Journal of Nanomaterials
Volume 2016 (2016), Article ID 1957612, 7 pages
http://dx.doi.org/10.1155/2016/1957612

Research Article

Fusarium Antifungal Activities of Copper Nanoparticles Synthesized by a Chemical Reduction Method

Pham Van Viet,1,2 Hai Thi Nguyen,² Thi Minh Cao,² and Le Van Hieu¹

¹Faculty of Materials Science, University of Science, Vietnam National University Ho Chi Minh City, 227 Nguyen Van Cu Street, District 5, Ho Chi Minh City 700000, Vietnam
²CM Thi Laboratory, Ho Chi Minh City University of Technology (HUTECH), 475A Dien Bien Phu Street, Binh Thanh District, Ho Chi Minh City 700000, Vietnam

Received 21 March 2016; Revised 20 June 2016; Accepted 29 June 2016

Academic Editor: Lavinia Balan

Copyright © 2016 Pham Van Viet et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

We report on the process of synthesizing copper nanoparticles (Cu Nps) for a short reactive time by chemical reduction method with a support of CTAB reductive agent. Their properties were determined by ultraviolet-visible (UV-Vis) absorption spectrum, the X-ray (XRD) analysis, Fourier transform infrared spectroscopy (FT-IR), and Transmission Electron Microscopy (TEM) images. The antifungal activity of Cu Nps was evaluated by testing against Fusarium sp. The Cu Nps were obtained with the average size in the range of 20–50 nm having spherical shape. The survey shows that when Cu Nps were used at 450 ppm concentration in 9-day incubation, 93.98% of fungal growth was inhibited.

1. Introduction

Transition metals and their oxides are widely used in materials because of their specific electrical, structural, catalytic, optical, and magnetic properties [1–3]. Among transition metal materials, copper is the most important material. The unique catalytic and optical properties show that copper nanoparticles (Cu Nps) are potential candidates for the reaction of H₂O dissociation [4], used in ultrafast catalytic activity for the degradation of some organic dyes such as methylene blue (MB) and rose bengal (RB) [5], and applied in a wide variety of conductive inks for printing in electronics [6–8] as well as antifungal/antibacterial applications [9–15]. In particular, the fungus inhibition efficiency of Cu Nps is better than other metal nanoparticles, such as Al, Fe, Mn, Ni, Zn, and products of bigger size Cu particles [16].

Fusarium species (sp.) is the largest expansion in “Tuberculariaceae” family and it exists in host plants and is the major cause which wilts host plants [17]. Because the colonies spread across the tissue and fill xylem vessels, water transport process is hindered, making the plants wilt [16, 18, 19]. Furthermore, Fusarium sp. also produces a number of toxic substances in the host vascular tree which can also cause wilting [20]. Fusarium sp. is a common fungal disease on many crops and it is one of the most devastating diseases spotted on tomato, potato, dragon fruit, watermelon plants and other cucurbits, and so forth [18, 21, 22].

Currently, the antagonistic organisms, such as Bacillus coagulans [23] or a wide variety of chemicals to eliminate harmful microorganisms are often used. In particular, the use of generic drugs with a large amount of copper leads to copper residues in produce as well as higher soil and water pollution. Plant microelements as Cu Nps are known to play critical roles in plant disease resistance through enzyme activation for defense barrier production [16]. Furthermore, the use of Cu Nps helps to reduce the amount of chemicals in the prevention against Fusarium sp. fungal diseases. According to Durán et al. [24] and Prabhu et al. [25], like silver nanoparticles, Cu Nps also demonstrated the size-dependent antibacterial activity. Therefore, to achieve the maximum antibacterial activity, it is necessary to develop various methods for the synthesis of monodisperse copper nanoparticles with small size; that is, the ratio of surface area to volume is large [26, 27].

