Experimental Investigation on Mechanical and Turning Behavior of Al 7075 / x % wt . TiB 2-1 % Gr In Situ Hybrid Composite

The present research work involves the study of AA 7075-TiB 2 -Gr in situ composite through stir casting route. This in situ method involves formation of reinforcements within the matrix by the chemical reaction of two or more compounds which also produces some changes in the matrix material within the vicinity. TitaniumDiboride (TiB 2 ) and graphite were the reinforcement in a matrix of AA 7075 alloy. The composite was prepared with the formation of the reinforcement inside the molten matrix by adding salts of Potassium Tetrafluoroborate (KBF 4 ) and Potassium Hexafluorotitanate (K 2 TiF 6 ). The samples were taken under casted condition and the properties of the composite were tested by conducting characterization using X-ray diffraction (XRD), hardness test, flexural strength by using three-point bend test, scanning electron microscope (SEM), optical microstructure, grain size analysis, and surface roughness. It was found that good/excellentmechanical properties were obtained inAA 7075-TiB 2 -Gr reinforced in situ hybrid composite compared to alloy due to particulate strengthening of ceramic particles of TiB 2 in the matrix. Further, Al 70753% TiB 2 -1% Gr hybrid in situ composite exhibited improved machinability over the alloy and composites due to self-lubricating property given by the Gr particles in the materials.


Introduction
Composite material is composed of two or more materials at a microscopic scale and has chemically distinct phases.In ordinary conventional materials the required properties cannot be obtained.However by using the composite materials the needed properties in the required materials can easily be achieved.In metal matrix composites (MMCs) high strength and fracture toughness and stiffness are offered by metal matrices compared to those offered by their polymer counterparts [1][2][3][4][5].They can withstand elevated temperature in corrosive environment compared to polymer composites [6].Aluminium based particulate reinforced MMCs have emerged as an important class of high performance and it has low density and high thermal conductivity [7].To improve its strength, high elastic modulus, and increased wear resistance over conventional base alloys, AA 7075 alloy was selected because of its low specific weight and high strength-to-weight ratio and also its excellent machinability, formability, and weldability [8].This alloy is widely used in automotive industry, aircraft industry, and defense industries [9,10].The composite was prepared with the formation of the reinforcement inside the molten matrix of Titanium Diboride (TiB 2 ) which was obtained by adding salts of Potassium Tetrafluoroborate (KBF 4 ) and Potassium Hexafluorotitanate (K 2 TiF 6 ) [11].TiB 2 is well known as a ceramic material with relatively high strength and durability as characterized by the relatively high values of its melting point, hardness, strengthto-density ratio, and wear resistance [9].
In the in situ methods reinforcements are clean and thermodynamically stable.This method gives better mechanical properties due to the effective bonding between the matrix and the reinforcements.This method is especially for the metal matrix composite [12].Reinforcements are added in the form of salts.These salts react inside the molten matrix to form the reinforcements.In situ techniques lead to 2 Advances in Materials Science and Engineering better adhesion at the interface and hence better mechanical properties [13].The composite material can be made by different types of processes but here most commercially used technique of stir casting method was selected because of its most potential method for engineering applications in terms of production capacity and cost efficiency [14].The technology is relatively simple and of low cost.Based on several literatures, there is no work related to Al 7075-Tib 2 -Gr in situ hybrid composite on mechanical and turning behavior.Therefore, the present work carried out the detailed study and investigation on microstructure and mechanical and turning behavior of Al 7075-TiB 2 -Gr in situ hybrid composite.

Material Choice.
In this study, AA 7075 alloy (Al-Zn-Mg-Cu-Si-Mn-Fe-Mn-Ti-Cr) had been chosen because it has excellent machinability and formability and low specific weight and high strength-to-weight ratio compared to many other aluminium alloys [4].The chemical composition of AA 7075 is shown in Table 1.Tests for the results (Table 1) were carried out as per optical emission spectrophotometer (OSM) in order to conform the matrix.

Manufacturing of AA 7075-TiB
The addition of salts based on sample composition for getting different samples is given in Table 2.This work involves the manufacturing of composite material of Al 7075/% TiB 2 -Gr hybrid composites by stir casting technique (Figure 1(a)).In this method, the Al 7075 is initially kept in a crucible furnace and it is heated to a temperature of 760 ∘ C. Then the powers of K 2 TiF 6 and KBF 4 are mixed finely through stirring to achieve TiB 2 .Then it is preheated to a temperature of 200 ∘ C. In the meantime, the Al 7075 attained its liquid state and the stirring motor was switched on.The stir casting set-up consists of a blade which was made of graphite coated stainless steel.The speed of the stirrer was limited to 300 rpm.After reaching the vortex in the molten metal, the preheated chemical salts with size of 200 m were mixed evenly.During the mixing the stirrer rotates at a constant speed.Then the mixed molten metal was kept out for some time (10 min) at high temperature for the chemical reaction to take place, due to which the reinforcement will form in the molten metal.After completing the chemical reactions, the 1% of graphite was added to the molten metal and mixed properly.Finally the molten metal was poured in the circular die of the size 30 mm diameter and 250 mm length.

