Impregnation of Silver Nanoparticles onto Polymers Based on Sugarcane Bagasse for the Remediation of Endocrine Disruptor–Bisphenol A from Water

This present study introduces a contemporary innovation of synthesized polymer–silver nanoparticle nanocomposite adsorbent based on sugarcane bagasse (AgNP-SB-βCD) for the sequestration of emerging micropollutant–bisphenol A from water matrix. Batch adsorption mode was carried out to assess the effectiveness of AgNP-SB-βCD nanocomposites towards eliminating bisphenol A (BPA). Characterization techniques including SEM, FTIR, and XRD have confirmed the successful incorporation of silver nanoparticles (AgNPs) onto bagasse–polymer. At 25°C, pH 7, and contact time of 120 min, the nanocomposites had a maximum uptake capacity of 158.4 mg g-1on BPA. The equilibrium isotherm of BPA on AgNPs-SB-βCD has fitted effectively with Langmuir model while the adsorption kinetics conformed to pseudo-second order. The adsorption phenomenon was controlled mainly by physisorption (via host–guest inclusion van der Waals bonding and pore filling effect). In addition, oxidative degradation of BPA by AgNPs-SB-βCD could marginally contribute the removal of BPA due to oxidative dissolution of AgNPs at pH 7. The thermodynamic results substantiate the spontaneity and exothermic behaviors of the adsorption phenomenon. The polymeric nanocomposite adsorbent was regenerated five times (using 75% ethanol) without considerable loss of its adsorption capacity. This authenticates its reusability and consistency performances; accordingly, it can be a market competitor adsorbent for the treatment of water contaminated with BPA.


Introduction
Water is amid the most fundamental natural resources in the life of living organisms, and therefore, it must be properly consumed to prevent future clean water scarceness [1,2]. In recent decades, the incident of emerging micropollutants (EMPs), including bisphenol A (BPA) in water bodies, has become a growing concern due to their toxicological consequences on aquatic organisms, human health, and ecosystem [3][4][5]. For humans, the consumption of water tainted with BPA can result a number of health complications including renal disorders [6], neurological problems, cardiovascular diseases, cancer, infertility, and sexual dysfunction [7].
BPA is among the primary manufactured and consumed chemicals worldwide [6,8]. Since the last few decades, the utilization of BPA in the industries for the fabrication of epoxy resins and polycarbonate plastic products has been observed to augment significantly. This has led to generation of immense amount of BPA wastewaters from the industries. Intentionally, most of these wastewater effluents are released to the environment without being completely treated; as a result, it causes adverse effects to the ecosystem [9].
In general, many researchers have focused on synthesized novel adsorbents as promising materials for remediation of water and wastewater to avoid human health complications and deterioration of the ecosystems [25]. Therefore, different adsorbents have been so far synthesized to adsorb BPA from water systems. These include the adsorbent based on natural materials, carbon and graphene, polymers, composite materials, nanomaterials, and agricultural waste materials [8]. However, a portion of adsorbents have demonstrated poor adsorptive and regeneration performances on bisphenol A [26], while some possess poor mechanical behaviors and are susceptible to extreme temperature and pH of the water surroundings. These limitations pose great challenges to the adsorbents for remediation of BPA and other noxious pollutants in water and wastewater. To surmount this challenge, in recent times, there has been an increasing concern on the application of polymer nanocomposite adsorbents (as a new class of adsorbents) for the treatment of noxious contaminants from aqueous systems. These advanced polymer nanocomposites are economical, highly stable, and effective adsorbents on removing a broad spectrum of chemical and biological pollutants [27]. They possess beneficial characteristics including dimensional flexibility, functionalities, film forming capability [28], medium mobility, porosity behaviors, and sturdy mechanical characteristics [29][30][31]. Thus, in this present research, we have reported for the first time the amalgamation of silver nanoparticles onto polymers based on sugarcane bagasse and applied for the sequestration of emerging micropollutant-bisphenol A from water. Incorporation of silver nanoparticles was done to increase the surface features, stability, and functional moieties on bagasse-polymers, whereby all these properties are accountable for increasing the uptake of bisphenol A.
Herein, the colloidal silver nanoparticles (AgNPs) were synthesized using reduction method, and then, a wet impregnation protocol was performed to immobilize AgNPs onto bagasse-β-cyclodextrin polymer to form novel bagasse-polymer-silver nanoparticle nanocomposites (AgNP-SB-βCD). These nanocomposites were characterized using various analytical techniques and then assessed their adsorptive performance towards bisphenol A in water matrix.  46.07 g mol −1 ), sodium sulfate (Na 2 SO 4 , 142.04 g mol −1 ), hydrochloric acid (HCl, 36.458 g mol −1 ), and sodium dihydrogen phosphate (NaH 2 PO 4 , 119.98 g mol −1 ) were used in this study. All chemicals and standard solutions were of highest purity and applied as delivery without additional modification and were purchased from Macklin Biochemical Co., Ltd (Shanghai, China), Loba Chemie Pvt. Ltd (Mumbai, India), Kas Medics Ltd, and Lab Equip Ltd (Dar es Salaam, Tanzania).

