Orthodontic treatment is increasingly popular as people worldwide seek esthetics and better quality of life. In orthodontic treatment, complex appliances and retainers are placed in the patients’ mouths for at least one year, which often lead to biofilm plaque accumulation. This in turn increases the caries-inducing bacteria, decreases the pH of the retained plaque on an enamel surface, and causes white spot lesions (WSLs) in enamel. This article reviews the cutting-edge research on a new class of bioactive and therapeutic dental resins, cements, and adhesives that can inhibit biofilms and protect tooth structures. The novel approaches include the use of protein-repellent and anticaries polymeric dental cements containing 2-methacryloyloxyethyl phosphorylcholine (MPC) and dimethylaminododecyl methacrylate (DMAHDM); multifunctional resins that can inhibit enamel demineralization; protein-repellent and self-etching adhesives to greatly reduce oral biofilm growth; and novel polymethyl methacrylate resins to suppress oral biofilms and acid production. These new materials could reduce biofilm attachment, raise local biofilm pH, and facilitate the remineralization to protect the teeth. This novel class of dental resin with dual benefits of antibacterial and protein-repellent capabilities has the potential for a wide range of dental and biomedical applications to inhibit bacterial infection and protect the tissues.
School of Dentistry, University of MarylandUniversity of Maryland, Baltimore CountyNational Natural Science Foundation of China81671032National Key R&D Program of China2017YFC1104304Beijing HospitalsZYLX2017031. Introduction
Orthodontic treatment is increasingly more popular as it can improve the facial esthetics, reduce the occurrence of dental diseases and injuries, enhance the oral functions, correct malocclusion, and minimize the psychosocial problems associated with poor dental and facial appearance. Complex appliances and retainers will be placed in the patients’ mouths for at least one year, which may facilitate the plaque aggregation despite good oral hygiene [1]. With the increase of plaque accumulation, the level of caries-inducing bacteria, especially Streptococcus mutans, is elevated, and the pH of the retained plaque on the enamel surface adjacent to the orthodontic brackets is decreased. This in turn hinders the remineralization process and causes decalcification [2–6]. The first clinical evidence of demineralization in tooth enamel is seen as white spot lesions (WSLs), which are defined as the “subsurface enamel porosity from carious demineralization” that presents as “a milky white opacity” [1–3, 7–10]. The incidence of WSLs in fixed orthodontic treatments is as high as 60.9%, and the demineralization can become noticeable around the brackets as early as 4 weeks after the beginning of multibracket appliance treatment [1, 10].
Several methods were investigated to inhibit WSLs, such as educating and motivating the patient, mechanical plaque control and removal, modifying diet (low carbohydrate), and treating with topical fluoride [9–11]. However, these strategies require good long-term patient compliance and therefore are unreliable, especially in children and teenagers [11–13]. Consequently, novel preventive measures that do not rely on patient compliance need to be developed to prevent WSLs.
One promising approach is the development of antibacterial and protein-repellent materials [11, 14–17]. Quaternary ammonium methacrylates (QAMs) have been incorporated into dental resins to inhibit bacterial growth and plaque formation because of their excellent antibacterial potency [14–17]. Salivary proteins in the mouth can adhere to a clean polymer surface, providing anchor points for bacteria attachment, which is the first step in biofilm formation [18, 19]. Accordingly, efforts were made to develop novel protein-repellent dental materials to prevent the adsorption of proteins from the acquired pellicle [11, 20, 21]. Recently, protein-repellent dental cements, adhesives, and methacrylate resins were developed for the first time to repel bacterial adhesion, decrease acid production, and protect tooth structures. This article reviews the new generation of nanostructured, bioactive, and therapeutic dental materials with protein-repellent and anticaries properties.
2. Antibacterial and Protein-Repellent Orthodontic Cement to Inhibit WSLs
Fixed orthodontic appliances contribute to the adhesion of oral bacteria due to their complex design and irregular surfaces. These features limit the naturally occurring self-cleaning mechanisms and restrict proper preventive measures, thus resulting in enamel demineralization [1, 2]. Indeed, Lucchese and Gherlone [1] showed that the levels of acidogenic bacteria, such as Streptococcus mutans and lactobacilli, increased significantly in orthodontic patients, leading to WSLs around the orthodontic appliances. These lesions, which are characterized by their opacity, mineral loss, and decrease of fluorescence radiance, were commonly seen on the buccal surfaces of the teeth, around the brackets, especially in the gingival area [1, 2].
To effectively inhibit the prevalence of WSLs, the most important strategy is to prevent demineralization and biofilm formation [9]. Resin-modified glass ionomer cements (RMGIs) have been used for bracket-bonding cements due to their fluoride- (F-) releasing capabilities and acceptable bond strengths [11]. However, researchers found that RMGIs could accumulate more bacteria due to their relatively rough surfaces, high-surface free energy, and polarity [22, 23]. In addition, RMGIs were unable to change the low-pH environment, which hindered the remineralization [24]. Therefore, it would be beneficial to add antimicrobial agents into RMGIs to inhibit protein adsorption, diminish biofilm adhesion, reduce acid production, and thereby prevent or minimize WSLs.
Previous studies incorporated QAMs into dental materials because they reduced the biofilm growth and viability [11, 15, 16, 25–27]. Novel dental materials with 12-methacryloyloxydodecylpyridinium bromide (MDPB), methacryloxylethyl cetyl dimethyl ammonium chloride (DMAE-CB), and cetylpyridinium chloride (CPC), as well as other compositions, effectively hindered bacteria and biofilm growth [28–34]. The antibacterial potency increased with increasing the alkyl chain length (CL) from 3 to 16, with DMAHDM having CL of 16 showing the strongest bactericidal potency [34]. Another bactericidal agent, nanoparticles of silver (NAg), effectively suppressed a wide range of microorganisms due to Ag ion release [35].
