We demonstrated a flash memory device with chemical-vapor-deposited graphene as a charge trapping layer. It was found that the average RMS roughness of block oxide on graphene storage layer can be significantly reduced from 5.9 nm to 0.5 nm by inserting a seed metal layer, which was verified by AFM measurements. The memory window is 5.6 V for a dual sweep of ±12 V at room temperature. Moreover, a reduced hysteresis at the low temperature was observed, indicative of water molecules or −OH groups between graphene and dielectric playing an important role in memory windows.
1. Introduction
Flash memory has been highly demanded for mobile phone, digital camera, communication system, and data storage owing to its small size, high density, and low power. However, lateral scaling in flash memory will increase the capacitive coupling between the adjacent floating gates [1]. This parasitic capacitive coupling between neighboring cells will induce a wide distribution of threshold voltage because of the cell-to-cell interference, leading to a remarkable read-out error in circuits. In particular beyond the 12 nm node, the issue of cell-to-cell interference will become much more severe [2]. To address this problem, the floating gate thickness reduction is one possible way. For conventionally used poly-Si floating gates, its thickness can be reduced to several nanometers; however, it will bring a large ballistic current during program processes [3], causing significant reliability issues. On the other hand, the charge storage capability in floating gates will degrade because of reduced density of state of poly-Si under such continuous scaling along the thickness direction [4]. Although thin metal layer was proposed to replace poly-Si floating gate, there are many other issues introduced at high temperatures, such as diffusion of metal into the blocking and tunneling oxide layer, and metal induced dielectric crystallization [5–7].
Recently, graphene, a two-dimension single layer of carbon atoms with sp2 hybridized structure, has emerged as a promising material for future electronic applications owing to its unique physical and electrical properties [8–13]. Because the interlayer spacing between two monolayer graphene sheets is 0.34 nm [8], then the thickness of multilayer (e.g., 4–8 layers) graphene is around 1.5–3 nm, which may be implemented into flash memory for the thickness reduction in the floating gate. Note that its work function of ~4.6 can be stabilized when the number of graphene layers reaches 4 [14]. Moreover, its thermal stability (>1000°C) vanishes the diffusion issues at high temperatures, offering the benefits to the integration of memory devices. There are additional advantages for multilayer graphene as a floating gate, for example, (1) being compatible with conventional planar CMOS process line; (2) suppression of the ballistic current along the thickness direction because of reduced conductivity between layers; (3) large DOS; and (4) high work function which can increase the capability for storage and long-term data retention [5, 15]. It was reported that graphene layers can be utilized as not only a floating gate for conventional silicon MOS capacitors [5, 15] but also a novel channel material of transition metal dichalcogenide, for example, MoS2 [16], high-k stack or PZT based charge-trap memory [17–20], organic nonvolatile memory [21], and transparent flexible charge-trap memory [22]. A large hysteresis (memory window) of ~6 V was observed under a low voltage program/erase process [15]. In addition, graphene oxide (GO) was also incorporated into TANOS as a trapping layer, while it suffers the reliability issues since the charge storage capability will significantly degrade at high temperatures [23].
In this work, we demonstrated a flash memory device with chemical-vapor-deposited graphene as a charge trapping layer. The fabricated devices exhibit an increased memory window as a dual sweep bias was enhanced. Interestingly, we also observed a reduced hysteresis at low temperature, indicative of −OH or water molecules between graphene and dielectric playing an important role in memory windows.
2. Experimental Details
Graphene layers were prepared by a chemical-vapor-deposition (CVD) technique in a home-made tube furnace. An 850 nm thick Cu film was thermally evaporated on the mica substrate at 500°C, where atomically flat surface of single crystal mica substrate was obtained by a tape cleaving [8]. To remove oxidized layer and contaminations on Cu surface, Cu/mica substrates were annealed in H2/Ar gas ambient at 1000°C for half hours prior to the graphene growth [24]. Then graphene was grown on the Cu/mica substrate by introducing CH4 in the tube at the same temperature and the pressure inside the tube was kept roughly at one atmosphere. Graphene size (50 μm × 50 μm) was patterned by definition by lithography and followed by an O2-plasma etching. The Cu film on mica was dissolved in HCl aqueous solution. The schematic device structure, optical image of the fabricated device, and its fabrication processes are illustrated in Figures 1(a), 1(b), and 1(c), respectively.
(a) The schematic of graphene flash memory cell (Au/Al2O3/graphene/SiO2/p-Si). (b) Top-view of fabricated graphene flash memory cell. The scale bar is 20 μm. (c) Process flow of fabricated graphene flash memory cell.
