Influence of Titania Dispersivity on the Conversion Efficiency of Dye-Sensitized Solar Cells

Titania powder (P25) was dispersed by bead-milling breakdown method, and the dispersivity of TiO2 was controlled by adjusting the mean secondary TiO2 particle size to 45, 56, and 75 nm by changing the dispersion solvent blend ratio of ethanol and terpineol. The transparency of the coated layer increased when the particle size of TiO2 aggregates became smaller than 100 nm. Although the transparency was significantly different according to differences in the size of nanocrystallyne-TiO2 aggregates, the resulting photovoltaic (PV) effect of a dye-sensitized solar cell (DSSC) was not significantly different between the different aggregate sizes. A double layer structure (transparent TiO2 layer/opaque TiO2 layer) was adopted to improve the PV effect, which resulted in an improvement of the photocurrent and conversion efficiency of 13.2% and 11.1%, respectively, from that for the DSSCs with single-layered TiO2 electrodes.


Introduction
Energy requirements throughout the world are primarily dependent on fossil fuel resources in the earth.In addition, various problems have occurred in a present global environment due to the global warming issue associated with carbon dioxide emissions from fossil fuel usage.Various problems include the recently unusual weather, depletion of the ozone layer, and sea level rise due to the greenhouse effect.Such problems are threatening the current status quo.In addition, fossil fuels such as petroleum oil are a limited resource that will be depleted and result in an oil crisis.Therefore, alternative energy sources, such as the sun, have been considered to change the dominant reliance on fossil fuels.
Solar cells are used to directly convert the energy from sunlight into electricity using the photovoltaic (PV) effect.Solar cells are generally classified into three types; silicon, metal compound, and organic-based systems.Organic-based solar cells are considered to be the next-generation solar cell, due to its ease of production.In addition, the production cost can be lowered, and it has features such as the ability for coloring and flexibility.
Dye-sensitized solar cells (DSSCs) [1] are one type of organic solar cell.The manufacturing cost of DSSCs is expected to be significantly lower than that of silicon-based solar cells.DSSCs employ TiO 2 as the semiconductor photoelectrode.The structure of the TiO 2 layer is nanocrystalline, which is important to improve the conversion efficiency, which is significantly influenced by the TiO 2 particle dispersivity.There are two chief methods for the production of fine TiO 2 particles (Figure 1).One is a build-up process, such as the hydrothermal method, and another is a breakdown method that uses a stirred media mill (such as a bead mill).TiO 2 particles produced by the buildup process are high purity and have a narrow particle size distribution because the TiO 2 particles can be gradually grown to optimum size without significant aggregation.However, the apparatus for synthesis is expensive and the crystallization process is time consuming; therefore, it is not suitable for mass production.
In contrast, the break-down method has advantages of low introduction costs of the manufacturing devices and the facile mass production, despite the broad particle-size distribution obtained compared with the hydrothermal method, which results from the imperfect dispersion of aggregate particles by bead collisions.However, the control of dispersivity has become possible through the use of computer simulation developed in recent years [2].
There have been many reports regarding the influence of factors such as the layer construction and type of the dye used on the conversion efficiency [3][4][5][6].Although some reports have been published on DSSCs using TiO 2 aggregates synthesized by the hydrothermal method [7][8][9][10], no reports has been published about the particle size distribution using the bead-milling breakdown method, because control of the size distribution by bead milling is quite difficult.In this paper, the particle distribution of P25 titania powder was differed by dispersion control, and the influence of the physical properties of the TiO 2 -coated layer on the PV conversion efficiency of a DSSC was investigated.

Dispersion Experiment and Preparation of TiO 2
Paste.A paint shaker (Paint shaker, Asada Iron Works Co. Ltd., Japan) was employed as the milling system.The beads made of alumina were used and their diameter is 0.1 mm.The 250 cc container made from polyethylene was used.The bead filling ratio was set at the same volume of the dispersion material.The dispersion sample consisted of 15 wt% titania powder (Aeroxide TiO 2 P25, Degussa, Germany) and 4.5 wt% highmolecular-weight acrylic block copolymer dispersant in a mixture of ethanol and terpineol.Three different evaluation samples were prepared with their dispersivity adjusted by changing the mixing ratio of ethanol and terpineol at w/w = 9/1, 7/3, and 5/5, respectively.The dispersion time was 10 h.The particle size distribution was evaluated by a dynamic light scattering (Zetasizer Nano, Malvern Instruments Ltd., England) method.The crystallinity of TiO 2 was analyzed using X-ray diffraction (XRD; Mini Flex II, Rigaku, Japan).

Evaluation of TiO
2 -Coated Layer.The TiO 2 layer used for evaluation of the PV conversion efficiency was made by screen-printing (230 mesh/inch) on fluorine-doped tin oxide (FTO) glass plate and heating at 500 • C for 30 min.The coated layer was photographed and the morphology of the TiO 2 particles was observed using field emission scanning electron microscopy (FE-SEM; S-5200 Hitachi High-Technologies Corporation).The total transmittance and haze ratio of the TiO 2 -coated layer were measured using ultraviolet-visible spectroscopy (UV-vis, Lambda 750, Perkin Elmer, USA).

