Macroporous TiO2 photocatalyst was synthesized by a facile nanocasting method using polystyrene (PS) spherical particles as the hard template. The synthesized photocatalyst was characterized by transmission electron microscope (TEM), scanning electron microscopy (SEM), thermogravimetry-differential thermogravimetry (TG-DTG), X-ray diffraction (XRD), and N2-sorption. TEM, SEM, and XRD characterizations confirmed that the macroporous TiO2 photocatalyst is composed of anatase phase. The high specific surface area of 87.85 m2/g can be achieved according to the N2-sorption analysis. Rhodamine B (RhB) was chosen as probe molecule to evaluate the photocatalytic activity of the TiO2 catalysts. Compared with the TiO2 materials synthesized in the absence of PS spherical template, the macroporous TiO2 photocatalyst sintered at 500°C exhibits much higher activity on the degradation of RhB under the UV irradiation, which can be assigned to the well-structured macroporosity. The macroporous TiO2 material presents great potential in the fields of environmental remediation and energy conversion and storage.
1. Introduction
For the environment protection purpose, the disposal of various toxic dyes from the textile industry has attracted extensive attention. Rhodamine B (RhB) is widely used as a colorant in textiles and food stuffs and is also a well-known water tracer fluorescent [1]. It is harmful to human beings and animals and causes irritation of the skin, eyes, and respiratory tract.
Owing to high photocatalytic efficiency, good oxidation capability, stable chemical reaction, low cost, and nontoxicity, titanium dioxide (TiO2) has been applied widely in wastewater treatment [2–4], environment purification [5, 6], solar energy transfer [7, 8], chemical sensing [9, 10]. Recently, it was found that incorporation of well-defined porosity of TiO2 materials could greatly enhance the photoactivity in the area of environmental remediation and energy conversion [11–13]. For a variety of practical applications, the fabrication of desired structure with network is important as well as control in grain size, crystallinity, and composition [14–16].
At present, porous TiO2, combining the outstanding properties of TiO2 with their porous structure, has gained great research interests, and various synthetic techniques had been developed. For example, Liu et al. prepared anatase TiO2 porous thin films by sol-gel method with CTAB surfactant as a pore-forming agent, and many factors were studied [17]. Bala et al. fabricated hollow spheres of anatase TiO2 by spherical CaCO3 nanoparticles as a template and investigated the photocatalytic activity [18]. Zheng et al. synthesized rutile and anatase TiO2 mesoporous single crystals with diverse mophologies by silica-templated hydrothermal method [19]. Dong et al. prepared highly ordered transparent TiO2 macropore arrays via a glass-clamping method and investigated the potential application in degradation of organic dyes [20]. However, the general synthesis usually involved complicated multistep to obtain porous skeleton. Firstly, it is required to assemble spheres into colloidal crystals as templates, and then the precursor is filled into interstices among the crystals for several times [21–23]. Moreover, for an efficient photodegradation catalyst, the macroporous structure is essential due to the run-through-macropore network which maximizes the uptake and the diffusion of the organic molecules [24–26]. Additionally, the porous structures are propitious to enhance the light scattering and improve the utilization rate of irradiation light [27–29].
Herein, a simple method without assembly and filling steps was introduced in this work for the preparation of macroporous TiO2 through a sol-gel process using polystyrene spheres as sacrificial templates. Compared with the TiO2 materials synthesized in the absence of PS spherical template [30, 31], the macroporous TiO2 photocatalyst sintered at 500°C exhibits much higher activity on the degradation of RhB under the UV irradiation. The macroporous TiO2 material present great potential in the fields of environmental remediation and energy conversion and storage.
2. Experiment2.1. Materials
Tetrabutyl titanate (Ti(OC4H9)4), sodium styrene sulfonate, sodium hydrogen carbonate, potassium persulfate, ethanol, Rhodamine B (RB), acetic acid, and nitric acid were all analytical grade and used without further purification. Styrene was washed by 5% NaOH solution several times to remove polymerization inhibitor. All of the reagents were purchased from Shanghai Chemical Reagent Ltd. Co.
