The aim of this study was to evaluate the discoloration effects of water, cola-based soft drink, coffee, and wine on resin composites used in restorative dentistry and the possibility of removing the stain with chair side manual polishing. The A2 shade of three materials was tested. Disc specimens were prepared. A spectrophotometer was used to measure the baseline CIE-Lab color parameters of each material (n=10) 24 hours after sample preparation. Samples were then immersed in a cola-based soft drink, coffee, or wine for 1 hour every day, for 30 days. For the remaining hours, the specimens were stored in distilled water. In the control group, the specimens were immersed in water for the whole period. The color differences (ΔE) were calculated after 7 and 30 days of storage, and after polishing with coarse Sof-Lex discs, and analyzed by two-way ANOVA with repeated measures and Tukey’s HSD test (α=0.05). Luna presented higher ΔE values 3.41a followed by Durafill 2.82b and Herculite 2.24c. For the drink solutions, ΔE values were higher for wine 4.40a followed by coffee 2.59b and for cola-based soft drink 2.23c and water 2.13c which were statistically similar. For time, ΔE values were higher for 30 days 3.97a and then for 7 days 2.48b and after polishing 2.04c. The results indicate that color stability is material dependent. The types of drinks that patients consume also influence the color stability of restorative materials.
1. Introduction
The color stability of composite materials used in restorative dentistry is crucial, both after the material is completely cured and throughout the restoration’s lifetime. Previous studies have described color changes occurring in direct dental composites [1, 2]; however, discoloration of resin-based materials may be caused by different factors [3].
Direct composite resins are composed of a polymer matrix and fillers and can be classified into nanocomposite, nanohybrid, microhybrid, and microfilled materials [4]. Chemical discoloration of these materials has been attributed to a change or oxidation in the amine accelerator, oxidation in the structure of the polymer matrix, and oxidation of the unreacted pendant methacrylate groups. Color stability can also depend on the interface of the matrix and the different fillers used in these materials [5, 6]. Thus, the color stability of direct composites can be affected by their chemical components.
Additionally, extrinsic factors can cause discoloration, for example, staining by absorption of colorants as a result of contamination from exogenous sources. The degree of discoloration from exogenous sources varies according to the eating and drinking habits of the patient. The effects of different drink solutions (e.g., coffee, wine, and cola-based soft drink) on the color stability of different restorative materials over time have been evaluated previously [1, 3].
Discoloration can be considered one of the main reasons for the replacement of esthetic restorations made with resin composite [7]. In general, the superficial layer of the restorations is the most affected by discoloration, since this is the one in contact with food and drink colorants, being more prone to extrinsic pigmentation. In some clinical situations, if the restoration is still in function but the material has been nonseverely stained, an attempt to avoid the premature replacement of a composite restoration in anterior teeth can be carried out. Depending on the depth of the stain, chair side repolish of the restoration could be a viable option to remove the superficial layer, attempting to recover its initial color or at least make it unnoticeable for the human eye [8–10].
The aim of this study was to evaluate the influence of different drink solutions on the color stability of different resin composites and the possibility of removing the stain with chair side manual repolishing. The following hypotheses were evaluated: (i) the type of resin composite evaluated may affect color stability; (ii) the type of drink solution might have an influence on color stability; and (iii) chair side repolishing would be effective in removing the stain.
2. Material and Methods
Disc specimens of three different methacrylate-based materials (Herculite Classic [Kerr Corporation, Orange, CA, USA], Durafill VS [Heraeus Kulzer GmbH & Co., Wehrheim, Germany], and Luna [SDI Ltd., Bayswater, Victoria, Australia]) (Table 1) were constructed with the aid of a polytetrafluorethylene matrix. All specimens were prepared under conditions of controlled humidity (55±5%) and temperature (23±1°C). Ten disk specimens, 8 mm in diameter and 1 mm in thickness, were prepared for each material.
Name, material type, and manufacturer of the resin composites tested.
Product/manufacturer
Material type
Composition
Herculite Classic (Kerr Corporation, Orange, CA, USA)
Durafill VS (Heraeus Kulzer GmbH & Co., Wehrheim, Germany)
Microfilled composite
BisGMA/TEGDMA, UDMA, silicon dioxide, splinter polymer (66% by volume)
Luna (SDI, Bayswater, Victoria, Australia)
Nanohybrid composite
Multifunctional methacrylate ester and inorganic filler (61% by volume)
The matrix was placed onto a microscope lamina of 1 mm in thickness, followed by the insertion of the resin composite. Next, a polyester strip was placed onto the orifice of the matrix and another microscope lamina of the same thickness was positioned on top of it. The resin composite was then light-cured for 40 seconds with a halogen curing unit (Optilux Demetron 400; Kerr Corporation) at a irradiance of 700 mW/cm2.
