Advances in Civil Engineering
Volume 2020 (2020), Article ID 8850436, 11 pages
https://doi.org/10.1155/2020/8850436

Research Article

The Effects of Different Nanoadditives on the Physical and Mechanical Properties of Similar Silty Mudstone Materials

Ji-jing Wang,¹ Zhen-ning Shi,² Ling Zeng,³ and Shuang-xing Qi³

¹School of Traffic & Transportation Engineering, Changsha University of Science & Technology, Changsha 410114, China
²School of Traffic & Transportation Engineering, National Engineering Laboratory of Highway Maintenance Technology, Changsha University of Science & Technology, Changsha 410114, China
³School of Civil Engineering, Changsha University of Science & Technology, Changsha 410114, China

Correspondence should be addressed to Zhen-ning Shi; shizhenning@126.com and Ling Zeng; zl001@csust.edu.cn

Received 18 June 2020; Revised 15 July 2020; Accepted 26 July 2020; Published 11 August 2020

Academic Editor: Songtao Lv

Copyright © 2020 Ji-jing Wang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

In order to analyze the influence of different nanoadditives on the physical and mechanical properties of similar silty mudstone materials, nano-TiO₂ (NTi), nano Al₂O₃ (NAl), and nanobentonite (NBe) were added to improve the physical and mechanical properties of silty mudstone similar materials. The physical and mechanical parameters are more in line with silty rock. Finally, nanometer additives suitable for silty mudstone similar materials are determined by conducting density test, natural water absorption test, uniaxial compression test, splitting test, softening coefficient test, expansibility test, and microscopic test. The effects of adding NTi, NAl, and NBe on improving the physical and mechanical properties of silty mudstone similar materials were studied to analyze the influence law of different NTi, NAl, and NBe contents on similar material density, natural water absorption, uniaxial compressive strength, tensile strength, softening coefficient, expansion rate, and other physical and mechanical parameters. The microscopic morphology of similar materials was analyzed by scanning electron microscopy and the mechanism of influence of nanoadditives on the microscopic structure of samples was revealed. The results are as follows. (1) The density of similar materials of silty mudstone increases with the increase of the content of nanoadditive. The natural water absorption rate decreased first and then increased with the increase of the content of nanometer additives, while the softening coefficient decreased with the increase of the content of nanometer additives. The uniaxial compressive strength and tensile strength increased first and then decreased with the increase of the content of nanometer additives. This is due to the incorporation of the nanoadditive amount effective to promote the hydration reaction of gypsum and accelerate the production of cement, while a similar material may be filled in the pores, reducing the internal defects, a similar material to make denser; when excessive dosage, nanoadditives agglomeration occurs, resulting in deterioration of the effect, but will reduce the mechanical properties of similar materials. (2) When the content of NBe is 6%, the physical and mechanical parameters of similar materials can reach or be closer to the silty raw rock except uniaxial compressive strength. The failure mode of the uniaxial compression specimen is also the same as that of the original rock, which can be used as the best choice. The research results laid the foundation for further analysis of NBe application in similar materials.

1. Introduction

In the experimental study on the ratio of similar materials in silty mudstone, gypsum is used as the binder, and barite powder is used as the aggregate to make similar materials. Because the physical and mechanical parameters of similar materials such as density, natural water absorption, uniaxial compressive strength, softening coefficient, and swelling are quite different from those of the silty Original rock, they cannot represent the physical and mechanical characteristics of the natural rock and affect the accuracy of model tests. The existing related research shows that choosing appropriate additives to incorporate into similar materials can improve the related physical and mechanical properties of similar materials of silty mudstone [1, 2]. In recent years, with the rapid development of nanotechnology, the production cost of nanomaterials has been decreasing year by year. At the same time, nanomaterials have shown physical effects that some macroscopic materials do not have, such as small size, large specific surface area, and high surface energy, and have been widely concerned [3]. The nanomaterials, often used as inorganic additives, are being widely used in housing, water conservancy, bridge, municipal, and other projects, which has achieved good application results [4–8].