2.2. Preparation of PS Microspheres
PS spheres were obtained by emulsion polymerization of styrene according to previous reports [32–34]. At first, 150 g deionized water was poured into a 300 mL jacket reactor, which was kept at 85°C until the end of the reaction. Then, 0.08 g sodium styrene sulfonate as the emulsifier and 0.0633 g sodium hydrogen carbonate as the buffer were dissolved in the deionized water. Under constant stirring, 18.30 mL styrene monomer was added to this solution, accompanied with nitrogen protection. After 1 h, 0.0833 g potassium persulfate as an initiator was introduced into the solution. After 18 h polymerization, the monodispersed PS spheres with the average diameter of 278 nm were obtained, and the standard deviation of spheres was less than 2.76%.
2.3. Preparation of TiO2 Sol
With the Ti(OC4H9)4 as precursor, ethanol as solvent and glacial acetic acid as inhibitor, TiO2 sol was synthesized by sol-gel method according to references elsewhere [35, 36]. The procedure can be divided into three steps. At first, solution A was prepared by mixing 3 mL deionized water and 16 mL absolute ethyl alcohol. And then solution B was obtained by adding 10 mL Ti(OC4H9)4 and 2 mL glacial acetic acid into 32 mL ethanol slowly with the rapid stirring. At last, solution A was dripped slowly into solution B under rapid stirring. The homogeneous and transparent solution of TiO2 sol was thus obtained.
2.4. Preparation of Macroporous TiO2
In a typical synthesis of macroporous TiO2, 11 mL PS spheres suspension with the concentration of 5.88 wt% was added slowly into 10 mL as-prepared TiO2 sol. The intimate mixture was obtained by stirring and ultrasonication. Then, the mixture was placed in an oven at 70°C for 12 h and then TiO2/PS sphere composites were obtained. To prepare macroporous TiO2, the as-obtained composites were sintered in muffle furnace at 500°C for 2 h in air. The ultima product was denoted as m-TiO2. For contrast, the synthesis of TiO2 nanoparticles was the similar to the preparation of macroporous TiO2 without adding the PS spheres, which was labeled as r-TiO2.
2.5. Characterization
Field emission scanning electron microscopy (FE-SEM) was carried out on FEI Sirion-200 and transmission electron microscopy TEM was taken on JEOL JEM-2100. The XRD patterns of the synthesized samples were obtained by a Bruker-AXS D8 Advance diffractometer with CuKα radiation (λ = 0.15418 nm). To determine the proper sintering temperature and analyze the weight content of PS spheres in the TiO2/PS composites, both the as-prepared PS spheres and TiO2/PS composites were investigated by thermogravimetry and derivative thermogravimetry (TG-DTG), which was operated at a program-controlled temperature elevation rate of 10°C/min in the air. N2 adsorption-desorption isotherms were measured on a Quantachrome NOVA 2000e sorption analyzer at liquid nitrogen temperature (77 K). The samples were degassed at 120°C overnight prior to the measurement. The surface areas were calculated by the multipoint Brunauer-Emmett-Teller (BET) method.
2.6. Photocatalytic Experiment
The photocatalytic activity tests of the synthesized TiO2 were performed by the degradation of Rhodamine B (RhB) under UV light irradiation under ambient conditions. The experiment was performed in a water-jacket reactor operated at 20°C. The light source was a 450 W high-pressure mercury lamp (Foshan Electrical and Lighting Co. Ltd.) with a strong peak centered at 362 nm. The distance between the sample and the lamp was about 10 cm. In a typical process, 0.1 g of the obtained product was placed into 100 mL of RhB aqueous solution (2×10-5 mol/L) under magnetic stirring. 5 mL of the mixture was collected at a given time interval of 15 min and was then centrifuged to discard any sediment. Then the concentration of RhB was determined on a TU-1810 UV-vis spectrophotometer at λmax=553nm [37, 38]. The decomposition efficiency of RhB was calculated by the following formula:
(1)Decompositionefficiency=A0-AtA0×100%,
where A0 and At represent the absorbance of the RhB solution before irradiation and the absorbance at time t, respectively.
