The electrical properties of tin dioxide (SnO2) nanoparticles induced by low calcination temperature were systematically investigated for gas sensing applications. The precipitation method was used to prepare SnO2 powders, while the sol-gel method was adopted to prepare SnO2 thin films at different calcination temperatures. The characterization was done by X-ray diffraction, scanning electron microscopy (SEM), and atomic force microscopy (AFM). The samples were perfectly matched with the rutile tetragonal structure. The average crystallite sizes of SnO2 powders were 45 ± 2, 50 ± 2, 62 ± 2, and 65 ± 2 nm at calcination temperatures of 300, 350, 400, and 450°C, respectively. SEM images and AFM topographies showed an increase in particle size and roughness with the rise in calcination temperature. The dielectric constant decreased with the increase in the frequency of the applied signals but increased on increasing calcination temperature. By using the UV-Vis spectrum, the direct energy bandgaps of SnO2 thin films were found as 4.85, 4.80, 4.75, and 4.10 eV for 300, 350, 400, and 450°C, respectively. Low calcination temperature as 300°C allows smaller crystallite sizes and lower dielectric constants but increases the surface roughness of SnO2, while lattice strain remains independent. Thus, low calcination temperatures of SnO2 are promising for electronic devices like gas sensors.
1. Introduction
Tin dioxide (SnO2) powders and thin films are essential for several applications such as a transparent electrode in panels [1], materials for rechargeable lithium batteries [2], solar cells [3], and gas sensing materials [4]. Due to the remarkable physical and chemical properties, SnO2 has attracted much attention as a gas sensing material. The interactions between SnO2 and neighboring gases (carbon monoxide/oxygen) enable this material as an excellent sensor [4].
The efficiency of the SnO2 gas sensor depends on its particle size, connectivity of atoms, and characteristics of its content. Researchers have shown that the execution of the SnO2 sensor can be improved by reducing the particle sizes of SnO2 in the nanometer length scale [4, 5]. The sensitivity increases rapidly when the particle size is less than 6 nm, considering as twice the thickness of the Schottky barrier [6]. The SnO2 powder and thin films can be achieved by several methods, such as sol-gel process [6], chemical vapor deposition [7], a hydrothermal method [8], and sputtering methods [9]. To control the size of SnO2 particles, there are at least two methods for succeeding. The powder synthesis method is the most common approach requiring standard chemistry apparatus and initial substances. The chemical interaction between reactant and reagent gives the desired product, which appears as colloid or deposit in product solution. Varying concentrations of SnCl4 and calcination temperatures can adjust the particle size [10], while other research works use spraying tin solution under pyrolysis or hydrolysis situation to obtain nanoparticles [11, 12]. The other method for deriving SnO2 nanoparticle is a thin film growth process using various techniques such as dip coating or sol-gel coating [13, 14].
As mentioned in the previous paragraph, the efficiency of the SnO2 sensor is firmly controlled by the crystal structure and particle sizes of SnO2. The precipitation method is a promising technique for controlling SnO2 crystal structure and particle size because it produces high purity powder, nanoparticle size, and easy composition control and is of low cost [3–5, 15]. However, only a few studies have examined crystal structure at low calcination temperature, morphology, and electrical properties in SnO2 powder. Earlier studies reported the features above 400°C calcinations [6,15–17]. The physical and mechanical properties of SnO2 powders may vary with temperatures. Hence, before using nano-SnO2 powders, it is crucial to check the above features at low-temperature conditions. Naseem et al. [18] first reported the lattice strain of SnO2 powder, which can vary due to the solvents used in the synthesis process. [18]. Furthermore, there is no report in the literature about the lattice strain generated between the crystal structure or the lattice mismatch during the phase transformation process. This lattice strain usually produces the internal electric, which helps in sensing behavior due to the variations in energy bandgap. However, sufficient research is required to strengthen the above statement. The main challenge is how to use the nano-SnO2 powder and thin films as a gas sensor in industrial uses.
