Advances in Materials Science and Engineering

Volume 2014 (2014), Article ID 409086, 5 pages

http://dx.doi.org/10.1155/2014/409086

Research Article

Degradation of Tetracycline by Birnessite under Microwave Irradiation

Meng Liu, Guocheng Lv, Lefu Mei, Xiaoyu Wang, Xuebing Xing, and Libing Liao

School of Material Sciences and Technology, China University of Geosciences, Beijing 100083, China

Received 19 June 2014; Revised 14 August 2014; Accepted 14 August 2014; Published 2 September 2014

Academic Editor: Ying Li

Copyright © 2014 Meng Liu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract.

The efficiency and factors affecting tetracycline (TC) degradation by birnessite under microwave irradiation (MI) were investigated under different initial TC concentrations, solution pH, MI time, and MI power. The crystal structure, degradation efficiency, and reaction mechanism were investigated using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and ultraviolet-visible spectroscopy (UV-Vis). The results showed that birnessite was an excellent microwave catalyst. The maximum TC removal efficiency by birnessite was 99% under MI at 400 W for 30 min in strongly acidic media. Under MI, the surface activity of birnessite increased, resulting in the ability to accelerate TC removal in high temperature.

1. Introduction

In 1999, Daughton presented the idea of pharmaceuticals and personal care products (pharmaceuticals and personal care products, PPCPs) [1]. They are considered as the emerging environmental contaminants leading to contaminations in surface water, groundwater, and wastewater [2]. Antibiotic tetracycline (TC, Figure 1) is widely used in livestock for growth promotion and treatment of diseases [3]. Since the late 1990s, the use of TC on poultry farming reached up to 3 × 10⁶ Kg annually [4]. As TC was not able to be completely digested and absorbed by most organisms, more than 85% of TC was excreted in its original drug form [5]. Livestock, after ingestion of TC, will gradually accumulate TC. The use of animal wastes as well as biosolids from wastewater treatment facilities as fertilizers for field application would result in elevated TC concentrations in a variety of ecosystems [6].

Figure 1: Molecular model of TC.

Microwave technology was originated in the 1930s, but it was not widely applied to the environmental protection fields until the late 1990s. Microwave catalytic technology can be highly efficient when used in degrading macromolecular organic pollutants [7]. In essence, macromolecular organic pollutants are put into the microwave field; through the perturbation of popular molecules, the bonding of macromolecular organic pollutants will be broken, and then the purpose of the degradation of pollutants is reached [8]. Microwave irradiation (MI) has a fast response, high efficiency and selectivity, fewer side effects, and energy saving features; thus it has been widely used in macromolecular degradation prospects [9]. MnO₂, Co₃O₄, and Fe₂O₃ were the most suitable microwave catalysts known as high-loss materials for microwave which presents a high activity by MI [10, 11].

Manganese oxides could act as an adsorbent, oxidant, and microwave catalyst; thus, they could be used in environmental remediation. Manganese oxides are mainly constituted by [MnO₆] octahedra with () pyrolusite pore structure in ramsdellite family, barium and manganese ore () pore structure in psilomelane family, barium, calcium, and manganese family () pore structure, and (∞) layered structure manganese oxide minerals [12, 13]. Birnessite (Figure 2) has a layered structure and it is a typical δ-type manganese dioxide material. The interlayer is made of a layer of water molecules containing different types of cations and [MnO₆] octahedral layers stacked together in the same direction [14–16]. Birnessite is one of the most widely distributed manganese oxides, and it is also an excellent material for microwave absorption [17]. This absorbing material has a long life, is nontoxic and efficient, and has no secondary pollution treatment. Microwave originated from the high energy sources could produce synergistic effect with a highly active center when exposed to air. The active center of birnessite will be oxidized under MI to produce an active substance, by which organic pollutants could be degraded into smaller, nontoxic molecules [18].

Figure 2: Layered structure of birnessite.

In this study, the degradation of TC by birnessite under MI was systematically investigated in order to explore the catalytic effects and optimize reaction conditions.

2. Experiments

2.1. Materials

NaOH, MnCl₂·4H₂O, and KMnO₄ were used for the preparation of birnessite. They were purchased from Beijing Chemical Works. TC was obtained from Calbiochem (Darmstadt, Germany). They were used as received without further purifications.

