Both n-channel and p-channel thin-film transistors have been realized on ZnO nanoparticle (NP) layers sprayed onto quartz substrates. In this study, nitrogen-doped ZnO-NPs were synthesized using an arc-discharge-mediated gas-evaporation method that was recently developed. Sprayed NP layers were characterized by scanning electron microscopy and Hall effect measurements. It was confirmed that p-type behaving NP layers can be obtained using ZnO-NPs synthesized with lower chamber pressure, whereas n-type conductivity can be obtained with higher chamber pressure. pn-junction diodes were also tested, resulting in clear rectifying characteristics. The possibility of particle-process-based ZnO-NP electronics was confirmed.
Japan Society for the Promotion of Science258704481. Introduction
Zinc oxide (ZnO) attracts considerable attention because it is an oxide semiconductor with a direct wide bandgap of 3.37 eV at room temperature, it can be developed for large-area substrates, and it exhibits high-field effect mobility. Due to these advantages, ZnO is a promising candidate for applications to optoelectronic devices such as light-emitting diodes (LEDs) [1] and laser diodes, as well as to electronic devices such as thin-film transistors (TFTs) [2–6].
One difficulty faced by ZnO application is that it is challenging to obtain p-type conductivity with this material because of the compensation by intrinsic donor defects such as oxygen vacancies and Zn interstitials [7, 8]. Various approaches have been reported for achieving p-type ZnO layers, like doping with group Ia [9, 10], Ib [11], and V [12–15] elements, codoping with group Ia, III, or V elements [16, 17], and so on [18, 19]. However, few results can achieve LED or TFT operations using the obtained p-type layers.
We recently succeeded in synthesizing nitrogen-doped ZnO nanoparticles (NPs) using a gas-evaporation method. This method was confirmed to p-type conductivity using the scanning nonlinear dielectric microscopy (SNDM) technique [20]. Fujita et al. [21] reported pn-junction-type near-ultraviolet (UV) LEDs using these NPs on Ga-doped ZnO (GZO) films. These results suggest that doped nitrogen atoms are incorporated into oxygen sites, acting successfully as acceptors [21–25]. By regulating the conditions of the gas-evaporation method, ZnO-NPs with n-type conductivity can also be obtained [20]. These results strongly indicate that both p-type and n-type ZnO-NP layers can be obtained, allowing the achievement of p- and n-channel ZnO-TFTs. Previously, some approaches were developed to form TFTs using ZnO-NP layers [26–29]; however, only n-type conductive NP layers succeeded for TFT operations.
In this study, we attempt to realize both p- and n-type ZnO-NP layers on glass (quartz) substrates using a spray method. Then, we present the first ever demonstration of p- and n-channel depletion-type TFTs.
2. Experimental
ZnO-NPs were synthesized by arc-discharge-mediated gas evaporation using dry air, as shown in Figure 1(a). By this method, Zn metal was evaporated by direct current (DC) arc discharge and oxidized in the supplied dry air. Incorporation and doping of nitrogen atoms at O-sites in ZnO-NPs were performed by N2 radicals generated by arc plasma. Thus, extending the lifetime of N2 radicals and increasing the number of O vacancies were effective means of nitrogen doping. The low chamber pressure led to the lifetime extension of N2 radicals through fewer collisions, and the high arc current caused excess evaporation of Zn, leading to deficiency of oxygen. In our evaporation system, a chamber pressure of 150 Torr and an arc current of 50 A were suitable for enhanced nitrogen doping (referred to as “type A”); on the other hand, 610 Torr and 30 A were chosen for suppressed nitrogen doping (referred to as “type B”), in the expectation of obtaining p-type and n-type ZnO-NPs, respectively.
Schematic illustrations of (a) the gas-evaporation method and (b) the spray method.
The dispersions used for the spray process were prepared by mixing and dispersing 0.2 g of ZnO-NPs and 20 g of water using an ultrasonic homogenizer with power of 150 W for 3 min and by centrifuging with a force of 3,000 G for 1 min to remove large-sized NPs. Particle size distributions using type A and type B NPs were similar to the median size of 200 nm.
