An Optimization of Particle Size and Additives of Slip Cast Alumina Samples to Reduce Warpage and Porosity

Alumina body densification using slip casting was investigated with low warpage rates. In order to optimize slurry and sintering, 1600 ° C has been used. As a starting material, three types of alumina were used. Alumina has been used in conjunction with PMAA, and carboxymethyl cellulose in order to prepare the slurry. It was found that warpage rates were reduced when coarser particles were included in the composition. An acid treatment of the slurry was carried out in order to improve densification of the alumina body and to reduce warpage. This study examines the microstructure of a sintered alumina body. In the investigation, it was found that preparing a dense product reduced porosity and warping rate by 1.1% and 4%, respectively.


Introduction
Al 2 O 3 , commonly referred to as aluminum oxide, is a highperformance ceramic material that possesses excellent thermal, chemical, and physical properties. Additionally, alumina is used as abrasives, rebricks, and IC packages. Alumina is mainly produced by the Bayer method using bauxite, which delivers more than 45 million tons to the world each year. e corundum/sapphire super lattice illustrates the period of Al 2 O 3 . For electronic packaging, corrosion resistance ceramics, erosion-resistant ceramics, and erosion-resistant ceramics, Al 2 O 3 is usually utilized and concentrated in high temperatures. e most thermodynamically stable form of alumina is the polymorphic phase α-Al 2 O 3 . ere are 5.2 cell sides and a rhombohedral plane angle of 55°for each unit cell of α-Al 2 O 3 . In the Bayer process, Al 2 O 3 powders have the greatest purity of 99.6-99.9%, which makes them suitable for assembling refractories, spark plugs, and substrates of coordinated circuits [1][2][3].
Rather than having to rely on post-process activities, such as inspection and determining defective items, process control is becoming increasingly important in managing the manufacturing process [4]. Traditional ceramics are manufactured by slip casting, since it produces muddled shapes with signi cant thickness at low cost. Usually, slip casting technology involves a combination of particle isolation and water removal procedures. To limit the drying exertion the water content of a slip ought to be set as low as could really be expected. Ideal (low) thickness prompts a surpassing green thickness and low shrinkage after resulting sintering. Green strength increments with expanding de occulated (binder) content [5].
An optimal amount of binder should be used, a high amount of binder may lead to the formation of porous material. To get fully de occulated slurry dispersant should be used. A well-dispersed suspension can fabricate green bodies and sintered samples with high density [6]. Grain-size distribution is perhaps of the most crucial parameters in the e ective sintering of alumina. e packing behaviour is one more basic parameter for sintering [7]. High densities and little grain sizes of alumina ceramics results in high strength and better mechanical properties [8].
e powder particle shapes may be needle-like, spherical, plain, platelet, or equiaxial. As compared to all other shapes the spherical-shaped powder of various sizes results in the best packaging capacity. e high-level physical and chemical properties of alumina ceramic request demand ultrafine and high purity alumina powder [9]. Due to their large surface area, fine ceramic particles often form agglomerates during processing, resulting in suspensions with extremely high viscosities and poor packing properties. We have therefore added coarser particles to reduce warpage. In order to achieve reduction in warpage and porosity, we have varied the particle size, amount of fines, amount of coarses, amount of solids, amount of dispersant, and the water/plaster of Paris content of the molds.

