Physics Research International
Volume 2015 (2015), Article ID 532825, 8 pages
http://dx.doi.org/10.1155/2015/532825

Research Article

Structure and Microhardness of Titanium-Based Coatings Formed by Multichamber Detonation Sprayer

M. Kovaleva,¹ Yu. Tyurin,² N. Vasilik,³ O. Kolisnichenko,² M. Prozorova,¹ M. Arseenko,¹ V. Sirota,¹ and I. Pavlenko¹

¹Belgorod State National Research University, Pobeda 85, Belgorod 308015, Russia
²E.O. Paton Electric Welding Institute, NASU, Bozhenko 11, Kiev 03650, Ukraine
³N.N. Semenov Institute of Chemical Physics, RAS, Kosygina 4, Moscow 119991, Russia

Received 14 November 2014; Accepted 3 March 2015

Academic Editor: Martin Kroger

Copyright © 2015 M. Kovaleva et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

A series of titanium-based coatings (50–550 μm thick) on an aluminium substrate was deposited via multichamber detonation sprayer with different barrel lengths (300, 400, and 500, all in mm). The titanium-based coatings obtained in these three experiments were examined by optical microscopy, scanning electron microscopy, and X-ray phase analysis. The hardness tests were carried out by the Vickers method with a test load of 50 g. The multichamber detonation sprayer with a barrel length of 500 mm produced the dense layers of coating with hardness of  HV0.05 and porosity of 0.24%, the best result in the experiments.

1. Introduction

Aluminium and its alloys are important materials of research because it is abundant in nature, cost effective, and easy to handle and represents an important category of materials due to its high technological value, electrical capacity, and wide range of industrial applications [1], especially in aerospace and household industries. By nature, aluminium alloys are highly reactive [2, 3]. The challenge now is to protect surfaces of the aluminium parts under the most severe atmospheric conditions for a term of not less than 6–8 years.

A possible approach to increase their corrosion resistance is the deposition of a titanium coating layer [4, 5]. A thin layer of the titanium-based coating will have no substantial effect on the weight of a structure [6].

The unique properties of titanium such as high strength to weight ratio, excellent corrosion resistance, and biocompatibility have made this material a favourable option for many applications in aerospace [7], implants [8], and corrosive environments [9]. In view of better physical-mechanical properties of titanium and its compounds, it is of interest to deposit a coating of titanium-based materials on aluminium [10, 11]. Due to the unique properties of titanium, the titanium-based coatings are commonly used in aircraft, pipes for power plants, armour plating, naval ships, spacecraft, and missiles [12, 13].

At present, the process of titanium-based coatings formation is usually performed by means of thermal spray processes such as APS [14, 15], CVD [16], HVOF [17–19], cold spray [10, 20, 21], and warm spray [22, 23]. In conventional thermal spray processes, spraying materials are heated to high temperatures to induce complete or partial melting.

The critical velocity necessary to form the bonding of powder and substrate is relatively high for titanium due to its lower deformability related to its hcp crystal structure [24]; the reported microstructures of titanium coating tend to be porous as compared to more easily sprayable materials such as copper and aluminium [25]. Therefore, the development of new methods for making thick coatings of titanium with high density is indispensable for many industrial applications [26].

Our previous research [27] has shown that the titanium-based coatings obtained using multichamber detonation sprayer (MCDS) are uniform and dense, with porosity below 1% and high hardness; the bulk of the coatings material is generally deformed and closely packed; however, coarse inclusions in the form of nondeformed discrete particles were detected.

The aim of this paper is to investigate the microstructure and microhardness of titanium-based coatings which were obtained by multichamber gas-dynamic accelerator with different barrel lengths (300, 400, and 500, all in mm).

2. Experimental Procedure

The titanium-based coatings were deposited using commercial pure titanium powder Gr 1 produced by plasma atomization (Raymor Industries Inc.). To study the microstructures and morphologies of the titanium powder, cross sections were prepared and analyzed by electron ion microscope (SEM: Quanta 200 3D, Quanta 600 FEG) (Figures 1(a) and 1(b)). The titanium particles had a spherical morphology (Figure 1(a)). The particle size was measured by laser diffractometry (Analysette 22 NanoTec, FRITSCH GmbH, Germany) and showed that 90% of the particles were in the supplier specified size range of −45 to +5 μm with approximately 10 vol.% below 9 μm (Figure 1(c)).

