30°C, (d) 40°C, (e) 50°C, and (f) 60°C.
Figures 4(a)–4(f) show the catalytic activity of NiNPs at all the tested temperatures. As the temperature changes, the proximity between the two curves (catalysed which is indicated with filled circles and uncatalysed which is indicated with filled squares) also changes mainly due to a change in the reaction kinetics of the uncatalysed hydration of CO2. A higher catalytic activity was observed for the NiNPs to catalyse the hydration of CO2 at ambient temperatures (20–30°C) than that at lower (10–20°C) or higher (40–60°C) temperatures, respectively. For all the profiles for the pH change for noncatalytic reaction (the filled squares in Figures 4(a)–4(f)) of CO2 hydration in DI water there is an initial slow change in pH followed by a rapid change in pH; these results are similar to the observations made by Bhaduri and Šiller [9]. It is evident form Figure 4(c) that the reaction rate of CO2 hydration in DI water is slower at 30°C than at other temperatures. The NiNPs suspension shows similar pH change profile at all tested temperatures. The observed changes in kinetic rates are likely due to the adsorption/desorption of water or CO2 on the NiNPs surface which is affected with temperature [37, 38] along with the solubility of CO2.
3.5. Enhancing CO2 Uptake in Potassium Carbonate Solution with NiNPs
In the current study, gravimetric method was used to study the enhancement of CO2 in carbonate solutions. Figure 5 shows the results of gravimetric uptake of CO2 in 50 wt% K2CO3 solution in the absence and presence of NiNPs. The experiment was run until no additional change in the weight of the reaction vessel was observed. The reaction in the reactor can be represented by the following reaction equations:(3a)CO32-+H2O⟷HCO3-+OH-(3b)CO2+OH-⟷HCO3-(3c)CO2+H2O⟷H2CO3(3d)H2CO3⟷H++HCO3-(3e)CO32-+H+⟷HCO3-Carbonate solutions (K2CO3 and Na2CO3) have a high pH (i.e., >11) and as CO2 is bubbled into the carbonate solution its pH drops [11]. The reaction 3a takes place when the K2CO3 is instantaneously dissolved in DI water and CO2 hydration reaction takes place via reaction (3b) till the pH reaches 10 [8]. Reaction mechanisms (3b) and (3c) simultaneously occur between pH 10 and 8 with reaction (3c) being the slowest step [8]. Reactions (3d) and (3e) like (3a) are instantaneous [39]. Thus, CO2 hydration is the most important step in the CO2 capture when using potassium carbonate solutions. Therefore, in summary, as the CO2 and carbonic acid start reacting with the carbonate solution, the pH of the solution changes and the reaction mechanisms of CO2 hydration changes [11] from (3b) to (3c) depending on the pH of the solution [8]. From Figure 5, it can be observed that initial rate of CO2 absorption is similar for 50 wt% K2CO3 solution both with and without NiNPs catalyst but after 60 minutes the rate of reaction is faster in presence of the NiNPs. This kind of enhancement in CO2 absorption is a result of the carbonate-bicarbonate buffering ability of carbonate solutions. Pinsent and Roughton [40] report that the rate of CO2 hydration increases as the bicarbonate/carbonate ([HCO3-]/[CO32-]) ratio increases. Therefore, as CO2 reacts with the carbonate solution, the bicarbonate ions are formed (following reaction (3b)) (the value of the numerator increases while that of the denominator decreases), leading to the observed autocatalytic enhancement absorption of CO2.
Increase in weight of 50 wt% K2CO3 solution with and without NiNPs when CO2 is bubbled in it.
Figure 5 shows that in the presence of NiNPs there is the increase in weight of the carbonate solution (after saturation) due to enhanced kinetic rate of CO2 hydration (but lower than the full capacity of the carbonate solution, which is 15.92 g, if there is 100% conversion of K2CO3 to KHCO3). There is an increase in CO2 loading (mol of CO2 per mol of K2CO3) by ~27%.