There are many methods for synthesis of Cu Nps such as hydrothermal [28], photoreduction [29–31], thermal decomposition [11], and polyol and microwave-assisted polyol method [9, 32, 33]. However, the production of Cu Nps is much more challenging in comparison to noble metals because Cu Nps are placed in the open air leading to the aggregation immediately due to surface oxidation. To avoid this problem, an inert environment, such as argon or nitrogen, inorganic solvents, protective polymers, or surfactants, was used [34]. In the chemical reduction techniques, a copper salt is reduced by a reducing agent such as sodium borohydride (NaBH₄), hydrazine (N₂H₄), ascorbate, polyol, isopropyl alcohol with cetyltrimethylammonium bromide (CTAB), and glucose [34]. Besides, a literature review of Xiong et al. has reported that a simple, environmentally friendly, and cost-effective method for preparing highly stable dispersions of Cu Nps was used from green chemicals, such as Vitamin C (ascorbic acid, AsA) [35]. However, the ascorbic acid is a weak reducing agent; the reaction rate in the water solvent is slow; therefore, it takes more time to form Cu Nps (approximately 14 hours) [36–38]. In addition, the higher reaction temperature or longer reaction time favors the growth rate of pure metallic Cu [39, 40]. Therefore, reductive chemicals such as ascorbic acid and CTAB were combined in aqueous solution at 80°C to improve reaction rate in this study. Moreover, we study the surface plasmon resonance effect of Cu Nps via UV-Vis spectrum and investigation of the Fusarium sp. antifungal properties at various Cu Nps concentrations. The purpose of this investigation shows that Cu Nps are a significant potential as bactericidal agents.

2. Experimental

2.1. Materials

Cu Nps solutions were prepared by chemical reduction method from chemicals and materials including copper (II) chloride dehydrate (CuCl₂·2H₂O, Merck, Germany, 99.99%), cetyltrimethylammonium bromide [(C₁₆H₃₃)N(CH₃)₃Br, CTAB, India, 99.99%], deionized (DI) water from Thermo Scientific Equipment, ascorbic acid (C₆H₈O₆, India, 99.99%), D-glucose (C₆H₁₂O₆, Sigma-Aldrich, 99.5%), chloramphenicol (C₁₁H₁₂Cl₂N₂O₅), double-distilled water (Vietnam), and the TCBS agar (Difco, USA). The potatoes and dragons were made in Vietnam.

2.2. Synthesis of Cu Nps by a Chemical Reduction Method

In a typical synthesis, 0.1712 gram CuCl₂·2H₂O was stirred with 50 mL DI water in 15 minutes to form CuCl₂ solution having blue color. Next, 10 mL ascorbic acid (0.1 M) was slowly dropped into the above solution and the mixture solution achieved a pH of around 5. To survey the effect of CTAB, 10 mL CTAB (0.025 M) solution was slowly dropped into the mixture of CuCl₂ solution and ascorbic acid. These mixtures were kept at 80°C until a red-brown solution was obtained. During the course of the reaction, the solution turned into red-brown color indicating the formation of Cu NPs.

2.3. Characterization of Cu Nps

To examine the existence of Cu Nps in the synthesized solution, we determined the surface plasmon resonance properties throughout the absorption spectra in the UV-Vis band taken by using UV-visible spectrophotometer (U2910, Hitachi, Japan). The Fourier transform infrared spectroscopy (FT-IR) spectrum was recorded on a FT-IR spectrometer (Vertex 80, Bruker, Germany) with the range of 400 to 4000 cm⁻¹ in transmission mode at room temperature to identify the functional group present on the samples and responsible for the stability of nanoparticles. Morphologies include the sizes and shapes of the samples which were recorded by Transmission Electronic Microscope (TEM) on a JEM 1400 instrument. The X-ray diffraction (XRD) analysis was carried out (Bruker D8 Advance 5005) at a voltage of 45 kV with Cu Kα radiation (λ = 1.5406 Å) to examine the crystalline phase of synthesized nanoparticles.