(a)

(b)

(c)

(d)

Figure 1: Titanium powder particles (100 wt.% Ti): SEM image (a), micrograph of an as-polished powder cross section (b), cumulative powder size distribution measured by laser diffractometry (c), and XRD spectra (d).

Hardness of titanium powder particles was measured and was found to be at the level of HV0.01. The spray powders are dense and show no internal porosity (Figure 1(b)). The titanium powder of the phase composition and structure tested by X-ray diffraction have been certified at angle 2θ of 10 to 1000 by scanning with step Δ(2θ) = 0.020 and an exposure time of 2.5 seconds at a point on a diffractometer Rigaku Ultima IV (Cu-Kα, λ = 0,154059 nm). The phase analysis shows that the main phase in the titanium powder is Ti with hexagonal structure (Figure 1(d)).

Flat specimens of an aluminium alloy 6063 (Fe-0.35Cr-0.06Cu-0.10Mg-0.05Ti-0.15, all in wt.%) were used as substrates being sandblasted by 25А F360 alumina grits prior to spraying. The dimensions of the samples were  mm. The specimens were transversally cut by spark erosion, mechanically polished, and prepared by standard metallographic sample preparation methods [28] of sectioning, mounting, and polishing [29]. The samples were prepared by grinding with abrasive SiC paper (200, 500, 800, and 1,000 grades), followed by polishing with 1 μm diamond slurry.

In the present study, a multichamber, vertically mounted detonation sprayer (MCDS) was employed to deposit the titanium-based coatings. The automated equipment (Figure 2) consists of (1) device for spraying, (2) standard powder feeder with a feed rate of up to 3 kg/h, (3) a standard low-pressure (max. 0.3 MPa) gas panel for feeding oxygen, propane-butane, and air, (4) an automated control system for the technological process, (5) an automated manipulator for moving MCDS, and (6) a specimen holder [27, 30, 31].

Figure 2: Equipment for deposition of coatings: (1) device for spraying; (2) standard powder feeder with feed rate of up to 3 kg/h; (3) standard low-pressure (maximum 0.3 MPa) gas panel for feeding oxygen, propane-butane, and air; (4) an automated control system for the technological process; (5) an automated manipulator for moving MCDS; (6) a specimen holder.

A characteristic feature of MCDS is that the powder is accelerated by using the combustion products, which are formed in the MCDS chambers and are converged before entering the barrel, where they interact with the two-phase gas-powder cloud. A standard powder feeder of the Metco Company is used to feed powder to the barrel. A continuous gas-powder jet is divided into portions and fed to the barrel by using a special device: gas-dynamic synchronizer. The process of detonation mode of combustion of the fuel mixture (propane-butane, oxygen, and air) is initiated in a special chamber by using a spark plug at a frequency of 20–50 Hz. Then, the detonation mode of combustion spreads to the other chambers. Such initiation system and powder feeding scheme synchronize both the processes of detonation combustion and the injection of the powder into the barrel [32].

The titanium-based coatings (50–550 μm thick) were deposited in 6 passes in the three experiments differing in barrel length (300, 400, and 500, all in mm). In all cases, the powder feed rate was 800–1050 g/h, the detonation initiation frequency was 20 Hz, the distance from the exit section of the barrel to the plate treated was 50 mm, and the diameter of barrel was 18 mm. Flow rate of fuel mixture components was oxygen (2.2–2.7 m³/h), propane 30% + butane 70% (0.5–0.7 m³/h), and air (1.2–1.4 m³/h).

Examinations of microstructure were carried out by scanning electron microscope (SEM: Quanta 200 3D and Quanta 600 FEG) and optical microscopy (OM, Olympus GX 51). Porosity was determined by the metallographic method with qualitative and quantitative analysis of pore geometry using an inverted optical microscope (Olympus GX51) [33]. Ten arbitrarily selected micrographs for each experimental point were registered in the optic microscope (in the bright field, magnified 500x) using SIAMS Photolab software. Local phase and analyses were conducted by X-ray powder diffractometry (Rigaku Ultima). An X-ray powder diffractometer Rigaku Ultima IV using Cu-Kα monochromatic radiation (wavelength λ = 0.154178 nm) operating at 40 kV and 40 mA was employed to determine the X-ray diffraction patterns. X-ray diffraction spectrum for phase analysis was shooting by the scheme θ-2Θ scan focusing by Brega-Brentano in the angular range 5–95 deg. Investigations were carried out in the θ/2θ step scan mode with a step of 0.02 degrees in the 2θ range and a rate of 0.6 deg./min. Crystalline phases were identified using the ICCD PDF-2 (2008) powder diffraction database [34].

