Structural and Morphological Characterization of Micro and Nanofibers Produced by Electrospinning and Solution Blow Spinning: A Comparative Study

1 Departamento de Engenharia de Materiais (DEMA), Universidade Federal de São Carlos (UFSCAR), Rodovia Washington Luis, KM 235, Monjolinho, 13.565-905 São Carlos, SP, Brazil 2 Laboratório Nacional de Nanotecnologia para o Agronegócio (LNNA), Embrapa Instrumentação Agropecuária (CNPDIA), Rua XV de Novembro, 1452 Centro, 13.560-970 São Carlos, SP, Brazil 3 United States Department of Agriculture (USDA), Western Regional Research Center (WRRC), Bioproduct Chemistry and Engineering (BCE), 800 Buchanan Street, Albany, CA 94710, USA 4Universidade Federal da Paraı́ba (UFPB), Departamento de Engenharia de Materiais (DEMAT), Cidade Universitária, 58.051-900 João Pessoa, PB, Brazil


Introduction
Polymer fibers are used in a wide variety of applications ranging from scaffolding biomaterials, textiles, and sensors to composite reinforcement and filtration [1].Traditional methods used to obtain polymer fibers include melt spinning [2][3][4], solution spinning, and gel-state fiber forming [5].These methods can be used to produce fibers with diameters of a few nanometers; however, in most cases, fiber diameter lies in the micron scale [6].
Since the 1990s there has been an increasing interest in methods of fiber production such as electrospinning [7][8][9], which can consistently produce submicron and nanometric fibers from a variety of polymers, including PLA, PCL, and PEO [1,[10][11][12].The preparation of nanofibers from these polymers for tissue engineering applications was recently reported in the literature [13].
Recently, another method of fiber production, known as solution blow spinning (SBS), was developed that is conceptually similar to electrospinning without the voltage requirement and also retains elements of solution spinning.This method has been successfully used to produce microand nanofibers of polymers with diameters ranging from a few tenths of nanometers to several microns, depending on the experimental conditions used [14][15][16][17].This technique applies a novel pair of concentric nozzles in which a polymer solution is forced through the inner nozzle at an appropriate rate.The droplet formed at the tip of the inner nozzle is then stretched by a high-pressure stream of compressed gas flowing around the droplet through the outer nozzle (Scheme 1(a)).This causes the surface of the drop to distort into a conical shape (solution cone) somewhat similar to electrospinning (Scheme 1(b)).When a critical air pressure is exceeded, this solution jets from the apex of the cone towards its target.As these jets travel across the working distance, they are stretched by the pressure drop, while the solvent evaporates, leaving behind polymer fibers which can be collected, basically, on any target.By varying polymer architecture and processing conditions, polymer fibers can be spun with a large surface area for different potential applications such as membranes for biological and chemical sensors, drug delivery, filtration media, and tissue engineering [14,16,18].The goal of this work was to study, by solution blow spinning and electrospinning, different polymer/solvent systems from which micro-and nanofibers are produced.Crystalline and amorphous polymers, including poly(ethylene oxide) (PEO), poly(lactid acid) (PLA), and poly(-caprolactone) (PCL), were spun from different solvent systems to investigate the influence of polymer type and processing parameters on fiber structure and morphology.Spun samples were characterized by scanning electron microscopy (SEM), Xray diffraction (XRD), thermogravimetry (TG), differential scanning calorimetry (DSC), and contact angle measurements.Fourier-transform infrared spectroscopy (FTIR) was also used in order to verify the presence of residual solvent on the spun fibers.

Preparation and Characterization of Polymer Solutions.
Poly(lactic acid), PLA, (  = 75,000 g⋅mol −1 ) was obtained from Biomater (São Carlos, Brazil).Poly(-caprolactone), PCL, (  = 50,000 g⋅mol −1 ) was obtained from Perstorp (Warrington, UK), and poly(ethylene oxide), PEO, (  = 100,000 g⋅mol −1 ) was obtained from Sigma-Aldrich (USA).Chemical structures of these polymers are shown in Figure 1.Chloroform, dichloromethane, and acetone, purchased from Synth (São Paulo, Brazil), were used to prepare the polymer solutions used in this study.In order to prepare these solutions for solution blow spinning and electrospinning, weighed amounts of PLA, PCL, and PEO were dissolved according to proportions listed in Table 1 and under vigorous stirring for several hours until complete dissolution.

