International Journal of SpectroscopyVolume 2012 (2012), Article ID 532385, 6 pagesdoi:10.1155/2012/532385

Research Article

Phonon Spectra of Small Colloidal II-VI Semiconductor Nanocrystals

Volodymyr Dzhagan,¹ Mykhailo Valakh,¹ Nikolai Mel'nik,² Olexandra Rayevska,³  Irina Lokteva,⁴ Joanna Kolny-Olesiak,⁵ and Dietrich R. T. Zahn⁶

¹V. Ye. Lashkaryov Institute of Semiconductor Physics, The National Academy Sciences of Ukraine, Prospekt Nauky 45, Kyiv 03028, Ukraine²P. N. Lebedev Physical Institute, Russian Academy of Sciences, Leninsky Prosp. 53, Moscow 119991, Russia³L.V. Pysarzhevskiy Institute of Physical Chemistry, National Academy Sciences of Ukraine, Prospekt Nauky 31, Kyiv 03028, Ukraine⁴Nanomaterials for Optoelectronics Group, Department of Materials Science, University of Erlangen-Nüremberg, Martensstrβe 7 91058 Erlangen, Germany⁵Energy and Semiconductor Research Laboratory, Department of Physics, Carl von Ossietzky University of Oldenburg, Carl-von-Ossietzky Strβe 9-11, 26111 Oldenburg, Germany⁶Semiconductor Physics, Chemnitz University of Technology, Reichenhainer Strβe 70, 09107 Chemnitz, Germany

Received 6 April 2011; Accepted 24 June 2011

Academic Editor: Sandip Dhara

Copyright © 2012 Volodymyr Dzhagan et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

Resonant Raman spectroscopy has been employed to explore the first- and higher-order phonon spectra of several kinds of II-VI nanocrystals (NCs), with the aim of better understanding of the nature of phonon modes and forming a unified view onto the vibrational spectrum of semiconductor NCs. Particularly, besides the previously discussed TO, SO, LO, and 2LO modes, the combinational modes of TO+LO and SO+LO can be assumed to account for the lineshape of the spectrum below 2LO band. No trace of 2TO or 2SO band was detected, what can be the result of the dominance of Fröhlich mechanism in electron-phonon coupling in II-VI compounds. The resonant phonon Raman spectrum of NCs smaller than 2 nm is shown to be dominated by a broad feature similar to the SO mode of larger NCs or phonon density of states of a bulk crystal.

The understanding of the phonon spectrum of semiconductor nanocrystals (NCs), electron-phonon coupling (EPC), dependence of the phonon spectra on the NC size, surface-bound moieties, and extended environment is of a large fundamental and application significance [1–11] due to the determinant role phonons play in the optical and electrical properties of semiconductor nanostructures [12, 13]. Though a number of in-depth studies have addressed the phonon spectra of colloidal [14–20], glass-embedded [21–23] NCs, and epitaxial nanostructures [24–26], a significant divergence of the results exists concerning both the nature of the modes and their response to such factors as size, surface conditions, properties of the hosting medium and so forth. In particular, the apparently similar Raman spectra of a wide range of compounds (e.g., II-VI, III-V, and IV) and NC morphologies (dots, rods, tetrapods, wires, and discs) have been assigned differently.

Recently, attempts were made to build a general picture of the phonon spectrum of various semiconductor NCs, based on analysis of the experimental Raman data and appropriate models [14, 27, 28]. This paper further explores the first- and higher-order phonon spectra of several kinds of II-VI NCs, as well as their similarity to other compounds, with the aim of better understanding of the vibrational spectrum of small NCs. High-quality NC samples were selected for this study in order to resolve Raman features, which are usually smeared by size dispersion, structural disorder, or low signal-to-noise ratio.

The NC samples studied in this work have been prepared by means of colloidal chemistry according to protocols reported elsewhere [29–32], and CdSe, CdS, and CdTe NC samples of the same mean diameter (~4 nm) were selected. Another sort of NCs studied were ultrasmall NCs of about 1.8 nm mean diameter, which revealed distinct Raman spectra. The attempts to measure the size and shape of these NCs directly by electron microscopy were unsuccessful [19], obviously due to ultrasmall NC size and charging of the stabilizing polymer. The broad X-ray features of these ultrasmall NCs [3] indicated their small size or/and noticeable structural deformations due to dominance of the surface atoms. Therefore, the size of the latter ultrasmall NCs has been estimated from the energy of the first excitonic maximum [19].

