Fluoride Coatings on Magnesium Alloy Implants

After several years of research and development, it has been reported that magnesium alloys can be used as degradable metals in some medical device applications. Over the years, fluoride coatings have received increasing research attention for improving the corrosion resistance of magnesium. In this paper, different methods for preparing fluoride coatings and the characteristics of these coatings are reported for the first time. The influence of the preparation conditions of fluoride coatings, including the magnesium substrate, voltage, and electrolyte, on the coatings is discussed. Various properties of magnesium fluoride coatings are also summarized, with an emphasis on corrosion resistance, mechanical properties, and biocompatibility. We screened experiments and papers that planned the application of magnesium fluoride coatings in living organisms. We have selected the literature with the aim of enhancing the performance of in vivo implants for reading and further detailed classification. The authors searched PubMed, SCOPUS, Web of Science, and other databases for 688 relevant papers published between 2005 and 2021, citing 105 of them. The selected time range is the last 16 years. Furthermore, this paper systematically discusses future prospects and challenges related to the application of magnesium fluoride coatings to medical products.


Introduction
Recently, with the rapid increase in the number of tissue injury repair procedures, metals have been widely used for the replacement and regeneration of injured tissues owing to their high mechanical properties [1]. eir common applications include scaffolds [2,3], bone plates [4,5], bone nails [6], wound closing devices [7], artificial joint prostheses [8], and guided tissue/bone regeneration membranes [9]. Nonbiodegradable metals used in traditional metal implants include stainless steel, titanium, and cobalt-chromium alloys [7,10]. Despite their excellent biocompatibility and mechanical properties, they can cause inflammatory reactions because of the release of toxic ions, which often require secondary surgical removal [11,12]. Moreover, the stress shielding effect of conventional bone implants often impedes healing because of the disparity in elastic modulus between the conventional metals and bone [10].
Fortunately, as a biodegradable metal, magnesium is preferred as a biologically essential trace element, with an elastic modulus similar to bone in fracture healing, eliminating the need for a secondary surgical removal [13]. e ideal clinical biodegradable metals must be perfectly suited for the injured tissue reconstruction in a biologically nontoxic precondition, providing absolute mechanical protection in the early stages and gradually degrading at an acceptable rate as the tissue heals [7]. Despite the developments in the research on magnesium alloys over the past decades, clinical studies on magnesium alloys can be traced back to 1878; at that time, Edward C. Huse first used magnesium wires to ligate blood vessels [14]. Nevertheless, the current bottleneck limiting the clinical application of magnesium is its extremely rapid degradation rate in vivo, which may result in the accumulation of local air pockets, an alkalinization effect, an osmotic pressure increase, and even a rapid decrease in the mechanical strength of the implants [2,15]. Currently, there are two ways to control the degradation rate of magnesium: composition modification and alloy surface treatment. e properties of magnesium alloys can be influenced by changing the amount and percentage of alloying elements, like Al, Li, Ca, Y, Mn, Zn, Zr, and rare earth [16]. e ideal magnesium alloy coating has properties such as corrosion resistance, degradability, and biocompatibility for clinical applications [17]. Surface modifications are known to be classified according to the method of coating preparation, which include mechanical [18], physical [19], chemical [20], and biological or biomimetic. Chemical coating is formed by the reaction between the magnesium substrate and coating solution, which makes the chemical coating strongly bonded to the substrate [21]. Since the formation is based on chemical reactions, it is more sensitive to thermodynamics and kinetics [17]. Typical chemical coating techniques include chemical conversion, plasma electrolytic oxidation (PEO), thermal treatment, and electrodeposition [15]. Among them, chemical conversion is often used as a pretreatment [12]. PEO, also known as microarc oxidation (MAO), is the use of plasma arc discharge at the electrolyte/electrolyte interface to react with the electrolyte and sinter the substrate surface to form a coating [10]. e PEO layer is usually more stable than the chemical conversion layer, but its porous surface may lead to pit corrosion [12]. Fluoride coating, tightly bonded to the substrate and insoluble in water, is formed via chemical reactions between fluorine and magnesium by the specific methods listed above. e main degradation products, Mg 2 + and low concentrations F − have both been shown to enhance osteogenesis [5,22]. Furthermore, F − ions have been proved to have antibacterial properties in dentistry [23]. As a burgeoning coating, fluoride coating has been validated to improve the corrosion resistance of magnesium to a certain extent while also meeting the requirements of an ideal coating, such as self-degradability and biocompatibility, making it a promising coating [24][25][26][27].
Currently, there is only one review of immersed fluoride conversion coatings for medical magnesium alloys [28]; however, no review for fluoride coatings is available. erefore, this paper reviews the advances in fluoride coatings for medical magnesium alloys, with the aim of discussing the pros and cons of existing fluoride coatings from the perspectives of preparation methods, coating structures and properties, and challenges and suggestions for further research.