Subsequently, the color of the resin was evaluated using the CIE-Lab system with the aid of a spectrophotometer (VITA Easyshade 3D Master; Vita Zahnfabrik, Bad Säckingen, Germany), in order to define a baseline color measurement. The specimens were then placed in water, cola-based soft drink, coffee, or wine for 1 hour every day, for 30 days. For the remaining hours, the specimens were stored in distilled water. Their color parameters were then evaluated after 7 and 30 days. After 30 days, the specimens were polished with coarse Sof-Lex disc and again submitted to color evaluation. In the control group, the specimens were immersed in water for the whole period.
The CIE L∗ parameter corresponds to the degree of lightness and darkness, whereas a∗ and b∗ coordinates correspond to red or green (+a∗ = red, -a∗ = green) and yellow or blue (+b∗ = yellow, -b∗ = blue), respectively. These coordinates were used to calculate the color difference (ΔE) between the baseline color measurement (24 hours after photo-curing) and color measurements after storage for 7 and 30 days and after polishing. Before each color measurement, the immersed specimens were dried with absorbent paper. The ΔE for each experimental time was calculated using the following:(1)ΔE=ΔL∗2+Δa∗2+Δb∗21/2.
In which ΔL∗, Δa∗, and Δb∗ represent the differences between the readings of the color parameters obtained from the specimens under the different conditions evaluated. The results of ΔE were analyzed by two-way ANOVA with repeated measures and Tukey’s HSD test (α=0.05).
3. Results
The mean and standard deviation values of ΔE are presented in Table 2. Statistical analysis indicated significant differences for all the main factors, double and triple interactions (p=0.000).
Mean ± standard deviation values of ΔE for all conditions tested. Values followed by the same letters are statistically similar (p > 0.05).
Material
Solution
Time
ΔE
Herculite Classic
Water
7 days
1.37 ± 0.36ab
30 days
1.83 ± 0.35abc
After polishing
1.59 ± 0.39ab
Cola
7 days
1.61 ± 0.32ab
30 days
1.97 ± 0.73abc
After polishing
1.73 ± 0.51abc
Coffee
7 days
1.33 ± 0.22ab
30 days
2.68 ± 0.71cdefg
After polishing
2.09 ± 0.48abcde
Wine
7 days
3.11 ± 0.72defgh
30 days
5.30 ± 1.36k
After polishing
2.36 ± 0.53bcdef
Durafill VS
Water
7 days
1.18 ± 0.79a
30 days
2.36 ± 0.95bcdef
After polishing
2.11 ± 0.39abcde
Cola
7 days
1.68 ± 0.56abc
30 days
2.27 ± 0.23bcdef
After polishing
1.85 ± 0.36abc
Coffee
7 days
1.83 ± 0.44abc
30 days
3.81 ± 0.50hij
After polishing
2.27 ± 0.72bcdef
Wine
7 days
4.28 ± 0.51ijk
30 days
6.78 ± 1.03l
After polishing
4.09 ± 0.82hij
Luna
Water
7 days
3.06 ± 0.57defgh
30 days
3.59 ± 0.35ghi
After polishing
2.12 ± 0.57abcdef
Cola
7 days
3.16 ± 0.47fgh
30 days
4.38 ± 0.37ijk
After polishing
1.47 ± 0.41ab
Coffee
7 days
3.04 ± 0.56defgh
30 days
4.85 ± 0.51jk
After polishing
1.45 ± 0.40ab
Wine
7 days
4.26 ± 0.62ij
30 days
8.07 ± 0.53m
After polishing
1.55 ± 0.67ab
Considering the individual factors, Luna presented higher ΔE values 3.41a, followed by Durafill VS 2.82b and Herculite 2.24c. For the drink solutions, ΔE values were higher for wine 4.40a, followed by coffee 2.59b, and for cola-based soft drink 2.23c and water 2.13c, which were statistically similar. For time, ΔE values were higher for 30 days 3.97a and then for 7 days 2.48b and after polishing 2.04c.
4. Discussion
The three hypotheses evaluated in the present study were accepted. There were significant differences between the resin composites evaluated, and significant effects of the type of drink solution and time on color stability were detected. Also, chair side polishing significantly reduced the color difference, when compared to the values obtained after staining for 30 days in the different drink solutions.
Discoloration can be evaluated visually or by instrumental techniques. Shade selection with visual guides can be considered a subjective method, while shade obtained with spectrophotometers can be thought of as an objective method. In the current study, the system used for measuring chromaticity was chosen to record color differences because it is more precise than visual techniques and is capable of detecting color differences below the threshold of visual perception [11, 12].