The main features observed in resonant Raman scattering spectra of II-VI NCs are the longitudinal optical (LO) phonon mode (fundamental) and its overtones (Figures 1 and 2), which are shifted to lower frequencies and broadened compared to the bulk crystal. The nature of a low-frequency shoulder of the LO peak, commonly observed for different kinds of semiconductor NCs, is still under discussion. It is related either with phonons at [33], surface optical (SO) [23], zone-edge (ZE) [22] phonons, or quantized optical phonons (vibrons) with a quantum number [17, 34, 35]. Fitting the Raman spectrum in the range of LO mode with two Lorentzians, corresponding to SO (or ZE) and LO phonon or to vibrons with different quantum numbers, is widely applicable for II-VI NCs [15, 18, 23, 36]. However, the similar shoulder has been observed in bulk alloys [37]. The alloys, even defect free, are known to possess a kind of disorder caused by the fluctuation of the electrostatic potential due to the inhomogeneous spatial distribution of the counterpart ions. This kind of disorder, along with the structural disorder, can lead to activation of some vibrational modes (disorder-activated ZE phonons) [37]. Investigation of the surface-related (SO) vibrations in NCs is important not only due to its potential in probing the NC-environment interaction [4], but also because they may take part in the optical transitions in NCs [38].

(a)

(b)

(c)

Figure 1: First-order Raman spectra of CdTe (a), CdSe (b), and CdS (c) NCs in the range of LO phonon with multi-Lorentzian fitting. Indicated is the assignment of the phonon modes.

(a)

(b)

(c)

Figure 2: Multi-Lorentzian fitting Raman spectra of CdTe (a), CdSe (b), and CdS (c) NCs in the range of 2LO phonon. The assignment of the phonon modes is indicated.

In a majority of experimental studies, the low-frequency shoulder being not resolved as a separate peak may lead to large errors in determination of its frequency position and widths. In addition, the LO phonon peak possesses in many cases a noticeable high-frequency shoulder (HFS, Figures 1(a) and 1(b)), which probably originates from vibrations of tellurium (selenium) on the CdTe (CdSe) NC surface or coupled optical-acoustical phonon modes [28, 29, 32]. Trying to satisfactory fit the whole spectrum in the range of the LO peak without taking into account the HFS can lead to overestimation of the frequency and bandwidth of the SO mode and affect the width of the LO peak and its ratio to overtones.

Our recent study of high-quality and monodispersed CdTe NCs revealed that the fitting of the lower-frequency asymmetry of the LO peak requires at least two components, attributed to TO and SO modes, correspondingly [28]. Here we extend this approach to fitting of the RRS spectra of the first-order spectra of CdSe and CdS NCs (Figure 1), as well as their overtones (Figure 2). According to this approach [28], the lowest frequency component, peaked at 145 cm⁻¹ for CdTe NCs, 177 cm⁻¹ for CdSe NCs, and 250 cm⁻¹ for CdS NCs, may be assigned to TO mode, because of its frequency proximity to the frequencies for the corresponding bulk crystals. The broad component between this mode and LO may be naturally assigned to the SO mode(s), as predicted by theory [39]. Quantitatively, the SO mode frequency is calculated using the same formalism as in previous works [18, 23, 31]—≈200 cm⁻¹ for CdSe NCs, ≈280 cm⁻¹ for CdS, and ≈160 cm⁻¹ for CdTe NCs—being in good correlation with the position of the component marked as “SO” in our experimental spectra in Figure 1, as well as with other reports [18, 23, 31].