Measuring of microhardness was done using an automatic microhardness tester (DM-8B, AFFRI) via Vickers’s test with a test load 50 g (HV0.05). Indentation was carried out on cross sections of samples of the coatings, with the distance between the indents being 20 μm. The average of ten tests was used as an indicator of coating hardness.

3. Results and Discussion

The typical lamellar microstructure of titanium-based coatings obtained in our experimental study is presented in Figure 3. The coatings have a thickness of about 50–550 μm. The analysis performed allows us to make a conclusion that the fine powder particles were heated and deformed to a state of fine lamellae and that they filled the spacing between the coarse particles to form a dense coating (Figure 3).

(a)

(b)

(c)

(d)

(e)

(f)

(g)

(h)

(i)

Figure 3: SEM micrographs of cross sections of titanium-based coatings and histogram plot of the pore size distribution: ((a), (b), and (c)) barrel length 300 mm; ((d), (e), and (f)) barrel length 400 mm; ((g), (h), and (i)) barrel length 500 mm (SEM, backscattered electron mode).

Electron microscopy studies of transverse sections of the system “coating-substrate” (Figures 3(a) and 3(b)) show that the bulk of the coating material deposited using barrel length of 300 mm is not deformed; it consists of the nondeformed discrete particles and has the porosity of 13.49% (Figure 3(c)). Some of the reactive products may solidify into a semimelt state when barrel length is 300 mm. The coating layer deposited using barrel length of 400 mm was denser (Figures 3(d) and 3(e)) and had a porosity of 0.92% (Figure 3(f)) [35]. However, a lot of coarse inclusions in the form of nondeformed discrete particles were detected.

The microstructure of the coatings deposited using barrel length of 500 mm is dense and homogeneous (Figures 3(g) and 3(h)). The coatings (barrel length: 500 mm) had porosity of 0.24% (Figure 3(i)).

Comparing the microstructures presented in Figure 3, it can be seen that the apparent porosity decreases with the increase of barrel length from 300 to 500 mm and dense coatings with porosity 0.24% are produced at barrel length of 500 mm. The absence of porosity and a largely deformed splat structure in Figure 3(h) confirms that barrel length was used correctly to achieve an optimal dense material.

The spectrum shown in Figure 1(d) indicates that the process used in producing the titania feedstock resulted in the presence of Ti with hexagonal structure. Figure 4 shows the XRD patterns of the titanium coatings.

Figure 4: XRD pattern of the titanium-based coatings fabricated with different barrel lengths.

The phase analysis shows that after spraying the main phase in the coatings layer is Ti with hexagonal structure (Figure 4). The distinguished interplanar spacing calculated from reflections makes it possible to identify the following phases in the coatings: TiO with a cubic lattice, Ti₂O₃ with hexagonal structure, Ti₃O₅ with orthorhombic structure, anatase with tetragonal structure, and rutile with tetragonal structure.

Titanium exists in different oxidation states: Ti²⁺, Ti³⁺, and Ti⁴⁺. The corresponding oxides are TiO, Ti₂O₃, Ti₃O₅, TiO₂, and a complex combination of oxides called Magneli phases, which correspond to the general formula (). The Magneli phases are formed when TiO₂ is annealed in a reducing atmosphere [36].

It can be seen (Figure 4) that the coating fabricated with a barrel length of 300 mm is mainly composed of unreacted Ti, TiO, and Ti₂O₃. When the barrel length increases to 400 mm, the coating is composed of unreacted Ti, TiO, Ti₂O₃, and Ti₃O₅. This is because, during the spraying process, the reaction between particles and gas is not complete and the intermediate and/or metastable oxides may be produced at a faster rate [37, 38]. With the increase of the barrel length up to 500 mm, the coating is composed of some unreacted Ti, TiO, and Ti₂O₃, and, as a new component, TiO₂ (anatase, rutile) was found in the coating. It means that, with the increase of the barrel length, more reaction time (higher temperature) and more reaction gas can be provided for the reactions of oxidation [39, 40]. As a result, more Ti oxides and stable Ti oxides will be produced.