Growth of Fluorinated Coatings
e fabrication of a dense, homogeneous, and biocompatible fluorinated coating on the surface of magnesium alloys by chemical transformation is a widely used treatment to enhance the corrosion resistance of magnesium alloys [29,30], that is, HF acid immersion treatment.
Subsequently, Mg 2+ reacts with F − and OH − in the solution to form a compound on the surface of the substrate (equations (4)-(6)). Because Mg(OH) 2 is extremely unstable under acidic conditions, it can undergo an exchange reaction (equation (7)), in which the OH − within the Mg(OH) 2-x F x coating is replaced by F − (Figure 1) [31]. e above reaction was also accelerated by increasing the concentration of HF in the conversion solution [31].
Fluoride coatings have received more attention in recent years, particularly for methods such as immersion fluorination, microarc fluorination [32], and ultrasonic immersion fluorination [24] based on the composite fluoride coatings derived from the abovementioned methods, such as hydroxyapatite/magnesium fluoride composite coatings [33], fluoride-treated and sol-gel film composite coatings [34], and composite coatings with fluoride as a pretreatment, an electrolyte, or additives [35][36][37][38][39][40][41]; these composite and multilayer coatings are not discussed in detail in this paper because there are no strict standards for their conceptual classification.

Anodic Fluorination.
Anodic fluorination is the replacement of the normal electrolyte with an electrolyte containing the element fluorine on the basis of anodic oxidation. Anodic fluorination uses the metal as an anode and forms a porous coating on the metal surface by means of electrolytic oxidation. After AF treatment, the surface of the sample forms a coral-like and shale-like surface morphology. Compared with untreated specimens, the treated specimens performed better in corrosion resistance. A better coating impedance effect appeared at relatively low voltages, which is consistent with the experimental expectations. In the low-voltage treatment group, the corrosion resistance of AF10, AF30, and AF20 showed a high to low level. 10 V treated samples showed the lowest current density and relatively high corrosion voltage. e thickness of the magnesium fluoride film increases with the increase of the voltage, reaching a peak at AF60. However, the bond between the coating and the substrate is not strong enough, and the coating tends to peel off as the coating thickness increases. erefore, samples treated at 10 V have the best corrosion resistance [32].
In the same way as microarc fluoridation, the thickness and microstructure of the coating can be changed by varying the applied voltage under fixed electrolyte conditions. It is also more environmentally friendly and economical than microarc fluorination due to the lower applied voltage and lower electrolyte concentration [26].

Immersion Fluorination.
Immersion is a popular technique for preparing coatings. e desired properties can be obtained by modifying the composition of the deposited layer. e traditional method of immersion fluorination involves immersing magnesium in a certain concentration of HF solution at a specific temperature for a certain amount of time before removing it [42]. Table 1 shows the characteristics of different HF-coated magnesium alloys prepared under various parameters. A thin fluoride film with MgF 2 as the main component was formed on the surface of magnesium alloys [43]. e coating obtained by immersion fluorination can effectively decrease the degradation rate of magnesium alloys in vivo. Meanwhile, the coating showed good biocompatibility [44][45][46]. is method is appreciated for its simplicity, low cost, and easy control, while the coating formed is loose and porous and may easily peel off [47].

