Enhanced Catalyst Activity of WO3 Using Polypyrrole as Support for Acidic Esterification of Glycerol with Acetic Acid

A series of polypyrrole supported WO 3 were fabricated and characterized by FT-IR, XRD, XPS, BET, TGA, and FESEM-EDX.The activity of the catalysts was tested in glycerol esterificationwith acetic acid, and it found thatWO 3 -Ppy-20 (nanocomposite with 20% WO 3 loaded) showed themaximum catalyst activity with 98% and selectivity of 70% to triacetin at 110Cwith a reaction duration of 10 h and also recorded the highest selectivity (75%) for acetylation of glycerol to monoacetin with about 59% conversion only. The highest acidity of WO 3 -Ppy-20 is also confirmed using TPD-NH 3 analysis. The activity and selectivity to triacetin of the catalyst were enhanced by increasing WO 3 loading amount, resulting in 82% conversion for WO 3 -Ppy-5 with about 32 and 50% selectivity to monoacetin and diacetin and about 18% selectivity to triacetin; in case of WO 3 -Ppy-20, these amounts were changed to 5, 25, and 70% selectivity to monoacetin, diacetin, and triacetin, respectively with the conversion of 98%. TPD-NH 3 analysis found that polypyrrole supportedWO 3 increases the catalyst acidity of WO 3 . BET and FESEM analyses revealed that WO 3 particles were well dispersed with the smallest average size in nanocomposite compared to pure WO 3 , which could contribute to the high activity of WO 3 -Ppy catalyst for esterification of glycerol.


Introduction
Nanocomposites have provided new and exciting possibilities in the field of materials science [1][2][3].Conducting polymerbased composites are more and more intensively studied since the end of the 1990s.These inorganic-organic hybrids form a promising class of new materials, owing to the advantageous properties of the polymer matrix and the embedded inorganic particles.The combinations often lead to synergistic effects, resulting in enhanced properties, making these materials applicable in various fields such as fuel cell [4], catalysis [5,6], and sensors [7].Metallic nanoparticles can be introduced in the polymer matrix either by chemical [8] or electrochemical methods [9][10][11].Although various metals have already been introduced into the conductive polymer matrix by electrochemical deposition for applications in electrocatalytic reaction, very few papers report the use of conducting polymers as a support of novel metals for applications in catalysis [12,13].Although conducting polymers are commonly used as a support for metallic catalysts, neither the exact role of the polymer nor the relative contribution of each component to the enhancement of the catalytic activity of the composite is fully understood yet.The incorporation of metallic or semiconducting nanoparticles in conducting polymers such as polyaniline (PANI) is of interest because of the strong electronic interaction between the nanoparticles and the polymer matrix [14,15].Metal nanoparticles incorporated into conducting polymers are also known to enhance the conductivity of the polymers.Using an oxide support such as SiO 2 , Al 2 O 3 , TiO 2 , and ZrO 2 to improve the catalytic activity of the active metal oxide phase is an old, well-known strategy.During the last decade, a significant development in catalysis research had been focused on improving the activity and selectivity of supported metal oxide catalysis by improving the properties of the support oxide material.This is generally known as the metal oxide support effect [16].The conducting polymers (polyaniline, polypyrrole, . ..) seem to be a convenient support for the active phase of catalyst [17,18].This kind of matrix is useful especially for oxidative-reductive catalysts, in which the catalytic process involves an exchange of electrons between reactants/products and catalyst [19].To maximize the excellent properties of polymer-metal nanocomposites, homogeneous dispersion of metal nanoparticles in the polymer matrix is required.This is a key challenge due to their easy aggregation arising from their high surface free energy [20].In the design of nanocomposites, one must consider the properties of the polymer matrix as well as the stability of the nanoparticles and more importantly the prevention of particle aggregation [21].
In the present work, we aimed to study the esterification of glycerol with acetic acid, as this reaction is a decent alternative for converting excess glycerol, which is obtained from biodiesel production process, to value-added chemical acetins (i.e., monoacetin, diacetin, and triacetin), which have significant applications in cryogenic manufacture, plastics, fuel additives, and many uses in cosmetic, food, and pharmaceutical industries.They are also used in the manufacture of explosives, plasticizers, softening, lubricants, and emulsifying agents uses and as a raw material in the production of biodegradable polyesters [22][23][24][25][26][27].
Typically, the esterification reaction is an acid-catalysed process.Many kinds of solid acids have been found: their acidic properties, their catalysis, and the structure of acid site have been elucidated, and those results have been reviewed by several workers [28].Acid catalysis plays a key role in many important reactions of the chemical and petroleum industries and in environmentally benign chemical processes [29].Liquid super acids based on sulphuric acid, which are efficient and selective at room temperature, are not suitable for industrial processes due to separation problems tied with environmental protection [30].Among solid acid catalysts, tungsten oxide-based materials comprise an interesting class of acid solids, first reported as a strongly acidic system by Hino and Arata [31].WO 3 -ZrO 2 , catalyst was also reported to be active for transesterification and esterification reactions under specific conditions [32,33].Thus, acid catalyst could play an important role in the glycerol dehydration stage as well as working under milder reaction conditions that might increase the conversion and selectivity.The use of two support materials could provide an alternative method to enhance the acidic condition and also the activities of the catalyst.To the best of our knowledge and with respect to what is extended above about the effective role of polypyrrole on enhancing the acidity of the metal oxide, we describe the preparation of a series of catalysts based on WO 3 supported on polypyrrole.
In relation to what is referred to above, we investigated the catalytic behaviour of WO 3 /Ppy composite in glycerol esterification with acetic acid.Micelle method was considered to synthesize the nanocomposite in order to achieve the maximum catalytic properties by making well-dispersed particles.In this paper, the influence of parameters such as temperature and time, catalyst amount, and WO 3 loading percentage on the acid properties has been studied; finally, the catalytic behaviour in the esterification of glycerol with acetic acid has been evaluated.