Preparation of the Novel Bagasse-Polymer-Silver
Nanoparticle Nanocomposites and Bisphenol A Solution. Optimization protocols were implemented to synthesize bagasse-polymer-silver nanoparticle nanocomposite (AgNP-SB-βCD) adsorbent. Herein, sugarcane bagasse (SB) material was thoroughly cleaned with water to eliminate unwanted materials and then rinsed with distilled water to remove other inorganic impurities. The clean SB was cured for over 12 h at 60°C and then milled to particle size of 150 μm. An accurate 1.5 g of SB was placed in vessel containing a solution mixture prepared by mixing CA (4.5 g), β-CD (9.0 g), and NaH 2 PO 4 (0.95 g) in 200 mL of distilled water. The mixture was agitated and cured at 180°C for 30 min to obtain bagasse-β-cyclodextrin (SB-βCD) polymers as explained by Mpatani et al. [26]. Then, preparation of colloidal silver nanoparticles (AgNPs) by reduction method was performed in fume hood with minor modification as described by Abdelwahab and Shukry [32]. 0.08 mol L -1 of AgNO 3 solution was prepared and added (while stirring) to a solution obtained by incorporating 1.0 g of PVP into 200 mL of ethanol. Then, N 2 H 4 ·H 2 O solution (0.02 mol L -1 ) was added in drops with constant stirring to the solution containing AgNO 3 and PVP. The solution was altered to pH 8 by 0.1 mol L -1 NaOH. Then, the formed solution was cured at 60°C under constant stirring till the solution color changed to yellow (AgNP colloidal solution). The SB-βCD polymer material was then introduced into colloidal solution and agitated at 120 rpm for overnight to allow sufficient amalgamation of AgNPs into polymer network of SB-βCD. The resulting polymeric nanocomposites were then filtered and cleaned with distilled water and cured at 60°C for 4 h. The AgNP-SB-βCD nanocomposite adsorbent was then stored in the container and used for adsorption process.
A concentrated solution of bisphenol A (BPA, 1000 mg L −1 ) was prepared by placing 1 g of BPA into a 1 L graduated flask containing a methanol : water solution (1 : 1 ratio). BPA working solutions were obtained by diluting a concentrated BPA solution using distilled water to the desirable concentration. BPA solutions were regulated to pH of 2.0 to 11.0 using 0.1 mol L -1 of HCl or NaOH solution.  (1) and (2), respectively.

Characterizations of Polymeric
In general, 0.01 g of AgNP-SB-βCD nanocomposites, 100 mg L of BPA, 10 mL of BPA, pH 7.0, adsorption temperature of 25°C, and contact duration of 120 min were used as the optimal experimental parameters for adsorption and regeneration studies.

Kinetic and Isotherm
Determination. Adsorption isotherm and kinetic can assist in understanding the adsorption affinity, surface chemistry of the adsorbent, the rate, and mechanisms that control adsorption phenomenon [33]. Herein, pseudo-first-order (PFO) and pseudo-second-order (PSO) models were employed to determine the kinetic study, while Freundlich and Langmuir models were employed to evaluate the equilibrium isotherms [1,34]. The expressions of isotherm and kinetic models are presented in Table 1.

Thermodynamic
Approach. The domination of temperature on BPA uptake was examined at 25, 35, and 45°C. This thermodynamic study can help to understand the adsorption behavior, interaction, and mechanisms involved [26]. The Gibbs free change (ΔG 0 ), change in entropy (ΔS 0 ), and standard enthalpy of the reaction (ΔH 0 ) were resolute using the subsequent equations.
where K d (L mg −1 ) is the partition coefficient of the least BPA concentration, q e (mg g −1 ) is the uptake capacity at equilibrium, C e (mg L −1 ) is the equilibrium mass concentration of the BPA, T (K) is the adsorption temperature, and R (8.314 J mol −1 K −1 ) is the molar gas constant. The Van't Hoff equation (Equation (5)) was employed to find ΔS 0 and ΔH 0 from the intercept and slope by sketching a graph of ln K d versus 1/T.