3. Results and Discussion3.1. Material Characterization
TG-DTG curves of both PS spheres and the TiO2/PS composites are shown in Figure 1. For PS spheres, three weight loss stages, below 300, 300–400, and 400–500°C, can be observed. The PS spheres undergo endothermic desorption of physically adsorbed water and residual solvent at low temperature below 300°C. The major weight loss of about 90% between 300 and 400°C can be assigned to the thermal decomposition of the polystyrene, which was decomposed from long chain to shorter chain and then depolymerized into volatile monomers with low molecular weight. While, the third stage in the range of 400–500°C can be attributed to the combustion of the residual coke. With respect to the TiO2/PS nanocomposite, it is found that PS spheres can be completely removed at 500°C (Figure 1(b)). Thus, 500°C was selected as the calcination temperature to prepare the macroporous TiO2 photocatalyst. The weight content of TiO2 in the TiO2/PS nanocomposite is calculated to be 43.2%.
TG-DTG curves of the PS spheres (a) and the TiO2/PS composite.
XRD are employed to characterize the crystallite structure of the synthesized TiO2 catalysts. It can be seen from Figure 2(a) that the diffraction peaks of TiO2 after being calcinated at 450°C can be indexed to anatase phase TiO2 (JCPDS NO. 21-1272) and rutile phase TiO2 (JCPDS NO. 21-1276), indicating that the sample calcined at 450°C is composed of bicrystalline phase. When the calcination temperature was increased to 500°C, all diffraction peaks can be indexed to pure anatase phase (JCPDS NO. 21-1272), and no characteristic peaks of other impurities can be detected. Thus, 500°C is a proper sintering temperature to prepare anatase phase macroporous TiO2, which is in accordance with the TG-DTG analysis (Figure 1). The sharp diffraction peaks in Figure 2(b) illustrate the well crystallization of m-TiO2 after the heat treatment. The crystallite size (D) was calculated to be about 10 nm according to the Scherrer formula D=Kλ/βcosθ [39], where K is a constant (shape factor, about 0.9), λ is the X-ray wavelength (0.15418 nm), β is the full-width at half-maximum, and θ is the diffraction angle. The values of β and θ were taken from TiO2 (101) diffraction line.
XRD patterns of TiO2 prepared through calcining the TiO2/PS composite at different temperatures: (a) 450°C and (b) 500°C.
TEM images of the PS spheres and m-TiO2 are given in Figure 3. Figure 3(a) shows the TEM image of the PS spheres. The size of the PS spheres is about 278 nm, and the standard deviation of monodispersed spheres is less than 2.76%. This indicates that the PS spheres are suitable to be employed as macroporous templates. As shown in Figure 3(b), the PS spheres are wrapped by TiO2 nanoparticles before being sintered. Figure 3(c) shows the low-magnification TEM image of macroporous TiO2 sintered at 500°C in air, from which macropores can be clearly seen, suggesting that PS spheres have been completely removed after calcination at 500°C in air. And the SEM image (Figure 3(e)) also demonstrates well-defined macroporous structure. The size of the hollow spheres is about 240 nm, which is smaller than the size of original PS spheres template, suggesting the significant shrinkage after the PS removal via calcination. Additionally, Figure 3(c) also illustrates that run-through-macropore network structure was formed. And the SEM images in Figure 3(e) further confirm that the macropores left by the templates are interconnective with neighboring hollow spheres. High-resolution TEM image (Figure 3(d)) displays that the crystalline size of TiO2 nanoparticles is about 10 nm, which is in good agreement with the XRD analysis.
Low-magnification TEM images of (a) the PS spheres, (b) the TiO2/PS composites, (c) the m-TiO2 catalyst after calcination at 500°C, and the high-resolution TEM image (d) and SEM image (e) of the m-TiO2 sample.