Storage in water is used frequently as a model of in vitro aging. It is well known that water absorbed by the polymer matrix causes filler matrix debonding and hydrolytic degradation of the filler [13–16]; however, it can also change the refractive index of the material [17]. Therefore, an increase in ΔE values might be affected by water absorption occurring in the resin composites used. In the present study, the ΔE values showed a tendency to increase as immersion period increased, suggesting that the color of resin composites would tend to darken over long-term clinical use [17]. Cola-based soft drinks, coffee, and wine are commonly consumed drinks and other investigators have demonstrated discoloration of composite materials upon exposure to these solutions [2, 18–20]. In the present study, there was no difference in discoloration between exposure to water and to cola-based soft drink. This is in accordance with other studies, because cola drinks do not appear to be strongly implicated in color change of composites, despite the presence of phosphoric acid [9, 21]. It is likely that the lower pH of the drinks tested affected the composite resin surface, increasing pigment absorption. However, the alcohol in wine increased this color degradation even further.
In the current study, color variation was considered imperceptible when <1, clinically acceptable when ≤3.3, and unacceptable when higher than 3.3. After aging, all specimens showed changes in the L∗, a∗, and b∗ coordinates, but all of the color differences were deemed acceptable. The mean color difference (ΔE) was the highest in Luna resin composite (ΔE=3.41), the lowest in Herculite resin composite (ΔE=2.24), and intermediate in Durafill VS resin composite (ΔE=2.82). This suggests that more color degradation occurred in the nanohybrid material than in the microfilled and microhybrid materials.
Degradation of residual amines and oxidation of residual unreacted carbon-carbon double bonds culminate in the formation of yellowing compounds in all resin-based materials [22, 23]. Durafill VS and Luna are microfilled and nanohybrid resin composites and have a small filler size. This might be expected to contribute to decreased staining and enhanced esthetic appearance [24]. However, composites with a smaller filler size do not necessarily show low levels of discoloration, as demonstrated in the present study. Staining of composite resins is dependent on monomer structure, as well as surface irregularities. Hence, the results of the present study are in agreement with previous findings.
As mentioned before, stained resin composite restorations are a common finding in the dental practice. In this way, the present study attempted to determine the superficial staining in three resin composites because it was expected that staining would occur in the most external layer of the material [8, 25]. Therefore, polishing the resin composite after the staining procedures would possibly remove discoloration. The results indicated that polishing of the specimens’ surface stained by the drink solutions was able to significantly reduce the ΔE values for the three tested composite resins, especially when stored in wine and coffee. In the groups immersed in water and cola-based soft drink, ΔE values were already lower than 2 in all times. Also, it is important to note that after polishing, ΔE values were considered clinically acceptable, being lower than 2.36 in all groups, except for Durafill VS (storage in wine), where ΔE was 4.09. Regarding storage in wine, which was considered the most staining of the drink solutions used in the present study, Luna showed a greater decrease in the ΔE values after polishing and a reduction of approximately 80% of discoloration, followed by Herculite with a reduction of 55% and Durafill VS with a 40% reduction in discoloration. Similar percentages of reduction in discoloration after polishing were also reported in the literature [9]. It is important to note that this difference between stained specimens’ and polished specimens’ color showed a good quality of polishing procedures. Also, the nature of the stain was an important factor influencing the level of the reduction in discoloration [10].
Many materials with different compositions are available on the market. More studies should be conducted in order to evaluate the color changes of resin composites in different situations. This would aid in understanding and improve esthetic results in the long term [26].
5. Conclusions
In the present study, all the materials tested showed visible color changes after immersion in drink solutions. The wine solution used caused the most staining. Luna resin composite showed a significantly higher color change as compared to the other resins investigated. Chair side polishing of the specimens’ surface stained by the drink solutions was able to significantly reduce the ΔE values for the tested materials, especially after being stored in wine and coffee.
Conflict of Interests
The authors declare that there is no conflict of interests regarding the publication of this paper.