The tunneling oxide was a thermally grown 5 nm thick SiO2. The thickness of the tunneling oxide is determined from both ellipsometer spectrometry and separate electrical C-V measurements. Graphene was then transferred onto the SiO2 (5 nm)/p-Si substrate using the polymethyl methacrylate- (PMMA-) assisted transfer method [24]. Prior to the growth of the blocking oxide, a seed layer of Al was deposited onto graphene/SiO2/Si and oxidized in the O2 ambient. A 20 nm thick Al2O3 was subsequently deposited by atomic-layer deposition (ALD), where Al2O3 was grown using trimethyl aluminum (TMA) and H2O as precursors at 200°C. The relative dielectric constant of Al2O3 is extracted to be 7.5 from the control sample. Finally the top electrode was formed in turn by electron-beam lithography, thermal evaporation of Au, and a lift-off process in acetone. The Raman characterization was carried out by an Ar laser unit of 488 nm excitation. The surface roughness (RMS) was analyzed by atomic force microscopy (AFM). The electrical I-V and C-V measurements were performed using a semiconductor (Agilent B1500A) device analyzer and a precise impedance analyzer (Agilent 4294A) with a 50 mV AC amplitude at 100 KHz, respectively.
3. Results and Discussion
Figure 2(a) shows the optical image of as-transferred graphene film on SiO2/Si substrate. To better characterize CVD graphene, a silicon substrate with 90 nm SiO2 was used here for the best optical contrast. The surface coverage of as-transferred bilayer graphene is more than 50%. Note that all the Raman spectra shown in this paper are calibrated using silicon peak at 520 cm−1. Figure 2(b) shows the typical Raman spectra of monolayer and bilayer CVD graphene. It can be clearly seen that there is a D band in the as-transferred CVD graphene. It is quite different from the pristine one mechanically exfoliated from bulky graphite, which only has two main characteristic peaks of G and 2D. This infers that transfer process needs to be further improved for the high quality graphene on SiO2/Si substrate. Note that a sharp line width (~30 cm−1) and a single Lorentzian lineshape in 2D band were also observed for bilayer CVD graphene. It is due to an ordered AB stacking, resulting in a week electronic coupling between graphene layers [25].
(a) The optical image of as-transferred CVD graphene on SiO2/Si substrate. The image size is 20 μm × 20 μm. (b) Raman spectra of as-transferred monolayer and bilayer graphene.
Owing to its inherent characteristic of no dangling bonds, the top gate dielectric is quite tough to be formed on graphene. In order to alleviate this issue, a seed layer of Al was deposited and oxidized into an Al2O3 layer. Figures 3(a) and 3(b) show the AFM images of an atomic-layer-deposited 100-cycle Al2O3 film on highly oriented pyrolytic graphite (HOPG) substrate without and with an Al seed layer, respectively. It was observed that a striped pattern of Al2O3 film was formed along grain boundaries and defects sites without an Al seed layer, while a fairly uniform Al2O3 surface was achieved on HOPG with an Al seed layer. This prominent difference in Al2O3/HOPG lies in the chemical inertness of HOPG surface, thus leading to a deep cluster or nucleation of Al2O3 dielectric film preferentially in the sites of grain boundaries [26, 27]. It is worthwhile to mention that, in contrast to the pristine graphene, the functionalized surface is prone to ALD growth of a uniform high-k dielectric film although the film quality still needs further improvement [28]. The surface roughness (RMS) of an atomic-layer-deposited 100-cycle Al2O3 film on HOPG using various thickness of Al seed layer was summarized in Figure 3(c). Without an Al seed layer, its average RMS is as large as ~5.9 nm, while it decreases to 0.55 nm when a 0.2 mg Al metal (~1 nm Al2O3) target was evaporated for the seed layer. It was also found that the RMS roughness can be further reduced if the thickness of an Al seed layer increases, as shown in Figure 3(c).
(a) Atomic force microscopy (AFM) image of an atomic-layer-deposited 100-cycle Al2O3 film on highly oriented pyrolytic graphite (HOPG) substrate without and with an Al seed layer. The scale bar is 500 nm. (b) Surface roughness (RMS) of an atomic-layer-deposited 100-cycle Al2O3 film on HOPG without and with 0.2 mg, 0.3 mg, and 0.4 mg Al for the seed layer thermal evaporation.