One drawback of the contact inhibition mechanism is that the antibacterial effect of the QAMs is decreased when a salivary protein pellicle separates the antibacterial polymer surface from the overlaying biofilm [36, 37]. Therefore, dental materials exhibiting the double benefits of protein-repellent and antibacterial activities are desirable. Recently, Zhang et al. [38] developed a novel bioactive orthodontic cement incorporating 3% MPC, 1.5% DMAHDM, and 0.1% NAg into a commercial RMGI, Vitremer (referred to as VT), for the first time. The enamel shear bond strength (SBS) of the cement was not compromised, when compared to the control (p>0.1), even after 30 days of immersed in distilled water at 37°C (Figure 1) [38]. Figure 2 illustrates the lactic acid results. VT with 1.5% DMAHDM alone reduced the lactic acid production to about 1/5 that of VT control, and VT with 0.1% NAg alone reduced to nearly 1/3. More dramatically, VT with both DMAHDM and NAg reduced the lactic acid production to 1/15 of that of VT control. A similar trend was observed in the CFU and MTT metabolic activity results, suggesting that DMAHDM and NAg as dual antibacterial agents in RMGI had a multiplying effect in reducing biofilm growth [38]. Representative live/dead bacterial staining images are shown in Figures 3(a)–3(d). VT control was covered with primarily live bacteria (staining green) in Figure 3(a). As illustrated in Figure 3(b), with the addition of MPC, the live bacteria (staining green) were decreased but dead bacteria (staining red) were not noticed, suggesting that MPC could repel the bacteria adsorption but could not kill them. In contrast, in Figure 3(c), VT+DMAHDM+NAg had much more staining of compromised bacteria. In Figure 3(d), VT+MPC+DMAHDM+NAg had the most red staining and least green staining [38].
Enamel shear bond strengths (SBS) (mean±sd; n=10). Incorporating 3% MPC+1.5% DMAHDM+0.1% NAg into VT did not adversely affect the SBS, compared to VT control (p>0.1). Water aging for 30 d had no significant effect on SBS, compared to those at 1 d (p>0.1). Bars with dissimilar letters indicate values that are significantly different from each other (p<0.05). (Adapted from reference [38], with permission).
Quantitative viability of the 2-day biofilms on disks: (a) metabolic activity and (b) lactic acid production (mean±sd; n=6). Biofilms on the VT containing 3% MPC+1.5% DMAHDM+0.1% NAg had the least metabolic activity and lactic acid production among all groups. In each plot, values with dissimilar letters are significantly different from each other (p<0.05). (Adapted from reference [38], with permission).
Representative live/dead staining images of 2-day biofilms grown on disks: (a) VT control, (b) VT with 3% MPC, (c) VT with 1.5% DMAHDM+0.1% NAg, and (d) VT with 3% MPC+1.5% DMAHDM+0.1% NAg. Live bacteria were stained green, and compromised bacteria were stained red. When live and dead bacteria were in close proximity or on the top of each other, the staining had yellow or orange colors. The VT with 3% MPC+1.5% DMAHDM+0.1% NAg had less bacterial adhesion, and the biofilms consisted of primarily compromised bacteria. (Adapted from reference [38], with permission).
In addition, Zhang et al. [38] also found that VT with 3% MPC+1.5% DMAHDM and VT with 3% MPC+0.1% NAg had lower acid production than those using DMAHDM or NAg without MPC. The acid production was the lowest in VT+3% MPC+1.5% DMAHDM+0.1% NAg, which indicated the synergistic effect of DMAHDM, NAg, and MPC in biofilm inhibition.
These results are related to the mechanism of QAMs and NAg to kill bacteria and the mechanism of MPC to repel protein and bacteria adsorption. QAMs are considered to exhibit the “contact killing” mechanism. The positively charged quaternary amine N+ of QAMs can attract the negatively charged cell membrane of bacteria, thus disrupting the bacterial membranes and causing cytoplasmic leakage [15, 16, 28]. The antimicrobial mechanism of NAg was suggested to be Ag ions interacting with vital enzymes of the bacteria, rendering DNA to lose its replication ability, thus leading to cell death [39–41]. Furthermore, studies indicated that NAg had a long distance killing capability and relatively long-term antibacterial activity [42].
The protein-repellent agent MPC is a methacrylate with a phospholipid polar group in the side chain. MPC has been shown to have excellent ability to repel protein adsorption and prevent bacterial adhesion [20, 36]. The mechanism of protein repellency of MPC relates to the structure of phospholipid which contains a hydrophilic head (attracted to water) and hydrophobic tails (repelled by water) [36, 37]. Phospholipids, a major component of all cell membranes, can form lipid bilayers in which the nonpolar tail region faces the inner area and the polar head region faces outward and interacts. Therefore, the MPC polymers are hydrophilic with an abundance of free water but no bound water in the hydrated MPC polymer. While the presence of bound water would cause protein adsorption, the large amount of free water around the hydrated MPC polymer is considered to detach proteins and repel protein adsorption [36, 37, 43]. MPC can greatly reduce the protein adsorption by maxing direct contacts between bacteria and the polymer surface, thus enhancing the antibacterial efficacy of DMAHDM and NAg. In return, DMAHDM and NAg greatly reduces biofilm buildup on the cement surface; this would help to expose more MPC to repel proteins.
