Optimization ofMixProportions forNovelDry Stack Interlocking Concrete Blocks Using ANN

)is paper proposes novel concrete interlocking blocks made of fly ash and GGBS which are an alternative for the conventional concrete blocks. )e artificial neural network (ANN) technique is used to estimate the mechanical strength of interlocking blocks and is verified with experimental investigation.)e ANNmodel is based on the Levenberg–Marquardt principle which is executed using MATLAB. )e inputs are given in the percentage ratio of cement: fly ash: crushed stone aggregate (FA): coarse aggregate (CA) for the process of learning, testing, and validation. )e selected model is subjected to several trials in terms of mean square error, containing 4 input, 2 sets of 10 hidden layers, and one output components. In this study, a total of 2600 blocks of different mixes were tested as per IS 2185-1 (2005) to assess 3, 7, 14, 21, and 28 days’ strength. )e experimental investigations were carried out in two phases. In the first phase, experimental investigations to identify the optimummix proportions of cement, aggregate, fly ash, and ground granulated blast furnace slag to achieve desired compressive strength was carried out. In the second phase, the identified mix proportions were analysed using ANN to predict the compressive strength of interlocking blocks. )e results indicate that the proposed ANN model developed to determine the mechanical strength and cost of interlocking blocks has excellent prediction ability.


Introduction
In the current scenario, the construction industry utilises the natural resources which is a threat for the environment. Compared to RCC framed construction, masonry construction is less expensive and faster [1]. To overcome the defects in the masonry system, the mortarless interlocking block system has emerged [2].
e key feature of the interlocking blocks is its curved grooves and protrusions that help to retain the blocks together so the mortar at each layer can be eliminated, thus saving materials, time, and manpower. Jaafar et al. [3] observed that the interlocking masonry has strength higher than conventional masonry in axial compression tests. In the system of interlocking blocks, the issue of shrinkage and continuous breaking of blocks does not happen. Few researchers discovered that interlocking blocks perform well in seismic regions [4,5]. Anand and Ramamurthy [6] discovered that when the interlocking block system is subjected to in-plane shear load, the interlocking blocks shift slightly, improving the energy dissipation under seismic loads. e seismic test on an unreinforced masonry block by Giamundo et al. [7] demonstrates that the interfaces between mortar and block are the weakest part of the wall, where cracks open and close. Due to physical and mechanical debasement of the mortar layer, numerous historical and old constructions built with mortar and blocks show a higher loss in structural performance. is issue can be avoided when interlocking bricks are employed, due to the elimination of the mortar layer. Ayed et al. [8] examined the contact behaviour of interlocking blocks and found that the interlocking joint behaviour is higher for the block having a rough surface rather than a smooth surface. is emphasizes the importance of surface texture of interlocking blocks.
ANN is a numerical model that reproduces the neural system of the central sensory system. An ANN comprises of large numbers of interconnected neurons, and it decodes data utilizing the dynamic state approach for the output [9,10]. ANN modelling is an advancement to the statistical regression approach. Every layer of neurons has an input or output of the previous neuron. e ANN system of operation is shown in Figure 1. Every input value X is multiplied by weight (W), and then, it is allotted a bias for the output: where W i is the weight, X i is the input, and b is the bias. e advanced feature of ANN is its capability of gaining knowledge directly from models and providing an excellent reaction to deficient undertakings. e ANN model utilized in this research provides the mix proportions for an optimized interlocking block at minimum cost.

Research Significance and Novelty of Proposed Interlocking
Blocks.
e mix proportions and the mechanical strength of vibro compacted interlocking blocks have received less attention. As a result, tests on mix proportions with varying mix ratios have been conducted for the vibro compacted interlocking blocks. Furthermore, the effects of fly ash and GGBS are examined, along with their influence on the failure mechanisms. e concrete mix used to make vibro compacted interlocking blocks is not the same as the regular concrete mix. e vibro compacted load-bearing interlocking concrete blocks are manufactured using the dry mix with precise optimum water content, as shown in Figure 2. e interlocking blocks are manufactured by feeding the mixture through a hydraulic vibro compression press machine, which produces a high level of vibration and compression from the top, resulting in a compacted, high-strength block. It is difficult or impossible to manufacture blocks if the moisture content is excessive, as the block deforms during the removal of the mould from the vibro compaction machine. e percentage of fine and coarse aggregate plays a vital role in strength and texture of the blocks. If the percentage of coarse aggregate increases, the strength of the blocks will be higher but the texture of the blocks becomes porous, which leads to seepage of water inside the blocks, and it increases the cost of plastering. However, if the percentage of fine aggregate increases, the strength of the blocks reduces.