Preparation of TiO 2
Electrodes. Figure 2 shows an outline of the method for preparation of TiO 2 paste from the dispersion.The TiO 2 paste was prepared by mixing the dispersion and ethyl cellulose dissolved in ethanol and then removal of the ethanol from the mixture.To prepare the DSSC working electrodes, the FTO glass used as current collector (Solar 4 mm thickness, 10 ohm/sq, Nippon Sheet Glass, Japan) was cleaned in a detergent solution using an ultrasonic bath for 15 min and then rinsed with water and ethanol.After treatment in a UV-O 3 surface-cleaning system for 3 min the FTO glass plates were immersed into a 40 mM TiCl 4 aqueous solution at 70 • C for 30 min, and then washed with water and ethanol.A layer of paste was screen printed (230 mesh/inch) on the FTO glass plates, which was then kept in a clean box for 3 min with ethanol to relax the paste film and reduce surface irregularities and then dried for 6 min at 125 • C.This screen-printing procedure (coating, storing, and drying) was repeated to adjust the thickness of the TiO 2 working electrode.The electrodes coated with TiO 2 paste were gradually heated under airflow at 325 • C for 5 min, 375 • C for 5 min, 450 • C for 15 min, and 500 • C for 15 min.

DSSC Assembly.
After measuring the thickness of the layer, the TiO 2 layer was treated with 40 mM TiCl 4 solution, rinsed with water and ethanol, and sintered at 500 • C for 30 min.After cooling to 80 • C, the TiO 2 electrode was immersed into a 0.5 mM N-719 dye solution in a mixture of acetonitrile and tert-butyl alcohol (volume ratio: 1 : 1) and kept at room temperature for 20-24 h to complete the sensitizer uptake.A hole was drilled in the FTO glass (Nippon-Sheet Glass-Pilkington, 15 ohm/sq, 2.2 mm thick) counter electrode to insert the electrolyte into the cell after sealing.A perforated sheet was washed with H 2 O and with a 0.1 M HCl solution in ethanol and cleaned by ultrasonication in an acetone bath for 10 min.After the removal of residual organic contaminants by heating in air for 15 min at 400 • C, a Pt catalyst was deposited on the FTO glass by coating with a drop of H 2 PtCl 6 solution (2 mg Pt in 1 mL ethanol) and repeating the heat treatment at 400 • C for 15 min.The dye-covered TiO 2 electrode and Pt-counter electrode were assembled into a sandwich-type cell and sealed with a 25 mm thick hot-melt gasket made of the ionomer Surlyn 1702 (DuPont).The aperture of the Surlyn frame was 2 mm larger than that of the TiO 2 area, and its width was 1 mm.A drop of the electrolyte, a solution of 0.60 M BMII, 0.03 M I 2 , 0.10 M guanidinium thiocyanate, and 0.50 M 4-tert-butylpyridine in a mixture of acetonitrile and valeronitrile (volume ratio: 85 : 15) was deposited through the hole in the back of the counter electrode.The electrolyte was introduced into the cell via vacuum backfilling.The cell was placed in a small vacuum chamber to remove internal air.Exposure of the cell to ambient pressure again causes the electrolyte to be driven into the cell.Finally, the hole was sealed using a hot-smelt ionomer film (Bynel 4164, 35 μm thick, Du-Pont) and a cover glass (0.1 mm thick).

Photovoltaic Measurement of DSSC.
Photovoltaic measurements were conducted using an AM 1.5 solar simulator.The power of the simulated light was calibrated to be 100 mWcm −2 using a reference Si photodiode equipped with an IR-cutoff filter (Bunkou Keiki, Japan).Current densityvoltage (I-V) curves were obtained by applying an external bias to the cell and measuring the generated photocurrent with a digital source meter.The voltage step and delay time of photocurrent were 10 mV and 40 ms, respectively.
Photo action spectra of dye-sensitized solar cells were measured using pyroelectric energy sensor (PE10-S, Ophir optronics Ltd., Israel) and bandpass filters from 400 nm to 800 nm.

Results and Discussion
The distribution of TiO 2 particles is shown in Figure 3.Each sample has different particle distributions due to the different ratios of ethanol and terpineol used, although the dispersion time used was the same.The mean particle sizes of TiO 2 in samples A, B, and C were 42.5, 56.9, and 73.4 nm, respectively.The primary particle size of P25 TiO 2 is 21 nm; therefore, approximately 2-4 primary particles were aggregated for sample A. The maximum particle size of sample A was around 100 nm.The mean particle size of sample B was 56.9 nm, and the TiO 2 particles were dispersed as aggregates composed of about 2-10 particles.The mean particle size of sample C was 73.4 nm, so that more than 10 TiO 2 particles are agglomerated and individual particles in sample C were largely agglomerated compared with sample A. Therefore, the dispersivity can be controlled according to the solvent blend ratio of ethanol and terpineol used in the dispersion.
Figure 4 shows XRD patterns for each TiO 2 sample.The peaks are confirmed as being almost the same position for all samples and the crystallinity was not degraded by the beadmilling process.The conversion efficiency of the DSSC may change with the crystallinity of TiO 2 , so that TiO 2 particles should be dispersed with consideration of the influence of bead-milling on the crystallinity.