The general appearance of the first-order resonant Raman spectrum of II-VI NCs studied here (Figure 1) is well reproduced by the model of quantized optical vibrations of spherical NC [34, 35], with the (, ) vibron corresponding to (fundamental) LO mode. However, as the experimental does not vary noticeably with NC size [32], it is unlikely to be related with the (, ) vibron mode revealing a strong size dependence of its frequency [34, 35]. Instead, the experimentally observed SO mode may be related to the density of vibron modes, centered around 180 cm⁻¹ for CdSe and 240–255 cm⁻¹ for CdS [34].

Based on a simple qualitative argument of the SO mode intensity, , being proportional to the NC surface-to-volume () ratio, the is expected to increase with NC size decrease. However, this approach may be oversimplified and prone to be offset by other factors, for example, by the saturation of the SO vibration intensity below a certain NC size at which the SO mode field extends over the whole NC volume. As a result, no noticeable dependence of on NC size will take place below certain critical NC diameter, as can be seen in Figure 3 for NC diameter decreasing from 4 down to 2 nm, with the corresponding increasing almost twice (from about 35 up to 60%). Furthermore, the analysis of the literature shows that the relative intensity of the SO mode can be very close for different NC morphologies and dimensions (dots, rods, tetrapods, and wires) with various .

Figure 3: Resonant Raman scattering spectra of a series of CdSe NCs of different size, measured with  nm at 50 K.

The nonsystematic sensitivity of the SO peak parameters to capping of the CdSe core with a ZnS (or CdS) shell [40] introduces further ambiguity in understanding of the nature of this mode. Based on similarity of the SO mode parameters for different NC morphologies, as well as existence of similar low-frequency asymmetry for bulk alloys [37]; one may assume it to be induced by the presence of atoms with coordination differing from the rest of (bulk) atoms. In NCs, these are the surface atoms with undercoordinated bonds, while in alloys these can be the atoms adjacent to the “impurity” atom or a structural defect. This kind of disorder can lead to activation in Raman scattering of vibrational modes forbidden for perfect crystal, particularly ZE phonons [22].

The ZE phonons, that is, phonons from the boundary of the Brillouin zone, where TO and LO branches approach each other, are forbidden in Raman spectra due to their large (compared to that of the probing light). However, they can be activated in Raman by a certain degree of disorder in the lattice. The surface of the NC is a case of such a disorder, with the spatial dimension of 1-2 lattice constants—the same length where ZE phonons exist. The probability of the appearance of the surface-related modes in Raman spectrum may be higher in smaller NCs not only due to a larger surface-to-volume ratio but also due to a larger overlap of the carrier’s wavefunction with surface. As to the role of the surface-trapped excitons, it may be not relevant, because the trapping times are usually much longer than the duration of the Raman scattering event.

Though the low-frequency shoulders of the LO overtones resemble strongly that of the fundamental peak, the fitting of the spectra shows that the former cannot be attributed to the nSO modes. The frequency position of the shoulder is much larger than the corresponding . More viable is the assignment of these shoulders to the SO+nLO () sum modes (Figure 2). At least the frequency position fits well to such a combination. This assignment can reveal new aspects of coupling between the strongly confined optical phonons in small semiconductor NC. Nevertheless, the contribution of second-order scattering on ZE phonons cannot be excluded and needs further studying. The second-order spectrum is also featured by the high-frequency shoulder centered around 20–40 cm⁻¹ above the 2LO band (Figure 2), similar to the HFS in the first-order spectrum (Figure 1).

The structure of the Raman spectrum has been observed to change qualitatively for NC smaller than 2 nm. The first-order spectrum of CdSe NCs as small as 1.8 nm (Figure 4) reveals a broad feature between bulk TO and LO frequencies, thus in the region of the SO mode observed for larger NCs. Simple estimation shows that at as small as 1.8 nm, most of the atoms can be classified as surface ones and such NCs can therefore be an illustration of a limiting case of small NC which do not support the bulk-like LO (and TO) phonon modes. Their spectrum more likely resembles the phonon density of states (DOS) predicted for bulk CdSe and CdSe nanowires with a diameter of  nm [41] or the spectrum of molecular-like clusters [16, 42]. From the viewpoint of the model based on bulk dispersion curves, the strong spatial confinement along with lattice distortion due to the reconstruction induced by a domination of surface atoms can lead to the situation when only phonons (TO and LO) close to (bulk) zone boundary exist in NCs. These ZE phonons manifest themselves in Raman spectrum as a single broad feature because of a very small TO-LO splitting near the zone boundary, as has been inferred previously for the description of IR phonon spectra of Cd₅₆Te₃₂ clusters [43].

