Study of Small Molecule Organic Solar Cells Performance Based on Boron Subphthalocyanine Chloride and C 60

The small molecule organic solar cells based on boron subphthalocyanine chloride (SubPc) and C 60 by varying the SubPc layer thickness from 3 nm to 21 nmwere fabricated.Themaximum power conversion efficiency (PCE) of 1.47% was obtained at the 9 nm SubPc layer under 100mW/cm AM1.5G illumination, which is attributed to reach the optimal balance between the light absorption efficiency and the carrier collection efficiency in the device. To increase the open-circuit voltage (Voc) of device, the molybdenum oxide (MoO 3 ) and poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) were inserted between the indium tin oxide and the SubPc layer, respectively. Finally, theVoc of device increased from 0.46V to 1 V by usingMoO3 buffer layer, resulting in the fact that the PCE of device increased from 1.47% to 2.52%.


Introduction
Solar cells are considered as an important source of renewable energy to solve the shortage of energy today.Various solar cells have been developed and one of the most promising solar cells is organic solar cells (OSCs).OSCs have received much attention recently due to several potential applications, including compatibility with flexible substrates, lowmanufacturing cost, and roll-to-roll fabrication process [1][2][3].In organic materials, light absorption leads to the formation of excitons (bound electron-hole pairs) rather than the free electron-hole pairs.The excitons dissociation occurred at the donor-acceptor interfaces, using the difference of energy level to overcome the binding energy of excitons, leading to the free electron and hole in device which can be extracted to the electrodes.Since Tang reported the first two-layer heterojunction OSC [4], the power conversion efficiency of OSCs had increased steadily in the recent years by using new materials and the different device structures [5][6][7][8].The shortage of organic materials is narrow absorption range in visible region, which leads to the low short-circuit current density ( sc ).Therefore, to get the highest  sc for the best performance, optimizing the device structure is necessary [9,10].
Boron subphthalocyanine chloride (SubPc) is a promising donor material for the small molecule OSCs due to its deep highest occupied molecular orbital (HOMO) energy level, which can get the higher  oc of device.In this paper, we used SubPc as donor and changed the thickness of SubPc layer to investigate the influences on performance and to obtain the optimal thickness of SubPc for the best efficiency.In addition, the  oc variation of device with different SubPc layer thicknesses and anode buffer layers is also investigated in detail.

Experimental
The indium tin oxide (ITO)/glass substrates (with a sheet resistance of 7 Ω/sq) are sequentially cleaned by ultrasonic treatment in acetone, isopropyl alcohol, and deionized water and blown by N 2 gas before deposition.The layer of poly ( (PEDOT:PSS) was formed by a spin-coating method.The spin coatings were performed at a rotation rate of 3500 rpm for 20s.The organic materials in the device were MoO 3 (99%), SubPc (99%), C 60 (99.95%), and BCP (99%), which were used without further purification.All layers in OSC were deposited at a deposition rate of 0.02∼0.04nm/s below the pressure of 6.4 × 10 −4 Pa.The Ag as a cathode was deposited at a deposition rate of 0.2∼0.3nm/s by thermal evaporation through a shadow mask, giving an active area of 6 mm 2 .The thickness of thin film was monitored by an oscillating quartz thickness monitor.The configurations of device and the energy level in this study are shown in Figure 1.
The current-voltage characteristics are measured with a Keithley 2400 sourcemeter, under an illumination of 100 mW/cm 2 with an AM1.5G sun simulator.The intensity of irradiation was measured by an optical power meter.All measurements were carried out in air without any encapsulation.

