The Bombyx mori silk fibroin (SF) films were prepared by solution casting method and effects of electron beam on the optical properties and optical constants of the films have been studied by using UV-Visible spectrophotometer. Optical properties like optical band gap Eg, refractive index n, extinction coefficient k, optical conductivity σopt, and dielectric constants ε∗ of virgin and electron irradiated films were determined by using UV-Visible absorption and transmission spectra. It was found that the reduction in optical band gap and increase in refractive index with increasing radiation dosage was observed. It is also observed from results that there is increase in dielectric constants with increasing photon energy. The observed optical changes have been tried to be correlated with the structural changes, revealed through FT-IR spectroscopy. The present study is quite important for tailoring the optical responses of SF films as per specific requirements.
1. Introduction
Silk is a natural semicrystalline biopolymer. Bombyx mori silk consists of two kinds of proteins, fibroin and sericin [1]. Silk fibroin (SF) can be obtained as pure regenerated solution from the silk fibers of Bombyx mori silkworm, by water based process. Silk fibroin from the Bombyx mori silkworm is easily formed into a variety of material forms such as hydrogels [2], ultrathin and thick films [3, 4], controlled-release coatings [5], and 3D porous matrices [6].
SF films are mechanically robust having very smooth surfaces and highly transparent across the visible region and possess high refractive index [7, 8]. Silk fibroin (SF) is found to be well suited for optical applications in film form with free standing materials of thickness between 20 and 100 μm. This is possible due to regenerated silk fibroin in the solid state containing extremely stable β-pleated sheets. These secondary structures are stabilized by interchain hydrogen bonding in which every amino acid is laterally bonded twice to its nearest neighbor chain segments. The hydrogen bonds are responsible for the extraordinary physical properties like high tensile strength, toughness, biocompatibility, and biodegradability [9, 10]. SF has been used for centuries for biomedical applications, but it is receiving increasing attention as technological material. Silk fibroin in film form has been recognized as a suitable biopolymer for the development of optical devices [11], optical waveguides [12], luminescent solar concentrators [13], 2D, 3D optical elements-holograms, lenses, optical gratings, and antireflective coatings [14, 15].
Nowadays the irradiation of polymers is one of the important fields for altering the polymer properties like electrical, optical, chemical, mechanical, and so forth, significantly [16]. The interaction of radiation with polymers leads to chain scission, chain aggregation, formation of double bonds, and molecular emission. As a result of this the polymer properties may be modified [17]. The knowledge of optical properties of silk is essential as it is used as biosensors, antireflective coatings, solar cells, optical waveguides, and so forth. This justifies the need for studying the irradiation effects on the optical properties of the SF fibroin films such as absorption, extinction coefficients, and optical parameters like energy band gap, refractive index, and optical conductivity. We have reported the influence of 8 MeV electron irradiation effects on the optical properties and optical constants of silk fibroin films (silk taken from Mysore, India).
2. Experimental2.1. Materials and Methods
The Bombyx mori CSR4 cocoons were obtained from silkworms reared in controlled condition at the Sericulture Department, University of Mysore, India. Na2CO3 and LiBr (>99% purity, Sigma Aldrich) were used without purification. Bombyx mori CSR4 silk cocoons were cut into small pieces and the product was rinsed with water, then treated with boiling aqueous solution of 0.02 M Na2CO3 for 40 min. with stirring, then rinsed thoroughly with distilled water to remove the glue like sericin protein, and then dried in hot air oven. The silk fibroin solution was prepared by dissolving 6 g of degummed silk in 9.3 M LiBr solution at 60°C for 4 h. This solution was dialyzed against distilled water using a dialysis cassette with molecular, cutoff weight 3500 Da for 72 h changing water every 6 h in order to remove salt. This solution was optically clear after dialysis and was centrifuged to remove the small amount of silk aggregates that formed during the process. The final concentration of SF was about 1% (w/v). The prepared fibroin solution was transferred into a polystyrene Petri dish, allowing the solvent to evaporate at room temperature for 3 days before the films were peeled off from the plates. The final films were vacuum dried and stored in desiccators to avoid the absorption of moisture. The thickness of the obtained films was 60 ± 0.8 μm. The transparency of the SF films in the visible range was more than 90%.