Materials and Preparation of WO 3 Nanoparticles (NPs).
For preparation of WO 3 NPs, hexadecyl trimethyl ammonium bromide (CTAB) (purity approx.99%) was purchased from Sigma.Tungsten(VI) chloride (WCl 6 ) (purity 99%) and ammonia solution (25% v/v) were purchased from Aldrich and BDH, respectively.Deionized and double distilled water was used for micelle and solution preparation.All the chemicals and solvents were used as received without further purifications.Firstly, the 0.05 M of CTAB solution was prepared.After getting the clear solution, 10 mL of ammonia solution (25 wt%) was added to the CTAB solutions while stirring.After getting a homogenous solution, 0.117 mol of WCl 6 1000 mL −1 of CTAB solution was added with vigorous stirring.After stirring for 4 h, the product was aged at ambient temperature for 72 h.The final product was filtered, washed with deionized water and absolute ethanol in order to remove surfactant, residual reactants, and by products, and then calcinated at 500 ∘ C for 2 h.

Polypyrrole and WO
) were all purchased from Sigma Aldrich.For polypyrrole synthesis, the solution of PTSA and APS with a fixed ratio of 60 mmol : 36 mmol in 400 mL deionized water was mixed and sonicated for 1 h in an ice-water bath.Pyrrole solution is added to the mixture (74 mmol in 100 mL deionized water, molar ratio of APS : PTSA : pyrrole = 0.81 : 0.49 : 1).The obtained solution turns to dark green, indicating the polymerization of pyrrole.The resultant precipitant is washed with deionized water and methanol to remove any possible oligomers.The obtained powders are dried completely at 50 ∘ C. For preparation of nanocomposite, the prepared WO 3 NPs were initially mixed with the solution of PTSA and APS with a fixed ratio of 60 mmol : 36 mmol in 400 mL deionized water, followed by 1 h sonication in an ice-water bath.The pyrrole solution (74 mmol in 100 mL deionized water, molar ratio of APS : PTSA : pyrrole = 0.81 : 0.49 : 1) was mixed with the above WO 3 NPs suspended solution at 0 ∘ C and then sonicated for an additional 1 h in an ice-water bath for further polymerization.The resultant solution turned greenish immediately and then black, indicating the polymerization of pyrrole.The product was precipitated naturally and washed with deionized water until the supernatant was transparent.The clear supernatant was then decanted to remove any unreacted PTSA and APS.The precipitant was washed with methanol to remove any possible oligomers.The obtained powders were dried completely at 50 ∘ C. Pure PPy, WO 3 -PPy nanocomposites, with a particle loading of 5, 10, 15, and 20 wt%, were fabricated.

