Biogenic Silver Nanoparticles of Clinacanthus nutans as Antioxidant with Antimicrobial and Cytotoxic Effects

Silver nanoparticles (AgNPs) previously synthesised using leaf (AgNP-L) and stem (AgNP-S) extracts of Clinacanthus nutans (C. nutans) were tested to evaluate antimicrobial, antioxidant, and cytotoxicity activities. The AgNPs showed good inhibition against bacteria, but not fungi. The inhibition results showed the highest activity against Staphylococcus aureus (S. aureus) with 11.35 mm (AgNP-L) and 11.52 mm (AgNP-S), while the lowest inhibition was against Escherichia coli (E. coli) with 9.22 mm (AgNP-L) and 9.25 mm (AgNP-S) in the disc diffusion method. The same trend of results was noted in the well diffusion method. The IC50 of AgNP-L and AgNP-S in 2,2-diphenyl-1-picrylhydrazyl (DPPH) and 2,2′-azino-bis (3-ethylbenzothiazoline-6-sulfonic acid) (ABTS) assays was 417.05 μg/mL and 434.60 μg/mL, as well as 304.31 μg/mL and 326.83 μg/mL, respectively. Ferric reducing power (FRAP) assay showed that AgNP-L [872.389 μmol/L Fe(II)] and AgNP-S [612.770 μmol/L Fe(II)] exhibited significantly (p < 0.05) greater antioxidant activities than leaf extract (CNL) [152.260 μmol/L Fe(II)] and stem extract (CNS) [110.445 μmol/L Fe(II)] of C. nutans. The AgNPs were also proven to possess cytotoxic effects on the breast (MCF-7), cervical (HeLa), and colon (HT-29) cancer cells in a dose-dependent manner. AgNP-S and AgNP-L showed significantly (p < 0.05) higher cytotoxicity against MCF-7 (117.43 μg/mL) and HT-29 (78.47 μg/mL), respectively. In conclusion, the biosynthesised AgNPs from aqueous extract leaves and stem of C. nutans have demonstrated promising potential towards antioxidant, antimicrobial, and cytotoxicity activities.


Introduction
AgNPs are well known as effective antimicrobial agents against bacteria and fungi [1][2][3][4]. erefore, they have been studied in bacterial applications, for instance, in the medical, cosmetics, food, and textile industries [5][6][7][8]. Various skin diseases caused by pathogenic microorganisms are treated with antibiotics. Commonly prescribed antibiotics include erythromycin, clindamycin, tetracycline, penicillin, and ciprofloxacin [9]. Due to the development of antibiotic resistance, researchers are keen to identify alternatives in the development of new antibacterial agents. e biosynthesis of AgNPs can overcome antibiotic resistance and reduce costs compared to conventional antibiotics [10]. Side effects have been observed in synthetic antioxidants such as butylated hydroxytoluene (BHT) and hydroxyanisole (BHA). Low doses of tested BHA appear to be toxic to Vero cells with mitochondrial function loss based on an MTT assay [11]. Several studies reported significant antioxidant activity of the C. nutans extract [12,13].
us, the biocompatible C. nutans-derived AgNPs could be an alternative for synthetic antioxidants. AgNPs demonstrated inhibition of free radicals, such as reactive oxygen species (ROS) produced from metabolic reactions to prevent damage to tissues or cells [14,15]. A previous study reported that the synthesised AgNPs using Costus afer aqueous leaf extract showed higher antioxidant activity compared to the leaf extract only [16]. AgNPs may, therefore, be a new/novel antioxidant agent with the ability to avoid side effects exhibited by synthetic antioxidants.
In addition to antibacterial and antioxidant properties, the plant-derived AgNPs are widely studied for their cytotoxic effects against cancer cells [17]. Cancer cells are formed from the transformation of normal cells over a number of stages. ese could be based on interactions between genetics and external influences, such as physical, chemical, and biological carcinogens [18]. Drug resistance can occur even after chemotherapy treatment [19]. erefore, alternative biocompatible and cost-effective chemotherapy drugs are needed. It is evident that plant-derived AgNPs have the potential to inhibit the proliferation of cancer cells [20,21]. Additionally, cytotoxicity of AgNPs has been reported to induce apoptosis of cancer cells through mitochondrial damage and oxidative stress leading to cell death [22,23]. e aim of this project is, therefore, to assess the antimicrobial, antioxidant, and cytotoxicity properties of C. nutans-derived AgNPs that were previously synthesised [13].