Furthermore, the use of triple agents may have a wide applicability not only to dental cements but also to other biomedical materials and tissue engineering scaffolds. The protein-repellent and antibacterial combination could be highly beneficial to inhibit biofilm growth and prevent infection in the wounds.
3. Multifunctional Cements to Protect Enamel from Demineralization
During orthodontic treatments, it is difficult to perform oral hygiene procedures on the bonded dental arches. Therefore, more bacteria are accumulated, which can lead to a decrease in pH that tips the demineralization-remineralization balance toward net mineral loss (demineralization) [2]. RMGIs are preferable to bond the brackets to the teeth because of F-releasing capability, which will reduce enamel demineralization [11, 44]. However, previous studies indicated that the initial F ion released form RMGIs was high and its concentration in the oral cavity was decreased rapidly over time due to salivary clearance and swallowing [45–48]. Moreover, the long-lasting low pH around the brackets restricted the remineralization process, so that more F ions could not produce a better cariostatic effect [24]. Therefore, a new bioactive orthodontic cement that could neutralize the acidic environment, alleviate subsurface enamel demineralization adjacent to brackets, and facilitate the remineralization effect would be highly desirable.
In a previous study, Ma et al. [44] developed a novel orthodontic cement containing protein-repellent MPC, antibacterial monomer DMAHDM, and remineralizing agent nanoparticles of amorphous calcium phosphate (NACP). They measured the average lesion depths (LD) via polarized light microscopy at three distance ranges: from 50 to 150 μm, from 150 to 250 μm, and from 250 to 350 μm, respectively. Among the four groups, the LD of group “RMGI+MPC+DMAHDM+NACP” was the least for all the three distance ranges (p<0.05) [44]. The LD of Transbond XT control was the deepest for the three tested distance ranges (p<0.05), which were 144.06±24.59μm, 148.24±21.14μm, and 157.51±24.34μm, respectively [44]. These results manifest that adhesives, which contain the NACP, do have the cariostatic effect. The results of enamel Knoop microhardness (KHN) also demonstrated the effect of preventing enamel demineralization by using NACP, MPC, and DMAHDM (Figure 4). “RMGI+MPC+DMAHDM+NACP” displayed the highest hardness from 25 to 175 μm deep at the three distances, which indicated that incorporating 3% MPC and 1.5% DMAHDM into RMGI could give the cement the ability of caries prevention close to the adhesive margin. The enamel hardness of novel cement with NACP was significantly greater than that without NACP; the novel cement with MPC, DMAHDM, and NACP exactly yielded significantly a better demineralization prevention effect when compared with a commercial RMGI control [44]. Zhang et al. [49] also added MPC, DMAHDM, NAg, and NACP into RMGI and obtained similar conclusions. They studied the release of Ca and P ions at different NACP filler levels and different pH values. They found that the cement with NACP significantly increased the ion release with the increase of the NACP filler level and with the decrease of pH from 7 to 4 (p<0.05) (Figure 5). These results demonstrate that NACP could release Ca and P ions at cariogenic pH when these ions are most needed to combat enamel demineralization [49].
Enamel Knoop microhardness (KHN) values according to materials and testing depths of CSMH analysis (mean±sd; n=12), respectively, at (a) 100 μm, (b) 200 μm, and (c), 300 μm distance from the margin of cements. Dissimilar letters indicate that values are significantly different with other groups (p<0.05) at each depth. (Adapted from reference [44], with permission).
Calcium (Ca) and phosphate (P) ion release (mean±sd; n=3) from the VT filled with: (a, b) 10% NACP, (c, d) 15% NACP, and (e, f) 20% NACP. Ion release increased with increasing the immersion time and the NACP filler level. Ion release increased with decreasing the solution pH. (Adapted from reference [49], with permission).
Several studies showed that the NACP nanocomposite achieved Ca and P ion releases similar to those of traditional CaP composites, but the mechanical strength was at least twice as high [50, 51]. NACP composite could achieve high levels of Ca and P ions release at relatively low NACP filler levels because of the high surface area of the nanoparticles of 17.76 m2/g [50, 52]. Indeed, the enamel bond strength was not compromised even if the NACP filler level was 20% [49]. The pH was an important factor that affected the demineralization-remineralization balance. Takahashi and Nyvad [53] suggested that the de- and remineralization balance was tilted toward demineralization by the ecological phenomena from bacterial acid production. The bacterial acid-induced adaptation and selection within the microbiota, from the dynamic stability stage to the aciduric stage via the acidogenic stage, could change the environment form being relatively safe to being cariogenic [53–55]. It was suggested that the pH was lower than 4.5 in the plaque around the brackets [22, 56]. RMGI-containing NACP was shown to be a “smart material”; it could rapidly increase the Ca and P ion release at such a low pH and neutralize the acidic environment to a safe level of pH [49]. Therefore, adding NACP to RMGI delivered greater remineralization for enamel lesions than a fluoride-releasing commercial composite, increased the hardness back to normal, and inhibited or minimized WSLs [57]. A further study is still needed to investigate the cytotoxicity and biocompatibility of novel cement and to evaluate biofilm acid reduction and remineralization effects under clinically relevant in vivo conditions.
4. Bioactive Self-Etch Adhesive to Prevent Enamel Demineralization
Acid etch techniques are used routinely to bond orthodontic brackets to the teeth [58]. In 1955, Buonocore introduced the phosphoric acid etching technique which has revolutionized and improved the clinical practice of orthodontics [3, 59]. However, 37% phosphoric acid etching has several disadvantages, including causing enamel surface roughness, removing irreversibly several microns of the enamel layer, demineralization of the superficial layer of enamel near the brackets and junctions, and enamel fracture and crazing at the time of bracket debonding [58–60]. Indeed, Kim et al. [58] found that using acid etching could cause from 5 up to 10 mm of enamel loss, which could render the enamel surface more susceptible to demineralization during and after orthodontic treatment.