2.2. Electron Irradiation
The polymers samples of size (2×2) cm2 were cut from the prepared films. One sample was kept as virgin and the other three samples were subjected to irradiation of different doses. Irradiation of samples was carried out at Microtron Center, Mangalore University, India, using the electron beam (by lanthanum hexafluorite source). The features of monochromatic beam are given in Table 1.
Specifications of the electron beam accelerator and irradiation conditions.
(1) Beam energy
8 MeV
(2) Beam current
20 mA
(3) Pulse repetition rate
50 Hz
(4) Pulse width
2.2 μs
(5) Distance source to sample
30 cm
(6) Dose range
0–150 kGy
(7) Atmosphere
Air
(8) Temperature
24°C
2.3. UV-Visible Spectroscopy
The UV-Visible absorption spectra of virgin and high energy electron irradiated silk fibroin film samples have been studied by using UV-Visible spectrophotometer (Shimadzu UV-1800, Japan) in the wavelength range 190–800 nm. All the spectra were recorded by mounting the samples in the integrating sphere assembly attached to the spectrometer, keeping air as the reference.
2.4. Fourier Transforms Infrared Spectra
Fourier transform infrared (FT-IR) spectra of the samples were recorded in transmission mode using Thermo Nicolet, Avatar 370, FT-IR spectrophotometer having a resolution 4 cm−1 in the wavenumber range 500–4000 cm−1.
3. Experimental Results and Discussion3.1. Study of Optical Behaviour
The transition of electrons in different orbitals from the ground state to excited energy states occurs during the absorption of light energy by polymeric materials in the ultraviolet and visible regions. The electronic transitions involved the following types: σ→σ∗, n→σ∗, n→π∗, and π→π∗. Many of the optical transitions which result from the presence of impurities have energies in the visible part of the spectrum. Consequently the defects are referred to as colour centres [18]. Energetic beam interaction with polymers generates damage which leads to the formation of new defects and new charge states. Ultraviolet-Visible (UV-Vis) spectrophotometer has become an important tool for investigation of these electronic transitions. It is used to estimate the value of optical energy band gap (Eg) in polymers.
The UV-Visible absorption spectra of virgin and 8 MeV electron irradiated (50–150 kGy) silk fibroin polymer samples are presented in Figure 1, in the wavelength range 280–400 nm. The recorded spectra of virgin silk fibroin film display absorption at 300 nm which is assigned to π→π∗ transition of the Tyr, Phe, and Try residues in the SF molecular chain [19]. The intensity of the absorption band changes with increasing dose, while its position slightly shifted towards the higher wavelength side [20]. This may be because electron irradiation of silk fibroin causes the creation of carbonyl group. This lowers the energy required for the optical transition so the absorption moves towards longer wavelengths. The carbonyl group modifies the optical transitions and hence the optical band gap.
Absorption spectra of virgin and electron irradiated silk fibroin films.
3.1.1. Absorption Coefficient and Optical Band Gap
The electron irradiation of polymer causes change in the polymer structure; hence a modification within the optical band gap is expected. The information about the optical band gap is obtained from the absorption edge of the UV-Vis spectra. Practically the optical absorption coefficient α can be calculated from the optical absorbance A, by using relation [18](1)αhν=2.303AX,where X is the sample thickness in cm and A is defined as A=log(I0/I), where I0 and I are the intensity of the incident and transmitted beam, respectively. Here the optical band gap was determined from the analysis of the spectral dependence of the optical absorption near the absorption edge. The optical absorption coefficient for noncrystalline materials has the following frequency dependence [21–23]:(2)αhν=Bhν-Egrhν,where hν is the energy of the incident photons, Eg is the optical energy gap between the valence band and conduction band, and r is an empirical exponent which characterizes the type of optical transition during the absorption process. The exponent r has value of 1/2 for allowed direct transition, while it takes the value 3/2 for the direct forbidden transition. And it has values 2, 3 for indirect allowed and forbidden transitions, respectively [24]. The simplest way to obtain the type of transition is to examine the value of r, which fits hν to αhν with a straight line relationship. In our case, r=1/2 which means an allowed direct transition, where the electron transition is vertical from the top of the valence band to the bottom of the conduction band. The nonvertical transitions are forbidden in this case. The factor B depends on the transition probability and can be assumed to be constant within the optical frequency range. The usual method for the determination of the value of Eg involves plotting (αhν)2 against (hν). Figure 2 illustrates (αhν)2 as a function of the photon energy hν for virgin and electron irradiated films. The values of the optical band gap Eg are normally obtained by extrapolation of the linear part of the curve to intersect the x-axis at zero absorption [25] which gives the corresponding energy band gap and which is presented in Table 2.