Characterization
Technique.X-ray diffraction (XRD) (using Cu-K radiation and operating at 40 kV and 100 mA) method was carried out to confirm the phases in fabricated hybrid composites.Those which require high magnification to be visible are termed microstructures.Microscopes are required for the examination of the microstructure of the metals.The maximum possible magnification with an electron microscope is approximately 2000 diameters.Then, the surface to be examined is scanned with an electron beam, and the reflected beam of electrons is collected and then displayed at the same scanning rate on a cathode ray tube.Magnifications ranging from 10 to an excess of 50 000 diameters and also very great depths of field are possible.Therefore, optical microscopes and scanning electron microscopes were used to examine the microstructures of the fabricated hybrid composites [5].Finally the microtexture of inserts before and after turning has been analyzed at highest cutting parameters and flank wear, nose deformation, and erosion of material over the tool have been examined.

Turning Process.
The turning experiments were carried out on Smart Jr CNC Turning centre using TiN coated carbide insert (K10) (Figure 1(b)).The cutting speed was selected (based on commercial one) in a range of 180 mm/min to 240 mm/min, feed rate range was selected in the range of 0.1 mm/rev to 0.3 mm/rev, depth of cut was selected in a range of 0.5 mm to 1.5 mm, and the surface roughness has been done by using 0.4 mm and 0.8 mm nose radius insert.Three types of combinations of feed rate and depth of cut were chosen in order to measure the surface roughness of the machined product.

Mechanical Property Measurement.
Hardness tests were used to determine the strength of a material to judge deformation ability.A standard specimen of 6.4 mm thickness is cut from fabricated composites.The material hardness was tested based on the standard of IS: 1500-205 of "B" scale.The given load is 100 Kgf and ball size is 1.5875 mm (indenter).Flexural strength has been obtained by conducting threepoint bending test (Figure 1(c)) which is made up of D3 steel.The D3 steel contains high carbon and high chromium.The samples are machined as per standards and then we heat treated it by hardening and ageing.Finally it was

Examination of Hardness Test.
The hardness behavior of fabricated both hybrid and monocomposite is shown in Figure 2. From Figure 2(a), it is revealed that the strength of hybrid composite started to increase steadily up to 3% TiB 2 and then increases slowly.This was due to more formation of TiB 2 particles which imported particulate strengthening in the matrix.The strength of Al 7075-3% TiB 2 -1% Gr hybrid composite exhibited 25% more than Al 7075-0% TiB 2 -1% Gr monocomposite.However, the strength of Al 7075-6% TiB 2 -1% Gr hybrid composite exhibited only 3.8% more than Al 7075-3% TiB 2 -1% Gr hybrid composite and 29% higher than Al 7075-0% TiB 2 -1% Gr monocomposite.Therefore, it was decided to stop the addition of reinforcement formation up to 6% TiB 2 particles.Further, the strength of Al 7075-3% TiB 2 (Figure 2(b)) monocomposite produced only 3.5% higher than Al 7075 alloy.Hence, the examination towards the addition of reinforcement to formation of TiB 2 particle beyond 3% in monocomposite was not carried out.Based on the results obtained from Figure 2, it can be concluded that the hybrid composite of Al 7075-3% TiB 2 -1% Gr showed improvement in hardness compared to others.to decrease beyond 3% TiB 2 in situ composites.This was expected to nonuniform embedded TiB 2 particles along with its agglomeration over the matrix.Further, the bending stress of monocomposite (Figure 3(b)) is lower than that of hybrid composite (Figure 3(a)).The bending stress of monocomposite (3%) was around 8.8% higher than monolithic alloy.However, the hybrid composite of Al 7075 + 3% TiB 2 + 1% Gr sample exhibited around 30% higher than monolithic alloy, 19% higher than 3% monocomposite, and 22% higher than 6% hybrid composite.These results also showed that the hybrid composite of Al 7075 + 3% TiB 2 + 1% Gr produced excellent results when compared to other samples.This was expected due to uniform distribution/embedding of 3% TiB 2 particles and 1% Gr particles.