Several alternative approaches have been undertaken to reduce the adverse effects of the phosphoric acid etching, such as the use of different enamel preparation and adhesive systems [58]. Therefore, self-etching adhesive systems have been used for bracket bonding with the advantages of eliminating the need for a separate etching step, allowing for the simultaneous etching and adhesive penetration and forming a protective layer on the enamel surface. This avoids the negative effects of the traditional method with a separate acid etching step on enamel [61].
Adhesion of S. mutans to surfaces in the mouth will support the subsequent attachment and growth of other bacterial species, ultimately forming a microecosystem known as a biofilm [62]. At the tooth surface around the brackets, oral biofilms can produce acids and cause WSLs or caries. Although dental plaque biofilm cannot be eliminated, it may be possible to reduce the pathogenic impact of the biofilm at the margin of the brackets by rendering the adhesive protein-repellent and antibacterial properties to suppress biofilm attachment and buildup [62]. It is highly desired to develop a new antibacterial self-etching adhesive to combat biofilms and WSLs.
In a previous study, Wang et al. [63] mixed MPC and DMAHDM into a self-etch adhesive (Adper Easy One, 3 M, St. Paul, MN, USA; referred to as AEO) to repel protein adsorption and decrease bacteria accumulation. In their study, the self-etch adhesive with 7.5% MPC had much less bacterial attachment and reduced the protein adsorption to only 5% that of control (Figure 6(a)). Adding either 5% DMAHDM or 7.5% MPC alone into AEO reduced the metabolic activity to nearly 17% and 33% of that of AEO control, respectively. More dramatically, biofilms on the adhesive containing both 7.5% MPC and 5% DMAHDM together had the lowest metabolic activity, which was only 5% of that of AEO control (Figure 6(b)) [63].
Protein adsorption and biofilm metabolic activity. (a) Protein adsorption onto self-etch adhesive (mean±sd; n=6). AEO with 7.5% MPC+5% DMAHDM had much less protein adsorption, which was about 5% that of AEO control (p<0.05). Bars with dissimilar letters indicate values that are significantly different from each other (p<0.05). (b) Biofilm metabolic activity on disks cultured for 2 days (mean±sd; n=6). Metabolic activity of biofilms on AEO with 7.5% MPC+5% DMAHDM was reduced to 5% that of AEO control (p<0.05). Values with dissimilar letters are significantly different from each other (p<0.05). (Adapted from reference [63], with permission).
Based on these results, Wang et al. [63] suggested that there was a synergistic effect of MPC and DMAHDM in the adhesive on antibiofilm properties. Quaternary ammonium compounds, which were positively charged, could bind to the negatively charged cell wall components, cause the leakage of the cytoplasmatic material, and finally lead to the lysis of the bacterial cells [31]. The antibacterial potency increased with increasing CL from 3 to 16 and decreased with CL further increasing to 18 [34]. DMAHDM with a chain length of 16 had the most potent antibacterial efficacy among all the QAMs tested [34]. The addition of MPC could dramatically enhance the antibacterial efficacy of DMAHDM by repelling the proteins on the adhesive resin to facilitate the mechanism of “contact killing” [64]. Therefore, the synergistic effect of MPC and DMAHDM was demonstrated not only in orthodontic cements but also in dental adhesives.
Another important issue is that an adequate bond strength is necessary for the fixed appliance therapy to be successful [61]. However, the bond strength also needs to be low enough to escape enamel damage during bracket debonding. Bishara et al. [59] suggest that enamel fracture and crazing existed at the time of bracket debonding, especially with ceramic brackets. As a result, orthodontists prefer bond failure at the bracket-adhesive interface to within the adhesive. Lamper et al. [65] found that, if the bond strength was lower than 12 MPa, little enamel damage was noticed; however, the risk would increase 14-fold if the strength was over 12 MPa. Reynolds et al. [66] suggested that the appropriate shear bonding strength for orthodontic cements was approximately 8 to 9 MPa, which was high enough to prevent the brackets from falling off the surface of the teeth, while avoiding enamel damage during the debonding process at the completion of the orthodontic treatment. The results of Wang et al. [63] showed that the enamel shear bond strength of the self-etch group containing MPC and DMAHDM was 9-10 MPa, which is clinically acceptable. Their research suggested that adding MPC and DMAHDM into the self-etch adhesive exhibited excellent antibacterial and protein-repellent effect without compromising the bond strength of the brackets.
5. Protein-Repellent and Antibacterial PMMA Resin to Suppress Biofilms
In addition to photopolymerization, heat cure is used in dentistry to increase the polymerization conversion and enhance the mechanical properties. Heat-cured resins are commonly used in orthodontics for making complicated functional appliances to correct severe skeletal class II and III malocclusions of preadolescent patients and for fabricating retainers to keep the esthetic results of orthodontic treatment [1, 67, 68]. The complex designing of appliances and retainers may prevent effective cleaning, thus inducing caries, periodontal diseases, and even denture-induced stomatitis in acrylate resin wearers [1, 69, 70]. Moreover, Takahashi et al. [21] suggested that polymethyl methacrylate- (PMMA-) based acrylic resins had a relatively high water absorption capacity and were prone to dental plaque accumulation. Because the appliances and retainers would wear at least 2 years in the patient’s mouth, so the accumulation of biofilms and plaque on the resin surfaces could create unfavorable odors and further accelerate oral bacteria-related infection [67]. Although adequate cleaning of the appliances and retainers is imperative for the prevention of bacterial related diseases, it is more beneficial and necessary to develop an antibacterial resin surface. Antimicrobial agents were added into dental materials, which can be divided into two classes: released and nonreleased materials [31]. However, there were several disadvantages of using released antibacterial agents, including compromising mechanical properties of the carrier material over time, short-term effectiveness, and possible toxicity if the release was not properly controlled [71–73]. In contrast, polymeric antibacterial agents, which were nonvolatile and chemically stable, exhibited a stronger antimicrobial effect by interacting with and disrupting bacterial cell membranes [31, 74].