At present, the appropriate amount of nanoadditives in the existing materials can effectively improve the relevant physical and mechanical parameters of the materials, formulate mixed materials suitable for different needs, and increase the scope of the original materials [9–14]. In terms of improving the cement substrate, Wang et al. found that adding nano-CaCO₃ into Portland cement can significantly improve the mechanical properties of cement-based materials and make the cement substrate more uniform. In [15–20], the control effect of mixing nano-SiO₂, nano-TiO₂, and nano-Al₂O₃ materials on water loss in oil well cement slurry was analyzed. The three nanoadditives mentioned above can effectively control the loss of liquid in cement when used separately, among which 3% nano-SiO₂ can reduce the amount of loss by 72%, with the most obvious effect. In terms of improving the performance of mixed materials, Anuj [21] found that, in the study of the properties of mixed materials, adding appropriate nanometer additives can not only promote hydration reaction but also play a role in filling the original micropores of the materials, thus improving the internal pore structure and significantly improving the physical and mechanical properties of the materials [22, 23]. In summary, the current research on the improvement of the physical and mechanical properties of related materials by different types of nanoadditives has obtained certain research results [24]. The incorporation of nanoadditives is mainly to improve the physical and mechanical properties of the materials, thereby increasing the range of materials used; however, about incorporating suitable nanoadditives, to improve the physical and mechanical properties of silty mudstone similar materials, studies on the effects of different types of nanoadditives on the physical and mechanical properties of similar silty mudstone materials are rarely involved [25, 26].

In order to deeply analyze the effects of different types of nanoadditives on the physical and mechanical properties of similar silty mudstone materials, based on the existing research results of similar silty mudstone materials [27, 28] on the basis of research results, using common NTi and NAl and Nbe additive for silty mudstone similar to the analysis of the physical and mechanical properties of related materials, and reveal its microcosmic mechanism, the following are carried out. Firstly, the scheme of mixing ratio of similar materials with different dosage of nanoadditives was designed. The effects of nanometer additives on the density, natural water absorption, uniaxial compressive strength, tensile strength, softening coefficient, and expansibility of similar materials were analyzed, and the effects of different nanometer additives on similar materials were analyzed. Finally, the influence mechanism of nanoadditives on the microstructure of silty mudstone was revealed by SEM. It provides some guidance for the application of nanometer additives in similar materials.

2. Test Content

2.1. Sample Preparation

2.1.1. Raw Materials

Similar to the materials of silty mudstone, barite powder is used as aggregate and gypsum is used as cementing material. Among them, the barite powder is produced by Hebei Lingshou, and its particle size is between 2 and 32 μm. And the chemical composition is shown in Table 1. The cementing material uses ultrahigh-strength gypsum with a particle size between 100 and 600 μm, and its chemical composition is shown in Table 2. The experiment used tap water for the laboratory.

Table 1: The chemical composition of barite powder (mass fraction) (%).

BaSO₄
SiO₂
Fe₂O₃
Al₂O₃
Water soluble salt
Other

98.00
0.40
0.05
0.01
0.20
<1%

Table 2: The chemical composition of ultrahigh-strength gypsum (mass fraction) (%).

SO₃
CaO
SiO₂
Al₂O₃
Na₂O

53.10
40.00
0.17
0.05
0.04

K₂O
SrO
Fe₂O₃
MgO
Other

0.04
0.04
0.03
0.02
<1%

2.1.2. Nanometer Additive Material

The additives mainly include NTi, NAl, and NBe. NTi is a kind of white loose powder material with hydrophilicity, good dispersion, and weather resistance. The particle diameter is between 25 ± 5 nm, the relative molecular weight is 79.9, the appearance is white, the specific surface area is 80∼85 m²/g, and the purity is greater than 99.9%. NAl is a new type of ultrafine white crystal powder material with a particle size between 30 and 60 nm, a relative molecular weight of 101.96 nm, an average particle size of 50 nm, a specific surface area of 5∼10 m²/g, and a purity greater than 99.99%. The particle size of the nanobentonite is between 40∼80 nm, with an average particle size of 60 nm. It is a white and light yellow powder with a good ability to bind water. The main composition of the NBe is more than 90% montmorillonite and a small amount of illite, kaolinite, and other minerals.

2.1.3. Preparation of Similar Materials

In order to study the physical and mechanical effects of nanomaterial additives (including NTi, NAl, and NBe) on the physical and mechanical effects of similar of silty mudstone, the dosage of different types of nanometer additives was set as 0 (control group), 2%, 4%, 6%, and 8% in the sample preparation process, respectively. The mixing scheme of similar materials is shown in Table 3.

Table 3: The mixture ratio of similar materials with different dosages of nanoadditives. Note. Quality of Barite powder + Quality of Gypsum = 400g.