In the present work, we have examined various characteristics of SnO2 thin films and powders by varying temperature. The crystallite structure, that is, particle size, lattice parameter and lattice strain, morphology, topography and roughness, optical properties, and dielectric property, was explored for achieving a suitable condition to obtain various morphologies of SnO2 nanoparticle for the application of devices in sensors.
2. Materials and Methods2.1. SnO2 Powder
So far, various synthesis methods are being used for preparing SnO2 powders [19, 20]. Here, we have used the precipitation technique to obtain SnO2 nanoparticles [17], and tin tetrachloride pentahydrate (SnCl4∙5H2O) was used as starting materials in the precipitation process. SnCl4∙5H2O (M = 260.7 g/mol MERCK, KGaA, Germany) and NH4OH (25% conc., 35 g/mol, from MERCK, Germany) were used as precursors. First, 26.07 g of SnCl4∙5H2O was dissolved in (gently dropped into) distilled water. Second, 14 g of NH4OH was added dropwise into the distilled water. Then, NH4OH solution was added to SnCl4∙5H2O till the pH becomes 9.0, precipitating milky white Sn(OH)4. Subsequently, the Sn(OH)4 solution was filtered, washed, and dried in an oven at 110°C for 24 hours. The reactions may be written as follows:(1)SnCl4+4NH4OH⟶SnOH4+4NH4Cl(2)SnOH4⟶SnO2+2H2O
The calcination temperature is an important parameter for determining the electrical property of a substance. Hence, SnO2 powder was made in a round-shaped plate by a single axis hydraulic press at 20.5 ± 0.5 MPa pressure. Then, the samples were set into a tubular furnace by varying the calcination temperatures as 300, 350, 400, and 450°C for three hours with a proportion of 3°C/min heating. The density was calculated using weight and thickness. Figure 1 presents the preparation of SnO2 nanoparticles.
The precipitation process of investigated SnO2 powder in this experiment.
2.2. SnO2 Thin Film
Tin-dichloride-dihydrate (SnCl2∙2H2O) was first dissolved in isopropanol, and then deionized water was added to it at a ratio of 0.6 : 6 : 0.4. While adding the deionized water, continuous stirring is required to start the hydrolysis and polycondensation reactions. Besides, 0.05 ml of acetic acid was used as a catalyst. Then, the magnetic stirrer was used for 3 h at 25°C to make the sol completely homogeneous and transparent, as reported by Terrier et al. [21]. The ITO-coated glass substrate [13], which is available in the market, was cut into equal pieces with a similar dimension of 1 × 1 inch2. The substrates were washed with deionized water and acetone to remove dirt. To overcome further impurities attached to the ITO substrate, an ultrasonicator was used to rinse with methanol and deionized water alternatively thrice. Substrates were then immersed into an earlier prepared solution for 5 min and pulled out with a fixed velocity with 3.0 mm/min, and the same procedure repeated ten times to achieve a desired thickness of the film.
2.3. Characterization
The crystal structures were obtained by X-ray diffraction (XRD, Bruker D8 Advance with Eulerian Cradle; CuKα1 with λ = 1.54060 Å, Spain) within the diffraction range of 2θ = 20° to 80° [7, 8]. The diffraction data were recorded at a 3° min−1 scan rate for the analyses of crystal phases [22]. The crystalline size βcrystalline and lattice strain of the sample βstrainn are related to the width βr [23]:(3)βr=βcrystallite+βstrain.
Here, βcrystallinevalues were estimated from the “Scherrer–Gottingen equation.” βcrystalline can be calculated by considering Bragg reflections with diffraction angle 2θ [24]:(4)βcrystallite=KλLcosθ,where K is a constant and considered as dimensionless shape factor (K = 0.89); λ is a wavelength of CuKα radiation. Hence, the lattice strain can be represented as follows:(5)βstrain=ηtanθ,where η denotes the strain of the sample. Thus, the total width of the diffraction peak becomes(6)βr=KλLcosθ+βstrain,(7)βrcosθ=KλL+ηsinθ.