Experimental
Experiments were carried out on raw alumina powders A (particle mean size 0.77356 µm), B (particle mean size 0.85156 µm), and C (particle mean size 3.69587 µm). As part of this study, Particle size (PS) and Particle Size Distribution (PSD), of the starting powders were manipulated, and the drying-shrinkage behavior of the powders was evaluated to assist us in reducing the warpage rate at the green stage. For slurry-based colloidal processing, high powder loading is critical to obtain a high packing density of the green body, which facilitates minimal drying and sintering shrinkage, reducing the final component warpage [10]. However, high powder loading is complex for fine powders due to the high tendency of agglomeration, so coarser particles were also used. Weights of the above materials were carefully taken based on their stoichiometric composition (99 wt% Al 2 O 3 ). e above composition was mixed with CMC and PMAA at concentrations ranging from 0.1 to 0.6 weight percent. To generate enough repulsive force, a dispersant agent is necessary to build up an electrical double layer and, in turn, to increase the particle's dispersibility [11]. A low warpage rate was also achieved by varying the solid loading. By varying the coarse and fine weight percentages of the raw material, the composition has also been altered. Prior to the preparation of the slurry, all batches were calculated. After 12 hours of stirring at 1200 rpm, they are homogeneously mixed and milled.
In an aqueous medium, alumina slurries with high concentrations are of great importance because it is the rheological properties that determine their stability from flocculation [12]. To achieve a stable and uniform dispersion, the type and amount of dispersant in slurry formation are crucial [13]. It is the optimal concentration of the dispersant that produces dispersed slurry with easy flow ability. In a well-stabilized suspension, the dispersant should be used in an optimum amount to provide the most surface charge [14]. Due to the bridging flocculation that occurs in suspensions with less than optimal concentrations of dispersants, viscosity increases with less than optimal concentrations of dispersants. As dispersant concentration exceeds the optimum concentration, excess non-adsorption dispersants reduce suspended particle zeta potentials by compressing double layers by absorbed counter ions [15]. Slurry processes have a major impact on colloidal microstructure and mechanical properties as a result of the quantity of polymer dispersant used. When air bubbles are entrapped during milling, the slurry's high viscosity will cause them to be difficult to remove, eventually resulting in defects [16,17]. It is therefore important to optimize the amount of dispersant. e prepared alumina slurry is poured into the designed mold. e characteristics of the mould played an important role in the reduction of green warpage. Variation in the water to the plaster ratio has a direct influence on product characteristics [18]. According to Lambi and Adegoke [19], the hardness, strength, durability, and weight are directly related to the mix ratio of water and plaster used in producing the mould. e percentage of water absorption for the samples prepared from different water to plaster ratios is determined. POP mould with an average absorption water level (74.52%) was used. In order to fill the hollow, the continuous slurry is added since the slurry immediately absorbs water from the plaster mould. As the mould absorbs no more water, the slurry begins to harden and becomes hard, then the drain casting is done. After 2 hours molding is done. Due to shrinkage, the green product comes out of the plaster mould automatically once it leaves the wall. Microstructures of green plants are commonly characterized by (i) Archimedes immersion, which measures density; and (ii) electron microscopy, which measures qualitative properties. A period of around 24 hours was required for the green products to be dried under atmospheric conditions at the RT. At this stage, some water is removed.
A period of 24 hours was then needed for the green product to completely dry ( * 99%) in the oven at 110°C. As soon as the alumina specimen and dried sample are polished with sandpaper, impurities are removed from their surface. e green warpage has been reduced by all possible means; after this sintering of green products is done at under 1600°C temperature with varied soaking time. Heat is used in the sintering process to achieve the desired microstructure of the green body. Based on the complexity of the starting material, the stage may involve quite a few changes [20,21].
A Siemens D-500 powder diffractometer with Cu K-radiation was used for X-ray diffraction (XRD) to identify the phases in sintered samples. A 5°C/min heating rate was used to prepare the powders from the compacts for XRD analysis. e bulk density of the samples was measured by the Archimedes principle. Zwick 1445 universal testing machine was used to measure the modulus of rupture (MOR) of rectangular samples sintered at 1600°C. e samples were subjected to 10 physical tests, with the results averaged. Polished and thermally etched samples were examined using the Cambridge Instruments-5526 scanning electron microscope after being polished and thermally etched for 1 h at a temperature lower than the sintering temperature. Figure 1 shows the SEM and XRD image of as received Al 2 O 3 powder particles. e Aumina powder particles are in uneven shape. XRD pattern corresponded to pure alpha Al 2 O 3 phase as per alpha phase JCPDS (Match Entry C 96-100-0033) [22].