Level
Raw material content

Water/(g)
Barite powder/(%)
Gypsum/(%)
Nanometer additive/(g)

NA0
20
36
64
0

NA1
20
36
64
2

NA2
20
36
64
4

NA3
20
36
64
6

NA4
20
36
64
8

2.2. Test Plan

In the process of testing the physical and mechanical properties of similar materials with different nanometer additives, the density, natural water absorption rate, uniaxial compressive strength, tensile strength, softening coefficient, and expansibility of the samples were mainly measured. The specific test plan is shown in Table 4 below. In order to analyze the influence mechanism of nanometer additives on the physical and mechanical properties of similar materials, uniaxial compression tests were carried out on the samples with different dosage of nanometer additives, and SEM tests were carried out on the typical damaged samples. Each group of samples is cured to a specified age in a standard curing box and tested according to the test regulations recommended by the international society for rock mechanics (IRSM) [29]. There are 5 parallel samples in each group, and the average values of the 3 samples closest to each other are taken as the experimental results. Due to the large number of samples and batch production, only parts of the finished samples are shown (Figure 1).

Table 4: Test schemes.

Test plan
Expansibility test
Splitting test
Density test
Natural water absorption test
Uniaxial compression test
Softening coefficient test

Test unit number
NTi
A1-1～1–5
A2-1～2–5
A3-1～3–5
A4-1～4–5
A5/6–1～5/6–5

NAl
B1-1～1–5
B2-1～2–5
B3-1～3–5
B4-1～4–5
B5/6–1～5/6–5

NBe
C1-1～1–5
C2-1～2–5
C3-1～3–5
C4-1～4–5
C5/6–1～5/6–5

Sample setting within the group
Each group of five diameters of 50 mm and heights of 50 mm sample
Each group of five diameters of 50 mm and heights of 100 mm sample

Initial state
The standard specimen after curing has reached the age

Dry (h)
——
——
——
——
——
48
——

Flooding (h)
48
——
——
48
——
——
48

Test content
Inflation rate
Tensile strength
First measure the density, then measure the natural water absorption
SEM test is carried out on damaged samples
(Saturated) Uniaxial compressive strength

Figure 1: Standard samples of similar materials with different contents of nanometer.

2.3. Test Equipment

According to the test scheme in Table 4, different groups of the standard age samples with different types and dosage of nanoadditives were tested. During the immersion process, the temperature is controlled at 25 ± 5°C by using a three-use water tank (as shown in Figure 2(a)). After immersing the sample for 48 h, it is fully saturated. The device can better control the immersion time and water pressure; during the drying process in the experiment, place the cured standard test in an electric thermostatic drying oven at 60 ± 5°C (as shown in Figure 2(b)) for 48h, then move it to a glass dryer to cool for 48h (as shown in Figure 2(c)). The uniaxial compression test in this paper adopts the MTS-810 electrohydraulic servo system testing machine in the highway engineering experimental center of Changsha University of Science and Technology (as shown in Figure 2(d)) to load the sample. According to the engineering rock mass test method standard, the loading speed of 0.8 MPa/s is set to apply axial pressure to the sample.

(a)

(b)

(c)

(d)

Figure 2: Test equipment: (a) three tanks; (b) electric constant temperature drying oven; (c) glass dryer; (d) MTS-810 electrohydraulic servo system testing machine.

3. Similar Material Optimization Experiment

3.1. Effects of Different Nanoadditives on Physical Properties of Similar Materials

Test the density of similar material samples with different nanoadditive dosages. The test results are shown in Figure 3. (1) With the addition of three nanoadditives in the same amount, compared with the control group, the effects of NAl on the density of similar materials are the most significant, followed by MBe and the minimum is NTi. (2) When the dosage of different nanoadditives increases from 0% to 6%, the density of similar materials increases with the continuous increase of the dosage of nanoadditives. (3) When the dosage is between 6% and 8%, similar materials are gradually increasing trend in density tends to 0. When incorporated into 8%, compared with the control group, NTi, NAl, and NBe, respectively, from 2.01 g/cm³ it increased to 2.16 g/cm³, 2.30 g/cm³, and 2.26 g/cm³. When 6% NBe is added, the density of similar materials is closest to the average density of silty original rocks [30]. It shows that all the three kinds of nanoadditives can effectively fill the pores between barite powder and gypsum particles so that the structure of similar material samples is more compact, and nanoadditives fully fill the pores of similar material samples, increasing the density.

Figure 3: Effects of nanoscale additives on density parameters of similar materials.