2.4. The Test of the Fusarium sp. Antifungal Activity of Cu Nps

Firstly, Fusarium sp. fungal samples were taken from tomato and dragon fruit plants. After that, Fusarium sp. fungal samples were isolated in agar water media. This media was chosen for the fungal isolation media including 1000 mL distilled water, 20 g/L agar, and 0.25 g/L chloramphenicol. Secondly, the fungal samples were isolated and incubated in potato D-glucose agar (PDA) media including 1000 mL of distilled water, 20 g/L agar, 200 g potatoes, 20 g D-glucose, and 0.25 g/L chloramphenicol. Thirdly, we recorded the temperature, date, and time of incubated samples at survey times and observed the growth of fungus. Finally, we measured diameter of fungal colonies and estimated the inhibition efficiency of Cu Nps at various concentrations. The inhibition percentage of fungal plant pathogens was calculated by using formula as suggested by Vincent [41]:

Hence, is inhibition percentage; is growth of fungal plant pathogens in control (mm), and is growth of fungal plant pathogens in dual culture plate (mm).

3. Results and Discussion

3.1. Preparation of Cu Nps

Figure 1(a) shows the absorption spectra of the prepared samples and these samples after being stirred for 15 minutes. The absorption spectrum of the prepared samples shows two peaks at 420 nm and 560 nm wavelengths. Nevertheless, the absorption spectrum of the samples which were stirred for 15 minutes shows only a peak at 560 nm wavelength and its intensity has significantly increased. The peak at 560 nm relates to existence of the Cu Nps [31] and peaks from 400 nm to 420 nm of wavelength relate to the copper oxide nanoparticles [32]. According to [42–45], the peak at 550–600 nm of the wavelength can be assigned to the absorption of Cu Nps. This result indicated the rapid formation of the Cu Nps for 15-minute reaction. However, if the synthesized sample with a reductive chemical as ascorbic acid is used, Cu Nps will be not formed for 2-hour reaction but for 14-hour reaction. The statement mentioned above was demonstrated by the absorption spectrum of the synthesized sample at only ascorbic acid condition for 2-hour and 14-hour reactions (Figure 1(b)). This result agrees with Xiong et al.’ research [35].

(a)

(b)

(c)

Figure 1: Absorption spectra of the samples (a) supported CTAB and (b) nonsupported CTAB at different reaction periods and (c) the color of the synthesized samples.

Figure 1(c) shows the color of the synthesized sample with ascorbic acid and CTAB reduction chemicals for a 15-minute period and the other one synthesized only with ascorbic acid for 14-hour period of time. This result exhibited that the synthesized sample with only ascorbic acid was brown while the synthesized sample with the support of CTAB was red-brown.

Furthermore, the Cu Nps solution synthesized by the support of CTAB was evaporated at 150°C for 2 hours at atmosphere. After that, the Cu Nps powder was characterized by XRD pattern. Figure 2 exhibits the XRD pattern of Cu Nps powder. The peaks observed at 2θ values of 43.39°, 50.49°, and 74.18° correspond to (111), (200), and (220) planes of metallic Cu [11, 30, 46]. Apart from the metallic Cu peaks, several other diffraction peaks appeared at 36.54° and 61.6° representing the formation of cubic copper (I) oxide nanocrystals [37, 47, 48]. The result was explained that Cu Nps might be formed by oxidation when the solution was evaporated at 150°C for 2 hours at atmosphere.

Figure 2: XRD pattern of the Cu Nps powder.

3.1.1. Fourier Transform Infrared Spectroscopy (FTIR) Analysis

Figure 3 represents the appearance of some different peaks, such as peaks at 3400 cm⁻¹, 1630–1761 cm⁻¹, 1142–1345 cm⁻¹, and 724–928 cm⁻¹ bands of the wavenumber. According to Xiong et al. [35], the peaks were observed at 3481 cm⁻¹, 1718 cm⁻¹, and 1681 cm⁻¹ corresponding to the -OH stretch of the H₂O molecules, oxidized ester carbonyl groups, and conjugated carbonyl groups, respectively. Besides, according to Viana et al., peaks at broadband of the 900–1000 cm⁻¹ were presented for N-CH₃ stretching vibration [49]. The appearance of these peaks was caused by the residual CTAB after reactions creating Cu Nps completely.

Figure 3: FTIR spectrum of the Cu Nps solution.

3.1.2. Transmission Electron Microscopy (TEM) Analysis

The sizes and shapes of Cu Nps were characterized by TEM images. Figure 4 shows that the shapes of Cu NPs are spherical with uniform sizes. The particles size of Cu Nps is in the range from 20 nm to 50 nm. Besides, the shapes of Cu Nps are mainly spherical, which relates to copper phase [50].