Figure 4: Resonant Raman spectrum of ultrasmall CdSe NCs ( nm), measured with  nm.

In conclusion, the resonant Raman spectra of several kinds of II-VI NCs have been analyzed. It is shown that similar set of phonon modes can be derived from fitting the spectra of high enough quality. Particularly, besides the previously discussed TO, SO, and LO modes, the combinational modes of TO+LO and SO+LO can be assumed to account for the lineshape of the spectrum below 2LO band. No trace of 2TO or 2SO band was detected, what can be the result of the dominant Fröhlich mechanism in electron-phonon coupling in II-VI compounds. The resonant phonon Raman spectrum of NCs smaller than 2 nm is shown to be dominated by a broad feature similar to the SO mode of larger NCs or a DOS of a bulk crystal.

Acknowledgments

The work was supported by NAS of Ukraine (32-08-10-Ukr), Russian Foundation for Basic Research (10-02-90468-Ukr), Ukrainian State Fund for Fundamental Researches (40.2/068, 41.1/017), and Alexander von Humboldt Foundation (Research Group Linkage Programme).

References

G. Gouadec and P. Colomban, “Raman spectroscopy of nanostructures and nanosized materials,” Journal of Raman Spectroscopy, vol. 38, no. 6, pp. 598–603, 2007.

F. García-Santamaría, S. Brovelli, R. Viswanatha et al., “Breakdown of volume scaling in auger recombination in CdSe/CdS heteronanocrystals: the role of the core-shell interface,” Nano Letters, vol. 11, no. 2, pp. 687–693, 2011.

Q. H. Zhong, “Optical phonon modes and electron-phonon interaction in a quantized CdS spherical film,” Physica B, vol. 404, no. 8–11, pp. 1241–1246, 2009.

P. M. Chassaing, F. Demangeot, V. Paillard et al., “Surface optical phonons as a probe of organic ligands on ZnO nanoparticles: an investigation using a dielectric continuum model and Raman spectrometry,” Physical Review B, vol. 77, no. 15, Article ID 153306, 2008.

C. Chen, M. Dutta, and M. A. Stroscio, “Surface-optical phonon assisted transitions in quantum dots,” Journal of Applied Physics, vol. 96, no. 4, Article ID 2049, pp. 2049–2054, 2004.

S. K. Gupta, S. Sahoo, P. K. Jha, A. K. Arora, and Y. M. Azhniuk, “Observation of torsional mode in CdS1-x Sex nanoparticles in a borosilicate glass,” Journal of Applied Physics, vol. 106, no. 2, Article ID 024307, 2009.

M. P. Lisitsa, M. Y. Valakh, and N. K. Konovets, “Phonons in mixed CdxZn1−xS semiconductors,” Physica Status Solidi B, vol. 34, pp. 269–278, 1969.

S. Biswas, M. Dutta, P. Snee, and M. A. Stroscio, “Phonon modes in semiconductor quantum dots,” Chinese Journal of Physics, vol. 49, no. 1, pp. 92–99, 2011.

S. Ma, R. Livingstone, B. Zhao, and J. R. Lombardi, “Enhanced raman spectroscopy of nanostructured semiconductor phonon modes,” Journal of Physical Chemistry Letters, vol. 2, no. 6, pp. 671–674, 2011.

T. T. K. Chi, G. Gouadec, P. Colomban, G. Wang, L. Mazerolles, and N. Q. Liem, “Off-resonance Raman analysis of wurtzite CdS ground to the nanoscale: structural and size-related effects,” Journal of Raman Spectroscopy, vol. 42, no. 5, pp. 1007–1015, 2011.

P. Kusch, H. Lange, M. Artemyev, and C. Thomsen, “Size-dependence of the anharmonicities in the vibrational potential of colloidal CdSe nanocrystals,” Solid State Communications, vol. 151, no. 1, pp. 67–70, 2011.