Bioinorganic Chemistry and Applications
Under different treatment conditions, the coating obtained may comprise Mg(OH) 2 , MgF 2 , and other substances, as shown in equations (8)- (10). Among them, the hydroxide in the coating was validated to have a negative impact on the corrosion resistance of the coating [54]. Since equations (8) and (9) have similar thermodynamic tendencies, it is assumed that both reactions will occur spontaneously and simultaneously when magnesium alloys are in contact with water and hydrofluoric acid. us, the rate of each reaction depends on the HF concentration [42]. When the acid concentration was too low, the Mg(OH) 2 level in the coating was too high to lose the protective effect of the coating. According to equation (10), a higher concentration of HF converted the Mg(OH) 2 generated during the treatment into  [31] found that the layer obtained at 10 vol % HF (approximately 2.2 μm) was thicker and had higher F content than that obtained at 4 vol% HF (approximately 1.9 μm). e authors concluded that although the 10% HFtreated coating had more cracks, the higher F content of the coating might be a reasonable explanation for the corrosion resistance of the 10% HF-treated coating. However, an overly high concentration of HF may lead to thinning of the coating, which may be attributed to the fact that the dissolution rate of the magnesium substrate is faster than the generation rate of the conversion coating [55]. Additionally, treatment time has also been proven to affect the coating thickness [31,44], which in turn affects the corrosion resistance of magnesium alloys by changing the probability of defects or "active spots" on the surface of the magnesium substrate, that is, the number of through-holes [56]. Usually, the thickness curve rises with treatment time and eventually flattens out ( Figure 2) [31], but the formation rate of the coating gradually decreases, which may be related to the thickening of the coating that prevents the HF from reacting with the internal magnesium [57]. da Conceicao et al. [54] treated AZ31 at HF acid concentrations at a concentration gradient from 12 to 49 vol%. It was found that the coating thickness of the samples treated with high concentrations of HF acid was thinner and formed more slowly than those treated with low concentrations of HF acid, leading to a lower corrosion resistance due to the slower formation rate. e low concentration for a long time resulted in a high hydroxide content in the transformed layer, explaining the low corrosion resistance of the 12 vol% HFtreated coatings. Nevertheless, some studies have shown that magnesium alloys after alkaline pretreatment, which commonly refers to the reaction of magnesium alloys with high concentrations of NaOH to produce Mg(OH) 2 , can develop thicker MgF 2 coatings than those without the alkaline pretreatment [3,46,50]. Furthermore, the crystalline phase on the alloy surface is also an essential factor affecting the formation of fluorinated magnesium coatings. Casanova et al. [58] analyzed the morphology of fluoride conversion coatings synthesized on Elektron 21 and AZ91D alloys. In a hydrofluoric acid (HF) solution, AZ91D and Elektron 21 alloys form MgF2 coatings, which provide good corrosion protection, where the presence and nature of different intermetallic phases play a pivotal role in its growth. e preferential dissolution of the reactive β-phase (Mg17Al12) in the AZ91D alloy promoted the growth of MgF2 coatings. Conversely, the microstructure of Elektron 21 alloys was more homogeneous, and the intermetallic compound Mg12(NdxGd1-x) phase remained stable, allowing the formation of continuous and homogeneous coatings. e microstructure of fluoride conversion coatings on AZ31 in relation to the degradation mechanism was studied by Barajas et al. e authors performed chemical conversion coating of AZ31 Mg alloy at 4 and 10% HF concentration with an immersion time of 24-168 hours [31]. During the conversion process, most of the metal particles in the α-Mg matrix on the surface of AZ31 were dissolved, but SEM observation revealed undissolved metal particles, and then EDX analysis revealed that the undissolved metal particles corresponded to rare earth-containing dispersions (La, Ce, and Nd). It may be due to the fact that Al is active under HF treatment conditions, and the preferred phase dissolved easily during the transformation process is AlxMny particles.