Next, we turn to the C-V measurements of fabricated graphene flash memory cell with the help of an Al seed layer. Figure 4(a) shows the representative C-V characteristics of fabricated graphene flash cell at room temperature. There is a clear hysteresis of ~2.3 V under a dual sweep of ±8 V for the Au/Al2O3/graphene/SiO2/p-Si cell. For the control sample, almost no noticeable hysteresis was observed, as shown in the inset of Figure 4(a). The comparison of hysteresis for both graphene flash memory and control cell under various dual sweep biases is illustrated in Figure 4(b). It can be noticed that the memory window is 1.0 V, 2.3 V, 4.0 V, and 5.6 V for the dual sweep of ±6 V, ±8 V, ±10 V, and ±12 V, respectively. The amount of charge storage in graphene layers can be estimated by Δn=Ccon×ΔV/q, where Ccon is the unit control gate capacitance, that is, the capacitance of Al2O3 layer,ΔV is the memory window, and q is the unit electron charge. As a result, the storage charge density in graphene layer for the hysteresis of ~2.3 V in Figure 4(a) is accordingly around 4.76×1012 cm−2. In contrast to graphene flash memory cell, only a small hysteresis of ~40 mV at the dual sweep of ±12 V remains for the control cell at room temperature; see Figure 4(b). This indicates a pronounced memory window in graphene flash memory cell, where the memory effect results from the charge storage in graphene film, consistent with the previous reports [7, 15]. Compared to monolayer and bilayer graphene, a significant hysteresis may take place in few layer graphene based flash memory because of its large density of state [15]. The process improvement of the growth of multilayer graphene is further needed to realize large memory windows.
(a) Representative capacitance-voltage (C-V) characteristics of fabricated graphene flash memory at room temperature (RT). Inset shows C-V characteristics of the control sample. The arrows denote the sweep directions. (b) Comparison of hysteresis of graphene flash memory cell and control sample at both RT and 250 K.
We also examined the C-V characteristics of graphene flash cells at low temperature of 250 K. It is interesting that the memory window for graphene flash memory cell decreases significantly, as shown in Figure 4(b), that is, even only a small hysteresis of 1.5 V for a dual sweep of ±12 V. Similar hysteretic behaviors have also been observed in the Id-Vg behaviors for a dual sweep Vg in the back-gated graphene field-effect transistor [29], and Dirac point shift in a quantum capacitance measurement [30]. This reduction in the hysteresis in graphene or carbon nanotube field-effect transistors was attributed to the orientation polarization of water [29–36]. Hydroxyl groups (−OH) can couple to the dangling bonds of Si and build up a layer of silanol (SiOH) groups, which is very hydrophilic [37, 38]. Water molecules can easily attach to the SiOH and contribute to the charge transfer [36]. It was reported that the formation of Si–O–Si siloxane from the hydration of silanol groups will take place at more than 450°C [39]. In case of our transfer process, water molecules bonding to Si–OH silanol groups will thus inevitably be introduced in the interfaces between graphene and dielectrics (e.g., SiO2). The fact that the hysteresis reduces significantly at low temperatures indicates there is a clear mechanism difference in electron trapping in graphene flash cell. Thus, it is believed that the orientation polarization of water molecules plays a crucial role in the memory window for graphene memory devices at the low temperature.
4. Conclusion
In summary, a flash memory device with chemical-vapor-deposited graphene as a charge trapping layer was fabricated. A buffer Al2O3 layer oxidized from a seed layer can reduce one order of magnitude of the average RMS roughness, prior to the growth of ALD Al2O3 blocking oxide, which is important to achieve high performance graphene memory devices. In addition, large memory window of 5.6 V was observed for a dual sweep of ±12 V at room temperature. It exhibits a remarkable reduction in memory window at the low temperature, which is attributed to the decrease of water polarization.
Conflict of Interests
The authors declare that there is no conflict of interests regarding the publication of this paper.
Acknowledgments
This work was supported in part by the Japan Society for the Promotion of Science (JSPS) and the Startup Project JJH1233103 at Fudan University in China. W. J. Liu would like to thank Professor A. Toriumi and K. Nagashio for their valuable comments and suggestions.