An average microhardness of the coatings is given in Table 1. A wide range of hardness values in obtained coatings is caused by their different phase composition and porosity. The fine powder fraction is almost completely melted, while the larger particles fraction might remain solid. In practice, this leads to the formation of a material with some local differences in mechanical properties.

Table 1: Microhardness of samples, data based on HV0.05 test.

Substrate (aluminium 6063)
100 ± 25

Titanium-based coatings

Barrel length, mm

300
685 ± 250

400
820 ± 250

500
1300 ± 250

The microhardness increases with the increase of barrel length in the range of 300–500 mm. This relationship can be explained as follows: with the increase of barrel length, more reaction time and more reactants are provided. This promotes the reactions of Ti with oxygen in the air and more Ti composite hard phases may be synthesized as mentioned in the former section [39].

Microhardness was similar in experiment #1 (barrel length: 300 mm) and in experiment #2 (barrel length: 400 mm), ranging from 435 to 1070 HV0.05. These coatings were fairly porous and their cross section micrographs (Figures 3(a)–3(f)) clearly revealed numerous spherically shaped particles, which is an indication of the lack of plastic deformation.

Thus, strain hardening was not prevalent, particularly when compared to denser coatings, as for barrel length of 500 mm. In these situations, the microhardness values increase significantly ( HV0.05). The highest value recorded was 1550 HV0.05 and it was observed in experiment #3 (barrel length: 500 mm). In particular, under these conditions, a significant amount of material jetting occurred (Figures 3(g) and 3(h)). This facilitated the plastic deformation of the titanium particles and, consequently, a denser coating is produced. Thus, the likelihood of the decreased coating microhardness caused by weaker interparticle bonding is reduced. Second, a tamping effect in which the initially sprayed particles would be further flattened and strain-hardened by the subsequent impacting particles would occur. It means that a significant strain hardening would take place. As a result, the coating microhardness would increase [40].

4. Conclusions

In the present investigation, the multichamber detonation sprayer was used for the deposition of the titanium-based coatings of titanium powder on aluminium substrate. The multichamber gas-dynamic sprayer (MCDS) has replaceable barrels (lengths 300, 400, and 500 mm) and operates on a fuel mixture of gases: propane (30%) + butane (70%), oxygen, and air. It was established that the apparent porosity and microhardness increase with an increase in barrel length from 300 to 500 mm and the densest coatings with the porosity of 0.24% and microhardness of 1300 ± 250 HV0.05 are produced at barrel length of 500 mm. At that spraying experiment, the fine powder particles were heated and deformed to a state of fine lamellae, and they filled the spacing between the coarse particles to form a dense homogeneous coating. Also it has been found that, with the increase of barrel length up to 500 mm, TiO₂ (anatase, rutile) appear in the coating besides Ti, TiO, and Ti₂O₃. This corresponds to the following phase transformation taking place during the spraying: TiO → Ti₂O₃ → Ti₃O₅ → phase Magnelli → TiO₂. It means that, with the increase of barrel length, more reaction time (higher temperature) and reaction gas can be provided for reactions of oxidation. It was established that the microhardness growth associated with a change in porosity, with the quantitative phase ratio in the coatings, and with the appearance of TiO₂ (anatase, rutile).

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This work was carried out on the equipment of the Joint Research Center “Diagnostics of Structure and Properties of Nanomaterials” of Belgorod State National Research University. This work was financially supported by the Ministry of Education and Science of the Russian Federation under Project no. 14.594.21.0010 (Code RFMEFI62114X0005).

References

J. W. Diggle, T. C. Downie, and C. W. Goulding, “Anodic oxide films on aluminum,” Chemical Reviews, vol. 69, no. 3, pp. 365–405, 1969.

S. Wernick, R. Pinner, and P. G. Sheasby, The Surface Treatment and Finishing of Aluminium and Its Alloys, vol. 1, ASM Handbook, ASM International, Novelty, Ohio, USA, 5th edition, 1987.

E. H. Hollingsworth and H. Y. Hunsicker, “Corrosion of aluminum and aluminum alloys,” in ASM Handbook, vol. 13, pp. 583–609, ASM International, Metals Park, Ohio, USA, 9th edition, 1987.