In Figure 5, the rapid increase in CO2 absorption after 60 min until saturation is used to estimate the enhancement in absorption rate of CO2 in carbonate solutions in presence of NiNPs. The data points between 60 min and saturation are linearly fitted (see Supplementary Figure S1) and the data is shown in Table 1. It can be observed that the data showed a good linear fit (R2>0.96) and the slope can be used to compare the enhancement in rate. There is ~77% increase in the absorption rate of CO2 in carbonate solution in the presence of NiNPs under the same operating conditions.
Rate of CO2 absorption in K2CO3 solutions with and without NiNPs.
System
Rate (moles/min)
Regression (R2)
Potassium carbonate
0.0048
0.963
Potassium carbonate + NiNPs
0.00852
0.971
3.6. Heat Treatment of NiNPs
Carbonate solutions are generally regenerated at a temperature of 150°C [4, 26, 29]; therefore, in order to use NiNPs as enhancers in carbonate separation technology a set of experiments were performed to test the effect of heating on the catalytic activity of NiNPs. The NiNPs were heated at 150°C for 8 hours to study the changes in surface chemistry and its catalytic activity for CO2 hydration. XPS analysis was done before and after heat treatment in order to check any surface chemistry changes due to heating.
Figure 6 shows the surface species present on the NiNPs surface before and after heat treatment. Three different species were observed in Ni 2p3/2 spectra for NiNPs before and after heat treatment, respectively. In Figure 6(a), the peaks at 852.5 eV, 854.1 eV, and 855.7 eV can be assigned to Ni0, NiO, and Ni(OH)x, respectively [41–44], and in Figure 6(b) the peaks at 852.4 eV, 854.0 eV, and 855.7 eV can be assigned to Ni0, NiO, and Ni(OH)x, respectively [42–44]. The peak at 861.0 eV in Figure 6(a) (or 860.9 eV in Figure 6(b)) is assigned the value for a collective plasmon peak of Ni [9, 33, 34]. No change in the peak positions of the Ni and NiO is observed (peaks are within the experimental error limit of ±0.1 eV) after heat treatment, although after heat treatment there is a 27% increase of oxide on the surface. The presence of the two peaks in the O 1s spectra shows the presence of oxygen in two oxidation states. In Figure 6(c), the peak at 529.3 eV corresponds to NiO [41] whereas the peak at 531.0 eV corresponds to NiOHx [45]. The existence of the NiOHx is due to the dissociative adsorption of water from the atmosphere. It is known that the OH bond on the surface has a binding energy difference of 1.8 eV higher than that of NiO [45]. Thus, the peak at 531.0 eV is assigned to NiOHx. The peaks in O 1s at 529.5 eV and 531.2 eV after heat treatment observed in Figure 6(d) also correspond to NiO [41] and NiOHx [45, 46]. The C 1s peak in Figures 6(e) and 6(f) at 284.4 eV can be attributed to adventitious carbon [33, 34]. The survey spectrum shows presence of Ni 3p, Ni 2p, C 1s, and O 1s peaks for NiNPs before (Figure 6(g)) and after (Figure 6(b)) heat treatment.
XPS results of the NiNPs before ((a) Ni 2p3/2, (c) O 1s, (e) C 1s, and (g) survey) heat treatment and after ((b) Ni 2p3/2, (d) O 1s, (f) C 1s, and (h) survey) heat treatment at 150°C for 8 hours in air.
Figure 7 shows the X-ray diffraction pattern of the NiNPs before and after heat treatment at 150°C for 8 hours. The XRD pattern detects the bulk changes taking place in the NiNPs due to heat treatment. The crystal planes observed as peaks can be associated with the 111,[200],220,[311], and [222] planes associated with 2θ = 44.43°, 51.78°, 76.26°, 92.77°, and 98.27°, respectively, of cubic nickel lattice with space group of Fm-m3 [47, 48]. The absence of NiO peaks (2θ = 43.20° (most intensive), 62.87°, 75.20°, and 79.38°) from the XRD diffraction patterns shows that no any significant bulk oxidation of the NiNPs occurred during the heat treatment.