In another study, Cao et al. [75] combined MPC and DMAHDM into the PMMA-based acrylic resin to decrease the biofilm amounts and metabolic activity. The MPC mass fraction incorporated into acrylic resin was 3%, which was selected to produce the strongest protein repellency while not compromising the mechanical properties. Similarly, the maximum amount of DMAHDM in the PMMA resin was determined to be 1.5%. The flexural strength of the composite containing 3% MPC and 1.5% DMAHDM was 71 MPa, similar to 73 MPa of a commercial composite without antibacterial or protein-repellent functions (p>0.1). The composite containing 3% MPC and 1.5% DMAHDM had an elastic modulus of 2020 MPa, similar to 2142 MPa of the commercial composite (p>0.1) [75]. Using human saliva as inoculum, dental plaque microcosm biofilms were grown on the resins for two days to form a relatively mature biofilm. The representative live/dead staining photos of the 2-day biofilms on acrylic resins are illustrated in Figure 7. There were much less, but alive, bacteria via MPC (green staining) which reduced bacteria attachment by means of protein repellence, and there were substantial amounts of compromised bacteria (red staining) via DMAHDM which killed the bacteria by way of contact inhibition. Furthermore, the acrylic resin with 3% MPC+1.5% DMAHDM had the least bacterial adhesion, and the biofilms consisted of primarily dead bacteria with red staining, which demonstrated the enhanced antibacterial efficacy when double agents (protein-repellant MPC+antibacterial DMAHDM) were used in the same acrylate resin [75].
Representative live/dead staining images of biofilms adherent on PMMA discs cultured for 2 days: (a) control group, (b) 3% MPC group, (c) 1.5% DMAHDM group, and (d) 3% MPC+ 1.5% DMAHDM group. The live bacteria were stained green, and the dead bacteria were stained red. When live and dead bacteria were in close proximity or on the top of each other, the staining had yellow or orange colors. (Adapted from reference [75], with permission).
The new bioactive PMMA resin incorporating double agents of MPC and DMAHDM greatly reduced protein adsorption and biofilm growth, which could decrease the incidence of caries, periodontal diseases, and acrylic resin-related stomatitis. Their combined use may be beneficial not only to dental materials but also to other biomedical materials and tissue engineering fields, such as a bone cement in total joint arthroplasty, spinal surgery, fracture repair, and limb-sparing procedures [76]. Further investigations are needed to determine whether and how the strength and the capabilities of the antibiofilm and protein repellence of the new PMMA resin would decrease after long-term aging in experiments simulating the oral environment.
6. Conclusions
This article represents a cutting edge review on the development of a new generation of antibacterial and protein-repellent dental cements and adhesives with bioactive and therapeutic properties to inhibit biofilms, promote remineralization, and protect the tooth structures. Compared with traditional materials, the new class of bioactive materials had excellent antibacterial and protein-repellent efficacy in various systems including orthodontic cements, self-etch adhesives, and polymethyl methacrylate resin-based appliances and retainers. These new materials incorporated novel agents, including antibacterial QAMs and NAg, protein-repellent agent MPC, and remineralization filler NACP. They inhibited oral bacterial pathogens, repelled protein adsorption, and promoted remineralization to effectively combat WSLs. This novel class of dental materials with antibacterial and protein-repellent activities provided the much-needed therapeutic capabilities that are lacking in traditional materials. These novel materials and methods are expected to have a wide range of applicability to other dental and biomedical materials to acquire antibacterial, protein-repellent, and therapeutic functions.
Disclosure
Li Cao, Junling Wu, and Qiang Zhang are co-first author.
Conflicts of Interest
The authors declare no conflict of interest.
Acknowledgments
This study was supported by Beijing Hospitals’ Program (ZYLX201703) (YB); National Key R&D Program of China (2017YFC1104304) (YB); National Natural Science Foundation (NSF) of China (81671032) (JLW); University of Maryland, Baltimore County seed grant (HX); and School of Dentistry, University of Maryland bridge fund (HX).