Regeneration
Approaches. Three desorption solutions (0.1 M NaOH, 0.1 M HCl, and 75% ethanol) were used to assess the adsorption performance (effectiveness, firmness, and reusability) of nanocomposite adsorbent towards decontaminating bisphenol A from water systems. Desorptionregeneration analysis is one of the important adsorption procedures which can be applied to define the economical and environmental perspective of the adsorbent [35]. In this study, desorption and regeneration procedures were carried out in quintuplicate. 0.01 g of AgNP-SB-βCD adsorbent was put into 50 mL Erlenmeyer flask having 10 mL of 100 mg L −1 BPA solution with pH 7.0 and agitated at 140 rpm for 120 min. After equilibrium time (120 min), the nanocomposite adsorbent loaded with BPA was then separated by centrifugation and thoroughly washed with distilled water and dried up at 60°C for 8 h. A dried AgNP-SB-βCD was weighed up and put into Erlenmeyer flask having 10 mL of desorption solution. The flask was shaken in a water bath with rotation speed of 140 rpm at 25°C for 120 min. AgNP-SB-βCD sample was centrifuged, cleaned with distilled water, and cured at 60°C for 8 h. The desorption solution containing BPA was then measured at 276 nm to calculate the BPA concentration desorbed. These approaches were carried out independently to all desorption solutions (0.1 M NaOH, 0.1 M HCl, and 75% ethanol). The desorption effectiveness (d) and regeneration effectiveness (r) of AgNPs-SB-βCD were calculated from Equations (6) and (7), respectively.
where m d is the weight (g) of AgNPs-SB-βCD desorbed, m 0 (g) is the weight of the BPA left over on the AgNPs-SB-βCD before desorption, q 0 (mg g −1 ) is the uptake capacity of

Adsorption Science & Technology
AgNPs-SB-βCD in the initial running experiment, q n (mg g −1 ) is the uptake capacity of AgNPs-SB-βCD after reused, and n is the sum total of regeneration cycles performed.
2.6. Statistical Data Approach. Adsorption isotherm and kinetic results were accomplished using nonlinear regression in Origin 8.5.1. Microsoft excel 2016 was applied in advance to analyze the data. All tests were carried out in triplicates (with the exception of regeneration analysis which was done in quintuplicate), and the results were expressed as mean ± standard error.

Results and Discussion
3.1. Characterization of AgNP-SB-βCD Nanocomposite Adsorbent. Taking into consideration that adsorption process is a surface incident, the nature of surface chemistry and structure of adsorbent can considerably influence the uptake of pollutants from water systems. The possession of surface features (such as functional groups, pores, particle sizes, and higher surface area) on adsorbent can attribute to the removal of BPA [20]. Herein, characterization of AgNP-SB-βCD nanocomposites was performed, and the results obtained are discussed as follows: 3.1.1. Point of Zero Charge. Determination of adsorbent point zero charge (pH pzc ) is imperative as it helps to under-stand the surface charge of adsorbent and an appropriate pH medium that suit adsorption process [1]. Analysis of pH pzc of AgNPs-SB-βCD was carried out with some modification using drift method as described by Doczekalska et al. [36]. As shown in Figure 1, AgNP-SB-βCD nanocomposites have pH pzc of 4.4. This indicated that, at pH solution < pH pzc (acidic medium), the AgNP loaded onto nanocomposites destabilized and aggregates causing lower uptake of BPA. However, at pH solution > pH pzc , the embedded AgNPs existed into two forms: oxidative dissolution state at neutral pH medium or stable suspension at alkaline condition [37,38]. The AgNPs-SB-βCD in the neutral pH solution had higher removal capacity towards BPA due to the occurrence of both adsorption and oxidative degradation of BPA.
3.1.2. FTIR Examination. FTIR analysis was carried out to identify the functional groups that are accountable for adsorption of bisphenol A onto polymeric nanocomposites. The change of band position and intensities of SB-βCD polymer after impregnation process were considered to confirm the successful incorporation of AgNPs onto bagasse-polymer. As appeared in Figure 2, the band intensity of AgNP-SB-βCD spectrum had lessened due to the integration of AgNPs. Moreover, the peak corresponding to the stretching vibration of -OH has slightly decreased from 3420 cm -1 (SB-βCD) to 3410 cm -1 (AgNPs-SB-βCD). This suggests that there was an interaction (during