Characterization of the Solutions.
Solution properties, such as surface tension () and shear viscosity (), were measured at ambient temperature using a Kibron Microtrough X pressure sensor and an Anton Paar Physica MCR rheometer, respectively.

Fiber Spinning.
Fibers prepared by electrospinning were spun using a voltage of 24 kV, working distance of 12 cm, and a feed rate of 2 L⋅min −1 .Fibers obtained by solution blow spinning were prepared under an air pressure of 0.4 MPa, working distance of 12 cm, and feed rate of 120 L⋅min −1 .In both cases, a polymer concentration of 6 wt.% was used.

Fiber Characterization
2.4.1.SEM.Fiber morphology was observed using a model DSM960 Zeiss scanning electron microscope (SEM), after gold coating with a sputter coater (Balzers, SCD 050).Fiber diameters were measured with the aid of image software (ImageJ, National Institutes of Health, USA).For each experiment, average fiber diameter and distribution were determined from about 100 random measurements using micrographs representative of fiber morphology.

FTIR.
FTIR data were recorded on a Nicolet 470 Nexus FTIR spectrometer.The FTIR spectrometer was purged continuously with nitrogen.A total of 64 scans were collected with a resolution of 2 cm −1 .The infrared spectra were recorded in transmission mode using thick films of spun (solution blow spinning and electrospinning) polymer nanofibers which were deposited on a silicon wafer.

XRD Characterization.
For XRD measurements, nonwoven fibrous mats, which were collected on aluminum foils, were deposited on circular glass slides for further analyses.X-ray diffraction patterns were recorded using a Shimadzu XRD-6000 diffractometer.Scans were carried out from 10 ∘ to 30 ∘ (2) at a scan rate of 2 ∘ /min using Ni-filtered CuK radiation.The full width at half-maximum height (FWHM) of the diffraction peaks was calculated by fitting the X-ray diffraction data with a Gaussian-Lorentzian function (Origin 7.5 software, Origin Lab, USA).The d-spacing for a given scattering angle, 2, was calculated by application of the Bragg equation where  is the wavelength of the CuK radiation ( = 0.154 nm).
The full width at half-maximum height of the diffraction peaks was calculated by fitting the X-ray diffraction data with a Lorentzian function, and the crystallite size, , was estimated by calculating the broadening of the diffraction peaks according to the Scherrer equation where  is the Scherrer constant that depends upon lattice direction and crystallite morphology, and  is the full width at half-maximum height given in radians.A  value of 0.9 was used in this study, which is based on values found in the literature for these polymers [19][20][21][22].
2.4.4.Thermal Analyses.TG experiments were performed on a Q500 TA Instruments thermogravimetric analyzer under nitrogen atmosphere, at a flow rate of 20 ml⋅min −1 .Samples were scanned from room temperature to 600 ∘ C at a scanning rate of 10 ∘ C/min using platinum crucibles.DSC studies were performed on a Q100 TA Instruments calorimetric analyzer under nitrogen atmosphere, at a flow rate of 20 mL/min.The samples were heated from 10 ∘ C to 200 ∘ C for PLA, −70 ∘ C to 110 ∘ C for PCL, and −20 ∘ C to 120 ∘ C for PEO at a scanning rate of 10 ∘ C/min using aluminum pans.

Contact Angle Measurements.
Contact angles of water on the surface of spun fibers (nonwoven mats) were measured by a CAM 101 model KSV Instruments equipped with a CCD camera (KGV-5000).In each measurement, a 5 L droplet was pipetted onto the surface, and images of the droplet were automatically taken as a function of time.From these images, contact angle values were calculated using dedicated software (KSV CAM2008).Measurements were carried out at 25 ∘ C and about 53% humidity.