(a)

(b)

Figure 4: TEM images of Cu Nps solution for different scales: (a) 100 nm and (b) 20 nm.

3.2. The Fusarium sp. Antifungal Properties of Cu Nps Solutions

We survey the effect of Cu Nps solutions on the development of Fusarium sp. by determining the diameter of the fungal colonies on the samples including the non-Cu Nps solution sample and other samples with Cu Nps solution with the concentrations of 300 ppm, 380 ppm, and 450 ppm, respectively. The diameter of the fungal colonies was determined after the incubation periods of 3 days, 6 days, and 9 days, respectively. The images of colonies according to incubation period at various Cu Nps concentrations are exhibited in Figure 5. These results show that Cu Nps inhibited the development of Fusarium sp. It demonstrated that the diameter of colonies in all samples was supplemented with Cu Nps being smaller than the reference sample. In 3-day incubation, the diameters of fungal colonies for additional formulations of 300 ppm and 380 ppm of Cu Nps were measured about 8.67 mm, while the reference sample developed rapidly with the diameter of the fungal colony being about 15.33 mm. The fungal colony of the sample at the Cu Nps concentration of 300 ppm is still developing in 9-day incubation, while the diameter of the fungal colony of the samples at the Cu Nps concentration of 380 ppm was approximately 44 mm after they were incubated for 6 days and it almost unchanged the next 3 days. Meanwhile, the diameter of Fusarium sp. colony was 5 mm. It remains after being incubated for 9 days. In addition, Figure 6 shows the change of the diameter of fungal colonies at various incubation periods for various concentrations of Cu Nps solutions. These diagrams show that the more the Cu Nps concentration increases, the more the diameter of fungal colonies decreases. Remarkably, the diagram of the diameter of the colonies with the Cu Nps concentration of 450 ppm was a straight line. This result demonstrated that the diameter of the fungal colony almost does not increase in the samples at the Cu Nps concentration of 450 ppm.

Figure 5: The diameter of Fusarium sp. colonies according to incubation period at various Cu Nps solution concentrations.

Figure 6: The diagram of the formation of the diameter of Fusarium sp. colonies according to incubation period at various Cu Nps solution concentrations.

From these above results, we determined the Fusarium sp. inhibition efficiency of Cu Nps solution and it was represented in Figure 7. These results show that the inhibition efficiency of Cu Nps was good in the in vitro condition. However, the inhibition efficiency of Cu Nps increases according to the concentration used. In a 3-day incubation, Cu Nps solutions inhibited 43% of growth of fungi of the samples at the concentration of 300 ppm and 380 ppm. Meanwhile, Cu Nps solution could inhibit 67.38% of the fungal growth at 450 ppm concentration after being incubated for 3 days and reaches 93.98% if incubated for 9 days. At this time the results show that inhibition efficiency of Cu Nps solution went up significantly due to 450 ppm concentration dish; the fungi were inhibited intensively and no longer grew in a 3-day incubation. In contrast, the fungi in the reference sample still grew normally and their diameter increased constantly.

Figure 7: The Fusarium sp. inhibition efficiency of Cu Nps solutions.

4. Conclusion

We successfully prepared Cu Nps for a short reaction time (about 15-minute reaction) by chemical reduction method with a support of CTAB reductive agent. The absorption spectrum of Cu Nps solutions prepared after a 15-minute reaction shows an absorption peak at 560 nm wavelength, a typical peak for the existence of Cu Nps. The size of Cu Nps is in the range from 20 nm to 50 nm and their shapes are mainly spherical. The more the Cu Nps concentration increases, the more the inhibition efficiency increases. Moreover, the diameter of the fungal colony almost does not increase and could inhibit 93.98% of the fungal growth at the 450 ppm Cu Nps concentration after a 9-day incubation.

Competing Interests

The authors declare that they have no competing interests.

Acknowledgments

The authors thank administration boards of University of Science, Vietnam National University Ho Chi Minh City and Ho Chi Minh City University of Technology (HUTECH) for supporting facilities. This research is funded by Ho Chi Minh City University of Technology (HUTECH).