Ultrasonic Immersion Fluorination.
One of the surface improvement methods that are both effective and environmentally friendly is HF. It enhances the corrosion and abrasion resistance of magnesium alloys by forming a thin and uniform fluoride coating that adheres to the alloy surface. However, this method is not applicable to clinical settings. Previous studies have shown that ultrasonic treatment of fluoride coatings can improve the corrosion resistance of Mg alloys and prepare denser and smoother coatings; this method is called ultrasonic immersion fluorination [24].
When immersed in an environment of 28 kHz ultrasound, the coatings of HF and UHF are identical in thickness and composition; however, UHF can reduce the porosity and cracks, exhibiting better corrosion resistance. e electrochemical tests showed that UHF had the highest electronic impedance and corrosion potential difference, as well as the lowest corrosion current density. Similarly, the mass loss test showed that the UHF-coated alloy exhibited a lower mass loss than the HF-coated and bare samples. erefore, the ultrasonic treatment of magnesium alloy with fluoride coating is promising as a biomaterial in various medical applications [24].
Lellouche et al. reported on the antimicrobial and antibiofilm activities of nanosized magnesium fluoride (MgF2) nanoparticles (NPs) synthesized in ionic liquid using microwave chemistry [59]. Compounds nanosized MgF 2 nanoparticles (MgF 2 NPs) by water-based synthesis of MgF 2 NPs using ultrasonic immersion. Ultrasonic chemical irradiation of aqueous solutions of ([Mg(Ac) 2 ·(H 2 O) 4 ]) containing hydrofluoric acid resulted in well-crystallized spherical MgF 2 NPs. Antimicrobial properties against two common bacteria (Escherichia coli and Staphylococcus aureus) were greatly improved. Using the ultrasonic chemical process described, the glass surface was coated, and the ultrasonically prepared magnesium fluoride crystals were shown to have an inhibitory effect on bacterial colonization within seven days.

MAF.
e treatment of magnesium alloys in highly concentrated fluoride solutions using the microarc oxidation technique, also known as MAF, has the advantages of short treatment time and almost no crack formation. When MAF was performed, ammonium hydrogen fluoride and hydrofluoric acid were selected as the electrolytes. e higher the concentration of fluoride ions in the electrolyte, the more corrosion-resistant the fluoride coating; thus, a high concentration of HF (46%) is preferred as the electrolyte [26,27]. In the electrolyte, a current is applied at a constant voltage for very short duration using magnesium alloy as the cathode and a graphite rod as the anode. According to the electrochemical and immersion tests, the best stability and corrosion resistance of the fluoride coating are achieved at 200 V, while too high voltage leads to the flaking of the coating [25]. e coatings prepared by MAF are dense and porous, with MgF 2 as the main component; further, the corrosion resistance of the alloy is determined by factors such as pore size and surface roughness of the coating. Compared to HF and UHF, the coating structure of MAF is much denser and forms a coral-like structure on the surface of the alloys, resulting in a higher surface roughness that is proportional to the voltage [32]. Cell proliferation was significantly more enhanced in the treated samples than that in the bare Mg alloys [25,60].

Properties
Magnesium alloys show promising biomedical applications owing to their biodegradability [61], with Young's modulus similar to that of bone, good biocompatibility, and osteogenesis. e ideal magnesium alloy implant maintains mechanical integrity during early implantation, provides absolute support, and eventually degrades as a bone defect or fracture repair without the requirement for secondary surgical removal [62]. In particular, magnesium, known to be one of the most essential substances in the human body, exists on human bone and soft tissue without obvious toxicity [25,[63][64][65][66][67] and is easily excreted in excess. e extremely high rate of magnesium alloy degradation in humans severely limits their clinical applications. Based on the different properties of magnesium alloy fluoride coatings, the following is a comprehensive review of the effect of fluoride coatings on magnesium alloys, regardless of the limiting preparation techniques and experimental types (in vivo/in vitro). We hope to offer some valuable suggestions for improving the corrosion resistance, mechanical properties, substrate bonding strength, biocompatibility, bone integration and osteogenic activity, and antimicrobial properties of magnesium alloy fluoride coatings.