Synthesis of AgNPs.
Synthesis of AgNP-S and AgNP-L from CNS and CNL, respectively, was conducted according to our previous published work [13].

Antimicrobial Activities of Synthesised AgNPs.
e antimicrobial activities were tested using the disc and well diffusion methods in the presence of an inhibition region. en, the broth-microdilution approach was used to achieve the minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC).

Microorganisms.
e antimicrobial activities were tested against Gram-negative bacteria: (1) ATCC 27853 Pseudomonas aeruginosa (P. aeruginosa) and (2)  e MHA was autoclaved at 121°C for 15 min. en, the media were poured into a sterile Petri dish (Bio-Rad, California, USA), and it was left to solidify for 24 h at room temperature to avoid contamination. e same protocol was applied for fungi with SDA as the media. e plates were labelled and stored at 4°C in a sealed plastic bag till further need and prewarmed in an incubator at 37°C prior to the experiment.

Preparation of Inoculum and Samples.
A single colony was transferred from the stock culture to 10 mL of MHB and PDB for bacteria and fungi, respectively. e culture suspension was incubated at 37°C for 24 h. Dilution of the culture with either MHB or PDB was performed corresponding to 1-2 × 10 8 CFU/mL of the 0.5 McFarland's standard using a UV-VIS spectrophotometer and measured at 600 nm. e absorbance should be at 0.1 equivalent to 10 8 CFU/mL concentration. Each sample (5 mg) was dissolved in 1 mL of distilled water (dH 2 O). A sonicator (WUC-A10H, Wise Clean, Sonic Wise, California, USA) was used to sonicate the samples for 15 min. en, the samples were sterile filtered before further use.

Disc Diffusion Method.
e procedure was carried out according to the Clinical and Laboratory Standards Institute (CLSI) (M02-A11). Briefly, the prepared inoculum solution was swabbed onto MHA and SDA with a sterile cotton swab. Next, sterile Whatman filter paper (6 mm) (Maidstone, UK) was added with 20 μL of tested samples. e positive controls were gentamicin and nystatin. e discs were gently pressed on the agar and incubated with bacteria and fungi at 37°C and 30°C for 24 and 48 h, respectively. A clear inhibition zone was measured and expressed in millimetre (mm).

Well Diffusion Method.
A well of 6 mm in diameter was punctured using sterile pipette tips. en, the inoculum solution was swabbed on the agar with a sterile cotton swab. Next, 20 μL of the sample was added to each well. e positive controls were gentamicin and nystatin. On the other hand, the negative control was dH 2 O. Diffusion of samples into the agar was conducted for 1 h. en, bacteria were incubated on the plate at 37°C and fungi at 30°C. e inhibition zones were obtained after 24 h for bacteria and 48 h for fungi [24].

Broth-Microdilution Assay.
A broth-microdilution assay was utilised to assess the MIC and MBC. e method described by the Clinical and Laboratory Standards Institute (CLSI) (M07-A9) was used, with certain modifications. A serial dilution (7.8125 μg/mL to 1000 μg/mL) of the sample was prepared in 96-well plates flat bottom. Each well contained a sample (20 μL) and inoculum suspension (180 μL). e positive and negative controls were gentamicin and dH 2 O, respectively. e plate was incubated at 37°C for 24 h. Every well was pipetted with MTT in PBS solution (50 μL, 0.5 mg/mL) after the incubation time. After that, the plate was incubated for 30 min. e appearance of a dark purple colour indicated the presence of live bacteria. To determine the MBC values, 10 μL from the wells without purple colour were streaked on MHA and incubated at 37°C for 24 h. After 24 h, the MBC was assessed to differentiate between bactericidal (no growth of bacteria on the plate) and bacteriostatic (bacteria growth on the plate) agents from the samples [25].