References

M. Sahu and P. Biswas, “Single-step processing of copper-doped titania nanomaterials in a flame aerosol reactor,” Nanoscale Research Letters, vol. 6, no. 1, article 441, pp. 1–14, 2011.

H. Tian, X. L. Zhang, J. Scott, C. Ng, and R. Amal, “TiO₂-supported copper nanoparticles prepared via ion exchange for photocatalytic hydrogen production,” Journal of Materials Chemistry A, vol. 2, no. 18, pp. 6432–6438, 2014.

H. M. Yadav, S. V. Otari, V. B. Koli et al., “Preparation and characterization of copper-doped anatase TiO₂ nanoparticles with visible light photocatalytic antibacterial activity,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 280, pp. 32–38, 2014.

C. S. Chen, C. C. Chen, T. W. Lai, J. H. Wu, C. H. Chen, and J. F. Lee, “Water adsorption and dissociation on Cu nanoparticles,” Journal of Physical Chemistry C, vol. 115, no. 26, pp. 12891–12900, 2011.

S. T. H. Sherazi, R. A. Soomro, S. Uddin, and N. Memon, “Synthesis and characterizations of highly efficient copper nanoparticles and their use in ultra fast catalytic degradation of organic dyes,” Advanced Materials Research, vol. 829, pp. 93–99, 2013.

H.-J. Hwang, W.-H. Chung, and H.-S. Kim, “In situ monitoring of flash-light sintering of copper nanoparticle ink for printed electronics,” Nanotechnology, vol. 23, no. 48, Article ID 485205, 2012.

S. Magdassi, M. Grouchko, and A. Kamyshny, “Copper nanoparticles for printed electronics: routes towards achieving oxidation stability,” Materials, vol. 3, no. 9, pp. 4626–4638, 2010.

X.-F. Tang, Z.-G. Yang, and W.-J. Wang, “A simple way of preparing high-concentration and high-purity nano copper colloid for conductive ink in inkjet printing technology,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 360, no. 1–3, pp. 99–104, 2010.

B. K. Park, S. Jeong, D. Kim, J. Moon, S. Lim, and J. S. Kim, “Synthesis and size control of monodisperse copper nanoparticles by polyol method,” Journal of Colloid and Interface Science, vol. 311, no. 2, pp. 417–424, 2007.

A. D. Karthik and K. Geetha, “Synthesis of copper precursor, copper and its oxide nanoparticles by green chemical reduction method and its antimicrobial activity,” Journal of Applied Pharmaceutical Science, vol. 3, no. 5, pp. 16–21, 2013.

R. Betancourt-Galindo, P. Y. Reyes-Rodriguez, B. A. Puente-Urbina et al., “Synthesis of copper nanoparticles by thermal decomposition and their antimicrobial properties,” Journal of Nanomaterials, vol. 2014, Article ID 980545, 5 pages, 2014.

A. K. Chatterjee, R. K. Sarkar, A. P. Chattopadhyay, P. Aich, R. Chakraborty, and T. Basu, “A simple robust method for synthesis of metallic copper nanoparticles of high antibacterial potency against E. coli,” Nanotechnology, vol. 23, no. 8, Article ID 085103, 2012.

A. K. Chatterjee, R. Chakraborty, and T. Basu, “Mechanism of antibacterial activity of copper nanoparticles,” Nanotechnology, vol. 25, no. 13, Article ID 135101, 2014.

A. M. Muthukrishnan, “Green synthesis of copper-chitosan nanoparticles and study of its antibacterial activity,” Journal of Nanomedicine & Nanotechnology, vol. 6, no. 1, 2015.

M. S. Usman, M. E. El Zowalaty, K. Shameli, N. Zainuddin, M. Salama, and N. A. Ibrahim, “Synthesis, characterization, and antimicrobial properties of copper nanoparticles,” International Journal of Nanomedicine, vol. 8, pp. 4467–4479, 2013.

A. Servin, W. Elmer, A. Mukherjee et al., “A review of the use of engineered nanomaterials to suppress plant disease and enhance crop yield,” Journal of Nanoparticle Research, vol. 17, no. 2, pp. 1–21, 2015.