LuccheseA.GherloneE.Prevalence of white-spot lesions before and during orthodontic treatment with fixed appliances201335566466810.1093/ejo/cjs0702-s2.0-84885082210SundararajD.VenkatachalapathyS.TandonA.PereiraA.Critical evaluation of incidence and prevalence of white spot lesions during fixed orthodontic appliance treatment: a meta-analysis20155643343910.4103/2231-0762.16771926759794OgaardB.Prevalence of white spot lesions in 19-year-olds: a study on untreated and orthodontically treated persons 5 years after treatment198996542342710.1016/0889-5406(89)90327-22-s2.0-00248418672816842Diamanti-KipiotiA.GusbertiF. A.LangN. P.Clinical and microbiological effects of fixed orthodontic appliances198714632633310.1111/j.1600-051X.1987.tb00979.x2-s2.0-00233767013509967BalenseifenJ. W.MadoniaJ. V.Study of dental plaque in orthodontic patients197049232032410.1177/002203457004900221012-s2.0-0014747432BoyarR. M.ThylstrupA.HolmenL.BowdenG. H.The microflora associated with the development of initial enamel decalcification below orthodontic bands in vivo in children living in a fluoridated-water area198968121734173810.1177/002203458906801203012-s2.0-0024845925TufekciE.DixonJ. S.GunsolleyJ. C.LindauerS. J.Prevalence of white spot lesions during orthodontic treatment with fixed appliances201181220621010.2319/051710-262.12-s2.0-78651280499LopatieneK.BorisovaiteM.LapenaiteE.Prevention and treatment of white spot lesions during and after treatment with fixed orthodontic appliances: a systematic literature review201672e1e810.5037/jomr.2016.720127489605KhoroushiM.KachuieM.Prevention and treatment of white spot lesions in orthodontic patients201781111910.4103/ccd.ccd_216_172-s2.0-8501897541228566845EnaiaM.BockN.RufS.White-spot lesions during multibracket appliance treatment: a challenge for clinical excellence20111401e17e2410.1016/j.ajodo.2010.12.0162-s2.0-79959986426ZhangN.ChenC.WeirM. D.BaiY.XuH. H. K.Antibacterial and protein-repellent orthodontic cement to combat biofilms and white spot lesions201543121529153810.1016/j.jdent.2015.09.0062-s2.0-8494995196026427311MaxfieldB. J.HamdanA. M.TüfekçiE.ShroffB.BestA. M.LindauerS. J.Development of white spot lesions during orthodontic treatment: perceptions of patients, parents, orthodontists, and general dentists2012141333734410.1016/j.ajodo.2011.08.0242-s2.0-8485775543822381494ChapmanJ. A.RobertsW. E.EckertG. J.KulaK. S.González-CabezasC.Risk factors for incidence and severity of white spot lesions during treatment with fixed orthodontic appliances2010138218819410.1016/j.ajodo.2008.10.0192-s2.0-7795548746420691360Sungurtekin-EkciE.Ozdemir-OzenenD.DumanS.AcunerI. C.SandalliN.Antibacterial surface properties of various fluoride-releasing restorative materials in vitro201513e169e17310.5301/jabfm.50002122-s2.0-84941219465ImazatoS.KinomotoY.TarumiH.EbisuS.TayF. R.Antibacterial activity and bonding characteristics of an adhesive resin containing antibacterial monomer MDPB200319431331910.1016/S0109-5641(02)00060-X2-s2.0-0041491419ImazatoS.Antibacterial properties of resin composites and dentin bonding systems200319644945710.1016/S0109-5641(02)00102-12-s2.0-004299411312837391HiraishiN.YiuC. K. Y.KingN. M.TayF. R.Effect of chlorhexidine incorporation into a self-etching primer on dentine bond strength of a luting cement201038649650210.1016/j.jdent.2010.03.0052-s2.0-7795586173720298738DonlanR. M.CostertonJ. W.Biofilms : survival mechanisms of clinically relevant microorganisms200215216719310.1128/CMR.15.2.167-193.20022-s2.0-003622850511932229GaoX.JiangS.KohD.HsuC. Y. S.Salivary biomarkers for dental caries201670112814110.1111/prd.121002-s2.0-84949679002SibaraniJ.TakaiM.IshiharaK.Surface modification on microfluidic devices with 2-methacryloyloxyethyl phosphorylcholine polymers for reducing unfavorable protein adsorption2007541889310.1016/j.colsurfb.2006.09.0242-s2.0-3384579156217112710TakahashiN.IwasaF.InoueY.MorisakiH.IshiharaK.BabaK.Evaluation of the durability and antiadhesive action of 2-methacryloyloxyethyl phosphorylcholine grafting on an acrylic resin denture base material2014112219420310.1016/j.prosdent.2013.08.0202-s2.0-8490442985724461942BadawiH.EvansR. D.WilsonM.ReadyD.NoarJ. H.PrattenJ.The effect of orthodontic bonding materials on dental plaque accumulation and composition in vitro200324193345335010.1016/S0142-9612(03)00166-22-s2.0-0038633596LimB.