In the graph, βrcosθ against sinθ, one can obtain the lattice strain of the sample η from the slope and the crystallite size L from the intercept Kλ/L.
Scanning electron microscopy (SEM, Hitachi S-3400N, Japan) with an energy-dispersive X-ray spectrometer (EDX, Oxford instrument, UK) was used to investigate the arrangement of atoms in the crystal, particle size, and chemical compositions of SnO2 powders. Gold and carbon were coated onto samples for SEM and EDX analysis, respectively.
The topography and crystallite size of SnO2 powders were investigated by atomic force microscopy (AFM, Nanosurf, Nanosurf Easy Scan 2, Switzerland) at room temperature. The principle and experimental setup of the AFM is described in the literature [25]. A commercial tip cantilever system (Scout 350, Nunano, UK) with spring constant of k = 42 N/m and tip apex radius less than 10 nm was used. Measurements were carried out in noncontact mode acquiring 256 pixels × 256 pixels images with a rate of scanning 2 to 5 Hz.
The permittivity was calculated from the measured capacitance by using a parallel plate method. The vector components of capacitance (C) and dissipation (D) were measured by the instrument. Finally, a computer program was used to calculate the relative permittivity and tangential loss as described from the following equation [26]:(8)ε′=tCPAε0,(9)ε″=tωRPAε0.
Here, t denotes the thickness and A signifies the area of SnO2 samples.
A double beam UV-Vis Spectrophotometer (Biochrom Libra S80, UK) was used to perform the optical properties of SnO2 films at room temperature with wavelength range 200–800 nm. From the reflection R(λ) and transmission T(λ) data, the absorption coefficient (α) was calculated using the following equation [27]:(10)αλ=1tln1−Rλ2Tλ.
Here, t is the thickness of the film. For direct energy bandgap, the above equation can be written as(11)α≈Ahν−Eg,where Eg is the optical bandgap and hν is the energy of a photon. A plot was generated earlier αhν2 versus hν for films at different calcination temperatures [28].
3. Results3.1. Effect of Calcination Temperature on the Crystal Structure of SnO2 Powder
At low calcination temperature, the measured XRD pattern of the product exhibited a very rough signal as several stray peaks appeared over the scan angles. However, some important broad peaks of SnO2 were strong enough to be identified. Figure 2 presents the XRD patterns obtained from the powder SnO2 samples at various calcined temperatures. The sharpness and an increase in peak intensity are attributed to the rise in calcination temperatures by crystallinity [16, 17]. The strong intensity was observed along (110) plane, while comparatively weak intensity was detected along (101) and (211) planes. However, the XRD results of calcination temperature of 400°C and 450°C appeared more crystallite than 300°C and 350°C. The crystallinity of the 300°C regimes indicated an amorphous structure as low intensity and broad peak attribution were found. Since the calcination temperature was increased, the intensity and width of XRD peaks became high and narrow, respectively, suggesting that powder SnO2 obtained enough energy to form a perfect crystalline form.
The XRD patterns of SnO2 powder calcined at different temperatures.
Using equation (7) and Figures 3(a)–3(d), the average sizes of nanocrystalline SnO2 powder were obtained, which could be 45 ± 2, 50 ± 2, 62 ± 2, and 65 ± 2 nm. The data in Table 1 manifest a linear relationship betweenβrcosθ and sinθ. From the experiments, the corresponding lattice strains became 0.0087, 0.0102, 0.0116, and 0.0084 while treated at 300, 350, 400, and 450°C, respectively. Table 1 presents the crystallite size of the sample, which was increased by the rise in calcination temperature. Hence, the continuing growth process was also found in the present research, as well as in the literature [10, 11]. Besides, a rise of the crystalline size of about 5 nm was observed after calcination at 400°C for 3 hours, which explains a small growth trend under such conditions. The XRD data revealed the polycrystalline nature of SnO2 powder, which was fitting well in the tetragonal crystal with a space group P42/mnm. The corresponding lattice parameters were found as a = b = 4.73 ± 0.04 Å, c = 3.18 ± 0.04 Å [2]. The lattice strains were 0.0102 and 0.0116, with 350°C and 450°C, respectively. The strength increases with the rise in temperature, which signifies that the structure might reorient due to the process of phase transformation. The internal electric field was produced between the grains of SnO2 powder and enhanced the electrical property of the SnO2 gas sensor.