DPPH Radical Scavenging Assay.
e radical scavenging DPPH method of antioxidant activity was adapted with some modifications from [26,27]. Briefly, in a 96-well plate, samples (50 μL) and 0.2 mM DPPH in methanol (150 μL) were added. e plate was incubated for 30 min in the dark, and the absorbance was then measured at 517 nm with microplate readers. e calculation of the antioxidant activity was based on DPPH radical scavenging (%) � Ab control − Ab sample Ab control × 100, where Ab control is the DPPH solution absorbance while Ab sample is the DPPH solution with sample absorbance.

ABTS Radical Scavenging Assay.
With some modifications, the ABTS radical scavenging assay was adapted from [28]. Briefly, the working solution of ABTS cation radical was prepared by mixing 7 mM ABTS solution and 2.45 mM potassium persulphate at 1 : 1 ratio, and this was kept at room temperature for 16 h in the dark. e working solution was diluted with ethanol, and the absorbance at 734 nm was measured using a microplate reader. Each well was pipetted with the sample (20 μL) and ABTS working solution (180 μL). In the dark, this mixture was incubated for 6 min at room temperature, and the absorbance was measured at a wavelength of 734 nm. As the positive control, the sample was compared with BHA. e ABTS radical scavenging calculation was based on where the absorbance of ABTS working reagent with ethanol is OD control and the absorbance of ABTS working reagent with the sample is OD sample .

FRAP Assay.
With some changes, the FRAP test was modified according to [29]. In brief, the acetate buffer

Cytotoxicity Studies.
e cytotoxicity tests against MCF-7, HT-29, and HeLa cancer cell lines were carried out on the basis of their percentage of viability after treatment.

Preparation of Cell Concentration and
Subculture. e cells were used upon reaching 80% confluent. e old media were pipetted out and rinsed with 5 mL of PBS. en, 0.5 mL of 0.25% Trypsin-EDTA was applied and incubated in a CO 2 incubator for 3 min. A 15 mL centrifuge tube was Bioinorganic Chemistry and Applications used to contain the solution. 5 mL of fresh media was then applied, and the mixture was centrifuged for 5 min at 1000 rpm (Heraeus Megafuge 16, ermo Scientific, Massachusetts, USA). e supernatant was removed, and the pellets in 1 mL of complete media were resuspended. 50 μL of suspension was added to 50 μL of Trypan Blue and placed into a slide counter using an automated cell counter TC10 (Bio-Rad, Richmond, California) to count the total cells. At concentrations of 1 × 10 4 cells/well (HT-29), 5 × 10 3 cells/ well (MCF-7), and 1 × 10 4 cells/well (HeLa), the cells were seeded. e residual suspension was subcultured into a new flask and incubated for further use at 37°C in a CO 2 incubator.
e samples used were AgNP-L, AgNP-S, CNL, CNS, C-AgNP, and 5-Fu as the positive control. en, after 72 h of incubation time, an MTS reagent (20 μL) was added to each well. e plates were then incubated for a further 4 h in the CO 2 incubator again. A microplate reader was used to measure the absorbance at 490 nm. e cell viability (%) was calculated using where OD sample is the sample absorbance of the treated cells, and OD control is the absorbance of the untreated cells.
2.6. Statistical Analysis. All of the above experiments were conducted in triplicate and expressed as mean ± standard deviation (SD). One-way variance analysis (ANOVA) and Tukey's honest significant difference (HSD)/Dunnett's t-test were used for the statistical analysis. e difference was considered statistically significant if p < 0.05. To screen for the presence of antimicrobial activity, the disc and well diffusion method was conducted. e microdilution of the broth was then carried out to obtain the values of MIC and MBC. Staphylococcus and Streptococcus are common bacteria genera present on the human skin [30], while S. epidermidis, S. aureus, and P. aeruginosa are among the normal "resident" bacteria on human skin. Skin disease can occur when the resident microorganism transforms into pathogenic forms under certain conditions [31,32]. S. aureus is one of the main pathogenic bacteria which can cause various illnesses from minor skin infections to life-threatening diseases. P. aeruginosa can lead to dermatitis and even deeper soft-tissue infections [33]. C. albicans is the most virulent among other Candida species [34]. e inhibition zones of the AgNPs against pathogenic microorganisms are shown in Tables 1 and 2. e concentrations used in the experiments were fixed for all samples at 1000 μg/mL. Table 1 summarises the antimicrobial activity against microorganisms using the disc diffusion method. Samples AgNP-L and AgNP-S showed antimicrobial activity compared to plant extracts as there was a presence of inhibition zones after 24 h of incubation. Based on the results of the disc diffusion method, AgNP-L and AgNP-S showed the highest activities against S. aureus with 11.35 mm and 11.52 mm, respectively. However, both AgNPs demonstrated the lowest activity levels against E. coli with inhibition zones at 9.22 mm (AgNP-L) and 9.25 mm (AgNP-S).