Band gap energy and Urbach energy of virgin and electron irradiated silk fibroin films.
Sample
Band gap energy (eV)
Urbach energy (eV)
Virgin
4.18
0.524
50 kGy
4.12
0.452
100 kGy
4.08
0.430
150 kGy
3.94
0.426
Variation of (αhν)2 as a function of the photon energy hν.
3.1.2. Urbach Energy
The exponential dependence on the photon energy (hν) by the absorption coefficient near the band edge for noncrystalline materials follows the Urbach relation [26, 27] (3)αν=α0exphνEu,where α0 is a constant, Eu is an energy which is interpreted as the width of the tail of localized states in the forbidden band gap, ν is the frequency of radiation, and h is Planck’s constant. Figure 3 shows the variation in the logarithm of the absorption coefficient as a function of the photon energy for all unirradiated and electron irradiated SF samples. The value of Urbach energy (Eu) is normally calculated by considering the reciprocal of the slope of the linear portion in the lower photon energy region of these curves. The calculated values of Urbach energy for virgin and electron irradiated silk fibroin film samples are presented in Table 2. The decrease in Urbach’s energy may be due to the decrease in the crystalline nature of the polymer [28]. Upon irradiation, the transparent silk fibroin film polymer became yellow and the degree of yellowness was found to be increased with increasing electron irradiation dose. Treatment of silk with radiations is reported to produce yellow colour due to oxidation of amino acid residues glycine, alanine, serine, and tyrosine [29, 30] and especially formation of chromophore products [31, 32].
Urbach energy for virgin and electron irradiated silk fibroin films.
3.1.3. Determination of Refractive Index
For many devices, accurate knowledge of the refractive index and its frequency dependence is very important. The refractive index (n) values for virgin and high energy electron irradiated SF samples at different wavelengths have been calculated by using the relation [27]:(4)n=4RR-12-k21/2-R+1R-1,where k is the extinction coefficient. The extinction coefficient is a measure of the fraction of light lost due to scattering and absorption per unit distance of the penetration medium. It can be estimated from the values of α and λ using the relation [33](5)k=αλ4π.
The spectral distributions of the values of n and k for different doses are shown in Figures 4 and 5, respectively.
Variation of refractive index as a function of wavelength.
Variation of extinction coefficient k as a function of wavelength.
Figure 4 shows the refractive index n increases with irradiation doses; indeed n changes from 1.72 to 2.13 at 600 nm, when radiation dose increases from 0 to 150 kGy. It is observed that the refractive index increased with increasing dosage and the radiation induced refractive index changes are very large. These changes showed that exposure of SF films to energetic electron radiation is most acceptable approach to tailor the refractive index efficiently. It has a potential applicability for optical devices, for example, optical waveguides and photonic devices [34, 35]. The dependence of extinction coefficient k on the wavelength is presented in Figure 5 for virgin and electron irradiated samples. The extinction coefficient k shows clear changes with increasing doses; indeed, k changes from 1.3 × 10−6 to 2.5 × 10−6 at λ = 630 nm for increase in radiation dose from 0 to 150 kGy. This change in refractive index and extinction coefficient with increasing irradiation is attributed to structural modifications occurring in the samples.
3.1.4. Optical Conductivity
Using the absorption coefficient (α) and refractive index (n) of the material one can calculate the optical responses of a material in terms of the optical conductivity σopt, which is given by the relation [36, 37] (6)σopt=αnc4π,where c is the velocity of light.
Figure 6 shows the variation of the optical conductivity as a function of photon energy for the SF samples. From Figure 6 it is very clear that the optical conductivity increases with increase in photon energy and also increasing radiation doses under investigation. The increase in optical conductivity can be attributed to the increase in absorption coefficient.
Variation of optical conductivity as a function of photon energy.