Results and Discussion
3.1.Solution Characterization.Values of viscosity (10 −1 s −1 ) for PLA, PEO, and PCL were found to be, respectively, 13, 71, and 35 mPa⋅s.These differences can be attributed to polymer structures and molecular weights as well as polymersolvent interactions.According to the manufacturers, these polymers have a number-average molecular weight (  ), respectively, of 75,000, 100,000, and 50,000 g⋅mol −1 which can account for the differences in the viscosity values found.
Although the molecular weight of PCL is lower than that of PLA, its higher value of viscosity can be attributed to the polar ester groups in PCL that promote stronger interchain interactions.Moreover, other factors that play an important role in polymer chain configuration [23], and therefore, in viscosity, such as polymer-solvent interaction parameters, may also be contributing to these differences found.
Solutions showed similar values of surface tension (34, 37, and 39 mN⋅m 1 , respectively, to PLA, PEO, and PCL), which can be due to the low concentration of polymer (6 wt.%) as well as because of differences in surface tension of each polymer and solvent, as can be seen in Table 2.
The knowledge of solution properties such as viscosity and surface tension is important to understand fiber morphology.Viscoelasticity was found to be one of the parameters that most influenced the morphology of solution blow spun fibers [14,24].On the other hand, surface tension is known to play a major role in fiber morphology developed during the electrospinning process [25].

Morphological
Characterization.SEM micrographs of PLA, PEO, and PCL fibers are shown in Figures 1(a)-1(c).Fiber average diameters, calculated using about 100 individual diameters to each sample, are shown in Table 3.
As outlined by the data trends in Table 3 and the micrographs (Figure 2), fiber morphology was different in each sample.PLA fibers (Figure 2(a)) had the most consistent morphology with small variations in diameter for both solution blow spinning and electrospinning (Table 3).On the other hand, PCL fibers when spun by SBS (Figure 2(b)) showed a very irregular structure with variable-sized fibers in a network of beads.When using electrospinning, a more regular structure was observed; that is, fibers had a more uniform cross-section.Nevertheless, numerous beads, which were much more irregular in size, were also present in electrospun samples.PEO fibers, like PLA, also had a regular morphology with small variations in diameter for both SBS and electrospinning (Figure 2(c)).Image analysis also  showed that many of these fibers are broken, possibly due to their brittle nature.
A plot of fiber dispersion as a function of zero-shear viscosity (ZSV) of the polymers is shown in Figure 3, outlining an increase in fiber dispersion as zero-shear viscosity increases.It can be observed that higher ZSV values led to a greater dispersion for solution blow spun fibers.This might have happened because the air pressure exiting the outer nozzle was not high enough to stretch the fibers being produced.As viscosity increases, fiber stretching becomes more difficult, and as a consequence, thick fibers are potentially produced with broader fiber diameter distribution.One likely explanation is that a balance must be achieved between solution viscosity and the fiber-forming forces that are derived from the pressurized air exiting the outer nozzle in order to produce fibers with regular cross-sections.
During fiber formation by SBS, a jet of polymer solution is subjected to aerodynamic drag [26][27][28].The shear forces that act upon the polymer solutions are therefore responsible for fiber stretching and, ultimately, for fiber diameter distribution [27].One can speculate that higher air turbulence due to high air flow would lead to a larger distribution of fiber diameter because of the irregular air flow exiting the nozzle.Variations in air flow would then impart different degrees of stretching and shearing on fibers being formed.However, higher air flow was generally required because the viscosity of the polymer solution is high.For higher viscosity polymer solutions, fiber stretching would become more difficult, less efficient, and unstable giving rise to broader fiber diameter distribution.Accordingly, the PLA system, with the lowest viscosity, produces the least variation in fiber diameter.Diameter histograms of spun fibers are shown in Figure 4.
In contrast, fiber formation in electrospinning is controlled by electrostatic repulsive forces that overcame surface tension, while a charged jet is ejected through a needle to produce fibers.As this jet travels through the air, the solvent evaporates, leaving behind ultrafine polymer fibers.Stretching by electric forces taking place on the surface of the jet is an important step during fibers formation [7].Therefore, in electrospinning, fiber formation is more dependent on surface tension as can be seen by comparing average fiber diameter in Table 3 with surface tension in Table 2.

FTIR Characterization.
FTIR spectra of spun fibers of PLA, PCL, and PEO solution blow spun fibers were recorded in the 600-3,000 cm −1 region.Similar spectra were obtained for electrospun fibers.Peak assignments for these polymers can be found in Figure 5 and Table 4.