LeeJ.-D.HurS.-H.ChoiJ.-D.Effects of floating-gate interference on NAND flash memory cell operation200223526426610.1109/55.9988712-s2.0-0036575326CaoW.KangJ. H.BertolazziS.KisA.BanerjeeK.Can 2D-nanocrystals extend the lifetime of floating-gate transistor based nonvolatile memory?201461103456346410.1109/ted.2014.23504832-s2.0-84907478469RaghunathanS.KrishnamohanT.ParatK.SaraswatK.Investigation of ballistic current in scaled floating-gate NAND FLASH and a solutionProceedings of the International Electron Devices Meeting (IEDM '09)December 2009Baltimore, Md, USA1410.1109/iedm.2009.54242162-s2.0-77952372931JayantiS.YangX.SuriR.MisraV.Ultimate scalability of TaN metal floating gate with incorporation of high-k blocking dielectrics for flash memory applicationsProceedings of the IEEE International Electron Devices Meeting (IEDM '10)December 2010San Francisco, Calif, USA5.3.15.3.410.1109/IEDM.2010.5703301MisraA.KalitaH.WaikarM.GourA.BhaisareM.KhareM.AslamM.KottantharayilA.Multilayer graphene as charge storage layer in floating gate flash memoryProceedings of the 4th IEEE International Memory Workshop (IMW '12)May 2012Milan, Italy1410.1109/imw.2012.62136262-s2.0-84864119961SinghP. K.SinghK. K.HofmannR.ArmstrongK.KrishnaN.MahapatraS.Au nanocrystal flash memory reliability and failure analysisProceedings of the 15th IEEE International Symposium on the Physical and Failure Analysis of Integrated Circuits (IPFA '08)July 2008SingaporeIEEE1510.1109/ipfa.2008.45881902-s2.0-51949105743JayantiS.YangX.MisraV.Investigation of thermal stability of high-k interpoly dielectrics in TaN metal floating gate memory structuresProceedings of the 3rd IEEE International Memory Workshop (IMW '11)May 2011Monterey, Calif, USA1410.1109/imw.2011.58731832-s2.0-79960015313NovoselovK. S.GeimA. K.MorozovS. V.JiangD.ZhangY.DubonosS. V.GrigorievaI. V.FirsovA. A.Electric field effect in atomically thin carbon films2004306569666666910.1126/science.11028962-s2.0-7444220645GeimA. K.NovoselovK. S.The rise of graphene20076318319110.1038/nmat18492-s2.0-33847690144ZhangY.TanY.-W.StormerH. L.KimP.Experimental observation of the quantum Hall effect and Berry's phase in graphene2005438706520120410.1038/nature042352-s2.0-27744475163LinY.-M.DimitrakopoulosC.JenkinsK. A.FarmerD. B.ChiuH.-Y.GrillA.AvourisP.100 GHz transistors from wafer-scale epitaxial graphene20103275966, article 66210.1126/science.11842892-s2.0-76249106631SchwierzF.Graphene transistors20105748749610.1038/nnano.2010.892-s2.0-77955231284SchedinF.GeimA. K.MorozovS. V.HillE. W.BlakeP.KatsnelsonM. I.NovoselovK. S.Detection of individual gas molecules adsorbed on graphene20076965265510.1038/nmat19672-s2.0-34548388792HibinoH.KageshimaH.KotsugiM.MaedaF.GuoF.-Z.WatanabeY.Dependence of electronic properties of epitaxial few-layer graphene on the number of layers investigated by photoelectron emission microscopy2009791212543710.1103/physrevb.79.1254372-s2.0-65149099405HongA. J.SongE. B.YuH. S.AllenM. J.KimJ.FowlerJ. D.WasseiJ. K.ParkY.WangY.ZouJ.KanerR. B.WeillerB. H.WangK. L.Graphene flash memory20115107812781710.1021/nn201809k2-s2.0-80055020282BertolazziS.KrasnozhonD.KisA.Nonvolatile memory cells based on MoS2/graphene heterostructures2013743246325210.1021/nn30591362-s2.0-84876526582ZhanN.OlmedoM.WangG. P.LiuJ. L.Graphene based nickel nanocrystal flash memory2011991111311210.1063/1.36402102-s2.0-80053206995LeeS.SongE. B.KimS.SeoD. H.SeoS.KangT. W.WangK. L.Impact of gate work-function on memory characteristics in Al2O3/HfOx/Al2O3/graphene charge-trap memory devices2012100202310910.1063/1.3675633ImamS. A.DeshpandeT.GuermouneA.SiajM.SzkopekT.Charge transfer hysteresis in graphene dual-dielectric memory cell structures201199808210910.1063/1.36302272-s2.0-80052421086SongE. B.LianB.Min KimS.LeeS.ChungT.