X-ray diffraction pattern of the NiNPs (a) before and (b) after heat treatment at 150°C for 8 hours.
Based on the results of the XPS analysis, the catalytic activity of the heat treated NiNPs was studied. Figure 8 shows the pH change profile when CO2 is bubbled in NiNPs suspension compared to DI water. The pH change profiles of heat treated (Figure 8(a)) and untreated (Figure 8(b)) NiNPs compared to DI water are similar. The catalytic activity of NiNPs was observed even after heat treatment (150°C for 8 hours in air) thus making the NiNPs a suitable candidate to be used as enhancers in carbonate absorber systems.
pH changes during bubbling of CO2 through DI water (a) heat treated NiNPs (at 150°C for 8 hours in air) suspension and (b) without heat treatment.
3.7. Increase in CaCO3 Precipitation with NiNPs
Figure 9 shows the amount of CaCO3 precipitated in presence and absence of NiNPs in DI water. The CaCO3 precipitate yield in the presence of the NiNPs was higher than that of DI water alone; therefore, the NiNPs increase the CO2 uptake and hydration constant rate even under the presaturation conditions. The CaCO3 precipitate yield in the presence of the NiNPs was three times higher than that of DI water, similar to the results observed by Bhaduri and Šiller [9].
CaCO3 precipitate obtained in DI water and NiNPs suspension after CO2 bubbling at different time intervals.
Figure 10 shows the SEM images of the CaCO3 precipitate in presence of NiNPs. Micron sized (2–10 μm) spherical precipitates are observed. XRD of the precipitate is shown in Figure 11, which confirms the presence of the calcite phase of CaCO3 [49]. The diffraction plane of Ni [111] is also present [50] which indicates also the presence of NiNPs in the precipitates. Therefore, the NiNPs could act as nucleation sites for the crystals to grow, since the NiNPs are spherical in shape (reported previously [9]), and the carbonate precipitates are also spherical (instead of normal cubic shape [51, 52]). Bodor et al. [22] studied the application of NiNPs for mineralization of CO2 using alkaline wastes slurries containing MgO or CaO. They suggested that the activity of NiNPs is dependent on the solid to liquid ratio of the slurry based on the observation of low enhancement at high solid to liquid ratio. They did not provide a reason for the decrease in the activity of NiNPs. We suggest, based on our mineralization results, that at higher solid to liquid ratio the in situ mineral precipitation of carbonates (MgCO3 or CaCO3) would have blocked the NiNPs active sites. The carbonate (MgCO3 or CaCO3) would have precipitated on the NiNPs coving the particles. Thus, this would have lowered the activity of NiNPs.
SEM images of the precipitate of CaCO3 obtained in presence of NiNPs catalysed hydration of CO2 using NaOH and CaCl2.
XRD of the precipitate of CaCO3 obtained in presence of NiNPs catalysed hydration of CO2 using NaOH and CaCl2. Insert is the magnification of the later end of the XRD pattern to show the Ni peak.
4. Summary
In the current study, the temperature, pH dependence, and CO2 partial pressure dependence of NiNPs catalysis for hydration of CO2 are studied. As compared to other homogenous catalysts used for CO2 hydration, NiNPs are cost-effective and have ease of separation for repeatable use. The NiNPs catalysis was optimum within 20–30°C for hydration of CO2 and at pH below 8. NiNPs catalysis for hydration of CO2 is observed at lower partial pressure of CO2. NiNPs show an enhancement in CO2 uptake of 50 wt% K2CO3 solution. An enhancement of CO2 absorption rate of ~77% was observed in the presence of NiNPs more than in its absence. This suggests that NiNPs can be used as enhancers for CO2 separation using carbonate solutions and could work for other alkaline absorbing solutions as well. It was observed the heat treatment does not have major changes on the surface of NiNPs and the catalytic activity of NiNPs is retained after heat treatment. As compared to other homogeneous catalysts, the NiNPs have an advantage to be used at high temperature CO2 separation with low loss in activity. The NiNPs also increase the precipitation of CO2 as CaCO3 in DI water by up to three times as compared to in its absence. The NiNPs act as nucleates for CaCO3 growth and thus the calcite precipitates are spherical in shape. This suggests that the NiNPs need to be separated from the solution before carbonate formation during aqueous mineralization carbon capture and storage. Alternatively, the NiNPs can be immobilised on supports for easy separation and reuse during aqueous mineralization of CO2 as it has been recently demonstrated by Han et al. [23].