Sum function
Log-activation function is study also highlights the effective replacement of river sand with crushed stone aggregate. Compared to natural river sand, the crushed stone aggregate has a higher fineness modulus index which provides good workability for the blocks [11]. Crushed stone aggregate is free from sediment and clay particles which gives better abrasion resistance, higher unit weight, and lower permeability. Cost of interlocking blocks is highly influenced by cement content. To minimise the cost, supplementary cementations materials such as fly ash and GGBS are incorporated. Higher                   Advances in Civil Engineering quantity of fly ash retards the strength and setting time of blocks. Bheel et al. [12] carried out mechanical examination on fly ash, and the results indicated that fly ash improves the microstructure in concrete as the breaking of fly ash plerospheres changes the behaviour of mortar. Zhou et al. [13] found that the replacement of fly ash and GGBS results in delay in setting time of concrete, but the replacement of fly ash and GGBS improves the workability of concrete [14]. is interlocking block will be a suitable replacement for the conventional concrete masonry blocks. Inclusion of fly ash in the concrete makes interlocking blocks greener by lowering CO 2 emissions. ese blocks can be assembled ten times faster by unskilled employees when compared with regular masonry construction and are easier to install as it does not require mortar. ese are self-aligning and interlock both horizontally and vertically ensuring proper alignment. is proposed block provides 50% horizontal interlocking connectivity over each block, resulting in a higher shear capacity than standard interlocking blocks, as illustrated in Figure 3. ese blocks are more resistant to earthquakes due to the elimination of mortar for binding. ese interconnecting blocks can be easily dismantled and reused. e research findings include a list of various mix proportions and the mechanical strength of the blocks at various ages. e main objective of this study is to investigate and predict the performance of interlocking blocks with various dosages of fly ash, cement, and crushed stone aggregate. is study also highlights the effective replacement of cement with pozzolanic materials such as fly ash and GGBS. is research work addresses the optimum and costeffective proportions for the manufacture of interlocking blocks which can be used for affordable housing. ese research data will be useful for researchers and entrepreneurs who are interested in manufacturing vibro compacted hollow concrete blocks for affordable housing.  Advances in Civil Engineering

Artificial Neural Network
e most commonly used artificial neural network utilized in the regression analysis is feedforward backpropagation. As demonstrated in Figure 4, for this research, four input and two layers of ten hidden node layers between input and one output are used. e input layer nodes do not perform any process, but it collects information from outside. Each artificial neuron present in the hidden layer or the outer layer collects a large number of weighted inputs, sends it to bias for summing and imposing an activation function, and then it transfers the data to output [15,16].
In the ANN feedforward propagation, the data flow is from the input layer to the output layer, where the prediction in ANN is accomplished from the provided input values and specific weights [9,17]. For the backpropagation, the weights are modified utilizing advanced training algorithms such as Levenberg-Marquardt (LM), scaled conjugate inclination, and Bayesian regularization to minimise the errors of predicted output values. is calculation is an augmentation of quasi-Newton strategy where there is no need to compute the Hessian framework to take care of nonlinear least squares issues. e weights and bias (wb n+1 ) can be determined utilizing the following equation [10]: where J represents the Jacobian matrix, which represents first derivative of network error regarding weights and bias, e represents the vector of the network, and µ and I indicate the real number factor and identity matrix.