3.1.5. Determination of Dielectric Properties
The complex dielectric constant (ε∗=εr+iεi) is a fundamental property of the material, which characterizes the optical properties of a solid material. The dielectric constant consists of two components, real part and imaginary part. The real part of the dielectric constant shows how much it will slow down the speed of light in the material, whereas the imaginary part indicates how a dielectric material absorbs energy from an electric field due to dipole motion. The knowledge of the real and imaginary parts of the dielectric constant gives the information about the loss factor which is the ratio of the imaginary part to the real part of the dielectric constant. The real and imaginary parts of the dielectric constant can be determined by the following relations [38]:(7)εr=n2-k2,(8)εi=2nk.
Figures 7(a) and 7(b) show the variation of the real and imaginary parts of the dielectric constant as a function of photon energy for the virgin and electron irradiated SF samples. From the figures it is clear that both real and imaginary parts of the dielectric constant increase with increase in photon energy. The real part of the dielectric constant depends on refractive index by (7) because the effect of extinction coefficient is very small and hence has a negligible contribution [39]. Increase in real part was observed with increase in photon energy and irradiation doses. The imaginary part of the dielectric constant depends on extinction coefficient by (8) because the refractive index is very small [40]. From the figure it is clear that the value of imaginary dielectric constant increases slowly in the lower energy region and increases sharply in the higher energy region. These results indicate that the loss factor increases with increase in photon energy.
Variation of (a) real part of dielectric constant and (b) imaginary part of dielectric constant as a function of photon energy.
3.2. Structural Studies3.2.1. FT-IR Analysis
The structure of fibroin proteins in the native SF and electron irradiated films were characterized by FT-IR spectroscopy. The FT-IR spectra of the native SF and electron irradiated films are given in Figure 8. The position of absorption bands indicated the conformation of fibroin protein. The absorption bands observed for SF are at 1617 cm−1 (amide I) which is mainly related with the C=O stretching, 1511 cm−1 (amide II) C–H stretching vibration, and 1236 cm−1 (amide III) C–N stretching vibration. In addition, the position of the amide bands indicates the conformations of the fibroin protein components, 1620 cm−1 (β sheet) for amide I, 1520 cm−1 (β sheet) for amide II, and 1230 cm−1 (random coil), were assigned as both silk I and silk II structure [41, 42] of the SF. This indicates that both random coil (α-helices) and β sheet structure occur in SF simultaneously. When the SF films were subjected to high energy electron irradiation, the FT-IR results showed that the absorption bands 1617, 1511, and 1229 cm−1 were shifted to 1623, 1516, and 1236 cm−1, respectively. Also the FT-IR spectrum shows the intensity of amides I–III, increased as irradiation dose increased, indicates the weakening of the peptide bond (C–N) in polypeptides [43]. Such structural changes as revealed through FT-IR spectroscopy corroborate the observations from optical measurements.
FT-IR spectra of virgin and electron irradiated silk fibroin films.
4. Conclusions
The basic optical properties and optical constants of the unirradiated and electron beam irradiated SF films have been investigated by means of absorbance and transmittance spectra. The observed variation in optical parameters such as the optical band gap (Eg), refractive index (n), extinction coefficient (k), optical conductivity (σopt), and dielectric constants (ε∗) of SF may lead to tailoring of the optical properties of this biopolymer as per specific requirements after electron irradiation. Refractive index and optical conductivity of the polymer increase with increasing radiation dosage indicating SF films are suitable for antireflective coating, photonic devices, and image sensors. To our knowledge, this is the first systematic work to report the variation in the refractive index of SF, in the almost complete visible range, as a result of electron irradiation.
Conflict of Interests
The authors declare that there is no conflict of interests regarding the publication of this paper.
Acknowledgment
The first author (S. Asha) thanks UGC (New Delhi, India) for an RGNF fellowship.