The NP layers were formed on the quartz substrates by a spray method, as shown in Figure 1(b). 30 mL of dispersion fluid was sprayed over 500 bursts with 5 s intervals. The hotplate temperatures were 250°C and 500°C for dispersions with type A and type B NPs, respectively. To avoid desorption of the nitrogen atoms from NPs, a reduced temperature was applied for the former ones.
Morphologies were examined by field-emission scanning electron microscopy (FESEM; JSM-7001FA, JEOL, 5 kV). The sheet resistance was determined independently by the transfer length method (TLM) for electrode distances of 100 to 500 μm, and the electronic mobility and carrier concentration were evaluated by the van der Pauw method (HL5500PC with HL5580 Buffer Amplifier, ACCENT). For ohmic electrodes, based on their different work functions, Au and Al were used for the layers using type A and type B NPs, respectively.
3. Results and Discussions
Figure 2(a) shows the typical cross-sectional SEM image for the obtained ZnO-NP layer, indicating that the thickness of the obtained NP layer was about 20 μm, which agrees with the value calculated using the sprayed area and the total volume of the sprayed particles. Figures 2(b) and 2(c) show the top view of the sprayed surfaces with type A and type B NPs, respectively. Both images indicate that the quartz surfaces were covered with NPs with sufficient uniformity. Figure 2(b) shows relatively rough morphology, since the hotplate temperature was lower and it needed a relatively long time to evaporate, leading to cohesion phenomenon.
(a) Cross-sectional SEM images of the ZnO-NP layer. SEM top view images for sprayed (b) type A and (c) type B NP layers.
The Hall effect measurement results for NP layers using type A and type B NPs are summarized in Table 1. A notable result is the carrier polarity shown in the signs of the carrier concentrations. Especially in the values for type A NP layers, signs of plus were obtained reproducibly. Furthermore, another behavioral analysis between the carrier concentration (sign and quantity) and the content of nitrogen atoms, which were examined using ZnO-NPs synthesized with different arc current and chamber pressure, showed significant relationship; that is, high nitrogen content yielded a plus sign and low content yielded a minus sign (not shown here). From these results, it can be guessed that the type A NP layers have p-type conductivity. The mobility of type A NP layers (hole) was larger than the mobility of type B ones (electron), whereas the hole mobility is smaller than the electron mobility in usual single crystal ZnO [19]. Recent nitrogen-doped ZnO-NP layers containing grain boundaries (GBs) show similar behaviors [13–15]. Generally, the GBs affect the carrier transfer, since the majority carriers will be trapped at the defects in GBs’ site with forming energy barriers as shown in Figure 3(a). But, in p-ZnO-NP layers, if the electrons were trapped at the defects in GBs’ site, hole transfer may not be affected by GBs (as shown in Figure 3(b)). One report [30] indicates that the excess oxygen at the GB area acts as acceptor, capturing the electrons and assisting the hole transfer. It was confirmed that there was OH group at the surface of ZnO-NPs used in this study [31], which may contribute to electron trapping at GB site and behave similarly as shown in Figure 3(b). Another approach to explain the higher hole mobility compared to electron one in the NP layers (quantum dot films) was provided in the recent literature [32], applying the variable-range hopping model to the carrier transfer from one NP to neighboring NPs. In this calculation, NP layers with size dispersions can be determined using molecular dynamics simulations. For the random distribution of various NP sizes in the film, which is suitable for ZnO-NP layers used in this study, the resultant degradation of the electron mobility increased with the increase of the size dispersion, while the hole mobility showed less degradation. Since the size dispersions of ZnO-NPs used in this study are large enough compared to those in these calculations, larger degradation of electron mobility than that of hole mobility should occur, leading to higher mobility in type A NP layers. Here, it is not clear yet which model (i.e., enlarging the hole mobility by the electrons in GBs or the degradation of the electron mobility by large-size dispersions of NPs) is true; however, the reproducible larger mobility values can be evidence for p-type conduction in type A ZnO-NP layers. On the other hand, the low carrier concentration and the high sheet resistance values indicate that further investigations and process optimizations are required. In this paper, for convenience, the layers formed using type A and type B NPs are described as p-type and n-type layers, respectively.