Catalyst Characterizations.
The surface area of the supported WO 3 catalyst was measured using the BET method (N 2 adsorption) with a Gemini apparatus (Micromeritics 2010 Instrument Corporation).The morphology and microstructure data for the samples were obtained from FESEM using LEO 1450 VP equipped with energy dispersive X-ray detector (EDX).All the samples were analysed in a high vacuum at 20 kV.The phase structures of the catalysts were determined by an X-ray diffraction (XRD) using Bruker AXS D8 Advance diffractometer with Cu K ( = 0.15406 nm) at an angle of 2 = 20-80 ∘ .The sample (2.0 g) was grinded, and the fine powder was pressed and placed on the sample holder.The X-ray photoelectron spectrum (XPS) data of the as-prepared samples was obtained using an XPS type Ultra from Kratos.The samples were analysed at 3 × 10 −9 mbar using C1s line at 284.6 eV from adventitious carbon as a reference for the binding energies.The acidity properties of the catalytic materials were measured by a temperatureprogrammed desorption of ammonia.These experiments were performed in a gas flow system equipped with a thermal conductivity detector (TCD).Prior to monitoring of the TPD-NH 3 profiles, the samples (50-60 mg) were placed in a U-shaped quartz reactor and heated in a helium flow at 150 ∘ C for 30 min.After a cooling temperature of 70 ∘ C, the samples were exposed to ammonia and flushed with 50 mL/min helium for 60 min.The TPD measurement was carried out with a heating rate of 10 ∘ C/min up to 600 ∘ C under flowing helium (50 mL/min).Desorption of ammonia was monitored by a TCD.The reduction characteristics of the catalysts were studied by a temperature-programmed reduction (TPR) using the same apparatus and pretreatment method for the TPD measurements.After pretreatment, the temperature was raised from 30 ∘ C to 1000 ∘ C at a rate of 10 ∘ C/min in a 10% H 2 /He flow (30 cm 3 /min).

Catalyst Activity Measurements.
The esterification reactions were carried out under a vacuum in the temperature range 50-110 ∘ C with acetic acid to glycerol mole ratio of 6 in a stirred batch reactor and reflux condition.A Dean-Stark trap was attached to the 50 mL round bottom flask, in order to extract the water that deactivates the catalysts and causes reversibility of the esterification reaction.In a typical experiment, 0.4 g of the catalyst was loaded into the well miscible solution of reactants in the container.The stirring speed was maintained at 500 rpm.After cooling, the catalyst was separated from the solution mixture by centrifugation.These products were analysed by a gas chromatography using GC-Hewlett Packard Model 6890N equipped with a flame ionization detector (FID) and a capillary column of HP-5 (with 30 m length, 0.25 mm ID, and 0.25 m of film thickness).The GC injection port and the detector temperature were set at 240 and 260 ∘ C, respectively.The initial column temperature was set at 70 ∘ C for 2 min and programmed from 70 ∘ C to 150 ∘ C for 1.5 min at the rate of 45 ∘ C ⋅ min −1 , from 150 ∘ C to 180 ∘ C at the rate of 8 ∘ C ⋅ min −1 , and from 180 to 240 ∘ C at the rate of 35 ∘ C ⋅ min −1 .The peak areas were used for quantification and the calibration curve.For every analysis, we transferred the weighted amount of the collected sample and 1 mL of 1-hexanol solution (5000 mg ⋅ L −1 ) as an internal standard to a volumetric flask and made up to 10 mL with absolute ethanol [34].