PLA.
In the PLA spectrum, the active modes overlapped to give a broad asymmetric band at about 1754 cm −1 .It is clear that C = O stretching mode is sensitive to morphology and chain conformation.According to Kister et al. [29], the intensity of the shoulder at 1754 cm −1 increases with the degree of syndiotacticity of polymer.The band observed at 1754 cm 1 for amorphous compounds was considered as resulting from entrainment of particular chiral unit generated by the pair addition mechanism [29,30].
The CH 3 asymmetric deformation modes appeared at about 1452 cm −1 as an intense IR band (Table 4).Their stability in frequency reflected a pure vibrational mode.This region was characterized by a band at 1360 cm −1 .The 1182 cm −1 band observed in PLA could be assigned to a symmetric C-O-C stretching mode of ester groups.Asymmetric C-O-C modes were observed at 1086 cm −1 as a nonsymmetric IR  band.Other bands were assigned as follows: the band near 1045 cm −1 corresponded to ]C-CH 3 stretching and the band 868 cm −1 to ]C-COO stretching.

PEO.
The infrared spectra of PEO spun fibers were recorded, and the observed wavenumbers are listed in Table 4.The spectrum is essentially the same as the spectrum of the crystalline PEO reported previously [31][32][33].The strong band observed at 1110 cm −1 was assigned to the skeletal stretching mode.This assignment is confirmed by Miyazawa et al. [32]  947 cm −1 has been much discussed in parallel with the conformation of the CH 2 groups.This band had been assigned to the symmetric CH 2 rocking mode of the O-CH 2 CH 2 -O group in the gauche conformation [33,34] although Miyazawa et al. [32] assigned this band to the asymmetric rocking mode.The weak band at 947 cm −1 is due to the hybridized mode of the C-O-C asymmetric stretching and the CH 2 symmetric rocking mode.Three strong bands are observed at 1148, 1062, and 843 cm −1 .The band at 843 cm −1 has been assigned previously to the CH 2 asymmetric rocking mode of the CH 2 group in the gauche conformation.The band at 1148 cm −1 is primarily due to the CH 2 symmetric rocking mode, whereas the band at 1062 cm −1 is primarily due to the C-O-C asymmetric stretching mode coupled with the CH 2 symmetric rocking mode.

PCL.
Regarding the PCL spectrum, strong bands such as the carbonyl stretching mode around 1726 cm −1 can be easily identified.Such as PLA and PEO, the important band and their assignments are outlined in Table 4.It is important to mention that some of these bands are only observed after band deconvolution, which is the case in the 1100-1190 cm −1 region, where three bands could be distinguished on the spectrum, while indeed three bands are overlapping.According to Coleman and Zarian [35], the band at 1294 cm −1 is assigned to the backbone C-C and C-O stretching modes in the crystalline PCL (see Table 4).He and Inoue [36] established a procedure for the quantitative crystallinity for analysis of PCL using a deconvolution of carbonyl vibration region (1726 cm −1 ) into two bands (amorphous and crystalline).
In summary, close inspection of the spectra above revealed the absence of peaks that are characteristics of the solvents used for fiber spinning, therefore indicating that there are no residual solvents left after spinning.This is an important factor in applications such as in scaffolds for cell and tissue growth since solvent residue may be harmful in biomedical applications.

XRD Characterization.
In order to determine the crystal structures in spun polymer fibers, X-ray diffraction was carried out.A comparison in terms of crystallinity, spacing and crystallite size () were also carried out and are summarized in Figure 6 and Table 5.

PLA.
Comparative studies for PLA cast films and electrospun fibers are reported in the literature [37].It is observed that nonwoven PLA spun fibers (Table 5) showed a strong amorphous halo, with one crystal peak found in the diffraction patterns (16.38 ∘ ).On the other hand, solution blow spun and electrospun PLA fibers clearly exhibited two reflection peaks (near 13 ∘ and 16 ∘ ), ascribed to  crystals, and a small peak (near 24 ∘ ) associated with  phase [38,39].Formation of  crystals is caused by the different extent of deformation of the polymer molecules during fiber formation by solution blow spinning compared to electrospinning [39].The critical factor for crystal formation is a high degree of deformation (present in both spinning processes) which was not observed for cast films.It can also be noted that  crystal peaks of electrospun fibers from PLA shifted toward higher 2 values and larger crystallites were also present when compared with solution blow spun fibers and cast films.This fact is probably due to a different degree of stretching during crystallization, resulting in crystallites with variations in relative defects.Decreased order would appear as peak broadening and a greater variation in unit cell parameters from "ideal" crystals.PLA cast films presented a crystallinity of 35%, based in the Lorentz fit, while electrospun and solution blow spun fibers presented crystallinity, respectively, of 82 and 71% (Table 5).This increase in crystallinity observed for PLA spun fibers, when compared with PLA cast films, is attributed to the high stretching of the polymer chains which lead to a higher degree of molecular organization.