Corrosion Resistance.
Poor corrosion resistance is a significant issue in magnesium implants. Electron microscopic fluoride films consist of fine particles, which improve problems such as voids and cracks on the metal surface.
us, fluoride coatings can improve corrosion resistance by surface modification. e fluoride coating of magnesium alloys demonstrated excellent corrosion resistance in in vitro immersion experiments. Li et al. [68] made screws and tensile specimens from magnesium alloys as substrates and HF to obtain HFcoated magnesium alloy samples. After immersing the HFcoated and bare magnesium alloy samples in a simulated body fluid (HBSS), the immersed screw samples were subjected to scanning electron microscopy (SEM) (Figure 3) [68] and mass loss detection. e calculations showed that the corrosion rate of the coated screw samples was only onequarter that of the uncoated samples because of the protection of the uniform and dense MgF 2 coating. ey also performed tensile tests and corrosion rate tests on tensile specimens after immersion, and the MgF 2 -coated samples showed a lower pitting corrosion rate than the bare samples, resulting in good mechanical properties even after one month of immersion.
In addition to HF-coated magnesium alloys, varying the parameters of different surface modification methods can also affect the corrosion resistance of magnesium alloys by changing the coating characteristics (Table 2). e majority of the findings indicate that the electrical parameters have the greatest influence on the coating morphology and phase composition [72][73][74][75][76][77][78][79][80]. Heydarian et al. [70] used magnesium alloy as the substrate; the coating generated at a high voltage maintained corrosion resistance for 28 days without significant substrate corrosion. e study also reported that applying higher voltages to the coatings was more conducive to increasing the thickness of the coatings, and the further incorporation of fluoride in the coatings resulted in an increase in the MgF 2 content in the inner layer of the coating, which contributed to the formation of coatings with stronger barrier properties.
Anodic polarization experiments were performed on untreated and 4.10 vol% HF immersion treated AZ31 magnesium alloy, and the electrochemical parameters were extracted as shown in Table 3 [31]; the majority of the coatings provided a scope of protection (Epit-Ecorr) to the metal substrate, and the fluoride coatings reduced the corrosion current density and enhanced the corrosion resistance of the alloy. Compared to previous studies [26], Dai et al. [32] used a low-voltage fluorination method to obtain coatings with controlled corrosion rates under safer conditions. is further confirms that MAF technology still has broad application prospects and research value in the use of magnesium alloy coatings. e above results show that the operating voltage has a significant influence on coating thickness.
Additionally, the preparation of fluoride coatings in an ultrasonic environment shows promise in the medical field. Sun et al. [24] used an AZ31 magnesium alloy for HF in a 28 kHz ultrasonic environment. e ultrasonic treatment of the coating allowed hydrogen to escape, resulting in a reduction in scratches and microporosity, as well as a significant increase in the corrosion resistance of the HFUcoating over the HF-coating. e electrochemical corrosion test results are represented in the curves shown in Figure 6 [24]. e HFU-coating had the lowest corrosion current density, highest corrosion potential, and highest electronic impedance, showing a noticeably higher corrosion resistance in the mass loss tests.
In summary, the formation conditions of the fluoride coating, such as voltage, current, and external conditions, determine its characterization and corrosion resistance.