Hall measurement results.
Parameters
Type A
Type B
Mobility (cm2/Vs)
5.04~6.98
0.18~0.74
Carrier concentration (cm−3)
+2.0×1012~+2.7×1012
-7.0×1015~-5.5×1016
Sheet resistance (Ω/□)
2.3×109
2.5×106
Carrier trapped conditions and band diagrams around GB regions for (a) the usual cases and (b) the acceptor type traps.
By stacking the p-type ZnO-NP layer on the n-type one, pn-junction diodes were fabricated on quartz substrates, as schematically shown in the inset of Figure 4(a). The spraying conditions for each of the n-type and p-type layers were the same as described above. The obtained I-V characteristic is shown in Figure 4(a), indicating some rectifying characteristics. To avoid Schottky barrier formation, ohmic behaviors were examined individually on n- and p-type layers, as shown in Figures 4(b) and 4(c), respectively. Obvious ohmic contacts were confirmed at the contacting electrodes on each n- and p-type ZnO-NP region. Thus, the rectifying behavior shown in Figure 4(a) was confirmed to be obtained from the pn-junction structure. However, the leakage current in the reverse bias region was relatively high; in synthesizing the p-type ZnO-NPs, an inhomogeneous arc plasma density distribution may have caused the formation of fewer nitrogen-doped or n-type NPs, whose possibility was discussed in [21]. One possible reason for the leakage current in the reverse bias region is the existence of n-type NPs in the p-type layer. Another problem is that the turn-on voltage in the forward bias region was smaller than about 3 V, which was expected from the ZnO bandgap energy. The conductive mechanism in the NP film may affect this point; however, further investigation is required.
(a) I-V characteristic of the pn-junction diode studied in this paper. The cross-sectional illustration is in the inset. Ohmic tests for the contact electrodes on (b) n-type and (c) p-type ZnO-NP layers, respectively.
Back gate metal-oxide-semiconductor depletion-type TFTs were fabricated on Si/SiO2 substrates using the sprayed p-type or n-type ZnO-NP layers obtained in this study. The schematic cross-sectional device structure was shown in Figure 5(a). The thicknesses of Si/SiO2/ZnO-NP were 500 μm/0.078 μm/20 μm, respectively. Au and Al electrodes were patterned on p-type and n-type layers, respectively, as source/drain contacts. The distance between source and drain (gate length) was 450 μm, and the width was 300 μm. Figures 5(b) and 5(c) show the ID-VD curves of TFTs using p-type and n-type ZnO-NP layers, showing the decrease in drain currents with the positive and negative back gate biases, respectively. It has been confirmed that transistor behaviors were obtained using each p-type or n-type ZnO-NP layer as a channel region. Transistor performances and stabilities are insufficient for the practical use in this stage; however, we have demonstrated the world’s first p-type and n-type ZnO-based TFTs using NP-deposition layers. The possibility of future contributions to extremely simple and low-cost NP and spray processes for ZnO-NP-based electronics has been confirmed.
(a) Schematic illustration of back gate thin-film transistor formed on Si/SiO2 substrate. The characteristics of IDS versus VDS of TFTs with channel regions using (b) p-type and (c) n-type ZnO-NP layers.
4. Conclusions
ZnO-NP layers were successfully obtained by spraying dispersions of ZnO-NPs, which can be an extremely simple and low-cost process. ZnO-NPs were synthesized using an arc-discharge-mediated gas-evaporation method, providing nitrogen-doped ZnO-NPs. Depending on the synthesizing conditions, sprayed NP layers showed p-type and n-type conductivities with high reproducibility. Discussions about the reason for higher mobility in p-type layers than that in n-type ones are added, which can support the fact of realization of the p-type ZnO-NP layers. pn-junction behaviors were tested using these layers, showing clear rectifying characteristics. Finally, operations of p-channel and n-channel TFTs on sprayed ZnO-NP layers used in this study were successfully demonstrated. These results are expected to lead to further contributions to the future ZnO-NP-based electronics.