Plot of βrcosθagainst sinθof SnO2 calcined at (a) 300°C, (b) 350°C, (c) 400°C, and (d) 450°C extracted from the XRD patterns.
3.2. Effect of Temperature Calcinations on the Morphology of SnO2 Powder
Figure 4 depicts the SEM micrographs of SnO2 powder calcined at different temperatures. At low temperature (300°C), the distribution of SnO2 particles is inhomogeneous, as shown in Figure 4(a), while raising the temperature (400°C) causes an improvement in particle distribution. Besides, Figures 4(b)–4(c) reveal that the crystallite sizes of each sample are uniform, depending on the calcination temperature. It is to be noted that a low calcination temperature takes more energy for crystal growth than high calcination temperature, as reported in the literature [12, 13, 29]. However, the SEM images show that high calcination temperature (400°C and 450°C) helps to form more crystalline states than the lower one (300°C and 350°C); this finding matches with the XRD result [6]. Figure 5 shows various crystallite sizes observed in the calcination temperature of 300°C and 350°C. These approximations obtained from the SEM images and the crystallite sizes within the range of 30 to 60 nm show an excellent agreement to the data presented in Table 1.
The SEM images of investigated SnO2 powder calcined under (a) 300°C, (b) 350°C, (c) 400°C, and (d) 450°C.
Crystallite size approximation obtained from high magnification SEM images of annealed under (a) 300°C and (b) 350°C of SnO2 sample.
The aggregation of the 200–400 nm particles only occurred in the samples prepared at the lower annealing temperature. These nonhomogeneous particles are usually observed when the annealing temperature of a sample was decreased to 300°C–350°C [30]. This is because the lower annealing temperature needs more energy growth than a higher annealing temperature. According to the fact that the SnO2 are crystallizes into the polymorphs, the observed 200–400 nm particles of SnO2 (Figure 5(b)) are composed of rutile type (P42/mnm) and pyrite type (Pa3) phases.
The purification of SnO2 powder investigated by the EDX indicated the atomic weight ratio of Sn by the increase in calcination temperature. At 300°C, the chloride atom left from the precipitation process and dominated over the synthesized crystal (Figures 6(a)). However, the Sn atom was found as a larger weight percentage in other temperatures (Figures 6(b)), as shown in Table 2.
EDX spectra data for SnO2 at calcination temperature of (a) 300°C and (b) 400°C.
The atomic and weight percentages of the mixture of Sn and oxide obtained from the EDX technique.
Calcinations temperature (°C)
Sn element
O element
Weight (%)
Atomic (%)
Weight (%)
Atomic (%)
300
21.78
3.21
—
—
350
75.97
34.76
17.19
58.34
400
78.54
41.26
13.00
50.66
450
74.33
26.46
18.30
48.33
Figure 7 depicts a series of AFM topographs of SnO2 powder with different calcination temperatures. The surface roughness and the crystallite size (40–100 nm) increase by rising calcination temperatures as the atoms obtain enough energy at higher temperatures. There is a probability of recrystallization at higher temperatures as atoms often change their position. This finding is similar to the results reported in the literature [31, 32]. The density and homogeneity of the SnO2 powders were improved after calcination, showing a strong agreement with the results obtained from XRD. Not only does calcination induce an apparent increase in the size of crystal but also it changes the phase content, which is the ratio between rutile (P42/mnm) and pyrite (Pa3) type phases. However, at a low calcination temperature as low as 300°C–450°C, the phase ratio was evaluated from the diffractograms and found to be quite stable (the results not shown here).
AFM topographies with 3D structure of SnO2 films: (a) 350°C (5 × 5 µm2) and (b) 450°C (2.5 × 2.5 µm2) of calcination temperatures.