Results and Discussion
Figure 2 showed the current density-voltage (-) characteristics of device (ITO/SubPc (3∼21 nm)/C 60 (30 nm)/BCP (10 nm)/Ag) with different SubPc layer thicknesses.The performance parameters and the series resistance (  ) were listed in Table 1.The SubPc layer thickness of device has not only influence on the amount of light absorption but also influence on the ability of carrier transportation in device.Both of light absorption and the   increased as the SubPc layer thickness increased.In Table 1, the  sc of device increased from 3.70 mA/cm 2 to 5.79 mA/cm 2 when the SubPc layer thickness from 3 nm to 9 nm, which is attributed to the more light absorption with thicker SubPc layer.However, the advantage of SubPc as an electron donor in device was not revealed, high  oc value, which will be discussed later.
It was found that the   of device with 12 nm SubPc layer is nearly four times than that of device with 9 nm SubPc layer, indicating that the carrier extracted from SubPc to ITO became hard as the thickness of SubPc layer exceeds 9 nm.It might result from the short diffusion length of SubPc which is only about 8 nm [11].As a result, the  sc of device continually decreased from 5.79 mA/cm 2 to 3.47 mA/cm 2 corresponding to the SubPc layer thickness from 9 to 21 nm.The fill factor (FF) of device is associated with the   , and the change of FF is consistent with the   variation.As the   of device increased, the FF of device decreased.Finally, the optimal balance between light absorption and carrier transportation was obtained at 9 nm SubPc, resulting in higher efficiency of 1.47% at 9 nm SubPc than that of device with other SubPc layer thicknesses.
The  oc of device increased as the SubPc layer thickness increased from 3 nm to 15 nm and then saturation at 0.58 ± 0.1 V from 15 nm to 21 nm.The tendency of  oc variation is in agreement with the result obtained by Kim and Yim [12].To investigate the origin of  oc which varied as a function of SubPc layer thickness, the surface morphologies of different SubPc layer thicknesses deposited on ITO/glass substrate were measured.Figure 3 showed the height profiles of bare ITO, 3 nm SubPc, 6 nm SubPc, and 9 nm SubPc deposited on ITO, respectively.It can be seen that the roughness of bare ITO is as high as 7 nm, resulting in that the vacancy of ITO cannot be fully covered by the 3 nm or 6 nm SubPc layer (as shown in Figures 3(b) and 3(c)).As a result, the contact between the ITO and the C 60 after depositing C 60 on SubPc layer cannot be avoided, causing that the  oc of device with 3 nm and 6 nm SubPc is only at 0.34 V and 0.32 V, respectively.In contrast, the 9 nm SubPc layer is thicker enough to cover the roughness of ITO, which can avoid the contact between ITO and C 60 , resulting in that the  oc of device with 9 nm SubPc layer is enhanced to 0.46 V.However, the  oc of device still continually increased from 0.46 V to 0.59 V as the SubPc layer thickness increased from 9 nm to 15 nm.It results from the carrier accumulation in SubPc layer, which can be realized from the   which dramatically increased, resulting in the increase of electric potential in SubPc layer.The  oc of device was maintained in a value at SubPc layer thickness from 15 nm to 21 nm, and it is due to the fact that the amount of carrier accumulated in SubPc layer is saturated.That is to say, the balance of carrier generation and recombination was achieved at SubPc layer thickness above 15 nm, leading to that the amount of carrier is the same in SubPc layer.However, the  oc of device based on SubPc and C 60 is still lower than that of other studies which also used the same materials.In theorem, the maximum  oc of OSCs is limited by the energy difference between the HOMO energy level of donor and the lowest unoccupied molecular orbital (LUMO) energy level of acceptor [13], and the  oc in device is determined by difference of work function of electrodes within the maximum  oc [14].From Figure 1, the energy level difference between HOMO of SubPc and the LUMO of C 60 is 1.1 V.The  oc of devices with different SubPc layer thicknesses ranges from 0.32 V to 0.59 V, which is far from 1.1 V.The results were attributed to the low work function of ITO typically at 4.7 V. To improve the work function of ITO, the MoO 3 layer and the PEDOT:PSS inserted between the ITO and the SubPc layer in the device with optimal SubPc layer thickness of 9 nm, respectively.The performance parameters were summarized in Table 2.The  oc of device was enhanced to 0.77 V and 1 V by inserting the PEDOT:PSS and the MoO 3 layer, respectively.The surface morphologies of bare ITO, ITO/PEDOT:PSS, and ITO/MoO 3 were measured to further clarify whether the  oc enhancement is attributed to the roughness of ITO. Figure 4 showed the AFM images of bare ITO, ITO/PEDOT:PSS, and ITO/MoO 3 corresponding to  the root mean square roughness of 3.73 nm, 2.08 nm, and 3.92 nm, respectively.It can be seen that the MoO 3 cannot smooth the ITO surface, indicating that the enhancement of  oc was not related to the roughness of ITO.As a result, the improvement of  oc can be ascribed to the work function of ITO modification by the PEDOT:PSS and the MoO 3 .In addition, the  oc of device using MoO 3 as a buffer layer is higher than that of device with PEDOT:PSS buffer layer due to the fact that the HOMO energy level of MoO 3 is deeper than that of PEDOT:PSS.The PEDOT:PSS layer was not optimized here, causing that the efficiency of device decreased from 1.47% to 1.13% by using PEDOT:PSS buffer layer.Eventually, the advantage of small molecule OSC based on the SubPc and the C 60 , high  oc , was achieved by depositing the MoO 3 layer on the ITO, resulting in the efficiency improvement from 1.47% to 2.56%.

Conclusions
The performances of devices with different SubPc layer thicknesses have been investigated.The maximum  sc and FF were achieved simultaneously at 9 nm SubPc, which is attributed to reach the optimal balance between the light absorption efficiency and the carrier collection efficiency in device, resulting in the efficiency of 1.47%.In addition, to obtain the highest  oc of device not only needs the deepest HOMO level of donor but also needs the highest work function of anode.The  oc of device by using MoO 3 as a buffer layer is better than that of device using PEDOT:PSS.As a result, the  oc is greatly improved from 0.46 V to 1 V by inserting the MoO 3 layer between the ITO and SubPc layer, leading to an increase in efficiency of device from 1.47% to 2.52%.