Results and Discussion
Figure 1 shows the FT-IR spectra of the pure Ppy and WO 3 -Ppy PNCs.Pure Ppy and the nanocomposites show the same peak locations at 1523 and 1428 cm −1 , which are assigned to C=C and C-N stretching, respectively.The peak near 1129 cm −1 corresponds to the breathing vibration of the pyrrole ring, and the peaks at 1271, 1003, and 702 cm −1 can be attributed to the C-H in-plane and out-of-plane deformation vibrations, respectively.The small band at 958 cm −1 is due to the C-C out-of-phase deformation vibration.It can be observed that the spectra of the PNCs have no obvious difference compared to that of pure Ppy.The slight peak shifts of the PNCs are as a result of the interaction between the NPs and the polymer matrix [35] Figure 2 illustrates the XRD patterns of the WO 3 NPs and Pure Ppy and their corresponding PNCs.The XRD patterns of WO 3 NPs (Figure 2(a)) match well to the previous reported monoclinic structure [35], and the strong intensity of the diffraction peaks indicates a highly crystalline structure.According to the XRD measurement, all WO 3 -Ppy catalysts contain monoclinic phase.The diffraction peaks (2) at 23.1, 23.6, 24.4,26.6, 28.9, 33.3, 34.2, and 36.2 ∘ are attributed to the (002), (020), ( 200), (120), (112), (022), (202), and (212) planes of the monoclinic WO 3 , respectively.Figures 2(b)-2(e) show the XRD patterns of the PNCs with different particle loadings.No additional peaks are observed for the PNCs as compared to those of the pure particles.However, a broad peak of the semicrystalline Ppy around 2 = 21-25 ∘ is observed in the previous reports [36].In this work, it is reasonable to consider that the broad peak of Ppy is Figure 3 shows the thermal stability of pure PPy and its WO 3 -Ppy PNCs with a particle loading of 5, 10, 15, and 20 wt%, respectively.All the samples show two distinct weight loss stages.The first stage, which corresponds to 5-10% weight loss from 25 to 260 ∘ C, is due to the evaporation of moisture and solvent residue in the samples.The major weight loss above 260 ∘ C is attributed to the degradation of PPy.With the addition of the WO 3 NPs, the degradation temperature (10% weight loss) of Ppy (231 ∘ C) increases to 269.4,275.0, 277.0, 282.9, and 297.0 ∘ C for the PNCs filled with a particle loading of 5, 10, 15, and 20 wt%, respectively.The enhanced  thermal stability of the nanocomposites is attributed to the more compact structure of Ppy induced by the addition of the WO 3 nanofillers, which can also be observed in the FESEM investigation.
The surface area of the pure Ppy, WO 3 NPs, and WO 3 -Ppy nanocomposite was measured using the Brunauer-Emmett-Teller (BET) method (N 2 adsorption) with a Gemini apparatus (Micromeritics 2010 Instrument Corporation), and the typical BET diagrams are depicted in Figure 4. WO 3 -Ppy-20 nanocomposite isotherm was considered, as this species exhibited the most acidic performance among other loading nanocomposite catalysts, which is obtained from NH 3 -TPD analysis.The isotherms were identified as type IV isotherms with H 3 hysteresis loop which is the indicator of mesoporous structure.The details of BET specific surface area and pore size, along with total acidity of pure Ppy, WO 3 , and WO 3 -Ppy nanocomposite, are listed in Table 1.The surface area of WO 3 loaded polypyrrole samples is higher than that of pure polypyrrole and WO 3 .The results indicated that the addition of WO 3 slightly increased the specific surface area of the polypyrrole.The highest surface area was observed from a sample with WO 3 -Ppy-20.The increase of WO 3 loading decreased the pore size on average.These results highlighted the mesoporous structure of the nanocomposite, which makes an efficient interaction between the surface of the compound and the nanocomposite catalyst.
The temperature programmed reduction was used to study the reducibility of the catalyst.According to the literature [37], pure WO 3 exhibits three reduction peaks, namely, a shoulder at 540 ∘ C (WO 3 → W 20 O 58 ), a sharp peak at 775 ∘ C (W 20 O 58 → WO 2 ), and a peak at higher temperature (WO 2 → W). Figure 5(a) shows the three main peaks of WO 3 , indicating reduction of WO 3 species to metallic W. To understand the promotion effect of polypyrrole, the H 2 -TPR of WO 3 -Ppy nanocomposite is considered.In terms of WO 3 -Ppy nanocomposite, all these peaks are observed, and also an additional peak is exhibited around 200 ∘ C due to some reduction on the support.The profile of nanocomposite indicates that all three reduction temperatures in WO 3 were decreased while their peak areas were increased in the presence of polypyrrole.Results revealed that the mobility and availability of O 2 in nanocomposite are higher than WO 3 .These phenomena might be related to the electron pair of N atoms in polypyrrole which acts as the donor of electron to WO 3 , increasing the electron density on W. In other words, it is concluded that polypyrrole improves the redox properties of W 6+ making WO 3 -Ppy nanocomposite a suitable redox catalyst.