3.2. Effect of Different Nanoadditives on Natural Water Absorption of Similar Materials

The natural water absorption rate reflects the water absorption capacity of dry similar material samples, which can effectively reflect the development degree of the material’s microcracks. According to the test requirements of “Road Engineering Rock Test Regulations” (JTG E41-2005) [26], the free water absorption method was used to determine the water absorption of similar materials with different types of nanoadditives. The test results are shown in Figure 3.

From the effect of different nanoadditive dosages on the natural water absorption of similar materials, as shown in Figure 4 (1) as the nanoadditive dosage increases, the natural water content of samples of similar materials tends to decrease first and then increase; (2) when the dosage is 4%, the natural water absorption of the similar material sample doped with NTi reaches the minimum, followed by NAl, and the maximum is NBe, which is reduced by 0.23%, 0.12%, and 0.08% compared with the control group; (3) when the doping amount is 8%, the natural water absorption of similar material samples doped with NTi, NAl, and NBe increases from 6.16% to 5.93%, 6.04%, and 6.15% respectively. However, when the doping amount is 6%, the natural water absorption rate of similar material samples is close to the average value of silty raw rocks. It shows that the incorporation of nanoadditives can effectively fill the pores of samples of similar materials and reduce the natural water absorption rate of samples. However, with the increase of nanoadditives, excess nanoadditive materials increase the natural water absorption rate of samples.

Figure 4: Effects of nanoadditives on natural water absorption parameters of similar materials.

3.3. Effect of Different Nanoadditives on Expansion Rate of Similar Materials

The specific changes of the expansion rate of similar materials under different nanoadditive dosages are shown in Figure 4. It can be seen from Figure 5 that (1) the expansion rate of samples of similar materials is increasing with the increase of three nanoadditives, in which the addition of NBe has the greatest influence on the expansion rate of the sample, followed by the effect of NAl, and the effect of NTi is the least; (2) compared with the control group, when 8% NTi, NAl, and NBe are added, the expansion rates of similar material samples increase by 0.028%, 0.035%, and 0.078% in sequence; (3) the expansion rate of silty primary rock is about 0.16%, while the similar material after incorporation of 6% NBe is 0.16% close to the original rock. It shows that the incorporation of nano-NBe has the most significant effect on increasing the water absorption expansion rate of similar materials mainly because the NBe itself has strong water absorption expansion characteristics.

Figure 5: Effects of nanometer additives on expansion rate parameters of similar materials.

3.4. Effect of Different Nanoadditives on Mechanical Properties of Similar Materials

3.4.1. Effect of Different Nanoadditives on the Uniaxial Compressive Strength of Similar Materials

The MTS-810 electrohydraulic servo system test machine was used to perform uniaxial compressive test on similar materials with different amounts of nanoadditives. Then, select the typical stress-strain curve, the average peak stress, and the typical sample failure form from each group for analysis.

It can be seen from Figures 6(a)–6(c) the curves under the three nanoadditives. Under the condition of incorporation of nanoadditives, the stress-strain curves of all the samples are roughly similar, and all of them undergo the compaction stage, in the elastic stage, plastic deformation stage, and strain softening stage, and when the dosage is 4%, the uniaxial stress of the sample is the largest. When the same nanoadditive is incorporated, for example, when NTi is incorporated into 0%, 2%, 4%, 6%, and 8%, the peak corresponding strains are 1.13%, 1.76%, 1.33%, 1.81%, and 1.31%, respectively. The maximum peak stress is 4.93 MPa, 6.14 MPa, 9.50 MPa, 9.70 MPa, and 6.80 MPa. Compared with the control group, no matter which kind of nanoadditive is added in an appropriate amount, it can improve the uniaxial compressive strength of similar materials to a certain extent.

(a)

(b)

(c)

(d)

Figure 6: The effects of different nanoadditives on the stress of similar material samples.

It can be seen from Figure 6(d) that, under the condition of doping the same nanoadditives, with the increase of the amount of nanoadditives, the uniaxial compressive strength of similar materials showed a trend of first increasing and then decreasing. When it is 4%, the average value of uniaxial compressive strength of similar materials reaches the maximum. It shows that the proper addition of nanoadditives has obvious improvement effect on the uniaxial compressive strength of similar materials, but not as much as possible. There is an optimal dosage of about 4%. The maximum values of NTi, NAl, and NBe are, respectively, 9.70 MPa, 10.58 MPa, and 9.43 MPa.