Conflict of Interests
The authors declare that there is no conflict of interests regarding the publication of this paper.
Acknowledgments
Gaurav Ashok Bhaduri thanks Newcastle University for Teaching Scholarship. All authors thank the EPSRC for the grant (EP/K004689/1) and EPSRC Impact Acceleration Account for financial support. The authors thank ACMA, Newcastle University, for SEM and XRD analysis and Dr. Alan Harvey for the HRTEM analysis. This work has been supported by Newcastle University and Patent PCT/GB2013/051243 (WO2013171480 A3) has been awarded. Data supporting this publication is openly available under an “Open Data Commons Open Database License”. Additional metadata are available at 10.17634/135315-1. Please contact Newcastle Research Data Services at rdm@ncl.ac.uk for access instructions.
IPCC2012New York, NY, USAIntergovernmental Panal on Climate Changeedited by: O. Edenhofer, R. P. Madruga, Y. SokonaIEA2013Lyon, FranceInternational Energy AgencyIEAGlobal CCS Institute2012Lyon, FranceInternational Energy Agency and Global CCS InstituteDanckwertsP. V.1970New York, NY, USAMcGraw-HillRobertsD.DanckwertsP. V.Kinetics of CO2 absorption in alkaline solutions—I Transient absorption rates and catalysis by arsenite1962171296196910.1016/0009-2509(62)80074-82-s2.0-50549167141SharmaM. M.DanckwertsP. V.Catalysis by Brönsted bases of the reaction between CO2 and water19635938639510.1039/tf9635900386ZhangG.WangX.ConwayW.MaederM.SunQ.YuH.Kinetics of CO2(aq),HCO3- with primary and secondary amines in aqueous solution20136482883289010.3969/j.issn.0438-1157.2013.08.026KernD. M.The hydration of carbon dioxide19603711410.1021/ed037p142-s2.0-33947476001BhaduriG. A.ŠillerL.Nickel nanoparticles catalyse reversible hydration of carbon dioxide for mineralization carbon capture and storage2013351234123910.1039/c3cy20791a2-s2.0-84879584389ŠillerL.BhaduriG. A.Carbon captureWorld patent WO2013171480 A3, 2013BhaduriG. A.HendersonR. A.ŠillerL.Reply to the ‘Comment on “nickel nanoparticles catalyse reversible hydration of carbon dioxide for mineralization carbon capture and storage’” by D. Britt, Catal. Sci. Technol., 2013, 3, DOI: 10.1039/C3CY00142C2013392197219810.1039/c3cy00357d2-s2.0-84881430575BongG.-M.StringerJ.BrandvoldD. K.SimsekF. A.MedinaM.-G.EgelandG.Development of integrated system for biomimetic CO2 sequestration using the enzyme carbonic anhydrase200115230931610.1021/ef000246p2-s2.0-0035263847VinobaM.BhagiyalakshmiM.JeongS. K.NamS. C.YoonY.Carbonic anhydrase immobilized on encapsulated magnetic nanoparticles for CO2 sequestration20121838120281203410.1002/chem.2012011122-s2.0-84866258855VinobaM.BhagiyalakshmiM.JeongS. K.YoonY. I.NamS. C.Immobilization of carbonic anhydrase on spherical SBA-15 for hydration and sequestration of CO22012901919610.1016/j.colsurfb.2011.10.0012-s2.0-82355190190VinobaM.LimK. S.LeeS. K.JeongS. K.AlagarM.Immobilization of human carbonic anhydrase on gold nanoparticles assembled onto amine/thiol-functionalized mesoporous SBA-15 for biomimetic sequestration of CO2201127106227623410.1021/la105029h2-s2.0-79958179977KernohanJ. C.The pH-activity curve of bovine carbonic anhydrase and its relationship to the inhibition of the enzyme by anions196596230431710.1016/0005-2787(65)90593-9PierreA. C.Enzymatic carbon dioxide capture201220122275368710.5402/2012/753687BooneC. D.GillS.HabibzadeganA.McKennaR.Carbonic anhydrase: an efficient enzyme with possible global implications20132013681393110.1155/2013/8139312-s2.0-84885465812SahooP. C.JangY.