N2 adsorption-desorption measurements were performed to investigate the textural properties of the macroporous TiO2. The N2 adsorption-desorption isotherms of r-TiO2 and m-TiO2 are shown in Figure 4. One can see that the isotherm of the r-TiO2 is of typical type IV, characteristic of mesoporous materials, according to IUPAC classification. The adsorbed nitrogen volume for m-TiO2 becomes steep in the P/P0 range of 0.8–1.0, which indicates the presence of large macropores. Based on the Brunauer-Emmett-Teller (BET) equation, the specific surface areas of r-TiO2 and m-TiO2 were evaluated to be about 91.2 and 87.8 m2/g, respectively.
Nitrogen adsorption-desorption isotherms of the r-TiO2 and m-TiO2 after calcination at 500°C for 2 h.
3.2. Photocatalytic Activity Test
The photocatalytic activities of the prepared TiO2 samples were examined through the photodegradation of RhB under UV light irradiation. The degradation efficiency was illustrated by the change of the RhB concentration during the photodegradation process and the results were shown in Figure 5. The photocatalytic results reveal that the photocatalytic activity of the macroporous TiO2 was significantly improved as compared to that of the traditional TiO2 nanoparticles. For the macroporous TiO2, 92.63% of the RhB was decomposed after 2 h irradiation. However, as to the r-TiO2 sample, the degradation percentage is only 81.66%. Here, the macroporous structure is believed to facilitate the transportation of reactant molecules and products through the interior space due to the run-through-macropore networks [40–43] and to favor the harvesting of exciting light due to enlarged surface area and multiple scattering within the porous framework [43, 44]. So the enhanced photoactivity of m-TiO2 could be achieved.
Degradation efficiency curves of RhB for the r-TiO2 and m-TiO2 after calcination at 500°C for 2 h.
4. Conclusions
In summary, macroporous TiO2 photocatalyst was successfully synthesized via a simple sol-gel method using polystyrene spheres as sacrificial templates. The prepared macroporous TiO2 exhibited higher photocatalytic activity than the TiO2 sample through a template-free approach in catalyzing the degradation of RhB under UV light illumination. And the superior photocatalytic performance can be related to the run-through-macropore network structure. Considering the facile preparation and high photocatalytic activity, the macroporous TiO2 materials display a good potential in the fields of environmental remediation and energy conversion and storage.
Conflict of Interests
The authors have no conflict of interests in relation to the instrumental companies directly or indirectly.
Acknowledgments
This work was supported by the National Natural Science Foundation of China (U1361119, 51174077), Specialized Research Fund for the Doctoral Program of Higher Education (20124116120002), the Education Department Key Programs for Science and Technology Research of He’nan Province (13A430336, 2011A480003).