MetcalfeA. D.FergusonM. W. J.Bioengineering skin using mechanisms of regeneration and repair200728345100511310.1016/j.biomaterials.2007.07.0312-s2.0-34748859797KimU.-J.ParkJ.LiC.JinH.-J.ValluzziR.KaplanD. L.Structure and properties of silk hydrogels20045378679210.1021/bm03454602-s2.0-2542519952JiangC.WangX.GunawidjajaR.LinY.-H.GuptaM. K.KaplanD. L.NaikR. R.TsukrukV. V.Mechanical properties of robust ultrathin silk fibroin films200717132229223710.1002/adfm.2006011362-s2.0-34548587170WangX. Y.KimH. J.XuP.MatsumotoA.KaplanD. L.Biomaterial coatings by stepwise deposition of silk fibroin20052124113351134110.1021/la051862m2-s2.0-28844440290WangX.HuX.DaleyA.RabotyagovaO.CebeP.KaplanD. L.Nanolayer biomaterial coatings of silk fibroin for controlled release2007121319019910.1016/j.jconrel.2007.06.0062-s2.0-34547699279GhoshS.ParkerS. T.WangX.KaplanD. L.LewisJ. A.Direct-write assembly of microperiodic silk fibroin scaffolds for tissue engineering applications200818131883188910.1002/adfm.2008000402-s2.0-47949108730AltmanG. H.DiazF.JakubaC.CalabroT.HoranR. L.ChenJ.LuH.RichmondJ.KaplanD. L.Silk-based biomaterials200324340141610.1016/s0142-9612(02)00353-82-s2.0-0037290140LawrenceB. D.OmenettoF.ChuiK.KaplanD. L.Processing methods to control silk fibroin film biomaterial features200843216967698510.1007/s10853-008-2961-y2-s2.0-55149106335ShaoZ.VollrathF.Surprising strength of silkworm silk20024186899, article 74110.1038/418741a2-s2.0-0037102416HollandC.VollrathF.RyanA. J.MykhaylykO. O.Silk and synthetic polymers: reconciling 100 degrees of separation201224110510910.1002/adma.2011036642-s2.0-84855275052KimD. H.KimY. S.AmsdenJ.PanilaitisB.KaplanD. L.OmenettoF. G.ZakinM. R.RogersJ. A.Silicon electronics on silk as a path to bioresorbable, implantable devices200995133701ParkerS. T.DomachukP.AmsdenJ.BressnerJ.LewisJ. A.KaplanD. L.OmenettoF. C.Biocompatible silk printed optical waveguides200921232411241510.1002/adma.2008015802-s2.0-67649337255TsuboiY.AdachiH.YamadaK.MiyasakaH.ItayaA.Laser ablation of silk protein (fibroin) films20024174772477910.1143/jjap.41.47722-s2.0-0036655545LawrenceB. D.Cronin-GolombM.GeorgakoudiI.KaplanD. L.OmenettoF. G.Bioactive silk protein biomaterial systems for optical devices2008941214122010.1021/bm701235f2-s2.0-43149124805PerryH.GopinathA.KaplanD. L.NegroL. D.OmenettoF. G.Nano- and micropatterning of optically transparent, mechanically robust, biocompatible silk fibroin films200820163070307210.1002/adma.2008000112-s2.0-54949125343SinhaD.SahooK. L.SinhaU. B.SwuT.ChemseddineA.FinkD.Gamma-induced modifications of polycarbonate polymer20041591058759510.1080/104201504123313305392-s2.0-28344442983KumarS. V.GhadeiB.JalP. K.DeyK.KrishnaJ. B. M.SahaA.Modification of polyethersulphone induced by high energy proton, C+, and Ne6+ ions: a spectroscopic study200610131591159710.1002/app.235522-s2.0-33746083230SangappaAshaS.DemappaT.ParameswaraP.SanjeevG.SomashekarR.Spectroscopic and thermal studies of 8 MeV electron beam irradiated HPMC films2009267142385238910.1016/j.nimb.2009.04.0072-s2.0-67649388064ZakiM. F.Gamma-induced modification on optical band gap of CR-39 SSNTD2008411717540410.1088/0022-3727/41/17/1754042-s2.0-54749135008BaltovaS.VassilevaV.ValtchevaE.Photochemical behaviour of natural silk—I. Kinetic investigation of photoyellowing1998601536010.1016/s0141-3910(97)00016-52-s2.0-0032036129GuoH.-L.LiuD.-Y.YuX.-D.XiaX.