Model Equation Description
Pseudo-first order q t = q e 1 − e −k 1 t k 1 (min −1 ) is the specific rate constant of PFO; q e or q t (mg g −1 ) are the uptake capacity at equilibrium or any time t.
Pseudo-second order q t = k 2 q 2 e t/1 + k 2 q e t k 2 (g mg −1 min −1 ) is the PSO reaction rate coefficient.
Langmuir q e = q m K L C e /1 + K L C e q m is the highest uptake capacity (mg g −1 ); K L is associated to the adsorption attraction of the binding energy (L mg −1 ).
Freundlich q e = K F C 1/n e K F is the Freundlich constant (mg g −1 )/(mg L −1 ) n and 1/n is the heterogeneity factor indicating the affinity of the BPA to the AgNP-SB-βCD nanocomposite.  Figure 3. The surface morphology of SB is appeared to be smooth with parallel fibers connected with pith. However, after being crosslinked with β-cyclodextrin, the SB-βCD became irregular, cracked, and possessed polymer networks. The amalgamation of silver nanoparticles with SB-βCD had resulted the formation of nanocomposites (AgNPs-SB-βCD) that have the surface area, average pore size, and total pore volume of 20.83 m 2 g −1 , 15.4 nm, and 0.061 cm 3 g −1 , respectively ( Table 2). The AgNPs seem to increase the pore volume, surface area, and pore size of bagasse-polymer. As reported by Mpatani et al. [26], SB-βCD polymer adsorbent had a respective pore size, surface area, and pore volume of 9.28 nm, 8.56 m 2 g −1 , and 0.0434 cm 3 g −1 . As seen in Figure 3, the AgNPs are scattered and clustered on the surface of AgNPs-SB-βCD. This means that during impregnation process, AgNPs were diffused on the surface of bagasse-polymer, breaking the fibrous network of cellulose, dispersed in the polymer network, and resulting bond formation between AgNPs and bagasse-polymer. These interaction phenomena have led to development of mesopores, micropores, and cracks. The nanostructure of AgNPs together with the bond-breaking-bond-forming phenomenon could contribute to the increasing of total pore volume and surface area of AgNPs-SB-βCD. These interaction incidents are consistent with the results reported by Trinh et al. [40].
3.1.4. XRD Analysis. As seen in Figure 4, the peak intensity of SB-βCD polymer adsorbent has increased after being impregnated with silver nanoparticles (AgNPs). Besides, the position of diffraction peak at 19.2°that attributed to amorphous nature of SB-βCD polymer had slightly shifted to 20.4°after impregnation process. In addition, three new peaks were formed at 35.5, 43.6, and 63.7°which are, respectively, attributed to crystal plane (111), (200), and (220) of cubic Ag nanoparticles [41]. These AgNPs have relative influences on altering bagasse-polymer signals. The shift of the peak (from 19.2 to 20.4°), development of new peaks (35.5, 43.6, and 63.7°), and formation of crystalline nature of AgNPs-SB-βCD confirm the successful incorporation of silver nanoparticles onto cyclodextrin polymer based on sugarcane bagasse.

Batch Adsorption Studies
3.2.1. Contribution of Contact Time on BPA Uptake. Adsorption experiments were conducted to assess the influence of contact duration on the uptake of 100 mg L -1 BPA onto AgNPs-SB-βCD. At both temperatures, the adsorption equilibrium for the uptake of BPA was attained within 120 min ( Figure 5). However, approximately half of adsorptive-oxidative capacity of AgNPs-SB-βCD on BPA has been achieved in the first 5 min, and afterward, the uptake became slowly increased until the equilibrium was reached. At 25°C, 40.3, and 75.2% of 100 mg L -1 , BPA was eliminated from the solution at 5 and 120 min. This means that the active sites of AgNPs-SB-βCD (through adsorption and oxidation processes) were more accessible at the beginning of contact process and then became occupied as the time goes.
Pseudo-first-order and pseudo-second-order models were regarded to give the kinetic information on the removal of BPA using AgNPs-SB-βCD. The values obtained from the determined coefficient (R 2 ), chi-square statistics (χ 2 ), and calculated adsorption capacity (q e calc.) were considered to determine the best fitted kinetic model. The kinetic model data and plotted curves are presented in Table 3 and Figure 5, respectively. As it can be seen in Table 3, the calculated q e obtained from pseudo-second-order model at 25, 35, and 45°C were moderately similar with experimental q e . Moreover, the values of coefficient of determination (R 2 ) of pseudo-second-order model were higher (R 2 > 0:98) compared to that of pseudo-first-order (R 2 < 0:89). In addition, the chi-square statistics (χ 2 ) values from the pseudosecond-order model were relatively smaller, and the plotted curves were closer to experimental points. This implied that the adsorption kinetics for the uptake of BPA onto AgNPs-SB-βCD was governed by PSO reaction.