Aqueous MnCl₂ solution (40 mL, 0.50 mol/L) was slowly added to NaOH solution (50 mL, 5.0 mol/L) under vigorous stir for 5 minutes, allowing formation of Mn(OH)₂. KMnO₄ solution (0.20 mol/L) was then gradually added dropwise, and stir was continued for 30 minutes to complete the reaction. The product was centrifuged for 3 min at 10000 rpm, washed 10 times with distilled water, and dried at 40°C for 48 h.

2.2. TC Degradation under MI

TC removal efficiency () was determined by the following equation [19]:

where and are the initial and equilibrium TC concentrations. The amount of TC degraded () was calculated by the following equation:

where is the solution volume and is the mass of the solid.

2.3. TC Concentration Measurement

Calibration was made with the following concentrations: 1, 2, 5, 10, 15, and 20 mg/L under pH 3, 7, and 11. The UV absorbance was determined at the wavelength of 360 nm [20]. The coefficients of linear regression were all greater than 0.999.

3. Results and Discussion Mechanism

3.1. Birnessite Characterization

The synthesized birnessite matched with the PDF file of birnessite well as revealed by XRD diffraction analyses (Figure 3).

Figure 3: The XRD of synthesized birnessite.

3.2. Effect of Microwave Irradiation Time on Removal Efficiency of TC Solution

With 0.2 g of birnessite and 50 mL of 50 mg/L TC solution, a significant increase in was found in the presence of MI (Figure 4). Also noticed was a fast increase in TC degradation rate within the first 5 to 10 min, suggesting a very significant role of MI. Meanwhile, equilibrium was reached at 30 min with an of 43%.

Figure 4: TC removal efficiency of different processes change over time.

3.3. Influence of Initial TC Solution Concentration on Removal Efficiency

With 0.2 g of birnessite and 50 mL of TC solution, the TC removal efficiency by birnessite under MI decreased as the TC solution concentrations increased (Figure 5). On the other hand, with an increase in initial TC concentration, the amount of TC degraded increases gradually to 6.5 mg/g, when the initial TC concentration reached 70 mg/L. Further increase in initial TC concentration resulted in no further change in amount of degradation.

Figure 5: Changes in removal efficiency and the amount of degradation with different initial concentrations of TC solution.

3.4. Influence of MI Time and Power on TC Degradation

With 0.2 g of birnessite and 50 mL of 50 mg/L TC solution, an increase in MI time from 5 to 20 min significantly increased when the MI power was 300 W (Figure 6). On the other hand at 20 or 30 min of MI, the change in was from 40 to 50% as the MI power increased from 300 to 700 W. XRD results showed no change in material phases under MI up to 700 W (data not shown); see Supporting Figure S1, available online at http://dx.doi.org/10.1155/2014/409086.

Figure 6: Removal efficiency varies with the microwave power.

3.5. Effect of Solution pH on TC Removal Efficiency

With 0.2 g of birnessite and 50 mL of 50 mg/L TC solution, TC removal efficiency was up to 99% under strong acidic conditions after MI for 30 min (Figure 7). Removal efficiency of about 60% was achieved under neutral pH conditions. The efficiency decreased to 29% under alkaline conditions.

Figure 7: Influence of solution pH on TC removal efficiency.

Different functional groups of TC will be ionized under different pH conditions, resulting in different numbers of electric charges. When pH is less than 3.3, the main form is a monovalent cation. When the pH is between 3.3 and 7.7, a neutral molecule was dominating. As the pH is greater than 7.7, a monovalent anion prevailed. A dianion is formed when the pH is greater than 9.3 [21–23]. Figure 7 showed that when TC was in its cationic form, degradation of TC was enhanced. On the contrary, when TC was in monoanionic or dianionic form, its degradation efficiency was greatly reduced. The XRD results showed no change in solid phases under different pH conditions, ruling out that the change in the TC degradation efficiency was due to different types of MnO₂ (data not shown); see Figure S2.

3.6. Mechanism of Action of the Reaction System

The enhanced TC degradation by birnessite resulted directly from MI and the oxidability of birnessite [23]. MI could increase the surface reactivity of birnessite and create a high temperature environment, resulting in an accelerated TC removal. Mn(IV), Mn(III), and little Mn(II) were found on the surface of birnessite and a cyclic trend was found with the valence of Mn increased under MI and decreased after reaction with methylene blue [24]. The oxidation reaction of Mn(II) was slow under normal conditions, but dissolved Mn(II) could be quickly oxidized by O₂ under MI [24]. Moreover, MI could provide a high temperature environment and accelerate the sustainable cyclic redox reaction processes until complete removal of MB [24].