Results and Discussion
It is possible to determine the average particle size and the range of particle sizes based on the particle size distribution. Table 1 shows the particle size distribution of the raw alumina powder namely fines, medium, and coarse respectively. e particle size measurement reveals bi-modal size distribution which is depicted in Figure 2.
Several factors contribute to slip casting performance, including particle density, homogeneity, and rheological behavior. e specimen was manufactured directly from the suspension of ceramic powders [23]. Solid loading, particle shape, and particle-particle interaction forces control the suspension properties and the structure of slip cast bodies [24]. A slurry's structure is commonly responsible for shear-thinning behavior. A higher specific surface area of fines coupled with a dominant role played by surface forces explains the more pronounced shearthinning characteristics of fines. As the shear rate increased, the coarser particles became progressively thicker, whereas the fines were shear-thinning over the entire shear rate range. Hydrodynamic interactions between particles become more important at high shear rates. A rise in PS can even lead to their dominance, resulting in a tendency for the particles to become more individualized. It is also important to note that coarse particles need to have a greater average separation distance in order to slide over one another [25]. Increasing alumina powder coarseness increased the green density, reaching a maximum on alumina powder coarsening. Particle packing in suspension results in a gradual decrease in viscosity with increasing particle size. Table 2 shows different compositions by varying fine and medium. e rheology of a slip does affect production. For optimal slip-casting performance, this factor is just as crucial as the formula. For a better understanding of the formula's rheological performance range, viscosity and thixotropy should be evaluated simultaneously. Rheology can help optimize production yields when combined with raw material selection and percentage.
Composition III is found to be the ideal composition for the fabrication of the alumina Specimen by analysing the rheology (Table 3) of the slip prepared by each composition.
It influences the rheology of the suspensions, as well as the packing behavior during slip casting, depending on the stabilizing mechanism. Solid loading in suspension always decreases total shrinkage. is may be due to both wet and dry bodies, the particles are surrounded by thinner hydrated layers [26]. In the formulation of the alumina slurry, the identification of an optimal range of solid loading is of great importance. A large amount of powder caused high friction and liquid phase migration while lower solid loading was unable to form the casting shape. Maximum solid loading has been identified by varying the solid loading and evaluating the results. Table 4 shows different solid loadings and their results.
One can observe from Table 4 that the density of a homogeneous slurry increases with the solid content, but it also depends on the flow behavior. e flocculation of alumina particles occurs in a less viscous slurry or in a highly viscous slurry. e particles come close enough to hinder each other's movement because of the attractive forces caused by high alumina loading. e dispersed particles start to agglomerate as a result of an insignificant repulsive force acting among them. e gravity forces begin to settle particles in less viscous slurries (slurries with high solid content) at optimal conditions. To reduce agglomeration and warpage dispersant has to be introduced in the slip. PMMA generates highly charged surfaces of the particles that will result in a strong double layer repulsion and decreases the electrostatic attractive forces [27]. is means that it is possible to achieve stable aqueous colloidal dispersion. Since most of the changes of alumina particle surface charge have been nearly beside the isoelectric point at the very limited range of pH 9.8. Table 5 shows that from viscosity measurements, the amount of dispersant agent significantly contributed to decreasing the viscosity and determining the effective concentration of the dispersant that allows the viscosity to reach a minimum steady, and thereby analysing the viscosity and shear rate relationship we may come to understand the optimal use of a dispersing agent in the slurry.       Approximately 2°C per minute is added to all samples during sintered at 1600°C. Instead of melting, the powder is joined together and its porosity is reduced, which is what is called densification in the fabrication process, which is performed by atomic diffusion in the solid state. e term "solid-state sintering" is often used to describe this type of sintering. A consolidated mass of particles reduces its surface free energy during sintering. Atom diffusion can reduce energy by causing the body to densify. Densification is improved with longer soaking times. Finally, composition III has been prepared by adding an optimal amount of binder (CMC), 0.3% of PMAA, and the specimen was fabricated with low warpage and porosity. e physical and mechanical properties of the specimen were also analyzed.

Advances in Materials Science and Engineering
Flexural strength value gives a material's ability to resist deformation under load [28]. For measuring flexural strength, three-point bending was used. e value obtained for composition III and found to be 418 MPa. Table 6 shows the physical and mechanical properties of the specimen made of composition III.
SEM was used to study the microstructural behaviour of the alumna samples are presented in Figure 4. In comparison of the SEM images, composition 3 is clearly characterized by close packing and smaller grain sizes, as well as the higher sintered density. In contrast to the other composition cast samples, there is a better coordination among the smaller grains and greater interparticle spaces between the coarser grains, resulting in higher densification [22].   Advances in Materials Science and Engineering

Conclusion
Slip casting is used in this study to create an alumina body that contains the inherent packing structure of powder particles. A slurry flowing with water has been observed to have an effect on density and microstructure. An excessive amount of water and a low amount of water in the slurry cause particles to flocculate, resulting in an inhomogeneous slurry. Slurry preparation with 45% water results in homogeneous slurries. Changing the composition by adding coarse particles which act as a skeleton and increase the stability of the product. Sintering product density is observed to be affected by soaking time. e densification improves and the porosity decreases as the holding time increases.
A better density can be achieved by better densification of the final body due to the homogeneous grains created by the acid treatment. We were successful to minimize the porosity up to 1.1%. Initially, the warpage rate was 36% and it has been reduced up to 4% by preparing a dense product. Measurements of slurries' viscosity based on shear rate indicated the state of dispersed alumina particles in aqueous media and contributed to the effective amount of dispersant agent required. Rheological measurements could be proposed as a route for designing the casting technique that causes particles to dissociate. Consequently, the stability of suspensions improves leading to achieving particle packing and high green bulk density of cast body with more uniform microstructures. e mechanical properties of the alumina body also improve as it becomes denser. e flexural strength is found to be 418 MPa. As a result of increasing the sintering temperature and soaking time, alumina is densified by controlling the particle size and water content. In addition to densifying and homogenizing grain size, acid treatment also produced dense, compact alumina bodies.

Data Availability
Data is available with the corresponding author. Will be submitted upon request.

Conflicts of Interest
e authors declare that there is no conflicts of interest.