Mechanical Property.
Magnesium alloys must have mechanical properties to meet the bone-healing process in the human body during degradation. e mechanical properties of medical magnesium alloy implants are critical for the success of fracture fixation and cardiovascular surgery [63]. e more widely used metal implants, such as titanium, stainless steel, and cobalt-chromium alloys, require secondary surgical removal. e higher Young's modulus leads to a mechanical mismatch between the bone and implant, triggering a stress shielding phenomenon, which causes reabsorption of the surrounding bone [81]. Compared to polymeric materials, magnesium alloys have better mechanical properties and Young's modulus (44 GPa) closer to natural human bone (7-25 GPa) [82]. e protective effect of fluoride coatings on the mechanical properties (compressive, tensile, and bending properties) of biodegradable magnesium alloys in recent years is reviewed as follows [83]. Drynda  layer. Due to the small crack size (width <10 μm; length <250 μm), no large tensile stress is generated, and the Mg(OH) 2 formed is relatively dense, which can separate magnesium alloy from the electrolyte and delay the corrosion process.
Dvorsky et al. [52] measured the compressive, tensile, and flexural properties of different magnesium-based materials after HF, as shown in Figure 7 [52]. e mechanical properties of pure magnesium samples improved after fluorination, with the best mechanical properties achieved after 24 h of fluorination. e MgF 2 coating formed after 1 h of immersion was thin and provided only a slight improvement in the mechanical properties; after 96 h of immersion, the coating was thicker, and brittleness increased. For the WE43 magnesium alloy, the exact opposite result was observed; a significant deterioration of the mechanical properties as the immersion time increased, which could be relevant to the inhomogeneous fluoride layer and YF3 phase. erefore, the interaction between the substrate and the coating is also a vital factor affecting the mechanical properties.
Li et al. [68] compared the mechanical properties of Mg-Zn-Zr (MZZ) alloy samples after immersion in SBF solution for various durations before and after the fluorination treatment, as shown in Figure 8 [68]. e yield strength (YS), ultimate tensile strength (UTS), and elongation (EL) of the fluorinated samples were much higher than those of the bare sample from day 3 to day 20 of the immersion, whereas the maximum corrosion rate (CRmax) of the coated samples was only approximately 50% that of the bare sample. ese results indicate that the MgF 2 coating can mitigate the effects of pitting corrosion on the magnesium matrix and contribute to maintaining preferable mechanical integrity.

Bonding with the Substrate.
e prerequisite for a qualified coating to perform its excellent surface    Figure 9 [85], and confirmed that the highest bonding strength was achieved at 50 s. Dai et al. [32] prepared fluoride coatings on magnesium alloy substrates. e surface morphologies of the generated coatings were compared at different voltages, and SEM images were obtained, as shown in Figure 10 [32]. Large areas of coating peeling appeared on the surface of the samples at voltages higher than 50 V. As stated in the study, the release of the plasma causes microporosity on the surface of the coating, leading to a coral-like appearance, which is required for the adhesion of the coating to the substrate. Excessively high voltages can roughen the coral-like structure, reducing adhesion. Furthermore, Heydarian et al. [70] used the PEO technique in their study to treat AZ91 magnesium alloy in an aluminate electrolyte. Comparing the magnesium fluoride coatings prepared at different voltages and observing the denseness and peeling of the coatings under SEM, it was confirmed that the voltage significantly affects the bond strength of the coating to the substrate. Consequently, it is possible to control the conditions during fluorination treatment to obtain fluoride coatings with better bond strength, which will have tremendous significance in clinical applications.