Contribution of BPA Concentration on Adsorption
Capacity of AgNPs-SB-βCD and Isotherm Studies. The sequestration of bisphenol A using 0.01 g of AgNPs-SB-βCD was assessed at different mass concentrations of BPA (25, 50, 75, 100, 125, 150, 175, and 200 mg L -1 ) and temperatures (25, 35, and 45°C). The deviation between the uptake capacity (q e ) and equilibrium concentration (C e ) is shown in Figure 6. At individual temperature, the uptake of BPA onto AgNPs-SB-βCD was steadily improved with the increase of bisphenol A concentration till the highest uptake capacity of AgNPs-SB-βCD was reached. Increasing of BPA concentration seemed to facilitate the interaction between AgNPs-SB-βCD and BPA molecules. These results are comparable with the findings described by Han et al. [42] and Aryee et al. [43].
In this study, the adsorption isotherm data were fit to Freundlich and Langmuir models using nonlinear regression analysis. The chi-square statistics (χ 2 ), coefficient of determination (R 2 ), separation factor (R L ), and fitted curves were considered mostly to predict the best isotherm model that governed adsorption phenomenon. It is apparent that the experimental data on the fitted curves are much closer for Langmuir than Freundlich model ( Figure 6). Moreover, Langmuir model had higher coefficient of determination (R 2 > 0:991) and lower chi-square statistics (χ 2 < 1:3) at both temperatures compared to Freundlich model (R 2 < 0:970 and χ 2 > 4:1) (Table 4). In addition, the R L values calculated from initial concentration of BPA (C 0 = 100 mg L -1 ) were Table 2: Textural characteristics of a novel bagasse-polymer-silver nanoparticle nanocomposite (AgNP-SB-βCD) adsorbent.

Nanocomposite absorbent
AgNPs-SB-βCD 20.83 0.022 15.4 0.061 S BET : BET surface area; V M : micropore volume; D P : pore diameter; V T : total pore volume. 6 Adsorption Science & Technology less than unit (R L < 1). These results confirm that adsorption isotherm is well governed by Langmuir model, and monolayer adsorption was occurred on the uniform surface of AgNPs-SB-βCD.
In this present study, the maximum adsorption uptake of AgNPs-SB-βCD for bisphenol A at 25, 35, and 45°C is 158.4, 149.1, and 141.2 mg g -1 (Table 4). By comparing from the study of Mpatani et al. [26], the adsorption capacity of bagasse-polymer towards BPA (at 25°C) has improved from 121 mg g -1 (SB-βCD) to 158.4 mg g -1 (AgNPs-SB-βCD) after amalgamation process. This increasing of adsorption capac-ity is due to the incorporation of AgNPs that led the improvement of surface features and functional moieties on the bagasse-polymer, whereby all these together brought adsorption and oxidation processes on BPA. In addition, these polymeric nanocomposites (AgNPs-SB-βCD) have demonstrated stability and reusability behaviors and possess higher removal capacity compared with a number of adsorbents (including 2-vinylpyridine functionalized magnetic nanoparticle, modified carbon nanotubes, magnetic nanoparticles, alfafa-derived biochar, molecularly imprinted polymer, bagasse-polymer, and CTAB-walnut shell) reported from the previous studies on removal of BPA from water system (Table 5). Therefore, there is market competent on AgNPs-SB-βCD for BPA wastewater remediation.