The size of the crystals increases by increasing the temperature of calcination. However, it is recommended to have a small particle size for gas sensors as a higher surface-to-bulk volume ratio increases the adsorption of gases at the sensor surfaces, leading to enhanced sensitivity. The results shown in Figures 2–7 indicate that the crystallite size of SnO2 powders is improved in the range of 40–100 nm after calcination. Hence, the present samples are promising for sensor applications.
3.3. Effect of Temperature Calcinations on the Dielectric Constants of SnO2 Powder
The electrical features of SnO2 powders were investigated by measuring the dielectric constant at different calcination temperatures. Figure 8 presents the behavior of dielectric properties with the effect of frequency at normal temperatures. The dielectric measurement of nanoparticles is a difficult task, and the present results could influence the apparent porosity. Pressing the SnO2 samples at 30.5 ± 0.5 MPa could eliminate the porosity effect of the dielectric measurement. During the analysis, several LC resonances were noticed on the graphs between dielectric constant and frequency. The resonance might come from the inductance of the wires but was removed before calculation.
Dielectric properties of SnO2 powders with different calcination temperatures as a function of driven frequencies.
The dielectric constant (ε′) decreases abruptly at lower frequencies while achieving a saturation at frequencies above 10 MHz. The inset of Figure 8 shows the saturated ε′ at high frequencies, illustrating ε′ as almost frequency independent and can be explained by the polarization mechanism. The dipole moment changes by varying applied electric field at low frequency, resulting in polarization. But dipole moment did not follow specifically by changing the applied electric field, resulting in a decrease in ε′ at a higher frequency. The values of ε′ obtained in the present research are much lower than the reported values [23, 29], attributing to the inhomogeneity of the dielectric structure. The inhomogeneity could occur due to the presence of grain structure, porosity, crystal defects, and stoichiometry. Figure 9 presents the plot of dielectric losses (ε″) at different calcination temperatures and frequencies. At higher frequency, ε″ decreases and, thus, polarization occur. At 400 Hz, ε″ becomes maximum, indicating the dissipation of samples and forms like loose materials while using in an external electric field.
The dielectric loss of SnO2 powders with different calcination temperatures as a function of driven frequencies.
3.4. Effect of Temperature on the Optical Bandgap of SnO2 Films
Figure 10 presents an optical absorbance of SnO2 nanoparticles at different temperatures of calcination. In the spectra, absorption is high at the lower wavelength region, attributing two sets of wavelengths. A sharp increase in absorption manifests in the first region (200 nm ≤ λ ≤ 250 nm), while, in the second region (250 nm ≤ λ ≤ 290 nm), an abrupt fall in absorption occurs. The average absorbance in the visible region lies within 25–30% by varying the calcination temperatures, while maximum absorbance comes to 38.5% at 450°C. By reducing the calcination temperature, the UV-visible absorbance shifts towards a smaller wavelength due to the decrease in particle size. Furthermore, the smaller sizes of particles can absorb at shorter wavelengths, and, thereby, the bandgap increases, showing a good agreement with the present SEM and XRD data.
The absorption of SnO2 films with different calcination temperatures.
Figure 11 presents the plot of energy of the optical bandgap at different calcination temperatures. The direct bandgap energy (Ed) values can be found from the intercepts with the energy axis. The bandgaps are 4.85, 4.80, 4.75, and 4.10 eV for 300°C, 350°C, 400°C, and 450°C, respectively. Notably, Ed values calculated from the present analysis are higher than those found in the reports [5, 16, 18]. These larger values are achieved due to the variation of the stoichiometry of the concentration of point defects associated with SnO2 films. Furthermore, Ed decreases with the increase in crystallite size, although independent of the lattice strain. A similar trend has been observed in earlier reports [33].
The energy bandgaps of SnO2 films with different calcination temperatures (Touc plot of αhν2 with photon energy in SnO2 thin film).