PEO. X-ray diffraction (XRD) patterns of PEO cast
films and spun fibers were carried out, and the results are summarized in Table 5. PEO is a semicrystalline polymer with diffraction peaks at 2 = 19 and 23 ∘ [33].Distinct peaks characteristic of PEO crystallites (2 = 14, 17, and 25 ∘ ) were observed for spun fibers which indicate that solvent-induced polymer crystallization occurred.When comparing SBS and electrospun fibers with cast films, it is interesting to note that SBS increased crystallinity, while electrospinning decreased relative crystallinity (Table 5).As a consequence, crystals developed under SBS were larger than those under electrospinning (Table 5).This fact suggests that in the crystallization of the fibers produced by electrospinning, the nucleation step is predominant, whereas in SBS the crystallite growth step is more predominant.Another factor that may have contributed to this difference, besides the nature of the forces involved, can be the timescale for each event to take place.SBS is depositing a much greater amount of polymer than electrospinning; it is roughly 10 times faster.The higher speed and greater forces in SBS likely favored chain orientation, leading to a higher crystallinity relative to electrospinning.

PCL. XRD patterns of PCL spun mats show that all
diffraction peaks correspond to PCL, which is a semicrystalline polymer with two distinct diffraction peaks reported at ∼21 and ∼23 ∘ [40].Moreover, these peaks were sharp and distinct, which indicated that samples were highly crystalline.Table 5 shows the degree of crystallinity, -spacing, and crystallite size obtained from XRD for all samples.Crystallinity measurements for PCL range between 56 and 81%.Crystallite size and interplanar distance range between 1.7-3.9nm and 4.6-5.3nm, respectively.Similar to the behavior for PEO, electrospinning also reduced fiber crystallinity relative to cast films, while SBS increased fiber crystallinity.This also led to larger crystals when the morphology was developed under SBS, as opposed to electrospinning.Again, this clearly indicates that fiber formation mechanism in SBS is different from electrospinning, and probably, a different timescale also governs the SBS process.
In summary, similar to electrospinning, the crystalline structure of polymer nanofibers obtained by solution blow spinning depends on process variables such as molecular weight, polymer-solvent interactions, and dynamics of fiber formation.
3.5.Thermal Analyses.TG and DSC results of spun fibers and films can be found in Table 6 and Figure 5. Characteristic temperatures (glass, crystallization, and melting), heat of fusion (Δ  ), and crystallization (Δ  ) for PLA, PEO, and PCL films obtained by casting, SB-spinning, and electrospinning are summarized in Table 6.
3.5.1.PLA.TG curves of PLA show that PLA cast films and spun nanofibers decomposed in a single step (Table 6).However, the onset of the decomposition temperature for PLA nanofibers was 327 and 311 ∘ C, respectively, for electrospun and SBS fibers, while for PLA cast films it was 333 ∘ C. A slight decrease in thermal stability for spun fibers, as opposed to cast films, is observed by TG, which might be due to their high surface area (Table 6).A very similar thermal behavior has already been reported in the literature [41,42].It must be noted that the surface areas of spun nanofibers are much higher than those of cast films.As is well noted in the literature [12], crystalline PLA fibers can exhibit two distinct crystalline morphologies, the  structure, with lamellar-folded chain morphology, and metastable  structure, with a planar "zigzag, " extended chain morphology.These are noted by two distinct peaks near the melting point.Figure 7(a) shows DSC curves for electrospun and solution blow spun PLA fibers with different average diameters compared with PLA cast films.
The lower cold crystallization temperature of electrospun fibers compared to SBS fibers (Table 6) suggested that electrospun fibers had a certain level of chain alignment that led to crystallization occurring at a lower temperature.Zong et al. [43] investigated PLA nanofibers with DSC and XRD analysis and found that polymer chains were noncrystalline but highly oriented.
3.5.2.PEO.Typical weight loss (TG) and derivative (DTG) curves (inset plots) of spun and cast films of PEO were obtained, and the results are presented in Table 6.The onset of the decomposition curves of these polymers is summarized in Table 6.The onset decomposition temperature of PEO cast films was 373 ∘ C and for spun fiber was found to be 375 and 371 ∘ C, respectively, for electrospun and SBS.PEO cast films show a thermal stability similar to that of spun fibers.TG curves of both spun fibers and cast film also indicate one reaction step (Table 6).This behavior is somewhat unexpected since both fibers produced by electrospinning and SBS have very high surface area when compared to films which can be due to the higher degree of crystallinity developed during fiber formation.
DSC analysis of PEO in hot pressed form presented a melting temperature (  ) of 62 ∘ C (Δ  = 109 J/g), whereas cast film and electrospun PEO nanofibers were determined at 65 ∘ C (Δ  = 103 J/g) and 63 ∘ C (Δ  = 110 J/g), respectively, during the first heating cycle (Figure 7(b); Table 6).In addition, the PEO fibers produced by solution blow spinning presented a melting temperature of 62 ∘ C (Δ  =143 J/g) in the first heating cycle, indicating an increase in crystallinity of fibers by solution blow spinning process.