Contribution of pH
Solution on BPA Uptake. The pH solution had a major influence on the characteristics of bagasse-polymer-silver nanoparticle nanocomposites (AgNP-SB-βCD) on removing BPA. The removal efficiency of AgNPs-SB-βCD was lower at both acidic and alkaline media (Figure 7). This might be elucidated by the, respectively, existence of AgNPs in aggregation and stable suspension states [38], whereby the removal of BPA was mostly governed by adsorption process through host-guest inclusion and pore diffusion mechanisms. However, at neutral medium, the uptake of BPA onto AgNPs-SB-βCD was much enhanced due to the dissolution of AgNPs which brought degradation of BPA. In this circumstance, the interaction of BPA and nanocomposites was managed by both adsorption and oxidative degradation processes, consequently resulted higher removal of BPA from water solution.

Adsorption Science & Technology
AgNPs-SB-βCD (0.0025, 0.005, 0.01, 0.015, and 0.02 g) were put individually into Erlenmeyer flask containing 100 mg L -1 , and then, adsorption process was done at 25°C. At equilibrium, the uptake capacity (q e ) of AgNPs-SB-βCD towards 100 mg L -1 of BPA was appeared to diminish from 197.2 to 46.8 mg g -1 , while the removal effectiveness (% P) increased from 49.3 to 93.7% with the raise of nanocomposite dosage from 0.0025 to 0.02 g (Figure 8). The higher uptake capacity (q e ) was achieved when the AgNP-SB-βCD dosage was low. This is because at higher dosage, most of the active sites become vacant, resulting lower BPA uptake. The same facts have been described in the studies by Ponnusami et al. [48], Mpatani et al. [26], and Kani et al. [49].

Influence of Cations and
Anions on BPA Uptake. Usually, the wastewater influents generated from the industries are accompanied with enormous amount of ions. These ions may greatly affect the performance of adsorbent for removing designated pollutants. Therefore, assessing the influence of coexisting ions on BPA uptake onto AgNPs-SB-βCD is of compulsory. The findings of this present study demonstrate that the presence of CaCl 2 in the water system can affect the uptake capacity of AgNPs-SB-βCD on BPA. At 25°C, the initial uptake capacity (75.2 mg g -1 ) of AgNPs-SB-βCD had decreased to 60.8 and 50.7 mg g -1 when a respective CaCl 2 concentration of 0.02 and 0.1 mol L -1 was used. Both coexistence ions (Ca-cations and Cl-anions) had positive effects of    [50,51] and resulting oxidative degradation of BPA. However, since adsorption incident where R L is the separation factor and C 0 is the initial concentration of BPA (100 mg L -1 ).  9 Adsorption Science & Technology (through βCD cavities and mesopores) contributed much for the uptake of BPA onto AgNPs-SB-βCD than oxidative degradation (through AgNPs), therefore the adsorption capacity of AgNPs-SB-βCD was reduced in the presence of CaCl 2 (Figure 9).
On the other side, the existence of Na 2 SO 4 had a positive effect of increasing the AgNP-SB-βCD capacity for eliminating BPA. According to the findings by Mpatani et al. [26], Na 2 SO 4 has a tendency of diminishing BPA solubility in the solution; as a result, more BPA can be taken onto AgNPs-SB-βCD through host-guest inclusion, pore filling effect, and oxidative degradation process. At 25°C, the initial adsorption capacity of AgNPs-SB-βCD (75.2 mg g -1 ) had escalated to 79.8 and 88.3 mg g -1 when a particular Na 2 SO 4 concentration of 0.02 and 0.1 mol L -1 was introduced (Figure 9).  3.3. Thermodynamic Study. Thermodynamic study stands as among the important analyses in adsorption process. This study can assist to know the adsorption behavior (nature) and temperature that suits adsorption interaction. As shown in Table 6, the negative Gibbs free change (ΔG 0 ) values imply the spontaneous comportment of adsorption phenomenon [26,52]. Since all ΔG 0 values are less than − 20 kJ mol -1 , the interaction of BPA and AgNPs-SB-βCD could be mostly controlled by physical adsorption [53] through host-guest inclusion (van der Waals bonding). Negative enthalpy change (ΔH 0 ) data suggests the exothermic character of the adsorption incident, while negative entropy change (ΔS 0 ) value indicates the lessening of degree of randomness at the interface of BPA and AgNPs-SB-βCD [44].