-H.Direct electrochemistry and electrocatalysis of hemoglobin on nanostructured gold colloid-silk fibroin modified glassy carbon electrode2009139259860310.1016/j.snb.2009.03.0462-s2.0-67349181073ZidanH. M.Electron spin resonance and ultraviolet spectral analysis of UV-irradiated PVA films filled with MnCl2 and CrF3200388110411110.1002/app.115692-s2.0-0037419373MottN. F.DevisN. F.19792ndNew York, NY, USAOxford University PressTaucJ.AbelesF.Optical properties of non-crystalline solids1972Amsterdam, The NetherlandsNorth-Holland277SinghS.PrasherS.The etching and structural studies of gamma irradiated induced effects in CR-39 plastic track recorder20042223-451852410.1016/j.nimb.2004.03.0042-s2.0-3142773397UrbachF.The long wavelength edge of photographic sensitivity and of the electronic absorption of solids19539251324132610.1103/physrev.92.13242-s2.0-26344442097MigahedM. D.ZidanH. M.Influence of UV-irradiation on the structure and optical properties of polycarbonate films200661919610.1016/j.cap.2004.12.0092-s2.0-27544500038AshaS.SangappaNaikP.ChandraK. S.SanjeevG.Microstructural, thermal and antibacterial properties of electron beam irradiated Bombyx mori silk fibroin films159158th DAE Solid State Physics SymposiumDecember 2013Punjab, India219221AIP Conference Proceedings10.1063/1.4872550BaltovaS.VassilevaV.Photochemical behaviour of natural silk—II. Mechanism of fibroin photodestruction1998601616510.1016/s0141-3910(98)80027-x2-s2.0-0032035828SargunamaniD.SelvakumarN.Effects of ozone treatment on the properties of raw and degummed tassar silk fabrics2006912644265310.1016/j.polymdegradstab.2006.05.001GiuliviC.TraasethN. J.DaviesK. J. A.Tyrosine oxidation products: analysis and biological relevance2003253-422723210.1007/s00726-003-0013-02-s2.0-0346731053CreedD.The photophysics and photochemistry of the near-uv absorbing amino acids-I. Tryptiphan and its simple derivatives198439453756210.1111/j.1751-1097.1984.tb03890.xForouhiA. R.BloomerI.Optical properties of crystalline semiconductors and dielectrics19883831865187410.1103/physrevb.38.18652-s2.0-25944452908KimD.-H.ViventiJ.AmsdenJ. J.XiaoJ.VigelandL.KimY.-S.BlancoJ. A.PanilaitisB.FrechetteE. S.ContrerasD.KaplanD. L.OmenettoF. G.HuangY.HwangK.-C.ZakinM. R.LittB.RogersJ. A.Dissolvable films of silk fibroin for ultrathin conformal bio-integrated electronics20109651151710.1038/nmat27452-s2.0-77954581072TaoH.BrenckleM. A.YangM.ZhangJ.LiuM.SiebertS. M.AverittR. D.MannoorM. S.McAlpineM. C.RogersJ. A.KaplanD. L.OmenettoF. G.Silk-based conformal, adhesive, edible food sensors20122481067107210.1002/adma.2011038142-s2.0-84863132674BakrN. A.FundeA. M.WamanV. S.KambleM. M.HawaldarR. R.AmalnerkarD. P.GosaviS. W.JadkarS. R.Determination of the optical parameters of a-Si:H thin films deposited by hot wire-chemical vapour deposition technique using transmission spectrum only201176351953110.1007/s12043-011-0024-42-s2.0-79952976474YakuphanogluF.CukurovaliA.YilmazI.Refractive index and optical absorption properties of the complexes of a cyclobutane containing thiazolyl hydrazone ligand20052781363136810.1016/j.optmat.2004.09.0212-s2.0-17444395968OmarM. A.1993New York, NY, USAAddison-WesleyKumarV.GoyalP. K.MahendiaS.GuptaR.SharmaT.KumarS.Tuning of the refractive index and optical band gap of CR-39 polymers by heating2011166210911310.1080/104201510035873852-s2.0-78649887533AhmadA. H.AwatifA. M.Abdul-MajiedN. Z.Doping effect on optical constants on polymethylmethacrylate (PMMA)2007254558568TsukadaM.GotohY.NaguraM.MinouraN.KasaiN.FreddiG.Structural changes of silk fibroin membranes induced by immersion in methanol aqueous solutions199432596196810.1002/polb.1994.0903205192-s2.0-0028413371KojthungA.MeesilpaP.SudatisB.TreeratanapiboonL.UdomsangpetchR.OonkhanondB.Effects of gamma radiation on biodegradation of Bombyx mori silk fibroin200862448749010.1016/j.ibiod.2007.12.0122-s2.0-53549121955Srisa-ArdM.BaimarkY.SrisuwanY.Conformation transition and thermal properties study of silk fibroin and poly (ε-caprolactone) blends20088193518352210.3923/jas.2008.3518.35222-s2.0-67649556226