International Journal of Photoenergy
The TiO 2 paste prepared by the method shown in Figure 2 was coated on the FTO glass plates by screenprinting, and then heated at 500 • C for 30 min.Figure 5 shows photographs of the ca. 4 μm coated layers.The coated layer of sample A is translucent; however, samples B and C are opaque.These differences are due to the scattering of light.The scattering of light increases according to (1) to (4) [11][12][13][14][15], where D opt is the particle size where the light scattering becomes the highest, λ is the wavelength of incident light, n 1 and n 2 are the refractive indices of the air and TiO 2 particles, respectively, and m is the ratio of refractive index, which is equal to n 2 /n 1 : When the incident wavelength is assumed to be 400 nm, light scattering becomes the highest for TiO 2 particle sizes of 167, 114, 131, and 145 nm from (1), ( 2), (3), and (4), respectively.That is, the scattering of light increases with the increase in the number of particles over 100 nm.The coated layer of sample A was translucent because the particles in sample A were almost all less than 100 nm (from Figure 3).In contrast, the coated layers of samples B and C appeared white because they consisted of particles over 100 nm.Therefore, the coated layer became significantly opaque due to light scattering of particles with sizes greater than 100 nm present in the coated layer.
Figures 6(a) and 6(b) show the transmittance and haze ratio of the coated layers from UV-vis measurements as a function of wavelength.The transmittance of sample A was higher than those of samples B and C, which had almost comparable transparency.The haze ratio of sample A was lower than those of the other samples for all wavelengths in the visual light range.The haze ratios of samples B and C were almost 100% for wavelengths below 500 nm, due to the light scattering of these samples.
Figure 7 shows FE-SEM images of the morphologies of the coated layers.Each sample was made of P25 TiO 2 nanoparticles heated at 500 • C for 30 min.The difference in the morphologies was attributed to the aggregation-size distribution.The pore size of the coated layer changes when the calcinations temperature is varied [7]; however, the samples were calcined under the same conditions.For sample A, the particles were well dispersed, so that the coated layer was flat and smooth.However, for samples B and C, many voids were clearly evident in the TiO 2 layer.The sizes of the voids in sample C were larger than that in sample B, due to the size of the TiO 2 aggregations (Figure 3).Although the primary particle size was the same, the voids between the TiO 2 aggregates influence the transmittance and haze ratio of the coated layer.It has been reported by previous report [16] that the void makes increasing of scatter light.When the mean particle size becomes large, the voids also may increase from Figure 7. Therefore, scatter light increases under the influence of the particle size and the void.The more a mean particle is large, the more scatter light increases, and then coated layer looks opaque.
Table 1 shows the PV properties of DSSCs prepared from TiO 2 dispersions.The mean particle size of sample A was small, so that the pore size of the coated layer was small.Therefore, the specific surface area of the coated layer was increased and much dye is adsorbed, so that the conversion efficiency increases.In contrast, samples B and C had many large voids in the coated layer, so that high conversion efficiency could not be expected.However, the conversion efficiencies and other PV properties of each of the samples were not significantly different, regardless of the mean particle size of the dispersion.The high transparency of the coated TiO 2 layer means that the incident light can pass through      has higher conversion efficiency than the single-layer DSSCs.The short-circuit density was increased to 1.2 mA/cm 2 and the PV conversion efficiency was improved by 10.1% using the double layer.Therefore, the characteristics of the layer structures can be controlled by changing the size distribution of TiO 2 aggregation in the layer, and the conversion efficiency can be improved easily improved by optimization of the PV characteristics.
Figure 10 shows normalized action spectra.Each cell shows the maximum value around 520 nm.However, it was confirmed that the action spectra differed by the wavelength; in spite of the similar response in the blue light region (400-430 nm), the action spectrum of A + C double layer was improved in the longer wavelength more than 440 nm.Then, the A + C double layer has higher the value of short-circuit photocurrent density than that of the single layer.

Conclusions
TiO 2 powder was dispersed by the bead-milling method, and the dispersivity of TiO 2 was controlled by changing the solvent blend ratio of ethanol and terpineol in the dispersion.The coated layer became significantly opaque due to light scattering when particles greater than 100 nm were present in the coated layer, although the resulting PV effects were very similar, regardless of the mean particle size of TiO 2 aggregations in the dispersion.A double-layer structure was adopted to improve the PV effect, and the photocurrent and conversion efficiency were successfully improved.

Figure 2 :Figure 3 :
Figure 2: Method for the preparation of TiO 2 paste.

Figure 7 : 6 International
Figure 7: FE-SEM micrographs showing the surface morphology of the TiO 2 layers.The mean particle size of samples A, B, and C were 42.4,56.9, and 73.4 nm, respectively.

Figure 8 :Figure 9 :
Figure 8: Schematic diagrams illustrating the effective use of incident light.

Figure 10 :
Figure 10: Photo action spectra of dye-sensitized solar cells, which were normalized to the peak of sample A + C.