Examination of X-Ray Diffraction Analysis and Optical
Microstructural Analysis.The X-ray diffraction profile analysis of prepared hybrid composite is shown in Figure 4. From Figure 4, the diffraction peaks of TiB 2 particles were observed clearly and the peaks increase as TiB 2 chemical salts content was increased which indicated the increasing of the amount of formation of TiB 2 particles over the matrix.From the XRD analysis, the presence of TiB 2 particles and Gr was conformed in AA 7075 matrix alloy.The Al 7075 peaks were higher because of larger amount of matrix materials present in the fabricated composites.It was observed that there was no TiB 2 peak formation at 0%, while increasing the amount of TiB 2 chemical salts the peak also increased.6% of TiB 2 peaks were higher than the 3% of TiB 2 ; this indicates that the in situ formed TiB 2 particles were thermodynamically stable and the interface between aluminum alloy and TiB 2 particles tends to be free.There was no graphite peak for 1% graphite added sample because the XRD can show only if the amount of any constituent is more than 2%.The optical micrographs of the hybrid composite of Al 7075/% wt.TiB 2 /1% Gr ( = 0, 1.5, 3, 4.5, and 6% wt.) are shown in Figures 5(a)-5(f).Common casting defects such as porosity, shrinkages, or slag inclusion were present in Figure 5(a) and the matrix had large size of grains.While considering Figure 5(b), these defects are decreased due to presence of 1.5% TiB 2 + 1% Gr reinforcements.But the amounts of reinforcements were comparatively low and little amount of grain size starts to decrease.The dark color particles were corresponding to TiB 2 particles and the big grey colour particles were corresponding to Gr.It was observed that the amount of formed TiB 2 particles started to increase corresponding to the increasing of chemical salts.Hence, the formation of TiB 2 particles was conformed and visually observed from microstructures (Figure 5).Figures 5(c) and 5(f) show the presence of 3% TiB 2 particles.This picture shows good bonding strength and uniform distribution of reinforcement in the matrix.However, the formation of agglomeration/nonuniform distributed formed TiB 2 particles can be observed from Figure 5(e) which might have decreased the mechanical properties when the formation of reinforcement goes beyond 3%.Further, the grain size of Al 7075/% wt.TiB 2 /1% Gr ( = 0, 1.5, 3, 4.5, and 6% wt.) is shown in Figure 6.Grain size of 0% reinforcement material shows more size, so it results in possessing of lower strength.While increasing the formation of reinforcement percentages to 1.5, 3, 4.5, and 6% with 1% Gr there was a considerable decrease in the grain size considerably up to 3% and then it started to decrease slowly up to 6%.

Evaluation of Scanning Electron Microscopy (SEM) on
Fabricated Hybrid Composite.The SEM micrographs of the fabricated hybrid composite are presented in Figure 7. General casting defects such as porosity, cracks, and peel-off were seen in the Al 7075/0% TiB 2 composites.While adding the chemical salts for formation of 3% and 6% TiB 2 /1% Gr reinforced hybrid composite, the in situ formed 3% TiB 2 particles were distributed nearly homogeneously in the matrix (Figure 7(b)) compared to 6% TiB 2 particulate hybrid composite (Figure 7(c)).Such kind of particulate distribution is an essential requirement to achieve enhanced mechanical properties of aluminium based hybrid composites.The in situ formed TiB 2 particles and graphite exhibit various shapes such as spherical, hexagonal, and cubic shapes.It was evident from Figures 7(b) and 7(c) that the interface between the TiB 2 and graphite particles and the matrix was clear and TiB 2 particles were well bonded to aluminum matrix.The presence of clear interface can be attributed to the thermodynamic stability of the TiB 2 particles and the formation of particles within the melt itself.When a ceramic particle behaves thermodynamically unstable in the aluminum melt, it produces undesirable compounds at the particle to matrix interface.A pure interface was needed to increase the load bearing capability of the aluminium matrix composites.In general, the increase in local melt temperature due to the in situ reaction causes good bonding between the TiB 2 particle, graphite, and the matrix which was achieved through the present research work.The corresponding EDAX analysis for 6% TiB 2 /1% Gr composite is also shown in Figure 7(d) which conforms the presence of reinforcements and no intermetallic compounds were observed.The fractography images of three-point bend tested samples are shown in Figure 8.With this evaluation of fractography images in SEM analysis as shown in Figure 8, Al 7075-0% reinforcement samples (Figure 8(a)) have more dimples and crack propagation and also it was more ductile in nature.While adding the chemical salts for the formation of 3% TiB 2 -1% Gr (Figure 8(b)) reinforcements to the Al 7075 matrix, it produced less dimples formation and it had good interfacial bonding in between matrix and reinforcements.These hybrid composite materials had changed the small amount ductile nature into brittle nature due to presence of hard ceramic particles.However, 6% TiB 2 -1% Gr hybrid composite had produced more particulate crack and it had larger amount of brittle nature and hence it exhibited decrease in mechanical properties.This was due to presence of more amounts of hard ceramic particles in the Al 7075 matrix material and agglomeration of TiB 2 particles over the matrix.