According to the above stress-strain curve of the sample and the test after the sample is mixed with different nanoadditives, combined with the failure morphology of multiple sets of nanoadditives during the test, it is found that the damage morphology of the sample is mainly affected by nanoadditives which vary considerably and affect the dosage, and the different types of nanoadditives incorporated shape of specimen destruction of substantially identical, and the sample was mostly dominated shear failure. Taking into account the limited space, the following will take NBe as the analysis object; typical damage photos are shown in Figure 7. According to the failure morphology and stress-strain curve of similar material samples after uniaxial compression failure under different NBe contents, as the NBe content increases, the sample cracks crack from the stressed end of the sample and continue to extend to the bottom. The more obvious the sudden stress drop when the specimen fails, the more obvious the shear failure characteristics. When the dosage is 6%, the destruction characteristics of similar materials in Figure 7(e) are basically the same as those in Figure 7(a).

(a)

(b)

(c)

(d)

(e)

(f)

Figure 7: Shear failure patterns of similar material samples with different NBe contents (water content are controlled at 10% to 12%).

3.4.2. Effects of Different Nanoadditives on the Tensile Strength of Similar Materials

Figure 8 shows the effect of different nanoadditives on the tensile strength of similar materials. It can be seen from Figure 7 that, as the amount of nanoadditives increases, the tensile strength of similar materials increases first and then decreases. When the amount of nanoadditives is 4%, the tensile strength of similar materials reaches the maximum, and NTi, NAl, and NBe are added the maximum value, respectively, is 2.14 MPa, 2.31 MPa, and 2.41 MPa. Later, as the amount of nanoadditives continued to increase, the tensile strength of similar materials decreased significantly. It shows that the incorporation of nanoadditives has a very significant effect on the tensile strength of similar materials; when 6% NBe is incorporated, the tensile strength of similar materials is taken to the average of silty raw rocks.

Figure 8: Effects of nanoadditives on uniaxial compressive strength of similar materials.

3.4.3. Effects of Different Nanoadditives on the Softening Coefficient of Similar Materials

Figure 9 shows the effect of blending different nanoadditives on the softening coefficient of similar materials. It can be seen from Figure 8 that the incorporation of different nanoadditives reduces the softening coefficient of similar materials. As the amount of nanoadditives increases, the softening coefficient of similar materials continues to decline, but the decline becomes slow. In the process of increasing the additive content from 0% to 4%, the softening coefficient of similar materials is significantly affected; from 4% to 8%, the softening coefficient gradually stabilizes, and finally the softening coefficient of similar materials after NTi, NAl, and NBe decreased by from 0.70 to 0.51, 0.52, and 0.54; when incorporated NBe is 6%, softening coefficient similar material is closest to the average value of the original rock silty.

Figure 9: Effect of nanoadditives on softening coefficient of similar materials.

In summary, the test results of the density, natural water absorption rate, swelling rate, uniaxial compressive strength, tensile strength, and softening coefficient of similar materials after mixing different nanoadditives can be seen; with the addition of nanoadditives, silt physical and mechanical properties of mudstone similar materials change significantly. When doped with 4% nanoadditives, it can effectively improve the related physical and mechanical properties of similar materials. However, when the dosage is 6%, especially after blending with NBe, all physical and mechanical parameters of similar material samples can reach or be closer to the silty raw rock except uniaxial compressive strength. The failure form of the axial compression specimen is also consistent with that of the original rock and can be used as the best choice. When the 8% nanometer is added immediately, the physical and mechanical properties of the silty mudstone similar materials will change obviously, and it is quite different from the parameters of the silty raw rock.

4. Microstructure and Analysis of Similar Material Samples

The nanometer additive added has high surface energy, and the high surface energy effect of nanometer additive in similar materials can be brought into play when added in an appropriate amount. The nanoparticle materials can play the following three effects [31–35]: (1) Size effect: selected raw materials of various particle sizes are above 2 μm, while additive nanometer average particle size of additive is between 10 and 100 nm. Because of the smaller geometric size of nanosized particles, they have stronger adsorption. Adding proper amount of nanometer material into the mixture showed better dispersion. Because the size of nanoparticles is small and the specific surface area is larger, when mixing too much, the particles will adsorb each other and tend to aggregate. (2) Filling effect: the appropriate amount of nanoadditives can optimize the particle gradation of the mixed material, and the nanoparticles have the function of filling the pores, displacing the water in the voids of samples of similar materials, reducing the porosity, and making the maximum pore size and average of the similar materials. The pore size is significantly reduced, improving the internal pore structure of similar materials, resulting in more uniform and dense similar materials. (3) Surface effect: it can be seen from the hydration of gypsum that the barite powder particles in similar materials are wrapped by the gypsum hydration product. The nanoadditive particles are extremely fine and the specific surface area is extremely large, which increases the contact surface with water. The surface of the nanoadditive has high activity and can adsorb a large amount of fine particles, which promotes the hydration reaction of gypsum. As shown in Figure 10, the microscopic structure of similar materials is now observed under 300 times electron microscopy at 0%, 2%, 4%, and 8% of NBe, and the microstructure of similar materials is revealed when nanoadditives are added an influence mechanism.