C. Booth, “The present status of fusarium taxonomy,” Annual Review of Phytopathology, vol. 13, no. 1, pp. 83–93, 1975.

D. S. Egel and R. D. Martyn, “Fusarium wilt of watermelon and other cucurbits,” The Plant Health Instructor, 2007.

K. A. Yadeta and B. P. H. J. Thomma, “The xylem as battleground for plant hosts and vascular wilt pathogens,” Frontiers in Plant Science, vol. 4, article 97, 2013.

P. E. Nelson, M. C. Dignani, and E. J. Anaissie, “Taxonomy, biology, and clinical aspects of Fusarium species,” Clinical Microbiology Reviews, vol. 7, no. 4, pp. 479–504, 1994.

S. Mandal, N. Mallick, and A. Mitra, “Salicylic acid-induced resistance to Fusarium oxysporum f. sp. lycopersici in tomato,” Plant Physiology and Biochemistry, vol. 47, no. 7, pp. 642–649, 2009.

K. Lairini and M. Ruiz-Rubio, “Detection of tomatinase from Fusarium oxysporum f. sp. Lycopersici in infected tomato plants,” Phytochemistry, vol. 45, no. 7, pp. 1371–1376, 1997.

K. Czaczyk, K. Trojanowska, and A. Mueller, “Antifungal activity of Bacillus coagulans against Fusarium sp,” Acta Microbiologica Polonica, vol. 51, no. 3, pp. 275–283, 2002.

N. Durán, P. D. Marcato, R. De Conti, O. L. Alves, F. T. M. Costa, and M. Brocchi, “Potential use of silver nanoparticles on pathogenic bacteria, their toxicity and possible mechanisms of action,” Journal of the Brazilian Chemical Society, vol. 21, no. 6, pp. 949–959, 2010.

B. M. Prabhu, S. F. Ali, R. C. Murdock, S. M. Hussain, and M. Srivatsan, “Copper nanoparticles exert size and concentration dependent toxicity on somatosensory neurons of rat,” Nanotoxicology, vol. 4, no. 2, pp. 150–160, 2010.

A. P. Ingle, N. Duran, and M. Rai, “Bioactivity, mechanism of action, and cytotoxicity of copper-based nanoparticles: a review,” Applied Microbiology and Biotechnology, vol. 98, no. 3, pp. 1001–1009, 2014.

P. Kanhed, S. Birla, S. Gaikwad et al., “In vitro antifungal efficacy of copper nanoparticles against selected crop pathogenic fungi,” Materials Letters, vol. 115, pp. 13–17, 2014.

H. Chen, J.-H. Lee, Y.-H. Kim et al., “Metallic copper nanostructures synthesized by a facile hydrothermal method,” Journal of Nanoscience and Nanotechnology, vol. 10, no. 1, pp. 629–636, 2010.

B. Wang, S. Chen, J. Nie, and X. Zhu, “Facile method for preparation of superfine copper nanoparticles with high concentration of copper chloride through photoreduction,” RSC Advances, vol. 4, no. 52, pp. 27381–27388, 2014.

X. Zhu, B. Wang, F. Shi, and J. Nie, “Direct, rapid, facile photochemical method for preparing copper nanoparticles and copper patterns,” Langmuir, vol. 28, no. 40, pp. 14461–14469, 2012.

N. Nishida, A. Miyashita, N. Hashimoto, H. Murayama, and H. Tanaka, “Regenerative synthesis of copper nanoparticles by photoirradiation,” The European Physical Journal D, vol. 63, no. 2, pp. 307–310, 2011.

M. Blosi, S. Albonetti, M. Dondi, C. Martelli, and G. Baldi, “Microwave-assisted polyol synthesis of Cu nanoparticles,” Journal of Nanoparticle Research, vol. 13, no. 1, pp. 127–138, 2011.

M. I. Dar, S. Sampath, and S. A. Shivashankar, “Microwave-assisted, surfactant-free synthesis of air-stable copper nanostructures and their SERS study,” Journal of Materials Chemistry, vol. 22, no. 42, pp. 22418–22423, 2012.

A. Umer, S. Naveed, N. Ramzan, and M. S. Rafique, “Selection of a suitable method for the synthesis of copper nanoparticles,” Nano, vol. 7, no. 5, Article ID 1230005, 2012.