4. Conclusions
We successfully prepared nano-SnO2 particles by the precipitated method. XRD analysis revealed a tetragonal rutile structure with P42/mnm (136) phase group from the synthesized compounds. The average crystalline size increases from 45 ± 2, 50 ± 2, 62 ± 2 to 65 ± 2 nm due to the increase in calcination temperature from 300, 350, 400, to 450°C, respectively. These results also show the persistence of lattice strain, which is independent of calcination temperature. SEM images show that the average particle size and grain size increased while increasing the calcination temperature. EDX analysis of the samples showed the existence of tin and oxygen in the pure sample. AFM images showed that the rise in calcination temperatures contributes to high surface roughness and large crystallite size. The dielectric constant was much lower than the expected value. The energy bandgap of SnO2 thin films was independent of their lattice strain but decreased with an increase in their crystallite size. Lattice strain was ambiguous and needed further investigation. However, the morphology of SnO2 powder can be altered in terms of particle size and crystal structure by different calcination temperatures, which could improve the sensitivity of the sensor. Hence, the present research caused by shallow calcination temperature should be carried out for future direction.
Data Availability
The data used to support the finding of this study are included within the article.
Conflicts of Interest
The authors declare no conflicts of interest.
MolloyJ.MaguireP.LavertyS. J.McLaughlinJ. A.The reactive ion etching of transparent electrodes for flat panel displays using Ar/Cl [sub 2] plasmas1995142124285428910.1149/1.20484982-s2.0-0029492990KöseH.AydinA. O.AkbulutH.Sol-gel synthesis of nanostructured SnO2Thin film anodes for Li-ion batteries2012121122722910.12693/aphyspola.121.2272-s2.0-84856103782ChappelS.ZabanA.Nanoporous SnO2 electrodes for dye-sensitized solar cells: improved cell performance by the synthesis of 18nm SnO2 colloids200271214115210.1016/s0927-0248(01)00050-22-s2.0-0036466461MillerT. A.BakraniaS. D.PerezC.WooldridgeM. S.GeckelerK. E.EdwardNanostructured tin dioxide materials for gas sensor applications2006Rosenberg, TX, USAAmerican Scientific Publishers124ArshakK.MooreE.LyonsG. M.HarrisJ.CliffordS.A review of gas sensors employed in electronic nose applications200424218119810.1108/026022804105259772-s2.0-1942468809MishraS.GhanshyamC.RamN.SinghS.BajpaiR. P.BediR. K.Alcohol sensing of tin oxide thin film prepared by sol-gel process200225323123410.1007/bf027111592-s2.0-0036603441FangT.-H.ChangW.-J.Nanomechanical characteristics of SnO2:F thin films deposited by chemical vapor deposition200525251863186910.1016/j.apsusc.2005.03.1512-s2.0-27944463158TanL.WangL.WangY.Hydrothermal synthesis of SnO2 Nanostructures with different morphologies and their optical properties2011201111052987410.1155/2011/5298742-s2.0-80052670357ChowdhuriA.HaridasD.SreenivasK.GuptaV.Mechanism of trace level H2S gas sensing using rf sputtered SnO2 thin films with cuo catalytic overlayer20092454054810.21307/ijssis-2017-366AcarbasO.SuvaciE.DoganA.Preparation of nanosized tin oxide (SnO2) powder by homogeneous precipitation200733453754210.1016/j.ceramint.2005.10.0242-s2.0-33947145233BrinzariV.KorotcenkovG.GolovanovV.SchwankJ.LanttoV.SaukkoS.Morphological rank of nano-scale tin dioxide films deposited by spray pyrolysis from SnCl4·5H2O water solution20024081-2515810.1016/s0040-6090(02)00086-x2-s2.0-0037012548HiedaK.HyodoT.ShimizuY.EgashiraM.Preparation of porous tin dioxide powder by ultrasonic spray pyrolysis and their application to sensor materials2008133114415010.1016/j.snb.2008.02.0022-s2.0-46449138035RayS. C.KaranjaiM. K.DasGuptaD.Tin dioxide based transparent semiconducting films deposited by the dip-coating technique19981021-2738010.1016/s0257-8972(97)00561-62-s2.0-0032046357CobianuC.SavaniuC.BuiuO.Tin dioxide sol-gel derived thin films deposited on porous silicon1997431-311412010.1016/s0925-4005(97)00196-22-s2.0-0031224614ZhaoQ.