Results and Discussion
e inhibition zones of AgNPs (AgNP-L and AgNP-S) were significantly higher than the plant extracts (CNL and CNS). Interestingly, both AgNPs showed the highest activity against S. aureus with inhibition zones of 18.29 mm (AgNP-L) and 17.24 mm (AgNP-S) in the well diffusion method (Table 2). Coincidentally, both also displayed the lowest activity against E. coli with inhibition zones of 12.83 mm and 13.41 mm, respectively. ere were no inhibition zones noted in samples using the aqueous plant extract (CNL and CNS). Despite showing higher antimicrobial activity against the pathogenic microorganisms, the AgNPs showed significant antimicrobial activity inhibiting the growth of the pathogenic microorganisms. However, no activity was observed when AgNPs and plant extracts were tested on fungi (C. albicans and C. glabrata).

Broth-Microdilution Assay.
Based on the antimicrobial activity using disc and well diffusion methods, the samples that produced inhibition zones (AgNP-L, AgNP-S, and gentamicin) were further used for the broth-microdilution assay to determine the MIC and the MBC. Based on the result of MBC, the bactericidal and bacteriostatic properties of the samples against pathogenic microorganisms can be determined. Bactericidal refers to the ability to kill microorganisms while bacteriostatic agents are able to inhibit microorganisms. Plates with no growth of bacteria indicate bactericidal properties while plates with bacteria growth indicate bacteriostatic abilities [25]. Table 3 shows the MIC and MBC values for the AgNPs. To determine the antimicrobial activity, the disc diffusion method was used because it is a simple and reliable method with a minimum cost [35]. However, MIC could not be determined because it requires a large range of concentrations and is not economic compared to disc or well diffusion. erefore, to determine the MIC values, a broth-microdilution assay was carried out.
e MIC was performed in a 96-well plate and incubated at 37°C for 24 hours.
e MTT reagent was used as an indicator after 24 h. e change in colour from purple to yellow was indicative of bacteria death [25]. e MIC of AgNP-L was reported at the concentration of 250 g/mL against S. aureus, S. epidermidis, S. pyogenes, and P. aeruginosa, and it was reported at 125 μg/mL against E. coli. As for S. aureus, S. epidermidis, and S. pyogenes, the MIC of AgNP-S was reported at the concentration of 250 μg/ mL, and it was reported at 125 μg/mL for E. coli and P. aeruginosa.
e AgNP-L MBC was the same as the bactericidal MIC due to the absence of bacterial growth at 250 μg/mL against S. aureus, S. epidermidis, S. pyogenes, and P. aeruginosa, and it was reported at 125 μg/mL against E. coli. In MIC, the MBC of AgNP-S also demonstrated the same concentration. ere were no MIC and MBC for fungi because there were no inhibition zones using the disc or well diffusion methods.
From the results in Tables 1 and 2, AgNP-L and AgNP-S showed inhibition zones compared to plant extracts (CNL and CNS). Plant extracts at 1000 μg/mL showed no inhibition zones. Previous studies have investigated the antimicrobial activity of C. nutans. However, results showed insignificant activity against acne-inducing bacteria even at high concentrations (5 mg/mL) [36]. e C. nutans leaf extract showed important antimicrobial effects against E. coli and S. aureus, with MIC values of 12.5 mg/mL [37].
As for AgNPs, the result in Tables 1 and 2 suggests that Gram-positive bacteria possess better inhibition zones compared to Gram-negative bacteria. Similar results were found by [38] where S. aureus inhibited a higher zone than E. coli, thus suggesting the absorption and accumulation of AgNPs on the cell wall. Nevertheless, insignificant inhibition zones occurred against C. albicans and C. glabrata. In the AgNPs synthesis with Lantana camara L. leaves, Grampositive (S. aureus; 28 mm) bacteria have a larger inhibition zone than Gram-negative bacteria (P. aeruginosa, 21 mm; and E. coli, 22 mm) using the well diffusion method. e other mechanism is due to the size of AgNPs. e small size of AgNPs results in a large surface area to volume ratio, and this is important in antimicrobial activity against Table 1: Inhibition zones (mm) of the biosynthesised silver nanoparticles against microorganisms using the disc diffusion method (mean ± SD, n � 3); mean values are significantly different (p < 0.05) between tested samples in each particular bacterium/fungus with different lower case superscript letters a, b, c, and d.