-S.LeeS. J.LeeJ. W.AhnS. J.Quantitative analysis of adhesion of cariogenic streptococci to orthodontic raw materials2008133688288810.1016/j.ajodo.2006.07.0272-s2.0-4444909617218538253DerksA.KatsarosC.FrenckenJ. E.van’t HofM. A.Kuijpers-JagtmanA. M.Caries-inhibiting effect of preventive measures during orthodontic treatment with fixed appliances. A systematic review200438541342010.1159/0000796212-s2.0-444426605315316184AntonucciJ. M.ZeigerD. N.TangK.Lin-GibsonS.FowlerB. O.LinN. J.Synthesis and characterization of dimethacrylates containing quaternary ammonium functionalities for dental applications201228221922810.1016/j.dental.2011.10.0042-s2.0-8485576545022035983XuX.WangY.LiaoS.WenZ. T.FanY.Synthesis and characterization of antibacterial dental monomers and composites2012100B41151116210.1002/jbm.b.326832-s2.0-8486282228622447582ShiX.LuH. B.MaoJ.GongS. Q.Current status and further prospects of dental resin-based materials with antibacterial properties201651956656910.3760/cma.j.issn.1002-0098.2016.09.0122-s2.0-8504405224727596349LiF.ChenJ.ChaiZ.ZhangL.XiaoY.FangM.MaS.Effects of a dental adhesive incorporating antibacterial monomer on the growth, adherence and membrane integrity of Streptococcus mutans200937428929610.1016/j.jdent.2008.12.0042-s2.0-60449095778HiroseN.KitagawaR.KitagawaH.MaezonoH.MineA.HayashiM.HaapasaloM.ImazatoS.Development of a cavity disinfectant containing antibacterial monomer MDPB201695131487149310.1177/00220345166634652-s2.0-8499652883327558263ImazatoS.Bio-active restorative materials with antibacterial effects: new dimension of innovation in restorative dentistry2009281111910.4012/dmj.28.112-s2.0-63449109089BeythN.Yudovin-FarberI.BahirR.DombA. J.WeissE. I.Antibacterial activity of dental composites containing quaternary ammonium polyethylenimine nanoparticles against Streptococcus mutans200627213995400210.1016/j.biomaterials.2006.03.0032-s2.0-33646053149WengY.HowardL.GuoX.ChongV. J.GregoryR. L.XieD.A novel antibacterial resin composite for improved dental restoratives20122361553156110.1007/s10856-012-4629-z2-s2.0-8486330264522466818ImazatoS.TayF. R.KaneshiroA. V.TakahashiY.EbisuS.An in vivo evaluation of bonding ability of comprehensive antibacterial adhesive system incorporating MDPB200723217017610.1016/j.dental.2006.01.0052-s2.0-3384604131216469372LiF.WeirM. D.XuH. H. K.Effects of quaternary ammonium chain length on antibacterial bonding agents2013921093293810.1177/00220345135020532-s2.0-8488425133223958761FanC.ChuL.RawlsH. R.NorlingB. K.CardenasH. L.WhangK.Development of an antimicrobial resin—a pilot study201127432232810.1016/j.dental.2010.11.0082-s2.0-7995228142321112619IshiharaK.NomuraH.MiharaT.KuritaK.IwasakiY.NakabayashiN.Why do phospholipid polymers reduce protein adsorption?199839232333010.1002/(SICI)1097-4636(199802)39:2<323::AID-JBM21>3.0.CO;2-C9457564IshiharaK.UedaT.NakabayashiN.Preparation of phospholipid polylners and their properties as polymer hydrogel membranes199022535536010.1295/polymj.22.3552-s2.0-0025229068ZhangN.MeloM. A. S.AntonucciJ. M.LinN. J.Lin-GibsonS.BaiY.XuH. H. K.Novel dental cement to combat biofilms and reduce acids for orthodontic applications to avoid enamel demineralization20169641310.3390/ma90604132-s2.0-8497577058028773534ChengY. J.ZeigerD. N.HowarterJ. A.ZhangX.LinN. J.AntonucciJ. M.Lin-GibsonS.In situ formation of silver nanoparticles in photocrosslinking polymers201197B112413110.1002/jbm.b.317932-s2.0-79952409747RaiM.YadavA.GadeA.Silver nanoparticles as a new generation of antimicrobials2009271768310.1016/j.biotechadv.2008.09.0022-s2.0-57249095780JungW. K.KooH. C.KimK. W.ShinS.KimS. H.ParkY. H.Antibacterial activity and mechanism of action of the silver ion in Staphylococcus aureus and Escherichia coli20087472171217810.1128/AEM.02001-072-s2.0-4204908826718245232MoronesJ. R.ElechiguerraJ. L.CamachoA.HoltK.KouriJ. B.RamirezJ. T.YacamanM. J.The bactericidal effect of silver nanoparticles200516102346235310.1088/0957-4484/16/10/0592-s2.0-25444497481GodaT.KonnoT.TakaiM.IshiharaK.Photoinduced phospholipid polymer grafting on Parylene film: advanced lubrication and antibiofouling properties2007541677310.1016/j.colsurfb.2006.09.0062-s2.0-3384572752417137760MaY.ZhangN.WeirM. D.BaiY.XuH. H. K.Novel multifunctional dental cement to prevent enamel demineralization near orthodontic brackets201764586710.1016/j.jdent.2017.06.0042-s2.0-8502109232628642057LynchC. D.Summary of: A retrospective , practice-based , clinical evaluation of Fuji IX restorations aged over five years placed in load-bearing cavities2013215629029110.1038/sj.bdj.2013.9092-s2.0-8494528078124072301PaschosE.GalosiT.HuthK. C.RudzkiI.WichelhausA.KunzelmannK. H.Do bonding agents protect the bracket-periphery?—Evaluation by consecutive μCT scans and fluorescence measurements201519115916810.1007/s00784-014-1378-z2-s2.0-8492551535825467239ChatzistavrouE.EliadesT.ZinelisS.AthanasiouA. E.EliadesG.Fluoride release from an orthodontic glass ionomer adhesive in vitro and enamel fluoride uptake in vivo20101374458.e1458.e810.1016/j.ajodo.2009.10.0302-s2.0-85058720777KashaniM.FarhadiS.RastegarfardN.Comparison of the effect of three cements on prevention of enamel demineralization adjacent to orthodontic bands201263899310.5681/joddd.2012.01922991644ZhangN.WeirM. D.ChenC.MeloM. A. S.BaiY.XuH. H. K.Orthodontic cement with protein-repellent and antibacterial properties and the release of calcium and phosphate ions201650515910.1016/j.jdent.2016.05.0012-s2.0-8497365221027157089XuH. H. K.MoreauJ. L.SunL.ChowL. C.Nanocomposite containing amorphous calcium phosphate