Microelectromechanical systems (MEMS) are a fast-growing field in microelectronics. MEMS are commonly used as actuators and sensors with a wide variety of applications in health care, automotives, and the military. The MEMS production cycle can be classified as three basic steps: (1) design process, (2) manufacturing process, and (3) operating cycle. Several studies have been conducted for steps (1) and (2); however, information regarding operational failure modes in MEMS is lacking. This paper discusses reliability in the context of MEMS functionality. It also presents a brief review of the most relevant failure mechanisms for MEMS.
Microelectromechanical systems (MEMS) are a relatively new and fast-growing field in microelectronics. MEMS are commonly used as actuators, sensors, and radio frequency and microfluidic components, as well as biocomposites, with a wide variety of applications in health care, automotive, and military industries. It is expected that the market for MEMS will grow to over $30B by 2050 [
The MEMS lifecycle can be divided into three basic steps: (1) the design process, (2) the manufacturing process, and (3) the operating cycle. Several research studies have been conducted for the design and manufacturing of MEMS; however, information regarding failure analysis for MEMS can still be considered in its infancy stage [
There is a need to develop new tools and methodologies to understand the behavior of MEMS devices for distinct applications and operation conditions. MEMS are extremely diverse and their failure modes can be unique under different conditions [
MEMS represent a technology that can be defined as miniaturized mechanical and electromechanical elements (i.e., devices and structures) that are made using the techniques of microfabrication. Dimensions of MEMS devices can vary from well below one micron on the lower end of the dimensional spectrum, all the way to several millimeters [
The real potential of MEMS starts to become fulfilled when these miniaturized sensors, actuators, and structures can all be merged onto a common silicon substrate along with integrated circuits (i.e., microelectronics). While the electronics are fabricated using integrated circuit (IC) process sequences (e.g., CMOS, bipolar, or BICMOS processes), the micromechanical components are fabricated using compatible “micromachining” processes that selectively etch away parts of the silicon wafer, or add new structural layers, to form the mechanical and electromechanical devices. MEMS can be merged not only with microelectronics, but with other technologies such as photonics. This is sometimes called “heterogeneous integration.” Clearly, these technologies are filled with numerous commercial opportunities [
Reliability for MEMS devices is identified as the next manufacturers challenge for the forthcoming years due to a growing market and stricter government safety regulations. It is necessary to understand several variables to have an approach of their behavior and functionality.
Very high levels of reliability are required in most industrial applications, such as automotive. For example, the automotive industry is now focused on failure rates lower than 10 FIT. 1 FIT is the usual unit corresponding to a proven failure over 109 hours [
In automotive applications, MEMS reliability analysis is extremely important to identify and understand the different failure mechanisms that can be implicit such as mechanical, thermal, and chemical aspects related to the diversity of materials that can be used. Recent studies expect airbag penetration to increase from 40 to 60 million vehicles over the next five years (i.e., 80% of cars worldwide) [
MEMS devices require interaction with the environment to perform their mission. For instance, applications in automotive as well as high-demand manufacturing systems represent environments and surroundings result aggressive for MEMS, and thus, they require special attention. Standardized testing of MEMS components is partially covered in the Society of Automotive Engineers and the military via SAE J1221, SAE J575G, and Military Standard 750. These standards detail accelerating testing such as high- and low-temperature storage, temperature cycling, and thermal shock [
In general, the automotive and manufacturing industries require most MEMS lifetime from five to ten years (or 100,000 to 150,000 miles on desert, tropical, or arctic locations in the case of automotive applications). For commercial trucks components, ten years or 1 million miles of problem free use are required [
One of the most critical points in developing a reliability analysis is to understand the way in which a system can fail, or commonly known as its “root cause.” For that reason, a failure mode is defined as the apparent failure of a system, and the failure mechanism as the physical cause (mechanical, chemical, or thermal) of the failure modes in the system [
Tanner et al. [
Walraven [ Class I: no moving parts (pressure sensors and microphones). Class II: moving parts, no rubbing or impacting surfaces (gyroscopes and RF oscillators). Class III: moving parts with impacting surfaces. Class IV: moving parts with impacting and rubber surfaces.
In addition, Walraven [
Materials can be considered critical for their behavior under extreme conditions such as high temperatures, humidity, and vibration. Sharpe and Bagdahn [
Several studies have been conducted to understand MEMS failures depending on the material composition, especially in silicon, which is commonly used for MEMS. Shea [
Pomeroy et al. [
Starman et al. [
Accelerated testing has also been used to determine materials properties and measure reliability. Brown et al. [
A critical part of understanding the reliability of any system comes from understanding the possible ways in which the system may fail. In MEMS, there are several failure mechanisms that have been found to be the primary sources of failure within devices [
Mechanical fracture is defined as the breaking of a uniform material into two separate sections. In MEMS, it usually leads to the catastrophic failure of the device, although there are some structures that may have moderate performance degradations. No matter what the actual outcome, any fracturing is a serious reliability concern (Figure
Surface fracture (courtesy of Sandia National Laboratories).
There are three types of fractures: ductile, brittle, and intercrystalline fractures. Ductile fracture, as the name implies, occurs in ductile materials. It is characterized by almost uninterrupted plastic deformation of a material. It is usually signified by the necking, or extreme thinning, of a material at one specific point. Brittle fracture occurs along crystal planes and develops rapidly with little deformation. Intercrystalline fracture is a brittle fracture that occurs along grain boundaries in polycrystalline materials, often beginning at a point where impurities or precipitates accumulate. For MEMS, the latter two types of fracture are more common [
Stiction is considered one of the most important problems in MEMS. Internal MEMS structures are so small that surface forces cause microscopic structures to stick together when their surfaces come into contact (see Figure
Stiction in MEMS fingers (courtesy of Sandia National Laboratories).