Samples
Inhibition zone (mm) Gram-positive bacteria Gram-negative bacteria Fungi SA SE SP EC PA CA CG CNL 0.000 a 0.000 a 0.000 a 0.000 a 0.000 a 0.000 a 0.000 a CNS 0.000 a 0.000 a 0.000 a 0.000 a 0.000 a 0.000 a 0.000 a AgNP-L 11.350 ± 0.243 b 11.597 ± 0.311 b 10.260 ± 0.125 b 9.220 ± 0.433 b 10.073 ± 0.280 b 0.000 a 0.000 a AgNP-S 11.517 ± 0.519 b 10.153 ± 0.232 c 10.493 ± 0.345 b 9.247 ± 0.081 b 10.000 ± 0.305 b 0.000 b 0.000 a C-AgNP 0.000 a 0.000 a 0.000 a 0.000 a 0.000 a 0.000 b 0.000 a dH 2 [10]. In a comparative study, size-controlled AgNPs with 5 nm showed the lowest minimum inhibitory concentrations compared to 100 nm against E.coli, B. subtilis, and S. aureus [39]. A former study hypothesised that cell death is caused by high concentrations of positive potassium (K + ) ions in the extracellular fluids as a consequence of bacterial cell damage by AgNPs [40]. e study also reported that the amount of proteins released by the bacterial cells increased with the concentration of AgNPs. Another study reported that silver ions interrupt the enzymes and proteins needed for adenosine triphosphate (ATP) production, thus disturbing the life cycle of the cell and leading to cell death [41]. On the other hand, a study by [42] reported that cell death could occur due to the interaction of silver with protein. AgNPs react with sulphur-containing amino acids with the abundance of sulphur-containing proteins within and outside the bacterial cell, thus influencing the viability of the bacterial cell. Furthermore, silver ions from the nanoparticles interact with phosphorus in deoxyribonucleic acid (DNA), resulting in the inactivation of DNA replication and the inhibition of enzyme functions [43,44]. Transmission electron microscopy (TEM) analysis showed a big gap between the cytoplasm and cell wall of the E. coli after treatment with silver, thus confirming the presence of phosphorous as a primary component in DNA molecules [45].