(a)

(b)

(c)

(d)

(e)

Figure 10: SEM photos of similar material samples with different NBe contents: (a) the structure is loose and contains many holes; (b) the structure gradually compacted and a large number of holes became smaller; (c) the surface is denser and the structure contains more pores; (d) the interface of the structure is smooth and dense with only a few holes; (e) the structure interface is agglomerated and there are many holes (×300 times).

According to Figure 10, it can be seen that, under the scanning electron microscope at 300 times, the mesostructure structure of similar materials is in silty mudstone under different NBe dosages. As shown in Figure 10(a), when it is 0%, a network structure is formed inside the similar material, and the mesostructure is loose, containing a large number of holes and cracks. From Figure 10(b), when the NBe content is 2%, the internal network structure of similar materials is gradually dense, and the pores of the mesostructure are filled in a large amount, but there are still a lot of pores and cracks. From Figure 10(c), a similar material doped with 4% NBe has the best effect of improving the structure interface and the structure is more dense. The gap between the barite powder and the gypsum hydration product can hardly be seen in the interface transition area. According to Figure 10(d), when the content of NBe is 6%, the structure interface has the best improvement effect, and the structure is more uniform and dense, and the interface transition area is even and smooth, with only a few holes. It shows that the appropriate amount of nanoadditives can promote the hydration reaction of internal gypsum and interweave with the hydration products, thereby forming a dense whole, making the mesostructure of similar materials more uniform and dense. As shown in Figure 10(e), 8% NBe similar material is blended. Because a large amount of nanoparticles will agglomerate, in similar materials, gypsum hydration products will wrap the barite powder particles and nanoagglomerates, and the internal structure will generate a large number of uneven pores. Destroying the dense structure inside similar materials leads to the deterioration of the mechanical properties of similar materials and the decrease of the softening coefficient.

The above analysis revealed the influence mechanism of nanoadditive dosage on the microstructure of similar materials, and the following conclusions were drawn: (1) in the control group, only gypsum and water hydration reaction occurred, and a large number of gypsum crystals were generated and interlaced into a network structure. After cementation, there was a certain strength, and the cementation product would have a large number of pores. The mixture of gypsum and barite powder was even. After hydration reaction of gypsum, the barite powder particles were wrapped by cementation, which could improve the compactness, but there would still be a large number of pores and the sample density was small. In this process, the macroscopic mechanical properties of similar materials are mainly affected by cementation. (2) When 2%∼6% content is added, on the one hand, nanoparticles can promote the hydration reaction of gypsum and accelerate the production of cement. On the other hand, the right amount of nanoparticles can fully disperse and fill the pores in similar materials, reduce the water in the pores, and make the materials more dense, and the sample density gradually increases. The macroscopic mechanical strength of similar materials corresponding to this process is further improved. (3) When 6%∼8% nanoadditive is added, the nanoparticle agglomeration occurs. The strength of the sample after the nanoadditive agglomeration decreases, and it becomes a primary defect in the similar materials after cementation. Besides, there is a large gap between the nanoadditive particles and the surrounding hydration products, with a poor interface. In this process, the macromechanics of similar material samples weakened to some extent, but too many nanoadditives can still further improve the density, expansion rate, and natural water absorption of similar material samples.

5. Conclusions

(1)Compared with the control group, with the addition of nanoadditives, the physical and mechanical properties of similar materials of silty mudstone changed significantly. When 4% nanoadditive is added, the physical and mechanical properties of similar materials can be improved effectively. When 8% nanoadditive is added, the mechanical properties of silty mudstone similar materials deteriorate obviously. This is because adding nanometer additive can effectively promote the hydration reaction of gypsum, accelerate the production of cement, fill the pores of similar materials, reduce internal defects, and make similar materials more compact. When too much is added, the nanoadditive will aggregate and degrade, which will reduce the mechanical properties of similar materials.(2)When the content of NBe is 6%, all the physical and mechanical parameters of similar materials, except the uniaxial compressive strength, can reach or be closer to the silty original rock, and the failure morphology of uniaxial compression samples is consistent with that of the original rock, which can be used as the best choice. Therefore, appropriate incorporation of NBe can effectively improve the similarity between similar materials and silty rock.