H. Schiht, H. Hildebrand, and U. Szumanuski, “Highly corrosion-resistant reflection layer systems on substrates,” GB Patent 2112815, 1983

A. Vovsi, N. Kashpur, and O. Rashevic, Deposition of Coatings in Vacuum, Zinatne, Riga, Latvia, 1986.

J. A. Mountford, “Titanium—properties, advantages and applications solving the corrosion problems in marine service,” Tech. Rep. 02170, U.S. Navy & Industry Corrosion Technology Information, 2001, RUST 2001.

R. R. Boyer, “An overview on the use of titanium in the aerospace industry,” Materials Science and Engineering A, vol. 213, no. 1-2, pp. 103–114, 1996.

O. E. M. Pohler, “Unalloyed titanium for implants in bone surgery,” Injury, vol. 31, no. 4, pp. D7–D13, 2000.

M. J. Donachie Jr., Titanium: A Technical Guide, ASM International, Materials Park, Ohio, USA, 2nd edition, 2000.

D. K. Christoulis, S. Guetta, V. Guipont, and M. Jeandin, “The influence of the substrate on the deposition of cold-sprayed titanium: an experimental and numerical study,” Journal of Thermal Spray Technology, vol. 20, no. 3, pp. 523–533, 2011.

T. Kinos, S. L. Chen, P. Siitonen, and P. Kettunen, “Densification of plasma-sprayed titanium and tantalum coatings,” Journal of Thermal Spray Technology, vol. 5, no. 4, pp. 439–444, 1996.

ASM Handbook Volume 2: Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM International, 1992.

J. A. Mountford Jr., “Titanium—properties, advantages and applications solving the corrosion problems in marine service,” in Proceedings of the CORROSION, Paper Number 02170, NACE International, Denver, Colo, USA, April 2002.

W.-M. Zhao, C. Liu, L.-X. Dong, and Y. Wang, “Effects of arc spray process parameters on corrosion resistance of Ti coatings,” Journal of Thermal Spray Technology, vol. 18, no. 4, pp. 702–707, 2009.

Y. Yao, Z. Wang, Z. Zhou, S. Jiang, and J. Shao, “Study on reactive atmospheric plasma-sprayed in situ titanium compound composite coating,” Journal of Thermal Spray Technology, vol. 22, no. 4, pp. 509–517, 2013.

A. C. Jones and M. L. Hitchman, “Overview of chemical vapour deposition,” in Chemical Vapour Deposition: Precursors, Processes and Applications, chapter 1, pp. 1–36, RSC Publishing, 2008.

R. S. Lima and B. R. Marple, “Nanostructured and conventional titania coatings for abrasion and slurry-erosion resistance sprayed via APS, VPS and HVOF,” in Proceedings of the Thermal Spray Connects: Explore Its Surfacing Potential (ITCS '05), C. C. Berndt, Ed., pp. 552–557, ASM International, Basel, Switzerland, May 2005.

J. Kawakita, S. Kuroda, T. Fukushima, H. Katanoda, K. Matsuo, and H. Fukanuma, “Dense titanium coatings by modified HVOF spraying,” Surface and Coatings Technology, vol. 201, no. 3-4, pp. 1250–1255, 2006.

K. Kim, M. Watanabe, and K. Mitsuishi, “Microstructure observation on the interface between warm spray deposited titanium powder and steel substrate,” in Proceedings of the Thermal Spray: Crossing Borders (ITSC '08), E. Lugscheider, Ed., pp. 1289–1294, ASM International, Maastricht, The Netherlands, June 2008.

S. H. Zahiri, C. I. Antonio, and M. Jahedi, “Elimination of porosity in directly fabricated titanium via cold gas dynamic spraying,” Journal of Materials Processing Technology, vol. 209, no. 2, pp. 922–929, 2009.

H. R. Wang, B. R. Hou, J. Wang, Q. Wang, and W.-Y. Li, “Effect of process conditions on microstructure and corrosion resistance of cold-sprayed Ti coatings,” Journal of Thermal Spray Technology, vol. 17, no. 5-6, pp. 736–741, 2008.

J. Kawakita, H. Katanoda, M. Watanabe, K. Yokoyama, and S. Kuroda, “Warm spraying: an improved spray process to deposit novel coatings,” Surface and Coatings Technology, vol. 202, no. 18, pp. 4369–4373, 2008.