Evaluation of Turning Behavior in terms of Surface Roughness.
The values of surface roughness at different cutting speeds, feed rates, and depth of cuts while turning of Al 7075 + 0% reinforcement, Al 7075 + 3% TiB 2 + 1% Gr, and Al 7075 + 3% TiB 2 composites, respectively, using carbide insert with 0.4 mm and 0.8 mm nose radius are shown in Table 3 and Figure 9. Surface roughness of all fabricated composite material decreases by increasing the cutting speed from 180 to 240 m/min at the feed rate of 0.3 mm/rev.Similarly while increasing the feed rate and depth of cut values, the surface roughness values start to increase, and this would be controlled by increasing the cutting speed and also each condition of depth of cut, feed rate, the surface roughness decreases with increasing of cutting speed from 180 m/min to 240 m/min, while compared Al 7075 + 3% TiB 2 + 1% Gr composites produce lower value of surface roughness among all other composite with insert of both 0.4 mm and 0.    Figure 11) and a discontinuous chip was observed in graphite reinforced composite (right of Figure 12).Further, for the high rate of feed, depth of cut, and cutting speed, less damage surface (serrations) was observed in the case of graphite reinforced alloy and composite.This was attributed to acicular structure of graphite.This enhances the softness and self-lubricating property of the material.Based on the results, 0.8 nose radius insert tool exhibited good surface finish irrespective of composition and cutting parameters.

Conclusions
The following conclusions can be drawn as the result of the experimental study of AA 7075/% TiB 2 /1% Gr and AA 7075/3% TiB 2 in situ composite on mechanical and machining behavior: (i) The XRD patterns of the prepared AMCs showed the formation of in situ TiB 2 particles without the presence of any other intermetallic compounds.Usually, it may occur during casting which can be identified via XRD.However, it was not observed.To ensure that, EDAX analysis was also performed (Figure 7(d)).(ii) The flexural or bending stress, deflection, flexural or bending strain of AA 7075/% TiB 2 /1% Gr hybrid composite exhibited more value than AA 7075/3% TiB 2 /0% Gr composite due to the presence of hard ceramic particles TiB 2 and graphite particles in the matrix.
(iii) The SEM micrograph shows a homogeneous distribution of TiB 2 particles and graphite particles in the aluminium matrix.The interface between the TiB 2 , Gr particles, and matrix material was clean without the presence of pores and inclusions while comparing to the Al 7075/0% reinforcement material.(iv) The SEM fractography images show that the larger amount of brittle nature contains Al 7075-6% TiB 2 -1% Gr hybrid composite, due to larger amount of hard ceramic particles and 1% graphite particles present in Al 7075 matrix materials.
(v) The surface roughness value of AA 7075/% TiB 2 /1% Gr hybrid composite exhibited higher value with respect to higher spindle speed and feed rate when compared to AA 7075/3% TiB 2 composite and by using 0.8 mm nose radius insert exhibits good surface finish compared to the 0.4 mm nose radius insert.The optimum feed rate and depth of cut were observed as 0.1 mm/rev and 0.5 mm, where the surface roughness values were minimum at 0.8 mm nose radius insert.
(vi) Chip thickness increased when depth of cut and feed rate increased, and discontinuous chips formed as these parameters increased.While adding graphite to the metal matrix composite, more and more discontinuous chips formed.The size of these chips also decreased when the cutting speed, feed rate, and depth of cut increased.
(vii) Less tool damage was observed in 0.8 mm nose radius insert while turning of AA 7075-3% TiB 2 -1% Gr hybrid in situ composite.

3. 6 .
Microtexture of Insert before and after Turning.Figures14(a), 14(b), 15(a), and 15(b) show the optical microtexture of carbide insert before and after turning of AA 7075-0% TiB 2 composite and AA 7075-3% TiB 2 of both with and without Gr in situ composite at highest cutting parameters.The optical inspection of flank face of the cutting inserts showed that more flank wear, nose deformation, and erosion of material over the tool occurred in the case of AA 7075-3% TiB 2 in situ composite when compared to AA 7075-3% TiB 2 -1% Gr hybrid composite.The less damage of flank wear of tool was expected to be due to the presence of Gr particles which might have acted as good tribofilm surface between workpiece and tool.

Table 1 :
Chemical composition of AA 7075 alloy.

Table 2 :
Amount of chemical salts required for formation of TiB 2 .

Table 3 :
Experimental values of surface roughness by using 0.4 mm and 0.8 mm nose radius inserts.The 0.8 mm nose radius insert produces lower value of surface roughness.The reason was expected due to that the contact between the tool and workpiece was more in 0.8 mm nose radius insert and also reduces the tool wear and tool breakdown while increasing value of feed rate and depth of cut values during turning process.