Birnessite could greatly enhance reactivity through reduction in activation reaction, variation, and a high frequency alternation of electromagnetic field. It could also lead to changes in dipole moment directions in birnessite, which, in conjunction with hysteresis, would also cause the dielectric loss of the reaction system (Figure 8), so that part of the microwave energy could be converted into heat energy to result in a sharp rise in temperature of the system [25]. Studies have shown that the surface temperature of birnessite after 1 min microwave heating could reach thousands of degrees Celsius [26]. Thus, when the reaction system was exposed to air or oxygen, the surface activity of birnessite increased and the temperature could rise to approximately 1378 K [27], resulting in an accelerated degradation of TC.

(a)

(b)

(c)

Figure 8: Schematic diagram of microwave heating. (a) Material distribution of molecules before microwave heating. (b) Distribution of materials during microwave heating. (c) Change in polarity under microwave field to generate heat.

4. Conclusion

(1)Birnessite is an excellent microwave catalytic oxidation material. TC removal efficiency of up to 99% could be achieved under MI power of 400 W for 30 min at a system of 0.2 g birnessite and 50 mL of 50 mg/L TC solution at pH = 1.(2)Comprehensive analysis showed that the mechanism of TC degradation by birnessite under MI was due to increased surface reactivity of birnessite and creation of a high temperature environment, resulting in an accelerated TC removal.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This research was jointly funded by the Beijing Higher Education Young Elite Teacher Project (YETP0634), the University Students’ Innovative Undertaking Training Program (201311415057), and International S & T Cooperation (S2014ZR0062).

References

C. H. Daughton and T. A. Ternes, “Pharmaceuticals and personal care products in the environment: agents of subtle change?” Environmental Health Perspectives, vol. 107, supplement 1, p. 598, 1999.

Y. Chen, C. Hu, J. Qu, and M. Yang, “Photodegradation of tetracycline and formation of reactive oxygen species in aqueous tetracycline solution under simulated sunlight irradiation,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 197, no. 1, pp. 81–87, 2008.

M. Miyata, I. Ihara, G. Yoshid, K. Toyod, and K. Umetsu, “Electrochemical oxidation of tetracycline antibiotics using a Ti/IrO₂ anode for wastewater treatment of animal husbandry,” Water Science and Technology, vol. 63, no. 3, pp. 456–461, 2011.

A. B. A. Boxall, D. W. Kolpin, B. Halling-Sørensen, and J. Tolls, “Are veterinary medicines causing environmental risks?” Environmental Science and Technology, vol. 37, no. 15, pp. 286A–294A, 2003.

A. Hartmann, A. C. Alder, and T. Koller, “Identification of fluoroquinolone antibiotics as the main source of umuc genotoxicity in native hospital wastewater,” Environmental Toxicology and Chemistry, vol. 17, no. 3, pp. 377–382, 1998.

A. L. Batt, I. B. Bruce, and D. S. Aga, “Evaluating the vulnerability of surface waters to antibiotic contamination from varying wastewater treatment plant discharges,” Environmental Pollution, vol. 142, no. 2, pp. 295–302, 2006.

Y. Yang, P. Wang, S. J. Shi, and Y. Liu, “Microwave enhanced Fenton-like process for the treatment of high concentration pharmaceutical wastewater,” Journal of Hazardous Materials, vol. 168, no. 1, pp. 238–245, 2009.

J. M. Hill and T. R. Merchant, “Modelling microwave heating,” Journal of Applied Mathematical Modelling, vol. 20, no. 1, pp. 3–15, 1996.

A. Patra, D. K. Bisoyi, P. K. Manda, and A. K. Singh, “Effect of microwave radiation on the macromolecular, morphological and crystallographic structures of sisal fiber,” Applied Physics A: Materials Science and Processing, vol. 112, no. 4, pp. 1063–1071, 2013.

H. A. Elazab, S. Moussa, B. F. Gupton, and M. S. El-Shall, “Microwave-assisted synthesis of Pd nanoparticles supported on Fe₃O₄, Co₃O₄, and Ni(OH)₂ nanoplates and catalysis application for CO oxidation,” Journal of Nanoparticle Research, vol. 16, no. 7, article 2477, 2014.