S. V. Kilina, D. S. Kilin, and O. V. Prezhdo, “Breaking the phonon bottleneck in PbSe and CdSe quantum dots: time-domain density functional theory of charge carrier relaxation,” ACS Nano, vol. 3, no. 1, pp. 93–99, 2009.

V. I. Klimov, “Linear and nonlinear optical spectroscopy of semiconductor nanocrystals,” in Handbook of Nanostructured Materials and Nanotechnology, H. S. Nalwa, Ed., vol. 4 of Optical Properties, pp. 473–481, Academic Press, New York, NY, USA, 2000.

M. I. Vasilevskiy and C. Trallero-Giner, “Resonant Raman scattering in spherical quantum dots: II-VI versus III-V semiconductor nanocrystals,” Physica Status Solidi (B), vol. 247, no. 6, pp. 1488–1491, 2010.

D. S. Liang, L. Shen, Z. B. Wang, Y. P. Cui, J. Y. Zhang, and Y. H. Ye, “Evolution of luminescence with shell's thickness in colloidal CdSe/CdS,” Chinese Physics Letters, vol. 25, no. 12, pp. 4431–4434, 2008.

Y. S. Park, A. Dmytruk, I. Dmitruk et al., “Aqueous phase synthesized CdSe nanoparticles with well-defined numbers of constituent atoms,” Journal of Physical Chemistry C, vol. 114, no. 44, pp. 18834–18840, 2010.

A. G. Rolo and M. I. Vasilevskiy, “Raman spectroscopy of optical phonons confined in semiconductor quantum dots and nanocrystals,” Journal of Raman Spectroscopy, vol. 38, no. 6, pp. 618–633, 2007.

H. Lange, M. Mohr, M. Artemyev, U. Woggon, T. Niermann, and C. Thomsen, “Optical phonons in colloidal CdSe nanorods,” Physica Status Solidi (B), vol. 247, no. 10, pp. 2488–2497, 2010.

O. E. Rayevska, G. Y. Grodzyuk, V. M. Dzhagan, et al., “Synthesis and characterization of white-emitting CdS quantum dots stabilized with polyethylenimine,” Journal of Physical Chemistry C, vol. 114, pp. 22478–22486, 2010.

V. Dzhagan, O. Rayevska, O. Stroyuk, et al., “Resonant Raman spectroscopy of confined and surface phonons in CdSe-caped CdS nanocrystals,” Physica Status Solidi C, vol. 6, no. 2, pp. 2043–2046, 2009.

Y. M. Azhniuk, V. V. Lopushansky, A. V. Gomonnai, V. O. Yukhymchuk, I. I. Turok, and Y. I. Studenyak, “Spectroscopic studies of thermal treatment effect on the composition and size of CdS1-xSex nanocrystals in borosilicate glass,” Journal of Physics and Chemistry of Solids, vol. 69, no. 1, pp. 139–146, 2008.

A. Ingale and K. C. Rustagi, “Raman spectra of semiconductor nanoparticles: disorder-activated phonons,” Physical Review B, vol. 58, no. 11, pp. 7197–7204, 1998.

A. Roy and A. K. Sood, “Surface and confined optical phonons in CdSx-Se1-x nanoparticles in a glass matrix,” Physical Review B, vol. 53, no. 18, pp. 12127–12132, 1996.

A. G. Milekhin, A. I. Toropov, A. K. Bakarov et al., “Interface phonons in InAs and AlAs quantum dot structures,” Physical Review B, vol. 70, no. 8, Article ID 085314, 5 pages, 2004.

A. I. Mashin, A. V. Nezhdanov, D. O. Filatov et al., “Confocal Raman microscopy of self-assembled GeSi/Si(001) Islands,” Semiconductors, vol. 44, no. 11, pp. 1504–1510, 2010.

A. M. Yaremko, V. O. Yukhymchuk, M. Y. Valakh et al., “Theoretical and experimental investigations of single- and multilayer structures with SiGe nanoislands,” Materials Science and Engineering C, vol. 23, no. 6–8, pp. 1027–1031, 2003.