K.-H. Kim, S. Kuroda, M. Watanabe, R.-Z. Huang, H. Fukanuma, and H. Katanoda, “Comparison of oxidation and microstructure of warm-sprayed and cold-sprayed titanium coatings,” Journal of Thermal Spray Technology, vol. 21, no. 3-4, pp. 550–560, 2012.

T. Schmidt, F. Gärtner, H. Assadi, and H. Kreye, “Development of a generalized parameter window for cold spray deposition,” Acta Materialia, vol. 54, no. 3, pp. 729–742, 2006.

T. Marrocco, D. G. McCartney, P. H. Shipway, and A. J. Sturgeon, “Production of titanium deposits by cold-gas dynamic spray: numerical modeling and experimental characterization,” Journal of Thermal Spray Technology, vol. 15, no. 2, pp. 263–272, 2006.

A. Papyrin, V. Kosarev, S. Klinkov, A. Alkhimov, and V. Fomin, Cold Spray Technology, Elsevier, Amsterdam, The Netherlands, 2007.

M. Kovaleva, Y. Tyurin, O. Kolisnichenko, M. Prozorova, and M. Arseenko, “Properties of detonation nanostructured titanium-based coatings,” Journal of Thermal Spray Technology, vol. 22, no. 4, pp. 518–524, 2013.

G. Sridhar, S. G. Chowdhury, and N. G. Goswami, Materials Characterization Techniques: Principles and Applications, 1999.

ASTM Standard, “Standard methods of preparing metallographic specimens,” in Annual Book of ASTM Standards E-3-86, vol. 03.01, p. 12, American Society for Metals, 1986.

M. Kovaleva, Y. Tyurin, N. Vasilik et al., “Deposition and characterization of Al₂O₃ coatings by multi-chamber gas-dynamic accelerator,” Surface and Coatings Technology, vol. 232, pp. 719–725, 2013.

N. Vasilik, N. Tyurin, and O. Kolisnichenko, “Method for gas-dynamic detonating speedup of powders and device for its implementation,” RU Patent 2506341, 2012

N. J. Vasilik, Y. N. Tyurin, O. V. Kolisnichenko, M. G. Kovaleva, M. S. Prozorova, and M. Y. Arseenko, “Properties, peculiarities and applications of powder coatings formed by multi-chamber detonation sprayer,” Applied Mechanics and Materials, vol. 467, pp. 179–184, 2014.

G. J. Moskal, “The porosity assessment of thermal barrier coatings obtained by APS method,” Journal of Achievements in Materials and Manufacturing Engineering, vol. 20, no. 1-2, pp. 483–486, 2007.

T. Hussain, D. G. McCartney, P. H. Shipway, and T. Marrocco, “Corrosion behavior of cold sprayed titanium coatings and free standing deposits,” Journal of Thermal Spray Technology, vol. 20, no. 1-2, pp. 260–274, 2011.

M. Kovaleva, Y. Tyurin, M. Arseenko, V. Sirota, and I. Pavlenko, “Titanium nanostructured coatings obtained by multi-chamber gas-dynamic accelerator,” in Proceedings of the 5th International Conference Nanocon, Brno, Czech Republic, October 2013, http://www.nanocon.eu/.

M. Miyayama, K. Koumoto, and H. Yanagida, Engineered Materials Handbook, Volume 4: Ceramics and Glasses, ASM International, Materials Park, Ohio, USA, 1991.

Y. Yao, Z. Wang, Z. Zhou, S. Jiang, and J. Shao, “Study on reactive atmospheric plasma-sprayed in situ titanium compound composite coating,” Journal of Thermal Spray Technology, vol. 22, no. 4, pp. 509–517, 2013.

R. S. Lima and B. R. Marple, “Optimized HVOF titania coatings,” Journal of Thermal Spray Technology, vol. 12, no. 3, pp. 360–369, 2003.

H. Okamoto, “O-Ti (Oxygen-Titanium),” Journal of Phase Equilibria and Diffusion, vol. 32, no. 5, pp. 473–474, 2011.

W. Wong, E. Irissou, A. N. Ryabinin, J.-G. Legoux, and S. Yue, “Influence of helium and nitrogen gases on the properties of cold gas dynamic sprayed pure titanium coatings,” Journal of Thermal Spray Technology, vol. 20, no. 1-2, pp. 213–226, 2011.