-R.Controllable synthesis and catalytic activity of SnO2 nanostructures at room temperature20091951227123110.1016/s1003-6326(08)60433-12-s2.0-76449099703JainK. V.KumarP.VijayY. K.Preparation of nanostructure ZnO- SnO2 thin films for optoelectronic properties and post annealing influence20127215751577SongK. C.KangY.Preparation of high surface area tin oxide powders by a homogeneous precipitation method200042528328910.1016/s0167-577x(99)00199-82-s2.0-0034140551NaseemA.ShakeelK.RichaB.AnsariM. M. N.“Study of lattice strain and optical properties of nanocrystalline SnO220181953030063SivashanmugamA.PremkumarT.GopukumarS.RenganathanN. G.Wohlfahrt-mehrensM.GarcheJ.Synthesis and electrochemical behaviour of tin oxide for use as anode in lithium rechargeable batteries200535111045105010.1007/s10800-005-9043-52-s2.0-27144467438MurayamaN.IzuN.ShinW.MatsubaraI.Preparation of SnO2 nanosized powder by precipitation method with nano-mixing of carbon powder2005113131633033210.2109/jcersj.113.3302-s2.0-18844431864TerrierC.ChatelonJ. P.RogerJ. A.Electrical and optical properties of Sb:SnO2 thin films obtained by the sol-gel method19972951-29510010.1016/s0040-6090(96)09324-82-s2.0-0031074747BabarA. R.ShindeS. S.MoholkarA. V.RajpureK. Y.Electrical and dielectric properties of co-precipitated nanocrystalline tin oxide2010505274374910.1016/j.jallcom.2010.06.1312-s2.0-77955921911SuryanarayanaC.GrantM.19981stNew York, NY, USANorton Springer Science + Business Media, LLCKroonR. E.Nanoscience and the scherrer equation versus the ‘Scherrer-Gottingen equation'20131095/61210.1590/sajs.2013/a00192-s2.0-84879393800KhaenamkaewP.BdikinI. K.KholkinA. L.MuensitS.Local piezoresponse and ferroelectric property of sol-gel Pb(Zrx,Ti1-x)O3 film20083015963Keysight Technologies. Basics of Measuring the dielectric Properties of materials. Application note. Published in USA. 5989-2589EN [Internet]. January 3, 2019. [cited 2019, July 17] Available from: http://www.keysight.com/find/materialsUysalB. Ö.Akkaya ArıerÜ.Ö.Structural and optical properties of SnO2 nano films by spin-coating method2015350747810.1016/j.apsusc.2015.04.0232-s2.0-84938744855TaucJ.Absorption edge and internal electric fields in amorphous semiconductors19705872172910.1016/0025-5408(70)90112-12-s2.0-0014832699VarshneyD.VermaK.Effect of stirring time on size and dielectric properties of SnO2 nanoparticles prepared by co-precipitation method2013103421622210.1016/j.molstruc.2012.10.0492-s2.0-84872921103KöseH.AydinA. O.AkbulutH.The effect of temperature on grain size of SnO2 Nanoparticles synthesized by sol-gel method2014125234534710.12693/aphyspola.125.3452-s2.0-84896849504UtriainenM.LattuH.ViirolaH.NiinistL.ReschR.FriedbacherG.Atomic force microscopy studies of SnO2 thin film microstruc tures deposited by atomic layer epitaxy20001331-411912310.1007/s0060400700802-s2.0-0000502719GuiT.HaoL.WangJ.Structure and features of SnO2 thin films prepared by RF reactive sputtering20108S113413610.3788/col201008s1.0134Al-GaashaniR.RadimanS.TabetN.DaudA. R.Optical properties of SnO2 nanostructures prepared via one-step thermal decomposition of tin (II) chloride dihydrate2012177646247010.1016/j.mseb.2012.02.0062-s2.0-84858796096