Competing Interests
The authors declare that there are no competing interests regarding the publication of this paper.
Acknowledgments
The authors acknowledge the cooperation of the Center for Integrated Research in Science, Shimane University, for providing the experimental facility of FESEM, which was introduced through Tatara Project supported by the Ministry of Education, Culture, Sports, Science and Technologies of Japan. This work was supported by JSPS KAKENHI Grant no. 25870448.
ChoiY.-S.KangJ.-W.HwangD.-K.ParkS.-J.Recent advances in ZnO-based light-emitting diodes2010571264110.1109/TED.2009.20337692-s2.0-73349136977ZhuJ.ChenH.SarafG.DuanZ.LuY.HsuS. T.ZnO TFT devices built on glass substrates20083791237124010.1007/s11664-008-0457-92-s2.0-51849127362ZhangL.ZhangH.BaiY.MaJ. W.CaoJ.JiangX.ZhangZ. L.Enhanced performances of ZnO-TFT by improving surface properties of channel layer20081469-1038739010.1016/j.ssc.2008.03.0362-s2.0-43049157966ChungJ. H.LeeJ. Y.KimH. S.JangN. W.KimJ. H.Effect of thickness of ZnO active layer on ZnO-TFT's characteristics2008516165597560110.1016/j.tsf.2007.07.1072-s2.0-43949087179NavamathavanR.ChoiC. K.YangE.-J.LimJ.-H.HwangD.-K.ParkS.-J.Fabrication and characterizations of ZnO thin film transistors prepared by using radio frequency magnetron sputtering200852581381610.1016/j.sse.2007.11.0102-s2.0-41449092578MünzenriederN.VoserP.PettiL.ZyssetC.BütheL.VogtC.SalvatoreG. A.TrösterG.Flexible self-aligned double-gate IGZO TFT2014351697110.1109/led.2013.22863192-s2.0-84891530094LajnA.Von WencksternH.BenndorfG.DietrichC. P.BrandtM.BiehneG.HochmuthH.LorenzM.GrundmannM.Shallow donors and compensation in homoepitaxial ZnO thin films201039559560010.1007/s11664-009-1017-72-s2.0-77954623600IwataK.FonsP.YamadaA.MatsubaraK.NikiS.Nitrogen-induced defects in ZnO:N grown on sapphire substrate by gas source MBE20002092-352653110.1016/S0022-0248(99)00613-22-s2.0-0034140970TangaL.WangB.ZhangY.GuY.Structural and electrical properties of Li-doped p-type ZnO thin films fabricated by RF magnetron sputtering2011176754855110.1016/j.mseb.2010.12.018LuY. F.WuK. W.ZengY. J.YeZ. Z.HuangJ. Y.ZhuL. P.ZhaoB. H.Local p-type conduction of Na-doped ZnO thin films grown by MOCVD2013582828510.1016/j.cplett.2013.04.0262-s2.0-84883257158SujaM.BasharS. B.MorshedM. M.LiuJ.Realization of Cu-doped p-type ZnO thin films by molecular beam epitaxy20157168894889910.1021/acsami.5b015642-s2.0-84928786985MaY.GaoQ.WuG. G.LiW. C.GaoF. B.YinJ. Z.ZhangB. L.DuG. T.Growth and conduction mechanism of As-doped p-type ZnO thin films deposited by MOCVD20134831239124310.1016/j.materresbull.2012.12.0352-s2.0-84872835115ChaoL.-C.ChenJ.-W.PengH.-C.HoC.-H.Characterization of nitrogen doped p-type ZnO thin films prepared by reactive ion beam sputter deposition201323149249510.1016/j.surfcoat.2012.10.0772-s2.0-84882923057NieX.ZhangB.WangJ.ShiL.DiZ.GuoQ.Room-temperature ferromagnetism in p-type nitrogen-doped ZnO films201516135535910.1016/j.matlet.2015.08.1432-s2.0-84940974080PathakT. K.KumarV.SwartH. C.PurohitL. P.Effect of doping concentration on the conductivity and optical properties of p-type ZnO thin