RichardsonS. D.WillsonC. S.RuschK. A.Use of rhodamine water tracer in the marshland upwelling system20044256786882-s2.0-4444267780RyuJ.ChoiW.Substrate-specific photocatalytic activities of TiO2 and multiactivity test for water treatment application20084212943002-s2.0-3754900211810.1021/es071470xCuiH.LiuH.ShiJ.WangC.Function of TiO2 lattice defects towards photocatalytic process: view of electronic driven force201320131610.1155/2013/364802364802ChouP.MatsuiS.MisakiK.MatsudaT.OH radical formation at distinct faces of rutile TiO2 crystal in the procedure of photoelectrochemical water oxidation2013117452383223839DaghrirR.DroguiP.RobertD.Modified TiO2 for environmental photocatalytic applications: a review2013521035813599HuangH.HuangH.HuP.YeX.LeungD. Y. C.Removal of formaldehyde using highly active Pt/TiO2 catalysts without irradiation20132013610.1155/2013/350570350570GiovannettiR.ZannottiM.AlibabaeuL.FerraroS.Equilibrium and kinetic aspects in the sensitization of monolayer transparent TiO2 thin films with porphyrin dyes for DSSC applications20142014910.1155/2014/834269834269WangB.KerrL. L.Stability of CdS-coated TiO2 solar cells2012163109110972-s2.0-8485926575310.1007/s10008-011-1496-3PhanichphantS.LiewhiranC.WetchakunK.WisitsoraatA.TuantranontA.Flame-made Nb-doped TiO2 ethanol and acetone sensors20111114724842-s2.0-7925165039010.3390/s110100472JiangL.-C.ZhangW.-D.Electrodeposition of TiO2 nanoparticles on multiwalled carbon nanotube arrays for hydrogen peroxide sensing20092189889932-s2.0-6534917096310.1002/elan.200804502Tajer-KajinebafV.SarpoolakyH.MohammadiT.Synthesis of nanostructured anatase mesoporous membranes with photocatalytic and separation capabilities for water ultrafiltration process201320131110.1155/2013/509023509023GuoC. S.GeM.LiuL.GaoG.FengY.WangY.Directed synthesis of mesoporous TiO2 microspheres: catalysts and their photocatalysis for bisphenol A degradation20104414194252-s2.0-7534910368710.1021/es9019854ParkY.-C.ChangY.-J.KumB.-G.KongE.-H.SonJ. Y.KwonY. S.ParkT.JangH. M.Size-tunable mesoporous spherical TiO2 as a scattering overlayer in high-performance dye-sensitized solar cells20112126958295862-s2.0-7995946409110.1039/c1jm11043hNgC. J. W.GaoH.Yang TanT. T.Atomic layer deposition of TiO2 nanostructures for self-cleaning applications200819442-s2.0-5814923699110.1088/0957-4484/19/44/445604445604BianZ.ZhuJ.CaoF.HuoY.LuY.LiH.Solvothermal synthesis of well-defined TiO2 mesoporous nanotubes with enhanced photocatalytic activity20104644845184532-s2.0-7804941031110.1039/c0cc02998jZhangH. Z.DongF.ZhaiS. N.KangX. J.FangS. M.Preparation of ordered TiO2 macroporous membrane using PBMA colloid crystal as template2012399–4016776822-s2.0-8375522521310.4028/www.scientific.net/AMR.399-401.677LiuG. Q.JinZ. G.LiuX. X.WangT.LiuZ. F.Anatase TiO2 porous thin films prepared by sol-gel method using CTAB surfactant200741149552-s2.0-3384596417910.1007/s10971-006-0122-9BalaH.YuY.ZhangY.Synthesis and photocatalytic oxidation properties of titania hollow spheres20086214207020732-s2.0-4064908437310.1016/j.matlet.2007.11.038ZhengX.KuangQ.YanK.QiuY.QiuJ.YangS.Mesoporous TiO2 single crystals: facile shape-, size-, and phase-controlled growth and efficient photocatalytic performance20135211124911257DongY.ChaoJ.XieZ.XuX.WangZ.ChenD.Highly ordered TiO2 macropore arrays as trandparent photocatalysts20122012676251010.1155/2012/762510JiangP.CizeronJ.BertoneJ. F.ColvinV. L.Preparation of macroporous metal films from colloidal crystals199912134795779582-s2.0-003319855010.1021/ja991321hSadakaneM.HoriuchiT.KatoN.TakahashiC.UedaW.Facile preparation of three-dimensionally ordered macroporous alumina, iron oxide, chromium oxide, manganese oxide, and their mixed-metal oxides with high porosity20071923577957852-s2.0-3634895028910.1021/cm071823rDavisM.RamirezD. A.Hope-WeeksL. J.Formation of three-dimensional ordered hierarchically porous metal oxides via a hybridized epoxide assisted/colloidal crystal templating approach201351677867792KimuraT.MiyamotoN.MengX.OhjiT.KatoK.Rapid fabrication of mesoporous titania films with controlled macroporosity to improve photocatalytic property200949148614932-s2.0-6964909464510.1002/asia.200900154LiX.