Biocompatibility.
Magnesium alloy has good biocompatibility as a medical implant material [22,68,[86][87][88]. Fluorine coating degrades and releases fluorine ions to surrounding tissues. A moderate amount of fluoride promotes teeth and bone growth and healing. In contrast, excessive fluoride in the body can lead to dental and skeletal fluorosis and affect the intellectual development of adolescents and the function of endocrine glands, damaging the gonads and other soft tissues such as the heart, liver, lungs, and kidneys. erefore, while using fluoride as an implant coating, the advantages of fluoride in enhancing bone quality and accelerating calcification should be exploited as much as possible to avoid any harm to the body.     Extensive in vivo and in vitro experiments lay the foundation for the clinical application of magnesium fluoride implants.
e MgF 2 -coated alloy improves its own corrosion resistance while maintaining the advantages of noncytotoxicity, favoring cell adhesion and proliferation, and not causing inflammation. In vitro cytotoxicity tests confirmed that the fluoride-coated AZ31B alloy is not toxic to human bone marrow mesenchymal stem cells (BMMSC) [49]. Jo et al. [89] performed an in vitro cellular response examination of preosteoblasts using cell proliferation assays and alkaline phosphatase (ALP) assays, indicating that hydroxyapatite coatings with MgF 2 as an intermediate layer also enhanced the level of cell proliferation and differentiation. HA/MgF 2 -coated magnesium had higher corrosion resistance than bare magnesium and the bone-to-implant contact (BIC) ratio in the cortical bone region of the rabbit femur at 4 weeks after implantation. Durisin et al. [90] observed nonspecific inflammation and mucosal thickening in an in vivo study using a novel magnesium alloy scaffold placed in the paranasal sinus, confirming that the Mg-2 wt% Nd alloy scaffold coated with MgF 2 has excellent biocompatibility while retaining functionality. ese advantages make MgF 2 -coated magnesium alloys promising for longterm therapeutic applications in various medical fields. Regarding in vivo experiments, Constantin Carboneras et al. [91] observed the performance of nasal MgNd 2 implants coated with MgF 2 over 6 months and found slow histocompatible degradation of the implants without repeated bacterial infections. Drynda et al. [84] observed the biocompatibility of fluoride-coated magnesium-calcium alloy scaffolds in a subcutaneous mouse model, and none of the samples showed tissue inflammatory reactions or extensive proliferative effects compared to bare magnesium implants while improving corrosion resistance in vivo, suggesting that magnesium fluoride coating may be a good strategy to reduce biodegradation of magnesium-based alloys.

Bone
Integration and Osteogenic Activity. Jiang et al. [22] prepared an MgF 2 coating on an Mg-Zn-Zr alloy and implanted it into the femoral condyles of rabbits. e changes in corrosion resistance, biocompatibility, and osteogenic activity of the coated alloy were observed at the histological and micromorphological levels. It was concluded that the MgF 2 coating was effective in reducing the rate of in vivo degradation of the Mg-Zn-Zr alloy. e bone tissue and mineral content gradually increased, demonstrating that the MgF 2 /Mg-Zn-Zr alloy promotes the formation of new bone on the alloy surface in vivo. Furthermore, the biological properties of the coating exhibited excellent biocompatibility and bioactivity.
Sun et al. [92] conducted a similar work, coating degradable Mg-3Zn-0.8Zr cylinders with a Ca-P layer or an MgF 2 layer; an uncoated Mg-3Zn-0.8zr alloy was used as a control group. Both specimens were implanted in the bone marrow of the white rabbits. During postoperative observation, SEM results showed a large number of cells, ample fibrillar collagen, and Ca-P products on the surface of the MgF 2 -coated implants. Also, micro-CT results revealed a slight decrease in volume (23.85%) and an increase in new bone volume (new bone volume fraction of 11.56% and tissue mineral density of 248.81 mg/cm 3 ) in MgF 2 -coated implants after 3 months when compared to uncoated and Ca-P composite-coated implants. As the samples degraded, new bone trabeculae gradually formed, which was associated with a large number of active osteoblasts and osteocytes. e arrangement of newly formed bone trabeculae in the MgF 2coated samples (Figure 11(f )) [92] was much greater and   (a) more compact than the rest of the specimens.
e bone trabeculae were well-structured and largely consistent with the original bone, which is in full accordance with Parfitt's study on the morphology of bone remodeling units [93].
Sun et al. [6] implanted fluorine-coated AZ31B magnesium alloy screws in rabbit mandibles and femurs and discussed how fluorine coating enhances corrosion resistance and promotes bone formation of AZ31B magnesium alloy at the histological and immunohistochemical levels ( Figure 12) [6]. Fluorine coating has been shown to enhance the corrosion resistance and bone formation of AZ31B magnesium alloy by upregulating type I collagen and BMP-2 expression (BMP-2 stimulates osteoclast differentiation and participates in bone tissue reconstruction) [94]. Nevertheless, due to the short observation time and complexity in vivo, further studies are required to clarify the exact mechanism by which degradation products affect osteogenesis.