Data Availability

The data used to support the findings of this study are available from the corresponding author upon request.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

This study was undertaken with funding from the National Natural Science Foundation of China (Grant nos. 51838001 and 51908069).

References

C. Wen, S. Jia, X. Fu, L. Meng, and Z. Zhao, “Experimental research and sensitivity analysis of mudstone similar materials based on orthogonal design,” Advances in Materials Science and Engineering, vol. 2020, Article ID 2031276, 14 pages, 2020.

X. Yang, D. L. Su, B. Zhou et al., “Experiment study on similarity ratio of similar material for model test on red-bed soft rock,” Rock and Soil Mechanics, vol. 37, no. 8, pp. 2231–2237, 2016.

Y. P. Yang, Y. D. Tang, B. Wang et al., “Impact of size on environmental behavior of metal oxide nanoparticles,” Environmental Science, vol. 39, pp. 2982–2990, 2018.

W. Jones, A. G. F. Gibb, C. I. Goodier et al., “Nanomaterials in construction-what is being used, and where?” Construction Materials, vol. 172, pp. 49–62, 2016.

B. Han, L. Zhang, S. Zeng et al., “Nano-core effect in nano-engineered cementitious composites,” Composites Part A: Applied Science and Manufacturing, vol. 95, pp. 100–109, 2017.

B. C. Chen, T. Ji, Q. W. Huang et al., “Review of research on ultrahigh performance concrete,” Archives of Civil and Mechanical Engineering, vol. 31, pp. 10–24, 2014.

Y. Ruan, B. Han, X. Yu et al., “Mechanical behaviors of nano-zirconia reinforced reactive powder concrete under compression and flexure,” Construction and Building Materials, vol. 162, pp. 663–673, 2018.

S. Jiang, D. Zhou, L. Zhang et al., “Comparison of compressive strength and electrical resistivity of cementitious composites with different nano- and micro-fillers,” Archives of Civil and Mechanical Engineering, vol. 18, no. 1, pp. 60–68, 2018.

L. Zeng, L. Xiao, J. Zhang, and H. Fu, “The role of nanotechnology in subgrade and pavement engineering: a review,” Journal of Nanoscience and Nanotechnology, vol. 20, no. 8, pp. 4607–4618, 2020.

L. Zeng, X. Yao, Q.-F. Gao, H. Bian, and D. Fan, “Use of nanosilica and cement in improving the mechanical behavior of disintegrated carbonaceous mudstone,” Journal of Nanoscience and Nanotechnology, vol. 20, no. 8, pp. 4807–4814, 2020.

X. Qiu, H. Jiang, and G. Zhang, “Modification effects of nano-CaCO3 on engineering performance of cement grouts,” Journal of Nanoscience and Nanotechnology, vol. 20, no. 8, pp. 5043–5048, 2020.

L. Zeng, J. Ye, J. Zhang, J. Liu, and C. Jia, “A promising SPEEK/MCM composite membrane for highly efficient vanadium redox flow battery,” Surface and Coatings Technology, vol. 358, pp. 167–172, 2019.

J. Mostafa, F. Mojtaba, and F. Mohammad, “Effects of fly ash and TiO₂ nanoparticles on rheological, mechanical, microstructural and thermal properties of high strength self-compacting concrete,” Mechanics of Materials, vol. 61, pp. 12–26, 2013.

M.-h. Zhang and H. Li, “Pore structure and chloride permeability of concrete containing nano-particles for pavement,” Construction and Building Materials, vol. 25, no. 2, pp. 608–616, 2011.

C. Wang, C. Zhang, J. C. Liu et al., “Influence of nano-CaCO₃ on hydration characteristic of Portland cement,” Bulletin of the Chinese Ceramic Society, vol. 35, pp. 824–830, 2016.

S. Lv, C. Xia, H. Liu et al., “Strength and fatigue performance for cement-treated aggregate base materials,” International Journal of Pavement Engineering, pp. 1–10, 2019.

M. T. Maagi, S. D. Lupyana, and J. Gu, “Effect of nano-SiO₂, nano-TiO₂ and nano-Al₂O₃ addition on fluid loss in oil-well cement slurry,” International Journal of Concrete Structures and Materials, vol. 13, p. 62, 2019.