-N.LeeS.-W.Immobilization of carbonic anhydrase and an artificial Zn(II) complex on a magnetic support for biomimetic carbon dioxide sequestration201282374510.1016/j.molcatb.2012.05.0202-s2.0-84862745337BräuerM.Pérez-LustresJ. L.WestonJ.AndersE.Quantitative reactivity model for the hydration of carbon dioxide by biomimetic zinc complexes20024161454146310.1021/ic00105102-s2.0-0037170520DennardA. E.WilliamsR. J. P.The catalysis of the reaction between carbon dioxide and water196681281610.1039/j196600008122-s2.0-37049125934BodorM.SantosR. M.ChiangY. W.VladM.Van GervenT.Impacts of nickel nanoparticles on mineral carbonation201420141092197410.1155/2014/9219742-s2.0-84893980685HanX.WilliamsonF.BhaduriG. A.HarveyA.ŠillerL.Synthesis and characterisation of ambient pressure dried composites of silica aerogel matrix and embedded nickel nanoparticles201510.1016/j.supflu.2015.06.017KimD.-H.VinobaM.ShinW.-S.LimK.-S.JeongS.-K.KimS.-H.Biomimetic sequestration of carbon dioxide using an enzyme extracted from oyster shell201128102081208510.1007/s11814-011-0071-z2-s2.0-80053379567ZamanM.LeeJ. H.Carbon capture from stationary power generation sources: a review of the current status of the technologies20133081497152610.1007/s11814-013-0127-32-s2.0-84880834136DanckwertsP. V.Promotion of CO2 mass-transfer in carbonate solutions198136101741174210.1016/0009-2509(81)80023-12-s2.0-49149136780SharmaM. M.DanckwertsP. V.Fast reactions of CO2 in alkaline solutions—(a) Carbonate buffers with arsenite, formaldehyde and hypochlorite as catalysts (b) Aqueous monoisopropanolamine (1-amino-2-propanol) solutions1963181272973510.1016/0009-2509(63)85041-12-s2.0-0001678979YeX.LuY.CO2 absorption into catalyzed potassium carbonate-bicarbonate solutions: kinetics and stability of the enzyme carbonic anhydrase as a biocatalyst201411656757510.1016/j.ces.2014.05.0402-s2.0-84902479522JayaweeraI.JayaweeraP.ElmoreR.BaoJ.BhamidiS.Update on mixed-salt technology development for CO2 capture from post-combustion power stations20146364065010.1016/j.egypro.2014.11.070MirjafariP.AsghariK.MahinpeyN.Investigating the application of enzyme carbonic anhydrase for CO2 sequestration purposes200746392192610.1021/ie060287u2-s2.0-33847320546ShirleyD. A.High-resolution x-ray photoemission spectrum of the valence bands of gold1972512, article 470910.1103/physrevb.5.47092-s2.0-33744538097YuJ.XiangQ.ZhouM.Preparation, characterization and visible-light-driven photocatalytic activity of Fe-doped titania nanorods and first-principles study for electronic structures2009903-459560210.1016/j.apcatb.2009.04.0212-s2.0-67649419150BiesingerM. C.PayneB. P.LauL. W. M.GersonA.SmartR. S. C.X-ray photoelectron spectroscopic chemical state quantification of mixed nickel metal, oxide and hydroxide systems200941432433210.1002/sia.30262-s2.0-65349111924PayneB. P.BiesingerM. C.McIntyreN. S.The study of polycrystalline nickel metal oxidation by water vapour20091751–3556510.1016/j.elspec.2009.07.0062-s2.0-70350622156DoraiswamiL. K.SharmaM. M.19842New York, NY, USAJohn Wiley & SonsBrittD.Comment on ‘nickel nanoparticles catalyse reversible hydration of carbon dioxide for mineralization carbon capture and storage’ by G. Bhaduri and L. Šiller, Catal. Sci. Technol., 2013, 3, 12342013392195219610.1039/C3CY00142CFreundH.