-Y.ChenL.-H.LiY.RookeJ. C.WangC.LuY.KriefA.YangX.-Y.SuB.-L.Self-generated hierarchically porous titania with high surface area: photocatalytic activity enhancement by macrochannel structure201236811281382-s2.0-8485585853310.1016/j.jcis.2011.10.018ZhangR.-F.YeJ.LongN.-B.Large-sized TiO2/SiO2 macroporous materials for photodegradation of organic compounds in water and air2011306-307115711612-s2.0-8005306625810.4028/www.scientific.net/AMR.306-307.1157SzymanskiL.SuroliaP.ByrneO.ThampiK. R.StubenrauchC.Porous “sponge-like” anatase TiO2 via polymer templates: synthesis, characterization, and performance as a light-scattering material20132914805815HuangF. Z.ChenD. H.ZhangX. L.CarusoR. A.ChengY.-B.Dual-function scattering layer of submicrometer-sized mesoporous TiO2 beads for high-efficiency dyesensitized solar cells2010208130113052-s2.0-7795103864110.1002/adfm.200902218YanT.LiL.LiG.WangY.HuW.GuanX.Porous SnIn4S8 microspheres in a new polymorph that promotes dyes degradation under visible light irradiation201118612722792-s2.0-7955154740810.1016/j.jhazmat.2010.10.114CappellettiG.TiO2 nanoparticles: traditional and novel synthetic methods for photocatalytic paint formulations2010Nova Science Publishers213254YurdakalS.TekB. S.AlagözO.Photocatalytic selective oxidation of 5-(Hydroxymethyl)-2-furaldehyde to 2,5-Furandicarbaldehyde in water by using anatase, rutile, and brookite TiO2 nanoparticles201315456461ZhouQ.DongP.YiG.-Y.LiuL.-X.ChengB.-Y.Preparation of TiO2 inverse opal via a modified filling process2005225115511582-s2.0-2414448471410.1088/0256-307X/22/5/036WangX.-D.DongP.YiG.-Y.Evaporation self-assembly method to fabricate high-quality polystyrene microsphere colloid crystal2006554209220982-s2.0-33646347404WangX.-D.YiG.-Y.LiuY.Preparation of Al2O3 catalytic material with run-through-macropore network structure20093023493542-s2.0-64749112491WangC.DengZ.-X.ZhangG.FanS.LiY.Synthesis of nanocrystalline TiO2 in alcohols2002125139442-s2.0-003707121910.1016/S0032-5910(01)00523-XLiY.WhiteT. J.LimS. H.Low-temperature synthesis and microstructural control of titania nano-particles20041774-5137213812-s2.0-164242183410.1016/j.jssc.2003.11.016SoaresE. T.LansarinM. A.MoroC. C.A study of process variables for the photocatalytic degradation of rhodamine B200724129362-s2.0-34250196150ByrappaK.SubramaniA. K.AnandaS.Lokanatha RaiK. M.DineshR.YoshimuraM.Photocatalytic degradation of rhodamine B dye using hydrothermally synthesized ZnO20062954334382-s2.0-3384559725310.1007/BF02914073KlongH. P.AlexanderL. E.1954New York, NY, USAWileyYuanZ.-Y.SuB.-L.Insights into hierarchically meso-macroporous structured materials20061676636772-s2.0-3364567124210.1039/b512304fParlettC. M. A.WilsonK.LeeA. F.Hierarchical porous materials: catalytic applications20134238763893YuJ. G.LiuS. W.YuH. G.Microstructures and photoactivity of mesoporous anatase hollow microspheres fabricated by fluoride-mediated self-transformation2007249159662-s2.0-3424967030310.1016/j.jcat.2007.03.032KauneG.MemesaM.MeierR.RudererM. A.DiethertA.RothS. V.DacunziM.GutmannJ. S.Müller-BuschbaumP.Hierarchically structured titania films prepared by polymer/colloidal templating2009112286228692-s2.0-7795395721510.1021/am900592uWangX. C.YuJ. C.HoC.HouY. D.FuX. Z.Photocatalytic activity of a hierarchically macro/mesoporous titania2005216255225592-s2.0-1584437159910.1021/la047979c