Wear is caused by the motion of one surface over another. It is defined as the removal of material from a solid surface as the result of mechanical action [
Wear debris in microengine (courtesy of Sandia National Laboratories).
Adhesive wear is caused by one surface pulling fragments off of another surface while they are sliding. This is caused by surface forces bonding two materials together. When the bonds break, they are unlikely to separate at the original interface, which fractures one of the materials. Initial studies on the long-term effects of adhesive wear have been completed, with some interesting results being discovered [
Abrasive wear occurs when a hard, rough surface slides on top of a softer surface and strips away underlying material. While less prevalent in MEMS than adhesive wear, it can occur if particulates get caught in microgears and can tear apart a surface. Corrosive wear occurs when two surfaces chemically interact with one another and the sliding process strips away one of the reaction products. This type of wear could cause failure in chemically active MEMS. Certain types of microfluidic systems and biological MEMS are susceptible to corrosive wear. Corrosive wear is dependent upon the chemical reactions involved [
Surface fatigue wear occurs mostly in rolling applications, such as bearings and gears. It affects highly polished surfaces that roll instead of sliding. Over time, the continued stressing and unstressing of the material under the roller will cause the appearance of fatigue cracks. These cracks then propagate parallel to the surface of a structure, causing material to flake off the surface. Surface fatigue wear tends to generate much larger particles than other wear mechanisms, with flakes as large as 100 nm being common in macroscopic applications [
Surface wear in drive gears (courtesy of Sandia National Laboratories).
A delamination condition occurs when a material interface loses its adhesive bond. It can be induced by a number of means, from mask misalignments to particulates on the wafer during processing. It can also arise as the result of fatigue induced by the long-term cycling of structures with mismatched coefficients of thermal expansion. No matter what the actual cause, the effects of delamination can be catastrophic. If the material is still present on the device, it can cause shorting or mechanical impedance [
Vibration is a large reliability concern in MEMS. Due to the sensitivity and fragile nature of many MEMS, external vibrations can have disastrous implications. Either through inducing surface adhesion or through fracturing device support structures, external vibration can cause failure. Long-term vibration can also contribute to fatigue [
Electrostatic discharge, or ESD, occurs when a device is improperly handled. A human body routinely develops an electric potential in excess of 1,000 V. Upon contacting an electronic device, this buildup will discharge, which will create a large potential difference across the device. The effect is known to have catastrophic effects in circuits and could have similar effects in MEMS. While the effects of ESD on MEMS structures have not been published to date, it can be assumed that certain electrostatically actuated devices will be susceptible to ESD damage [
ESD failure in electrostatic actuator (courtesy of Sandia National Laboratories).
Dielectric charging and breakdown is the charging that may occur in the dielectric layer. Sensors are known to drift over time due to charge accumulating at the surface [
The field of radiation effects on MEMS is becoming increasingly important. It has long been known that electrical systems are susceptible to radiation, and recent research has raised the possibility that mechanical devices may also be prone to radiation-induced damage. Especially sensitive to radiation are devices that have mechanical motion governed by electric fields across insulators, such as electrostatically positioned cantilever beams. Insulators can fail under single event dielectric rupture. A further complication is the fact that radiation can cause bulk lattice damage and make materials more susceptible to fracture [
This is a serious concern for MEMS. Internal stresses in devices are extremely temperature dependent. The temperature range in which a device will operate within acceptable parameters is determined by the coefficient of linear expansion. In devices where the coefficients are poorly matched, there will be a low tolerance for thermal variations [
Thermal effects cause problems in metal packaging, as the thermal coefficient of expansion of metals can be greater than ten-times that of silicon. For these packages, special isolation techniques have to be developed to prevent the package expansion from fracturing the substrate of the device. Another area that has yet to be fully examined is the effect of thermal changes upon the mechanical properties of semiconductors. It has long been known that Young’s modulus is a temperature-dependent value [
Humidity is considered another serious concern for MEMS. Surface micromachined devices are extremely hydrophilic for reasons related to processing. In the presence of humidity, water will condense into small cracks and pores on the surface of these structures [
Figure
Micro engine gears under humidity stress (courtesy of Sandia National Laboratories).
Particulates are fine particles that are prevalent in the atmosphere. These particles have been known to electrically short out MEMS and can also induce stiction. While these particles are normally filtered out of the clean room environment, many MEMS are designed to operate outside the confines of the clean room and without the safety of a hermetically sealed package.
As a result, devices must be analyzed to ensure that they are particle-tolerant before they can be used as high-reliable devices in environments with high particulate densities. Another area in which contaminants cause problems is in adhesion. Proper device processing requires most materials interfaces to be clean in order to have good adhesion. If dust particles are present, the two materials are weakly bonded and are more likely to have delamination problems [
Particles on MEMS (courtesy of Sandia National Laboratories).
MEMS components by nature have different and unique failure mechanisms than their macroscopic counterparts. As it was mentioned before, Walraven [
MEMS failure mechanisms.
Reliability for MEMS devices is identified as the next manufacturers challenge for the forthcoming years due to a growing market and stricter government safety regulations. It is necessary to understand several variables to have an approach of their behavior and functionality. Very high levels of reliability are required in most industrial applications for MEMS, hence, a good understanding of MEMS internal variables (i.e., technologies related) and external variables (i.e., environment and operation conditions). MEMS reliability analysis is extremely important to identify and understand the different failure mechanisms that can be implicit such as mechanical, thermal, and chemical aspects related to the diversity of materials that can be used.