films2016480313510.1016/j.physb.2015.09.0332-s2.0-84958761775JosephM.TabataH.SaekiH.UedaK.KawaiT.Fabrication of the low-resistive p-type ZnO by codoping method2001302-30314014810.1016/S0921-4526(01)00419-72-s2.0-17144450356HeS.XinS. C.ShanL. J.HuiL. B.ZhongZ. Z.ZhenS. D.Stable p-type ZnO films obtained by lithium-nitrogen codoping method2013250102102210510.1002/pssb.2013000152-s2.0-84885471297MengL.ZhangJ.AnJ.HouX.Stable p-type ZnO thin films on sapphire and n-type 4H-SiC achieved by controlling oxygen pressure using radical-source laser molecular beam epitaxy20162131727810.1002/pssa.2015324432-s2.0-84954105679FanJ. C.SreekanthK. M.XieZ.ChangS. L.RaoK. V.P-Type ZnO materials: theory, growth, properties and devices201358687498510.1016/j.pmatsci.2013.03.0022-s2.0-84876727540TakahashiI.HashimotoH.FujitaY.ChoY.Measurement of distribution of P-type ZnO nano-particles by scanning nonlinear dielectric microscopyProceedings of the 21st International Colloquium on Scanning Probe MicroscopyNovember 2013Tsukuba, Japan8PN-89FujitaY.MoriyamaK.HiraginoY.FurubayashiY.HashimotoH.YoshidaT.Electroluminescence from nitrogen doped ZnO nanoparticles2014117-81260126210.1002/pssc.2013006452-s2.0-84903994606LookD. C.ReynoldsD. C.LittonC. W.JonesR. L.EasonD. B.CantwellG.Characterization of homoepitaxial p-type ZnO grown by molecular beam epitaxy200281101830183210.1063/1.15048752-s2.0-79958230334TuM. L.SuY. K.MaC. Y.Nitrogen-doped p-type ZnO films prepared from nitrogen gas radio-frequency magnetron sputtering2006100505370510.1063/1.2337766GarcesN. Y.GilesN. C.HalliburtonL. E.CantwellG.EasonD. B.ReynoldsD. C.LookD. C.Production of nitrogen acceptors in ZnO by thermal annealing20028081334133610.1063/1.14500412-s2.0-79956028331GuoX.-L.TabataH.KawaiT.Pulsed laser reactive deposition of p-type ZnO film enhanced by an electron cyclotron resonance source20012231-213513910.1016/s0022-0248(00)00952-02-s2.0-0034817670VargaT.KovarikL.SanghaviR.ShutthanandanV.ThevuthasanS.Formation of zinc oxide films using submicron zinc particle dispersions201230404180510.1116/1.4731255MechauN.BubelS.NikolovaD.HahnH.Influence of stabilizers in ZnO nano-dispersions on the performance of solution-processed FETs201020771684168810.1002/pssa.2009837682-s2.0-77955616909WaltherS.PolsterS.JankM. P. M.ThiemH.RysselH.FreyL.Tuning of charge carrier density of ZnO nanoparticle films by oxygen plasma treatment201122225325610.1016/j.apt.2011.01.0122-s2.0-79955384561RajachidambaramM. S.VargaT.KovarikL.SanghaviR.ShutthanandanV.ThevuthasanS.HanS.-Y.ChangC.-H.HermanG. S.Formation of zinc oxide films using submicron zinc particle dispersions201230404180510.1116/1.47312552-s2.0-84864212774WangB.MinJ. H.ZhaoY.SangW. B.WangC. J.The grain boundary related p-type conductivity in ZnO films prepared by ultrasonic spray pyrolysis2009941919210110.1063/1.3134486YoshidaT.ShinoharaK.ItoharaD.FujitaY.Effects of thermal pressing on ZnO nanoparticle layers deposited by drop casting20161417517810.1380/ejssnt.2016.175LeeS.ZhitomirskyD.GrossmanJ. C.Manipulating electronic energy disorder in colloidal quantum dot solids for enhanced charge carrier transport201626101554156210.1002/adfm.201504816