Experimental Study
e experimental investigation involves assessing of material properties and determination of the engineering properties of the interlocking blocks. e material proportions are considered according to Frasson's method to achieve the desired density. e texture of the mixtures as well as optimum water Advances in Civil Engineering 9 content with cohesion is also evaluated by casting specimens in Frasson's equipment, as shown in Figure 5. For the experimentation, the choice of aggregate should pass through 9.5 mm sieve, it should be retained on 4.8 mm sieve, and the aggregate should be of cubical shape. e crushed stone aggregate must have a fineness of 2.20 to 2.80. Mix design methodology is based on moulding a 5 × 10 cm cylinder using a 5 × 13 cm tri-panel cylindrical mould, as shown in Figure 5(b). In addition to the cylindrical mould, the moulding equipment has a metallic base plate, which measures 7 cm in diameter and 2 cm height, and a compacting bar to compact the mortar. For moulding the specimens, first the materials need to be weighed to obtain the density of concrete after compacting. e materials should be placed in the tri-panel cylindrical mould and be divided in four equal parts in order to mould the specimen with four-layer filing. e first layer of the mix is filled in the cylinder, and it should receive 20 strokes with the compacting bar for proper compaction. e mould is again filled and compacted with 20 strokes, and this process is continued for 4 layers. e energy applied during the compaction needs to be distributed equally among each layer in such a way that the specimen height reaches 10.2 cm to 10.5 cm after 80 stokes of compaction. e final height of the specimen is achieved by applying additional strokes on a stopper with a rubber hammer. Finally, the mould is unscrewed for demoulding. e physical examination on the freshly prepared mould is an excellent predictor for the final surface texture of the blocks. e texture of the specimen needs to be assessed visually for each type of mix proportion at optimum water content and density.
To determine the optimum water content for a given mix proportion, we need to assess the surface texture of the specimens following its removal from the cylindrical mould. When the water content in the mix reaches its optimal value, the surface of the specimen will start to become slightly humid. Moreover, the internal surface of the moulds and metallic base used for supporting the mould also starts to become humid. If the moisture content of the mixture is below this point, more energy will be required to compact the materials which leads to loss in productivity and wear of the vibro compaction machine. If the water content  10 Advances in Civil Engineering increases, it is difficult or impossible to manufacture blocks due to block deformation during the time of removal of the mould from the vibro compaction machine. From the experimental results, it is seen that an optimum water content of 4% to its total weight is required.

Selection of Materials.
For casting of interlocking blocks, locally available raw materials such as fly ash, crushed stone aggregate, cement, and coarse aggregate were used. e properties of the materials such as cement, coarse aggregate, crushed stone aggregate, and fly ash are given in Tables 1-4.

Casting of Interlocking
Blocks. An elaborate experimental work is carried out by casting 2600 interlocking blocks. e interlocking blocks are cast by feeding the concrete mix into the moulds of the vibro compression machine which has a geometric size of 400 mm × 150 mm × 150 mm, as shown in Figures 6 and 7. e concrete mix is vibrated and compacted using a hydraulic press, and then, the blocks come out from the vibro compression machine. e density of the block ranges from 2380 to 2440 kg/m 3 .

Compressive Strength Test.
A universal testing machine of capacity 1000 kN is used for testing the compressive strength of interlocking blocks. e interlocking block specimens were placed with their key facing upward so that the load will be transferred in the vertical direction of the block. Blocks are placed between the jaws, and load is applied gradually at the rate of 4.6 kN/sec. Special steel plates were placed to a create horizontal platform for the interlocking blocks on the top to distribute the load uniformly, as shown in Figure 8.

Advances in Civil Engineering
As per IS 2185-1 (2005), the compressive strength of any individual specimen shall not fall below the minimum average compressive strength by more than 20%. e compressive strength results provided in this investigation represent the average compressive strength of eight samples tested for each curing age.

Results and Discussion
e results of the compressive strength test of 65 mix proportions are given in Table 5, and the summarized mix proportions are given in Table 6. In addition to compressive strength, surface texture is also an important parameter in the production of interlocking blocks as there is no need for plastering when the surface looks uniform and smooth. From the results, it is seen that higher proportions of crushed stone aggregate with respect to coarse aggregate result in a smooth surface texture, as shown in Figure 9, but the compressive strength of the blocks gets reduced. Increase in coarse aggregate results in higher compressive strength but the surface texture looks grainy, and it has lots of pores, as shown in Figure 10. From the tests conducted on specimens having fly ash as replacement, it is seen that mix proportions with 65% coarse aggregate and 25% crushed stone aggregate show the best smooth surface texture and higher compressive strength with optimal cost.