C. C. Yang and S. Li, “Size-dependent raman red shifts of semiconductor nanocrystals,” Journal of Physical Chemistry B, vol. 112, no. 45, pp. 14193–14197, 2008.

V. Dzhagan, M. Y. Valakh, J. Kolny-Olesiak, et al., “Resonant Raman study of phonons in high-quality colloidal CdTe nanocrystals,” Applied Physics Letters, vol. 94, no. 24, Article ID 243101, 2009.

V. Dzhagan, I. Lokteva, C. Himcinschi, et al., “Phonon Raman spectra of colloidal CdTe nanocrystals: effect of size, non-stoichiometry and ligand exchange,” Nanoscale Research Letters, vol. 6, no. 1, pp. 79–88, 2011.

A. E. Raevskaya, A. L. Stroyuk, S. Y. Kuchmii, et al., “Optical study of CdS- and ZnS-passivated CdSe nanocrystals in gelatin films,” Journal of Physics, vol. 19, no. 38, Article ID 386237, 2007.

V. M. Dzhagan, M. Y. Valakh, A. E. Raevskaya, et al., “Size effects on Raman spectra of small CdSe nanocrystals in polymer films,” Nanotechnology, vol. 19, Article ID 305707, 2007.

V. M. Dzhagan, I. Lokteva, M. Y. Valakh, et al., “Spectral features above LO phonon frequency in resonant Raman scattering spectra of small CdSe nanocrystals,” Journal of Applied Physics, vol. 106, Article ID 084318, 2009.

H. Richter, Z. P. Wang, and L. Ley, “The one phonon Raman spectrum in microcrystalline silicon,” Solid State Communications, vol. 39, no. 5, pp. 625–629, 1981.

A. G. Rolo, M. I. Vasilevskiy, M. Hamma, and C. Trallero-Giner, “Anomalous first-order Raman scattering in III-V quantum dots: optical deformation potential interaction,” Physical Review B, vol. 78, no. 8, Article ID 081304, 2008.

M. P. Chamberlain, C. Trallero-Giner, and M. Cardona, “Theory of one-phonon Raman scattering in semiconductor microcrystallites,” Physical Review B, vol. 51, no. 3, pp. 1680–1693, 1995.

L. Lu, X. L. Xu, W. T. Liang, and H. F. Lu, “Raman analysis of CdSe/CdS core-shell quantum dots with different CdS shell thickness,” Journal of Physics Condensed Matter, vol. 19, no. 40, Article ID 406221, 2007.

D. Nesheva, Z. Aneva, M. J. ŠĆepanović et al., “Composition and structure of ZnxCd1-xSe single layers prepared by thermal evaporation of ZnSe and CdSe,” Journal of Physics: Conference Series, vol. 253, no. 1, 2010.

C. Chen, M. Dutta, and M. A. Stroscio, “Surface-optical phonon assisted transitions in quantum dots,” Journal of Applied Physics, vol. 96, no. 4, Article ID 2049, pp. 2049–2054, 2004.

S. Hayashi and R. Ruppin, “Raman scattering from GaP microcrystals: analysis of the surface phonon peak,” Journal of Physics C, vol. 18, no. 12, Article ID 2583, 1985.

V. M. Dzhagan, M. Y. Valakh, O. E. Raevska, et al., “The influence of shell parameters on phonons in core–shell nanocrystals: a resonant Raman study,” Nanotechnology, vol. 20, Article ID 365704, 2009.

M. Mohr and C. Thomsen, “Phonons in bulk CdSe and CdSe nanowires,” Nanotechnology, vol. 20, no. 11, Article ID 115707, 2009.

S. Xu, C. Wang, and Y. Cui, “Theoretical investigation of CdSe clusters: influence of solvent and ligand on nanocrystals,” Journal of Molecular Modeling, vol. 16, no. 3, pp. 469–473, 2010.

A. G. Rolo, M. I. Vasilevskiy, N. P. Gaponik, A. L. Rogach, and M. J. M. Gomes, “Confined optical vibrations in CdTe quantum dots and clusters,” Physica Status Solidi (B), vol. 229, no. 1, pp. 433–437, 2002.