C. C. Liu, S. T. Lv, X. H. Peng et al., “Analysis and comparison of different impacts of aging and loading frequency on fatigue characterization of asphalt concrete,” Journal of Materials in Civil Engineering, vol. 32, 2020.

J. Zhang, L. Ding, F. Li, and J. Peng, “Recycled aggregates from construction and demolition wastes as alternative filling materials for highway subgrades in China,” Journal of Cleaner Production, vol. 255, p. 120223, 2020.

J. Zhang, F. Gu, and Y. Zhang, “Use of building-related construction and demolition wastes in highway embankment: laboratory and field evaluations,” Journal of Cleaner Production, vol. 230, pp. 1051–1060, 2019.

T. Anuj and S. Tarun, “A review study on strength properties of different soils treated with different materials including nanomaterials,” International Journal of Management Technology and Engineering, vol. 9, pp. 1769–1774, 2019.

K. Nihat and M. Nausad, “A comparative study on the physical and mechanical properties of alkali activated materials,” Sigma Journal of Engineering and Natural Sciences Sigma Mühendislik Ve Fen Bilimleri Dergisi, vol. 38, no. 2, pp. 649–658, 2020.

J. Qian, Y. Yao, J. Li, H. Xiao, and S. Luo, “Resilient properties of soil-rock mixture materials: preliminary investigation of the effect of composition and structure,” Materials, vol. 13, no. 7, p. 1658, 2020.

G. Y. Li, P. M. Wang, and X. Zhao, “Mechanical behavior and microstructure of cement composites incorporating surface-treated multi-walled carbon nanotubes,” Carbon, vol. 43, no. 6, pp. 1239–1245, 2005.

T. Nochaiya and A. Chaipanich, “Behavior of multi-walled carbon nanotubes on the porosity and microstructure of cement-based materials,” Applied Surface Science, vol. 257, no. 6, pp. 1941–1945, 2011.

B. Zou, S. J. Chen, A. H. Korayem, F. Collins, C. M. Wang, and W. H. Duan, “Effect of ultrasonication energy on engineering properties of carbon nanotube reinforced cement pastes,” Carbon, vol. 85, pp. 212–220, 2015.

E. Mohseni, M. M. Ranjbar, M. A. Yazdi, S. S. Hosseiny, and E. Roshandel, “The effects of silicon dioxide, iron (III) oxide and copper oxide nanomaterials on the properties of self-compacting mortar containing fly ash,” Magazine of Concrete Research, vol. 67, no. 20, pp. 1112–1124, 2015.

C.-l. Dong, G.-m. Zhao, X.-y. Lu, X.-r. Meng, Y.-m. Li, and X. Cheng, “Similar simulation device for unloading effect of deep roadway excavation and its application,” Journal of Mountain Science, vol. 15, no. 5, pp. 1115–1128, 2018.

E. Hoek, D. Wood, and S. Shah, “A modified Hoek-Brown failure criterion for jointed rock masses,” in Proceedings of the Rock Characterization, Symposium Of ISRM, pp. 209–214, Thomas Telford Publishing, London, UK, September 1992.

J. C. Chen, Study on Seepage, Mechanical Properties and Fracture Evolution of Silty Mudstone under Hygrothermal Action, Changsha University of Science & Technology, Changsha, China, 2019, Ph.D. thesis.

A. Nazari and S. Riahi, “Improvement compressive strength of concrete in different curing media by Al2O3 nanoparticles,” Materials Science and Engineering: A, vol. 528, no. 3, pp. 1183–1191, 2011.

J. Camiletti, A. M. Soliman, and M. L. Nehdi, “Effect of nano-calcium carbonate on early-age properties of ultra-high-performance concrete,” Magazine of Concrete Research, vol. 65, no. 5, pp. 297–307, 2013.

S. Lv, S. Wang, C. Liu, J. Zheng et al., “Synchronous testing method for tension and compression moduli of asphalt mixture under dynamic and static loading states,” Journal of Materials in Civil Engineering, vol. 211, pp. 1085–1093, 2018.

I. Mansouri, M. Nejat, S. Shahbazi et al., “Effect of magnetite nanoparticles (ferroferric oxide) on discrete concrete properties,” Proceedings of the Institution of Civil Engineers–Construction Materials, vol. 172, pp. 95–102, 2018.

G. Prakasam, A. R. Murthy, and M. Saffiq Reheman, “Mechanical, durability and fracture properties of nano-modified FA/GGBS geopolymer mortar,” Magazine of Concrete Research, vol. 72, no. 4, pp. 207–216, 2020.