nanoparticles for caries inhibition201127876276910.1016/j.dental.2011.03.0162-s2.0-7995804507521514655DickensS. H.FlaimG. M.TakagiS.Mechanical properties and biochemical activity of remineralizing resin-based Ca–PO4 cements200319655856610.1016/S0109-5641(02)00105-72-s2.0-004149145712837405XuH. H. K.WeirM. D.SunL.MoreauJ. L.TakagiS.ChowL. C.AntonucciJ. M.Strong nanocomposites with Ca, PO4, and F release for caries inhibition2010891192810.1177/00220345093519692-s2.0-7244918485819948941TakahashiN.NyvadB.Ecological hypothesis of dentin and root caries201650442243110.1159/0004473092-s2.0-8498033896827458979TakahashiN.NyvadB.The role of bacteria in the caries process : ecological perspectives201190329430310.1177/00220345103796022-s2.0-7995206585620924061DawesC.What is the critical pH and why does a tooth dissolve in acid?2003691172272414653937RogersS.ChadwickB.TreasureE.Fluoride-containing orthodontic adhesives and decalcification in patients with fixed appliances: a systematic review20101384390.e1390.e810.1016/j.ajodo.2010.02.0252-s2.0-85058251880WeirM. D.ChowL. C.XuH. H. K.Remineralization of demineralized enamel via calcium phosphate nanocomposite2012911097998410.1177/00220345124582882-s2.0-8486649875822933607KimM. J.LimB. S.ChangW. G.LeeY. K.RheeS. H.YangH. C.Phosphoric acid incorporated with acidulated phosphate fluoride gel etchant effects on bracket bonding200575467868410.1043/0003-3219(2005)75[678:PAIWAP]2.0.CO;216097241BisharaS. E.AjlouniR.LaffoonJ. F.WarrenJ. J.Effect of a fluoride-releasing self-etch acidic primer on the shear bond strength of orthodontic brackets200272319920210.1043/0003-3219(2002)072<0199:EOAFRS>2.0.CO;212071602BisharaS. E.GordanV. V.VonWaldL.OlsonM. E.Effect of an acidic primer on shear bond strength of orthodontic brackets1998114324324710.1016/S0889-5406(98)70205-72-s2.0-0032162164GrünheidT.LarsonB. E.Repeated bracket bonding: conventional or self-etching primer?20143310210510.1016/j.ejwf.2014.05.0012-s2.0-84908028303SpencerP.YeQ.ParkJ.ToppE. M.MisraA.MarangosO.WangY.BohatyB. S.SinghV.SeneF.EslickJ.CamardaK.KatzJ. L.Adhesive/dentin interface: the weak link in the composite restoration20113861989200310.1007/s10439-010-9969-62-s2.0-7795465814220195761WangB.ZhangN.WangX.ParkS. R.WeirM. D.OatesT. W.XuH. H. K.BaiY.Novel self-etch adhesive with antibacterial and protein-repellent functions to prevent enamel demineralization201837690491110.4012/dmj.2017-4222-s2.0-85061893126MüllerR.EidtA.HillerK. A.KatzurV.SubatM.SchweiklH.ImazatoS.RuhlS.SchmalzG.Influences of protein films on antibacterial or bacteria-repellent surface coatings in a model system using silicon wafers200930284921492910.1016/j.biomaterials.2009.05.0792-s2.0-6784910357219545893LamperT.IlieN.HuthK. C.RudzkiI.WichelhausA.PaschosE.Self-etch adhesives for the bonding of orthodontic brackets: faster, stronger, safer?201418131331910.1007/s00784-013-0942-22-s2.0-84891559649ReynoldsI. R.A review of direct orthodontic bonding19752317117810.1080/0301228X.1975.11743666LeeJ. H.El-FiqiA.JoJ. K.KimD. A.KimS. C.JunS. K.KimH. W.LeeH. H.Development of long-term antimicrobial poly(methyl methacrylate) by incorporating mesoporous silica nanocarriers201632121564157410.1016/j.dental.2016.09.0012-s2.0-8499593232527671462LinF.YaoL.SunH.NiZ.ZhengM.A feasible method to improve adherence of Hawley retainer in adolescent orthodontic patients: a randomized controlled trial201591525153010.2147/PPA.S941112-s2.0-84946075934JepsonN. J. A.MoynihanP. J.KellyP. J.WatsonG. W.ThomasonJ. M.Caries incidence following restoration of shortened lower dental arches in a randomized controlled trial2001191314014410.1038/sj.bdj.480112211523885AltarawnehS.BencharitS.MendozaL.CurranA.BarrowD.BarrosS.PreisserJ.LoewyZ. G.GendreauL.OffenbacherS.Clinical and histological findings of denture stomatitis as related to intraoral colonization patterns of Candida albicans, salivary flow, and dry mouth2013221132210.1111/j.1532-849X.2012.00906.x2-s2.0-8487215908623107189KohnenW.JansenB.Polymer materials for the prevention of catheter-related infections1995283217518610.1016/S0934-8840(11)80199-42-s2.0-00294351788825109NohrR. S.Gavin MacdonaldJ.New biomaterials through surface segregation phenomenon: new quaternary ammonium compounds as antibacterial agents19945660761910.1163/156856294X002392-s2.0-0028252465ShearerA. E. H.PaikJ. S.HooverD. G.HaynieS. L.KelleyM. J.Potential of an antibacterial ultraviolet-irradiated nylon film200067214114610.1002/(SICI)1097-0290(20000120)67:2<141::AID-BIT3>3.0.CO;2-#KawabataN.NishiguchiM.Antibacterial activity of soluble pyridinium-type polymers19885410253225353202632CaoL.XieX.WangB.WeirM. D.OatesT. W.XuH. H. K.ZhangN.BaiY.Protein-repellent and antibacterial effects of a novel polymethyl methacrylate resin201879394510.1016/j.jdent.2018.09.0072-s2.0-85054170692YangA.ZhaoD.WuY.XuC.Effect of polyimide addition on mechanical properties of PMMA-based denture material201736556056510.4012/dmj.2016-2612-s2.0-85030184447