Antioxidant Activities.
Reactive oxygen species (ROS) released in excess during metabolic reactions in the human body cause cell damage [46]. ROS can cause the development of cancer, cardiovascular disease, inflammation, aging, and neurological diseases [47]. Antioxidants function as scavengers to the free radicals caused by ROS, which decreases the risk of chronic disease [48]. Antioxidant activity of AgNPs was analysed in serial concentrations of 31.25, 62.5, 125, 250, and 500 μg/mL using DPPH, ABTS, and FRAP assays. ese three assays were chosen as they are simple and inexpensive and produce fast results. Figure 1(a) shows the effects of radical scavenging activity for CNL, CNS, C-AgNP, AgNP-L, and AgNP-S compared with the standard antioxidant BHA. Inhibitory activity against the DPPH radical was seen in the samples examined. e determined halfmaximal inhibitory concentration (IC 50 ) values for CNL and CNS were >500 μg/mL, 417.05 μg/mL (AgNP-L), 434.60 μg/ mL (AgNP-S), and 40.97 μg/mL (BHA). e results showed that control (BHA) exhibited significantly higher values, while C-AgNP showed significantly lower IC 50 values than CNL, CNS, AgNP-L, and AgNP-S. Based on the order of BHA > AgNP-L > AgNP-S > CNL > CNS > C-AgNP, the scavenging effects of samples on radical DPPH decreased.

DPPH, ABTS, and FRAP Assays.
It was discovered that each sample's capacity to scavenge free radicals differed and increased in a dose-dependent manner.
erefore, the interaction between sample form and concentration had significantly affected CNL, CNS, C-AgNP, and control (BHA).
ere were no significant differences between CNL and CNS for all concentrations. e same goes for AgNP-L and AgNP-S. However, there was a significant difference between the plant extracts (CNL and CNS) and AgNPs (AgNP-L and AgNP-S). Both AgNPs were significantly higher compared to C-AgNP. It shows that AgNPs are more effective as antioxidant agents compared to C. nutans plant extracts at all concentrations.
A previous study showed that synthesised AgNPs using Cleistanthus collinus leaf extract inhibited DPPH by 43.5% at 1000 μg/mL [49]. e current synthesised AgNPs showed 51.39% (AgNP-L) and 49.94% (AgNP-S) at 500 μg/mL. Previous studies reported that AgNPs showed 51% of DPPH inhibition at 200 μg/mL for AgNPs synthesised with Cassia tora leaf extract [50] and 80% inhibition at 100 μg/mL for AgNPs synthesised from the leaf extract of Croton bonplandianum [51]. e reaction of DPPH towards antioxidants occurs through a hydrogen atom donor and electron transfer [52]. e synthesised AgNPs would be rich in hydrogen after adding the free radical (DPPH). Accordingly, the colour change from purple to yellow is a result of the conversion of free radical DPPH• (2,2-diphenyl-1-picrylhydrazyl radical) to non-free radical DPPH-H (2,2-diphenyl-1-picrylhydrazine). is is due to the transfer of hydrogen from AgNPs to free radicals in developing stable products [51]. e conjugation of biocompounds to silver ions has