Influence of Fly Ash and GGBS on Interlocking Blocks.
According to Indian Standard IS 2185-1 (2005), the average compressive strength for load bearing blocks should be between 3.5 and 15 N/mm 2 . According to American Standard C90-14, the average compressive strength for loadbearing hollow blocks should be at least 13.8 N/mm 2 .
ere are several types of supplementary cementitious materials such as fly ash, GGBS, metakaolin, silica fumes, and rice husk. Among all the supplementary cementitious material, fly ash and GGBS have good pozzolanic nature and so they are utilized in this research for manufacturing of interlocking blocks. Fly ash increases the chemical resistance, durability, and workability of the concrete mix when mixed at an optimum percentage. Figure 11 shows the results of compressive strength and cost of interlocking blocks with varying percentages of cement, fly ash, crushed stone aggregate, and coarse aggregates. From the results, it is seen that the MPF2b mix gives the required compressive strength and surface texture with an optimum cost compared to the standard mix with cement satisfying the codal specifications. Fly ash reacts slowly at the initial stages which gives less compressive strength. At later ages, due to its reactions with alkali and lime in the concrete mix, an additional cementitious compound is produced which helps to gain strength over time.
It is observed that replacement of cement with GGBS results in faster strength gain than fly ash. e experimental results shown in Figure 9 reveal that the mix proportion MPGb has the compressive strength required for loadbearing blocks as specified in the code.
Overall, results showed that the use of alternative materials such as fly ash and GGBS in the given ratio does not affect the quality and strength of the specimen. Replacement of cement with GGBS and fly ash mix reduces the cost. Reduction in the cement content results in reduction in cost.
ese results can be used as guidelines for the manufacturing of interlocking blocks using cement, fly ash, and crushed stone aggregate with improved strength properties at optimum cost.

Artificial Neural Network
Results. In the present study, the MATLAB neural network tool is utilized for predicting the cost and compressive strength of interlocking blocks. e utilization of ANN in predicting the compressive strength of concrete provides a quick and easy method to determine the optimal mix proportion for a desired strength. e accuracy of ANN prediction generally relies upon the network architecture selected, so various number of trials with several hidden node numbers were tested before the final architecture model is chosen. e input for the ANN model is the proportion of cement, fly ash, GGBS, coarse aggregate, and crushed stone aggregate; the Advances in Civil Engineering 13 variations in proportions of the above materials will have a significant effect on the strength and cost of interlocking blocks. e output results are compressive strength and cost. Figures 12-17 show the regression plot for all the test data along with predicted values of compressive strength and cost. e algorithm is tested and validated. e overall regression value for 3, 7, 14, 21, and 28 days is above 0.98 indicating that the model fits best for predicting compressive strength at all ages. From the results, it is clear that the network is well trained as the predicted values of compressive strength for interlocking blocks are almost similar to the actual strength. So, this neural model can be used to find optimal mix proportions for the desired strength at optimum cost.

Cost Analysis
e dimension of the wall considered for cost analysis is given in Table 7. Interlocking blocks can reduce the construction cost of walls by more than 50%. Costing for blocks, labor, and material is given in Tables 8 and 9.

Conclusion
is research investigation provides a predictive model for determination of the optimum mix proportion for interlocking blocks using the artificial neural network algorithm. e ANN trained model using the Levenberg-Marquardt algorithm with 4 input 2 sets of 10 hidden layers exhibits good mechanical strength prediction on novel concrete interlocking blocks. Moreover, predicted ANN values are 98% accurate when compared to experimental results. In general, the proposed ANN model with cement, fly ash, GGBS, and fine and coarse aggregates as the architectural model has high capability and reliability in predicting the mechanical strength and cost of interlocking blocks. By adopting the ANN architecture model, there will be no need to develop and test large number of mix proportions for determining the mechanical strength. is developed ANN architecture simplifies the challenge of determining the interlocking blocks' mechanical strength and optimum cost for the mix proportion within the bounds of the ranges discussed in this study.
Based on the experimental investigation reported in this paper, following conclusions are drawn:

Advances in Civil Engineering
(1) e best combination of strength and surface texture of the interlocking blocks can be achieved using 65% coarse aggregate and 25% crushed stone aggregate with 4% cement and 6% fly ash. (2) If the percentage of cement is less than 4% to weight of fly ash, brittle failure occurs in the interlocking blocks. e percentage of cement by more than 4% shows fracture failure in the interlocking blocks. (3) Interlocking blocks with GGBS reaches early compressive strength when compared to blocks with fly ash. (4) e innovative geometric design of the interlocking block provides better strength and stability eliminating the need for mortar resulting in faster and economical construction. (5) is proposed interlocking block system is more than 50% cost efficient compared to the conventional masonry system since the construction is faster and less manpower is utilized. (6) e experimental values are close to the predicted values showing a strong statistical correlation between the input and output values, and so this neural model can be used to find the optimal mix proportions for the desired strength at an optimum cost rather than performing lots of experiments.

Data Availability
e data used to support the findings of this study are available from the corresponding author upon request.