PCL.
The TG curve obtained for spun and cast films of PCL displays one main degradation step with an inflection point at 380 ∘ C for PCL cast films and spun fibers.The DSC curves of the PCL fiber mats and hot pressed and cast film forms are shown in Figure 7(c).It can be seen from the first heating run (Figure 7(c) and Table 6) that in all cases the melting point (  ) of PCL was 56 ∘ C. Their fusion enthalpies were 32 J/g for hot pressed form, 29 J/g for cast film and electrospun forms and 38 J/g for solution blow spun form.Such as PEO case, these results indicate that there was little to no variation in Tm with the processing method.
The crystalline structure developed in PCL nanofibers by electrospinning, as well as molecular orientation, is different from as-received materials, as reported in the literature [6,12,40,44].In electrospinning and SBS processes, rapid solidification occurs due to quick solvent evaporation.Because of this, solvent properties and polymer-solvent interactions play important roles in polymer crystallinity and chain orientation of the spun fibers.Since molecular chains do not have enough time to form a fully crystalline structure, development of crystallinity under a fast solidification is impacted.This particularly affects flexible polymers with lower glass transition (  ) temperatures, which have more mobility at their process temperatures and crystallize in a shorter time than a rigid polymer with high   .
values for PLA, PEO, and PCL are, respectively, 60, −11, and −72 ∘ C. Consequently, PEO and PCL crystallization can be facilitated by chain stretching during fiber formation under SBS and electrospinning, even after PEO and PCL are solidified.These may be the reasons why solution blow spun fibers of PEO and PCL developed higher crystallinity, whereas the crystallization of PLA was reduced.Moreover, the DL structure of PLA is another factor that is, responsible for its crystallinity.Polymerization of a racemic mixture of L-and D-lactides forms poly-D,L-lactide (PLA), which is amorphous and has a glass transition temperature of 55-60 ∘ C. The degree of crystallinity can be tuned by altering the ratio of D to L enantiomers within the polymer.Selection of the PLA stereochemistry can have a major effect on the polymer properties, processability, and biodegradability [45].These results of thermal analysis and X-ray diffraction suggest that the fast solvent evaporation occurs by different mechanisms in SBS and electrospinning.This can be related to the atmosphere surrounding these processes.In the latter case, it is predominantly controlled by the characteristics (relative humidity type of gas, temperature, etc.) of the pressurized gas.