Acidity Studies
Using TPD-NH 3 .The acidity of the catalysts was quantified by the integration of desorption curves for TPD-NH 3 .The areas under the curves were considered as being proportional to the number of moles of gas desorbed from the surface.The number of moles of NH 3 per weight of active phase is hereafter referred to as NH 3 .
The maximum temperature on the curves was designated as  max .Desorption peaks in maximum temperature ranges of 180-250, 280-330, and 380-500 ∘ C are normally attributed to NH 3 chemisorbed on weak, medium, and strong acid sites, respectively [38].The TPD profiles corresponded to desorption of NH 3 from the surface of catalysts which were summarized in Figure 6, and the values of  max and NH 3 were shown in Table 1.The NH 3 -TPD technology was usually used to measure the acidic properties of supports.The acidity strength was characterized by the temperature of desorption peak, while the number of acidic sites was measured by the amount of NH 3 desorbed.The NH 3 -TPD profiles of the WO 3 -Ppy nanocomposite catalyst with different loading ratios are shown in Figure 7.One broad peak was centred at 340 ∘ C for WO 3 [39], while three consequent peaks appeared in the temperature range of 100 to 250 ∘ C for polypyrrole.
In the case of WO 3 -Ppy nanocomposites, all species with 5, 10, 15, and 20% loadings exhibited a shoulder at around 135 ∘ C in the weak acid site, followed by two sequential peaks at about 250 and 400 ∘ C, which designated the medium and strong acid sites.It is observed that the intensity of the desorption peak decreased in relation to the increase in amount of WO 3 loading.This resulted in WO 3 -Ppy-20 indicating the higher NH 3 desorption among all species by 1252 mol ⋅ g −1 total acidity, which is in accordance with the fact that the amount of acid sites increased gradually as the WO 3 loading increased.As the glycerol acetylation is an acid catalysed reaction, the conversion of glycerol increased with an increasing amount of acid site, confirming that WO 3 -Ppy-20 shows the most acidic properties among all species.The morphologies of the prepared WO 3 -Ppy nanocomposite and pure polypyrrole are shown in Figure 7.Both  pure Ppy and its nanocomposite present a specific structure with a fairly uniform size distribution.The nanocomposite exhibits a highly mesoporous structure, which leads to the interest in its application as a catalyst [40].This structure is totally incompatible with the results obtained from the N 2 -adsorption/desorption isotherms.The pure PPy particles are observed to be relatively loosely packed as compared to the nanocomposite.For the nanocomposite filled with WO 3 nanoparticle, the particles are closely packed, and no bare nanoparticles are observed, which confirms that the micelle technique produced a well-dispersed nanoparticle.Micelle does not only provide a favourable site for the growth of the particulate assemblies but also influences the formation progress including nucleation, growth, coagulation, and flocculation.The surfactant-assisted method is an effective process to prepare size controllable nanocrystals, which is a simple, convenient, and low-cost process [41].
To determine surface composition and the chemical state of prepared samples, the XPS measurements were done, and results are depicted in Figure 8.The C1s photoelectron peak with binding energy of 284.6 eV was used as a reference to correct any charging effect.There was not any impurity peak observed due to thorough washing and removal of residue.The narrow scan of O1s, C1s, N2p, and W4f elements has been done for chemical state investigation.The major feature of the core level spectrum of C1s is a peak at around 284.6 eV, characteristic of the neutral carbon species.This peak is also ascribed to the carbon backbone of the polypyrrole.Another two components with binding energies at around 285.6 and 286.7 eV are associated with the presence of C-N and C=N or may come from contaminant or residual surfactant and environment [42].The O1s core level peak is as expected, located at 531 eV.It can be resolved into three components, namely, as terminal oxygen (=O), the linkage oxygen (-O-), and the peak fitted around 533 eV which is assumed to come from humidity in ambience or -OH group.The photoelectron peak of the W4f region in nanocomposite showed a wellresolved double peak due to W4f 7/2 and W4f 5/2 components with Δ ≈ 2.1 eV which is in good agreement with reference and revealed the presence of tungsten in W 6+ state and oxide form in compound [41].The peak at around 399.0 eV is attributed to the N1s which comes from polypyrrole.The spectrum deconvoluted into two major component peaks centred at 399.6 and 400.5 eV which are characteristic of pyrrolylium nitrogen's (-NH structure) and the positively charged nitrogen (-NH + (polaron)).[43,44].The oxidation state of W4f and O1s in WO 3 nanoparticle and WO 3 -Ppy nanocomposite is shown in Figure 9.In both elements, binding energies in WO 3 -Ppy nanocomposite exhibited a slight shift to the higher value compared to WO 3 nanoparticle, indicating an interaction between the WO 3 and polymer on the surface of the composite.The selectivity to monoacetin dropped sharply from 75% to about 10% while the temperature decreased from 50 to 110 ∘ C (Figure 10).Besides that, selectivity to triacetin increased drastically from about 5 to 70% at this temperature range.It was found that a higher reaction temperature favoured the conversion of glycerol and increased the selectivity towards triacetin due to the further acetylation of monoacetin, as the glycerol conversion is being completed from 50 to 110 ∘ C.