caused DPPH radical scavenging [53]. erefore, biosynthesised AgNPs have potential as antioxidative agents. Although DPPH assay is simple and easy, it has its limitations. Samples that react rapidly with peroxyl radicals may either react slowly or not at all towards DPPH [52]. erefore, the samples were further analysed using ABTS and FRAP assays. Figure 1(b) demonstrates the antioxidant activity dependent on the ABTS radical scavenging assay. AgNPs with IC 50 antioxidant activity of 304.31 μg/mL (AgNP-L) and 326.83 μg/mL (AgNP-S) are lower than CNL and CNS IC 50 (>500 μg/mL). e IC 50 for BHA is less than 31.25 μg/mL, and for C-AgNP, it is recorded at 341.81 μg/mL. e ABTS radical scavenging inhibition of all tested samples shows a dose-dependent manner. e reduction of free radicals is significantly increased at higher concentrations. e results obtained, however, also show that the sample reduction of ABTS•+ is significantly lower than BHA (p < 0.05). Based on the data, CNL has a higher activity for each concentration and is significantly different (p < 0.05) from CNS. AgNP-L and AgNP-S also showed significantly different (p < 0.05) results at every concentration, with AgNP-L possessing higher activity of ABTS scavenging compared to AgNP-S. e ABTS assay defines how efficient antioxidants are at scavenging ABTS and forming the ABTS radical 2,2′-azinobis(3-ethylbenzothiazoline-6-sulphonic acid (ABTS•+). Antioxidants serve as agents for donating hydrogen. e blue/green colour of ABTS•+ is produced from the reaction of ABTS with a strong oxidising agent (potassium persulphate) which produces radical cations [54].
From the calibration curve (y � 0.0017x + 0.0451; R 2 � 0.9992), the FRAP values were calculated and expressed as mM Fe(II) per μg of the sample (μmol/L Fe(II)/μg sample). e calibration curve was determined using (FeSO 4 .7H 2 O). Figure 1(c) shows the antioxidant activity results based on the FRAP assay. e FRAP activity of all tested samples increased in a dose-dependent manner.
ere was no significant difference (p < 0.05) between CNL and CNS. However, the difference between plant extracts and AgNPs (AgNP-L and AgNP-S) was significant (p < 0.05), with AgNP-L showing higher activity compared to AgNP-S. At the highest concentration of AgNPs (500 μg/mL), the antioxidant activity of AgNP-L was found to be 872. e FRAP assay is based on the principle of reducing antioxidants from ferric 2,4,6-tripyridyltriazine (Fe(III)-TPTZ) to ferrous (Fe(II)-TPTZ) complexes. Antioxidants act as electron donors. e colour of the end product (Fe(II)-TPTZ) is blue, and the antioxidant capacity is directly proportional to the colour intensity [55,56]. Figure 2(a) shows the percentage of viability for MCF-7 after treatment with different samples. All samples showed a reduction in viable cells as the concentrations of samples increased. e IC 50 was observed at 117.43 μg/mL for AgNP-S whereas the values were more than 200 μg/mL for CNL, CNS, AgNP-L, and C-AgNP.