Al-SamadaniK. H.Color stability of restorative materials in response to Arabic coffee, Turkish coffee and Nescafe201314468169010.5005/jp-journals-10024-13852-s2.0-84893408834ReddyP. S.TejaswiK. L. S.ShettyS.AnnapoornaB. M.PujariS. C.ThippeswamyH. M.Effects of commonly consumed beverages on surface roughness and color stability of the nano, microhybrid and hybrid composite resins: an in vitro study201314471872310.5005/jp-journals-10024-13902-s2.0-84893378148TopcuF. T.SahinkesenG.YamanelK.ErdemirU.OktayE. A.ErsahanS.Influence of different drinks on the colour stability of dental resin composites2009315056FerracaneJ. L.Resin composite—state of the art2011271293810.1016/j.dental.2010.10.0202-s2.0-78651229763CraigR.PowersJ. M.2002MosbyFuruseA. Y.GordonK.RodriguesF. P.SilikasN.WattsD. C.Colour-stability and gloss-retention of silorane and dimethacrylate composites with accelerated aging2008361194595210.1016/j.jdent.2008.08.0012-s2.0-53549093560DeligeorgiV.MjörI. A.WilsonN. H.An overview of reasons for the placement and replacement of restorations20018151110.1308/1355761017717993352-s2.0-0035232172AnfeT. E. D. A.AgraC. M.VieiraG. F.Evaluation of the possibility of removing staining by repolishing composite resins submitted to artificial aging201123426026710.1111/j.1708-8240.2011.00435.x2-s2.0-79961082229MundimF. M.GarciaL. D. F. R.Pires-de-SouzaF. D. C. P.Effect of staining solutions and repolishing on color stability of direct composites201018324925410.1590/s1678-775720100003000092-s2.0-77957726585RutkunasV.SabaliauskasV.Effects of different repolishing techniques on colour change of provisional prosthetic materials20091141021122-s2.0-77951237123BahannanS. A.Shade matching quality among dental students using visual and instrumental methods2014421485210.1016/j.jdent.2013.11.0012-s2.0-84891009372Gómez-PoloC.Gómez-PoloM.Celemin-ViñuelaA.Martínez Vázquez De PargaJ. A.Differences between the human eye and the spectrophotometer in the shade matching of tooth colour201442674274510.1016/j.jdent.2013.10.0062-s2.0-84901244630BreschiL.MazzoniA.RuggeriA.CadenaroM.Di LenardaR.DorigoE. D. S.Dental adhesion review: aging and stability of the bonded interface20082419010110.1016/j.dental.2007.02.0092-s2.0-37049006519FerracaneJ. L.BergeH. X.CondonJ. R.In vitro aging of dental composites in water—effect of degree of conversion, filler volume, and filler/matrix coupling199842346547210.1002/(sici)1097-4636(19981205)42:3lt;465::aid-jbm17>3.0.co;2-f2-s2.0-0032488231SilamiF. D. J.MundimF. M.GarciaL. D. F. R.SinhoretiM. A. C.Pires-De-SouzaF. D. C. P.Color stability of experimental composites containing different photoinitiators2013413e62e6610.1016/j.jdent.2012.10.0092-s2.0-84880308998SöderholmK. J.ZiganM.RaganM.FischlschweigerW.BergmanM.Hydrolytic degradation of dental composites198463101248125410.1177/002203458406301017012-s2.0-0021503430KoishiY.TanoueN.AtsutaM.MatsumuraH.Influence of visible-light exposure on colour stability of current dual-curable luting composites200229438739310.1046/j.1365-2842.2002.00823.x2-s2.0-0036550747FontesS. T.FernándezM. R.de MouraC. M.MeirelesS. S.Color stability of a nanofill composite: effect of different immersion media200917538839110.1590/s1678-775720090005000072-s2.0-70749158973MalekipourM. R.SharafiA.KazemiS.KhazaeiS.ShiraniF.Comparison of color stability of a composite resin in different color media201294441446TuncE. S.BayrakS.GulerA. U.TulogluN.The effects of children's drinks on the color stability of various restorative materials200934214715010.17796/jcpd.34.2.953q2556214367882-s2.0-77950107338Aliping-MckenzieM.LindenR. W. A.NicholsonJ. W.The effect of Coca-Cola and fruit juices on the surface hardness of glass-ionomers and ‘compomers’200431111046105210.1111/j.1365-2842.2004.01348.x2-s2.0-9144238743LuH.PowersJ. M.Color stability of resin cements after accelerated aging20041753543582-s2.0-16544394369PatelS. B.GordanV. V.BarrettA. A.ShenC.The effect of surface finishing and storage solutions on the color stability of resin-based composites2004135558759410.14219/jada.archive.2004.02462-s2.0-2642564252VichiA.FerrariM.DavidsonC. L.Color and opacity variations in three different resin-based composite products after water aging200420653053410.1016/j.dental.2002.11.0012-s2.0-2342483659TürkünL. Ş.LeblebicioğluE. A.Stain retention and surface characteristics of posterior composites polished by one-step systems20061963433472-s2.0-33846144715GönülolN.YilmazF.The effects of finishing and polishing techniques on surface roughness and color stability of nanocomposites201240supplement 2e64e7010.1016/j.jdent.2012.07.0052-s2.0-84870909726