Y. Su, L.-C. Wang, Y.-M. Liu, Y. Cao, H.-Y. He, and K.-N. Fan, “Microwave-accelerated solvent-free aerobic oxidation of benzyl alcohol over efficient and reusable manganese oxides,” Catalysis Communications, vol. 8, no. 12, pp. 2181–2185, 2007.

L. Kang, M. Zhang, Z.-H. Liu, and K. Ooi, “IR spectra of manganese oxides with either layered or tunnel structures,” Spectrochimica Acta A: Molecular and Biomolecular Spectroscopy, vol. 67, no. 3-4, pp. 864–869, 2007.

S. Turner and P. R. Buseck, “Todorokites: a new family of naturally occurring manganese oxides,” Science, vol. 212, no. 4498, pp. 1024–1027, 1981.

M. Villalobos, I. N. Escobar-Quiroz, and C. Salazar-Camacho, “The influence of particle size and structure on the sorption and oxidation behavior of birnessite: I. Adsorption of As(V) and oxidation of As(III),” Geochimica et Cosmochimica Acta, vol. 125, pp. 564–581, 2014.

J. G. Parra, V. C. Cala Rivero, and T. I. Lopez, “Forms of Mn in soils affected by a forest fire,” Science of the Total Environment, vol. 181, no. 3, pp. 231–236, 1996.

J. E. Post, “Manganese oxide minerals: crystal structures and economic and environmental significance,” Proceedings of the National Academy of Sciences of the United States of America, vol. 96, no. 7, pp. 3447–3454, 1999.

F. Z. Lv, R. Z. Zhang, L. N. Xu, B. C. Luo, and Y. H. Zhang, “Composition and ionic change capacity variation of surfactant-intercalated MgFe-layered double hydroxides in the one step synthesis,” Journal of Sol-Gel Science and Technology, vol. 69, no. 1, pp. 26–32, 2014.

T. G. Spiro, J. R. Bargar, G. Sposito, and B. M. Tebo, “Bacteriogenic manganese oxides,” Accounts of Chemical Research, vol. 43, no. 1, pp. 2–9, 2010.

P. Hu, Y. H. Zhang, F. Z. Lv et al., “Organic pollution removal from TNT red water using Cu-Impregnated activated coke,” Water, Air, & Soil Pollution, vol. 225, no. 4, pp. 1–10, 2014.

W.-T. Jiang, P.-H. Chang, Y.-S. Wang et al., “Removal of ciprofloxacin from water by birnessite,” Journal of Hazardous Materials, vol. 250-251, pp. 362–369, 2013.

J. L. Colaizzi and P. R. Klink, “pH-Partition behavior of tetracyclines,” Journal of Pharmaceutical Sciences, vol. 58, no. 10, pp. 1184–1189, 1969.

S. A. Sassman and L. S. Lee, “Sorption of three tetracyclines by several soils: assessing the role of pH and cation exchange,” Environmental Science and Technology, vol. 39, no. 19, pp. 7452–7459, 2005.

P. di Leo, M. D. R. Pizzigallo, V. Ancona et al., “Mechanochemical transformation of an organic ligand on mineral surfaces: the efficiency of birnessite in catechol degradation,” Journal of Hazardous Materials, vol. 201-202, pp. 148–154, 2012.

X. Y. Wang, L. F. Mei, X. B. Xing et al., “Mechanism and process of degradation of methylene blue under microwave induced manganese xoides,” Applied Catalysis B: Environmental, vol. 211, pp. 160–161, 2014.

L. X. Yang, Y. J. Zhu, and G. F. Cheng, “Synthesis of well-crystallized birnessite using ethylene glycol as a reducing reagent,” Materials Research Bulletin, vol. 42, no. 1, pp. 159–164, 2007.

J. Zhu, Q. Li, W. Bi et al., “Ultra-rapid microwave-assisted synthesis of layered ultrathin birnessite K0.17MnO₂ nanosheets for efficient energy storage,” Journal of Materials Chemistry A, vol. 1, no. 28, pp. 8154–8159, 2013.

D. Yuping, M. He, L. Xiaogang, L. Shunhua, and J. Zhijiang, “The microwave electromagnetic characteristics of manganese dioxide with different crystallographic structures,” Physica B: Condensed Matter, vol. 405, no. 7, pp. 1826–1831, 2010.