Cytotoxicity Activities.
When the maximum sample concentration (200 μg/mL) was used, cell viability using plant extract was higher: CNL (77.05%) and CNS (72.10%) compared to synthesised AgNPs; AgNP-L (57.24%) and AgNP-S (26.47%). AgNP-L and AgNP-S showed lower cell viability compared to C-AgNP (83.27%). All samples tested showed a significant difference from untreated cells (control) (p < 0.05) at 100 and 200 μg/mL concentrations. Both AgNP-L and AgNP-S demonstrated a substantial difference from the control at the lowest concentration (12.5 μg/mL). AgNP-S showed the lowest cell viability compared to other samples (CNL, CNS, AgNP-L, and C-AgNP). Figure 2(b) shows the percentage viability of HT-29 after treatment. All samples showed a decrease in cell viability when the concentrations increased. e IC 50 for AgNP-L was 78.47 μg/mL, while the CNL, CNS, AgNP-S, and C-AgNP were more than 200 μg/mL. e IC 50 for 5-Fu was less than 12.5 μg/mL. At the maximum concentration (200 μg/mL), the viabilities of AgNP-L (22.44%) and AgNP-S (74.00%) were higher than those of the plant extracts which were CNL (73.91%) and CNS (78.82%). Both AgNP-L and AgNP-S showed lower viability compared to C-AgNP (65.61%). All the samples examined showed a significant difference (p< 0.05) from the control at concentrations of 50, 100, and 200 μg/mL. AgNP-L displayed a higher sensitivity relative to AgNP-S as AgNP-L showed a large difference as compared to the control at the lowest concentration (12.5 μg/ mL).   50 for CNL, CNS, AgNP-S, and C-AgNP were more than 200 μg/mL and 5-Fu was less than 12.5 μg/mL. At the highest concentrations of samples used (200 μg/mL), the cytotoxic effects of AgNP-L (43.87%) and AgNP-S (54.33%) were higher compared to plant extracts which were CNL (87.72%) and CNS (90.23%). Both AgNP-L and AgNP-S showed higher cytotoxicity activity compared to C-AgNP (79.75%). All the samples analysed showed substantial variations at concentrations of 100 and 200 μg/mL. AgNP-L demonstrated a significant difference relative to AgNP-S, which was not significant at the lowest concentration of 12.5 μg/mL. e MTS assays were used to determine the viability of the cancer cells (MCF-7, HT-29, and HeLa) after treating with samples. MTS solution is based on tetrazolium salt which measures the mitochondrial dehydrogenase activity of viable cells. e cell produces a dark purple formazan product when tetrazolium salt is cleaved by active mitochondria. erefore, it can be used to measure the viability of the cells since the reaction only occurs in active living cells. If the cells die, they lose the ability to convert MTS into formazan [57].
e determined values are based on the formation of colours and are directly proportional to the number of cells that are viable.
Based on the findings shown, both AgNP-L and AgNP-S have produced higher cytotoxicity effects compared to plant extracts (CNL and CNS). e antiproliferative activities are categorised into four groups according to the values of IC 50 : ≤20 μg/mL (active), >20-100 μg/mL (moderately active), >100-1000 μg/mL (weakly active), and >1000 μg/mL (inactive) [58]. According to the National Cancer Institute (NCI), a crude extract is considered active for anticancer activity if it has an IC 50 of less than 20 μg/mL [59]. us, the AgNPs were in the group weakly active as the IC 50 value of AgNP-L was more than 200 μg/mL (MCF-7), 78.47 μg/mL for HT-29, and 173.35 μg/mL for HeLa. Also, the IC 50 of AgNP-S was 117.43 μg/mL (MCF-7) and more than 200 μg/mL (HT-29 and HeLa). Furthermore, in previous experiments, it was discovered that AgNPs were not cytotoxic to 3T3-L1, a normal mouse embryonic fibroblast [22]. e disruption of the mitochondrial respiratory chain by AgNPs increases the production of ROS and DNA damage due to the interruption of ATP synthesis [60]. ROS are constantly being generated and eliminated in a biological system. e death of the cancer cell is hypothesised based on the excessive production of ROS (apoptosis) [61,62]. e oxidative stress that induces apoptosis leads to the damage of cellular components in the cell [63]. Furthermore, the positive silver (Ag + ) ion released by the dissolution of AgNPs causes cytotoxicity effects. Ag + reacts with the thiol group of antioxidants such as glutathione and superoxide dismutase, thus leading to lipid peroxidation, oxidative stress, DNA damage, and cell death [64]. To conclude, the results indicate that AgNPs have cytotoxic effects against the cancer cell lines of MCF-7, HT-29, and HeLa.

Conclusions
Both Gram-positive and Gram-negative bacteria were inhibited by AgNP-L and AgNP-S, but the fungi response was negative. In addition, AgNP-L and AgNP-S showed the highest inhibition against S. aureus and lowest inhibition against E. coli. e results of these antimicrobial activities proved that AgNPs have the potential to be antimicrobial agents. In the DPPH, ABTS, and FRAP assays, AgNP-L and AgNP-S exhibited significantly greater antioxidant potency (p < 0.05) than plant extracts (CNL and CNS), which show promising potential for AgNPs as antioxidant agents. In the treatment of MCF-7, HT-29, and HeLa, both AgNP-L and AgNP-S demonstrated higher toxicity compared to CNL and CNS at similar concentrations. Furthermore, both AgNPs possessed a significant (p < 0.05) toxicity on all the cancer cells compared to the control. To conclude, the AgNPs have demonstrated potential as anticancer agents. However, more research is nseeded to support the potential for human cancer treatment. From all the studies conducted thus far, biologically synthesised AgNPs from C. nutans are simple and eco-friendly and have great potential to be applied as nanomedicine.
Data Availability e data used to support the findings of this study are included within the article.

Conflicts of Interest
e authors declare that they have no conflicts of interest.