J. Xiong, Y. Wang, Q. Xue, and X. Wu, “Synthesis of highly stable dispersions of nanosized copper particles using l-ascorbic acid,” Green Chemistry, vol. 13, no. 4, pp. 900–904, 2011.

B. Zümreoglu-Karan, “A rationale on the role of intermediate Au(III)-vitamin C complexation in the production of gold nanoparticles,” Journal of Nanoparticle Research, vol. 11, no. 5, pp. 1099–1105, 2009.

A. Khan, A. Rashid, R. Younas, and R. Chong, “A chemical reduction approach to the synthesis of copper nanoparticles,” International Nano Letters, vol. 6, no. 1, pp. 21–26, 2016.

H. Kang, B.-G. Kim, H. B. Na, and S. Hwang, “Anti-galvanic reduction of silver ion on gold and its role in anisotropic growth of gold nanomaterials,” The Journal of Physical Chemistry C, vol. 119, no. 46, pp. 25974–25982, 2015.

Y. C. Zhang, R. Xing, and X. Ya. Hu, “A green hydrothermal route to copper nanocrystallites,” Journal of Crystal Growth, vol. 273, no. 1-2, pp. 280–284, 2004.

Q.-L. Zhang, Z.-M. Yang, B.-J. Ding, X.-Z. Lan, and Y.-J. Guo, “Preparation of copper nanoparticles by chemical reduction method using potassium borohydride,” Transactions of Nonferrous Metals Society of China, vol. 20, no. 1, pp. s240–s244, 2010.

J. M. Vincent, “Distortion of fungal hyphæ in the presence of certain inhibitors,” Nature, vol. 159, no. 4051, p. 850, 1947.

C. Barrière, K. Piettre, V. Latour et al., “Ligand effects on the air stability of copper nanoparticles obtained from organometallic synthesis,” Journal of Materials Chemistry, vol. 22, no. 5, pp. 2279–2285, 2012.

J. A. Creighton and D. G. Eadon, “Ultraviolet-visible absorption spectra of the colloidal metallic elements,” Journal of the Chemical Society, Faraday Transactions, vol. 87, no. 24, pp. 3881–3891, 1991.

N. A. Dhas, C. P. Raj, and A. Gedanken, “Synthesis, characterization, and properties of metallic copper nanoparticles,” Chemistry of Materials, vol. 10, no. 5, pp. 1446–1452, 1998.

P. K. Khanna, T. S. Kale, M. Shaikh, N. K. Rao, and C. V. V. Satyanarayana, “Synthesis of oleic acid capped copper nano-particles via reduction of copper salt by SFS,” Materials Chemistry and Physics, vol. 110, no. 1, pp. 21–25, 2008.

H. Zhu, C. Zhang, and Y. Yin, “Novel synthesis of copper nanoparticles: influence of the synthesis conditions on the particle size,” Nanotechnology, vol. 16, no. 12, pp. 3079–3083, 2005.

P. Martis, A. Fonseca, Z. Mekhalif, and J. Delhalle, “Optimization of cuprous oxide nanocrystals deposition on multiwalled carbon nanotubes,” Journal of Nanoparticle Research, vol. 12, no. 2, pp. 439–448, 2010.

M. S. M. Suan, M. R. Johan, N. L. Hawari, and H. A. Ching, “Annealing effects on the properties of copper oxide thin films prepared by chemical deposition,” International Journal of Electrochemical Science, vol. 6, no. 12, pp. 6094–6104, 2011.

R. B. Viana, A. B. F. da Silva, and A. S. Pimentel, “Infrared spectroscopy of anionic, cationic, and zwitterionic surfactants,” Advances in Physical Chemistry, vol. 2012, Article ID 903272, 14 pages, 2012.

M. A. Ben Aissa, B. Tremblay, A. Andrieux-Ledier, E. Maisonhaute, N. Raouafi, and A. Courty, “Copper nanoparticles of well-controlled size and shape: a new advance in synthesis and self-organization,” Nanoscale, vol. 7, no. 7, pp. 3189–3195, 2015.