Regeneration Analysis.
The tendency of an adsorbent to be reused for removing pollutant can promote its practical application and economical worth. This analysis can be used to confirm the stability and effectiveness of adsorbent on pollutant remediation [26,54,55]. According to the results, 75% ethanol had an uppermost desorption and regeneration ability of 72 and 95%, respectively, followed by 0.1 mol L -1 HCl solution. The slight lower desorption efficiency of AgNP-SB-βCD nanocomposites (72%) could be explained by the fact that not all BPA molecules presented in the aqueous solution were adsorbed via host-guest inclusion and pore filling mechanisms, but some were disintegrated (degraded) by the oxidative activity of AgNPs loaded onto bagasse-polymer. Therefore, this 72% could represent the BPA desorbed on AgNPs-SB-βCD from the total BPA concentration removed (adsorbed) by means of adsorption process. AgNP-SB-βCD nanocomposites have possessed a stable adsorption performance by not being affected greatly by desorption process and have demonstrated a great desorption and regeneration performances. Its regeneration capacity was lessened by 5% after five succeeding cycles. This confirms the market competition of AgNPs-SB-βCD towards remediation of wastewater tainted with BPA.

Adsorption and Oxidation
Mechanisms. The surface features of AgNP-SB-βCD nanocomposites have played momentous roles in adsorption mechanisms. Figure 10 is a diagrammatic representation of the mechanism involved in the elimination of BPA from water matrix. The adsorbate-adsorbent interaction mechanism was mainly operated by host-guest inclusion through involvement of van der Waals bonding. The 2 ′ hydroxyl (-OH) groups on the betacyclodextrin (β-CD) cavities of AgNPs-SB-βCD were accountable for the uptake of bisphenol A through intermolecular hydrogen bonding and resulted the formation of inclusion complexes. These results are analogous to the findings reported by Ragavan et al. [56] and Mpatani et al. [26].
In addition to host-guest inclusion, pore diffusion effect has also participated in removing BPA from water matrix. The presence of mesopores (15.4 nm) on AgNP-SB-βCD surfaces had caused the diffusion of BPA into the interior part of polymeric nanocomposites; consequently, it brought adsorption process. On the other hand, oxidative dissolution of AgNPs embedded onto polymers has initiated the degradation of BPA. The dissolution incident of AgNPs assisted by poly(Nvinyl pyrrolidone) can trigger the generation of HO. radicals in the sunlight's presence; as a result, it causes the decomposition of BPA through benzene ring cleavage [17,57].

Conclusions
This research offers a comprehensive understanding on the greener synthesis of an innovative bagasse-polymer-silver nanocomposite adsorbent and its application in remediation of emerging micropollutant-bisphenol A (BPA) from water system. The process synthesis is reliable and sustainable and approaches on a cleaner and facile route. The impregnation of AgNPs onto bagasse-polymer material had increased the surface features (active sites/species, surface area, pore sizes, and cracks) and removal performance of polymeric nanocomposites towards BPA. The uptake of BPA onto AgNPs-SB-βCD is significantly dependent on the solution pH. In this present study, pH 7 had resulted the best removal performance due to the simultaneous occurrence of both adsorption and oxidative degradation processes. The kinetics and isotherms of adsorption followed pseudo-secondorder and Langmuir models, respectively. The adsorption incident was governed mainly by physical adsorption via host-guest inclusion (van der Waals bonding) and pore filling effect. Besides, oxidative degradation had contributed marginally on the removal of BPA due to oxidative dissolution of AgNPs at pH 7. AgNP-SB-βCD had a maximum uptake capacity of 158.4 mg g -1 and was reused five times 11 Adsorption Science & Technology without substantial loss on its efficiency. This novel AgNP-SB-βCD nanocomposite adsorbent had provided good removal capacity and higher steadiness on BPA compared to a number of adsorbents reported from the literature, consequently substantiates its practical application by offering a competition for BPA wastewater remediation.

Data Availability
All data generated and analyzed in this study are included within the article.

Additional Points
Highlights. (i) Novel AgNP-SB-βCD was fabricated to eliminate bisphenol A from aqueous matrix. (ii) AgNPs-SB-βCD had a highest uptake capacity of 158.4 mg g -1 on bisphenol A. (iii) AgNP-SB-βCD possesses both adsorptive and oxidative properties on bisphenol A. (iv) AgNP-SB-βCD nanocomposites are stable and reusable; this promotes their market competition for remediation of BPA wastewater.

Conflicts of Interest
The authors declare that they have no competing interests.