Contact Angle Measurements.
For determination of the hydrophilic character of the spun nonwoven nanofibers, the contact angle between the mats and the water and ethylene glycol was measured.It is known that the lower the contact angle, the higher the hydrophilic nature of the surface.Changes of the contact angle values between the water/ethylene glycol with the different spun fibers (PLA, PCL, and PEO) are illustrated in Figure 8.
It is reported in the literature [46][47][48] that polyesters and polyethers are not highly hydrophobic materials (PLA, PCL, and PEO cast film shows a contact angle of 84 ∘ , 89 ∘ , and 48 ∘ , resp.); the initial hydrophobicity of the as-spun mats is metastable; that is, contact angle decreases gradually with time over a period of about 2 min under ambient conditions.Ma et al. [49] attributed the origin of this decrease in contact angle from the evaporation of water from the droplet and the conversion of the contact zone from an initial Cassie-Baxter state to a final Wenzel state as the water droplet sinks into the pores of the mat due to capillarity.The changes in contact angle as a function of the average fiber diameter for water droplets (dipole moment 1.84 D) and ethylene glycol (dipole moment 2.31 D) can be observed in Figure 8.
A parabolic behavior was observed for both electrospun and solution blow spun fibers.It is believed that these variations in contact angle are associated with the average fiber diameter.Moreover, the porous nature of spun mats acts as roughness in the nanoscale.It is well known that if a polymer is hydrophobic, increasing its roughness causes an increase in the hydrophobicity of this polymer; on the other hand, if the polymer is hydrophilic, its hydrophilicity is also found to increase with increasing surface roughness.
As a general summary, solution blow spinning and electrospinning of polymers from solution may yield submicron and nanometric fibers which are characterized by several structures (fiber, bead, and network), depending on the working conditions used.Fibers formation is apparently controlled by a rapid evaporation of the solvent and a high strain rate caused by electrical forces (electrospinning) and aerodynamic forces (SBS).The fibers obtained by solution blow spinning have properties which make them ideal candidates for cell adhesion, catalysis, and sensors applications.

Conclusions
Electrospinning and solution blow spinning of PLA, PEO and PCL from solution yield fibers whose diameters range from the nanometer to the submicron scale.Polymer molecular weight, surface tension, and evaporation rate of polymer solutions contribute to fiber diameter.These fibers can possess different morphologies, such as fibers with and without beads, and fiber bundles which can be controlled by process variables.In both techniques, morphology development is apparently controlled by solvent evaporation and a subsequent rapid solidification.Nonwoven mats are of interest for a broad range of applications in areas such as tissue engineering or drug delivery given the absence of residual solvents in the SBS fibers for PLA, PCL and PEO, which was confirmed by FTIR studies.XRD analysis indicated that either a different mechanism or a timescale, or both, may be playing an important role in fiber crystallinity development by electrospinning and SBS.Therefore, crystalline structure and chain orientation in polymer nanofibers electrospun and solution blow spun depend on process variables such as molecular weight, polymer-solvent interactions, and process timescale.PLA nanofibers presented a decreased thermal stability compared to powder PLA, but this effect was not observed for PEO and PCL.In addition, DSC analysis showed two peaks near the melting point ( and  crystalline phases) for PLA spun samples.Thermal analysis showed that PEO and PCL crystallization can be facilitated by chain stretching during fiber formation by SBS and electrospinning, even after PEO and PCL are solidified.These may be the reasons why solution blow spun fibers of PEO and PCL developed higher crystallinity, whereas the crystallization of PLA was reduced.

Scheme 1 :
Scheme 1: Cutaway diagram of the (a) concentric nozzle system used in solution blow spinning and (b) electrospinning processes.

Figure 1 :
Figure 1: Chemical structure of the polymers used for fiber spinning: (a) PLA, (b) PEO and (c) PCL.

Figure 2 :
Figure 2: Scanning electron micrographs of spun fibers obtained by solution blow spinning and electrospinning for PLA (a), PCL (b), and PEO (c).Right side: electrospun and left: SB-spun.

Figure 3 :
Figure 3: Effect of viscosity on fiber diameter and dispersion by (a) solution blow spinning and (b) electrospinning.

Figure 8 :
Figure 8: Effect of the fiber average diameters on contact angle (a) water and (b) ethylene glycol as a function of the spinning technique.

Table 1 :
Solution parameters of spun fibers.

Table 2 :
Experimental values of surface tension in mN/m for the polymer solutions and solvents (23 ∘ C, 43% RH).

Table 3 :
Average diameter of spun fibers.
* 1% of the fibers observed has 3 m of diameter.

Table 4 :
Characteristic infrared bands of PLA, PEO, and PCL.

Table 5 :
Crystalline structure parameters for PLA, PEO, and PCL.