-K.WangM.ZengC.XuG.WongK.ZhouY.RasoolH. I.SeoD. H.ChungH.-J.HeoJ.SeoS.WangK. L.Robust bi-stable memory operation in single-layer graphene ferroelectric memory201199404210910.1063/1.36198162-s2.0-79961097218JiY. S.ChoeM.ChoB. J.SongS. H.YoonJ. W.KoH. C.LeeT.Organic nonvolatile memory devices with charge trapping multilayer graphene film2012231010520210.1088/0957-4484/23/10/1052022-s2.0-84863155473KimS. M.SongE. B.LeeS.ZhuJ.SeoD. H.MecklenburgM.SeoS.WangK. L.Transparent and flexible graphene charge-trap memory2012697879788410.1021/nn302193q2-s2.0-84866638173WangS.PuJ.ChanD. S. H.ChoB. J.LohK. P.Wide memory window in graphene oxide charge storage nodes2010961414310910.1063/1.3383234QiJ. L.NagashioK.NishimuraT.ToriumiA.The crystal orientation relation and macroscopic surface roughness in hetero-epitaxial graphene grown on Cu/mica2014251818560210.1088/0957-4484/25/18/1856022-s2.0-84898987638ReinaA.JiaX.HoJ.NezichD.SonH.BulovicV.DresselhausM. S.JingK.Large area, few-layer graphene films on arbitrary substrates by chemical vapor deposition200991303510.1021/nl801827v2-s2.0-60749107706TakahashiN.WatanabeK.TaniguchiT.NagashioK.Direct deposition of high-k Y2O3 on h-BN by atomic layer depositionProceedings of the International Conference on Solid-state Devices and Materials (SSDM '14)September 2014Ibaraki, Japan1076TakahashiN.TaniguchiT.WatanabeK.NagashioiK.Atomic layer deposition of Y2O3 on h-BN for a gate stack in graphene FETs20152617175708ZhouP.YangS. B.SunQ. Q.ChenL.WangP. F.DingS. J.DavidW. Z.Direct deposition of uniform high-κ dielectrics on graphene20144, article 644810.1038/srep06448LiuW. J.SunX. W.TranX. A.FangZ.WangZ. R.WangF.WuL.ZhangJ. F.WeiJ.ZhuH. L.YuH. Y.Observation of the ambient effect in BTI characteristics of back-gated single layer graphene field effect transistors20136082682268610.1109/ted.2013.22675412-s2.0-84880883167NagashioK.NishimuraT.ToriumiA.Estimation of residual carrier density near the Dirac point in graphene through quantum capacitance measurement20131021717350710.1063/1.48044302-s2.0-84877308824LevesqueP. L.SabriS. S.AguirreC. M.GuillemetteJ.SiajM.DesjardinsP.SzkopekT.MartelR.Probing charge transfer at surfaces using graphene transistors201111113213710.1021/nl103015w2-s2.0-79951524112RyuS.LiuL.BerciaudS.YuY.-J.LiuH.KimP.FlynnG. W.BrusL. E.Atmospheric oxygen binding and hole doping in deformed graphene on a SiO2 substrate201010124944495110.1021/nl10296072-s2.0-78650122340KimW.JaveyA.VermeshO.WangQ.LiY.DaiH.Hysteresis caused by water molecules in carbon nanotube field-effect transistors20033219319810.1021/nl02592322-s2.0-0042948502LohmannT.Von KlitzingK.SmetJ. H.Four-terminal magneto-transport in graphene p-n junctions created by spatially selective doping2009951973197910.1021/nl900203n2-s2.0-66449102397NagashioK.YamashitaT.NishimuraT.KitaK.ToriumiA.Electrical transport properties of graphene on SiO2 with specific surface structures2011110202451310.1063/1.36113942-s2.0-79961117487LafkiotiM.KraussB.LohmannT.ZschieschangU.KlaukH.KlitzingK. V.SmetJ. H.Graphene on a hydrophobic substrate: doping reduction and hysteresis suppression under ambient conditions20101041149115310.1021/nl903162a2-s2.0-77951026437AsayD. B.KimS. H.Evolution of the adsorbed water layer structure on silicon oxide at room temperature200510935167601676310.1021/jp053042o2-s2.0-25444433657AsayD. B.BarnetteA. L.KimS. H.Effects of surface chemistry on structure and thermodynamics of water layers at solid-vapor interfaces200911362128213310.1021/jp806815p2-s2.0-65249154200HirashitaN.TokitohS.UchidaH.Thermal desorption and infrared studies of plasma-enhanced chemical vapor deposited SiO films with tetraethylorthosilicate1993324, part 1178710.1143/JJAP.32.1787