-J.RobertsM. W.Surface chemistry of carbon dioxide199625822527310.1016/s0167-5729(96)00007-62-s2.0-0030290112CarleyA. F.RassiasS.RobertsM. W.The specificity of surface oxygen in the activation of adsorbed water at metal surfaces19831351–3355110.1016/0039-6028(83)90208-x2-s2.0-0009010764SnoeyinkV. L.JenkinsD.1980New York, NY, USAJohn Wiley & SonsPinsentB. R. W.RoughtonF. J. W.The kinetics of combination of carbon dioxide with water and hydroxide ions19514726326910.1039/tf95147002632-s2.0-0010471151KimK. S.WinogradN.X-ray photoelectron spectroscopic studies of nickel-oxygen surfaces using oxygen and argon ion-bombardment197443262564310.1016/0039-6028(74)90281-72-s2.0-0016070147LorenzP.FinsterJ.WendtG.SalynJ. V.ŽumadilovE. K.NefedovV. I.Esca investigations of some NiO/SiO2 and NiO-Al2O3 /SiO2 catalysts197916326727610.1016/0368-2048(79)80023-72-s2.0-45449087172McIntyreN. S.CookM. G.X-ray photoelectron studies on some oxides and hydroxides of cobalt, nickel, and copper197547132208221310.1021/ac60363a0342-s2.0-0016569995RoustilaA.SeveracC.ChêneJ.Percheron-GuéganA.Hydrogen effects on the electronic and microstructural properties of Ce, Ni, and CeNi2 intermetallic compound19943111-2334410.1016/0039-6028(94)90478-22-s2.0-0028436864CistonJ.SubramanianA.KienzleD. M.MarksL. D.Why the case for clean surfaces does not hold water: structure and morphology of hydroxylated nickel oxide (1 1 1)2010604215516410.1016/j.susc.2009.10.0332-s2.0-72649104395SalvatiL.Jr.MakovskyL. E.StencelJ. M.BrownF. R.HerculesD. M.Surface spectroscopic study of tungsten-alumina catalysts using X-ray photoelectron, ion scattering, and Raman spectroscopies198185243700370710.1021/j150624a0352-s2.0-0345948592DellisS.ChristoulakiA.SpiliopoulosN.AnastassopoulosD. L.VradisA. A.Electrochemical synthesis of large diameter monocrystalline nickel nanowires in porous alumina membranes20131141616430810.1063/1.48269002-s2.0-84887275217TakeshitaH. T.OishiT.KuriyamaN.Disproportionation of CaNi3 hydride: formation of new hydride, CaNiH320023331-226627310.1016/s0925-8388(01)01739-x2-s2.0-0037074687SwansonH. E.FuyatR. K.National Bureau of Standards (U.S.) Circular II (1953) 51ZhangD. E.NiX. M.ZhengH. G.LiY.ZhangX. J.YangZ. P.Synthesis of needle-like nickel nanoparticles in water-in-oil microemulsion200559162011201410.1016/j.matlet.2005.02.0402-s2.0-17844387093YadavR.JoshiM.WanjariS.PrabhuC.KotwalS.SatyanarayananT.RayaluS.Immobilization of carbonic anhydrase on chitosan stabilized Iron nanoparticles for the carbonation reaction201222385345535610.1007/s11270-012-1284-42-s2.0-84867329123WanjariS.PrabhuC.YadavR.SatyanarayanaT.LabhsetwarN.RayaluS.Immobilization of carbonic anhydrase on chitosan beads for enhanced carbonation reaction20114641010101810.1016/j.procbio.2011.01.0232-s2.0-79952316124