Effect of Reaction Time.
The conversion of glycerol and the selectivity to products at different reaction times were studied using WO 3 -Ppy-20 catalysts, as shown in Figure 11.
The increase in conversion displayed a near linear relation with reaction time and rose from 58% to about 98% conversion within 10 h reaction time.The same trend was observed in the case of triacetin.The selectivity to triacetin increased rapidly with reaction time and hit the peak of 70% at 10 h reaction time.By contrast, the selectivity to monoacetin declined sharply after 10 h of reaction time.It is due to the monoacetin conversion to diacetin and triacetin as a result of further acetylation which is being completed from 2 to 10 hours.Along with these changes, the selectivity towards diacetin was found to increase significantly from 25% to 50% after 6 h reaction time.There was then a slight drop, reaching its primary value (25%) at 10 h of reaction time.The lower selectivity towards diacetin after a long reaction period was  due to the conversion of diacetin to triacetin from further acetylation.

Effect of WO 3
Loading.Besides NH 3 -TPD analysis to figure out the acid functionality, the effect of metal oxide loading of a catalyst on conversion and selectivity was investigated.As it is expected and examined by NH 3 -TPD analysis, for acid-catalysed glycerol esterification WO 3 -Ppy with 20% metal oxide loading and highest acidic performance, it showed the highest glycerol conversion and selectivity to triacetin by about 98% and 70%, respectively.As we could observe in Figure 12, catalyst with 5 wt% performed poorly in glycerol esterification with only 65% of glycerol being converted.When metal oxide was increased to 20%, glycerol conversion increased to 98%.The reaction with WO 3 as a catalyst and the blank reaction were done in the same circumstances for the sake of comparison, and the results are depicted in Figure 12.

Effect of Catalyst Weight.
The effect of catalyst amount on glycerol acetylation was also investigated.The range of 0.1 to 0.5 g of catalyst was selected, while the reaction temperature was maintained at 110 ∘ C for 10 h. Figure 13 represents a slight increase in glycerol conversion with an increase in catalyst amount from 0.1 to 0.5 g. while the selectivity to monoacetin declined by catalyst amount from 45 to 5%.In contrast, in terms of triacetin, the trend was the opposite, which means, by increasing the catalyst weight, the selectivity to triacetin increased from 15% with 0.1 g catalyst to 70% with 0.5 g catalyst, confirming the consecutive type of glycerol acetylation.It is worthwhile to mention that in case of a catalyst weighing above 0.5 g, the selectivity towards products was less influenced by the catalyst amount.

Effect of AcOH/Gly
Ratio.Glycerol conversion and selectivity during acetylation of glycerol also depend on glycerol to acetic acid molar ratio.The reaction by changing the glycerol to acetic acid molar ratio from 1 : 3 to 1 : 7 was studied, and the results are shown in Figure 14.The conversion of glycerol does not vary much with a change in molar ratio.The conversion of glycerol increased with increasing acetic acid concentration in the reaction mixture, and maximum conversion was attained at a ratio of 1 : 6.The conversion was not varied above the molar ratio of 1 : 6.However, the selectivities varied with glycerol to acetic acid molar ratio.It was observed that high molar ratio of acetic acid to glycerol leads in lower selectivity values to monoacetin, which can be explained due to the high glycerol conversion which promotes the diacetin and triacetin formations.At higher acetic acid concentrations, it is expected to get more diacetin and triacetin due to the availability of more acetic acid.

Conclusion
The composite of WO 3 and polypyrrole provided a novel catalytic platform for a good dispersion of nanosizeed WO 3 particles and enhanced acidic properties which made a composite with a significant catalytic activity.Composite with 20% WO 3 loaded exhibited a high activity (98%) and selectivity (70%) to triacetin at 110 ∘ C and also high selectivity (75%) to monoacetin at a milder reaction condition (50 ∘ C).This study indicated that the acidity nature of polypyrrole support played a very important role in the selectivity of the composite catalyst.

3. 2 .
Optimization Parameter Reaction.The influence of metal oxide loading, AcOH/Gly mole ratio, reaction temperature, catalyst weight, and reaction time on the production of monoacetin, diacetin, and triacetin were investigated for the WO 3 -polypyrrole catalyst.

3. 2 . 1 .
Effect of Reaction Temperature.The temperature effect was investigated in the range of 50 to 110 ∘ C using WO 3 -Ppy-20 catalyst as it exhibited maximum acidity value in NH 3 -TPD analysis.The reaction temperature had a significant effect on the catalytic performance of the catalyst.The conversion increased greatly from 58.2% at 50 ∘ C to 98% at 110 ∘ C.

Table 1 :
Acidic properties of the samples obtained from TPD of ammonia.