Antibacterial Properties.
When fluoride-coated magnesium alloys are used as surgical implants, the antibacterial requirements of the implants are strict due to the complexity of antibiotic treatment and wounds and the repetitive nature of surgery [95,96]. ere are various methods to improve the antimicrobial properties of the surface, such as reducing the generation of surface biofilm by coating properties, special coating space structure, and adding antimicrobial elements to the coating to change the environment or physiological function in which bacteria are located. e antimicrobial research of fluorinated coatings mainly focuses on the porous structure to change the surface PH antimicrobial and fluorine release antimicrobial.
Ren et al. [97] investigated the behavior of pure Mg and AZ31 alloys against Escherichia coli and Staphylococcus aureus with and without surface coatings. is paper focuses on the effects of surface pH, porosity, cracking, and coating density on surface antibacterial ability. e antimicrobial ability of pure Mg is high because of the very rapid rate of degradation, resulting in a significant increase in the surrounding pH to 10. Alkaline environments are not conducive to the growth and reproduction of Escherichia coli and Staphylococcus aureus. Robinson et al. [98] suggest that the degradable nature of Mg in physiological solutions causes a rapid increase in the Mg 2+ concentration and the pH of the solution, with the latter supposedly being the cause of the bacterial inhibitory effect of Mg. Interestingly, if the Mg-based metal surface is covered with a porous layer, a relatively low degradation rate can not only be obtained but also acquire an antibacterial function to some extent. However, outside the fluorine-containing coatings of pure Mg and AZ31 alloys, the antimicrobial capacity is lost as the surface coating is too dense, slowing down the release of Mg 2+ and leaving the pH of the surrounding tissue almost unchanged.
Due to the degradable nature of fluoride coatings, their fluoride-releasing properties are unquestionable. In oral studies, fluoride has been combined with other substances to release fluoride to improve its antimicrobial properties and prevent secondary caries. Although there are few studies related to the antimicrobial properties of MgF 2 coatings associated with magnesium alloys, the study of fluoride releases to improve antimicrobial properties can provide a reference for the antimicrobial properties of fluorinated coatings. Zheng et al. [99] combined zirconia nanoparticles with fluorine (F-ZrO 2 ) and investigated the effect of fluorine content on surface colonization. As shown in Figure 13 [99], the number of colonies decreased significantly with the addition of fluorine, indicating that F-ZrO 2 has a significant antibacterial effect on Streptococcus pyogenes. Since the 20th century, fluoride has been shown to reduce the acid resistance of bacteria [100], and the application of fluoride-releasing materials has become a way to apply fluoride topically.

Challenges and Perspectives
Magnesium-based materials are limited in clinical applications because of the progressive decrease in mechanical properties caused by their fast degradation rate in the body fluid environment. Fluorination techniques are currently the most efficient and feasible solution for the surface modification of magnesium alloys. Although many studies have been reported on the use of magnesium and its alloys, more extensive studies are still necessary to better evaluate the potential of fluoride coatings. e mechanical properties of magnesium materials, as well as their increased resistance to corrosion changes, must be thoroughly evaluated. Further optimization of corrosionresistant fluoride coating technology is also a subject for further research. In addition, the effects of elemental fluorine entering human tissue fluids on biological organisms require extensive research data to support their safety.

Data Availability
All data, figures, and tables in this review paper are labeled with references.

Conflicts of Interest
e authors declare that there are no conflicts of interest regarding the publication of this paper.

Authors' Contributions
ChuanYao Zhai, Chun Yu Dai, and Xun Lv conceptualized the study, developed methodology, were responsible for formal analysis, and wrote the original draft. Biying Shi conceptualized the study and wrote the original draft. Yu Ru Li and Di Fan contributed to data curation and wrote the original draft. Yifan Yang validated and supervised the study. Professor Eui-Seok Lee, Professor Yunhan Sun, and Professor Heng Bo Jiang validated the study, responsible for resources, supervised the study, and responsible for project administration and funding acquisition. ChuanYao Zhai, Chun Yu Dai, and Xun Lv contributed equally to this work.